Clear understanding the mechanism of resistive switching is the important prerequisite for the realization of high performance nonvolatile resistive random access memory. In this paper, binary metal oxide MoOx layer sandwiched by ITO and Pt electrodes was taken as a model system, reversible transition of abnormal and normal bipolar resistive switching (BRS) in dependence on the maximum voltage was observed. At room temperature, below a critical maximum voltage of 2.6 V, butterfly shaped I-V curves of abnormal BRS has been observed with low resistance state (LRS) to high resistance state (HRS) transition in both polarities and always LRS at zero field. Above 2.6 V, normal BRS was observed, and HRS to LRS transition happened with increasing negative voltage applied. Temperature dependent I-V measurements showed that the critical maximum voltage increased with decreasing temperature, suggesting the thermal activated motion of oxygen vacancies. Abnormal BRS has been explained by the partial compensation of electric field from the induced dipoles opposite to the applied voltage, which has been demonstrated by the clear amplitude-voltage and phase-voltage hysteresis loops observed by piezoelectric force microscopy. The normal BRS was due to the barrier modification at Pt/MoOx interface by the accumulation and depletion of oxygen vacancies.
There is a strong technological demand to develop faster, smaller, cheaper, and more reliable nonvolatile memory devices, which is therefore promoting the intensive researches on various mechanisms1,2. Among them, resistive random access memory (RRAM) has received much attention due to its simple structure, rapid operation, and high density integration3,4,5,6. In recent years, remarkable improvements have been made to understand the physics of RRAM devices4. Based on the polarity of applied voltages of switching, resistive switching (RS) characteristics between high resistance state (HRS) and low resistance state (LRS) can be classified into two types, i.e., unipolar and bipolar4,7,8. For unipolar resistive switching (URS), the set (HRS to LRS) and reset (LRS to HRS) processes happen at the same polarity. For the bipolar resistive switching (BRS), a resistance changing from HRS to LRS occurs at certain voltage polarity, with an inverse process from LRS to HRS with reversed voltage polarity. The mechanism has been intensively studied for the RS behavior. Based on the RS region, RS can be categorized into two types, bulk type with conducting filaments and interface type with tunneling barrier height and width modulation7,9,10,11. The reversible structure modification and resulted RS mainly originates from the thermal activated7 or electric field driven ion migration, such oxygen vacancies12,13, metallic electrode atoms14, etc. The RS is also very sensitive to the selected electrode, and abnormal BRS might be observed with fixed resistance state at zero field no matter the RS at high field15,16.
Oxides are the most intensively studied materials for RRAM. For the binary metallic oxide with RS based on migration of oxygen vacancies, those material with highly sensitive of resistivity on oxygen content is very attractive. It has been reported that molybdenum oxides show variable electrical conductivity from metallic MoO2 to insulating MoO3 with variation of oxygen content17,18, and amorphous MoOx film shows 5 orders change of resistivity with oxygen partial pressure ranging from 1.00 × 10−3 mbar to 1.37 × 10−3 mbar19. In this paper, we report the RS in amorphous MoOx films sandwiched by ITO and Pt electrodes. In contrast to the previous reports of abnormal BRS and normal BRS in distinctive structures16,20,21, reversible transition between abnormal BRS and normal BRS in dependence on the maximum applied voltage has been observed in the same structure. It has been suggested that the metastable pinning sites in the vicinity of equilibrium positions may immobilize the oxygen vacancies, leading to the induced dipoles with opposite electric field and abnormal BRS at low voltage. Higher voltage mobilizes the fixed oxygen vacancies, modify the barrier at Pt/MoOx, leading to the normal BRS.
Results and Discussion
The sweeping voltage was applied on the bottom ITO electrode in the way of 0 → −2 → 0 → 2 → 0 V (shown in the Fig. 1(a) in semi-log scale). During the measurements, no current compliance was applied. In this paper, we take the absolute value of current, and the original I-V curves in linear scale are shown in Figure S1. It should be noted that we do not need a power consuming electroforming process to realize the resistive switching, which is usually required in conventional filament-like resistive switching22. The fresh memory cells of Pt/MoOx/ITO sandwiched structure were always in the LRS state, and gradually switched to the HRS state with increasing voltage in both polarities. Interestingly, the cell switched back to the LRS state at zero field, which is a typical abnormal BRS16. In contrast to the general observed abnormal BRS with negligible current at zero field16,23,24, significantly large current can be observed for our cells at zero bias, and the I-V curves showed a butterfly shape with current minimum at voltage of −0.6 V and 0.56 V after the voltage switching back from the maximum value. The significant large current at zero voltage clearly suggested the existence of some internal electric field inside the cell depending on the voltage polarization. Similar phenomenon has also been observed in other films, e.g. SrTiO325, BiFeO326. With increasing the maximum voltage to 3 V applied in the same sequence as Fig. 1(a), HRS to LRS switching was observed in the negative voltage branch, LRS state was preserved at zero voltage and switched back to HRS with increasing positive voltage (shown in Fig. 1(b)). The cell can keep the LRS and HRS states stably depending on the voltage polarity, which is a typical normal BRS. If we decreased the maximum voltage to 2 V again, the similar abnormal BRS behavior as Fig. 1(a) can be recovered (shown in Figure S2). Thus, in the same cell, we can reversibly switch between abnormal BRS and normal BRS by the maximum voltage. We further checked whether the HRS to LRS switching can happen in the positive voltage branch if we applied positive voltage to 3 V first, only LRS to HRS switching can be observed, as shown in Fig. 1(c). It should be noted that we even first applied positive voltage to 9 V, but only LRS to HRS switching was observed (Figure S3). If we applied the positive voltage first, and then applied negative voltage to maximum value of −3 V, clear HRS to LRS switching can be observed, and normal BRS was observed again (Fig. 1(d)). From above results, we can conclude that abnormal to normal RS can be observed in the negative voltage branch in dependence on the maximum voltage (LRS to HRS with low maximum voltage, and HRS to LRS with high maximum voltage), while in positive voltage branch only LRS to HRS switching can be observed.
To clear understand the evolution of abnormal BRS to normal BRS, the maximum voltage was gradually increased in a range of 2.1 to 2.9 V in step of 0.1 V, and the corresponding I-V curves are shown in Fig. 2. As can be seen, the clear abnormal BRS behavior can be observed with butterfly shaped I-V curves when small maximum voltage was applied. With increasing the maximum voltage, the current value of HRS state in step 2 became larger. There is a critical maximum voltage (VC) of 2.6 V, at which the LRS curve in step 1 and HRS curve in step 2 are nearly overlapping. With further increasing the maximum voltage above 2.6 V, the LRS and HRS interchanged. The resistance state in step 1 now changed to HRS state, and a HRS to LRS switching happened in the negative voltage branch. The separation between the current value in the curves of step 1 and 2 became larger with increasing the maximum voltage, and normal BRS can be observed, which persisted with further increasing the maximum voltage, as shown in Figure S4 (maximum voltage of 5 V).
The stability property of BRS in the Pt/MoOx/ITO device below and above the VC at room temperature was measured, and is shown in Fig. 3. When we applied the maximum voltage of 2 V, it shows that the consecutive 100 switching cycles almost overlap with each other, which indicates a stable abnormal BRS behavior, as can be seen in Fig. 3(a). However, if we applied the maximum voltage (2.7 V) to just above the VC of 2.6 V, a gradual evolution of the consecutive I-V curves can be observed, as can be seen in Fig. 3(b). In the initial I-V curve, the separation between HRS and LRS in the negative branch is small. After the consecutive I-V measurements, both the currents at HRS and LRS increased with broader separation between the HRS and LRS branches. It can be seen that the increase of current value in LRS state is much faster than that in the HRS state. Less significant shift can be observed in the positive branch. Furthermore, it can be seen that the I-V curves became nearly stable after the consecutive 50 runs. This can be understood by the effect of electric field on the migration of oxygen vacancies. Under high voltage, the electric field can drag the oxygen vacancies out from the equilibrium positions. However, the electric field is not strong enough when the maximum voltage is just above VC, and it will take time for the migration of oxygen vacancies. The final state needs time to reach due to the low migration speed of oxygen vacancies, leading the gradual evolution of I-V curves. The time dependent HRS and LRS in normal BRS was further measured, and shown in Figure S5, which showed the highly stable retention.
In contrast to the previous reported I-V curves with current minimum nearly overlapping at zero voltage, butterfly-shaped I-V curves were observed with two current minimums in the Pt/MoOx/ITO structure, which is quite similar to the slow dielectric relaxation of induced dipoles in ferroelectric materials26. The significant large current at zero voltage clearly demonstrated the existence of internal electric field. We performed the piezoelectric force microscopy (PFM) measurements, the amplitude-voltage and phase-voltage curves are shown in Fig. 4. The clear observation of the hysteretic butterfly-shaped loops is the general indication of ferroelectricity. However, Q. N. Chen et al. have observed the similar phenomenon in soda-lime glass which is clearly not ferroelectric and they attributed this to the induced dipole moment27. For the induced dipole moment, the phase-voltage loops showed significant broadening with increasing maximum voltage and variation of the shape of amplitude-voltage loops with increasing measuring periods, while nearly unchanged shape for ferroelectric materials27. As can be seen, the phase-voltage loops were significantly broadened with increasing maximum voltage and the shape of amplitude-voltage loops varied notably with increasing the measuring period. With the maximum voltage above 2.5 V (close to VC), the phase-voltage loops became distorted. The phase-voltage curves became more distorted with larger maximum voltages, as shown in Figure S6. Thus, the abnormal BRS can be understood by the induced dipoles due to the shift of oxygen vacancies from the equilibrium positions to the metastable sites, which induced an electric field opposite to the applied electric field, leading to the switching from LRS to HRS.
Temperature always influences the migration rate of oxygen vacancies. We also measured the temperature dependent RS of our device in the step of 5 °C with decreasing temperature from 300 K. Figure 5 shows the RS behavior with maximum voltage of 4 V at various temperatures. As can be seen, stable normal BRS can be observed at 300 K. However, the HRS and LRS branches in I-V curves at the negative voltage branches became overlapped if we decreased the temperature to 270 K. The abnormal BRS became more obvious if we further decreased the temperature, and finally stable abnormal BRS can be observed at temperature of 240 K. This can be understood by the thermal activated migration of oxygen vacancies. With decreasing temperature, higher electric field was needed to drag the oxygen vacancies from the metastable sites to migrate inside the films. The average activation energy values vary from 0.139–0.262 eV (comparable to the known value of 0.141 eV (at 325 K))28 for different constant voltages from 1 V to 5 V (Figure S7). It is clearly revealed that the migration of oxygen vacancies is significantly decreased by the temperature.
Several models have been attempted to interpret the RS phenomenon in RRAM28,29,30,31,32,33,34. In order to identify which model is suitable to describe the behavior in our devices, we analyzed the I-V curves of the BRS behavior by various models, such as space charge limited current (SCLC)29,32 Schottky emission30,33 Poole-Frenkel (PF) emission28,34 and electron tunneling35. Figure 6 shows the best fitting of the typical I-V curves of LRS and HRS in voltage branches of both abnormal and normal BRS. For abnormal BRS, Ohmic and SCLC are more obvious in the positive voltage (Fig. 6(a)), and in the negative voltage, LnI is proportional to V (Fig. 6(c))35, indicating the electron tunneling conduction because the migration of oxygen vacancies by electric field is negligible. For the positive branches in normal behavior, as can be seen, the dependence of LnJ and LnE for the LRS shows nearly linear relation with slope close to 1, indicating the Ohmic conduction, while the slope of the curve changes from 1.13 to 1.90, showing the typical trap-controlled SCLC mechanism (Fig. 6(b))29,32. In the negative branches in normal BRS, to investigate the dominant conduction mechanism in the junction, we used several conduction mechanisms to fit the I−V curves, including Schottky emission, PF emission, SCLC, and Fowler−Nordheim (FN) tunneling (Figure S8). The dielectric constants obtained by the fitting using Schottky emission or PF emission significantly deviate from the ideal value, excluding these two mechanisms (Figure S8). The good linear fitting at high voltage region between LnJ/E2 and 1/E suggests that FN tunneling is the dominant mechanism (Fig. 6(d)). To clarify which interface played the main role in the RS, we replaced the top Pt electrodes by Ti electrodes. As can be seen in Figure S9, the resistance became at least one order smaller, and only negligible RS can be observed. This confirms that RS happened at the Pt/MoOx interface. The conduction mechanism in negative branches change from abnormal BRS to normal BRS can be understood by the different Pt/MoOx interface state. In the abnormal BRS, the oxygen vacancies are fixed close to the equilibrium position, and will not modify the sharp interface between the Pt and MoOx, making it susceptible to electron tunneling16. In the normal BRS, the Pt/MoOx interface was modified by the migration of oxygen vacancies under enough high electric field. Due to the accumulation of oxygen vacancies at Pt/MoOx interface, the interface layer became thicker. The electrons can tunnel through the potential barrier at high electric field due to the formation of the triangle potential barrier36.
The Fermi level of the MoOx (4.89 eV)37 is close to the ITO work function (4.7 eV)38 but much lower than Pt (5.65 eV). Thus, the ITO/MoOx interface tends to be Ohmic contact, and the RS mainly happens at the Pt/MoOx interface. In order to assist us to better understand the microscopic mechanism of this BRS, a schematic diagram under different maximum applied electric fields is drawn and shown in Fig. 7. As can be seen, under small voltage, the oxygen vacancies cannot migrate inside the film, but slightly shift from the equilibrium positions to the metastable positions. The dipoles are formed, which induce the electric field opposite to the applied field. Due to the compensation of the external electric field, the actual internal electric field is smaller, leading to the higher resistance (Fig. 7(a)). With decreasing the voltage in the negative branch to some value, the electric field from dipoles is larger than the external applied electric field due to the much slow dielectric relaxation26, current is reversed and the cell gradually switches back to LRS, as the oxygen vacancies shift back to the equilibrium positions (Fig. 7(b)). With further increasing positive voltage, similar process will happen with only the polarity is reversed (Fig. 7(c,d)). When a higher maximum voltage is applied (>2.6 V at room temperature), oxygen vacancies will not be fixed around the equilibrium positions, and can migrate inside the film. When a positive voltage was applied, oxygen vacancies would move toward the Pt/MoOx interface and accumulate there (Fig. 7(f)), leading to the higher trap density and the transition from LRS to HRS. When the voltage is reversed, the oxygen vacancies drift away from the interface (Fig. 7(e)), leading to the decrease of trap density. Under high electric field, triangle potential barrier is formed at the interface layer and electrons can tunnel through this barrier layer, leading to the HRS to LRS switching.
In summary, a reversible transition between abnormal BRS and normal BRS has been observed in Pt/MoOx/ITO sandwiched structures without electroforming process. The critical maximum voltage for the transition between abnormal BRS and normal BRS is 2.6 V at room temperature, which increases with decreasing temperature. Under low maximum voltage, the electric field is not large enough to drive the oxygen vacancies, which can only occupy the metastable sites near the equilibrium positions. The dipoles were formed, inducing the electric field which may partially compensate the external applied field. Thus LRS to HRS transition can always be observed in both polarities, leading to the abnormal BRS. Under high maximum voltage, the oxygen vacancies can migrate inside the film, the accumulation/depletion of oxygen vacancies at Pt/MoOx interface will modulate the trap density, leading the normal BRS.
Amorphous MoOx films were prepared by pulsed laser deposition (PLD) on indium-tin-oxide (ITO) substrates under various oxygen pressures from 0.2 Pa to 5.0 Pa at room temperature. The amorphous nature of the films was confirmed by X ray diffraction (XRD), as shown in Figure S10(a). The thickness of MoOx films were estimated to be 277 nm from cross-sectional sample observed by a field emission scanning electron microscope (FE-SEM), as shown in Figure S11(a). Then 100 nm thick Pt top electrodes with diameter of 160 μm were sputtered on the MoOx films through a shadow mask. The I–V characteristics of the Pt/MoOx/ITO sandwich structures were measured by a Keithley 2400 SourceMeter and 2182 A Nanovoltmeter, as the schematic structure shown in Figure S11(b). As can be seen from Figure S12, the resistivity of MoOx film increased dramatically with increasing oxygen partial pressure above 1.0 Pa. In this paper, we selected the MoOx film prepared under oxygen partial pressure of 4.0 Pa for the electrical characterization, which exhibited the most significant RS behavior. The valence state of Mo was characterized by X ray photoelectron spectroscopy (XPS, ThermoFisher SCIENTIFIC) with Al Kα X-ray source (hν = 1486.6 eV), shown in Figure S10(b) and Figure S10(c), which confirms the existence of oxygen vacancies. The I-V curves at different temperatures were measured by a Cascade Summit 11000 M. The piezoelectric hysteresis loops were characterized by a scanning probe microscope (SPM, Asylum Research Cypher).
How to cite this article: Wang, G. et al. Reversible voltage dependent transition of abnormal and normal bipolar resistive switching. Sci. Rep. 6, 36953; doi: 10.1038/srep36953 (2016).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Burr, G. W. et al. Overview of candidate device technologies for storage-class memory. IBM J. Res. Dev. 52, 449–464 (2008).
Yang, J. J., Strukov, D. B. & Stewart, D. R. Memristive devices for computing. Nat. Nanotechnol. 8, 13–24 (2013).
Kim, K. M., Jeong, D. S. & Hwang, C. S. Nanofilamentary resistive switching in binary oxide system; a review on the present status and outlook. Nanotechnology 22, 254002 (2011).
Waser, R. & Aono, M. Nanoionics-based resistive switching memories. Nat. Mater. 6, 833–840 (2007).
Baek, I. G. et al. Highly scalable nonvolatile resistive memory using simple binary oxide driven by asymmetric unipolar voltage pulses. In Electron Devices Meeting, IEDM Technical Digest. IEEE International 587–590, doi: 10.1109/IEDM.2004.1419228 (2004).
Yoshida, C., Tsunoda, K., Noshiro, H. & Sugiyama, Y. High speed resistive switching in Pt/TiO2/TiN film for nonvolatile memory application. Appl. Phys. Lett. 91, 223510 (2007).
Kwon, D.-H. et al. Atomic structure of conducting nanofilaments in TiO2 resistive switching memory. Nat. Nanotechnol. 5, 148–153 (2010).
Xu, D. L., Xiong, Y., Tang, M. H., Zeng, B. W. & Xiao, Y. G. Bipolar and unipolar resistive switching modes in Pt/Zn0.99Zr0.01O/Pt structure for multi-bit resistance random access memory. Appl. Phys. Lett. 104, 183501 (2014).
Choi, B. J. et al. Resistive switching mechanism of TiO2 thin films grown by atomic-layer deposition. J. Appl. Phys. 98, 33715 (2005).
Yang, J. J. et al. Memristive switching mechanism for metal/oxide/metal nanodevices. Nat. Nanotechnol. 3, 429–433 (2008).
Yang, J. J., Borghetti, J., Murphy, D., Stewart, D. R. & Williams, R. S. A Family of Electronically Reconfigurable Nanodevices. Adv. Mater. 21, 3754–3758 (2009).
Lee, D. et al. Resistance switching of the nonstoichiometric zirconium oxide for nonvolatile memory applications. IEEE Electron Device Lett. 26, 719–721 (2005).
Seo, S. et al. Reproducible resistance switching in polycrystalline NiO films. Appl. Phys. Lett. 85, 5655–5657 (2004).
Kudo, M., Arita, M., Ohno, Y. & Takahashi, Y. Filament formation and erasure in molybdenum oxide during resistive switching cycles. Appl. Phys. Lett. 105, 173504 (2014).
Kim, W.-G. & Rhee, S.-W. Effect of the top electrode material on the resistive switching of TiO2 thin film. Microelectron. Eng. 87, 98–103 (2010).
Guo, D. Y. et al. Abnormal bipolar resistive switching behavior in a Pt/GaO1.3/Pt structure. Appl. Phys. Lett. 107, 32104 (2015).
Dissanayake, M. A. K. L. & Chase, L. L. Optical properties of CrO2, MoO2, and WO2 in the range 0.2–6 eV. Phys. Rev. B 18, 6872–6879 (1978).
Julien, C., Khelfa, A., Hussain, O. M. & Nazri, G. A. Synthesis and characterization of flash-evaporated MoO3 thin films. J. Cryst. Growth 156, 235–244 (1995).
Cauduro, A. L. F. et al. Tuning the optoelectronic properties of amorphous MoOx films by reactive sputtering. Appl. Phys. Lett. 106, 202101 (2015).
Chen, M.-C. et al. Influence of electrode material on the resistive memory switching property of indium gallium zinc oxide thin films. Appl. Phys. Lett. 96, 262110 (2010).
Zhou, L. W. et al. Interface engineering for improving reliability of resistance switching in Cu/HfO2/TiO2/Pt structure. Appl. Phys. Lett. 107, 72901 (2015).
Li, M. et al. Nonvolatile resistive switching in metal/La-doped BiFeO3/Pt sandwiches. Nanotechnology 21, 425202 (2010).
Jeong, D. S., Schroeder, H. & Waser, R. Abnormal bipolar-like resistance change behavior induced by symmetric electroforming in Pt/TiO2/Pt resistive switching cells. Nanotechnology 20, 375201 (2009).
Sun, J., Jia, C. H., Li, G. Q. & Zhang, W. F. Control of normal and abnormal bipolar resistive switching by interface junction on In/Nb:SrTiO3 interface. Appl. Phys. Lett. 101, 133506 (2012).
Cho, S. et al. Self-assembled oxide films with tailored nanoscale ionic and electronic channels for controlled resistive switching. Nat. Commun. 7, 12373 (2016).
Lu, Z.-X. et al. Temperature dependences of ferroelectricity and resistive switching behavior of epitaxial BiFe O3thin films. Chin. Phys. B 24, 107705 (2015).
Chen, Q. N., Ou, Y., Ma, F. & Li, J. Mechanisms of electromechanical coupling in strain based scanning probe microscopy. Appl. Phys. Lett. 104, 242907 (2014).
Arslan, E., Bütün, S. & Ozbay, E. Leakage current by Frenkel–Poole emission in Ni/Au Schottky contacts on Al0.83In0.17N/AlN/GaN heterostructures. Appl. Phys. Lett. 94, 142106 (2009).
Chen, Y. et al. Reproducible bipolar resistive switching in entire nitride AlN/n-GaN metal-insulator-semiconductor device and its mechanism. Appl. Phys. Lett. 105, 193502 (2014).
Yang, J.-B. et al. Resistive switching characteristics of gallium oxide for nonvolatile memory application. Thin Solid Films 529, 200–204 (2013).
Aoki, Y. et al. Bulk mixed ion electron conduction in amorphous gallium oxide causes memristive behaviour. Nat. Commun. 5, 3473 (2014).
Zuo, Q. et al. Self-rectifying effect in gold nanocrystal-embedded zirconium oxide resistive memory. J. Appl. Phys. 106, 73724 (2009).
Chen, R. et al. Multilevel resistive switching effect in sillenite structure Bi12TiO20 thin films. Appl. Phys. Lett. 104, 242111 (2014).
Sharma, Y., Misra, P., Pavunny, S. P. & Katiyar, R. S. Multilevel unipolar resistive memory switching in amorphous SmGdO3 thin film. Appl. Phys. Lett. 104, 73501 (2014).
Wang, Y. H. et al. Investigation of the resistance switching in Au/SrTiO3:Nb heterojunctions. Appl. Phys. Lett. 103, 31601 (2013).
Toumi, S., Ouennoughi, Z., Strenger, K. C. & Frey, L. Determination of Fowler–Nordheim tunneling parameters in Metal–Oxide–Semiconductor structure including oxide field correction using a vertical optimization method. Solid-State Electron. 122, 56–63 (2016).
Butler, K. T. et al. Band energy control of molybdenum oxide by surface hydration. Appl. Phys. Lett. 107, 231605 (2015).
Sugiyama, K., Ishii, H., Ouchi, Y. & Seki, K. Dependence of indium–tin–oxide work function on surface cleaning method as studied by ultraviolet and x-ray photoemission spectroscopies. J. Appl. Phys. 87, 295–298 (2000).
This work is supported by the National Natural Science Foundation of China (51172044, 51471085), the Natural Science Foundation of Jiangsu Province of China (BK20151400), and the open research fund of Key Laboratory of MEMS of Ministry of Education, Southeast University.
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Wang, G., Li, C., Chen, Y. et al. Reversible voltage dependent transition of abnormal and normal bipolar resistive switching. Sci Rep 6, 36953 (2016). https://doi.org/10.1038/srep36953
This article is cited by
Forming-free RRAM device based on HfO2 thin film for non-volatile memory application using E-beam evaporation method
Journal of Materials Science: Materials in Electronics (2023)
Effects of Resistance States on the Magnetoresistance in Ni/Al2O3/Ni by Resistive Switching
Journal of Superconductivity and Novel Magnetism (2020)
Influence on loading terbium manganate on optical, thermal and electrical properties of polyvinyl alcohol nanocomposite films
Journal of Materials Science: Materials in Electronics (2019)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.