Abstract
Non-emissive triplet excited states in devices that undergo thermally activated delayed fluorescence (TADF) can be up-converted to singlet excited states via reverse intersystem crossing (RISC), which leads to an enhanced electroluminescence efficiency. Exciton-based fluorescence devices always exhibit a positive magneto-electroluminescence (MEL) because intersystem crossing (ISC) can be suppressed effectively by an external magnetic field. Conversely, TADF devices should exhibit a negative MEL because RISC is suppressed by the external magnetic field. Intriguingly, we observed a positive MEL in TADF devices. Moreover, the sign of the MEL was either positive or negative, and depended on experimental conditions, including doping concentration, current density and temperature. The MEL observed from our TADF devices demonstrated that ISC in the host material and RISC in the guest material coexisted. These competing processes were affected by the experimental conditions, which led to the sign change of the MEL. This work gives important insight into the energy transfer processes and the evolution of excited states in TADF devices.
Similar content being viewed by others
Introduction
Recently, significant research efforts have been focused on organic light-emitting diodes (OLEDs) that undergo thermally activated delayed fluorescence (TADF)1,2,3,4,5,6,7,8,9,10. TADF-based OLEDs can generate fluorescence with an internal quantum efficiency (IQE) of 100% without the need for rare metal complexes, which are commonly used in phosphorescent OLEDs11,12,13. The high IQE of TADF-based devices is the result of reverse intersystem crossing (RISC)14,15. RISC can cause the up-conversion of triplet excited states to produce singlet excited states, which can then undergo delayed fluorescence leading to a theoretical increase in the IQE from 25% to 100%4,5,6,7,8,9,10. For RISC to occur efficiently, a small energy gap between the singlet and triplet energy levels (ΔEST) is required. Intramolecular charge transfer states (CTs) within molecules that contain spatially separated donor and acceptor moieties have a small exchange interaction because of the large interaction distance16,17,18. Thus, a small ΔEST can occur in molecules that contain CTs.
To avoid concentration quenching, the TADF material is usually incorporated into a device as a guest15,16,17,18,19. In energy-transfer dominated host-guest systems the host molecule generally serves as a recombination center where holes and electrons combine to form excited states before transferring their energy to the guest20. To the best of our knowledge, there are few reports that give a detailed understanding of the energy transfer process and evolution of excited states in TADF-based OLEDs. The magneto-electroluminescence (MEL) of an OLED is an effective tool to investigate the spin-dependent processes that occur within organic semiconducting materials and devices21,22,23,24. MEL is defined as: MEL = ΔEL/EL = [EL(B) − EL(0)]/EL(0), where EL(B) and EL(0) are the measured electroluminescence (EL) intensities with and without an applied external magnetic field (B), respectively. A small applied B can alter the population balance between singlet and triplet excited states in OLEDs and consequently change the total light intensity. Generally, the MEL in exciton-based OLEDs is positive with a full width at half maximum (FWHM) of several mT because the intersystem crossing (ISC) of polaron pairs is suppressed by the B23. Conversely, a negative MEL is observed in TADF-based OLEDs because any RISC from CTs is suppressed by the B, which has been described in the literature25,26,27.
In this paper, we report an unexpected positive MEL in a TADF-based device that contained CBP as host and 4CzTPN-Ph as guest. This device configuration was recently reported by Adachi et al.15 Moreover, the sign of the MEL became negative depending on experimental conditions, including doping concentration, current density and temperature. The MEL was positive when the concentration of 4CzTPN-Ph was lower than 5 wt% and became negative when the doping concentration was greater than 50 wt%. These observations were inconsistent with the argument that RISC is dominant in TADF devices. When the concentration of 4CzTPN-Ph was 50 wt%, the MEL tended to be negative under small injection currents (<100 μA), and positive at larger injection currents (~200 μA). Furthermore, the MEL tended to be negative at ambient temperature but positive at low temperature (20 K). These complicated behaviors were dictated by the energy transfer processes and evolution of the excited states between the host and guest materials.
Results and Discussion
Molecular structure and luminance properties
To ensure that a TADF material containing intra-molecular CT states has a sufficiently small ΔEST, they are generally composed of donor and acceptor moieties4,5,6,7,8,9,10. The center of 4CzTPN-Ph contains a dicyanobenzene unit, which acts as an electron acceptor. The peripheral biphenyl carbazolyl units act as electron donors. The molecular geometry of 4CzTPN-Ph was optimized and the molecular orbitals were calculated using density functional theory (DFT) based on B3LYP27, as shown in Fig. 1(a). The highest occupied molecular orbital (HOMO) of 4CzTPN-Ph was localized on the carbazolyl moieties (donor), and its lowest unoccupied molecular orbital (LUMO) was centered on the dicyanobenzene moiety (acceptor). Consequently, the holes and electrons of the excited states are well separated in this molecule, which should lead to a small ΔEST and a large RISC rate constant8,19.
The structure and energy levels of the TADF-based device are shown in Fig. 1(b). PEDOT:PPS, NPB, CBP, 4CzTPN-Ph, and TPBi were used as hole injection layer, hole transport layer, host material, guest material, and electron transport layer, respectively. An exciton-based device (ITO/PEDOT:PSS/NPB/Alq3/LiF/Al) was fabricated for comparison. Normalized EL spectra of TADF devices with different doping concentrations, and normalized photoluminescence (PL) spectra of the organic materials at ambient temperature are shown in Fig. 1(c). CBP, TPBi and NPB all exhibited luminescence maxima between 350 and 420 nm. The EL emission maxima of the TADF-based device was located at 588 nm, which is close to the PL emission maxima of 4CzTPN-Ph (577 nm)15. Thus, the fluorescence of the host material (CBP) in the TADF-based device was completely quenched, which suggested that energy transfer between the guest and host molecules was efficient. As the concentration of the guest material (4CzTPN-Ph) was increased, the EL emission maxima exhibited a slight red shift, which was caused by the decrease in the polarity of 4CzTPN-Ph, as reported by Suh et al.28 The luminance of the TADF devices increased with increasing current density, as shown in Fig. 1(d). However, the luminance efficiency (LE) and external quantum efficiency (EQE) decreased with increasing doping concentration because of concentration quenching29,30 (inset, Fig. 1(d)). When the concentration of 4CzTPN-Ph was 5 wt%, the highest LE and EQE were 18.5 cd/A and 7.9%, respectively. This EQE was significantly higher than that of the exciton-based Alq3 device (EQE~2%). When the concentration of 4CzTPN-Ph was increased to 75 wt% the LE and EQE dropped to 0.8 cd/A and 0.5%, respectively. This indicated that concentration quenching within devices that are dense with TADF materials is significant.
MEL response and mechanism of energy transfer within TADF devices
The MEL of exciton-based devices typically increases rapidly at low B strength and then slowly at high B strength, as shown in Fig. 2(a). When a device is subjected to a biased voltage the injected electrons and holes form polaron-pair (PP) states before excitons23. The ΔEST between singlet PP (1PP) and triplet PP (3PP) levels is comparable to the energy of the hyperfine interactions, which leads to ISC (1PP → 3PP) or RISC (3PP → 1PP)31,32,33. When an external B is applied, Zeeman splitting of the 3PP states suppress the ISC and leads to a positive MEL. As the B is increased further, the MEL saturates because of saturated suppression.
The spatial separation between the LUMO and HOMO levels in TADF molecules is much larger than that of the molecules used in exciton-based devices. This separation leads to significantly smaller ΔEST values between the singlet CT states (1CT) and triplet CT states (3CT), which in turn promotes RISC (3CT → 1CT). Therefore, the IQE is enhanced significantly, which leads to EL efficiencies that are several times higher in TADF devices than in exciton-based devices4,5,6,7,8,9,10. Therefore, if the external B suppresses RISC, this should result in a negative MEL25,26,27. However, a positive MEL was observed in our TADF device, as shown in Fig. 2(b).
Generally, the guest molecules in host-guest TADF devices are excited by energy transfer from the host molecules through Förster resonance energy transfer (FRET) and Dexter energy transfer (DET). FRET occurs at low doping concentrations between singlet excited states because it operates via an electrostatic dipole-dipole coupling. In contrast, DET normally occurs at higher doping concentrations between triplet excited states because it generally requires an electron exchange process34,35,36,37.
In our TADF device, the energy from the singlet exciton (S1) in CBP was transferred to the 1CT in 4CzTPN-Ph via FRET. The 3CT in 4CzTPN-Ph was excited by the triplet exciton (T1) in CBP through DET, and subsequently converted to the 1CT through RISC. The suppression of ISC between PPs (1PP → 3PP) in CBP by an external B should result in a positive MEL. However, the external B also suppressed RISC between CTs (3CT → 1CT), which led to a negative MEL. As ISC between PPs in the host material and RISC between CTs in the TADF material compete with each other, if the doping concentration of a TADF device is low, FRET will dominate. Therefore, if energy transfer from S1 to 1CT is dominant, a positive MEL will result. A schematic diagram showing the processes discussed above are presented in Fig. 2(c).
The experimental MEL curve (hollow black symbols) and its fitted line (red solid lines) at a current intensity of 200 μA within a B of ±500 mT are shown in Fig. 2(d) (the characteristic MEL of ISC and RISC are also shown). The MEL curves fitted perfectly to a Lorentzian function25,26, which can be expressed as:
where the characteristic saturation field (B0) for ISC is ~10 mT. This value was consistent with the reported B0 for ISC25,26,27. At a current density of 5 mA/cm2, the MEL of the ISC process in exciton-based devices is generally ~6%, while the MEL in TADF devices is only ~1.5%. Therefore, RISC in our devices containing only 5 wt% TADF materials contributes ~−4.5% to the MEL.
The MEL curves from the TADF device (Fig. 2(b)) exhibited a similar line shape to those of the exciton-based device (Fig. 2(a)). However, the magnitude of the MEL from the TADF device increased with increasing injection current, while that of the exciton-based device showed the opposite trend. The EL of the exciton-based device increased faster than the ΔEL as the current was increased, which caused a decrease in the MEL (MEL = ΔEL/EL). Conversely, the ΔEL increased faster than the EL with increasing injection current in the TADF device. The mechanism for this opposing effect may be related to the influence of a high electric field on the lifetime of 3CT states25.
The lifetime of photo-generated excitons in most organic semiconductors has been estimated to be approximately 10−7~10−9 s23,24. Therefore, the lifetime of an exciton is greater than that of the spin flipping process (~10−9 s)38. The probability of exciton dissociation increases at higher electric fields, which leads to a dramatic decrease in the lifetime of an exciton. The dissociation of loosely bound CT states is more favorable because of their weak Coulomb attraction39,40. Therefore, 3CT states with shortened lifetimes cannot undergo RISC (3CT → 1CT) efficiently when a high voltage bias is applied. This then leads to MEL with larger magnitudes.
MEL response of devices with different 4CzTPN-Ph concentrations
The concentration of the 4CzTPN-Ph in the TADF devices was altered to investigate our hypothesis. The concentration of guest molecule should affect the competition between the FRET and DET processes. A device that contained 25 wt% 4CzTPN-Ph exhibited a similar MEL line shape to that of a device containing 5 wt% (Fig. 3(a)), except that the magnitude of the MEL in the former device was approximately 0.7% smaller than that of the latter. This difference indicated that both DET and RISC (3CT → 1CT) were enhanced with increasing guest concentration. When the concentration of 4CzTPN-Ph was raised to 50 wt%, the sign of the MEL was either positive or negative, depending on the current intensity (Fig. 3(b)). In this case, the FRET and DET processes were comparable and competed with each other. RISC (3CT → 1CT) is dominant under low current conditions, and leads to a negative MEL line shape. As the current was increased, the strength of the electric field was enhanced and the 3CT lifetime was shortened, which diminished the RISC (3CT → 1CT) process.
When the concentration of 4CzTPN-Ph was greater than 75 wt%, DET was prominent, which caused the population of 3CT states to be larger than 1CT states. Under these conditions, RISC (3CT → 1CT) was dominant and caused the negative MEL line shape (Fig. 3(c) and (d)). However, when large currents were used, the lifetime of the 3CT state was lowered. Thus, RISC (3CT → 1CT) was weakened and the magnitude of the MEL decreased as the current was increased.
MEL response of devices at different temperatures
RISC in TADF devices is an endothermic process that can be suppressed effectively at low temperatures15,27. Hence, if the negative MEL was caused by RISC (3CT → 1CT), it should become weaker at lower temperatures. Therefore, the MEL of the TADF device that contained 5 wt% 4CzTPN-Ph was measured at 20 K, as shown in Fig. 4(a). At low temperatures, the MEL was positive. Moreover, the exciton-based Alq3 device clearly exhibited triplet-triplet annihilation (TTA)41,42 (inset, Fig. 4(a)), while the TADF devices only exhibit weak TTA at low temperatures and high currents because TTA does not occur efficiently from CT states43. The effects of temperature on the MEL at a fixed current of 50 μA is shown in Fig. 4(b). The magnitude of the MEL increased from 1% to 3% with decreasing temperature, while that of the exciton-based device dropped from 6% to 2%. This indicated that RISC (3CT → 1CT) was suppressed at low temperature. When the doping concentration was increased to 25 wt% (Fig. 4(c)), the line shape of the MEL was characteristic of ISC without the presence of TTA, which was caused by the increased number of CT states. Moreover, the magnitude of the MEL was much larger at lower temperatures (Fig. 4(d)). This was consistent with a significant suppression of RISC from the CTs at lower temperature.
The MEL of a TADF device that contained 50 wt% 4CzTPN-Ph when measured at different currents at 20 K is shown in Fig. 5(a). The MEL of this device was also positive. At a current of 200 μA, the magnitude of the MEL increased from 0.6% to 4.5% as the temperature was decreased from 300 K to 20 K (Fig. 5(b)). This increase in magnitude was caused by a decrease in RISC from the CTs at low temperature, which is equivalent to an enhancement of the ISC process. Intriguingly, the sign of the MEL was affected by temperature. At a current of 50 μA, the MEL was negative at 300 K and positive at 20 K (Fig. 5(c)). This behavior was also observed in the devices that contained 75 wt% (Fig. 5(d)) and 100 wt% 4CzTPN-Ph, indicating that the negative MEL at ambient temperature was caused by RISC (3CT → 1CT).
MEL response with different luminance efficiencies relating to temperature and concentration
The saturated MEL of the TADF devices within the hyperfine interaction range (<40 mT) are shown in Fig. 6(a). The hyperfine saturation value of the MEL increased with decreasing temperature, which was caused by a decrease in RISC from 3CT to 1CT at lower temperatures. Additionally, the magnitude of the MEL at 20 K was observed to increase as the doping concentration was increased from 25 wt% to 75 wt%, which indicated that the strength of RISC was proportional to the doping concentration. RISC is an endothermic process that can be suppressed at low temperatures. Thus, the highest EL efficiencies for the TADF devices decreased with decreasing temperature (Fig. 6(b)). Although RISC should improve the efficiency of a TADF device, concentration quenching can cause an overall lowering of device efficiency when TADF materials are present at high concentrations. This effect was observed in our devices, which indicated that concentration quenching was indeed dominant.
Time-resolved spectroscopy can be used to investigate the delayed fluorescence of TADF devices15,24. However, both RISC and TTA can generate delayed fluorescence and are difficult to distinguish using time-resolved spectroscopy. Fortunately, the MEL characteristics of RISC and TTA are clearly different and can be used to determine which process produced the delayed fluorescence. The MEL of RISC decreases monotonically (<40 mT) and quickly saturates as the B increases, while that of TTA increases slightly (<5 mT) and then drops with increasing B strength25. Additionally, ISC causes a MEL curve that is opposite to that of RISC. The MEL of our TADF devices showed characteristics of ISC and RISC but not TTA at ambient temperature. Thus, MEL allowed us to conclude that the delayed fluorescence from our TADF devices originated from RISC.
Conclusion
In summary, the energy transfer processes and evolution of the excited states in TADF devices were investigated using MEL. This was done using OLEDs that had an energy transfer-dominated host-guest active layer. The host material acted as a recombination center for holes and electrons to generate excited states, followed by energy transfer to the guest. At low doping concentration, FRET was the dominant energy transfer mechanism. The TADF devices exhibited a positive MEL because ISC was dominant in the host material. However, the energy transfer of triplet excited states from the host to the guest was limited, which led to a low utilization of triplet excitons from the host material. Moreover, RISC was suppressed significantly at high current densities, which led to a decrease in the utilization of triplet CTs in the guest. At high doping concentrations, DET was dominant. The TADF devices exhibited a negative MEL because RISC was dominant in the guest. Although RISC should improve the efficiency of a device, the high concentrations of the TADF material can cause a decrease in efficiency because of concentration quenching. The results of this study indicated that the use of TADF materials as guests in devices may not result in improved efficiencies. However, if a TADF material was used as a host, both singlet and triplet excited states in the host material may be harvested efficiently via RISC and then subsequent FRET from the host to the guest. This hypothesis will be investigated in depth using MEL as a tool in future work.
Methods
The TADF devices were fabricated with the following structure: ITO (120 nm)/poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) (40 nm)/N,N′-bis(1-naphthalenyl)-N,N′-bisphenyl-(1,1′-biphenyl)-4,4′-diamine (NPB) (30 nm)/x wt% 2,3,5,6-tetrakis(3,6-diphenylcarbazol-9-yl)-1,4-dicyanobenzene (4CzTPN-Ph) (x = 5, 25, 50, 75, 100): 4,4′-bis(carbazol-9-yl)biphenyl (CBP) (40 nm)/1,3,5-tris(1-phenyl-1H- benzimidazol-2-yl) benzene (TPBi) (50 nm)/LiF (1 nm)/Al (120 nm). The structure of the exciton-based OLED device that was used for comparison had the following structure: ITO (120 nm)/PEDOT:PSS (40 nm)/NPB (40 nm)/Alq3 (60 nm)/LiF (1 nm)/Al (120 nm). The PEDOT:PSS layer was spin-coated onto the ITO patterned glass substrate and then annealed for 10 min at 120 °C in a vacuum chamber. The layers consisting of small molecules were grown using an organic molecular beam deposition method under a base pressure of ~10−6 Pa. All devices were prepared with active area of 2 mm × 2 mm.
During measurement, the samples were mounted on the cold finger of a closed-cycle cryostat (Janis CCS-350S) that was located between two poles of an electromagnet (Lakeshore EM647). A Keithley 2400 SourceMeter was used to provide a constant voltage and measure the current. The brightness was determined using a magnetic insensitive silicon photodetector and recorded using a Keithley 2000 apparatus. The photoluminescence (PL) was measured with SpectraPro-2300i spectrometer with a laser excitation wavelength of 325 nm.
Additional Information
How to cite this article: Deng, J. et al. Guest concentration, bias current, and temperature-dependent sign inversion of magneto-electroluminescence in thermally activated delayed fluorescence devices. Sci. Rep. 7, 44396; doi: 10.1038/srep44396 (2017).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Reineke, S. et al. White organic light-emitting diodes: Status and perspective. Rev Mod Phys. 85, 1245–1293 (2013).
Obolda, A. et al. Triplet–Polaron‐Interaction‐Induced Upconversion from Triplet to Singlet: a Possible Way to Obtain Highly Efficient OLEDs. Adv. Mater. 28, 4740–4746 (2016).
Liu, X. K. et al. High performance, simplified fluorescence and phosphorescence hybrid white organic light-emitting devices allowing complete triplet harvesting. ACS Appl. Mater. Interfaces 8, 26135–26142 (2016).
Sun, J. W. et al. A fluorescent organic light-emitting diode with 30% external quantum efficiency. Adv. Mater. 26, 5684–5688 (2014).
Kim, B. S. & Lee, J. Y. Engineering of mixed host for high external quantum efficiency above 25% in green thermally activated delayed fluorescence device. Adv. Funct. Mater. 24, 3970–3977 (2014).
Im, Y. & Lee, J. Y. Above 20% external quantum efficiency in thermally activated delayed fluorescence device using furodipyridine-type host materials. Chem. Mater. 26, 1413–1419 (2014).
Zhang, Q. et al. Efficient blue organic light-emitting diodes employing thermally activated delayed fluorescence. Nat. Photon. 8, 326–332 (2014).
Ye, T. et al. Thermally activated delayed fluorescence materials towards the breakthrough of organoelectronics. Adv. Mater. 26, 7931–7958 (2014).
Gaj, M. P. et al. Highly efficient organic light-emitting diodes from thermally activated delayed fluorescence using a sulfone–carbazole host material. Org. Electron. 16, 109–112 (2014).
Li, J. et al. Highly efficient organic light-emitting diode based on a hidden thermally activated delayed fluorescence channel in a heptazine derivative. Adv. Mater. 25, 3319–3323 (2013).
Baldo, M. A. et al. Highly efficient phosphorescent emission from organic electroluminescent devices. Nature 395, 151–154 (1998).
Kalinowski, J. et al. Magnetic field effects on organic electrophosphorescence. Phys. Rev. B 70, 205303 (2004).
Endo, A. et al. Thermally activated delayed fluorescence from Sn4+-porphyrin complexes and their application to organic light emitting diodes-a novel mechanism for electroluminescence. Adv. Mater. 21, 4802–4806 (2009).
Goushi, K., Adachi, C., Kou, Y. & Sato, K. Organic light-emitting diodes employing efficient reverse intersystem crossing for triplet-to-singlet state conversion. Nat. Photon. 6, 253–258 (2012).
Uoyama, H. et al. Highly efficient organic light-emitting diodes from delayed fluorescence. Nature 492, 234–238 (2012).
Wu, S. et al. High-efficiency deep-blue organic light-emitting diodes based on a thermally activated delayed fluorescence emitter. J. Mater. Chem. C 2, 421–424 (2013).
Youn Lee, S. et al. High-efficiency organic light-emitting diodes utilizing thermally activated delayed fluorescence from triazine-based donor–acceptor hybrid molecules. Appl. Phys. Lett. 5, 093306 (2012).
Wang, H. et al. Novel thermally activated delayed fluorescence materials-thioxanthone derivatives and their applications for highly efficient oleds. Adv. Mater. 26, 5198–204 (2014).
Sato, K. et al. Organic luminescent molecule with energetically equivalent singlet and triplet excited states for organic light-emitting diodes. Phys. Rev. Lett. 110, 247401 (2013).
Nakanotani, H. et al. High-efficiency organic light-emitting diodes with fluorescent emitters. Nat. Commun. 5, 4016 (2014).
Chen, Q. et al. Determining the Origin of Half-bandgap-voltage Electroluminescence in Bifunctional Rubrene/C60 Devices. Sci. Rep. 6, 25331 (2016).
Bai, J. W. et al. Studying singlet fission and triplet fusion by magneto-electroluminescence method in singlet–triplet energy-resonant organic light-emitting diodes. Org. Electron. 15, 169–174 (2014).
Hu, B., Yan, L. & Shao, M. Magnetic-field effects in organic semiconducting materials and devices. Adv. Mater. 21, 1500–1516 (2009).
Hontz, E. et al. The role of electron-hole separation in thermally activated delayed fluorescence in donor-acceptor blends. J. Phys. Chem. C 119, 25591–25597 (2015).
Chen, P. et al. Magneto-electroluminescence as a tool to discern the origin of delayed fluorescence: reverse intersystem crossing or triplet–triplet annihilation? Adv. Optical. Mater. 2, 142–148 (2014).
Peng, Q. et al. Studying the influence of triplet deactivation on the singlet-triplet inter-conversion in intra-molecular charge-transfer fluorescence-based OLEDs by magneto-electroluminescence. J. Mater. Chem. C 2, 6264–6268 (2014).
Chen, P. et al. Delayed fluorescence in a solution-processable pure red molecular organic emitter based on dithienylbenzothiadiazole: a joint optical, electroluminescence, and magnetoelectroluminescence study. ACS Appl. Mater. Interfaces 7, 2972–2978 (2015).
Cho, Y. R. et al. Ideal combination of the host and dopant materials showing thermally activated delayed fluorescent behavior. Synthetic Metals 209, 47–54 (2015).
Parka, Y. H. et al. Concentration quenching effect of organic light-emitting devices using DCM1-doped tetraphenylgermole J. Phys. Org. Chem. 25, 207–210 (2012).
Zhang, Y. Q., Zhong, G. Y. & Cao, X. A. Concentration quenching of electroluminescence in neat Ir(ppy)3 organic light-emitting diodes J. Appl. Phys. 108, 083107 (2010).
Kohler, A. & Beljonne, D. The singlet-triplet exchange energy in conjugated polymers. Adv. Funct. Mater. 14, 11–18 (2004).
Karabunarliev, S. & Bittner, E. R. Spin-dependent electron-hole capture kinetics in luminescent conjugated polymers. Phys. Rev. Lett. 90, 057402 (2003).
Crooker, S. A. et al. Spectrally resolved hyperfine interactions between polaron and nuclear spins in organic light emitting diodes: Magneto-electroluminescence studies. Appl. Phys. Lett. 105, 153304 (2014).
Zhang, Y. & Forrest, S. R. Triplet Diffusion Leads to Triplet−Triplet Annihilation in Organic Phosphorescent Emitters. Chem. Phys. Lett. 590, 106–110 (2013).
Eersel, H. V., Bobbert, P. A. & Coehoorn, R. Kinetic Monte Carlo Study of Triplet-Triplet Annihilation in Organic Phosphorescent Emitters. J. Appl. Phys. 117, 5048 (2015).
Kawamura, Y. et al. Intermolecular interaction and a concentration-quenching mechanism of phosphorescent Ir(Ш) complexes in a solid film. Phys. Rev. Lett. 96, 017404 (2006).
Oevering, H. et al. Long-Range Exchange Contribution to Singlet-Singlet Energy Transfer in a Series of Rigid Bichromophoric Molecules. Chem. Phys. Lett. 143, 488–495 (1988).
Sheng, Y. et al. Hyperfine interaction and magnetoresistance in organic semiconductors. Phys. Rev. B 74, 045213 (2006).
Hu, B. & Wu, Y. Tuning magnetoresistance between positive and negative values in organic semiconductors. Nat. Mater. 6, 985–991 (2007).
Kalinowski, J. et al. Magnetic field effects on emission and current in alq3-based electroluminescent diodes. Chem. Phys. Lett. 380, 710–715 (2003).
Staroske, W., Pfeiffer, M., Leo, K. & Hoffmann, M. Single-step triplet-triplet annihilation: An intrinsic limit for the high brightness efficiency of phosphorescent organic light emitting diodes. Phys. Rev. Lett. 98, 197402 (2007).
Lei, Y. L. et al. Large contribution of triplet excitons to electro-fluorescence in small molecular organic light-emitting diodes. Org. Electron. 12, 1512–1517 (2011).
Xiang, J. et al. Realization of triplet-triplet annihilation in planar heterojunction exciplex-based organic light-emitting diodes. Org. Electron. 28, 94–99 (2016).
Acknowledgements
This work was financially supported by the National Natural Science Foundation (NSF) of China (Grant No. 11374242) and the Research and Innovation Project of Graduate Students of Chongqing (CYS16049) and Fundamental Research Funds for the Central Universities (XDJK2015C149).
Author information
Authors and Affiliations
Contributions
Z.X. conceived the experiments. J.D., D.L. and Y.H. conducted the experiments. J.D., W.J. and Y.C. analyzed the results. J.D. wrote the main manuscript text. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Deng, J., Jia, W., Chen, Y. et al. Guest concentration, bias current, and temperature-dependent sign inversion of magneto-electroluminescence in thermally activated delayed fluorescence devices. Sci Rep 7, 44396 (2017). https://doi.org/10.1038/srep44396
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep44396
This article is cited by
-
Understanding degradation of organic light-emitting diodes from magnetic field effects
Communications Materials (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.