Abstract
Graphene is known as a two-dimensional Dirac semimetal, in which electron states are described by the Dirac equation of relativistic quantum mechanics. Three-dimensional analogs of graphene are characterized by Dirac points or lines in momentum space, which are protected by symmetry. Here, we report a novel 3D carbon allotrope belonging to a class of topological nodal line semimetals, discovered using an evolutionary structure search method. The new carbon phase in the monoclinic C2/m space group, termed m-C8, consists of five-membered rings with sp3 bonding interconnected by sp2-bonded carbon networks. Enthalpy calculations reveal that m-C8 is more favorable than recently reported topological semimetallic carbon allotropes, and the dynamic stability of m-C8 is verified by phonon spectra and molecular dynamics simulations. Simulated X-ray diffraction patterns indicate that m-C8 could be one of the unidentified carbon phases observed in detonation shoot. The analysis of electronic properties indicates that m-C8 exhibits a nodal line protected by both inversion and time-reversal symmetries in the absence of spin-orbit coupling and the surface band connecting the projected nodal points. Our results may help design new carbon allotropes with exotic electronic properties.
Similar content being viewed by others
Introduction
Carbon, which is one of the most abundant elements in nature, has a rich variety of structural allotropes due to its capacity to form sp, sp2 and sp3 hybridized bonds. Graphene, a single layer of carbon in a honeycomb lattice, consists of all-sp2 bonds and exhibits a semimetallic band structure with Dirac points. Recently, topological materials, including topological insulators (TIs) and topological semimetals (TSMs), have received a great deal of attention because of the intriguing physical phenomena underlying their behavior, as well as their potential applications. The prediction of the TI phase in graphene with spin-orbit coupling (SOC)1 has stimulated a tremendous amount of theoretical and experimental work to explore new topological materials. The TI state has been demonstrated for two-dimensional (2D) HgTe/CdTe quantum wells2 and three-dimensional (3D) Bi-based chalcogenides.3 The band structure of a TI is characterized by the existence of a bulk band gap, as well as gapless boundary states that are protected by the nontrivial topology of bulk electronic states. By contrast, in TSMs, the valence and conduction bands cross each other at discrete points (Dirac and Weyl semimetals) or along curves (nodal line semimetals) in momentum space. In Dirac semimetals, which have been realized with Na3Bi (ref. 4) and Cd3As2,5 the band crossing points at the Fermi energy have four-fold degeneracy. By breaking either inversion or time-reversal symmetry in Dirac semimetals, one can obtain Weyl semimetals in which each Dirac point splits into a pair of doubly degenerate Weyl points with opposite chirality. Weyl semimetals have been proposed for compounds containing heavy elements, such as pyrochlore iridates,6 HgCr2Se4,7 and transition metal dichalcogenides,8 and the prediction of the Weyl semimetal state in the TaAs family9 has been verified experimentally.10
In nodal line semimetals, the formation of Dirac nodes along a closed loop or line requires inversion and time-reversal symmetries without SOC in Cu3(Pd, Zn)N (ref. 11), Ca3P2,12 and alkaline-earth metals (Ca, Sr, Yb)13 and compounds AX2 (A=Ca, Sr, Ba; X=Si, Ge, Sn).14 When SOC is included, additional non-symmorphic symmetry is necessary to protect the nodal line against gap opening in ZrSiS.15 In non-centrosymmetric PbTaSe2, the nodal line is protected by mirror reflection symmetry even in the presence of SOC.16 Meanwhile, the TSM phase has also been reported for 3D carbon networks constructed from graphene, such as Mackay-Terrenes crystals,17 interpenetrated graphene networks (IGNs)18 and bco-C16.19 Due to the negligible SOC,20 the nodal lines of these semimetallic carbon allotropes are protected by a combination of inversion and time-reversal symmetry. Recent experiments have demonstrated the synthesis of 3D graphene networks with high-electrical conductivities by a chemical vapor deposition technique, although the associated crystal structure has not yet been identified.21 Other 3D metallic carbon allotropes have been proposed, including H18 carbon22 and T6 carbon23 in mixed sp2-sp3 bonding networks, and ThSi2-type tetragonal bct4 carbon24 and H6 carbon25 with all-sp2 bonding. However, the band overlap occurs at different crystal momenta in H18 and T6 carbon,22, 23 whereas the metallic nature of bct4 and H6 carbon arises from the twisted π states that make these allotropes dynamically unstable.26
In this work, we report a new 3D carbon allotrope belonging to a class of topological nodal line semimetals, based on global optimization and first-principles density functional calculations. The new carbon phase, termed m-C8, consists of five-membered rings with sp3 hybridized bonds and sp2-bonded carbon networks, and the enthalpy of m-C8 is lower than those of recently proposed carbon allotropes with topological nodal lines. The dynamic stability of m-C8 is verified by phonon spectra and molecular dynamics simulations. On the basis of the analysis of X-ray diffraction patterns and enthalpy-pressure curves, we propose that m-C8 may be present in detonation soot27 and a phase transition from graphite to m-C8 can occur under pressure.
Methods
Computational structure search and electronic structure calculations
We explored new carbon allotropes with sp2-sp3 hybridized bonds by using a computational search method,28 in which the conformational space annealing (CSA) algorithm29 for global optimization is combined with first-principles electronic structure calculations. The efficiency of this approach has been demonstrated by successful applications to predict Si and C allotropes with direct band gaps.30, 31 For various carbon systems with N atoms per unit cell (N=8, 12, 16, 20), we optimized the degrees of freedom, such as atomic positions and lattice parameters, with the number of configurations set to 40 in the population size of the CSA.
The goal of computational materials design is to obtain the optimal crystal structure with specific target properties, which can be expressed in terms of an objective function.28 In this work, the objective function is composed of two parts: enthalpy and penalty. For all configurations, a local minimization was performed for the enthalpy within the framework of density functional theory. Our work aimed to find low-energy 3D carbon allotropes with exotic electronic properties. Thus, the penalty function was designed to prevent carbon structures from forming all-sp2 or all-sp3 hybridized bonds, such as diamond and graphite, and to promote mixed sp2-sp3 bonding networks. In each configuration, sp2- and sp3-hybridized atoms were determined by using the bond lengths of 1.42 and 1.54 Å. If configurations only consisted of sp2- or sp3-hybridized atoms, the penalty function, defined as eV, was included in the objective function, so that configurations with high-objective function values were excluded. For the first-principles calculations we used the functional form proposed by Armiento and Mattsson (AM05) (ref. 32) for the exchange-correlation potential and the projector augmented wave potentials,33 as implemented in the VASP code.34 In graphite, interlayer interactions are described more accurately with the AM05 functional compared to other functional forms of the exchange-correlation potential (Supplementary Table S1). The wave functions were expanded in plane waves up to an energy cutoff of 600 eV. At the final stage of optimization, we used an even higher energy cutoff of 800 eV.
Results and Discussion
Structure and stability of a new carbon allotrope
Among many low-energy allotropes (Supplementary Table S2), we obtained a very distinctive crystal structure in the C2/m space group (Figure 1a), especially for the N=8 system. For the N=16 system, the same low-energy allotrope was also found by the computational search method, although both the number of atoms per unit cell and the cell volume are doubled. The monoclinic C2/m structure, denoted as m-C8, has the equilibrium lattice parameters, a=7.010 Å, b=2.480 Å, c=6.608 Å and β=71.2°, and four inequivalent Wyckoff positions, 4i (0.272, 0, 0.446), (0.632, 0, 0.79), (0.781, 0, −0.072) and (0.007, 0, 0.878), occupied by the C1, C2, C3 and C4 atoms, respectively. The m-C8 allotrope is characterized by five-membered carbon rings interconnected by graphitic carbon networks, similar to penta-graphene ribbons linked with hexa-graphene ribbons.37 The graphitic networks are composed of sp2-bonded C1 atoms, with the bond length of =1.412 Å, whereas the C2, C3, and C4 atoms forming five-membered rings are all sp3-bonded, with the bond lengths of =1.553 Å, =1.527 Å, =1.540 Å, =1.514 Å and =1.570 Å. Note that the bond length between the C1 and C2 atoms, which connect graphitic sheets to five-membered rings, is =1.493 Å, between those of graphite (1.420 Å) and diamond (1.544 Å).
In Table 1, the calculated equilibrium volume, lattice parameters, bond lengths and total energy of m-C8 are compared to those of diamond, graphite and several recently reported metallic allotropes: T6 carbon25 and IGN,20 in mixed sp2-sp3 bonding networks, and oC8 carbon38 and bco-C16,19 in all-sp2 bonding networks. The equilibrium volume of m-C8 is 6.80 Å3 per atom, between those of graphite and diamond. Because of the mixture of sp2 and sp3 hybridized bonds, the m-C8 allotrope has four different bond angles of 93.7, 107.3, 114.1 and 121.3°, which deviate from the ideal bond angles of graphite (120°) and diamond (109.5°). Owing to the induced strain, the m-C8 structure has an excess energy of 0.22 eV/atom compared to the diamond phase. By contrast, m-C8 is more stable by 0.13 0.29 eV/atom than T6 carbon, oC8 carbon and bco-C16. It is interesting to note that although the total energy of m-C8 at the equilibrium volume is higher by 0.05 eV/atom than that of IGN, its enthalpy is lower for pressures above 10 GPa (Figures 2a and b). From the enthalpy vs pressure curve, a possible synthesis of m-C8 is expected under compression of graphite. It has been suggested that graphite may transform to oC8 carbon, which is a denser form of bco-C16, above 65 GPa.19, 38 However, our calculations indicate that m-C8 is lower in enthalpy than bco-C16 up to 77 GPa, and a transition from graphite to m-C8 is more likely to occur at the lower pressure of 60 GPa.
We examined the stability of m-C8 by calculating the full phonon spectra and found no imaginary phonon modes over the entire Brillouin zone (BZ) (Figure 1b), indicating that m-C8 is dynamically stable. In addition, we carried out first-principles molecular dynamics (MD) simulations at a temperature of 1500 K. For a 2 × 4 × 2 supercell containing 128 atoms, we confirmed that the m-C8 allotrope is stable for up to 100 ps (Figure 1c). Owing to the thermal stability, the synthesis of m-C8 is expected under high-pressure and high-temperature. We also calculated the elastic constants of m-C8, and confirmed that the elastic constants meet the criteria for mechanical stability in monoclinic structure.39
The X-ray diffraction patterns of m-C8 were simulated and compared to the experimental data from detonation soot (sample Alaska B),27 along with those of graphite, diamond, T6 carbon, bco-C16 and IGN, as shown in Figure 3. In the detonation soot, the prominent peaks ~26.5° and 43.9° are attributed to the graphite (002) and diamond (111) diffractions, respectively. The (101) peak of T6 carbon, (101) peak of bco-C16, and (001) peak of IGN match with the experimental X-ray diffraction data located at 37.4°, 30.0° and 21.4°, respectively. However, the low-angle peak at 13.4° does not match any previously reported carbon phases. This peak was also observed in different detonation soot,27 indicating that an unknown carbon phase should be produced. Our simulated X-ray diffraction results show that the main (001) peak of m-C8 reasonably explains the unidentified peak at 13.4°. Moreover, the (111), (002) and (112) peaks of m-C8 match those in the experimental X-ray diffraction pattern located at 25.1°, 27.8° and 32.1°, respectively, indicating the presence of m-C8 in the specimen produced by detonation experiments.27
Band structure of a new carbon allotrope
Finally, we examined the band topology of m-C8. In Figure 4a, the band structure exhibits linear dispersions around the Fermi level where the valence and conduction bands touch, similar to graphene. The linear bands are mainly derived from the sp2 hybridized C atoms in graphitic sheets, as illustrated in the distribution of charge densities (Figure 4b), whereas more dispersive bands far from the Fermi level are associated with the sp3 hybridized bonds in five-membered rings. From the band structure in the full BZ, we find that the crossing points of the valence and conduction bands form a continuous nodal line piercing the extended BZ, without interfering with sp3-hybridized bands (Figures 4 and 5). Thus, the m-C8 allotrope with symmorphic symmetry belongs to a class of topological nodal line semimetals.11, 12, 13, 14, 15, 16, 17, 18, 19 Recently, two types of topological nodal line semimetals were proposed, depending on systems with and without SOC.39 In the former, because the SOC may open up gaps at the band crossing points, both inversion and time-reversal symmetries are insufficient to protect the band crossings, whereas additional non-symmorphic symmetry can protect the nodal line.40 In carbon systems such as m-C8, with a negligible SOC, the topological nodal line survives by a combination of inversion and time-reversal symmetries.
Based on the analysis of parity eigenvalues, Fu and Kane proposed the Z2 topological invariants to describe the topological nature of TIs.41 Similarly, the parities of energy states can be used to assign the Z2 topological invariants in topological nodal line semimetals. For the eight time-reversal invariant momenta (Figure 5a), the products of the parity eigenvalues (δ) for the occupied bands are listed in Table 2. We found that m-C8 is characterized by the weak Z2 indices (0;111) due to the value of δ=−1 at the Y and Z points. As m-C8 has no mirror reflection symmetry, the bulk nodal line does not appear in a mirror-invariant plane. To visualize the formation of topological surface states, we calculated the surface band structure for a slab geometry composed of 20 graphitic layers, where the (110) surface is exposed to vacuum. As the bulk BZ is projected onto the (110) surface BZ, one can expect that the nodal line is located near the and points (Figure 5a). In fact, the projected band structure clearly shows the formation of the nearly flat surface state connecting the projected nodal points around the point (Figure 5b).
In summary, we have predicted a novel carbon allotrope m-C8 with mixed sp2-sp3 bonding networks using the evolutionary structure search method. The monoclinic structure of m-C8 is composed of five-membered rings connected by graphitic sheets. The stability of m-C8 is verified by calculating the full phonon spectra and MD simulations at a temperature of 1500 K. From the analysis of the electronic band structure, we have identified that m-C8 belongs to the class of topological nodal line semimetals, exhibiting the topological nodal line in bulk and the topological surface states at surface boundaries. As the SOC is extremely weak in m-C8, the nodal line is protected by the coexistence of inversion and time-reversal symmetries. Although it remains a challenge to synthesize the crystalline form of m-C8, our results provide not only a perspective for the novel electronic structure of carbon allotropes but also promote future studies to explore new carbon allotropes with exotic electronic and transport properties.
References
Kane, C. L. & Mele, E. J. Quantum spin Hall effect in graphene. Phys. Rev. Lett. 95, 226801 (2005).
König, M., Wiedmann, S., Brüne, C., Roth, A., Buhmann, H., Molenkamp, W., Qi, X.-L. & Zhang, S.-C. Quantum spin hall insulator state in HgTe quantum wells. Science 318, 766–770 (2007).
Xia, Y., Qian, D., Hsieh, D., Wray, L., Pal, A., Lin, H., Bansil, A., Grauer, D., Hor, Y. S., Cava, R. J. & Hasan, M. Z. Observation of a large-gap topological-insulator class with a single Dirac cone on the surface. Nat. Phys. 5, 398–402 (2009).
Liu, Z. K., Zhou, B., Zhang, Y., Wang, Z. J., Weng, H. M., Prabhakaran, D., Mo, S.-K., Shen, Z. X., Fang, Z., Dai, X., Hussain, Z. & Chen, Y. L. Discovery of a three-dimensional topological Dirac semimetal, Na3Bi. Science 343, 864–867 (2014).
Neupane, M., Xu, S.-Y., Sankar, R., Alidoust, N., Bian, G., Liu, C., Belopolski, I., Chang, T.-R., Jeng, H.-T., Lin, H., Bandsil, A., Chou, F. & Hasan, M. Z. Observation of a three-dimensional topological Dirac semimetal phase in high-mobility Cd3As2 . Nat. Commun. 5, 3786 (2014).
Wan, X., Turner, A. M., Vishwanath, A. & Savrasov, S. Y. Topological semimetal and Fermi-arc surface states in the electronic structure of pyrochlore iridates. Phys. Rev. B 83, 205101 (2011).
Xu, G., Weng, H., Wang, Z., Dai, X. & Fang, Z. Chern semimetal and the quantized anomalous Hall effect in HgCr2Se4 . Phys. Rev. Lett. 107, 186806 (2011).
Soluyanov, A. A., Gresch, D., Wang, Z., Wu, Q., Troyer, M., Dai, X. & Bernevig, B. A. Type-II Weyl semimetals. Nature 527, 495–498 (2015).
Weng, H., Fang, C., Fang, Z., Bernevig, B. A. & Dai, X. Weyl semimetal phase in noncentrosymmetric transition-metal monophosphides. Phys. Rev. X 5, 011029 (2015).
Lv, B. Q., Weng, H. M., Fu, B. B., Wang, X. P., Miao, H., Ma, J., Richard, P., Huang, X. C., Zhao, L. X., Chen, G. F., Fang, Z., Dai, X., Qian, T. & Ding, H. Experimental discovery of weyl semimetal TaAs. Phys. Rev. X 5, 031013 (2015).
Kim, Y., Wieder, B. J., Kane, C. L. & Rappe, A. M. Dirac line nodes in inversion-symmetric crystals. Phys. Rev. Lett. 115, 036806 (2015).
Xie, L. S., Schoop, L. M., Seibel, E. M., Gibson, Q. D., Xie, W. & Cava, R. J. A new form of Ca3P2 with a ring of Dirac nodes. APL Mater. 3, 083602 (2015).
Hirayama, M., Okugawa, R., Miyake, T. & Murakami, S. Topological Dirac nodal lines in fcc Calcium, Strontium, and Ytterbium. Preprint at https://arxiv.org/abs/1602.06501 (2016).
Huang, H., Liu, J., Vanderbilt, D. & Duan, W. Topological nodal-line semimetals in alkaline-earth stannides, germanides, and silicides. Phys. Rev. B 93, 201114 (2016).
Neupane, M., Belopolski, I., Hosen, M. M., Sanchez, D. S., Sankar, R., Szlawska, M., Xu, S.-Y., Dimitri, K., Dhalkal, N., Maldonado, P., Oppeneer, P. M., Kaczorowski, D., Chou, F., Hasan, M. Z. & Durakiewicz, T. Observation of topological nodal fermion semimetal phase in ZrSiS. Phys. Rev. B 93, 201104 (2016).
Bian, G., Chang, T.-R., Sankar, R., Xu, S.-Y., Zheng, H., Neupert, T., Chiu, C.-K., Huang, S.-M., Chang, G., Belopolski, I., Sanchez, D.S., Neupane, M., Alidoust, N., Liu, C., Wang, B., Lee, C.-C., Jeng, H.-T., Zhang, C., Yuan, Z., Jia, S., Bansil, A., Chou, F., Lin, H. & Hasan, M.Z. Topological nodal-line fermions in spin-orbit metal PbTaSe2 . Nat. Commun. 7, 10556 (2016).
Weng, H., Liang, Y., Xu, Q., Yu, R., Fang, Z., Dai, X. & Kawazoe, Y. Topological node-line semimetal in three-dimensional graphene networks. Phys. Rev. B 92, 045108 (2015).
Chen, Y., Xie, Y., Yang, S. A., Pan, H., Zhang, F., Cohen, M. L. & Zhang, S. Nanostructured carbon allotropes with Weyl-like loops and points. Nano Lett. 15, 6974–6978 (2015).
Wang, J.-T., Weng, H., Nie, S., Fang, Z., Kawazoe, Y. & Chen, C. Body-centered orthorhombic C16: A novel topological node-line semimetal. Phys. Rev. Lett. 116, 195501 (2016).
Yao, Y., Ye, F., Qi, X.-L., Zhang, S.-C. & Fang, Z. Spin-orbit gap of graphene: first-principles calculations. Phys. Rev. B 75, 041401 (2007).
Chen, Z., Ren, W., Gao, L., Liu, B., Pei, S. & Cheng, H.-M. Three-dimensional flexible and conductive interconnected graphene networks grown by chemical vapour deposition. Nat. Mater. 10, 424–428 (2011).
Zhao, C.-X., Niu, C.-Y., Qin, Z.-J., Ren, X. Y., Wang, J.-T., Cho, J.-H. & Jia, Y. H18 Carbon: a new metallic phase with sp2-sp3 hybridized bonding network. Sci. Rep. 6, 21879 (2016).
Zhang, S., Wang, Q., Chen, X. & Jena, P. Stable three-dimensional metallic carbon with interlocking hexagons. Proc. Natl. Acad. Sci. USA 110, 18809–18813 (2013).
Hoffmann, R., Hughbanks, T., Kertész, M. & Bird, P. H. A hypothetical metallic allotrope of carbon. J. Am. Chem. Soc. 105, 4831–4832 (1983).
Liu, A. Y., Cohen, M. L., Hass, K. C. & Tamor, M. A. Structural properties of a three- dimensional all-sp2 phase of carbon. Phys. Rev. B 43, 6742 (1991).
Wang, J.-T., Chen, C. & Kawazoe, Y. New carbon allotropes with helical chains of complementary chirality connected by Ethene-type π-conjugation. Sci. Rep 3, 3077 (2013).
Pantea, D., Brochu, S., Thiboutot, S., Ampleman, G. & Scholz, G. A morphological investigation of soot produced by the detonation of munitions. Chemosphere 65, 821–831 (2006).
Lee, I.-H., Oh, Y. J., Kim, S., Lee, J. & Chang, K. J. Ab initio materials design using conformational space annealing and its application to searching for direct band gap silicon crystals. Comp. Phys. Commun. 203, 110–121 (2016).
Lee, J., Lee, I.-H. & Lee, J. Unbiased global optimization of Lennard-Jones clusters for N ≤ 201 using the conformational space annealing method. Phys. Rev. Lett. 91, 080201 (2003).
Lee, I.-H., Lee, J., Oh, Y. J., Kim, S. & Chang, K. J. Computational search for direct band gap silicon crystals. Phys. Rev. B 90, 115209 (2014).
Oh, Y. J., Lee, I.-H., Kim, S., Lee, J. & Chang, K. J. Direct band gap carbon superlattices with efficient optical transition. Phys. Rev. B 93, 085201 (2016).
Armiento, R. & Mattsson, A. E. Functional designed to include surface effects in self-consistent density functional theory. Phys. Rev. B 72, 085108 (2005).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953 (1994).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169 (1996).
Occelli, F., Loubeyre, P. & Letoullec, R. Properties of diamond under hydrostatic pressures up to 140 GPa. Nat. Mater. 2, 151–154 (2003).
Hanfland, M., Beister, H. & Syassen, K. Graphite under pressure: Equation of state and first-order Raman modes. Phys. Rev. B 39, 12598 (1989).
Zhang, S., Zhou, J., Wang, Q., Chen, X., Kawazoe, Y. & Jena, P. Penta-graphene: A new carbon allotrope. Proc. Natl. Acad. Sci. USA 112, 2372–2377 (2015).
Wang, J.-T., Chen, C. & Kawazoe, Y. Phase conversion from graphite toward a simple monoclinic sp3-carbon allotrope. J. Chem. Phys. 137, 024502 (2012).
Wu, Z.-J., Zhao, E.-J., Xiang, H.-P., Hao, X.-F., Liu, X.-J. & Meng, J. Crystal structures and elastic properties of superhard IrN2 and IrN3 from first principles. Phys. Rev. B 76, 054115 (2007).
Fang, C., Chen, Y., Kee, H.-Y. & Fu, L. Topological nodal line semimetals with and without spin-orbital coupling. Phys. Rev. B 92, 081201 (2015).
Fu, L. & Kane, C. L. Topological insulators with inversion symmetry. Phys. Rev. B 76, 045302 (2007).
Acknowledgements
This work was supported by Samsung Science and Technology Foundation under Grant No. SSTF-BA1401-08.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Competing interests
The authors declare no conflict of interest.
Additional information
Supplementary Information accompanies the paper on the NPG Asia Materials website
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Sung, HJ., Kim, S., Lee, IH. et al. Semimetallic carbon allotrope with a topological nodal line in mixed sp2-sp3 bonding networks. NPG Asia Mater 9, e361 (2017). https://doi.org/10.1038/am.2017.26
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/am.2017.26
This article is cited by
-
Orthorhombic C36: a sp2–sp3 carbon with pressure-induced metallization and superconductivity
Journal of Materials Science (2021)