Article | Open

Electronic structure and electron-phonon coupling in TiH2

  • Scientific Reports 6, Article number: 28102 (2016)
  • doi:10.1038/srep28102
  • Download Citation
Received:
Accepted:
Published online:

Abstract

Calculations using first principles methods and strong coupling theory are carried out to understand the electronic structure and superconductivity in cubic and tetragonal TiH2. A large electronic density of states at the Fermi level in the cubic phase arises from Ti-t2g states and leads to a structural instability towards tetragonal distortion at low temperatures. However, constraining the in-plane lattice constants diminishes the energy gain associated with the tetragonal distortion, allowing the cubic phase to be stable at low temperatures. Calculated phonon dispersions show decoupled acoustic and optic modes arising from Ti and H vibrations, respectively, and frequencies of optic modes to be rather high. The cubic phase has a large electron-phonon coupling parameter λ and critical temperature of several K. Contribution of the hydrogen sublattice to λ is found to be small in this material, which we understand from strong coupling theory to be due to the small H-s DOS at the Fermi level and high energy of hydrogen modes at the tetrahedral sites.

Introduction

Materials containing light elements such as hydrogen are promising candidates for high temperature superconductors1, particularly under pressure when the materials become metallic2. Recent discovery of superconductivity above 200 K in H2S under pressure3 has confirmed these predictions4,5 and reinvigorated the excitement in the potential of these systems. Metal-hydrogen systems are a class of hydrogen rich materials characterized by large electronic densities at the Fermi level at ambient pressure6. Although critical temperatures (Tc) are much smaller than hydrogen rich materials under pressure, metal-hydrides such as Th4H15 (Tc 8 K) and PdHx (Tc 11 K) are superconductors at ambient pressure7,8, and high pressure phases of TiD0.74 have been reported to be superconducting near 4 K9.

In conventional superconductors, the relevant parameter is the electron-phonon coupling, defined within strong coupling theory10 as:

The numerator contains the electronic terms, where N(εF) is electron density at the Fermi level and 〈I2〉 is the electron-ion matrix element averaged over the Fermi sea. The denominator arises from lattice phonons, M is ion mass and 〈ω2〉 is the average phonon frequency squared10. Inspection of Eq. (1) reveals that large electron phonon coupling (and consequently high critical temperatures Tc) is realized in a system with a large density of electronic states at the Fermi level, relatively low phonon energies and/or low ionic mass6.

Dihydrides of the form MH2 (M = Ti, Zr, Nb etc.) with face centered cubic structure exhibit a sharp peak in density of states at the Fermi level and have soft phonon modes from the heavy metal atoms, thus making them good candidates for superconductivity11,12. Unfortunately, the large N(εF) coupled with weak lattice stiffness leads to a martensitic phase transition to a body-centered tetragonal structure below 310 K13,14. This transition diminishes the density of electrons at the Fermi level. Consequently, AC susceptibility measurements of slightly hydrogen rich TiH2.07 found a superconducting transition to be very small, below 15 mK15. Theoretical calculations on related compounds ZrH2 and NbH2 suggested the Tc in these systems to be lower than that of pure metals16.

In this manuscript, we present results of first principles calculations carried out to understand the electronic structure and electron-phonon interaction in cubic and tetragonal phases of TiH2. We find that constraining the in-plane lattice constants close to 3.13 Å can preserve the cubic phase at low temperatures which we find to have large electron phonon coupling and Tc of several K. Surprisingly, the contribution of H vibrations to λ is found to be small in this material and possible reasons are discussed.

Results

In the cubic phase () of TiH2, the Ti ions occupy a face centered lattice (fcc) with a = 4.42 Å in which the H ions occupy tetrahedral sites17. The Ti ions are surrounded by eight H ions forming a cube with Ti-H distance of 1.92 Å. Below 310 K, a tetragonal phase is stable in which the unit cell is compressed along c and expanded along other directions. In the smallest cell with full symmetry, the Ti ions form a body centered tetragonal (bct) lattice with space group I4/mmm with a = b = 3.2 Å and c = 4.28 Å (note that, in this cell corresponds to the cubic lattice)18. Other than a small increase in Ti-H bondlengths to 1.93 Å as a consequence of a small squeeze of TiH8 cube along c, the bonds remain unchanged.

Electronic structure

The band structures for fcc and bct phases are shown in Fig. 1. The bands around −8 eV and +8 eV (not shown) have strong Ti-s character which leads to approximately half filled s band. In the fcc phase, under the influence of the cubic crystal field, the eg and t2g states are split by 1.8 eV at the Γ point with triply degenerate t2g states occupied just below the Fermi level and the doubly degenerate eg states empty. Away from Γ, the t2g bands couple strongly with H-s states and exhibit a large dispersion from −6 to 6 eV. In contrast, the eg bands are narrower with a bandwidth of 6 eV. The band starting at −5 eV at L and increasing along L − Γ − X has strong H-s character and is half filled, indicating 1s1 configuration for H ions.

Figure 1: Electronic band structure for the cubic fcc (left) and tetragonal bct (right) phases of TiH2.
Figure 1

Red and blue colored bands correspond to Ti-eg and Ti-t2g characters, respectively.

The tetragonal distortion breaks the cubic crystal field19 and lifts the degeneracy of t2g into a singlet dxy band just above εF and a doublet dxz/yz below. The eg also splits into (above) and (below). Otherwise, as the figure shows, the dispersion of bands at generic k-points are hardly affected by the distortion.

The total and partial density of states (DOS) plotted in Fig. 2 suggest electronic configuration of 3d34s1 for Ti. The DOS is dominated by a peak around −6 eV mostly containing H-s and Ti-t2g states and a broad feature around the Fermi level originating from Ti-d states. Due to the nearly flat bands in the Γ − L direction, there is a large density at the Fermi level N(εF) = 2.59 eV−1 per Ti. Most of this density comes from the t2g states with Nt2g(εF) = 1.92 and Neg(εF) = 0.67 eV−1. Note that the contribution from H-s states to the density is quite small at Ns(εF) = 0.001 eV−1 per H, which has important implications for superconductivity as will be discussed later. The crystal field in the tetragonal structure breaks the degeneracy of the states and splits the peak in the DOS at εF (see Fig. 2). There are two peaks at −0.16 and 0.27 eV with peak heights of 1.7 and 2.0 eV−1, respectively. The Fermi level sits in the valley, with N(εF) = 0.97 eV−1, which is a more than a 60% drop from that of the cubic phase. Since the electron-phonon coupling strength is proportional to N(εF), we can see why the tetragonal phase is not a favorable candidate for superconductivity.

Figure 2: Total and partial density of states for the cubic fcc (top) and tetragonal bct (bottom) phases of TiH2.
Figure 2

The Fermi level is set to 0 eV. Lines indicate total (black), Ti-eg (blue) and Ti-t2g (red) characters while green shaded area is H-s.

The Fermi surfaces for the two phases of TiH2 are shown in Fig. 3. As can be seen from the band structure plots in Fig. 1, two bands cross the Fermi level, leading to large electron pockets around Γ. In the tetragonal phase, the band splittings lead to additional features in the Fermi surfaces. Figure 3 suggests that Fermi surfaces in TiH2 are not amenable to nesting induced instabilities.

Figure 3
Figure 3

Calculated Fermi surfaces for the (a) fcc and (b) bct phases corresponding to the two bands that cross the Fermi level.

The Jahn-Teller (JT) theorem stipulates that a non-linear molecule with degenerate electronic ground states will be unstable against symmetry lowering distortion20. For a single electron in doubly degenerate states, JT distortion Q lowers the energy of one of the states by −gQ and the equilibrium configuration is decided by the competition between this and an elastic term of the form KQ2/2, where g and K are proportionality constants. In a solid, the expression also involves a positive band energy term since electron hopping prefers degenerate states21. It can be shown that, JT distortion occurs in a material when the coupling parameter g is sufficiently strong, viz., g2/(WK) > μc, where W is the bandwidth and μc is the critical limit21, which is μc 0.5 for a two state, one electron system discussed above. Incidentally, in systems with heavy elements such as HfH2, spin-orbit coupling partially lifts the degeneracy of the levels near εF14, but the system remains JT active, since the distortion Q can further lower the energy.

In the relaxed structure within GGA, the lattice constants of TiH2 tetragonal phase are a = b = 3.21 Å and as can be seen from Fig. 4(a), the energy is minimum for . Decreasing a shifts the minimum to higher c/a and for a = 3.13 Å the optimal , making the cubic phase stable. As shown in Fig. 4(b), the ratio c/a decreases almost linearly as the in-plane lattice constants are increased. Thus, constraining the in-plane lattice constants close to a = b = 3.13 Å can shift the stable phase of TiH2 close to cubic, which may be achievable in experiments by growing the material on a suitable substrate with appropriate lattice constants.

Figure 4
Figure 4

(a) Energy variation of the system as function of c/a ratio for fixed in-plane lattice constant a as marked left of the curves. The energy is shifted by its value when (Ec). The minima of the curves are marked by dashed vertical lines. (b) Variation of c/a corresponding to minimum energy as a function of a. The ratio corresponds to the cubic phase.

Electron-phonon coupling

The phonon dispersion curves and corresponding densities of states for the cubic and tetragonal structures in the experimental structures calculated using density functional perturbation theory are plotted in Fig. 5. As expected, the acoustic dispersions have predominantly Ti character while the optic modes that lie between 33–40 THz originates from hydrogen vibrations. We find soft modes in the phonon dispersion curves of the cubic phase around the Γ point, which can be suppressed by choosing a larger temperature smearing, σ, of electronic states near the Fermi level12. Figure 5 is calculated with σ = 0.2 eV, which barely removes the negative frequencies in the fcc phase (σ = 0.14 eV is used for the bct phase). Similar to the electronic band structure, the reduced symmetry in the tetragonal phase lifts the degeneracies of dispersions at high symmetry points, but leaves very similar phonon density of states in both structures.

Figure 5: The phonon dispersions and density of states for cubic (left) and tetragonal (right) phases of TiH2.
Figure 5

Electronic smearing of σ = 0.2 eV is used to remove the negative frequencies in the cubic phase. Partial DOS for Ti (blue) and H (red) are plotted in the right panel.

To get the strength of coupling between electrons and phonons, we calculated the Eliashberg spectral function α2F(ω) using QE package for fcc and bct phases, that are shown in Fig. 6. We find that in both cases the function has two main peaks; one below 10 THz and another between 33–42 THz. The low energy peak arises from the acoustic modes, while the high energy peak arises from optic modes that are nearly decoupled in these systems. As a consequence of the reduction of N(εF) in the case of the tetragonal phase α2F(ω) is smaller. The electron-phonon coupling parameter, , is also plotted as dotted lines in Fig. 6, which show that Ti modes contribute predominantly towards λ. In the cubic phase, we get λfcc = 0.87, which drops to λbct = 0.33 in the bct phase. More accurate estimate of λ values calculated by summing over the reciprocal space λ(q) yield, λfcc = 0.84 and λbct = 0.22. Using these values in the simplified Allen-Dynes formula22 to calculate the Tc with the typical value of μ* = 0.1 for the Coulomb coefficient23, we get Tc = 6.7 K in the cubic phase, which drops to Tc = 2 mK in the tetragonal phase. In comparison, the experiments on TiH2.07 report superconducting behavior below 15 mK15, which is reasonably close to our calculated value for bct phase. We note that the λfcc is comparable to that of MgB2, which is superconducting at 40 K. The lower Tc here is because of the smaller log mean frequency ωlog in TiH2, which is 127.1 K, compared to ωlog = 650 K in MgB224.

Figure 6: Calculated Eliashberg spectral function α2F(ω) (solid lines) and electron-phonon coupling parameter λ(ω) (dashed lines) for fcc (black) and bct (blue) phases.
Figure 6

The contribution of hydrogen modes to electron-phonon coupling and consequently to Tc is much smaller than other hydrides such as PdH and H3S, where hydrogen plays a dominant role16,25. To understand this, we calculate λ using McMillan’s strong coupling theory10 given in Eq. (1). Since the acoustic and optic modes have negligible hydrogen and metal character respectively, we can write λ = λTi + 2λH. We calculate the numerator in Eq. (1), η = N(εF)〈I2〉, with the help of Gaspari-Gyorffy theory26,

where, is the ratio of the lth partial DOS at Fermi energy to single-site DOS at Fermi energy and δl are the scattering phase shifts for the angular momentum l. Taking the calculated phase shifts and partial densities for cubic TiH2 from ref. 27, we get: η Ti = 3.9 eV/Å2 and ηH = 0.07 eV/Å2. The ηH is much smaller than that of Ti in this system compared to PdH where ηPd/ηH = 1.3816. It is a consequence of much smaller H-s density at the Fermi level in TiH2, which is only 0.001 eV−1 (Fig. 2), in contrast to PdH, where it is 0.019 eV−1.

The renormalized phonon frequencies 〈ω2〉 are calculated using the definitions in ref. 10 and our phonon data to get, 〈ω2Ti = 6.72 × 1026 (rad/sec)2 and 〈ω2H = 5.32 × 1028 (rad/sec)2. The frequencies of hydrogen modes in TiH2 are higher than those in other hydrogen rich systems, which also lead to the smaller contribution of hydrogen modes to λ in this system. Putting everything together, we get for the cubic phase of TiH2:

Adding up, we get λfcc = 1.19 from strong coupling theory, which overestimates λ from our first principles calculated value of 0.84. However, considering the crudeness of the strong coupling model, the agreement is reasonable. Crucially, it explains the insignificant contribution from hydrogen in this system, due to a small density of H electronic states at the Fermi energy coupled with unusually high energies of the hydrogen sublattice vibrations in TiH2. In H3S, the N(EF) at high pressures, although small, is dominated by H-s states and is crucial for the reported high Tc. To enhance the Tc in transition metal hydrides such as TiH2, will likely require manipulating the electronic structure via pressure, doping or replacing Ti with other transition metal ions to increase the H-s density near the Fermi level. We hope that this work inspires further studies to this end.

Discussion

In summary, our theoretical calculations show that the cubic phase of TiH2 has large electron density at the Fermi level arising from nearly flat triply degenerate Ti-t2g bands in the Γ − L direction. This large density of N(εF) = 2.59 eV−1 combined with relatively weak structural elastic energy, leads to a cubic-to-tetragonal distortion at low temperatures. However, constraining the in-plane lattice constants to 3.13 Å makes the cubic geometry energetically favorable, which may be possible to achieve by a suitably lattice matched substrate. The calculated phonon dispersions for the cubic and tetragonal phases show many similarities owing to the smallness of the distortion. We estimate that, λfcc = 0.84, Tc = 6.7 K for the cubic phase and λbct = 0.22, Tc =2 mK for the tetragonal phase. The contribution of hydrogen modes to the electron-phonon coupling is small, which is a consequence of small H-s density at the Fermi level and unusually hard hydrogen modes in this system. Alloying with other transition metals and with isotopes of hydrogen can potentially enhance the contribution from the hydrogen sublattice, by shifting the H-s levels and lowering optic modes, respectively, and require further investigations.

Methods

First principles calculations within density functional theory and the generalized gradient approximation (GGA)28 are employed. The VASP code29,30 with projector augmented waves as basis is used for the electronic structure calculations. An energy cutoff of 450 eV and k space sampling on a 24 × 24 × 24 grid are found sufficient to get converged results. The phonon dispersions and electron-phonon couplings are obtained using the Quantum Espresso package31 with ultrasoft pseudopotentials, energy cutoff of 544 eV (40 Ry) and a q-grid of 8 × 8 × 8.

Additional Information

How to cite this article: Shanavas, K. V. et al. Electronic structure and electron-phonon coupling in TiH2. Sci. Rep. 6, 28102; doi: 10.1038/srep28102 (2016).

References

  1. 1.

    Metallic hydrogen: A high-temperature superconductor? Phys. Rev. Lett. 21, 1748–1749, 10.1103/PhysRevLett.21.1748 (1968).

  2. 2.

    , , , & General trend for pressurized superconducting hydrogen-dense materials. P. Natl. Acad. Sci. USA 107, 2793–2796, 10.1073/pnas.0914462107 (2010).

  3. 3.

    , , , & Conventional superconductivity at 203 kelvin at high pressures in the sulfur hydride system. Nature (London) 525, 73–76, 10.1038/nature14964 (2015).

  4. 4.

    et al. Pressure-induced metallization of dense (h2s)2h2 with high-tc superconductivity. Sci. Rep. 4, 6968, 10.1038/srep06968 (2014).

  5. 5.

    et al. Pressure-induced decomposition of solid hydrogen sulfide. Phys. Rev. B 91, 180502, 10.1103/PhysRevB.91.180502 (2015).

  6. 6.

    Electron-phonon coupling and superconductivity in metal-hydrogen systems. J. Less-Common Met. 101, 53–67, 10.1016/0022-5088(84)90087-0 (1984).

  7. 7.

    & Superconductivity of hydrides and deuterides of thorium. Phys. Rev. Lett. 25, 741–743, 10.1103/PhysRevLett.25.741 (1970).

  8. 8.

    & Superconductivity in the palladium-hydrogen and the palladium-deuterium systems. Z. Physik 257, 1–8, 10.1007/bf01398191 (1972).

  9. 9.

    , , & Superconductivity in the ti-d system under pressure. Phys. Solid State 40, 1950–1952, 10.1134/1.1130711 (1998).

  10. 10.

    Transition temperature of strong-coupled superconductors. Phys. Rev. 167, 331–344, 10.1103/PhysRev.167.331 (1968).

  11. 11.

    , , & First-principles investigations of isotope effects in thermodynamic properties of TiX2 (X = H, D, and T) system. J. Alloy. Compd. 450, 369–374, 10.1016/j.jallcom.2006.10.130 (2008).

  12. 12.

    , , , & Ab initio study of the electronic structure and phonon dispersions for TiH2 and ZrH2. In , , , & (eds.) Carbon Nanomaterials in Clean Energy Hydrogen Systems, 705–712 (Springer Netherlands, 2008).

  13. 13.

    Electronically driven tetragonal distortion in TiH2. Solid State Commun. 29, 47–51, 10.1016/0038-1098(79)90149-2 (1979).

  14. 14.

    , & Electronic structure and energetics of the tetragonal distortion for TiH2, ZrH2, and HfH2: A first-principles study. Phys. Rev. B 80, 184103, 10.1103/PhysRevB.80.184103 (2009).

  15. 15.

    , , & Interplay of nuclear magnetism and superconductivity. J. Low Temp. Phys. 110, 405–410, 10.1023/A:1022565607158 (1998).

  16. 16.

    Electronic properties and electron-phonon coupling in zirconium and niobium hydrides. Phys. Rev. B 25, 1027–1038, 10.1103/PhysRevB.25.1027 (1982).

  17. 17.

    et al. Structure and stability of high pressure synthesized Mg–TM hydrides (TM = Ti, Zr, Hf, V, Nb and Ta) as possible new hydrogen rich hydrides for hydrogen storage. J. Mater. Chem. 19, 8150, 10.1039/b911263d (2009).

  18. 18.

    Thermocrystallography of higher hydrides of titanium and zirconium. Acta Cryst. 11, 46–51, 10.1107/s0365110×58000098 (1958).

  19. 19.

    Introduction to ligand field theory (McGraw-Hill, New York, 1962).

  20. 20.

    & Stability of polyatomic molecules in degenerate electronic states. I. orbital degeneracy. P. Roy. Soc. A-Math. Phy. 161, 220–235, 10.1098/rspa.1937.0142 (1937).

  21. 21.

    , & Electronic structure of Ba3CuSb2O9: A candidate quantum spin liquid compound. Phys. Rev. B 89, 085130, 10.1103/PhysRevB.89.085130 (2014).

  22. 22.

    Influence of the phonon spectra of In-Tl alloys on the superconducting transition temperatures. Phys. Rev. B 2, 644–656, 10.1103/PhysRevB.2.644 (1970).

  23. 23.

    Properties of boson-exchange superconductors. Rev. Mod. Phys. 62, 1027–1157, 10.1103/RevModPhys.62.1027 (1990).

  24. 24.

    , & Beyond Eliashberg superconductivity in MgB2: Anharmonicity, two-phonon scattering, and multiple gaps. Phys. Rev. Lett. 87, 087005, 10.1103/PhysRevLett.87.087005 (2001).

  25. 25.

    , , & Cubic H3S around 200 GPa: An atomic hydrogen superconductor stabilized by sulfur. Phys. Rev. B 91, 184511, 10.1103/PhysRevB.91.184511 (2015).

  26. 26.

    & Electron-phonon interactions, d resonances, and superconductivity in transition metals. Phys. Rev. Lett. 28, 801–805, 10.1103/PhysRevLett.28.801 (1972).

  27. 27.

    Superconductivity in metal hydrides. In & (eds.) Electronic Structure and Properties of Hydrogen in Metals, 321–334 (Springer Science + Business Media, 1983).

  28. 28.

    , & Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865, 10.1103/PhysRevLett.77.3865 (1996).

  29. 29.

    & Ab-initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558, 10.1103/physrevb.47.558 (1993).

  30. 30.

    & Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169, 10.1103/PhysRevB.54.11169 (1996).

  31. 31.

    et al. QUANTUM ESPRESSO: a modular and open-source software project for quantum simulations of materials. J. Phys.: Condens. Matter 21, 395502 (2009).

Download references

Acknowledgements

This research was supported by the US Department of Energy, Basic Energy Sciences, Office of Science, Materials Sciences and Engineering Division.

Author information

Affiliations

  1. Materials Science & Technology Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831-6056, USA

    • K. V. Shanavas
    • , L. Lindsay
    •  & D. S. Parker

Authors

  1. Search for K. V. Shanavas in:

  2. Search for L. Lindsay in:

  3. Search for D. S. Parker in:

Contributions

K.V.S. carried out the calculations. K.V.S., L.L. and D.S.P. analyzed the results. All authors reviewed the manuscript.

Competing interests

The authors declare no competing financial interests.

Corresponding author

Correspondence to K. V. Shanavas.

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Creative Commons BYThis work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/