Abstract
Pressure experiments provide a unique opportunity to unravel new insights into glassforming liquids by exploring its effect on the dynamics of viscous liquids and on the evolution of the glass transition temperature. Here we compare the pressure dependence of the onset of devitrification, T_{on}, between two molecular glasses prepared from the same material but with extremely different ambientpressure kinetic and thermodynamic stabilities. Our data clearly reveal that, while both glasses exhibit different dT_{on}/dP values at low pressures, they evolve towards closer calorimetric devitrification temperature and pressure dependence as pressure increases. We tentatively interpret these results from the different densities of the starting materials at room temperature and pressure. Our data shows that at the probed pressures, the relaxation time of the glass into the supercooled liquid is determined by temperature and pressure similarly to the behaviour of liquids, but using stabilitydependent parameters.
Introduction
Glasses constitute one of the most intriguing materials in condensedmatter^{1}. Having a liquidlike disordered structure they behave mechanically as solids. Glasses are typically formed by cooling the liquid at a rate that overcomes the crystallization threat. One of the main features of glasses is the glass transition temperature, T_{g}, which characterizes the reversible transformation between the metastable supercooled liquid (SCL) state and the nonequilibrium amorphous solidlike material. The heat capacity of the glass is lower than that of the liquid and, upon heating, the jump in heat capacity marks the onset temperature of devitrification, T_{on}. Its value strongly depends on the previous thermal history of the glass and on the heating rate that follows a predefined cooling procedure. Another characteristic feature of glasses is that they age if stored below the glass transition temperature, T_{g}, for long periods of time^{2}. Aging produces glasses with enhanced stability. The stability of a glass can be established by means of its limiting fictive temperature (T_{f}’), i.e. the temperature at which the glass would be in equilibrium with its own liquid. While the glass transition temperature can only be accessed by cooling from the liquid state, the limiting fictive temperature is a property of the glass. The enthalpic T_{f}’ is obtained by integration of the normalized heat capacity curve that is measured during a calorimetric cooling scan or during a calorimetric heating scan starting from a given glassy state. Improving the glass stability by aging is a rather inefficient process due to the exponential increase of the relaxation time (or viscosity) below the glass transition temperature. A breakthrough in the field was the recent discovery that vapourdeposition can produce glasses that rival in stability with ambers naturally aged for millions of years^{3}. Those glasses, dubbed ultrastable glasses (UG), are typically grown at temperatures around 0.85 T_{g}, where T_{g} stands for the conventional glass (CG) transition temperature measured when the liquid is cooled at 10 K/min^{4,5,6,7,8}. Besides the enhanced kinetic and thermodynamic stability, vapourdeposited stable glasses have been shown to exhibit striking properties with respect to a conventional glass obtained from the liquid. Among them, higher densities and higher sound velocities which imply higher modulus^{9,10}, surfaceinitiated transformation mechanism into the supercooled liquid in thin films^{11,12,13,14}, absence of TLS (tunnelling twolevel systems) in Indomethacin (IMC) at cryogenic temperatures^{15} and lower heat capacities and thermal expansion coefficients^{16}. In particular, ultrastable IMC glasses, one of the archetypical UG’s^{3,5}, have a higher density by about 1.2% and a lower heat capacity of the glass by about 4%^{17}.
While the properties of the glass transition temperature have been deeply studied as a function of temperature by calorimetry in many different glasses, the pressure dependence of the calorimetric glass transition is a subject relatively little explored^{18}. The main reason can be attributed to experimental difficulties, in relation to applying high pressures in calorimetric experiments. On the contrary, dielectric or PressureVolumeTemperature (PVT) measurements are more abundant and permit to broadly infer several tendencies with respect to molecular interactions^{19,20}. For instance, it has been found that glasses with strong molecular interaction of hydrogen bonding type, systematically show lower values of dT_{g}/dP compared to glasses dominated by van der Waals forces^{18,21,22,23}. Another universal feature of glasses is that over a sufficiently large pressure range the pressure dependence of T_{g} is nonlinear, i.e. the effect of pressure on temperature weakens when pressure increases and can be adjusted with the empirical AnderssonAndersson equation^{24},
where κ_{1}, κ_{2} and κ_{3} are empirical constants. Davies and Jones derived, based on the Ehrenfest equations, two expressions for dT/dP in the liquid state evaluated at T_{g}^{25}. One of these expressions has been found to describe a large range of materials^{23}:
where ∆α and ∆C_{p} refer to the difference in isobaric expansivity and heat capacity at T_{g}, between the liquid and its corresponding glass and v is the molar volume at T_{g}. We are not aware of previous studies that analyse the pressure dependence of aged glasses over a wide range of stabilities.
In a previous work, we developed an empirical model that could simultaneously describe the relaxation time of the liquid and of glasses of different stability^{26}. The model was built with data taken at ambient pressure and therefore only depends on temperature and density. What would be the effect of pressure on glasses of different stability? Can we explain the new data measured as a function of pressure introducing a density dependence on pressure? We present in this work measurements of the devitrification temperature of ultrastable and conventional IMC glasses as a function of pressure. We also propose a tentative extension of our previous empirical model that aims to describe the relaxation dynamics of the system as a function of temperature and pressure by considering the dependence of density on these variables.
Results
Evolution of the onset of devitrification as a function of pressure
Two sets of Indomethacin samples, 20–40 μm thick UGs with T_{f}’ = 280 K and CGs obtained by cooling the liquid at 2–10 K/min, with T_{f}’ = 315 K, were temperaturescanned at pressures ranging up to 300 MPa in a homemade highpressure differential thermal analyser (HPDTA). The values of T_{f}’ at ambient pressure were determined from differential scanning calorimetry (DSC) measurements, as detailed in the methods section. The calorimetric curves obtained at different pressures, for both ultrastable and conventional glasses, are shown in Fig. 1. It is apparent for both glasses how the onset of devitrification shifts to higher temperatures as pressure increases.
Besides possible pressure effects, the shape and the smaller overshoot of the DTA signal at the onset of devitrification, T_{on}, for pressures above 0.1 MPa are due to the lack of sensitivity of the HPDTA setup, precluding a proper evaluation of the limiting fictive temperature as a function of pressure. Therefore, we will concentrate the analysis on the evolution of T_{on} as a function of pressure for both types of glasses (Fig. 2). We also note that onset temperatures obtained for CGs produced by cooling the liquid at normal pressure and then pressurizing the glass before carrying on the temperature scan or, alternatively, obtained by cooling the liquid at high pressure, were the same within the experimental uncertainty of our HPDTA setup. The observed reversibility between temperature and pressure does not necessarily hold for all glasses. While an increase of pressure in the conventional IMC glass or in the supercooled state induces a similar dynamic response, an increase of pressure in an ultrastable glass may have a different response. Therefore, if one could obtain a highly stable (aged) glass by cooling from the supercooled liquid, a change of pressure in the glassy state and a change of pressure in the liquid state, followed by a decrease of temperature could yield different final glassy systems.
The T_{on} vs. pressure data have been fitted using equation (1) (dashed lines in Fig. 2). For the CG (dT_{on}/dP)_{Patm} evaluated at P = 0.1 MPa yields a value of 280 ± 22 K/GPa. The CG was produced and measured at the same cooling/heating rate around 2 K/min. Therefore, the devitrification temperature evaluated on heating, T_{on} and the glass transition measured on cooling, T_{g}, coincide, i.e. From this we infer that dT_{on}/dP = dT_{g}/dP. In fact, our experimental value is in relatively good agreement with previous experimental data reported by Wojnarowska et al. using dielectric spectroscopy^{19}, who obtained 254 K/GPa (black points in Fig. 2). This value suggests that van der Waals interactions dominate over hydrogen bonding, as typically found in polymers and other van der Waals glassformers^{18,23}. Furthermore, the experimental value of (dT_{g}/dP)_{Patm} for the CG agrees remarkably well (within 3%) with the one calculated from equation (2) using available data from literature for glass and liquid specific volumes, thermal expansion coefficients and heat capacity jump (Table 1). The slope of the UG at P = 0.1 MPa is 201 ± 24 K/GPa, approximately 30% lower than the value obtained for the conventional IMC glass. This may be an indication of the existence of a higher degree of strong intermolecular interactions, such as hydrogen bonds, compared to conventional IMC, a tendency already reported in other works^{27,28}.
The direct comparison of the experimental data dT_{on}/dP for the ultrastable glass with equation (2) can be questioned since the devitrification temperature measured on heating, T_{on}, for the UG is different to the glass transition temperature evaluated on cooling. Ultrastable glasses are somehow equivalent to glasses cooled at extremely low cooling rates leading to T_{on} > T_{g} if the glass is reheated at conventional heating rates, i.e. 1–10 K/min. In this sense, the experimental dT_{on}/dP (201 K/GPa) and the value of dT_{g}/dP calculated using equation (2) (255 K/GPa) are not directly comparable. We could use the value of the limiting fictive temperature as a potential indicator of the validity of equation (2) for the UG, since T_{f}’ can be considered very close to the T_{g} of a hypothetical glass obtained by cooling the liquid at the equivalent cooling rate^{29}. In fact, using T_{f}’ in equation (2), dT/dP_{T = Tf’} yields a value of 210 GPa/K, much closer to the experimental value of dT_{on}/dP at T_{on}. If we assume that fictive temperatures are affected by pressure in the same way as the glass transition temperature T_{g}, then it would be natural to use the generalized limiting fictive temperature, as a trace of the validity of the Ehrenfesttype relationship^{30,31}. Although we have no theoretical framework supporting the validity of this experimental observation, it seems logical that the Ehrenfest relations can be applied at the point where the thermodynamic parameters of the glass are equal to those of its corresponding equilibrium liquid.
Interestingly, extrapolation of the AnderssonAndersson function (equation (1)) to higher pressures seems to yield a completely different scenario where the onsets of devitrification of both UG and CG, as well as dT_{on}/dP, approach each other as pressure increases. The dynamics and the thermodynamic state of vapourdeposited UGs at ambient pressure are clearly different with respect to CGs, cooled from the liquid. The different onset of the calorimetric glass transition temperature and the different value of the limiting fictive temperature at P = 0.1 MPa for UG and CG can be related to the change of the energy barriers between metabasins and their different energy position in the energy landscape respectively. At ambient pressure the difference in onset of devitrification is 20 K, while at higher pressures it is significantly reduced. i.e., at high pressure both glasses transform into the SCL at a similar temperature. Since during cooling/heating at 10 K/min the relaxation time of the system equals approximately 100 s at the transformation temperature^{19}, T_{on}(CG) ≈ T_{on}(UG) implicitly means that they share a common relaxation time at that temperature. This is a dramatic change, since at ambient pressure the variation in relaxation times between ultrastable and conventional glasses of many glassformers is 4–5 orders of magnitude^{4,7,13,26}.
Unfortunately, the experimental setup does not permit an accurate evaluation of the limiting fictive temperature at high pressures and therefore precludes finding a direct relation between T_{f}’ and pressure. Most of the prior measurements at high pressure have only access to dynamic properties of the system and the resulting information is not directly connected to the thermodynamics of the glass itself. However, to test whether a pressure change leads to irreversible changes in the structure of the glass we carried out an additional experiment. The methodology consisted on exposing a UG glass to a pressure of 300 MPa at room temperature. We then returned the glass to ambient pressure to subsequently perform a temperature scan. Figure 3 shows the calorimetric curves for a pressurized and an unperturbed glass measured at ambient pressure in the pressureDTA setup. As has been mentioned before, the sensitivity of this setup is rather limited and the shape and area of the transition peaks are not reproducible. Furthermore, the effects of pressure on the container crucible may yield variations in some features of the transition peak. However, the onset of the transition is indeed accurate and, as can be seen in the figure, both glasses show the same onset. Moreover, when comparing these two curves to measurements performed in a DSC (lower curves) on a UG glass, we can see how the onset of the transition is similar. This is by no means obvious, since according to the values of compressibility reported in the literature^{9}, a pressure of 300 MPa should change the volume of the glass by ~4%.
Glass relaxation time as a function of pressure
It has been shown that van der Waals’ bonded liquids and polymers obey powerlaw density scaling^{32,33,34}, which means that the average relaxation time of the liquid is a function of Tv^{γ}, where v(T, P) = 1/ρ is the specific volume and γ is a material constant. Casalini et al.^{33} derived an expression, , considering that the relaxation time is governed by the entropy of the system, S_{c}, as the AdamGibbs model proposes, but using a generalised equation for S_{c} that takes into account the influence of both temperature and, also, pressure (or, equivalently, changes in specific volume). In particular,
where and ϕ are constants and , with T_{g} the conventional value of glass transition temperature for IMC, 315 K and v_{g} the specific volume of a CG at that temperature. γ is a materialdependent constant, that is generally identified with the Grüneisen parameter, although the exact association is still under discussion^{34}.
Although this description is generally applied to equilibrium liquids, we concluded in a previous work that the relaxation times of glasses with different stability, as well as the supercooled liquid, can be described by equation (3) choosing the adequate stabilitydependent parameters in the expression for v(T, T_{f}’)^{26}. The proposed model was applied to data obtained at ambient pressure, as were all the relations used for the parameters of the model, such as the dependence of density on temperature. We suggest that the same model can be applied to the data presented here by introducing in the mentioned equations the dependence of density on pressure.
According to the Murnaghan equation of state^{35}, the bulk modulus of a system, K_{T}, can be expressed as a linear function of pressure,
where K_{0} is the bulk modulus at ambient pressure and K′ accounts for the linear variation of K_{T} with pressure. The dependence of K_{T} on temperature is typically small and is considered as a small perturbation at very high temperatures. In the temperature range explored in this work, we impose the bulk modulus to be constant in relation to temperature changes. Integrating the expression for the isothermal bulk modulus, and using equation 4, the specific volume of a system can be expressed as a function of pressure. The density, inverse of the specific volume, takes the following form,
where ρ_{0} is the density at normal pressure. Since the temperature range probed in this work is relatively small, we argue, as it was done when deriving the parameters used in equation (3), that the dependence of density on temperature can be considered linear. Introducing the effect of pressure given by equation (5), we obtain
The variation of the thermal expansion coefficient with pressure is related to the variation of the bulk modulus with temperature as . Since the dependence of K_{T} with temperature is small relative to K_{T}, we consider to be negligible. We also note that we have considered no dependence of the thermal expansion coefficient on temperature.
We show in Fig. 4 reported values from Paluch and coworkers of relaxation time of supercooled IMC liquid measured at different temperatures and pressures^{19}. We use these data to infer the values of K_{0} and K′ for the supercooled IMC liquid by fitting the curves using equations (3) and (6), where the values of , C, ϕ, γ, α and T_{ref} have been extracted from ref. 26. The fit of the data yields K_{T} = 2.52 · 10^{9} + 8.66P for the bulk modulus of IMC supercooled liquid.
We now focus on the relaxation time of glasses. In order to infer the value of K_{T} (equation (4)) for IMC glasses of different stability at ambient pressure, K_{0}, we use the adiabatic bulk modulus, K_{S}, reported by Kearns et al. at ambient pressure^{9}. The adiabatic bulk modulus and the isothermal bulk modulus can be related by ^{36}, where α is the thermal expansion coefficient and γ_{G} is the Grunesein parameter. The Grüneisen parameters for the two glasses can be calculated from thermodynamic quantities^{26}, yielding and . We obtain Pa and Pa for the bulk modulus of CG and UG at atmospheric pressure, respectively. Further details can be found in the Supplementary Information. We note that the use of a different value of γ_{G} does not alter the conclusions reached below, but only the absolute value of K_{T}.
Since this set of reported data has been measured at ambient pressure, no information regarding K′ can be derived. Therefore, we will consider two alternative plausible scenarios. First, we consider that K′ remains unaltered after vitrification and, therefore, glasses and liquid have the same K′ value, . By introducing the dependence of density on pressure in equation (3) and using the parameters found in ref. 26, we can infer the relaxation time of both glasses as a function of temperature and pressure, . The temperature at which s is considered as the onset of devitrification^{19}. We have plotted these temperatures in Fig. 5a for the conventional and ultrastable IMC glass for different values of pressure (dashed lines in Fig. 5). We find that, under the assumption of invariant K′, the onset of devitrification of conventional and ultrastable glasses do not seem to approach at high pressures, contrary to our experimental results. As a second scenario, we assume that: i) the bulk modulus of glass and liquid respond differently to pressure changes and ii) that this response depends on the stability of the glass. Considering the calculated values of K_{0}, we speculate that the value of K′ follows the same tendency, i.e. the larger the thermodynamic stability of the glass the higher the values of K_{0} and K′ are. In particular, we find that we can qualitatively describe the experimental data shown in Fig. 2 by assuming and and using equations (3) and (6), as can be seen in Fig. 5b. We note that, according to this model, the density of each glass is different, as well as its dependence with pressure. A similar result was deduced from the application of the meanfield theory on glasses with different stability^{37}.
Based on the above description we tentatively propose that the different curvature in Fig. 2 is due to the different bulk modulus between the conventional and ultrastable glass. In particular, ultrastable glasses not only have a higher bulk modulus than CG at ambient pressure, as was already reported^{9}, but also this value is more affected by pressure than the bulk modulus of the liquid or conventional glass.
Under this framework and considering the relationship between density and relaxation time expressed in equation (3), the experimental data shown in Fig. 2 would depict a scenario in which relaxation dynamics of glasses with very different stabilities at ambient pressure (ΔT_{f}’ = 35 K), have similar relaxation dynamics at sufficiently high pressures. A representation of this scenario is given in Fig. 6. In other words, high pressure would make, from our experimental point of view, glasses of different stability practically undistinguishable. We remark that by using equations (3, 4, 5, 6) to describe the dynamics of ultrastable and conventional glasses, we are implicitly assuming that the observed differences between these two systems mainly originate from their distinct density values at atmospheric pressure and to the different density variation with the thermodynamic parameters, pressure and temperature. From this point of view one could infer that an ultrastable glass behaves similarly with pressure as a highly aged glass. Although more data is necessary in order to identify the specific dependence of density with pressure, the analysis developed here permits us to tentatively extend the relaxation time model that described the behaviour of a liquid and its glasses of different stability to include the influence of pressure. The analysis presented in this work, would indicate that the relaxation time of glasses of different stability will converge in the high pressure limit.
Conclusions
We have analysed the pressure dependence of the glasstoliquid transformation in two glasses of indomethacin that have extremely different values of limiting fictive temperature, ∆T_{f}’ = 30 K. The two glasses show a different dependence of the temperature of devitrification on pressure when evaluated between normal pressure and 300 MPa. This variation could be related to the differences in packing and molecular binding of the two glasses. Interestingly, extrapolation to high pressures, shows that both glasses would share the same onset temperature and the same (dT_{on}/dP)_{Patm}. Preliminary results show an invariance of the onset temperature of ultrastable glasses before and after submitting the sample to high pressure, an indication that pressure would not irreversibly affect the stability of the glass.
We extend the joint description of relaxation dynamics of glasses and liquids, including a particular pressure dependence of the glass and liquid density through the bulk modulus of the system, K_{T} = K_{0} + K′P, where K_{0} is the isothermal bulk modulus at ambient pressure and . Under this assumption, we find that the measured experimental data can be satisfactorily described considering a systemdependent value of K′, i.e. different glasses and liquids have different values of K′. While further experiments are required to corroborate this assumption, its verification would imply that i) we can extend our relaxation time generalization, at least qualitatively, to variations of pressure by assuming a particular dependence of density on pressure and ii) the bulk modulus of glasses with different stability and the liquid would be differently affected by pressure.
According to the unified description of glass dynamics, the relaxation time of glasses at high pressure converges towards a unique value, in analogy to the effect of temperature on glasses with different stability, that converges to a unique value of relaxation time at high temperatures.
Methods
Sample Preparation
Indomethacin (IMC) films with thickness ranging 20–40 μm were grown by thermal evaporation within a UHV setup with base pressure of 5 × 10^{−9 }mbar. The growth rate was fixed to 0.12 ± 0.02 nm/s and the deposition temperature was set to 266 K, 0.85 T_{g}, values that produces glasses with high kinetic and thermodynamic stability. The films were grown onto aluminium foil to introduce sufficient mass (100 mg) in the calorimetric vessels and enable subsequent highpressure experiments. Conventional glasses of IMC were prepared by cooling approximately 200 mg of melted IMC at a cooling rate of around 2 K/min directly into the calorimetric vessel at ambient pressure. Crystalline IMC powder with purity higher than 99.9% was purchased from SigmaAldrich and used without further purification.
Measurement Protocol
The heat capacity of IMC ultrastable and conventional glasses at ambient pressure was measured by Differential Scanning Calorimetry (DSC) with a Perkin Elmer DSC7. To calculate the limiting fictive temperature of each type of glass we have followed the procedure described by Moynihan et al.^{38}. Basically, the limiting fictive temperature is determined by the intersection temperature between the enthalpy of the liquid and the enthalpy of the glass, which are obtained by integrating the specific heat as a function of the temperature.
Experiments above ambient pressure were carried out with a homemade highpressure differential thermal analysis (HPDTA) setup, described in detail elsewhere^{39}. Essentially, the temperature of the irimo calorimeter block is surrounded by an external resistance for temperature linear changes controlled by a Pt100 thermometer embedded in the block. Sample and reference temperature sensors are calibrated Ktype (chromelalumel) thermocouples which are inserted into Sn cylindrical pans. The pressure into the calorimetric block was transmitted by compressing a liquid and measured by calibrated Bourdon gauges with an accuracy better than 0.5 MPa. Because pressure increases concomitantly with the temperature increase during the scan, the error in P_{g} is intrinsically linked to the error in T_{on}, which is mainly associated with the onset uncertainty. For the ultrastable glass, the asdeposited samples together with the Al foil substrate were mixed with an inert perfluorinated liquid (Galden^{®} from Bioblock Scientifics, Illkirch, France) before sealing to guarantee the hydrostatic transmission of pressure as well as to ascertain that incell volumes were free from residual air. DSC runs at ordinary pressure (i.e., in standard aluminum pans) with mixtures of IMC and perfluorinated liquid were carried out to verify that the latter was inert.
Afterwards, the produced glass (CG) is pressurized to each pressure value, in the range from 0.1 to 300 MPa. After a stabilization time, a heating ramp at 2 K/min was initiated and the sample was heated from 300 K to 400 K in order to record the devitrification signal. Subsequently, the supercooled liquid is cooled back to ambient temperature at the same pressure and at around 2 K/min, obtaining a new conventional glass. Alternatively, the supercooled liquid was depressurized and, afterwards, cooled down to ambient temperature to produce the glass. As indicated in the main text, there is no appreciable difference in the onset of devitrification of the conventional glass produced by either of the described procedures.
In the case of the UG, each measured sample was kept at ambient temperature while the pressure was set to the working value, in the range from 0.1 to 300 MPa. After a stabilization time, a heating ramp at 2 K/min was initiated and the sample was heated from 300 K to 400 K. Each measurement was performed on a new sample. After the first calorimetric scan the glass transforms into the supercooled liquid, which is subsequently cooled at around 2 K/min and submitted to a second heating scan at a similar pressure to make certain that the now conventional glass falls on the same curve obtained for the conventional glass samples prepared by melting IMC.
Additional Information
How to cite this article: RodríguezTinoco, C. et al. Ultrastable glasses portray similar behaviour to ordinary glasses at high pressure. Sci. Rep. 6, 34296; doi: 10.1038/srep34296 (2016).
References
Angell, C. A., Ngai, K. L., McKenna, G. B., McMillan, P. F. & Martin, S. W. Relaxation in glassforming liquids and amorphous solids. J. Appl. Phys. 88, 3113 (2000).
PérezCastañeda, T., JiménezRiobóo, R. J. & Ramos, M. A. TwoLevel Systems and Boson Peak Remain Stable in 110MillionYearOld Amber Glass. Phys. Rev. Lett. 112, 165901 (2014).
Swallen, S. F. et al. Organic glasses with exceptional thermodynamic and kinetic stability. Science 315, 353–356 (2007).
LeonGutierrez, E., Sepúlveda, A., Garcia, G., ClavagueraMora, M. T. & RodríguezViejo, J. Stability of thin film glasses of toluene and ethylbenzene formed by vapor deposition: an in situ nanocalorimetric study. Phys. Chem. Chem. Phys. 12, 14693–14698 (2010).
Kearns, K. L. et al. Hiking down the Energy Landscape: Progress Toward the Kauzmann Temperature via Vapor Deposition. J. Phys. Chem. B 112, 4934–4942 (2008).
Ramos, S. S. L. L. M., Oguni, M., Ishii, K. & Nakayama, H. Character of devitrification, viewed from enthalpic paths, of the vapordeposited ethylbenzene glasses. J. Phys. Chem. B 115, 14327–14332 (2011).
RodríguezTinoco, C., GonzalezSilveira, M., RàfolsRibé, J., Garcia, G. & RodríguezViejo, J. Highly stable glasses of celecoxib: Influence on thermokinetic properties, microstructure and response towards crystal growth. J. Non. Cryst. Solids 407, 256–261 (2015).
LeónGutierrez, E., Garcia, G., ClavagueraMora, M. T. & RodríguezViejo, J. Glass transition in vapor deposited thin films of toluene. Thermochim. Acta 492, 51–54 (2009).
Kearns, K. L., Still, T., Fytas, G. & Ediger, M. D. Highmodulus organic glasses prepared by physical vapor deposition. Adv. Mater. 22, 39–42 (2010).
Pogna, E. A. A. et al. Probing equilibrium glass flow up to exapoise viscosities. Proc. Natl. Acad. Sci. USA 112, 2331–2336 (2015).
Kearns, K. L., Whitaker, K. R., Ediger, M. D., Huth, H. & Schick, C. Observation of low heat capacities for vapordeposited glasses of indomethacin as determined by AC nanocalorimetry. J. Chem. Phys. 133, 014702 (2010).
Sepúlveda, A., Swallen, S. F., Kopff, L. A., McMahon, R. J. & Ediger, M. D. Stable glasses of indomethacin and α,α,βtrisnaphthylbenzene transform into ordinary supercooled liquids. J. Chem. Phys. 137, 204508 (2012).
RodríguezTinoco, C. et al. Evaluation of growth front velocity in ultrastable glasses of indomethacin over a wide temperature interval. J. Phys. Chem. B 118, 10795–10801 (2014).
RodriguezTinoco, C., GonzalezSilveira, M., RafolsRibe, J., Lopeandia, A. F. & RodriguezViejo, J. Transformation kinetics of vapordeposited thin film organic glasses: the role of stability and molecular packing anisotropy. Phys. Chem. Chem. Phys. 17, 31195–31201 (2015).
PerezCastaneda, T., RodriguezTinoco, C., RodriguezViejo, J. & Ramos, M. A. Suppression of tunneling twolevel systems in ultrastable glasses of indomethacin. Proc. Natl. Acad. Sci. 111, 11275–11280 (2014).
Dalal, S. S., Fakhraai, Z. & Ediger, M. D. Highthroughput ellipsometric characterization of vapordeposited indomethacin glasses. J. Phys. Chem. B 117, 15415–15425 (2013).
Kearns, K. K. L., Ediger, M. D. M., Huth, H. & Schick, C. One micrometer length scale controls kinetic stability of lowenergy glasses. J. Phys. Chem. Lett. 1, 388–392 (2009).
Roland, C. M., HenselBielowka, S., Paluch, M. & Casalini, R. Supercooled dynamics of glassforming liquids and polymers under hydrostatic pressure. Reports Prog. Phys. 68, 1405–1478 (2005).
Wojnarowska, Z. et al. Broadband dielectric relaxation study at ambient and elevated pressure of molecular dynamics of pharmaceutical: indomethacin. J. Phys. Chem. B 113, 12536–12545 (2009).
Paluch, M. et al. General rules prospected for the liquid fragility in various material groups and different thermodynamic conditions. J. Chem. Phys. 141, 134507 (2014).
Zhang, S. H., Casalini, R., Runt, J. & Roland, C. M. Pressure Effects on the Segmental Dynamics of HydrogenBonded Polymer Blends. Macromolecules 36, 9917–9923 (2003).
Pawlus, S., Paluch, M., Ziolo, J. & Roland, C. M. On the pressure dependence of the fragility of glycerol. J. Phys. Condens. Matter 21, 332101 (2009).
Koperwas, K., Grzybowski, A., Tripathy, S. N., Masiewicz, E. & Paluch, M. Thermodynamic consequences of the kinetic nature of the glass transition. Sci. Rep. 5, 17782 (2015).
Andersson, S. P. & Andersson, O. Relaxation Studies of Poly(propylene glycol) under High Pressure. Macromolecules 31, 2999–3006 (1998).
Davies, R. O. & Jones, G. O. Thermodynamic and kinetic properties of glasses. Adv. Phys. 2, 370–410 (1953).
RodríguezTinoco, C., RàfolsRibé, J., GonzálezSilveira, M. & RodríguezViejo, J. Relaxation dynamics of glasses along a wide stability and temperature range. arXiv 26 at <http://arxiv.org/abs/1603.08829> (2016).
Andronis, V., Yoshioka, M. & Zografi, G. Effects of sorbed water on the crystallization of indomethacin from the amorphous state. J. Pharm. Sci. 86, 346–351 (1997).
Dawson, K. J., Kearns, K. L., Ediger, M. D., Sacchetti, M. J. & Zografi, G. D. Highly stable indomethacin glasses resist uptake of water vapor. J. Phys. Chem. B 113, 2422–2427 (2009).
Badrinarayanan, P., Zheng, W., Li, Q. & Simon, S. L. The glass transition temperature versus the fictive temperature. J. Non. Cryst. Solids 353, 2603–2612 (2007).
Christian Öttinger, H. Nonequilibrium thermodynamics of glasses. Phys. Rev. E 74, 011113 (2006).
Wondraczek, L., Krolikowski, S. & Behrens, H. Relaxation and PrigogineDefay ratio of compressed glasses with negative viscositypressure dependence. J. Chem. Phys. 130, 204506 (2009).
Dyre, J. C. Hidden scale invariance in condensed matter. J. Phys. Chem. B 118, 10007–10024 (2014).
Casalini, R., Mohanty, U. & Roland, C. M. Thermodynamic interpretation of the scaling of the dynamics of supercooled liquids. J. Chem. Phys. 125, 014505 (2006).
Roland, C. M., Feldman, J. L. & Casalini, R. Scaling of the local dynamics and the intermolecular potential. J. Non. Cryst. Solids 352, 4895–4899 (2006).
Murnaghan, F. D. The Compressibility of Media under Extreme Pressures. Proc. Natl. Acad. Sci. 30, 244–247 (1944).
Anderson, D. L. Theory of the Earth (Blackwell Scientific Publications, 1989).
Mariani, M. S., Parisi, G. & Rainone, C. Calorimetric glass transition in a meanfield theory approach. Proc. Natl. Acad. Sci. 112, 2361–2366 (2015).
Moynihan, C. T., Easteal, A. J., Bolt, M. A. & Tucker, J. Dependence of the Fictive Temperature of Glass on Cooling Rate. J. Am. Ceram. Soc. 59, 12–16 (1976).
Mañosa, L. et al. Giant solidstate barocaloric effect in the NiMnIn magnetic shapememory alloy. Nat. Mater. 9, 478–481 (2010).
Acknowledgements
This work was financially supported by the Spanish MINECO MAT201340896P, MAT201457866REDT and FIS201454734P. M.B., J.L.T. and P.L. also acknowledge support from Generalitat de Catalunya, 2014SGR00581.
Author information
Affiliations
Contributions
C.R.T., J.L.T. and J.R.V. conceived the idea, C.R.T. and J.R.V. prepared the samples, M.B., P.L. and J.L.T. performed the pressure experiments, C.R.T., J.L.T. and J.L.G. analysed the data, J.L.T. and J.R.V. supervised the work, C.R.T., M.G.S. and J.R.V. with the help of all authors, wrote the paper. All authors contributed to the discussion of the results.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
RodríguezTinoco, C., GonzálezSilveira, M., Barrio, M. et al. Ultrastable glasses portray similar behaviour to ordinary glasses at high pressure. Sci Rep 6, 34296 (2016) doi:10.1038/srep34296
Received
Accepted
Published
DOI
Further reading

Density Scaling in Ionic Glass Formers Controlled by Grotthuss Conduction
The Journal of Physical Chemistry B (2019)

Why is the change of the Johari–Goldstein βrelaxation time by densification in ultrastable glass minor?
Physical Chemistry Chemical Physics (2018)

Vapordeposited organic glasses exhibit enhanced stability against photodegradation
Soft Matter (2018)

Secondary relaxation in ultrastable etoricoxib: evidence of correlation with structural relaxation
Physical Chemistry Chemical Physics (2018)

Perspective: Highly stable vapordeposited glasses
The Journal of Chemical Physics (2017)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.