Sb2O3/Ag/Sb2O3 Multilayer Transparent Conducting Films For Ultraviolet Organic Light-emitting Diode


A novel UV transparent conducting films based on Sb2O3/Ag/Sb2O3 (SAS) structure, which were prepared by an electron-beam thermal evaporation at room temperature. This SAS exhibits excellent electrical, optical and stable properties. Especially for UV region, the SAS has high transmittance of 80% at 306 nm and 92% at 335 nm, meanwhile achieving low sheet resistance ( ≤ 10 Ω sq−1). The UV OLED based on the SAS show competitive device performance. The UV OLED obtains the peak of UV electroluminescence at 376 nm and shows a very high maximum EQE of 4.1% with the maximum output power density of 5.18 mW cm−2. These results indicate that the potential of SAS applications in deep UV transparent electrodes and large-scale flexible transparent electronics.


Transparent conducting films (TCFs) have been widely used in optoelectronics fields including flat panel displays (FPD)1, organic light-emitting diodes (OLEDs)2, thin film solar cells3, and photodetectors4. Currently commercial TCFs are transparent conducting oxides (TCOs) including indium tin oxides (ITOs) and fluorine-doped tin oxides (FTOs) films. Recently, several emerging materials such as conducting polymers5, carbon nanotubes6, graphene7, and metallic nanowires have shown favorable electrical conductivity and transparency as those of ITO8, which plays important role in devices. However, all the above conducting materials are only transparent in the visible region.

With the development of ultraviolet (UV) optoelectronic devices such as UV photodetectors9, UV electrically pumped laser and UV LEDs10, there are an enhanced need for the UV TCFs. While, UV transparency means a wide energy gap (Eg) for the TCOs. Most intrinsic wide band gap materials are close to insulation, showing poor conductivity. It is theoretically feasible to obtain UV TCFs by the introduction of shallow donor level in wide band gap materials through doping. However, up to now, few UV TCFs were reported. By doping β-Ga2O3 (Eg = 4.9 eV) with Sn, Masahiro Orita et al.11,12 obtained a transmittance of 50% at deep UV 248 nm with a conductivity of 1 S cm−1 and electron concentration of 1.43 × 1019 cm−3, these parameters are significantly lower compared to the TCFs in the visible region.

According to previous studies13, a dielectric-metal-dielectric (DMD) structure can be optimized through tuning the thickness of dielectric and metal layers to achieve high transparency in the visible region as well as high conductivity3,14. Nowadays, the DMD electrodes have been applied to organic light-emitting diodes15 and organic PV cells16, and the properties of these devices are comparable to those devices based on ITO electrodes. Generally, DMD TCFs have advantageous of excellent conductivity properties than most single layer TCFs and an easy tunable transparent area by adjusting the thickness of the dielectric film. By employing a wider bandgap material, it is possible to achieve UV TCFs with high transparency and conductivity. Antimony trioxide (Sb2O3) is a UV transparent semiconductor material with a wide Eg of 3.6 eV17, which has higher electrical conductivity than that of other UV transparent semiconductors18,19. Therefore, we introduce Sb2O3 into DMD structure in this work, and develop a deep UV Sb2O3/Ag/Sb2O3 (SAS) TCFs under room temperature, and successfully make it with high adjustable transmittance from UV to visible region, with low resistivity at an order of 10−5. A UV OLEDs has been obtained based on SAS anode, which shows superior performance with EL Peak at 376 nm in the UV region.


Figure 1a shows 250–2500 nm transmission spectrum of a series of SAS, they have high transmission from the UV to visible region, and low transmission in infrared region (IR), respectively. However, those regions are not fixed, they vary with the SAS each layer thicknesses. Through optical designing13,15, the SAS films can realize high transmission in different regions (Figure S1). We developed SAS with the structure of 51 nm/18 nm/32 nm, and achieved high transmittance in deep UV region (Fig. 1b). In TCO, deep UV transparent is quite dependent on wide Eg, which contradicts with good electron properties. In this SAS films, due to the middle high conductive Ag layer is parallel to the Sb2O3 layers, the Hall carrier concentration is 7.722 × 1021 cm−3, the mobility is 21.92 cm2V−1s−1, the resistivity is 3.688 × 10−5Ω cm, the sheet resistance is 8 Ω sq−1, and the work function is −5.22 eV. The plasma resonance frequency is proportional to the carrier concentrations. The SAS carrier concentration is about one order bigger than TCO carrier concentration, thus it has a lower transmission (higher reflection) in IR region (Fig. 1a). It prevents absorbing thermal irradiation, which is good for many optoelectronic devices. Figure 1c shows the change in measured sheet resistance and average transmittance (λ = 300–380 nm) of SAS electrodes as a function of Ag thickness. The SAS sheet resistance decreases dramatically, from 40 Ω/sq to 3.5 Ω/sq, with increasing Ag thickness. This result indicates that the Ag thickness determines the electrical properties of the SAS electrodes. SAS electrodes with Ag layer thickness of less than 8 nm show higher sheet resistance because of the discontinuous Ag island growth20,21. With the thickness of Ag layer increased to 18 nm, the average transmittance (λ = 300–380 nm) of SAS decreases gradually, which can result from the high reflectance of Ag layer.

Figure 1: The optical and electrical properties of SAS.

(a) The transmittance spectra of a series of SAS. (b) The deep UV transmittance spectra of SAS. (c) Average transmittance (300–380 nm) and sheet resistance of the SAS electrodes as a function of the Ag thickness. The structure of the electrodes is 35 nm/x (Ag thickness) nm/40 nm.

Surface morphology and roughness are also very important for transparent electrodes, when they are applied in optoelectronics devices. As shown in Fig. 2, the root-mean-square roughness of the SAS structure deposited on glass is only 0.97 nm, which is much lower than that of sputter-derived commercial ITO (2.51 nm) and might contribute to the carrier injection and transportation performance21. The high quality surface morphologies can result from the process of electron-beam evaporator deposition, which affects the film deposition, oxidation, and crystallization simultaneously22.

Figure 2: The characterization of surface morphology of SAS.

AFM micrographs of SAS (ITO) sample.

TCFs that can sustain high temperature are rare. In TCFs of DMD structure with Ag as the central metal layer, thermal stability is a research difficulty. They tend to have problems with thermal and time stability, because Ag is easy to have chemical reaction with ambient air, generates Ag2S. We studied the electrical property of SAS under different annealing temperatures. We prepared two SAS samples, with the structures a: 55 nm/14 nm/45 nm; b: 53 nm/14.5 nm/46 nm, and studied their resistivity, mobility, work function and film figure of merit against annealing temperatures under 100, 200, 300, and 400 °C (Fig. 3).

Figure 3: The properties of SAS under different annealing temperatures.

(a) Resistivity, (b) mobility, (c) work function and (d) merit factor of the SAS films before and after annealing at different temperatures for 30 min in air. The structure of SAS sample a: 55 nm/14 nm/45 nm; sample b: 53 nm/14.5 nm/46 nm.

From the Fig. 3a and b we can see that, both the resistivity and the carrier mobility of two samples shown the optimal performance under 300 °C annealing temperature, they got worse when the temperature increased to 400 °C. Also, we noticed that under 100 °C, almost all the electrical properties are the worst. Ag film structure has a change between 100 ~ 200 °C according to literature23. In the heat treatment conditions, the size of the particles etc. factors that affect the electrical performances are changing and 100 °C might just be the worst situation. From the Fig. 3c, we can see that the work function of two samples increase with annealing temperature after 100 °C. From Bardeen’s theory24, we know that the interaction strength of a double layer of atomic dimension at the semiconductor surface acts a comparable role to that space charge, which can determine the work function. Due to oxygen vacancy conductivity, Sb2O3 is a metal oxide semiconductor. Under thermal treatment, Sb2O3 reacts with the ambient air, the charge dipole layer of the surface has been changed, which may cause the altering of work functions. Work function is a critical factor for many microelectronics, a proper work function can reduce the contact barrier significantly, thus improve the device performance effectively. However, compare to the abundant semiconductor materials, the current available different work function TCFs are few. The changeable work function of SAS will match many more materials’ energy level, which will be helpful in many devices.

Generally we use figure of merit ФTC to evaluate whether a TCF is good or not, the bigger, the better. According to Haacke function25:

where T denotes the TCF film transmittance, Rs represents the film sheet resistance. Similarly, two SAS samples achieved the best performance under 300 °C annealing temperature (Fig. 3d).

Both SAS sample still have good performance under high temperature 400 °C, SAS is the first DMD TCF that can endure such a high temperature. Sb2O3 has very good thermal stability, the dense Sb2O3 film can protect Ag layer against oxidant with ambient air, and therefore SAS can sustain high temperature. We suggest that the DMD TCFs’ thermal stability is mainly dependent on the dielectric layer, hence adopting proper materials, we can obtain high thermal stability TCFs.

Time stability is another key factor for the applications of DMD TCFs. We compared three different SAS samples (a, b and c) of their electrical properties after 12 months and 10 days, 12 months and one week, and 10 months, respectively. They all had very good stability, the rate of change are all below 6% (Fig. 4). All the samples were stored in the atmosphere.

Figure 4: Time stability of SAS.

Time stability of sample a, b and c. Sample a: 12 months and 10days, Sample b: 12 months and one week and Sample c: 10 months.

The SAS as UV transparent anode was used in OLED. The effective area is etched as 1 mm × 1 mm. The device structure is Glass/SAS/WO3/TcTa/CBP/PBD/TPBI/LiF/Al. The J-V characters were recorded by Keithley 2611 SourceMeter, as shown in Fig. 5a. The device exhibits attractive UV emission with the Peak at 376 nm (Fig. 5b). Owing to the high work function that matches the energy level better, and the lower sheet resistance, the turn on and operation voltage are relative lower compare to the reported results26. The output power and EL spectra were measured by PM310E (thorlabs), Avantes fiber spectrometer. The maximum external quantum efficiency (EQE) of 4.1% has been demonstrated with the maximum output power density of 5.18 mW cm−2 (in Fig. 5c), which is one of the best results among the research of UV OLED to our knowledge.

Figure 5: Characteristics of the UV OLED based on SAS.

(a) Current density–voltage characteristics of OLED. (b) EL spectrum of OLEDs at 60 mA cm−2. (c) EQE and output power density changing with the injection current density.

In conclusion, we have developed SAS TCFs under room temperature. SAS have extraordinary performance that can have high transparency from deep UV to visible region, meanwhile obtaining low sheet resistance. By varying layer thicknesses, the high transparent regions are changeable, and the SAS work functions are adjustable under annealing. It is the first UV TCF that has such properties that SAS can sustain 400 °C temperature and longtime stability. The SAS was used in UV OLED, which achieved UV electroluminescence at 376 nm and exhibited a very high maximum EQE of 4.1% with the maximum output power density of 5.18 mW cm−2. The outstanding optical and electrical properties of the SAS films enable numerous applications including deep UV transparent electrodes and large-scale flexible transparent electronics.


Sb2O3/Ag/Sb2O3 Multilayer Films Fabrication and Characterization

The thin layers of Sb2O3/Ag/ Sb2O3 multilayer films were deposited on glass and polymer substrate using an electron-beam evaporator under room temperature. For both Sb2O3 layers, the oxygen gas was introduced upstream at 15 ~ 16.9 SCCM to insure that the vacuum pressure was among 1.9 ~ 2.2 × 10−2 Pa. The evaporation rate of Sb2O3 material was about 0.06 ~ 0.1 nm s−1, and the optimal one is 0.08 nm s−1. The Ag material was evaporated below 1.0 × 10−3 Pa with a rate of 1 nm s−1. Optical transmittance spectra of SAS were evaluated with a Shimadzu UV-3101PC spectrophotometer. Carrier concentrations, resistivities and Hall carrier mobility were carried out by Hall Effect measurements with the maximum magnetic filed applied of 0.55 T. Film thicknesses were measured with an Ambios XP-1 surface profiler. The surface resistance was measured using the four-point probe method with a surface resistivity meter. The work functions of samples were investigated by a KP Technology Ambient Kelvin probe system package.

UV OLED Fabrication and Characterization

A glass substrate coated with thin layers of Sb2O3/Ag/Sb2O3 multilayer films, which technological parameters have optimized. The SAS film was cleaned with acetone, methanol, distilled water, and isopropyl alcohol sequentially. The device structure is Glass/SAS/WO3 (1 nm)/TcTa (20 nm)/CBP (30 nm)/PBD (20 nm)/TPBI (35 nm)/LiF (1 nm)/Al (100 nm). All organic layers were sequentially deposited on to the substrate without breaking the vacuum at a pressure of 5 × 10−4 Pa. using thermal evaporation equipment. The deposition rates were controlled from 2.0 to 3.0 Å s−1 for organic materials and 0.1 Å s−1 for lithium fluorine (LiF). Finally, the aluminum cathode was deposited at a rate of 10 Å s−1. The deposition rates were controlled with a quartz crystal monitor and corrected by footstep machine simultaneously. The devices had emission areas of 1 mm × 1 mm. Electroluminescence spectra were taken using an Avantes USB 3648 spectrometer. Power-current-voltage curves were measured using a system incorporating a Thorlabs PM320E powermeter and a Keithley 2611 source-measure unit. The method of direct measurement of EQE was introduced by S.R. Forrest and D.D.C27. Bradley, using a placed probe (Thorlabs) in contact with the active pixel, making sure the device under test underfilled the probe area. The emission from the device was then measured as output power while the current through the device was monitored simultaneously. These two quantities were then used to calculate the EQE (as photons per electron) by converting the power signal to emitted photons and the device current to electrons. All measurements were performed in air at room temperature.

Additional Information

How to cite this article: Song, C. et al. Sb2O3/Ag/Sb2O3 Multilayer Transparent Conducting Films For Ultraviolet Organic Light-emitting Diode. Sci. Rep. 7, 41250; doi: 10.1038/srep41250 (2017).

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.


  1. 1

    Chae, J., Appasamy, S. & Jain, K. Patterning of indium tin oxide by projection photoablation and lift-off process for fabrication of flat-panel displays. Appl. Phys. Lett. 90, 261102 (2007).

  2. 2

    Liao, Y., Lu, Q., Fan, Y. & Liu, X. Manganese-doped indium oxide and its application in organic light-emitting diodes. Appl. Phys. Lett. 99, 023302 (2011).

  3. 3

    Xue, Z. et al. High-Performance NiO/Ag/NiO Transparent Electrodes for Flexible Organic Photovoltaic Cells. ACS Appl. Mater. Interfaces 6, 16403–16408 (2014).

  4. 4

    Gong, X. et al. High-Detectivity Polymer Photodetectors with Spectral Response from 300 nm to 1450 nm. Science 325, 1665–1667 (2009).

  5. 5

    Leem, D.-S. et al. Micron-scale patterning of high conductivity poly(3,4-ethylendioxythiophene):poly(styrenesulfonate) for organic field-effect transistors. Org. Electron. 11, 1307–1312 (2010).

  6. 6

    Cao, Q. et al. Transparent flexible organic thin-film transistors that use printed single-walled carbon nanotube electrodes. Appl. Phys. Lett. 88, 113511 (2006).

  7. 7

    Suganuma, K., Watanabe, S., Gotou, T. & Ueno, K. Fabrication of Transparent and Flexible Organic Field-Effect Transistors with Solution-Processed Graphene Source-Drain and Gate Electrodes. Appl.Phys.Express. 4, 021603 (2011).

  8. 8

    Guo, X. et al. Silver nanowire/polyimide composite transparent electrodes for reliable flexible polymer solar cells operating at high and ultra-low temperature. RSC Adv 5, 24953–24959 (2015).

  9. 9

    Lin, H. W. et al. Highly efficient visible-blind organic ultraviolet photodetectors. Adv. Mater. 17, 2489 (2005).

  10. 10

    Kim, K. H., An, H.-M., Kim, H.-D. & Kim, T. G. Transparent conductive oxide films mixed with gallium oxide nanoparticle/single-walled carbon nanotube layer for deep ultraviolet light-emitting diodes. Nanoscale.Res.Lett. 8, 507 (2013).

  11. 11

    Orita, M., Ohta, H., Hirano, M. & Hosono, H. Deep-ultraviolet transparent conductive beta-Ga2O3 thin films. Appl. Phys. Lett. 77, 4166–4168 (2000).

  12. 12

    Orita, M., Hiramatsu, H., Ohta, H., Hirano, M. & Hosono, H. Preparation of highly conductive, deep ultraviolet transparent beta-Ga2O3 thin film at low deposition temperatures. Thin Solid Films 411, 134–139 (2002).

  13. 13

    Zhang, N., Hu, Y. & Liu, X. Transparent organic thin film transistors with WO3/Ag/WO3 source-drain electrodes fabricated by thermal evaporation. Appl. Phys. Lett. 103, 033301 (2013).

  14. 14

    El Hajj, A. et al. Optimization of ZnO/Ag/ZnO multilayer electrodes obtained by Ion Beam Sputtering for optoelectronic devices. Thin Solid Films 520, 4666–4668 (2012).

  15. 15

    Hong, K. et al. Optical Properties of WO3/Ag/WO3 Multi layer As Transparent Cathode in Top-Emitting Organic Light Emitting Diodes. J. Phys. Chem. C 115, 3453–3459 (2011).

  16. 16

    Xue, Z., Liu, X., Lv, Y., Zhang, N. & Guo, X. Low-Work-Function, ITO-Free Transparent Cathodes for Inverted Polymer Solar Cells. ACS Appl. Mater. Interfaces 7, 19960–19965 (2015).

  17. 17

    Yasir, M. et al. Synthesis and properties of crystalline thin film of antimony trioxide on the Si(100) substrate. Appl. Surf. Sci. 349, 259–263 (2015).

  18. 18

    Tigau, N. et al. The influence of heat treatment on the electrical conductivity of antimony trioxide thin films. Journal of Optoelectronics and Advanced Materials 5, 907–912 (2003).

  19. 19

    Tigau, N., Ciupina, V. & Prodan, G. Structural, optical and electrical properties of Sb2O3 thin films with different thickness. Journal of Optoelectronics and Advanced Materials 8, 37–42 (2006).

  20. 20

    Song, C. et al. High work function transparent conductive oxides with multilayer films. Appl.Phys.Express. 5, 1102 (2012).

  21. 21

    Guo, X. et al. Ultrathin and efficient flexible polymer photovoltaic cells based on stable indium-free multilayer transparent electrodes. J. Mater. Chem. 22, 17176–17182 (2012).

  22. 22

    Wang, N., Liu, X. & Liu, X. Ultraviolet luminescent, high effective work function LaTiO3 doped indium oxide and its effects in organic optoelectronics. Adv.Mater. 22, 2211–2215 (2010).

  23. 23

    Aslan, K., Leonenko, Z., Lakowicz, J. R. & Geddes, C. D. Annealed silver-island films for applications in metal-enhanced fluorescence: Interpretation in terms of radiating plasmons. J. Fluoresc. 15, 643–654 (2005).

  24. 24

    Bardeen, J. Sufrace states and rectification at a metal semi-conductor contact. Phys. Rev. 71, 717–727 (1947).

  25. 25

    Haacke, G. New figure of merit for transparent conductors. J. Appl. Phys. 47, 4086–4089 (1976).

  26. 26

    Zhang, X. et al. Electroluminescence enhancement in ultraviolet organic light-emitting diode with graded hole-injection and -transporting structure. Physica Status Solidi-Rapid Research Letters 9, 353–357 (2015).

  27. 27

    Forrest, S. R., Bradley, D. D. C. & Thompson, M. E. Measuring the efficiency of organic light-emitting devices. Adv. Mater. 15, 1043–1048 (2003).

Download references


This work is supported by the CAS Innovation Program, and National Science Foundation of China No. 51103144, 61106057, 61274126.

Author information




C.S. designed and performed experiments, analysed data and wrote the paper; N.Z. participated in discussion and polished the paper; J.L. and X.G. assisted in sample preparation and measurements; X.L. proposed the idea and supervised the research.

Corresponding authors

Correspondence to Nan Zhang or Xingyuan Liu.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Song, C., Zhang, N., Lin, J. et al. Sb2O3/Ag/Sb2O3 Multilayer Transparent Conducting Films For Ultraviolet Organic Light-emitting Diode. Sci Rep 7, 41250 (2017).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.