Abstract
Finding highly active and low-cost catalysts is a crucial endeavour to harvest clean hydrogen via electrochemical water splitting. Currently, the best catalyst for the hydrogen evolution reaction is based on metallic platinum whose high price severely restricts large-scale application. Here we report a silver catalyst with superior activity and durability in an acid medium that outperforms commercial platinum on carbon, especially under high applied voltages. We adopt a physical technique—laser ablation in liquid—to generate a high density of stacking faults in silver nanoparticles. We find that the stacking faults can cause a low coordination number and high tensile strain, which jointly improve the adsorption energy and transform the non-active silver into a highly active catalyst. In light of the high activity, conductivity, durability and low price, the silver catalyst can serve as a promising alternative to commercial platinum on carbon for industrial application.
This is a preview of subscription content, access via your institution
Access options
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 12 digital issues and online access to articles
$119.00 per year
only $9.92 per issue
Buy this article
- Purchase on Springer Link
- Instant access to full article PDF
Prices may be subject to local taxes which are calculated during checkout
Similar content being viewed by others
Data availability
The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.
References
Su, J. W. et al. Ruthenium-cobalt nanoalloys encapsulated in nitrogen-doped graphene as active electrocatalysts for producing hydrogen in alkaline media. Nat. Commun. 8, 14969 (2017).
Lu, X. F., Yu, L. & Lou, X. W. Highly crystalline Ni-doped FeP/carbon hollow nanorods as all-pH efficient and durable hydrogen evolving electrocatalysts. Sci. Adv. 5, 6009 (2019).
Zheng, Y., Jiao, Y., Jaroniec, M. & Qiao, S. Z. Advancing the electrochemistry of the hydrogen evolution reaction through combining experiment and theory. Angew. Chem. Int. Ed. 54, 52–65 (2015).
Jiao, Y., Zheng, Y., Jaroniec, M. & Qiao, S. Z. Design of electrocatalysts for oxygen- and hydrogen-involving energy conversion reactions. Chem. Soc. Rev. 44, 2060–2086 (2015).
Fan, X. B. et al. Controlled exfoliation of MoS2 crystals into trilayer nanosheets. J. Am. Chem. Soc. 138, 5143–5149 (2016).
Xia, Y. N. In my element: silver. Chem. Eur. J. 24, 1–2 (2018).
Zhou, Y. et al. Oxygen reduction at very low overpotential on nanoporous Ag catalysts. Adv. Energy Mater. 5, 1500149 (2015).
Uchida, T., Mogami, H., Yamakata, A., Sasaki, Y. & Osawa, M. Hydrogen evolution reaction catalyzed by proton-coupled redox cycle of 4,4’-bipyridine monolayer adsorbed on silver electrodes. J. Am. Chem. Soc. 130, 10862–10863 (2008).
Campbell, F. W., Belding, S. R., Baron, R., Xiao, L. & Compton, R. G. The hydrogen evolution reaction at silver nanoparticle array and a silver macroelectrode compared: changed electrode kinetics between the macro- and nanoscales. J. Phys. Chem. C. 113, 14852–14857 (2009).
Safavi, A., kazemi, S. H. & Kazemi, H. Electrocatalytic behaviors of silver-palladium nanoalloys modified carbon ionic liquid electrode towards hydrogen evolution reaction. Fuel 118, 156–162 (2014).
Khorshidi, A., Violet, J., Hashemi, J. & Peterson, A. A. How strain can break the scaling relations of catalysis. Nat. Catal. 1, 263–268 (2018).
Calle-Vallejo, F. et al. Finding optimal surface sites on heterogeneous catalysts by counting nearest neighbors. Science 350, 185–189 (2015).
Zambelli, T., Wintterlin, J., Trost, J. & Ertl, G. Identification of the “active sites” of a surface-catalyzed reaction. Science 273, 1688–1699 (1996).
Nørskov, J. K., Bligaard, T., Rossmeisl, J. & Christensen, C. H. Towards the computational design of solid catalysts. Nat. Chem. 1, 37–46 (2009).
Tedsree, K. et al. Hydrogen production from formic acid decomposition at room temperature using a Ag–Pd core–shell nanocatalyst. Nat. Nanotechnol. 6, 302–307 (2011).
Escudero-Escribano, M. et al. Pt5Gd as a highly active and stable catalyst for oxygen electroreduction. J. Am. Chem. Soc. 134, 16476–16479 (2012).
Wang, H. T. et al. Direct and continuous strain control of catalysts with tunable battery electrode materials. Science 354, 1031–1036 (2016).
Wang, L. et al. Tunable intrinsic strain in two-dimensional transition metal electrocatalysts. Science 363, 870–874 (2019).
Strasser, P. et al. Lattice-strain control of the activity in dealloyed core–shell fuel cell catalysts. Nat. Chem. 2, 454–460 (2010).
Escudero-Escribano, M. et al. Tuning the activity of Pt alloy electrocatalysts by means of the lanthanide contraction. Science 352, 73–76 (2016).
Edalati, K. & Horita, Z. J. High-pressure torsion of pure metals: Influence of atomic bond parameters and stacking fault energy on grain size and correlation with hardness. Acta Mater. 59, 6831–6836 (2011).
Qin, Y. C. et al. Microwave-assisted synthesis of multiply-twinned Au–Ag nanocrystals on reduced graphene oxide for high catalytic performance towards hydrogen evolution reaction. J. Mater. Chem. A 4, 3865 (2016).
Xia, X. H., Shen, X., Zhao, X. J., Ye, W. C. & Wang, C. M. Operando synthesis of a dendritic and well-crystallized molybdenum oxide/silver catalyst for enhanced activity in the hydrogen evolution reaction. ChemCatChem 7, 2517–2525 (2015).
Yin, J. et al. Ni–C–N nanosheets as catalyst for hydrogen evolution reaction. J. Am. Chem. Soc. 138, 14546–14549 (2016).
Deng, J. et al. Multiscale structural and electronic control of molybdenum disulfide foam for highly efficient hydrogen production. Nat. Commun. 8, 14430 (2017).
Kiritani, M. Story of stacking fault tetrahedra. Mater. Chem. Phys. 50, 133–138 (1997).
Cao, L. L. et al. Identification of single-atom active sites in carbon-based cobalt catalysts during electrocatalytic hydrogen evolution. Nat. Catal. 2, 134–141 (2019).
Jiao, J. Q. et al. Copper atom-pair catalyst anchored on alloy nanowires for selective and efficient electrochemical reduction of CO2. Nat. Chem. 11, 222–228 (2019).
Sun, Y. F. et al. Pits confined in ultrathin cerium (iv) oxide for studying catalytic centers in carbon monoxide oxidation. Nat. Commun. 4, 2899 (2013).
Behafarid, F. et al. Structural and electronic properties of micellar Au nanoparticles: size and ligand effects. ACS Nano 8, 6671–6681 (2014).
Ling, T. et al. Activating cobalt (ii) oxide nanorods for efficient electrocatalysis by strain engineering. Nat. Commun. 8, 1509 (2017).
Gan, L., Yu, R., Luo, J., Cheng, Z. Y. & Zhu, J. Lattice strain distributions in individual dealloyed Pt–Fe catalyst nanoparticles. J. Phys. Chem. Lett. 3, 934–938 (2012).
Jiao, Y., Zheng, Y., Davey, K. & Qiao, S. Z. Activity origin and catalyst design principles for electrocatalytic hydrogen evolution on heteroatom-doped graphene. Nat. Energy 1, 16130 (2016).
Wang, C. Q. et al. Creation of controllable high-density defects in silver nanowires for enhanced catalytic property. Nano Lett. 16, 5669–5674 (2016).
Zheng, Y. et al. High electrocatalytic hydrogen evolution activity of an anomalous ruthenium catalyst. J. Am. Chem. Soc. 138, 16174–16181 (2016).
Mahmood, J. et al. An efficient and pH-universal ruthenium-based catalyst for the hydrogen evolution reaction. Nat. Nanotechnol. 12, 441–446 (2017).
Banerjee, A., Dick, G. R., Yoshino, T. & Kanan, M. W. Carbon dioxide utilization via carbonate-promoted C–H carboxylation. Nature 531, 215–219 (2014).
Acknowledgements
This work was supported in part by the Natural Science Foundation of China (grant nos. 51871160, 51671141, 51471115). The authors thank the BL14W1 beam line of the Shanghai Synchrotron Radiation Facility for synchrotron beam time and Y. L. Liang from Shanghai Institute of Applied Physics (Chinese Academy of Sciences) for XAS measurements. The authors thank R. C. Luo from the State Key Laboratory of Metal Matrix Composites (Shanghai Jiao Tong University) for TEM measurements.
Author information
Authors and Affiliations
Contributions
X.-W.D. designed the project. Z.L. and Y.F. performed the experiment under the direction of X.-W.D. Z.L. and X.-WD. performed the experimental data analysis. J.-Y.F. and C.-K.D. performed the theoretical calculation. Z.L. and H.L. conducted the XAS test and analysed the data. Z.L. and X.-W.D. wrote the paper. All authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Supplementary Information
Supplementary Figs. 1–54, Tables 1–3 and references.
Supplementary Dataset 1
Atomic coordinates of the optimized computational models.
Rights and permissions
About this article
Cite this article
Li, Z., Fu, JY., Feng, Y. et al. A silver catalyst activated by stacking faults for the hydrogen evolution reaction. Nat Catal 2, 1107–1114 (2019). https://doi.org/10.1038/s41929-019-0365-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41929-019-0365-9
This article is cited by
-
Extrinsic hydrophobicity-controlled silver nanoparticles as efficient and stable catalysts for CO2 electrolysis
Nature Communications (2024)
-
Recent progress on catalyst design of nitrogen reduction reaction by density functional theory
Science China Materials (2024)
-
Edge dislocation-induced strains break the limit of PtNi alloys in boosting Pt mass activity for efficient alkaline hydrogen evolution
Nano Research (2024)
-
Accelerating multielectron reduction at CuxO nanograins interfaces with controlled local electric field
Nature Communications (2023)
-
Coherent hexagonal platinum skin on nickel nanocrystals for enhanced hydrogen evolution activity
Nature Communications (2023)