Tungsten oxide and its associated bronzes (compounds of tungsten oxide and an alkali metal) are well known for their interesting optical and electrical characteristics. We have modified the transport properties of thin WO3 films by electrolyte gating using both ionic liquids and polymer electrolytes. We are able to tune the resistivity of the gated film by more than five orders of magnitude, and a clear insulator-to-metal transition is observed. To clarify the doping mechanism, we have performed a series of incisive operando experiments, ruling out both a purely electronic effect (charge accumulation near the interface) and oxygen-related mechanisms. We propose instead that hydrogen intercalation is responsible for doping WO3 into a highly conductive ground state and provide evidence that it can be described as a dense polaronic gas.
Electrolyte gating has attracted much attention lately as an alternative to chemical doping to tune the carrier concentration in various materials.1,2,3,4,5,6,7,8,9,10,11,12,13,14,15,16,17,18,19,20,21,22,23 It enables large changes in the sheet carrier density, as high as 1015 cm−2, which can be utilized for detailed studies of electronic phase transitions and search for new superconducting phases. The mechanisms at play in this technique, however, are under debate. One view is that the charging process is purely electronic. In this case two electric double layers are formed, one at the gate and one at the material being gated, as the ions in the electrolyte are drawn to these two surfaces. The strong electric fields created at these two locations are screened on the scale of the screening length (~ 1 nm) by mobile charge carriers drawn into the gate and the material being studied, changing their carrier concentrations.3,4,5,6,7,8, 12, 23 On the other hand, in recent experiments, it has been observed that entire gated films of oxides, 100 nm thick and even more, became metallic upon electrolyte gating.10, 11, 14, 16 This apparent paradox has led to the competing claim that the main mechanism of sample charging is in fact an electrochemical process, such as oxygen intercalation or the formation of oxygen vacancies induced by the strong electric field, as indeed thoroughly substantiated in the case of VO211 and SrRuO3.16 Furthermore, some studies have also shown that this dichotomy in mechanisms does not always strictly hold and that both processes can be important in affecting changes in materials.15, 18, 20
Tungsten oxide (WO3) is a natural candidate for electrolyte gating measurements as it has been widely studied for its special optical and electrical properties24, 25 and can be chemically doped by a large variety of elements, forming an extensive family of compounds known as tungsten bronzes. Some of these compounds are superconducting,26,27,28,29,30 with the transition temperature (Tc) in the range from 0.5 K to 7 K. More alluring, Reich et al. have reported a two-dimensional (2D) superconducting phase at the surface of Na-doped WO3, with Tc ≈ 90 K.31, 32 Evidence for similar localized but disconnected superconducting regions with Tc ≈ 125 K have also been reported in Na x WO3-y infiltrated into nanoporous materials.33 A few groups have recently performed electrolyte gating work with ionic liquids on WO3,19,20,21,22 varying the resistivity by at least an impressive 8 orders of magnitude and producing transitions from insulating to metallic behavior when the sample sheet resistance is around 1 kΩ/□. None, however, have observed any superconducting phases. Several explanations for how the excess conductivity is created in WO3 by electrolyte gating have been put forth from electrostatic,19, 22 to a mix of electrostatic and electrochemical processes,20 to a structural phase transition driven by oxygen removed from WO3 by the applied electric field,21 with no apparent consensus.
In the present study, we performed extensive charging experiments on atomically flat WO3 films using either polymer electrolytes or ionic liquids as gate dielectrics. After the samples are fully charged, we observe large drops in the sheet resistance, and a clear insulator-to-metal transition. Although we have densely covered a large range of doping levels, we have seen no indications of superconductivity down to 300 mK. Our experiments on films of different thicknesses indicate that the entire films are affected by the electrolyte gating, and hence the charging process cannot be purely electrostatic. By further experiments we have demonstrated that oxygen electromigration is not involved in the charging process, either. Instead, we propose and provide evidence for charging dominated by hydrogen (specifically H+) intercalation.
The WO3 films were synthesized by rf-magnetron sputtering on single-crystal YAlO3 substrates (see Methods). The small lattice mismatch enabled us to synthesize high quality WO3 films with atomically flat surfaces (Fig. 1). The films were patterned in Hall-bar configuration devices (Supplementary Fig. S1) of different sizes using microfabrication techniques. Two different electrolytes were used in the experiments. One was a polymer electrolyte, sodium fluoride salt dissolved in 1000 molecular weight polyethylene glycol (PEG-NaF). It is a wax-like solid at room temperature and can be charged (i.e., it acts as a conductive electrolyte) at T = 305 K. The other electrolyte was the ionic liquid diethylmethyl(2-methoxyethyl)ammonium bis(trifluoromethylsulfonyl)imide (DEME-TFSI).5 It is liquid at room temperature but freezes to a glassy state at T = 240 K. In our experiments, we changed the gate voltage (V G ) at the charging temperature, kept it at that temperature for 30 min, and then slowly cooled down to liquid helium temperature, while measuring the device resistance.
In Fig. 2 we show the temperature dependence of the resistivity (ρ) at various gate voltages for four films of different thicknesses. We used the ionic liquid DEME-TFSI for sample C and the polymer electrolyte PEG-NaF for the other three samples. Despite the differences, the transport data for these four samples are very similar to each other. The original samples (V G = 0 V) are very insulating, with the resistivity exceeding 10 Ω-cm at 250 K. When a positive gate voltage is applied, the resistance drops, indicating that mobile electrons have been induced in the sample. The highest gate voltage we used was in the range 2.0–2.2 V; at higher voltages, the resistance saturates. We usually keep the samples charged at the highest voltage for several hours until the resistance shows no further changes. At the highest gate voltage, the samples reach a metallic state with a positive temperature slope of resistance (dρ/dT > 0). The sheet resistance drops more than 5 orders of magnitude at T = 200 K, and much more at lower temperatures, comparable to the change in resistivity observed in previous electrolyte gating studies on WO3.
The resistivity of a charged and saturated WO3 film at T = 200 K is about 110 μΩ-cm, which is three times smaller (i.e., more metallic) than what we see in optimally doped cuprate films showing high-T c superconductivity. However, we did not see any signs of superconductivity, down to T = 300 mK, in any of the WO3 films we have studied so far (Supplementary Fig. S2). Given that we have covered a wide range of doping levels, this seems to contradict the claims of 2D high-Tc superconductivity at the surface of Na-doped WO3.31, 32 A (remote) possibility is that doping by Na may not only provide mobile carriers but also cause unidentified structural changes, presumably crucial for superconductivity yet absent in the case of electrolyte gating. Reproducible bulk (3D) superconductivity has been observed in Na-doped WO3 but only at very low temperatures, with the maximum Tc = 0.57 K.26 However, we did not see this low-temperature superconductivity either.
A clear metal-insulator transition is seen in the electrical transport data taken on each of our samples. The insulating (dρ/dT < 0) and metallic (dρ/dT > 0) regimes are separated by the critical sheet resistance RC ≈ 200 Ω/□. Within the purely electronic charging scenario, the electrolyte gating should only affect the sample surface, and hence one would expect a 2D metal-insulator transition, for which R C should be close to the universal resistance quantum RQ = h/e2 = 25.8 kΩ/□.34 However, the critical sheet resistance we observe here is two orders of magnitude smaller, suggesting that the whole film might have been affected.
We fabricated and studied a step-like film, as illustrated in the inset of Fig. 3, in order to determine the depth over which a WO3 sample can be affected by electrolyte gating. We have charged the whole film with PEG-NaF to the saturating point, then measured the conductance of each section simultaneously. In Fig. 3, we can see that the saturated sheet conductance GS increases almost linearly with the film thickness, d. Therefore, the conductivity σ = GS/d is essentially constant for sections of different thicknesses, which suggests that the whole sample has been affected by the electrolyte gating, even for the thickest (70 nm) section. All other measurements performed on films with uniform thicknesses (Fig. 2) are in qualitative agreement with the results in Fig. 3. Given that the Thomas-Fermi screening length in a metal is very short (<1 nm), the electric field cannot penetrate through a 70 nm thick metallic film, and hence this finding rules out a purely electrostatic effect. Some chemical process that affects the entire film must be involved.
To check whether oxygen electromigration is playing a role in our experiments, we performed a series of charging/discharging experiments in vacuum (10−6 Torr overall, oxygen partial pressure less than 10−7 Torr) and in air (oxygen partial pressure close to 155 Torr). We cycled the gate voltage with time, occasionally switching the environment between vacuum and air. The charging temperature was fixed at T = 305 K and the sample resistance was measured at that temperature during charging/discharging processes. The results are shown in Fig. 4. The top panel shows the changes in the gate voltage, and the bottom panel shows the concomitant changes in the resistance. One can see that both the charging and discharging processes are reversible and reproducible. However, there is no apparent difference between the charging-discharging cycles performed in vacuum and in air, in contrast to what was observed in VO211 and SrRuO316 experiments, as well as one report with WO3.21 This implies that oxygen electromigration is not relevant when discussing the resistivity changes observed in our electrolyte gating experiments on WO3.
The WO3 structure can be viewed as an ABO3 perovskite where tungsten occupies the B site but the A site remains empty. Thus, it is relatively easy to intercalate small atoms (hydrogen or alkali metals) to occupy the A site as was demonstrated in much of the early work on WO3.35 Since we are using PEG-NaF as electrolyte, intercalation of Na+ is conceivable. To check this possibility, we have tried gating with pure polyethylene glycol (adding no salts whatsoever) on WO3; the outcome turned out to be the same (see Supplementary Fig. S3), ruling out sodium intercalation. This leaves us with the possibility that the primary effect of electrolyte gating is hydrogen (H+) intercalation, as it is well known that hydrogen intercalation, i.e. protonation, can make WO3 metallic.35 While we made every best effort to dehydrate our electrolytes under vacuum before applying them to our samples and to minimize the time between removing the electrolyte from vacuum, applying it to our samples, and beginning the transport measurements, we believe that the source of hydrogen ions is the self-ionization of water that the electrolytes absorbed in the short time that they were exposed to air. Indeed, several studies have used hygroscopic solids as a proton source to controllably modify the conductivity of WO3 in a transistor geometry36,37,38 so this means of conductivity enhancement in WO3 that is covered with a hygroscopic electrolyte cannot be overlooked. We note that controlled protonation can be used to tune the conductivity of other oxides as well, as has recently been demonstrated in VO2,39, 40 and In2O3/ZnO.41
We performed a comparison of operando XRD patterns measured during electrolyte charging/discharging processes with XRD data taken after vacuum, ozone and hydrogen annealing procedures, shown in Fig. 5, to directly compare to samples where hydrogen was added in the more traditional way and also to confirm that oxygen vacancies are not at play here. The operando XRD curves measured during the charging and discharging processes (Fig. 5a) show negligible shift (~ 0.01°) of WO3 Bragg peaks; the change of the lattice constant is smaller than 0.05%. This differs with previous XRD data taken while electrolyte gating WO3 that showed the lattice constants changing by at least 2%.21, 22 However, we point out that there is really no agreement on this particular point as the c-axis lattice constants have been observed to both decrease21 and increase22 while charging in the range of gate voltages used here (up to + 3 V). Several differences between our work and that of refs 21 and 22 exist that could account for this disparity in the XRD data. Different combinations of substrates and growth temperatures were used in each of these three studies, which affects the resulting film structure, quality, and epitaxial strain. Also, different electrolytes and measurement environments were used which could contribute to the differences in the XRD results. Regardless, we clearly find that the WO3 unit cell in our work stays essentially the same during the charging process, even though the sample has been driven to the metallic state (Supplementary Fig. S4). If there were any cations intercalated/doped into the film during this process, they must be small enough to maintain the original WO3 lattice constants.
In contrast, annealing in vacuum at 550 °C shifts the WO3 Bragg peak to a lower angle by 0.16°, corresponding to a 0.7% change in the lattice constant (the top panel of Fig. 5b), which means that the film structure has changed significantly. Vacuum annealing at a lower temperature (T ≤ 520 °C) did not change the XRD pattern at all. Moreover, the sample modified by high-temperature annealing in vacuum can be brought back towards the original state by annealing in ozone at 450 °C for just 1 h (the bottom panel of Fig. 5b). Both the Bragg peak and the thickness fringes are moving back towards the XRD curve measured for the as-grown film. This points to changes in oxygen stoichiometry, and shows that we can clearly detect them if they are present, and that they do not occur in our films except at high temperatures.
In Fig. 5c, we present XRD curves measured for a sample annealed in hydrogen. We have tuned the annealing temperature from 300 to 520 °C, and yet the WO3 Bragg peak did not shift at all, although the fringes smear out after annealing at the highest temperature, indicating some surface degradation. The XRD patterns in Fig. 5a (charging) and 5c (H2 annealing) are similar to each other while the ones in Fig. 5b (vacuum annealing) are very different. This indicates that hydrogen has been involved in the charging process, comparable to the hydrogen annealing process. Furthermore, we have also measured the transport properties of the WO3 film after the hydrogen annealing procedures as illustrated in Fig. 2 by empty squares (“□”, H2 annealed at 300 °C) and empty circles (“○”, H2 annealed at 520 °C). When the resistivity reaches a certain level, the R(T) curves of the electrolyte-gated and hydrogen-annealed samples show almost the same slope, which suggests the changes in the sample induced by the electrolyte gating are the same as those induced by the hydrogen annealing.
We performed one additional transport experiment in which we covered a portion of a WO3 film patterned into a Hall bar with an electrolyte and looked for possible changes in the resistivity nearby in areas of the bar that were not covered by the electrolyte. If a change were to be seen, this would clearly point to electromigration; given the small probe voltage and the relatively large distances involved, the longitudinal (in-plane) electric field is negligible compared to the minimum needed for an observable electronic field effect. Since this portion of the sample stays essentially charge neutral, any increase in the mobile electron density must be exactly compensated by intercalation of positive ions. In Supplementary Fig. S5, we show that in a region of the Hall bar that is 300 µm away from the electrolyte the resistance drops by 70%. This experiment clearly demonstrates that doping takes place by cation intercalation. Note that this effect is seen only if the applied gate voltage is positive, i.e., if the electromigrating ions are positively charged. We know that they must also be very small based on our x-ray experiments, which uniquely points to hydrogen.
To evaluate how many hydrogen atoms are intercalated into the WO3 films, we need to measure the carrier density of the charged and saturated sample. For ordinary semiconductors, the standard method is to measure the Hall effect and infer n from the Hall number, RH = 1/ne, where e is the electron charge. However, the Hall effect measurement of our WO3 films gives too high a value if we assume one type of carrier, n = 2.8 electron per one WO3 formula unit (see Supplementary Fig. S6), which is questionable on physical grounds. (Similarly large carrier densities were also determined from Hall effects measurements in ref. 22). One possible explanation for the low Hall number from which the high carrier density was derived is that more than one type of charge carrier is present. Another is that this may point to polaron formation, since it is known that electron-phonon coupling is very strong in many transition metal oxides, including WO3 specifically42, and that for polaronic materials the above simple Hall formula is not applicable.
We modified a Fourier transform infrared (FTIR) spectrometer to allow operando measurements during the charging/discharging processes to test the polaronic scenario. Typical absorption spectra obtained from a charging process are shown in Fig. 6a. During the charging process a strong IR band appears around 0.45 eV (see Supplementary for fitting details). In these experiments DEME-TFSI was used as the electrolyte and the cut-off observed at 0.2 eV is due to a glass cover slip that we used to hold the ionic liquid in place. We have also used Teflon foil instead of the glass and we can see a similar peak around 0.45 eV (Supplementary Fig. S7). This type of feature has been interpreted as a telltale signature of polaron formation in a large number of oxide materials and their energy was assigned to the polaron binding energy.43, 44 Hence, our IR data support the idea that hydrogenation leads to the formation of a polaronic gas. Furthermore, while similar mid-IR peaks were observed in both absorption44 and photo-induced measurements45 in WO3-δ samples, the peak energy in Fig. 6 is in better agreement with the latter experiments. A natural explanation is that in hydrogenated films the absorption would correspond to a Frank-Condon transition from a (reduced) W5+ ion (like in photo-doping) rather than a transition of an electron trapped at a vacancy site in oxygen deficient samples.
As the gate voltage is applied, the spectral weight of the IR polaronic band increases monotonically with time and finally saturates. The 3D carrier concentration at saturation extracted from the plasma frequency associated with the IR band (Fig. 6b) renders a value n ~ 4.4 × 1021 cm−3, which corresponds to approximately 0.2 carriers per WO3 primitive unit cell. It is conceivable that we have reached the maximum for this mechanism; if only the nearest neighbor W-O lattice distortions were involved, the absolute upper bound for non-overlapping small polarons would be 0.5. Within our scenario, if an even higher doping could be achieved, it could trigger a collapse of small polarons and a transition into a state of matter not explored before.
Although the sample has been charged to the metallic state, the nominal Hall mobility is quite low, μH = RH/ρ ≈ 1 cm2/Vs. Such a low mobility is typical of small polarons, and in fact it has been reported42 that polarons of small or intermediate size form in some structural phases of WO3. Since hydrogen intercalation induced by the electrolyte gating process is slow, reversible, and reproducible for all of the properties we have measured so far, including transport (Fig. 4), XRD (Fig. 5) and IR absorption (Supplementary Fig. S8), electrolyte-gated WO3 may prove to be a convenient platform to study polaron physics, including the elusive polaronic metal state.
While we believe that we have presented a strong case that hydrogen is involved in the electrolyte gating of WO3 films, the mechanism of electrolyte gating might well be different in other materials. A case in point is VO2 or SrRuO3, as previously mentioned. Both are very sensitive to oxygen; annealing in vacuum or oxygen significantly changes their oxygen stoichiometry, crystal structure, and carrier densities. Electric field induced electromigration of oxygen will therefore clearly play a role in electrolyte gated VO2 or SrRuO3 devices and may also be relevant when gating other oxygen sensitive materials such as SrTiO3, InO x , or YBaCuO7−x . In contrast, WO3 seems to be relatively stable against the formation of oxygen vacancies as we find that annealing in vacuum at 520 °C for 2 h does not change the oxygen stoichiometry at all. Still, because of its vacant center (A) site, WO3 is very susceptible to intercalation of hydrogen and small alkali cations, which must be considered when gating this material. The larger narrative of this and much of the recent electrolyte gating work seems to be that no one mechanism—purely electrostatic, oxygen vacancies, lattice deformations, intercalations, etc.—is universal in all situations. Even thin film samples of the exact same material can be affected by electrolyte gating in different ways depending on how it was prepared (e.g., epitaxial or polycrystalline films, based on lattice match of substrates) as has been demonstrated in SmNiO312, 13 and VO2.46 All of these possibilities must evidently be considered and carefully investigated before making any broad conclusions about the mechanisms at work in any electrolyte gated materials.
Thin film synthesis
Atomically flat WO3 films have been synthesized by r.f. magnetron sputtering. The growth temperature was 750–850 °C and the pressure during growth was about 60 mTorr with an O2/Ar ratio of 4:1. The thickness was determined using X-ray reflectivity data, and the growth rate was about 1 nm/min. The substrates we used were YAlO3 single crystals with the surfaces polished perpendicular to the crystallographic  direction. YAlO3 has an orthorhombic structure with lattice constants a0 = 5.176 Å, b0 = 5.307 Å, and c0 = 7.355 Å. Along the  direction of YAlO3, the lattice mismatch between YAlO3 and the γ-monoclinic WO3 is + 0.7% (7.355 Å vs. 7.306 Å) along the a-axis and –1.7% (7.413 Å vs. 7.540 Å) along the b-axis. The small lattice mismatch enabled us to synthesize high quality WO3/YAlO3 films with atomically flat surfaces, as confirmed by the XRD and atomic force microscope results.
The WO3 films were patterned into a set of Hall bar devices of various aspect ratios with gold contacts. We used photolithography for larger features and electron-beam lithography for features smaller than 1 µm. The gate, a piece of thin platinum mesh, was situated above the Hall bars for the transport measurements (Supplementary Fig. S1a) with both ionic liquid DEME-TFSI and polymer PEG-NaF used as electrolytes. Note that resistance was measured using delta method averaging to eliminate the effects of offset currents, such as gate leakage.
For operando XRD and FTIR measurements we used side-gated devices (Supplementary Fig. S1b). Gold contacts were sputtered at the four corners of the sample in a van der Pauw configuration. These four probes were connected and grounded at the beginning of the electrolyte gating to make sure they were at the same equipotential surface. After the sample was charged to a low-resistivity state these four contacts were used to measure the changes in resistivity during further charging. We used polymer electrolyte PEG-NaF for XRD measurements, and the ionic liquid DEME-TFSI for FTIR measurements. A glass coverslip or Teflon foil was used to hold the ionic liquid during the FTIR measurements.
The data that support the findings of this study are available from the corresponding author upon reasonable request.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
The experimental work reported here was performed at BNL and supported by U.S. Department of Energy, Basic Energy Sciences, Materials Sciences and Engineering Division. This research used resources of the Center for Functional Nanomaterials, which is a U.S. DOE Office of Science Facility, at Brookhaven National Laboratory under Contract No. DE-SC0012704. X.L. was supported by the Center for Emergent Superconductivity, an Energy Frontier Research Center funded by the U.S. DOE, Office of Basic Energy Sciences. G.D. and D.P. were supported by the Swiss National Science Foundation. J.P. and C.P. acknowledge financial support from the National Research Foundation, Singapore through Grant NRF-CRP4-2008-04. A.G. is supported by the Gordon and Betty Moore Foundation’s EPiQS Initiative through Grant GBMF4410.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.