Gd(III)-induced Supramolecular Hydrogelation with Enhanced Magnetic Resonance Performance for Enzyme Detection


Here we report a supramolecular hydrogel based on Gd(III)-peptide complexes with dramatically enhanced magnetic resonance (MR) performance. The hydrogelations were formed by adding Gd(III) ion to the nanofiber dispersion of self-assembling peptides naphthalene-Gly-Phe-Phe-Tyr-Gly-Arg-Gly-Asp (Nap-GFFYGRGD) or naphthalene-Gly-Phe-Phe-Tyr-Gly-Arg-Gly-Glu (Nap-GFFYGRGE). We further showed that, by adjusting the molar ratio between Gd(III) and the corresponding peptide, the mechanical property of resulting gels could be fine-tuned. The longitudinal relaxivity (r1) of the Nap-GFFYGRGE-Gd(III) was 58.9 mM−1 S−1, which to our knowledge is the highest value for such peptide-Gd(III) complexes so far. Such an enhancement of r1 value could be applied for enzyme detection in aqueous solutions and cell lysates.


The interaction of metal ions with amino acid side chains in proteins prevails in nature, and such interaction is crucial to the biological functions of proteins1,2. Inspired by nature, researchers have developed many biofunctional nanomaterials formed by the specific interactions between metal ions and peptides3,4,5,6,7. Among them, supramolecular hydrogels8,9,10,11,12, especially those of peptides13,14,15,16,17,18,19,20,21,22,23,24,25, have attracted research interests due to their inherent biocompatibility, degradability, and fast responsiveness to external stimuli26,27,28,29,30,31,32. Successful examples of metal ion-induced supramolecular hydrogelations have been reported. For example, Scheneider and co-workers reported on the zinc-induced formation of a hydrogel that was promising for wound healing33. Xu and Stupp had also used potassium and calcium ions, respectively, to induce the formation of supramolecular hydrogels with adjustable mechanical properties34,35. We recently reported copper ion-induced formation of nanofibers and hydrogels with quenched fluorescence property36. These works highlight the potential of metal ion-triggered supramolecular hydrogels in cell culture, tissue engineering, sensing, and drug delivery.

Magnetic resonance imaging (MRI) is a powerful, non-invasive diagnostic technology with high spatial resolution. MRI contrast agents, such as Gd(III) complexes, are often used to enhance the contrast37 between pathological and normal tissues by altering the longitudinal and transverse (T1 and T2) relaxation times. The relaxivity of a contrast agent is dependent on several factors, including the number of water molecules in the coordination shell, the exchange rate of the coordinated water with the bulk water, and the tumbling rate of the complex in solution38. However, the majority of Gd(III) complexes used as MRI contrast agents in clinical practice, such as Magnevist (DOTA(Gd)), do not display optimal relaxivity due to small sizes and rapid tumbling in solution. To improve relaxivity, the small molecular contrast agents were covalently or noncovalently bound to macromolecules such as polymers39, dendrimers40, carbohydrates41, liposomes42, and proteins43. In this respect, our goal is to develop a supramolecular hydrogel based on Gd(III)-peptide complexes with optimized relaxivity.

Results and Discussion

We opted to use Gd(III) to trigger the formation of supramolecular nanofibers and hydrogels, because we believed that the formation of supramolecular nanostructures of Gd(III) complex might improve the magnetic resonance (MR) performance of the MR contrast agent of Gd(III). We first chose one of our recently developed self-assembling peptides, Nap-GFFYGRGD for the test (Fig. 1A). Similar to many self-assembling peptide molecules that can form supramolecular nanostructures, the driving force of the self-assembly of the Nap-GFFYGRGD is hydrogen bond between peptide chain and π -π interaction between aromatic groups on Nap and amino acid of F. The peptide Nap-GFFYGRGD could self-assemble into supramolecular nanofibers but not hydrogels at the concentrations lower than 0.7 wt% in 4-(2-Hydroxyethyl)-1-piperazineethanesulfonic acid (HEPES, pH = 7.4) solution44. The reason for the peptide incapable of forming hydrogels at these concentrations was the weak inter-fiber interaction and repulsion between negatively charged fibers. We hypothesized that, if we could enhance the inter-fiber interaction or decrease the repulsion force between fibers, we might obtain stable three dimensional (3D) network of nanofibers and supramolecular hydrogels (Fig. 1B). There were two carboxylic acid residues on the terminal amino acid (aspartic acid (D)) of the peptide that might form complex with metal ions such as Gd(III) (Fig. 1A). We therefore planned to test whether the addition of Gd(III) would cross-link the nanofibers and trigger the formation of supramolecular hydrogels of the peptide.

Figure 1

(A) The chemical structures of Nap-GFFYGRGD and possible Gd3+-peptide complex (Insert: optical images of a HEPES solution of Nap-GFFYGRGD (0.25 wt%, pH = 7.4) with or without 0.33 equiv. of Gd(III)) and (B) The schematic illustration for hydrogel formation.

We fixed the peptide concentration to be 0.25 wt% (2.5 mg/mL) in the HEPES solution for the test. The peptide formed a solution at this concentration, and the addition of 0.33 mole equivalent of Gd(III) to the peptide into the solution could indeed trigger the supramolecular hydrogel formation (Fig. 1A) within 10 seconds. The minimum equiv. of Gd(III) needed for gelation was 0.05 (Supplementary Fig. S7). However, it took a longer time (about 16 h) for the formation of a hydrogel. In addition, it took about 10 h and 6 h to form the hydrogels with the addition of 0.1 and 0.2 equiv. of Gd(III) into the peptide (0.25 wt%) solution, respectively. It suggested that the gelation time decreased with increasing the Gd(III) concentration. The diameter of nanofibers in the gel would become smaller with the increasing Gd(III) concentration as well. The short-peptide hydrogels are different with polymeric hydrogels. They are soft enough to be filtered. Therefore we used the filtration to remove the nanofibers. If passing the resulting gel through a filter (0.45 μm), it was found that less than 1.0% of Gd(III) remained in the filtrate (determined by Inductively Coupled Plasma (ICP)). In the meantime, we also found that 90.2% of the Nap-GFFYGRGD converted to the hydrogel by calculating the residual amount of the peptide in the filtrate. This observation indicated that the Gd(III) could form a tight complex with the peptide. Several pioneering results had demonstrated that one Gd(III) could form a complex with three carboxylic acids25. We therefore hypothesized that Gd(III) served as a cross-linker to enhance the inter-fiber interaction of nanofibers of Nap-GFFYGRGD, resulting in supramolecular hydrogelations (Fig. 1B). The result was similar to our previous report that a recombinant protein with four binding sites could serve as a cross-linker to trigger hydrogelations of peptide nanofiber solutions45. We then introduced the peptide naphthalene-Gly-Phe-Phe-Tyr-Gly-Arg-Gly-Glu (Nap-GFFYGRGE) and naphthalene-Gly-Arg-Gly-Asp (Nap-GRGD) (Fig. 2) as the control to justify that the Gd(III) could serve as a cross-linker to enhance the inter-fiber interactions in the peptide solutions and lead to the hydrogelation. The peptide Nap-GFFYGRGE has the same self-assembly motif, Nap-GFFY, as the Nap-GFFYGRGD, while the Nap-GRGD doesn’t have. The critical difference between Nap-GFFGRGD and Nap-GFFYGRGE is the last amino acid residue. The former is aspartic acid (D), the latter is glutamic acid (E). The addition of 1 equiv. of Gd(III) to the HEPES solution of the peptide Nap-GRGD (1.0 wt%) did not lead to hydrogelations, because it could not firstly self-assemble into nanofibers. Hydrogelations could also be observed by adding 0.33 equiv. of Gd(III) to the HEPES solution of Nap-GFFYGRGE (0.25 wt%, Supplementary Fig. S8) because the peptide Nap-GFFYGRGE could also form a nanofiber dispersion at this concentration (Supplementary Fig. S11A). These observations further suggested that the hydrogelations were due to the enhancement of inter-fiber interactions. Another possible reason for hydrogelation was the charge screening of fibers because the Gd(III) was positively charged and the fibers were negatively charged.

Figure 2

The chemical structures of Nap-GFFYGRGE and Nap-GRGD.

Afterward we performed rheological measurements to study the mechanical properties of the hydrogel containing 0.25 wt% of Nap-GFFYGRGD and 0.33 equiv. of Gd(III). The result in Fig. 3A showed that both the storage moduli (G’) and the loss storage (G”) values exhibited weak frequency dependences at the range of 0.1 to 100 rad/s. The G’ value of the gel was about 200 Pa and it was about an order of magnitude bigger than its G” value. These observations suggested the formation of a true hydrogel46. The gels formed with higher amounts of Gd(III) exhibited slightly bigger G’ values (Supplementary Figs S9 and S10), which was consistent with results from Xu and Stupp groups that increasing the concentration of metal ions led to better mechanical property of the gels33. The transmission electron microscopy (TEM) was also used to characterize the nanostructures in the solution and the gel. As shown in Fig. 3B, uniform nanofibers with the diameter of 30–50 nm was observed for the HEPES solution of the peptide, which was consistent with our previous observations36. Upon the addition of 0.33 equiv. of Gd(III) into the peptide solution, the diameter of the nanofibers became smaller (20–35 nm, Fig. 3C). The density of cross-linking points of the nanofibers in the gel was much higher than that in the peptide nanofiber solution, which was consistent with our recent observations in hydrogels formed by adding cis-dichlorodiamineplatinum(II) (DDP) to a taxol-peptide amphiphile solution47. Similar to our previous report36, the metal ions chelated with the peptide molecules by forming complex with two intra-molecular carboxylic acids on the same peptide molecules. With increasing amount of metal ions, more peptide molecules dissociated from the nanofibers to form complex with the metal ions and the complex re-assembled into nanofibers with smaller diameters. The formation of Gd(III)-peptide complex decreased the inter-fiber repulsion, leading to the formation of stable 3D fiber networks and hydrogels.

Figure 3

(A) Dynamic frequency sweep at the strain of 1% of the gel in Fig. 1 and TEM images of (B) a HEPES solution of Nap-GFFYGRGD (0.25 wt%) and (C) the resulting gel in the presence of 0.33 equiv. of Gd(III).

We further investigated whether the hydrogelation could improve the MR performance of Gd(III) with a 1.2 T MRI scanner. Figure 4A showed the T1-weighted MR images of HEPES solutions of Gd(III) with different equiv. of the peptide and the HEPES solution of clinically used Magnevist (DOTA(Gd)). The results clearly indicated that, for the Gd(III) solutions with different amounts of the peptide, their MR signal enhanced with the increase of the peptide concentrations. Such enhancement reached the equilibrium when the equiv. of peptide was more than 4. When the equiv. of the peptide was bigger than 3, the peptide-Gd(III) complexes exhibited big contrast enhancements and therefore we observed much brighter images from these samples (Fig. 4A-c,d,e, and f) than the sample of Magnevist (Fig. 4A-h) and the sample of Gd(III) without the peptide (Fig. 4A-g). We then quantified the MR signal enhancement by calculating the r1 value. As shown in Fig. 4B, the r1 value of Magnevist was about 4.3 mM−1 S−1, while this value for our peptide-Gd(III) complex (peptide: Gd(III) = 6: 1) was 44.6 mM−1 S−1. Similar observations were obtained for Nap-GFFYGRGE-Gd(III) complex, and its r1 value was 58.9 mM−1 S−1 (Supplementary Fig. S14). The r1 value of our peptide-Gd(III) complexes (Nap-GFFYGRGD-Gd(III) and Nap-GFFYGRGE-Gd(III) complexes) was about 10.4 and 13.7 times that of Magnevist. To the best of our knowledge, these values were the biggest ones for peptide-Gd(III) complexes3,42,43,48,49,50. Such a huge enhancement was due to the binding of Gd(III) to the nanofibers and the formation of complexes between Gd(III) and the peptides. The formation of complexes dramatically slowed the molecular tumbling of Gd(III) and reduced the relaxation time of water molecules binding to the Gd(III), thus leading to the huge enhancement of the r1 value. We thought that amino acid E possessed one more CH2 between peptide backbone and the side chained carboxylic acid. Therefore E is more flexible and it might be more easily to form a complex with Gd(III), which explained why the r1 value of Nap-GFFYGRGE was higher than that of Nap-GFFYGRGD.

Figure 4

(A) T1 map of samples of HEPES solutions containing 125 μM of Gd(III) and (a) 1 equiv., (b) 2 equiv., (c) 3 equiv., (d) 4 equiv., (e) 5 equiv., (f) 6 equiv. of the peptide, (g) without peptide, and (h) the HEPES solution containing 125 μM of DOTA(Gd) (Magnevist), (B) Plot of relaxation rate r1 versus Gd3+ concentration for peptide-Gd(III) complex (Nap-GFFYGRGD: Gd(III) = 6:1, HEPES solution, pH = 7.4) and the Magnevist. The relaxivity value r1 was obtained from the slope of linear fitting of the experimental data.

Supramolecular hydrogelations have been extensively applied for the detection of important analytes by naked eyes in complex fluids51,52,53,54,55. We envisioned that the formation of Gd(III)-peptide complex with dramatically enhanced MR performance could also be used to detect enzyme activity in complex samples. We therefore designed and synthesized a peptide naphthalene-Gly-Phe -Phe-Tyr(phosphate)-Gly-Arg-Gly-Asp (Nap-GFFpYGRGD) (Fig. 5A). We assumed that the peptide Nap-GFFpYGRGD could not self-assemble into nanofibers due to the presence of highly hydrophilic phosphoric acid residue on pY. However, the peptide could be converted to Nap-GFFYGRGD by the enzyme of alkali phosphatase (ALP), which could self-assemble into nanofibers and form complexes with Gd(III). We used TEM to characterize the nanostructures of peptide solution before and after the addition of ALP in the presence of Gd(III). As shown in Fig. 5B, we observed few nanofibers in the HEPES buffer solution containing 125 μM of Gd(III) and 750 μM of Nap-GFFpYGRGD (6 equiv. to Gd(III)). Upon the addition of ALP for 1 h, more than 95% of Nap-GFFpYGRGD was converted to Nap-GFFYGRGD (Supplementary Fig. S16), and we observed high density of nanofibers in the solution (Fig. 5C).

Figure 5

(A) The chemical structure of Nap-GFFpYGRGD and its enzymatic transformation by phosphatase, TEM images of a HEPES solution containing 125 μM of Gd(III) and 6 equiv. of Nap-GFFpYGRGD (750 μM) (B) without or (C) with phosphatase, T1 map of HEPES solutions containing 125 μM of Gd(III) and 6 equiv. of Nap-GFFpYGRGD incubated with (D) different concentrations of phosphatase (U/mL) or (E) different cell lines (lysates from 2 * 104 cells) for 1 h at room temperature.

We then tested whether the Nap-GFFpYGRGD-Gd(III) system could be applied to detect ALP activity. Different concentrations of ALP (0–1 U/mL) were added to the HEPES solutions containing 125 μM of Gd(III) and 6 equiv. of Nap-GFFpYGRGD (750 μM). The solutions were then incubated for 1 h at room temperature (20–25 °C) before scanning by a 1.2 T MRI scanner. As shown in Fig. 5D, we obtained a dark image from the sample without ALP and observed more and more bright images from samples with more and more amounts of enzyme. These observations clearly suggested that our system could be used to detect enzyme concentration. It is well known that different cell lines express different levels of phosphatase and cancer cells have much higher expression level of phosphatase than normal cells. It is of great importance to detect the expression level of phosphatase in different cell lines. We therefore tested whether our strategy could be applied for the detection of enzyme activity in the complex sample of cell lysates. Different kinds of cell lysates (HeLa, HepG2, PC-3, and NIH 3T3) were prepared and added into the HEPES solution containing Gd(III) and Nap-GFFpYGRGD. After incubation for 1 h at room temperature, we captured the T1-weighted MR images by a 1.2 T MRI scanner. As shown in Fig. 5E, compared to the image from normal cell lysate (3T3), those from cancer cell lysates were much brighter, suggesting the higher expression levels of phosphatase in cancer cells. Among samples of cancer cells, the one containing HeLa cell lysate showed the brightest image, indicating the highest expression level of phosphatase in HeLa cells. These observations suggested that our method could be applied for direct detection of enzyme activity in complex fluids such as cell lysates.


In summary, we have successfully used the MR contrast agent Gd(III) to trigger the formation of supramolecular hydrogels of self-assembling peptides. The Gd(III) could form tight complexes with the peptide, resulting in reducing the relaxation times of water molecules and a huge enhancement of r1 value of Gd(III). The hydrogelations and the enhancement of MR signal were instant after simply mixing the peptide and Gd(III) in aqueous solutions. The huge enhancement of MR performance of Gd(III) after chelating with the peptide could be applied for the detection of enzyme activity in both buffer solutions and cell lysates. One of shortcomings of our system is probably the leakage of Gd(III) after the peptide digestion in vivo, which may cause toxicity and hinder the in vivo application of our system at high concentrations. This shortcoming might be overcome by attaching DOTA(Gd) to the self-assembling peptide nanofibers.

Methods Summary


Fmoc-amino acids were obtained from GL Biochem (Shanghai). Naphthalene acetic acid and Gadolinium (III) chloride hexahydrate were purchased from Aladdin Chemistry CO. Ltd (Shanghai). 2-Cl-trityl chloride resin was obtained from Nankai University Resin Co. Ltd. Commercially available reagents were used without further purification, unless noted otherwise. Ultrapure water (produced by a Mili-Q-A10 Advantage Ultrapure Water Purification System, America) was used for all experiments. All other chemicals were reagent grade or better.

General methods

The synthesized compounds were characterized using 1H NMR (Bruker ARX 400, Germany). The LC-MS spectrometric analyses were performed at the Thermo Finnigan LCQ AD System (America). HPLC was conducted at LUMTECH HPLC (Germany) system using a C18 RP column with MeOH (0.1% of Trifluoroacetic acid (TFA), 1 μl/L) and water (0.1% of TFA, 1 μl/L) as the eluents. Rheology was performed on an AR 2000ex (TA instrument, America) system using a parallel plates (40 mm) at the gap of 500 μm. TEM was done on a Tecnai G2 F20 system, operating at 200 kV. The MR and relaxation time was measured by 1.2 T magnetic field (NightOWLIILB985, Germany).

Peptide synthesis

The peptide was prepared by solid-phase peptide synthesis (SPPS) using 2-chlorotrityl chloride resin and the corresponding N-Fmoc protected amino acids with side chains properly protected by a tert-butyl group or Pbf group or Boc group. After the first amino acid was loaded on the resin by its C-terminal, 20% piperidine in anhydrous N, N’-dimethylformamide (DMF) was used to de-protect Fmoc group. Then the next Fmoc protected amino acid was coupled to the free amino group using O-(benzotriazol-1-yl)-N,N,N’,N’-tetramethyluranium- hexafluorophosphate (HBTU) as the coupling reagent and diisopropylethylamine (DIEA) as catalytic reagent. The growth of the peptide chain was according to the established Fmoc SPPS protocol. After the last amino acid was coupled, excessive reagents were removed by a single DMF wash for 5 min (5 mL per gram of resin), followed by 5 times dichloromethane (DCM) wash for 2 min (5 mL per gram of resin). The peptide was cleaved using 95% of TFA with 2.5% of trimethylsilane (TMS) and 2.5% of H2O for 30 min. TFA was removed by rotary evaporator, then 20 mL of ice-cold diethylether was added. The resulting precipitate was filtrated and washed by ice-cold diethylether. The resulting solid was further purified by HPLC and dried by a lyophilizer.


1H NMR (400 MHz, DMSO-d6) δ 9.19 (s, 1 H), 8.29–8.17 (m, 4 H), 8.13 (d, J = 6.8 Hz, 2 H), 8.09–8.02 (m, 2 H), 7.89–7.79 (m, 3 H), 7.75 (s, 1 H), 7.69 (s, 1 H), 7.48 (dd, J = 8.9, 5.8 Hz, 2 H), 7.42 (d, J = 8.6 Hz, 2 H), 7.25–7.10 (m, 12 H), 7.06 (d, J = 8.3 Hz, 2 H), 6.66 (d, J = 8.3 Hz, 2 H), 4.57–4.41 (m, 4 H), 4.31 (d, J = 5.8 Hz, 1 H), 3.74 (dd, J = 16.3, 10.9 Hz, 5 H), 3.65–3.54 (m, 3 H), 3.10 (d, J = 5.7 Hz, 2 H), 2.94 (ddd, J = 17.6, 16.4, 6.3 Hz, 3 H), 2.83–2.73 (m, 2 H), 2.72–2.64 (m, 2 H), 2.60 (dd, J = 16.7, 6.6 Hz, 1 H), 1.80–1.67 (m, 1 H), 1.52 (dd, J = 13.7, 8.5 Hz, 3 H). MS: calc. M+ = 1086.15, obsd. M+ = 1086.70.


1H NMR (400 MHz, DMSO-d6) δ 8.33 (t, J = 5.6 Hz, 1 H), 8.23 (dd, J = 15.3, 6.9 Hz, 2 H), 8.11 (d, J = 7.8 Hz, 1 H), 7.97–7.81 (m, 3 H), 7.78 (s, 1 H), 7.48 (td, J = 12.5, 7.2 Hz, 4 H), 7.25 (s, 1 H), 7.12 (s, 1 H), 7.00 (s, 1 H), 4.55 (dd, J = 13.8, 6.5 Hz, 1 H), 4.29 (t, J = 7.3 Hz, 1 H), 3.78 (ddd, J = 17.1, 14.1, 5.7 Hz, 4 H), 3.67 (s, 2 H), 3.07 (d, J = 5.9 Hz, 2 H), 2.89 (s, 1 H), 2.75–2.53 (m, 3 H), 1.76–1.61 (m, 1 H), 1.59–1.35 (m, 3 H). MS: calc. M+ = 571.23, obsd.[M + H]+ = 572.45.


1H NMR (400 MHz, DMSO) δ 8.52 (d, J = 9.1 Hz, 1 H), 8.33 (d, J = 7.6 Hz, 1 H), 8.18 (d, J = 8.2 Hz, 2 H), 8.06 (d, J = 8.5 Hz, 1 H), 7.21 (dt, J = 37.8, 15.0 Hz, 10 H), 7.09 (t, J = 7.5 Hz, 2 H), 6.42 (d, J = 9.2 Hz, 1 H), 4.57 (s, 1 H), 4.52–4.38 (m, 2 H), 3.63 (ddd, J = 22.6, 16.7, 8.4 Hz, 5 H), 3.04 (d, J = 13.7 Hz, 2 H), 2.99–2.90 (m, 2 H), 2.83–2.57 (m, 4 H), 2.55 (s, 2 H). MS: calc. M+ = 1166.13, obsd. [M + H]+ = 1167.55.


1H NMR (400 MHz, DMSO-d6) δ 9.22 (s, 2 H), 8.32 (s, 1 H), 8.30 (d, J = 5.3 Hz, 1 H), 8.21 (s, 1 H), 8.16 (s, 2 H), 8.13 (s, 2 H), 8.12–8.08 (m, 4 H), 7.88 (s, 1 H), 7.86 (s, 1 H), 7.83 (s, 3 H), 7.81 (s, 1 H), 7.75 (s, 2 H), 7.56 (s, 1 H), 7.48 (d, J = 3.2 Hz, 1 H), 7.47 (s, 1 H), 7.42 (d, J = 8.4 Hz, 2 H), 7.21 (s, 1 H), 7.20 (s, 3 H), 7.18 (s, 1 H), 7.16 (s, 4 H), 7.07 (s, 1 H), 7.05 (s, 1 H), 6.66 (s, 1 H), 6.64 (s, 1 H), 4.49–4.45 (m, 3 H), 4.29 (d, J = 6.6 Hz, 1 H), 4.22 (d, J = 5.0 Hz, 1 H), 3.75 (s, 6 H), 3.09 (d, J = 5.9 Hz, 2 H), 2.92 (d, J = 13.7 Hz, 4 H), 2.75 (s, 2 H), 2.69–2.63 (m, 2 H), 2.25 (s, 1 H), 1.98–1.94 (m, 1 H), 1.79–1.72 (m, 2 H), 1.54–1.49 (m, 3 H). MS: calc. M+ = 1099.47, obsd.[M + 2 H]+ = 1101.40.

Formation of the hydrogels

In order to investigate the hydrogel formation, the Nap-GFFYGRGD was first dissolved in a small amount of HEPES in a little glass bottle (as shown in Supplementary Fig. S7), then about 2 equiv. of sodium hydroxide solution (1 M) were added to adjust the pH to about 7.4. Afterward, a certain amount of HEPES was supplemented to obtain Nap-GFFYGRGD solution with desired concentration. Then HEPES solution (pH = 7.4) containing different equivalents (0.02, 0.05, 0.1, 0.2, 0.33) of Gd(III) was added into the above solution to initial the hydrogelation. The similar procedure were conducted when the hydrogels of Nap-GFFYGRGE were prepared.


Rheology test was carried out on an AR 2000ex (TA instrument) system, 40 mm parallel plates was used during the experiment at the gap of 500 μm. For the dynamic time sweep, the solution of compounds were directly transferred to the rheometer and it was conducted at the frequency of 1 rad/s and the strain of 1% immediately. The gel was also characterized by the mode of dynamic frequency sweep in the region of 0.1–100 rad/s at the strain of 1%. A dynamic strain sweep at the frequency of 1 rad s−1 was conducted finally.

Preparation of TEM samples

HEPES solutions of Nap-GFFYGRGD and Nap-GFFYGRGD with different equiv. of Gd(III) were prepared as described above. Next, 10 μL of each sample placed on a carbon-coated copper grid and incubated for 30 seconds to allow the peptide nanostructures to adhere to the substrate, then rinsed twice with ultrapure water. The samples were then stained with a saturated uranyl acetate solution and placed in a desiccator overnight prior to analysis. Similar process was used to prepare samples of HEPES solution containing 125 μM of Gd(III) and 6 equiv. of Nap-GFFpYGRGD (750 μM) with or without phosphatase.

Preparation of cell lysates for MRI measurements

The 3T3, HepG2, HeLa were maintained in our lab. Cells were cultured in DMEM supplemented with 10% vFBS and 100 U/mL penicillin/streptomycin at 37 °C in a humidified atmosphere of 5% CO2. Different cell lines were counted and then broken by a sonic oscillator. Next, 100 μL of lysates (from 2 * 104 cells) of different cell lines were added into the HEPES solution containing Gd(III) and Nap-GFFpYGRGD.

In Vitro MRI

In vitro T1-weighted MR images were obtained on a 1.2 T MRI system (Huantong Corporation, Shanghai, China). The parameters adopted were as follows: TR/TE = 100.0/8.8 ms, slice thickness = 1mm, 30.0 °C. Gd(III)-peptide samples were dispersed in HEPES buffer at various Gd(III) concentrations. The relaxation time values (T1) were also measured on the same MRI system (1.2 T) by the inversion recovery sequence. The r1 and r2 relaxivity values were determined through the curve fitting of 1/T1 and 1/T2 relaxation time (s−1) versus the Gd (III) concentration (mM).

Removal of Gd(III) from water

To investigate the removal of Gd (III) from water, 10 mL of the solution containing 10 ppm of Gd(III) was prepared. Hydrogel was prepared by 125 μM of Gd(III) mixed with 6 equiv. of Nap-GFFYGRGD (Gd(III): peptide = 1:6) overnight. Then resulting hydrogel was filtered (0.45 μm) to remove the nanofibers. After filtered, the amount of Gd(III) in the filtrate was determined by Inductively Coupled Plasma-Atomic Emission Spectrometry (ICP-AES).

Additional Information

How to cite this article: Hua, Y. et al. Gd(III)-induced Supramolecular Hydrogelation with Enhanced Magnetic Resonance Performance for Enzyme Detection. Sci. Rep. 7, 40172; doi: 10.1038/srep40172 (2017).

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.


  1. 1

    Berthon, G. Critical evaluation of the stability constants of metal complexes of amino acids with polar side chains (Technical Report). Pure. Appl. Chem. 67, 123 (1995).

    Article  Google Scholar 

  2. 2

    Lenz, G. R. & Martell, A. E. Metal Chelates of Some Sulfur-Containing Amino Acids. Biochemistry 3, 745–750 (1964).

    CAS  Article  Google Scholar 

  3. 3

    Berwick, M. R. et al. De Novo Design of Ln(III) Coiled Coils for Imaging Applications. J. Am. Chem. Soc. 136, 1166–1169 (2014).

    CAS  Article  Google Scholar 

  4. 4

    Gao, Y. et al. Enzyme-Instructed Molecular Self-assembly Confers Nanofibers and a Supramolecular Hydrogel of Taxol Derivative. J. Am. Chem. Soc. 131, 13576–13577 (2009).

    CAS  Article  Google Scholar 

  5. 5

    Suzuki, K., Hiroaki, H., Kohda, D., Nakamura, H. & Tanaka, T. Metal ion induced self-assembly of a designed peptide into a triple-stranded alpha-helical bundle: A novel metal binding site in the hydrophobic core. J. Am. Chem. Soc. 120, 13008–13015 (1998).

    CAS  Article  Google Scholar 

  6. 6

    Luo, J. N. & Tong, Y. W. Self-Assembly of Collagen-Mimetic Peptide Amphiphiles into Biofunctional Nanofiber. ACS Nano 5, 7739–7747 (2011).

    CAS  Article  Google Scholar 

  7. 7

    Lee, S. S. et al. Bone regeneration with low dose BMP-2 amplified by biomimetic supramolecular nanofibers within collagen scaffolds. Biomaterials 34, 452–459 (2013).

    CAS  Article  Google Scholar 

  8. 8

    Naskar, J., Palui, G. & Banerjee, A. Tetrapeptide-Based Hydrogels: for Encapsulation and Slow Release of an Anticancer Drug at Physiological pH. J. Phys. Chem. B 113, 11787–11792 (2009).

    CAS  Article  Google Scholar 

  9. 9

    Rasale, D. B., Maity, I., Konda, M. & Das, A. K. Peptide self-assembly driven by oxo-ester mediated native chemical ligation. Chem. Commun. 49, 4815–4817 (2013).

    CAS  Article  Google Scholar 

  10. 10

    Vemula, P. K. et al. Prodrugs as self-assembled hydrogels: a new paradigm for biomaterials. Curr. Opin. Biotechnol. 24, 1174–1182 (2013).

    CAS  Article  Google Scholar 

  11. 11

    Lloyd, G. O., Piepenbrock, M. O. M., Foster, J. A., Clarke, N. & Steed, J. W. Anion tuning of chiral bis(urea) low molecular weight gels. Soft Matter 8, 204–216 (2012).

    CAS  ADS  Article  Google Scholar 

  12. 12

    Nanda, J., Biswas, A., Adhikari, B. & Banerjee, A. A Gel-Based Trihybrid System Containing Nanofibers, Nanosheets, and Nanoparticles: Modulation of the Rheological Property and Catalysis. Angew. Chem.-Int. Edit. 52, 5041–5045 (2013).

    CAS  Article  Google Scholar 

  13. 13

    Sun, Z. F. et al. Ferrocenoyl Phenylalanine: A New Strategy Toward Supramolecular Hydrogels with Multistimuli Responsive Properties. J. Am. Chem. Soc. 135, 13379–13386 (2013).

    CAS  Article  Google Scholar 

  14. 14

    Liu, H. et al. Incorporation of tyrosine phosphate into tetraphenylethylene affords an amphiphilic molecule for alkaline phosphatase detection, hydrogelation and calcium mineralization. J. Mat. Chem. B 1, 5550–5556 (2013).

    CAS  Article  Google Scholar 

  15. 15

    Raeburn, J., Cardoso, A. Z. & Adams, D. J. The importance of the self-assembly process to control mechanical properties of low molecular weight hydrogels. Chem. Soc. Rev. 42, 5143–5156 (2013).

    CAS  Article  Google Scholar 

  16. 16

    Ikeda, M. et al. Installing logic-gate responses to a variety of biological substances in supramolecular hydrogel-enzyme hybrids. Nat. Chem. 6, 511–518 (2014).

    CAS  Article  Google Scholar 

  17. 17

    Ikeda, M., Fukuda, K., Tanida, T., Yoshii, T. & Hamachi, I. A supramolecular hydrogel containing boronic acid-appended receptor for fluorocolorimetric sensing of polyols with a paper platform. Chem. Commun. 48, 2716–2718 (2012).

    CAS  Article  Google Scholar 

  18. 18

    Xue, B. et al. An integrated artificial photosynthesis system based on peptide nanotubes. Nanoscale 6, 7832–7837 (2014).

    CAS  ADS  Article  Google Scholar 

  19. 19

    Li, Y., Ding, Y., Qin, M., Cao, Y. & Wang, W. An enzyme-assisted nanoparticle crosslinking approach to enhance the mechanical strength of peptide-based supramolecular hydrogels. Chem. Commun. 49, 8653–8655 (2013).

    CAS  Article  Google Scholar 

  20. 20

    Li, Y., Qin, M., Cao, Y. & Wang, W. Designing the mechanical properties of peptide-based supramolecular hydrogels for biomedical applications. Sci. China-Phys. Mech. Astron. 57, 849–858 (2014).

    CAS  ADS  Article  Google Scholar 

  21. 21

    King, K. N. & McNeil, A. J. Streamlined approach to a new gelator: inspiration from solid-state interactions for a mercury-induced gelation. Chem. Commun. 46, 3511–3513 (2010).

    CAS  Article  Google Scholar 

  22. 22

    Bremmer, S. C., McNeil, A. J. & Soellner, M. B. Enzyme-triggered gelation: targeting proteases with internal cleavage sites. Chem. Commun. 50, 1691–1693 (2014).

    CAS  Article  Google Scholar 

  23. 23

    Hughes, M., Debnath, S., Knapp, C. W. & Ulijn, R. V. Antimicrobial properties of enzymatically triggered self-assembling aromatic peptide amphiphiles. Biomater. Sci. 1, 1138–1142 (2013).

    CAS  Article  Google Scholar 

  24. 24

    Kuang, Y., Gao, Y. & Xu, B. Supramolecular hydrogelators of N-terminated dipeptides selectively inhibit cancer cells. Chem. Commun. 47, 12625–12627 (2011).

    CAS  Article  Google Scholar 

  25. 25

    Bai, S. et al. Stable Emulsions Formed by Self-Assembly of Interfacial Networks of Dipeptide Derivatives. ACS Nano 8, 7005–7013 (2014).

    CAS  Article  Google Scholar 

  26. 26

    Collier, J. H., Rudra, J. S., Gasiorowski, J. Z. & Jung, J. P. Multi-component extracellular matrices based on peptide self-assembly. Chem. Soc. Rev. 39, 3413–3424 (2010).

    CAS  Article  Google Scholar 

  27. 27

    Fleming, S. & Ulijn, R. V. Design of nanostructures based on aromatic peptide amphiphiles. Chem. Soc. Rev. 43, 8150–8177 (2014).

    CAS  Article  Google Scholar 

  28. 28

    Gao, Y., Zhao, F., Wang, Q. G., Zhang, Y. & Xu, B. Small peptide nanofibers as the matrices of molecular hydrogels for mimicking enzymes and enhancing the activity of enzymes. Chem. Soc. Rev. 39, 3425–3433 (2010).

    CAS  Article  Google Scholar 

  29. 29

    He, M., Li, J., Tan, S., Wang, R. & Zhang, Y. Photodegradable Supramolecular Hydrogels with Fluorescence Turn-On Reporter for Photomodulation of Cellular Microenvironments. J. Am. Chem. Soc. 135, 18718–18721 (2013).

    CAS  Article  Google Scholar 

  30. 30

    Li, P., Dou, X. Q., Zhang, D. & Feng, C. L. Self-assembled gelator-polysaccharide hybrid hydrogel for controllable dye release. J. Control. Release 172, E23–E23 (2013).

    CAS  Article  Google Scholar 

  31. 31

    Miao, X. M. et al. Switchable Catalytic Activity: Selenium-Containing Peptides with Redox-Controllable Self-Assembly Properties. Angew. Chem.-Int. Edit. 52, 7781–7785 (2013).

    CAS  Article  Google Scholar 

  32. 32

    Wei, H., Zhang, X. Z., Cheng, C., Cheng, S. X. & Zhuo, R. X. Self-assembled, thermosensitive micelles of a star block copolymer based on PMMA and PNIPAAm for controlled drug delivery. Biomaterials 28, 99–107 (2007).

    CAS  Article  Google Scholar 

  33. 33

    Micklitsch, C. M. et al. Zinc-Triggered Hydrogelation of a Self-Assembling beta-Hairpin Peptide. Angew. Chem.-Int. Edit. 50, 1577–1579 (2011).

    CAS  Article  Google Scholar 

  34. 34

    Kuang, Y., Gao, Y., Shi, J. F., Lin, H. C. & Xu, B. Supramolecular hydrogels based on the epitope of potassium ion channels. Chem. Commun. 47, 8772–8774 (2011).

    CAS  Article  Google Scholar 

  35. 35

    Spoerke, E. D., Anthony, S. G. & Stupp, S. I. Enzyme Directed Templating of Artificial Bone Mineral. Adv. Mater. 21, 425–430 (2009).

    CAS  Article  Google Scholar 

  36. 36

    Cai, Y. B. et al. Environment-Sensitive Fluorescent Supramolecular Nanofibers for Imaging Applications. Anal. Chem. 86, 2193–2199 (2014).

    CAS  Article  Google Scholar 

  37. 37

    Britton, M. M. Magnetic resonance imaging of chemistry. Chem. Soc. Rev. 39, 4036–4043 (2010).

    CAS  Article  Google Scholar 

  38. 38

    Tóth, É., Helm, L. & Merbach, A. E. In Contrast Agents I: Magnetic Resonance Imaging Contrast Agents I: Magnetic Resonance Imaging (ed Werner, Krause ) 61–101 (Springer Berlin Heidelberg, 2002).

  39. 39

    Opsahl, L. R., Uzgiris, E. E. & Vera, D. R. Tumor imaging with a macromolecular paramagnetic contrast agent: Gadopentetate dimeglumine-polylysine. Academic Radiology 2, 762–766 (1995).

    CAS  Article  Google Scholar 

  40. 40

    Langereis, S. et al. Evaluation of Gd(III)DTPA-terminated poly(propylene imine) dendrimers as contrast agents for MR imaging. NMR in Biomedicine 19, 133–141 (2006).

    CAS  Article  Google Scholar 

  41. 41

    Sirlin, C. B. et al. Gadolinium-DTPA-dextran: A macromolecular MR blood pool contrast agent1. Academic Radiology 11, 1361–1369 (2004).

    Article  Google Scholar 

  42. 42

    Strijkers, G. J. et al. Relaxivity of liposomal paramagnetic MRI contrast agents. Magnetic Resonance Materials in Physics, Biology and Medicine 18, 186–192 (2005).

    CAS  Article  Google Scholar 

  43. 43

    Yang, J. J. et al. Rational Design of Protein-Based MRI Contrast Agents. J. Am. Chem. Soc. 130, 9260–9267 (2008).

    CAS  Article  Google Scholar 

  44. 44

    Liu, J. F. et al. Self-Assembling Peptide of D-Amino Acids Boosts Selectivity and Antitumor Efficacy of 10-Hydroxycamptothecin. ACS Appl. Mater. Interfaces 6, 5558–5565 (2014).

    CAS  ADS  Article  Google Scholar 

  45. 45

    Zhang, X. L. et al. Rational Design of a Tetrameric Protein to Enhance Interactions between Self-Assembled Fibers Gives Molecular Hydrogels. Angew. Chem.-Int. Edit. 51, 4388–4392 (2012).

    Article  Google Scholar 

  46. 46

    Raeburn, J. et al. Fmoc-diphenylalanine hydrogels: understanding the variability in reported mechanical properties. Soft Matter 8, 1168–1174 (2012).

    CAS  ADS  Article  Google Scholar 

  47. 47

    Huang, A. et al. In situ enzymatic formation of supramolecular nanofibers for efficiently killing cancer cells. RSC Adv. 6, 32519–32522 (2016).

    CAS  Article  Google Scholar 

  48. 48

    Caravan, P., Ellison, J. J., McMurry, T. J. & Lauffer, R. B. Gadolinium(III) Chelates as MRI Contrast Agents: Structure, Dynamics, and Applications. Chemical Reviews 99, 2293–2352 (1999).

    CAS  Article  Google Scholar 

  49. 49

    Xu, Q. et al. Gadolinium(III) chelated conjugated polymer as a potential MRI contrast agent. Polymer 51, 1336–1340 (2010).

    CAS  Article  Google Scholar 

  50. 50

    Bull, S. R., Guler, M. O., Bras, R. E., Meade, T. J. & Stupp, S. I. Self-Assembled Peptide Amphiphile Nanofibers Conjugated to MRI Contrast Agents. Nano Letters 5, 1–4 (2005).

    CAS  ADS  Article  Google Scholar 

  51. 51

    Ren, C., Zhang, J., Chen, M. & Yang, Z. Self-assembling small molecules for the detection of important analytes. Chem Soc Rev 43, 7257–7266 (2014).

    CAS  Article  Google Scholar 

  52. 52

    Peltier, R. et al. The rational design of a peptide-based hydrogel responsive to H2S. Chem Commun (Camb) 51, 17273–17276 (2015).

    CAS  Article  Google Scholar 

  53. 53

    Zhang, J. et al. Visualized detection of melamine in milk by supramolecular hydrogelations. Chem Commun (Camb) 50, 12873–12876 (2014).

    CAS  Article  Google Scholar 

  54. 54

    Bremmer, S. C., Chen, J., McNeil, A. J. & Soellner, M. B. A general method for detecting protease activity via gelation and its application to artificial clotting. Chem Commun (Camb) 48, 5482–5484 (2012).

    CAS  Article  Google Scholar 

  55. 55

    Ren, C. et al. When Molecular Probes Meet Self-Assembly: An Enhanced Quenching Effect. Angew. Chem.-Int. Edit. 54, 4823–4827 (2015).

    CAS  Article  Google Scholar 

Download references


This work is supported by International S&T Cooperation Program of China (ISTCP, 2015DFA50310), NSFC (31370964 and 51373079), Tianjin MSTC (15JCZDJC38100), and Program for Changjiang Scholars and Innovative Research Team in University (No. IRT13023).

Author information




J.T. Sun, Z.M. Yang, and M.S. Chen designed the project and wrote the paper, Y.Q. Hua, G.J. Pu, C.W. Ou, and X.L. Zhang conducted the experiments, L. Wang, Y.Q. Hua, and G.J. Pu analyzed the results and drew the figures.

Corresponding authors

Correspondence to Jiangtao Sun or Zhimou Yang or Minsheng Chen.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Hua, Y., Pu, G., Ou, C. et al. Gd(III)-induced Supramolecular Hydrogelation with Enhanced Magnetic Resonance Performance for Enzyme Detection. Sci Rep 7, 40172 (2017).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing