Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Super-Resolution Imaging at Mid-Infrared Waveband in Graphene-nanocavity formed on meta-surface


Plasmonic structured illumination microscopy (PSIM) is one of the promising wide filed optical imaging methods, which takes advantage of the surface plasmons to break the optical diffraction limit and thus to achieve a super-resolution optical image. To further improve the imaging resolution of PSIM, we propose in this work a so called graphene nanocavity on meta-surface structure (GNMS) to excite graphene surface plasmons with a deep sub-wavelength at mid-infrared waveband. It is found that surface plasmonic interference pattern with a period of around 52 nm can be achieved in graphene nanocavity formed on structured meta-surface for a 7 μm wavelength incident light. Moreover, the periodic plasmonic interference pattern can be tuned by simply changing the nanostructures fabricated on meta-surface for different application purposes. At last, the proposed GNMS structure is applied for super-resolution imaging in PSIM and it is found that an imaging resolution of 26 nm can be achieved, which is nearly 100 folds higher than that can be achieved by conventional epi-fluorescence microscopy. In comparison with visible waveband, mid-infrared is more gently and safe to biological cells and thus this work opens the new possibility for optical super-resolution imaging at mid-infrared waveband for biological research field.


In last few decades, the great progress in optical imaging has led to a profound impact on biological living cells research. Various methods were developed to improve the optical imaging resolutions1,2 including stimulated emission depletion microscopy (STED)3,4, near-field scanning optical microscopy (NSOM)5,6, and structured illumination microscopy (SIM)7,8, etc. Among these methods, more and more attentions are being paid to SIM for it can achieve high resolution optical imaging at wide-field. However, the spatial resolution of SIM is theoretically limited to λ/4NA, where λ is the wavelength of incident light and NA is numerical aperture of the objective lens9,10. More recently, plasmonic structured illumination microscopy (PSIM) was proposed to further improve the resolution by taking advantage the higher wave vector of surface plasmons11,12. Normally, noble metal is used for generating surface plasmons. However, the main problem of noble metals is that the loss is rather high so that the coupling efficiency as well as the propagation length of surface plasmons is limited.

Graphene, as a two-dimensional (2D) material formed by carbon atoms in honeycomb arrangement13, is only about 0.34 nm thick and has drawn extensive attentions in recent years. More recently, it was reported that strong coupling of light with electrons in graphene, i.e. graphene plasmons14,15,16, at middle-infrared and THz wavebands can be realized, and thus magnetic (TM) polarized surface plasmons can be stimulated and excited17,18. In comparison with conventional plasmons excited in noble metals, graphene plasmons have stronger ability to confine optical field with lower loss. Moreover, it can be tuned by gating or doping to make active devices in a broadband from middle-infrared to THz due to its extreme high conductivity19,20. Therefore, there is the possibility to incorporate graphene plasmons in PSIM method to further improve the optical imaging resolution.

In this work, we propose a so called graphene nanocavity on meta-surface (GNMS) structure model by intelligently integrating graphene nanocavity with meta-surface for super-resolution imaging in PSIM method. The dispersion relationship of the model is firstly discussed and then followed by simulating the structure by employing FDTD method. It is found that the plasmonic interference pattern generated on graphene has a period of 52 nm for a 7 μm incident light wavelength. There have been PSIM techniques based on surface plasmons excited on the surface of thin silver, and the imaging resolution improvement with 3 to 4 folds in comparison with conventional epi-fluorescence at visible waveband have been reported11,21,22. Nevertheless, once the model is applied for PSIM for optical imaging and it is found a resolution of 25 nm can be achieved, which is about 100 folds higher than that of traditional optical imaging and thus has the great potential to be applied for optical super-resolution imaging for biological research.


Structure description and analytical theory

Figure 1 shows the proposed GNMS model that consists of a nanocavity formed by two layers of graphene23 located on the top of a meta-surface structure, in which the wave vector of certain scattered or diffracted light by the silver grating matches with the graphene plasmonic wave vector under the phase-matching condition24,25. Additionally, TM polarized light incidents normally onto the silver grating to illuminate the structure from the bottom. Figure 1(b) shows the simplified cross-sectional view of the model to assist analyzing its electromagnetic property.

Figure 1
figure 1

Schematic of GNMS.

(a) Schematic of the GNMS model which consists of the nanocavity formed by two layers of graphene located on the top of a meta-surface, and the meta-surface is formed in a thin silver layer. (b) The cross-sectional view of the GNMS model.

According to Maxwell’s electromagnetic theory, the H and E field in each layer of GNMS can be expressed.

In Layer 1,

In Layer 2 and 3,

In Layer 4,

Here, with i = 1–4 stands for the wavenumber along x direction in each layer. ω is the angular frequency, εi is the relative permittivity of the materials in layer i, and k0 is the free-space wave vector. Under the assumption that surface current exists on graphene, one can obtain a series of relationships by matching the boundary conditions at each interface.

At interface x = d1, since the boundary condition is , , therefore one can get,

By combining equations (10) and (11), one can get,

Similarly, the relationships between layer 2 and 3 (x = d2) can be derived by considering boundary conditions of , ,

Because there is no surface current exists at the interface between layer 3 and 4 (x = 0) and the boundary conditions are , , hence one can get,

Finally, the following dispersion relationship can be obtained,

In GNMS model, both ε1 and ε4 are the relative permittivity of silica, and ε2 is the relative permittivity of water. Once the duty cycle of silver gate is set as γ, the relative permittivity of dielectric 3 is determined to be approximately. Besides, the dispersion relationship is also related to the permittivity of each layer determined by the angular frequency of incident light. Therefore, the wave vector () of surface plasmons on graphene can be calculated.

Figure 2(a) shows the calculated dispersion relationship of GNMS under different chemical potential of graphene. In the figure, n′ is defined by , which shows the ratio of wave vector between graphene plasmons and the free space incident light. If n′ is much larger than 1, it means that the graphene plasmonic wave with a much higher wave vector has been obtained, which is preferred for PSIM. In the calculation, the thickness of silver grating is d2 = 50 nm, and the thickness of water Δd = d1d2 = 10 nm. The conductivity of graphene σ can be determined by Kubo formula26,27,28,29,

Figure 2
figure 2

Dispersion curve of GNMS.

(a) Dispersion relationship of GNMS under different chemical potential of graphene. (b) Dispersion curve of GNMS and single-layer-graphene structure (shown in the inset picture) when chemical potential of graphene is 0.6 eV.

Where e, ω, T, μc, τ, kB and ħ stands for the charge of electron, radian angular frequency, temperature, chemical potential, momentum relaxing time, Boltzmann constant and the reduced Planck constant respectively. The first term of equation (20) represents the intraband conductivity and the second term is the interband conductivity approximately. Furthermore, equation (20) can be simplified to Drude-like form when the intraband term domains on the condition that ħω<μc, KBT and μc>>KBT30,31,32,

When ω<ωoph (ωoph is the optical phonon frequency)33, the relaxing time τ can be calculated by 34,35,36, where nc, μdc and vF stands for electron concentration, carrier mobility and the Fermi velocity respectively. If we define , then the conductivity of graphene can be expressed as,

In this paper, the carrier mobility Fermi velocity is set as vF = 106m/s and carrier mobility is μdc = 10000 cm2V−1s−1.

For comparison, the dispersion curve of single-graphene structure (shown in the inset in Fig. 2(b)) is given as well. The dispersion relationship of single-layer-graphene structure can be expressed as35,37,38.

It can be found from Fig. 2(b) that the wave vector of graphene plasmons of GNMS is apparently larger than that in single-layer-graphene structure. Therefore, the GNMS model is preferred for PSIM for optical imaging resolution enhancement purpose.

Simulation results

To further study the electromagnetic property of GNMS structure, the finite-difference time domain (FDTD) method was employed to simulate the GNMS structure (See Methods Section). Figure 3 shows the simulation results of 20 um × 20 um GNMS structure. In the simulation, the thickness of the silica substrate is set as ds = 150 nm and two dimensional periodic rectangular slits array with depth of 50 nm and period of 500 nm is fabricated in silica substrate. The slits are then filled with silver to form a two dimensional periodic silver grating with a period of 500 nm and a duty cycle of 0.1. This meta-structure is used to stimulate graphene plasmons. The nanocavity in between two layers of graphene film has a thickness of 10 nm and is filled with water. The top and bottom graphene film is supported by silica substrate and meta-surface respectively. The silica substrate on the top graphene film has a thickness of 100 nm. The wavelength of the incident light is set as 7 μm, corresponding with angular frequency of around 2.69 × 1014 rad/s. Actually, the wavelength of incident light can be tuned in infrared waveband and the proposed structure performs well in waveband ranging from 6 μm~9 μm. The relative permittivity of silica, water and silver is exported from FDTD material explorer and is , , εAg = −1634.61 + 566.379i. The chemical potential, carrier mobility and Fermi velocity of graphene is set as: μc = 0.64 eV, μdc = 10000 cm2V−1, vF = 106m/s respectively. Figure 3(a) shows cross sectional view of GNMS structure and Fig. 3(b) shows the cross sectional view of electric field distribution of the formed periodic plasmonic interference pattern in GNMS structure in z-x plane. As can be seen from Fig. 3(b), the electric field distribution is quite uniform inside the graphene nanocavity. This means if the observed object is put into the nanocavity, the object is always within the working depth of PSIM. Figure 3(c) shows the electric field distribution of plasmonic interference pattern at plane x = 55 nm. Figure 3(d) is the electric field distribution along the dashed line. As can be seen, the intensity of electric field in graphene nanocavity is strongly enhanced which is about 5 times of that of the incident light. The period of the graphene plasmonic interference pattern is 52 nm and the full width at half maximum (FWHM) is around 26 nm. Considering the wavelength of the incident light is 7 μm and the wavelength of graphene plasmonic wave is calculated to be 104 nm, hence the wave vector of graphene is increased for about 67 folds higher in graphene nanocavity.

Figure 3
figure 3

Simulation of GNMS structure and results.

(a) Cross-sectional view of the GNMS structure. (b) Cross-sectional view of electric field distribution of graphene plasmonic interference pattern. (c) Top view of electric field distribution of graphene plasmonic interference pattern. (d) Electric field distribution along the white dashed line in Fig. 3(c).

To explain the function of the grating in meta-surface on the graphene plasmonic interference pattern, parameters of the silver grating including duty cycle, material and period are discussed respectively. Figure 4 shows the influence of the grating duty cycle on graphene plasmonic interference pattern. Obviously, the grating duty cycle ranging from 0.1–0.4 has little impact on the field distribution in nanocavity as the period of the plasmonic interference pattern is always 52 nm. However, it is found that the uniform of the field distribution becomes worse when duty cycle larger than 0.1. Furthermore, the structure with duty cycles of 0 and 1 was simulated as well and it is found that in graphene plasmons can not be excited for both cases, which means that the grating structure is necessary to stimulate graphene plasmons.

Figure 4
figure 4

The graphene plasmonic interference pattern with different duty cycle of grating.

(a) Interference pattern with duty cycle is set as 0.1. (b) Interference pattern with duty cycle is set as 0.2. (a) Interference pattern with duty cycle is set as 0.3. (a) Interference pattern with duty cycle is set as 0.4.

In order to show the effect of the grating material on graphene plasmons, grating structure with different materials was studied and the results are shown in Table 1(a). As can be seen clearly that although the grating material is changed, but the period of the plasmonic interference pattern keeps constant. This means graphene plasmons can always be excited for different grating materials. However, the peak intensity of graphene plasmons is significantly different for different material. As can be seen, the peak intensity for metal and semiconductor materials is about the same. But for dielectric material, i.e. Al2O3, the peak intensity is quite weaker. We attribute this reason to the possible contribution localized surface plasmonic enhancement effect of metal and semiconductor materials.

Table 1 Effects of grating parameters on graphene plasmons.

Furthermore, the effect of the period of metal grating on graphene plasmons was also discussed for the same duty cycle of 0.1 and the results are shown in Table 1(b). It is found that the period of the silver grating seems has no effect on the period of the graphene plasmonic interference pattern as it is always 52 nm when grating period changes from 500 nm to 1000 nm. However, the peak intensity of the field is significant different. The maximum intensity can be obtained when grating period is 700 nm. Consequently, in the next analytical calculation, the parameter γ will be set as 0 approximately for accuracy when the grating duty cycle is small.

Tuning of graphene plasmons in nanocavity

To tune the graphene plasmons in nanocavity, the influence of the structural parameters on the graphene plasmonic interference field is systematically studied. The structural parameters that can be changed include the thickness of water film Δd and the height of silver grating d2. Table 2(a) shows the period of the plasmonic interference pattern against the thickness of water film when silver film thickness is fixed to be 50 nm. The propagation length of the graphene plasmons () was also calculated and is shown in the same table. In general, it is found that the smaller the water film thickness, the smaller the period of the plasmonic interference pattern. Meanwhile, the propagation length of graphene plasmons becomes smaller when the water film thickness becomes smaller. Table 2(b) shows the influence of silver film thickness on graphene plasmons. As can be seen clearly, despite the plasmonic wavelength have relationship with parameter d2 through the dispersion equation (19), it seems that the film thickness of the silver grating almost does not influence graphene plasmons when thickness changes from 40 to 80 nm, which well verified the previous assumption.

Table 2 Tuning of the period of graphene plasmonic interference pattern.

Moreover, it is found that the period of graphene plasmonic interference pattern can also be tuned by changing the chemical potential of graphene. Table 2(c,d) shows the period of the plasmonic pattern against the chemical potential of the graphene film on top and bottom respectively. In general, the lower the chemical potential, the smaller the period of the plasmonic pattern.

Application of GNMS structure for super-resolution imaging

The proposed GNMS structure can be applied for super-resolution imaging at mid-infrared waveband. If DNA or protein is put in the nanocavity, the formed plasmonic pattern can be used to illuminate the biological sample as a structured illumination light for PSIM method. Figure 5(a–c) show the simulation results of the electric field distribution of graphene plasmonic interference pattern. According to the theory of PSIM11,12, the resolution limit of optical imaging is determined by λemission/(2NA+2NAeffective), where λemission is the wavelength of incident light and NAeffective represents . which means the larger the NAeffective, the higher resolution limit the PSIM can be achieved. Since the period of the plasmonic pattern is 52 nm, the resolution limit can be achieved is 25 nm for PSIM. Figure 5(d) shows the FWHM of the point spread function (PSF) of a traditional immersion oil objective lens with a NA of 1.42 and the reconstructed PSF of GNMS structure based PSIM for a 10 nm quantum dot (See Methods Section). As can be seen, the FWHM is about 2536 nm for traditional optical lens and therefore the imaging resolution has been enhanced for more than 100 folds. This has significantly improved the optical imaging resolution at mid-infrared waveband.

Figure 5
figure 5

Application of GNMS structure in super-resolution imaging.

(a) Cross sectional view of electric field distribution of surface plasmonic interference pattern. (b) Top view of the graphene plasmonic interference pattern in water in nanocavity. (c) Electric field intensity distribution along the dashed line in Fig. 5(b). (d) Comparison of the normalized FWHM of a quantum dot obtained by conventional epifluorescence microscopy (red line) and by using GNMS in PSIM (green line). The inset shows the normalized FWHM in Fig. 5(d)


As a summary, we have proposed a so called GNMS model for PSIM method to improve the optical imaging resolution. The GNMS model takes advantage of merits of both graphene and meta-structure. As proved by both analytical and numerical simulations, deep compression of the period of plasmonic interference pattern can be achieved in graphene nanocavity at mid-infrared waveband. Moreover, the proposed GNMS model can be applied for optical imaging resolution when applied in PSIM method. The rigorous numerical simulation results show that the imaging resolution has been enhanced for more than 100 folds by GNMS in comparison with traditional optical imaging method. More importantly, as the infrared light is safer than visible light for biological samples, the proposed GNMS method should be more preferred for biological research when applied in optical imaging.


The proposed GNMS is simulated by using Finite Difference Time Domain (FDTD) software supported by Lumerical Solutions Inc. In the simulation, temperature is set as 300 K, the model of graphene is represented by a 2D-rectangle to reduce the simulation time and ensure the precision of the simulation. The scattering rate and chemical potential of graphene are set according to the design, and the conductivity scaling of graphene keeps 1. Furthermore, in the simulation the 8th mesh accuracy which is the highest is used. The mesh type is set as auto-uniform which means that the minimum grid is the 34th of the minimum wavelength. The periodical boundary condition is set along both y and z axes and PML boundary condition is used in x direction. In addition, in the region of water film and silver grating, a finer grid of 0.5 × 5 × 0.5 nm3 is used to ensure the sufficient precision near graphene regions.

In the numerical experiment of super-resolution imaging, a 10 nm quantum dot is used as the object. The PSF in far field was calculated by the first order Bessel functions39,

Where J1 is the first-order Bessel function, NA is the numerical aperture of oil objective, λe represents the reflection wavelength of the quantum dot and is the radius of quantum dot, thus in the far field, the image of the quantum dot can be obtained. For GNMS based PSIM method, O(r) is set as 1 at where the dot is illuminated. Furthermore, at least three different phase, i.e. 0, 120°, −120°, of the illumination pattern should be recorded to realize the image reconstruction. This can be achieved by changing the angle of the incident light or by employing the vortex beams with different topological charges.

Additional Information

How to cite this article: Yang, J. et al. Super-Resolution Imaging at Mid-Infrared Waveband in Graphene-nanocavity formed on meta-surface. Sci. Rep. 6, 37898; doi: 10.1038/srep37898 (2016).

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.


  • Heilemann, M. Fluorescence microscopy beyond the diffraction limit. Journal of Biotechnology. 149, 243–251 (2010).

    CAS  ADS  Article  Google Scholar 

  • Hao, X. et al. From microscopy to nanoscopy via visible light. Light: Science & Applications. 2, e108 (2013).

    Article  Google Scholar 

  • Hell, S. W. & Wichmann, J. Breaking the diffraction resolution limit by stimulated emission: stimulated-emission-depletion fluorescence microscopy. Optics letters. 19, 780–782 (1994).

    CAS  ADS  Article  Google Scholar 

  • Hell, S. W. Far-field optical nanoscopy. science. 316, 1153–1158 (2007).

    CAS  ADS  Article  Google Scholar 

  • Inouye, Y. & Kawata, S. Near-field scanning optical microscope with a metallic probe tip. Optics letters. 19, 159–161 (1994).

    CAS  ADS  Article  Google Scholar 

  • Sánchez, E. J., Novotny, L. & Xie, X. S. Near-field fluorescence microscopy based on two-photon excitation with metal tips. Physical Review Letters. 82, 4014 (1999).

    ADS  Article  Google Scholar 

  • Hirvonen, L. M., Wicker, K., Mandula, O. & Heintzmann, R. Structured illumination microscopy of a living cell. Eur Biophys J. 38, 807–12 (2009).

    Article  Google Scholar 

  • Gustafsson, M. G. et al. Three-dimensional resolution doubling in wide-field fluorescence microscopy by structured illumination. Biophys J. 94, 4957–70 (2008).

    CAS  ADS  Article  Google Scholar 

  • Gustafsson, M. G. Surpassing the lateral resolution limit by a factor of two using structured illumination microscopy. Journal of microscopy. 198, 82–87 (2000).

    CAS  Article  Google Scholar 

  • Schermelleh, L. et al. Subdiffraction multicolor imaging of the nuclear periphery with 3D structured illumination microscopy. Science. 320, 1332–1336 (2008).

    CAS  ADS  Article  Google Scholar 

  • Wei, F. & Liu, Z. Plasmonic structured illumination microscopy. Nano Lett. 10, 2531–6 (2010).

    CAS  ADS  Article  Google Scholar 

  • Fernández-Domínguez, A. I., Liu, Z. & Pendry, J. B. Coherent Four-Fold Super-Resolution Imaging with Composite Photonic–Plasmonic Structured Illumination. ACS Photonics. 2, 341–348 (2015).

    Article  Google Scholar 

  • Zhao, Y. & Zhu, Y. Graphene-based hybrid films for plasmonic sensing. Nanoscale. 7, 14561–76 (2015).

    CAS  ADS  Article  Google Scholar 

  • Grigorenko, A. N., Polini, M. & Novoselov, K. S. Graphene plasmonics. Nat Photon. 6, 749–758 (2012).

    CAS  ADS  Article  Google Scholar 

  • Koppens, F. H. L., Chang, D. E. & García de Abajo, F. J. Graphene Plasmonics: A Platform for Strong Light–Matter Interactions. Nano Letters. 11, 3370–3377 (2011).

    CAS  ADS  Article  Google Scholar 

  • Ju, L. et al. Graphene plasmonics for tunable terahertz metamaterials. Nature nanotechnology. 6, 630–634 (2011).

    CAS  ADS  Article  Google Scholar 

  • Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science. 306, 666–669 (2004).

    CAS  ADS  Article  Google Scholar 

  • Wang, B. et al. Strong Coupling of Surface Plasmon Polaritons in Monolayer Graphene Sheet Arrays. Physical Review Letters. 109 (2012).

  • Stauber, T., Peres, N. M. R. & Castro Neto, A. H. Conductivity of suspended and non-suspended graphene at finite gate voltage. Physical Review B. 78 (2008).

  • Horng, J. et al. Drude conductivity of Dirac fermions in graphene. Physical Review B. 83, 165113 (2011)

    ADS  Article  Google Scholar 

  • Wei, F. et al. Wide Field Super-Resolution Surface Imaging through Plasmonic Structured Illumination Microscopy. Nano Letters. 14, 4634–4639 (2014).

    CAS  ADS  Article  Google Scholar 

  • Ponsetto, J. L., Wei, F. & Liu, Z. Localized plasmon assisted structured illumination microscopy for wide-field high-speed dispersion-independent super resolution imaging. Nanoscale. 6, 5807–12 (2014).

    CAS  ADS  Article  Google Scholar 

  • Wang, B., Zhang, X., Yuan, X. & Teng, J. Optical coupling of surface plasmons between graphene sheets. Applied Physics Letters. 100, 131111 (2012).

    ADS  Article  Google Scholar 

  • Davoyan, A. R., Popov, V. V. & Nikitov, S. A. Tailoring terahertz near-field enhancement via two-dimensional plasmons. Phys Rev Lett. 108, 127401 (2012).

    ADS  Article  Google Scholar 

  • Weilu Gao, J. S., Ciyuan, Qiu & Qianfan, Xu*. Excitation of PlasmonicWaves in Graphene by Guided-Mode Resonances.

  • Gusynin, V. P., Sharapov, S. G. & Carbotte, J. P. Magneto-optical conductivity in graphene. Journal of Physics: Condensed Matter. 19, 026222 (2007).

    ADS  Google Scholar 

  • Emani, N. K. et al. Electrical modulation of fano resonance in plasmonic nanostructures using graphene. Nano Lett. 14, 78–82 (2014).

    CAS  ADS  Article  Google Scholar 

  • Falkovsky, L. A. & Pershoguba, S. S. Optical far-infrared properties of a graphene monolayer and multilayer. Physical Review B. 76 (2007).

  • Zhang, R. R. et al. Free-space carpet cloak using transformation optics and graphene. Optics Letters. 39, 6739–6742 (2014).

    CAS  ADS  Article  Google Scholar 

  • Fan, Y., Wei, Z., Zhang, Z. & Li, H. Enhancing infrared extinction and absorption in a monolayer graphene sheet by harvesting the electric dipolar mode of split ring resonators. Optics letters. 38, 5410–5413 (2013).

    CAS  ADS  Article  Google Scholar 

  • Fan, Y. et al. Tunable mid-infrared coherent perfect absorption in a graphene meta-surface. Scientific reports. 5 (2015).

  • Hanson, G. W. Dyadic Green’s functions and guided surface waves for a surface conductivity model of graphene. Journal of Applied Physics. 103, 064302 (2008).

    ADS  Article  Google Scholar 

  • Jablan, M., Buljan, H. & Soljačić, M. Plasmonics in graphene at infrared frequencies. Physical Review B. 80 (2009).

  • Wang, G., Liu, X., Lu, H. & Zeng, C. Graphene plasmonic lens for manipulating energy flow. Sci Rep. 4, 4073 (2014).

    ADS  Article  Google Scholar 

  • Gao, W. et al. Excitation and active control of propagating surface plasmon polaritons in graphene. Nano Lett. 13, 3698–702 (2013).

    CAS  ADS  Article  Google Scholar 

  • Fan, Y., Shen, N. H., Koschny, T. & Soukoulis, C. M. Tunable Terahertz Meta-Surface with Graphene Cut-Wires. Acs Photonics. 2 (2015).

  • Zeng, C., Liu, X. & Wang, G. Electrically tunable graphene plasmonic quasicrystal metasurfaces for transformation optics. Sci Rep. 4, 5763 (2014).

    ADS  Article  Google Scholar 

  • Lu, H. et al. Graphene-based active slow surface plasmon polaritons. Sci Rep. 5, 8443 (2015).

    CAS  Article  Google Scholar 

  • So, P. T. C., Kwon, H.-S. & Dong, C. Y. Resolution enhancement in standing-wave total internal reflection microscopy: a point-spread-function engineering approach. Journal of the Optical Society of America A. 18, 2833–2845 (2001).

    CAS  ADS  Article  Google Scholar 

Download references


The authors acknowledge the financial supports from Natural Science Foundation of China under grant numbers 61361166004 and 61475156. Financial supports from Science and Technology Department of Jilin Province under grant no. 20140519002JH is acknowledged as well.

Author information

Authors and Affiliations



W. Yu conceived the idea. J. Yang completed the theoretical derivation and carried out numerical simulation. J. Yang and W. Yu prepared the manuscript. T. Wang, Z. Chen and B. Hu helped to discuss the results and improve the manuscript substantially.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Yang, J., Wang, T., Chen, Z. et al. Super-Resolution Imaging at Mid-Infrared Waveband in Graphene-nanocavity formed on meta-surface. Sci Rep 6, 37898 (2016).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing