Organic molecules are currently investigated as redox species for aqueous low-cost redox flow batteries (RFBs). The envisioned features of using organic redox species are low cost and increased flexibility with respect to tailoring redox potential and solubility from molecular engineering of side groups on the organic redox-active species. In this paper 33, mainly quinone-based, compounds are studied experimentially in terms of pH dependent redox potential, solubility and stability, combined with single cell battery RFB tests on selected redox pairs. Data shows that both the solubility and redox potential are determined by the position of the side groups and only to a small extent by the number of side groups. Additionally, the chemical stability and possible degradation mechanisms leading to capacity loss over time are discussed. The main challenge for the development of all-organic RFBs is to identify a redox pair for the positive side with sufficiently high stability and redox potential that enables battery cell potentials above 1 V.
The widespread interest in replacing fossil fuels with renewable energy sources is a challenging task motivated by a need for energy independence and carbon footprint reduction. The cost of wind and photovoltaics electricity is still decreasing and will be integrated even more in a future fully renewable-based utility grid. However, this integration is faced with major challenges with respect to stability and security of supply because of the mismatch between electricity production and demand1. This can to some extent be solved by expansion of the transmission grid, intelligent demand-response schemes and storage/use of surplus electricity with heat pumps in reservoirs or pumped hydro2,3,4,5. Nonetheless, there will be a need for local/regional electricity storage5. Here batteries, which already are applied in the utility grid, are an obvious solution. However, a broader market penetration is critically dependent on the cost, which can be quantified by the levelized cost of electricity storage (LCES)6,7. In the simplest form it is given by , where LCES expresses the cost of storing and discharging one kWh in a cycle, CC are the capital costs per kWh, N the number of cycles during lifetime and η is the cycle efficiency8. Here capital cost in the range $120-$150 kWh−1 and a LCES of less than ¢10 kWh−1 cycle−1 is generally considered a breakthrough in energy storage9,10.
Recently, organic aqueous flow batteries have been proposed as a low-cost alternative to the present metal-based RFB technology11,12,13,14. Additionally, it is envisioned that the redox potential and solubility can be tailored by introduction of specific side groups on the organic redox-active species. The maximum allowable cost of organic redox species was studied in a scenario where a system capital cost for an aqueous RFB of $120 kWh−1 was targeted9. With moderately optimistic assumptions of $300 kW−1 for balance-of-plant/profit and flow cell cost normalised to internal resistance of 5 $ mΩ, it was shown that cell potentials of 1 V and 1.5 V result in a maximum acceptable costs of redox species of $4 kg−1 ($15 kAh−1) and $7 kg−1 ($26 kAh−1) respectively9. An interesting point here is that the redox species maximum allowable cost scales with the cell potential with a power greater than one. This is because not only the energy density increases with cell potential, but also cycle efficiency for a given internal flow cell resistance. Cost limits in the range $4 kg−1 ($15 kAh−1) and $7 kg−1 ($26 kAh−1) for organic redox species are not unrealistic. The base chemical cost for e.g. benzene is around $1.2 kg−1 while the cost of unsubstituted anthraquinone is $10–15 kAh−1 (see Supplementary, S9).
Figure 1 outlines an all-organic RFB13. It is based on 4,5-dihydroxy-1,3-benzenedisulfonate (HQ(1,2)DS) on the positive side (container A) and anthraquinone-2-sulfonate (AQ(2)S) on the negative (container B). During charging/discharging, two electrons are exchanged through an external circuit as HQ(1,2)DS and AQ(2)S is reduced and oxidized and two protons are exchanged through a Nafion membrane. It shows high coulombic efficiency, however the cell voltage is merely 0.7 V and significant capacity loss was observed due to chemical instability of the sulfonated hydroquinone13,15. Two other all-organic, radical based RFBs were recently demonstrated with a cell potential of 1.25 V14,16. They employ the organic radical TEMPOL (4-hydroxy-TEMPO) on the positive side and viologen on the negative side. In one of the studies, TEMPOL and viologen are bonded to water soluble polymers, which allows the use of a cheap Celgard separator14. However, at higher concentrations both systems lose capacity after only 100 cycles.
In addition to all-organic systems, RFBs that employ organics only on one side have been studied11,12. Here anthraquinone-2,7-disulfonic acid (AQDS(2,7)) and bromine in an acidic environment result in a cell voltage of 0.9 V, while 2,6-dihydroxy anthraquinone (AQDH(2,6)) and potassium ferricyanide in an alkaline environment results in a cell potential of 1.2 V11,12. A similar more recent advance is the use of an alloxazine-based (i.e. a vitamin B analogue) anolyte with ferrocyanide in an alkaline environment also producing a cell voltage of 1.2 V and high capacity retention17. Although discharge current densities in these RFBs are almost twice those observed for optimised vanadium RFBs, the maximum discharge power densities are about the same (0.4–0.6 W cm−2) because of the lower cell potentials18.
The possibility of tuning the solubility and redox potentials through substitutions of the side groups has recently been explored for quinones with density functional theory (DFT) calculations19,20. The results show that all-quinone aqueous RFBs with cell potential above 1.0 V is attainable by addition of electron withdrawing groups on hydroquinones and electron donating groups on anthraquinones.
However, so far there have been no systematic experimental studies of the actual change in redox potential and solubility with different functionalization. In the present study, we have experimentally determined redox potentials and aqueous solubility of 28 different benzo/hydroquinones (BQs), naphtoquinones (NQs) and anthraquinones (AQs) in acidic, neutral and alkaline solutions along with a few nitrogen based redox species. We discuss the limitations of their properties with respect to RFB performance and discuss some of the main challenges with respect to realising all-organic RFBs.
Figure 2 shows the structures of tested organic compounds as well as their abbreviations. In this work the denotation anthraquinone (AQ) is strictly the 9,10 isomer.
Cyclic voltammetry studies
The investigated compounds were used as-purchased and without any purification. Supplier data and purity are found in Supplementary, S4. Cyclic voltammograms (CVs) were recorded with a Chemical Instruments potentiostat (CHI660E) using a standard three-electrode configuration consisting of a 3 M KCl Ag/AgCl reference electrode (+0.210 VNHE) (CHI111), a platinum wire counter electrode (CHI115) and a homemade circular 1 mm glassy carbon (GC) electrode prepared as reported elsewhere21. For each series of CVs, a freshly polished electrode was used. The CVs for soluble compounds in 1 mM concentration were recorded in a glass beaker with a customized lid in nitrogen purged solutions of three different pHs, namely pH 0 (1 M H2SO4), pH 7 (0.5 M phosphate buffer) and pH 13 (1 M NaOH). The pH of the NaOH solution is taken as 13 to account for carbonization of the solution with exposure to air. A background CV was recorded before each CV experiment to exclude background contaminations. The CVs of insoluble compounds in 1 M H2SO4, or 0.5 M phosphate buffer were recorded as follows: 6 mL of the supporting electrolyte was mixed with approximately 4 mL of acetone, and then a small amount of the quinone was added so that its concentration was around 1 mM. When the concentration of water in the mixture with organic solvent is greater than 7.2 M (here it was around 30 M) the separation between first and second reduction peak becomes 0 V22. This procedure gives a fair estimate of the redox potential of the quinone at pHs where it is insoluble in water. All CVs are found in Supplementary, S6.
Each CV was analyzed in terms of peak potentials and peak currents. Peak currents were determined by subtracting a polynomial fit of the background from the recorded current as exemplified in Supplementary, S1. A plot of the absolute values of the peak currents to the square root of the scan rate was constructed and, when reasonable, a linear fit included to evaluate the electrochemical (Nernstian) reversibility of the electrochemical reaction. The peak current Ip for reversible reactions are given by equation (1) 23.
Where F is the Faraday constant, R the gas constant, T the temperature, n the number of electron transferred, A the area of the electrode, DOthe diffusion coefficient and CO*the bulk concentration of the analyte and v the scan rate. The peak current ratio is expected to be close to one for reversible species. The formal redox potential (E0’), which is the adjusted form of the standard redox potential, where effects of the medium is taken into account, is reported here as the midpoint potential between the two peak potentials in the CV24. All half-cell potentials in this work refer to the normal hydrogen electrode (VNHE). All derived CV and solubility data are found in Supplementary, S4 and S5.
A single 25 cm2 cell with carbon felt electrodes, graphite bipolar plates, copper current collectors and Nafion-117 ion exchange membrane was used. Prior to all battery tests the solutions were purged with nitrogen for 10 min and the tests were performed at room temperature. Carbon felt electrodes (4 mm thick, Sigracell) were pre-treated for one hour at 80 °C in H2SO4/HNO3 mixture (3:1 volumetric ratio) and then they were thoroughly washed with demineralized water. Nafion-117 was pre-treated in a following way: i) boiled for 30 min in 3% H2O2 aqueous solution, ii) washed with milliQ water and iii) left for one hour in 1 M H2SO4, phosphate buffer or KOH, depending on the pH value of the solution during RFB test. To assemble the cell, current collectors were screwed together by 6–11 bolts with bipolar plates, electrodes and Teflon + silicon gaskets in between. Two Grundfos DDA pumps circulated the electrolyte at a flow rate of 100 mL/min using Teflon tubing. The current was maintained constant at +/− 200 mA during tests using a Neware Battery Testing System CT-3008-5V3A-S1 (Shenzhen, China).
Aqueous solubility estimation
Aqueous solubility (OECD test #105) was estimated in 1 M H2SO4, 1 M KCl and 1 M KOH prepared from MilliQ water25. Around 0.10 g of the pulverized compound was transferred to a glass tube after which increasing volumes of the supporting electrolyte solution was added in intervals of 10–100 μL depending on the expected solubility. After each addition the test tube was ultrasonicated and/or shaken vigorously using a Vortex Generator for at least 10 minutes at room temperature. Then the tube was inspected visually for undissolved sample and the addition of supporting electrolyte solution continued until the sample seemed just dissolved. The volumes just before and after full dissolution are used for calculating the solubility interval (Supplementary, S4 and S5) and the solubility is estimated as the average between the two. Addition of water was terminated when the solubility of the compound was less than 10 mM. Dissolved samples were left to stand for 12 hours and visually inspected for thixotropy using a vortex generator. For very insoluble compounds the amount of sample was decreased to 0.01 g and the dissolution time increased up to 24 h.
Results and Discussion
The electrochemical reaction of quinones in aqueous media
Quinones generally undergo a reversible two-electron reduction/oxidation. The redox potential is strongly pH dependent, as the reaction may or may not involve two protons as illustrated in the scheme-of-squares mechanistic pathway in Fig. 3 26. At pH < pKa1, the reaction includes two protons and thus E0’ decreases with 59 mV per pH unit (at 25 °C)24. At pKa1 < pH < pKa2 and pKa2 < pH only one and no protons are involved, whereby E0’ decreases with 30 and 0 mV per pH unit, respectively. Generally, the reactions that include protons are slower and result in a lower electrochemical rate constant (k0) and may ultimately lead to higher charge-transfer resistance in the RFB. Thus, the choice of pH in the RFB environment strongly influences quinone electrochemical performance.
E0’ of anthraquinone derivatives
Figure 4 shows the experimental E0’ at three different pH values for all quinones in the study. Figure 5 shows a more detailed Pourbaix diagrams of selected AQ species, where it is seen that E0’ of unsubstituted AQ is about 300 mV lower than that of HQ(1,4) at pH 0. This illustrates that AQs are inherently electron rich species with redox potentials that are generally lower than those of the BQs, because unsubstituted AQ is in fact a BQ substituted with two benzene groups. In a recent DFT studies on a large ensample of quinones with various functional groups, it was found that it should be possible to change the standard redox potential from as high as 0.6 VNHE to −1.5 VNHE19,20. Functional groups such as halogens, sulfonate or carboxyl groups were considered as electron withdrawing groups (EWGs) and hydroxyl and methyl groups as electron donating groups (EDGs). In this sense, higher redox potential would be expected for AQs with EWDs such as sulfonated AQs and lower for hydroxylated due to electron donation/withdrawal19. Nonetheless, the experimental data presented in Fig. 4 does not reproduce the full impact of this trend. It is seen that for sulfonated AQs, E0’ is only about 200 mV–300 mV higher than that of hydroxylated ones. Additionally, the position of sulfonate groups is very important, while the number seems to have very little effect. For instance, the two sulfonate groups in the edge positions in AQDS(2,7) decrease E0’ compared to the parent AQ from + 0.4 VNHE,pH=0 to + 0.165 VNHE,pH=0. Almost the same effect on E0’ is observed with only one sulfonate group in AQS(2), which has E0’ of + 0.163 VNHE,pH=0, indicating that sulfonate groups behave as EDGs by decreasing the potential, not as EWGs as expected. Changing only the positions of the sulfonate groups lowers the potential even further, by about 400 mV to + 0.03 VNHE,pH=0 for AQDS(1,8) and −0.03 VNHE,pH=0 for AQDS(1,5). This leads to the conclusion that when substituting with sulfonate groups, there is a higher electron donating effect in positions 1, 5 and 8 close to the quinone groups, while it is less pronounced in edge positions 2,7. This is also the case for edge position 6, as E0’ for AQDS(2,6) is around +0.166 VNHE,pH=026.
Addition of two hydroxyl groups to the mono-sulfonated AQS(2) to give AQS(2)DH lowers E0’ to +0.015 VNHE,pH=0 indicating that the electron donating effect of hydroxyl groups is larger than that of one sulfonate group and similar to sulfonate group substitution closer to the quinone. Addition of one bromo and one amino group on the mono-sulfonated AQ to AQS(2)NBr lowers E0’ by only 20 mV at pH 0 indicating very small overall effect by these groups.
E0’ for the hydroxylated AQs is around 0 VNHE,pH=0, −0.4 VNHE,pH=7 and −0.6 VNHE,pH=13 and the variation is limited. Compared to E0’ of unsubstituted AQ of + 0.4 VNHE,pH=0, 0 VNHE,pH=7 and an estimated −0.4 VNHE,pH=13 (by extrapolation in Fig. 5), the electron donating effect of hydroxyl groups on AQ decreases E0’ by 200 mV–400 mV depending on pH. Again the experimental data here does not reproduce the large effect on E0’ expected from theoretical calculations. Addition of more hydroxyl groups does not lower the potential significantly, though the number of hydroxyl groups slightly affects E0’ in alkaline, which agrees well with DFT calculations19. For example, the tetrahydroxylated AQTH(1,4) has approximately 100 mV more negative E0’ compared to AQDH(1,4), but none have more negative E0’ than AQDH(2,6) at −0.70 VNHE,pH=13. AQDH(1,2) has an E0’ of −0.67 VNHE,pH=13, very similar to AQDH(2,6) indicating the importance of having a hydroxyl group in an edge position in order to reach the most negative potential. It is quite similar to AQTrH M which has three hydroxyl groups on the AQ (one edge group) and a methyl group on the edge giving E0’ of −0.69 VNHE,pH=13.
Similarly to sulfonated AQs, the positions of the hydroxyl groups affect E0’, but in acidic only to a small extent. Comparing dihydroxylated AQs, the two hydroxyl groups in AQDH(2,6) gives the most positive potential, of +0.04 VNHE,pH=0 while AQDH(1,5) and AQDH(1,8) is most negative (just below 0 VNHE,pH=0). In alkaline, E0’ of the hydroxylated AQs varies much more with position, by 200 mV from about −0.50 VNHE,pH=13 for AQDH(1,4), AQDH(1,8) and AQDH(1,5) to −0.70 VNHE,pH=13 for AQDH(2,6). The three former all have the hydroxyl groups on positions close to the quinone groups. The difference in E0’ for these hydroxylated AQs and others may be found in the pKa values of the central (hydro)quinone groups. Those are not trivial to measure given the insolubility at lower pH values for hydroxylated AQs, but they can be estimated from the Pourbaix diagram in Fig. 5 24,26. For instance, in the Pourbaix diagram of AQDS(2,7), E0’ follows the expected −59 mv/pH unit from pH 0 to pH 7 (pKa1). Then the first (hydro)quinone group deprotonates, and the slope changes to 30 mV/pH unit until pH 10 (pKa2) and E0’ becomes pH-independent. AQDH(1,8) shows a different dependence, where pKa1 is somewhere around pH 4 and pKa2 above pH 13. AQDH(2,6) shows an even more different behaviour as E0’ follows −59 mV/pH unit dependence straight to pH 13, which implies that both pKa values are higher than 13. The difference in protonation behaviour explains the observed more negative E0’ for AQDH(2,6) compared to AQDH(1,8) since it is only at higher pH than pKa1 of AQDH(1,8) around pH 4 that E0’ deviates between the compounds. Thus, if one can predict or measure reasonable values for these pKa values, it should be possible to predict which ones will have a more negative or positive E0’ at higher pH.
Taken together, it thus appears that the magnitude of the negative potentials that can be reached by hydroxyl group substitution is limited to about −0.7 VNHE,pH=13 and redox potentials below −1 VNHE,pH=13 appear unlikely. This is in good agreement with experimentally obtained E0’ of around −0.7 VNHE,pH=13 for hexahydroxy anthraquinone27. Irrespective of pH, EWGs placed on the edge of the dihydroxylated AQ do not alter E0’. This can be seen by comparing AQDH(4,5)CA with other AQDHs which have hydroxyl groups in similar positions. E0’ of AQDH(4,5)CA is around −0.53 VNHE,pH=13, which is similar to the other dihydroxylated AQs with hydroxyl groups in positions close to the quinone groups. Additionally, AQS(2)DH has both a hydroxyl and a sulfonate group in edge positions, and E0’ of +0.07 VNHE,pH=0 and −0.69 VNHE,pH=13, very close to that of AQDH(2,6). It virtually behaves as there is no EWG group.
E0’ of naphtoquinone and benzoquinone derivatives
Of the tested naphthoquinones, NQ(1,2)S show the highest E0’ of +0.6 VNHE,pH=0. The halogenated and hydroxylated NQ(1,4)DHDCl are electrochemically irreversible. Interestingly, the addition of one hydroxyl group in the case of NQ(1,4)H and NQ(1,4)HB shifts E0’ in alkaline by 0.8 V, to around −0.5 VNHE,pH=13, which gives a slope of 67 mV/pH unit. This is higher than observed for AQs, and lower than BQs, as will be described later. The potentials of NQs in alkaline are sufficiently negative for use as anolyte, provided sufficient solubility and stability can be reached.
It can be seen from Fig. 4 that ortho-BQs in general have an E0’ almost 100 mV higher compared to para-BQs. The most interesting results are the effect of substituting these two parent BQs with EWGs, and its implication on chemical stability. Although DFT calculations suggest that sulfonate group substitution on para-BQ should change E0’ by +100 mV, such an electron withdrawing effect was not observed experimentally as seen from HQ(1,4) and HQ(1,4)S where the opposite tendency is seen19. Similarly, the two sulfonate groups on ortho-BQ in HQ(1,2)DS increases E0’ by only +50 mV, which is less than predicted. The halogens, e.g. four fluoro or chloro groups (EWGs) on HQ(1,4)TC and HQ(1,4)TF show very small effect on the potential, which is in good agreement with the DFT calculations19. However, halogen substituents are prone to the nucleophilic attack of/in water and substitution reactions28. This can be verified by comparing the chemically irreversible CVs at pH 13 (Supplementary, S6, Figs 31 and 33). Chemical instability in water has also been reported for other benzoquinones, e.g. tetracyano benzoquinone29. E0’ was estimated to be +0.3 V higher than that of dicyano dichloro benzoquinone, which has E0´ of 0.9 VNHE, and also readily reacts with water30. Another example of a high-potential but very reactive benzoquinone is tetracarboxyl para benzoquinone which decomposes after synthesis and has a calculated standard potential of above +1 VNHE19,31. From the BQ CVs (Supplementary, Figures 25–33) they all generally appear (electro)chemically unstable in water.
Hydroxylation and methylation should affect E0’ towards more negative values19. Two hydroxyl groups on HQ(1,4)DH reduce E0’ by 300 mV at pH 0 compared to the parent BQ compound. Further reduction of E0 by substitution with more hydroxyl groups lowers the electrochemical reversibility. This is exemplified by BQ(1,4)TH which completely loses its electrochemical activity (Supplementary, S6, Figure 32). Other EDGs do not cause this instability, as BQ substituted with four methyl groups (duroquinone) has been reported to remain electrochemically reversible and chemically stable, with a potential of 0.5 VNHE in aqueous (acidic and neutral) solutions32. Many methylated and alkylated BQs are natural compounds, i.e. Coenzyme Q10 (ubiquinone), duroquinone or plastoquinone. Generally, it appears that fully methyl and alkyl group substituted BQs are chemically stable in water, but this comes at the cost of a low E0’ and very low solubility.
Perhaps the most interesting effect from hydroxyl groups on BQs is their effect on the pH dependence of E0’. With just two hydroxyl groups in BQ(1,4)DH, E0’ changes from +0.38 VNHE,pH=0 to −0.73 VNHE,pH=13 corresponding to almost −90 mV/pH unit change. For para-BQ it changes from +0.70 VNHE,pH=0 to +0.11 VNHE,pH=13, and is only half (−45 mV/pH unit). This suggests that one of the two hydroxyl substituents also protonates/deprotonates in the electrochemical reaction adding around −30 mV/pH unit to the −59 mV/pH unit ending up at the total of −90 mV/pH unit. A similar effect is observed for BQ(1,4)DHDCl where the potential changes by 0.99 V for 13 pH units, which corresponds to −76 mV/pH unit. Both species have large negative E0’ in alkaline, −0.73 VNHE,pH=13 for the former and −0.60 VNHE,pH=13, for the latter. This suggests that E0’ is more affected by the pH of the supporting electrolyte than expected. To our knowledge this has not been described or explained in literature and it leads to the surprising conclusion that the E0’ of BQs are in the range, and in some cases even more negative than of those of AQs in alkaline. This could make them possible to use as anolytes in alkaline, provided it is possible to achieve fair aqueous solubility and in particular chemical stability.
Chemical stability of organics in RFBs
The chemical stability of redox couples in RFBs is very important, since low life-time leads to impractical systems and increased LCES. By introducing organic molecules in high concentrations in oxidative/reductive environments, the possibility of (electro)chemical side reactions increases compared to state-of-the-art inorganic RFBs.
Figure 6 shows single cell flow battery tests of selected organic redox species mainly illustrating the challenges associated with stability of smaller, unsubstituted quinones. In Fig. 6a and b, a hydroxylated and sulfonated NQ are used on the negative side and fast, gradual capacity loss is seen. In Fig. 6c and d two possibilities for a small organic species for the positive side is tested and here capacity loss is observed after a small number of cycles. Generally, capacity loss in flow batteries can be attributed to redox species crossover through the membrane, oxidation from the outside environment and chemical degradation of redox species. Here major external oxidation is not likely since sealed and purged containers are used. Furthermore, a dense and highly selective Nafion membrane was used in all RFB tests displayed in Fig. 6 and crossover has been shown to be unlikely for the relatively large quinone molecules (HQ(1,2)DS, AQDS(2,7) and AQDH(2,6))11,12,15. For this reason we attribute the capacity loss to chemical degradation of the organic redox species. The interpretation is substantiated by considering the CVs of e.g. HQ(1,2)DS and HQ(1,4)S. At all pH values they show significantly low reduction/oxidation peak ratio, which indicate a fast side-reaction that follows the electrochemical oxidation (Supplementary, S6, Figure 25 and 28) and creates non-electroactive species. According to recent work, HQ(1,2)DS transforms to the tri- and tetrahydroxylated versions shortly after the oxidation to the quinone form, since water performs a Michael addition (1,4 to the α-β unsaturated carbonyl compound) as exemplified in Fig. 7a 15.
The multi-hydroxylated quinones are usually found to be electrochemically irreversible and/or insoluble. In the case of increasing the pH, a stronger nucleophile (OH−) is predominant and thus the reduction/oxidation peak ratio is even smaller than in acidic and neutral solution. This is confirmed further in an RFB battery tests in Fig. 6c, where an acidic all-organic RFB with HQ(1,4)S loses half of its capacity after only 30 cycles.
NQ(1,4)H has a E0’ of −0.5 VNHE,pH=13 and seemingly reversible CV (Supplementary, S6, Figure 13) in addition to being soluble in 1 M KOH making it is a fairly good anolyte candidate. However, RFB test shows significant capacity loss over time (Fig. 6a). Possible side-reactions includes a Michael-like conjugated addition of hydroxyl as in Fig. 7a for the sulfonated benzoquinone on the unsubstituted position (3), while the rest are protected by the benzene ring. In addition, an oxygen-sensitive possibility can be identified from the literature being the epoxidation with the hydroperoxide anion33. Epoxidation is usually followed by a nucleophilic attack here creating a non-aromatic and electrochemically irreversible hydroxylated species (Fig. 7b)34:
In practical RFB setups, there is always a risk of contamination with small amounts of oxygen which in the case of hydroquinones creates extremely reactive superoxides and usually hydrogen peroxide. Hydrogen peroxide, and the hydrogen peroxide anion created from it in alkaline solutions, are even better nucleophiles than the hydroxide ion itself. In addition, superoxides can oxidize a range of substituents and side groups. The formation is described in Fig. 7c.
Another example is an RFB test with NQ(1,2)S shown in Fig. 6b that also suffers from significant capacity loss. Here data indicates that the degradation process involves formation of a new redox active species giving a cell voltage of 0.9 V with ferrocyanide as seen from the main panel. This corresponds to the NQ compound having transformed to an electroactive hydroxylated form. Two possibilities can be readily identified, namely the addition of a hydroxyl group in position 3 in a Michael-like conjugated addition as earlier described in Fig. 7a or a nucleophilic substitution as that suggested in Fig. 7d 35. This reaction indicates how OH− is a stronger nucleophile than water as its conjugate base pair and is able to substitute the usually bad leaving group sulfonate (see Fig. 7a for comparison in acidic media). The following capacity loss is then explained as in the case of NQ(1,4)H by further hydroxylation to electrochemically inactive species.
Obviously, there are stability issues with organic redox species and in particular with partially substituted quinones (NQs and BQs). The quinone contains a ketone functional group and a carbon-carbon double bond next to it (α,β unsaturated ketone). Because of the electron withdrawing property of the ketone, this double bond is prone to react with nucleophiles, while hydroquinone is a phenol derivative (aromatic) so because of the structural differences of these two compounds, they behave differently. Generally, small aromatic rings (e.g. the hydroquinone) are nucleophilic, so they are prone to react with electrophiles34. There is a difference in reactivity between the charged and discharged species: the phenolate form – as a conjugate base pair of the phenol – is a stronger nucleophile so in basic condition it reacts with quinones if it is sterically allowed. A range of nucleophilic reactions of quinones are available in the literature36. Nucleophiles such as H2O and hydroxyl ions are predominant in the RFB environment, especially in an alkaline solution so it is likely that the nucleophilic substitution of the quinone will be the greatest challenge in quinone stability28,33. In alkaline solution e.g. a sulfonate group can be substituted by a hydroxyl group as exemplified by the reaction in Fig. 7d while in acidic solution the same reaction can take place with water, but since the hydroxyl group is stronger nucleophile than water, the reaction is slower and the Michael-addition of Fig. 7a is more likely28.
Consequently, quinones with possible leaving groups and unsubstituted sites are likely to be unstable in aqueous solutions, however, the degradation reaction rate depends on the specific supporting electrolyte. A further complication is that as both oxidation states are present in the battery during operation and hydroquinones can act as nucleophiles and react with the benzoquinones, there can be unwanted polymerizations at both low and high pH37,38. Thus, when considering stability the use of only partially substituted BQs and NQs and those substituted with possible leaving groups in aqueous RFBs is very limited.
As an alternative to quinones, the nitroxide radical TEMPOL, was tested. It has reversible CVs at pH 7, and no degradation even after 30 days in aqueous buffer in the uncharged state (Supplementary, S7). However, in a great number of RFB battery tests of which an example seen in Fig. 6d, it performed well for only a limited number of cycles, after which significant capacity loss was observed, even at low concentrations. This behaviour is similar to previous studies16,14. It has been shown that the similar TEMPO radical disproportionates to the N-oxo ammonium salt in warm acidic water and further on to the hydroxylamine with the possibility of further dimerization39: While the temperatures in the RFB environment are generally lower than those studied, it is plausible that the TEMPOL radical reacts in a similar manner after a couple of cycles, which would explain the capacity loss observed in Fig. 6d. A few other nitrogen-containing redox active species (Fig. 2 and Supplementary, S7) were included. The general conclusion from this data is that the pyrazine-derived heteroaromatics are only seemingly stable only at pH values between 0 and 3 and have quite negative potentials.
Aqueous solubility of quinones in different supporting electrolytes
Potentially, an all-quinone RFB can reach the same energy density (30 WhL−1) as the vanadium RFB given a cell potential of 1 V and a solubility of 1 M40. Apart from some of the sulfonated anthraquinones/benzoquinones, the properties of quinones in aqueous solution is that of weak acids or salts of weak acids and strong bases. In that case their solubility can be described by the Henderson–Hasselbalch equation41:
The total concentration of species dissolved in water (Stot) is the sum of the concentration of dissociated species ([A−]) and the non-dissociated species ([HA]). If [HA] is replaced with the intrinsic solubility of the species (S0) from above, and [A−] = Stot − S0, the total solubility can be presented as41:
by rearranging equation 2. From equation 3, one can conclude that solubility/miscibility of the quinones in/with water can be further enhanced if the substituent groups dissociate in water, i.e. their pKa values are low and preferably the pH is high. In this report, the aqueous solubility of the chemicals was measured as-received. In the case of the BQs many of them are in hydroquinone form, which gives higher solubility compared to the quinone form. For instance it is expected that HQ(1,4)TF or HQ(1,2) have very low solubility in water in their benzoquinone form. Figure 8 show that quinones tested in this work in general do not show aqueous solubility greater than 1.6 M (HQ(1,2)), in any supporting electrolyte. One would expect a decreasing maximum solubility with the molar mass, since the dissolved mass and volume of the molecules becomes comparable to that of water. However, such behaviour cannot be clearly observed from Fig. 8 especially given the high solubility of AQDS(2,7).
The solubilites of all quinones are shown in Fig. 9 sorted by quinone type and functional groups. The general trend is that sulfonated quinones have high solubility in all supporting electrolytes, while the hydroxylated are soluble only in alkaline. This is reasonable, as hydroxyl groups in general have much higher pKa values, so higher pH is needed to deprotonate them to salts. Most halogen substituted quinones, exemplified by AQS(2)NBr, HQ(1,4)TC, BQ(1,4)DCDH and NQ(1,4)DHDC, are insoluble in water and limits their practical use in aqueous flow batteries.
The solubility of all of the sulfonated AQs is lower in 1 M KCl and KOH than in 1 M H2SO4. Considering the sulfonate group position, AQDS(2,7) is the most soluble followed by AQS(2) while AQDS(1,8) and AQDS(1,5) shows more than ten times lower solubility. For these compounds, solubility and redox potential follow the same trend where solubility increases with E0’. With addition of hydroxyl or halogen groups to sulfonated AQs, i.e. AQS(2)DH and AQS(2)NBr, the compounds become barely soluble in 1 M H2SO4 and almost insoluble in 1 M KCl. The two hydroxyl groups on AQS(2)DH does however considerably increase solubility in 1 M KOH.
Hydroxylated AQs are almost insoluble in 1 M H2SO4 and KCl which limits their practical use to only alkaline RFBs. This also indicates that S0 for these compounds is low, and that the solubility in alkaline is almost entirely related to the pKa of the substituent groups. Changing the hydroxyl group positions to 1,4,5 and 8 in AQDHs dramatically reduces the solubility, this is the same trend as observed for sulfonated AQs. In general, whenever the edge substituent is a hydroxyl group, the solubility is between 0.5 and 0.7 M.
The highest solubility observed in alkaline is for the trihydroxylated and methylated AQTrHM. When substituting the otherwise insoluble AQDH(1,8) with carboxylate or hydroxymethyl on the edge groups, the solubility increases to above 0.3 M. A higher number of hydroxyl groups can reduce the solubility in alkaline, as exemplified by AQTH(1,4), with four hydroxyl groups, which has only half the solubility compared to AQDH(1,4). However, this effect is not observed for AQTH(1,2), which again underlines the importance of edge group substitution compared to positions closer to the ring.
NQs are more soluble in alkaline than AQs. NQ(1,2)S has high solubility of 0.9 M, while NQ(1,4)H has solubility of 0.82 M, Interestingly, addition of the large butenyl group on NQ(1,4)H in NQ(1,4)HB only slightly reduces the solubility to 0.70 M in alkaline.
Thixotropy of AQs
When performing solubility tests, thixotropy was observed for a number of compounds42. In practical RFBs thixotropy is not wanted, as the redox solutions can be kept still for long times. Samples were observed to dissolve well in the supporting electrolyte under agitation, but when left for hours it turned into a thick paste that could be brought back to the liquid state by repeated agitation. This was most notably observed for AQDS(2,7) in all supporting electrolytes (tested in the disodium form as received) and for a number of hydroxylated AQs in 1 M KOH solution (namely AQS(2)DH, AQDH(1,4), AQDH(1,2), AQDH(1,8)MH, AQDH(4,5)CA). Thixotropy of AQ dyes in aqueous dispersions has been described earlier, as well as some methods to overcome the problem such as addition of polyvinylpyrrolidone to the solution43.
Conclusions & future perspectives
By combining the quinones with the highest and lowest E0’ (HQ(1,2)DS and AQTH) a hypothetical cell potential for an all-quinone RFB can be as high as 1.1 V at pH 7, while at pH 0 and 13 it could be around 0.9 V. A cell potential in between 0.9 V and 1.1 V provide fair energy density of an RFB, provided the compounds on both sides have sufficient water solubility (>1 M) and chemical stability.
Currently, only semi-organic RFBs appear feasible, since many AQ derivatives have sufficiently low E0’ for the negative side together with high solubility and seemingly high chemical stability, while the positive side remains a challenge. Both sulfonated and hydroxylated AQs, which are low cost compounds used in large quantities in the dye industry, are examples of promising anolytes, however future studies are needed to determine their long term stability.
Most AQ derivatives have a negative E0’ with a rather narrow variation between different functionalized derivatives. This behaviour is not fully predicted by DFT calculations and it is doubtful whether redox potential improvements to the already reported AQs, AQDS(2,7) and AQDH(2,6) for use as anolytes in aqueous RFBs can be realised. The solubility of AQDH(2,6) might be improved by further functionalization in the edge positions.
The experimental data presented here, together with existing work in literature, shows that the main challenge is to develop highly soluble and chemically stable organic redox species for the positive side with a sufficiently high E0’ that would enable a cell potential >1 V. Benzoquinones generally have the most positive E0’ from around +0.4 to +1.2 VNHE,pH=0. However, currently known BQs with high E0’ are not stable in aqueous solutions which is exemplified by most studied BQs in this work.
While it is clear that functional groups are needed to enhance the solubility and chemical stability of benzoquinone compounds and obtain the desired redox potential for practical applications, the experimental data here shows that this functionalization is not simple, and could possibly add significantly to the BQs costs. A way of addressing the stability issue could be synthesis of fully substituted BQs with more stable C-R or C-C-R bonds, where R is a functional substituent i.e. hydroxyl, sulfonate or other groups (e.g. phosphates) that increases solubility and does not compromise the redox potential. An alternative approach is water soluble polymers with immobilized and fully substituted benzoquinone species as has been attempted with the TEMPOL radical.
How to cite this article: Wedege, K. et al. Organic Redox Species in Aqueous Flow Batteries: Redox Potentials, Chemical Stability and Solubility. Sci. Rep. 6, 39101; doi: 10.1038/srep39101 (2016).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Heide, D. et al. Seasonal optimal mix of wind and solar power in a future, highly renewable Europe. Renewable Energy 35, 2483–2489 (2010).
Stuggins, G., Sharabaroff, A. & Semikolenova, Y. Energy efficiency: Lessons learned from success stories. https://openknowledge.worldbank.org/handle/10986/12236 (The World Bank, 2013).
Agora Energiewende. Energy Transition in the Power Sector in Europe: State of Affairs in 2015. https://www.agora-energiewende.de/fileadmin/Projekte/2016/EU-Review_2015/Agora_State_of_Affairs_EU_2015_WEB.pdf (2016).
Rodríguez, R. A., Becker, S., Andresen, G. B., Heide, D. & Greiner, M. Transmission needs across a fully renewable European power system. Renewable Energy 63, 467–476 (2014).
Heide, D., Greiner, M., von Bremen, L. & Hoffmann, C. Reduced storage and balancing needs in a fully renewable European power system with excess wind and solar power generation. Renewable Energy 36, 2515–2523 (2011).
Yang, Z. G. et al. Electrochemical Energy Storage for Green Grid. Chem. Rev. 111, 3577–3613 (2011).
Dunn, B., Kamath, H. & Tarascon, J.-M. Electrical Energy Storage for the Grid: A Battery of Choices. Science 334, 928–935 (2011).
Pawel, I. The Cost of Storage – How to Calculate the Levelized Cost of Stored Energy (LCOE) and Applications to Renewable Energy Generation. Energy Procedia 46, 68–77 (2014).
Darling, R. M., Gallagher, K. G., Kowalski, J. A., Ha, S. & Brushett, F. R. Pathways to low-cost electrochemical energy storage: a comparison of aqueous and nonaqueous flow batteries. Energy & Environmental Science 7, 3459–3477 (2014).
U.S. Department of Energy. Grid Energy Storage, http://energy.gov/oe/downloads/grid-energy-storage-december-2013 (2013).
Huskinson, B. et al. A metal-free organic-inorganic aqueous flow battery. Nature 505, 195–198 (2014).
Lin, K. et al. Alkaline quinone flow battery. Science Magazine 349, 1529–1532 (2015).
Yang, B., Hoober-Burkhardt, L., Wang, F., Prakash, G. & Narayanan, S. An Inexpensive Aqueous Flow Battery for Large-Scale Electrical Energy Storage Based on Water-Soluble Organic Redox Couples. Journal of the Electrochemical Society 161, A1371–A1380 (2014).
Janoschka, T. et al. An aqueous, polymer-based redox-flow battery using non-corrosive, safe, and low-cost materials. Nature 527, 78–81 (2015).
Yang, B. et al. High-Performance Aqueous Organic Flow Battery with Quinone-Based Redox Couples at Both Electrodes. Journal of The Electrochemical Society 163 (2016).
Liu, T., Wei, X., Nie, Z., Sprenkle, V. & Wang, W. A Total Organic Aqueous Redox Flow Battery Employing a Low Cost and Sustainable Methyl Viologen Anolyte and 4-HO-TEMPO Catholyte. Advanced Energy Materials 6, 1501449 (2016).
Lin, K. et al. A redox-flow battery with an alloxazine-based organic electrolyte. Nature Energy 1, 16102 (2016).
Aaron, D. S. et al. Dramatic performance gains in vanadium redox flow batteries through modified cell architecture. Journal of Power Sources 206, 450–453 (2012).
Er, S., Suh, C., Marshak, M. & Aspuru-Guzik, A. Computational design of molecules for an all-quinone redox flow battery. Chemical Science 6, 885–893 (2015).
Bachman, J. E., Curtiss, L. A. & Assary, R. S. Investigation of the Redox Chemistry of Anthraquinone Derivatives Using Density Functional Theory. The Journal of Physical Chemistry A 118, 8852–8860 (2014).
Chernyy, S. et al. Elucidation of the Mechanism of Redox Grafting of Diazotated Anthraquinone. Langmuir 28, 9573–9582 (2012).
Hui, Y., Chng, E. L. K., Chng, C. Y. L., Poh, H. L. & Webster, R. D. Hydrogen-Bonding Interactions between Water and the One- and Two-Electron-Reduced Forms of Vitamin K1: Applying Quinone Electrochemistry To Determine the Moisture Content of Non-Aqueous Solvents. Journal of the American Chemical Society 131, 1523–1534 (2009).
Bard, A. J. & Faulkner, L. R. Potential Sweep Methods In Electrochemical Methods: Fundamentals and Applications (2nd edn.) 231 (Wiley, 2001).
Compton, R. & Banks, C. Cyclic Voltammetry at Macroelectrode In Understanding Voltammetry. (2nd edn) 131 (Imperial College Press, 2011).
OECD Publishing. OECD guidelines for the testing of chemicals, Section 105 http://www.oecd-ilibrary.org/docserver/download/9710501e.pdf?expires=1471436169&id=id&accname=guest&checksum=5D8FDD03F4036447E795D082FDBCCC55 (1995).
Batchelor-McAuley, C., Li, Q., Dapin, S. M. & Compton, R. G. Voltammetric Characterization of DNA Intercalators across the Full pH Range: Anthraquinone-2,6-disulfonate and Anthraquinone-2-sulfonate. The Journal of Physical Chemistry B 114 (2010).
Bechtold, T., Fitz-Binder, C. & Turcanu, A. Electrochemical characteristics and dyeing properties of selected 9,10-anthraquinones as mediators for the indirect cathodic reduction of dyes. Dyes and Pigments 87, 194–203 (2010).
Tandon, V. K. & Maurya, H. K. ‘On water’: unprecedented nucleophilic substitution and addition reactions with 1,4-quinones in aqueous suspension. Tetrahedron Letters 50, 5896–5902 (2009).
Vazquez, C., Calabrese, J. C., Dixon, D. A. & Miller, J. S. Cyanil. Synthesis and characterization of the strongest isolated electron acceptor and its reduced forms. The Journal of Organic Chemistry 58, 65–81 (1993).
Walker, D. & Hiebert, J. D. 2,3-Dichloro-5,6-dicyanobenzoquinone and Its Reactions. Chemical Reviews 67, 153–195 (1967).
Hammond, P. R. 1,4-Benzoquinone Tetracarboxylic Acid Dianhydride, C1008:A Strong Acceptor. Science 142, 502–502 (1963).
Alt, H., Binder, H., Klempert, G., Köhling, A. & Sandstede, G. Evaluation of organic battery electrodes: Voltammetric study of the redox behaviour of solid quinones. Journal of Applied Electrochemistry 2, 193–200 (1972).
Brunmark, A. & Cadenas, E. Redox and addition chemistry of quinoid compounds and its biological implications. Free Radical Biology and Medicine 7, 435–477, (1989).
Clayden, J., Greeves, N. & Warren, S. Conjugate addition and nucleophilic aromatic substitution In Organic Chemistry (2nd edn.) 514 (Oxford University Press, 2001).
Fieser, L. A comparison of heterocyclic systems with benzene I 6,7-Indazolequinone-4-sulfonic acid. Journal of the American Chemical Society 48, 1097–1107 (1926).
Kutyrev, A. A. Nucleophilic reactions of quinones. Tetrahedron 47, 8043–8065 (1991).
Sabaa, M. W., Madkour, T. M. & Yassin, A. A. Polymerization products of p-Benzoquinone as bound antioxidants for styrene-butadiene rubber: Part I—Preparation of quinone polymers. Polymer Degradation and Stability 22, 195–203 (1988).
Ragimov, A. V., Mamedov, B. A. & Liogon’kii, B. I. The alkali initiated polymerization of p-benzoquinone. Polymer Science U.S.S.R. 19, 2922–2928 (1977).
Ma, Y., Loyns, C., Price, P. & Chechik, V. Thermal decay of TEMPO in acidic media via an N-oxoammonium salt intermediate. Organic & Biomolecular Chemistry 9 (2011).
Yang, Y., Zheng, G. & Cui, Y. A membrane-free lithium/polysulfide semi-liquid battery for large-scale energy storage. Energy & Environmental Science 6 (2013).
Ghosh, T. K. & Jasti, B. R. Theory and Practice of Contemporary Pharmaceutics. (Taylor & Francis, 2004).
Barnes, H. A. Thixotropy—a review. Journal of Non-Newtonian Fluid Mechanics 70, 1–33 (1997).
Moran, A. E. & Earl, K. Vat dye dispersions containing polyvinylpyrrolidone. United States Patent Office 2971812 (1961).
We would like to acknowledge the Department of Chemistry at Aarhus University for the use of GC electrodes and procurement of AQTH(1,2). We thank A. M. Kalvig for use of TEMPOL stability data. K. Wedege is grateful to the Danish Council for Independent Research, Technology & Production (Grant no. DFF–4005-00517) and E. Drazevic to the Marie Sklodowska-Curie Individual Fellowship (H2020-MSCA-IF-2014, grant number 657041).
The authors declare no competing financial interests.
Electronic supplementary material
About this article
Cite this article
Wedege, K., Dražević, E., Konya, D. et al. Organic Redox Species in Aqueous Flow Batteries: Redox Potentials, Chemical Stability and Solubility. Sci Rep 6, 39101 (2016). https://doi.org/10.1038/srep39101
Tailoring Dihydroxyphthalazines to Enable Their Stable and Efficient Use in the Catholyte of Aqueous Redox Flow Batteries
Chemistry of Materials (2020)
Journal of The Electrochemical Society (2020)
IOP Conference Series: Materials Science and Engineering (2020)
ACS Applied Energy Materials (2020)
Chemical Research in Chinese Universities (2020)