Abstract
IN an earlier letter1 one of us (W. F. B.) tried to explain the discrepancies which exist concerning the plasticity of bismuth. It was confirmed that crystals obtained by different methods behave quite differently; for example, that soft crystals, that is, crystals which slip in tensile tests at room temperature, occur among those made in air (Czochralski method), whereas only hard crystals are obtained in vacuo (Bridgman method). Since the crystals made under atmospheric pressure were found to contain some gas, it was suggested that the gas was responsible for their softness. Hard crystals made in vacuo were found to slip in compression tests at room temperature and in tensile tests at higher temperatures2. Experiments by Gough3 and by Andrade and Roscoe4 seem to support these findings.
Similar content being viewed by others
Article PDF
References
NATURE, 133, 831; 1934.
NATURE, 134, 143; 1934.
Proc. International Conference on Physics, 2, 180; 1934.
ibid., 2, 176.
ibid., 2, 176.
Z. Phys., 36, 759; 1926.
J. Inst. Metals, 48, 227; 1932.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
BERG, W., SANDLER, L. Plasticity of Bismuth. Nature 136, 915 (1935). https://doi.org/10.1038/136915a0
Issue Date:
DOI: https://doi.org/10.1038/136915a0
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.