Abstract
One of the most promising means to increase the energy density of state-of-the-art lithium Li-ion batteries is to replace the graphite anode with a Li metal anode. While the direct use of Li metal may be highly advantageous, at present its practical application is limited by issues related to dendrite growth and low Coulombic efficiency, CE. Here operando electrochemical scanning transmission electron microscopy (STEM) is used to directly image the deposition/stripping of Li at the anode-electrolyte interface in a Li-based battery. A non-aqueous electrolyte containing small amounts of H2O as an additive results in remarkably different deposition/stripping properties as compared to the “dry” electrolyte when operated under identical electrochemical conditions. The electrolyte with the additive deposits more Li during the first cycle, with the grain sizes of the Li deposits being significantly larger and more variable. The stripping of the Li upon discharge is also more complete, i.e., there is a higher cycling CE. This suggests that larger grain sizes are indicative of better performance by leading to more uniform Li deposition and an overall decrease in the formation of Li dendrites and side reactions with electrolyte components, thus potentially paving the way for the direct use of Li metal in battery technologies.
Similar content being viewed by others
Introduction
Over the years there have been many attempts to eliminate the formation of dendrites in Li metal batteries using various means including by increasing the uniformity of the solid electrolyte interphase (SEI) layer1,2,3,4,5,6,7,8,9, alloying the Li metal deposits with other metals10,11, or using a polymer electrolyte to mechanically inhibit the growth12. Recently, it was demonstrated that dendrite formation was reduced and uniform Li deposition was achieved by using a highly concentrated electrolyte composed of 4M lithium bis(fluorosulfonyl)imide (LiFSI) in 1,2-dimethoxyethane (DME)3. This approach enabled high-rate cycling with a >99% Coulombic efficiency (CE) for the Li deposition/stripping without dendrite growth. A similar increase in the uniformity of the Li films grown on the anode during the charging process has been obtained by incorporating a CsPF6 additive into the electrolyte, which resulted in the formation of high density, self-aligned nanorod structures surrounded by the SEI layer13. Notably, LiPF6-based electrolytes containing trace amount of H2O (25–50 ppm) also suppress Li dendrite growth and lead to the same formation of Li columnar structures as noted for the CsPF6 additive (in contrast to the Li morphology obtained using an electrolyte containing only the residual H2O (~10 ppm) content), thus demonstrating that minor changes to the electrolyte’s chemical composition can completely transform the Li deposition morphology14.
To investigate how the morphology of the Li deposits leads to improved CE, we have employed an operando electrochemical cell (ec-cell), illustrated in Fig. 1, in an aberration-corrected scanning transmission electron microscope (STEM) to study the cycling process at high spatial resolution. This approach enables the direct observation of the initial stages of Li deposition/stripping in an electrolyte (1M LiPF6 in propylene carbonate (PC)) with controlled trace-amounts of H2O additive (10 and 50 ppm). In recent years, rapid growth has occurred in the use of in-situ liquid stages for TEM15 that, in addition to electrochemistry16,17,18,19,20,21, have enabled nucleation/growth phenomena22,23,24,25 and biological systems26 to be observed first-hand providing tremendous insight into molecular-level interactions. By using this stage to evaluate the initial stages of Li deposition, we have correlated the deviations in the microstructure evolution directly with the presence of the additive.
Figure 2 shows a summary of the key parts of an electrochemical deposition/stripping cycle for two electrolytes prepared and analyzed under identical conditions. During the CV cycling, the deposition and stripping of Li metal can be clearly delineated — i.e., since Li is less dense than the surrounding electrolyte, it can be identified by its “reversed” contrast in the STEM images27. As seen from the video captures at the start of the scan, at the end of the deposition and stripping processes there are significant differences in both the amount and morphology of the Li deposited and stripped using the two electrolytes (Fig. 2B–G). The amount of Li at the electrode-electrolyte interface can be quantified by using a multi-particle tracking algorithm28. In each of the video frames, the Li grains are not moving, but are instead actively nucleating and growing from the electrode surface into the electrolyte solution. To determine the changes in size and shape, we first applied an image thresholding method to each of the video frames to extract the outlines and the interiors of select Li nanoparticles/grains. We then combined this method with the M 1⁄4 3, Henriques’ method, Jaqaman’s method and MCMC Data Association to relate the individual extractions from the different time frames to track the nanoparticles and their interactions28. Figure 3A shows that the electrolyte with 50 ppm of the H2O additive exhibits a more rapid Li deposition and an increase in the amount of Li deposited at the peak of the deposition. More importantly, at the end of the stripping process, there is less overall Li remaining at the interface. This means that the electrochemical process in the electrolyte with the additive is more reversible than in the one without it, i.e., it has a higher CE (85% compared to 75% for the electrolyte without the additive). We can also use the tracking algorithm to measure the grain size of the Li deposits (Fig. 3B). There are issues with the overlap of grains (the image is a 2-D projection of an evolving 3-D structure) making it difficult to measure all of the grains independently. For both of the experiments, however, there are 8 grains that can be clearly identified throughout the CV scans (Figures S2 and S3). In the case of the electrolyte without the additive, the grain size is small and relatively uniform with clearly defined interfaces (grain boundaries). In contrast, for the electrolyte with the additive, the grain sizes are 2–3 times larger on average with a much wider variability in size. Thus, there are fewer grain boundaries in the deposits that form with the additive. As we will discuss later in this paper, the grain size of the electrodeposit appears to correlate directly with CE.
To understand the origins of the differences in the morphology of the electrodeposited Li in the two electrolytes, the chemistry that is occurring in the presence of an increased H2O content (50 ppm) must be considered. When H2O is added to the electrolyte, it reacts as follows:
The electrolyte with the additive therefore has an increased HF content relative to the one without the additive. This, in turn, promotes the formation of LiF:
LiF is a well-known component within the solid electrolyte interphase (SEI) layer that forms during the cycling of Li-ion batteries1,2, which, during electrodeposition, has been shown to be highly effective at increasing the ionic conductivity of the system. Other well-known components of the SEI layer include lithium alkyl carbonates (e.g., C3H6(OCO2Li)), LiCO3 and Li2O, in addition to other organic products from the solvent. Note that, for the initial stages of the Li deposition/stripping in the Li battery shown in Fig. 1, the term SEI layer refers to the electrochemical products formed at the interface.
Each of the SEI components has a different contribution to the ionic and electronic conductivities of the interface and LiF, in particular, has much higher conductivities than the other components. It is this which we believe is the origin of the dramatic effect on the Li plating morphology and its relationship to the cycling characteristics (the additive is present at the ppm level, meaning that it is widely distributed and will only affect certain areas during the electrodeposition process). Recent work on the failure mechanisms which manifest under fast-charging conditions has shown that the SEI layer consists of highly porous regions of organic electrolyte products29. Fast-charging increases the concentration of the non-conducting porous/organic regions relative to the amount of the Li metal deposited, resulting in tortuous conducting paths and an increase in the overall battery impedance due to the formation of a non-uniform layer with poor electronic/ionic conductivity. For the electrolyte with 50 ppm of H2O, the increased amount of LiF formed increases the ionic conductivity of the SEI layer, which in turn increases the round trip efficiency of the Li deposition/stripping processes, resulting in a lower impedance and decreased buildup of “dead Li” (more of the electron density at the interface reacts with the continuous supply of Li+ cations rather than neighboring electrolyte components), as compared to the electrolyte with only 10 ppm of H2O. Similarly, the higher conductivity facilitates larger grain growth and the subsequent stripping of the Li metal as the grains remain in electrical contact with the electrode. The result is a more uniform Li and SEI layer deposition, an absence of dendritic Li growth and a reduction in the accumulation of electrolyte degradation products and dead Li metal (sometimes called mossy Li)13.
The effect of the SEI layer conductivity on the morphology of the electrodeposits was further validated by studying galvanostatic charging under constant current conditions of 1 and 4 mA cm−2; this permits direct monitoring of the rate of Li deposition/stripping for a set time period. Figure 4A shows the current density of the cell as a function of time for 1 mA cm−2 (the data for 4 mA cm−2 are reported in Figure S4). Figure 4B shows BF (left) and HAADF (right) frames from the movies (Movies SM3 and SM4) in which we focus primarily on the insertion and accumulation of Li into the Pt electrode27. As seen from Fig. 4C (using the tracking algorithms to measure the electrode size from the Movies SM3-SM6), the effect of the additive promotes faster Li+ cation diffusion and larger Li grain growth at the electrode. Under fast-charging conditions (4 mA cm−2), the Pt electrode itself degrades for the electrolyte without the additive. In stark contrast, the electrolyte with the additive is stable under the fast-charging conditions suggesting that the diffusion of Li+ cations through the SEI layer is faster with the additive, i.e., under the fast-charging conditions, the electrolyte without the additive cannot supply enough Li+ cations to the electrode surface, resulting in electrostatic breakdown. These results again suggest that larger grain sizes of the electrodeposits are desirable for better CE.
The quantified observations shown in Figs 3 and 4 allow us to understand the impact of grain morphology on the deposition/stripping processes and the CE shown in Fig. 5. The formation of LiF in the SEI layer provides “fast” Li+ cation diffusion channels that lead to the rapid deposition of Li on the surface of the electrode (and during discharge, the rapid stripping of Li and thus the higher cycling CE). Extended over many cycles, the increase in the CE and ease of the Li deposition/stripping will result in a much more compact Li layer on the surface, a reduction in the formation of dendrites and the minimization of SEI and dead Li buildup on the electrode surface.
Conclusions
In conclusion, we have demonstrated that the formation of Li dendrites can be effectively controlled and suppressed by understanding and optimizing the effect of the H2O content on the morphology of the Li grains. The elevated H2O content increases the total concentration of HF in the electrolyte and consequently increases the LiF concentration in the SEI layer, which leads to the abnormally large grain growth of Li as opposed to the “mossy” Li formed in the dry electrolyte. The appearance of large grains of Li in the electrodeposit can be taken as a direct measurement of the improved CE of the battery — large grains are more desirable for high CE values, while small randomly interconnected grains are not. The LiF-rich SEI layer is able to sustain faster Li+ cation diffusion across the electrolyte-electrode interface through the highly conductive LiF channels, in stark contrast to what occurs for the lower concentration of LiF. Such analyses indicate that controlling the diffusion of Li+ cations through the SEI layer defines the Li grain size and presents a critical opportunity to tailor the performance of Li metal anodes, which may lead to their successful incorporation into next generation batteries.
Methods
Materials
The electrolyte-grade lithium hexafluorophosphate, LiPF6 and propylene carbonate, PC, were purchased from BASF and used without further purification. The specific H2O content in the electrolytes was determined by Karl Fischer titration, while the HF level was estimated using an acid–base titration technique30. The water content in the PC solvent and 1M LiPF6 in PC electrolyte were 13 and 10 ppm H2O, respectively. The additional amount of H2O (raising the amount to 50 ppm) was introduced after preparing the 1M LiPF6 in PC electrolyte using a micropipette. The precise water content in the electrolyte during the hydrolysis reaction was measured at specific time intervals by monitoring the amount of the H2O and HF in the electrolytes.
Characterization
The in-situ ec-(S)TEM experiments shown here were performed on a FEI 80–300 kV Cs corrected Titan microscope equipped with a Schottky field-emission electron source and a CEOS hexapole spherical aberration probe corrector. For these experiments, the microscope was operated at 300 kV in both bright field (BF) and high angle annular dark field (HAADF) modes. All images were obtained after calibration of the electron dose, which was kept below ≤0.3 electrons Å−2 s−1 to avoid beam damage effects18,28. Under these conditions, typical beam effects such as the formation of bubbles and/or damage resulting in the formation of precipitates from the breakdown of the electrolyte18 are completely avoided.
In-situ electrochemical measurements
The measurements were performed with a commercially available Poseidon 510 (Protochips Inc., Raleigh, NC, USA) microfluidic in-situ electrochemical stage, which allows for the simultaneous observation of electrochemical measurements with video showing dynamics of Li dendrite deposition/stripping process at the Pt electrode surface in the liquid environment. The electrochemical cell itself is located in the tip of the TEM holder with two Si microchips (a top ec-chip with three Pt electrodes, a 500 nm SU-8 spacer and a 50 nm Si3N4 membrane and a bottom chip with a 150 nm spacer and a 50 nm Si3N4 membrane) sealed within the tip by two O-rings (Fig. 1). This configuration is then used to form an operating battery with an anode, cathode and non-aqueous liquid electrolyte. The microfluidic channels are integrated inside the holder to permit the circulation of the electrolyte at a 3 μL min−1 flow rate, thereby providing the Li+ ions for the battery operation. This approach permits the direct observation of the electrochemical processes at the anode/electrolyte interface without the need for a Li metal source. To prevent unwanted contamination of the battery electrolyte (1M LiPF6 in PC) by H2O and O2, the electrolyte solutions were prepared and the operando cell was assembled in an Ar glove box. The control experiment performed on an electrolyte without the additive had a residual H2O content of 10 ppm, while the electrolyte with the additive was designed to have an H2O content of 50 ppm13 (details on the measurement of H2O content are given in the Supplementary Information and shown in Fig. 1). The cyclic voltammetry experiments (CV) were conducted with a Gamry Reference 600 potentiostat scanning at a rate of 20 mV s−1, with a simultaneous recording of the video sequence of the Li deposition/stripping at the Pt electrode (also shown in Fig. 1). Full movies of the experiments are provided in the Supplementary Information as Supplementary Movies 1 and 2 (SM1 and SM2).
Additional Information
How to cite this article: Mehdi, B. L. et al. The Impact of Li Grain Size on Coulombic Efficiency in Li Batteries. Sci. Rep. 6, 34267; doi: 10.1038/srep34267 (2016).
References
Tarascon, J. M. & Armand, M. Issues and challenges facing rechargeable lithium batteries. Nature 414, 359–367 (2001).
Goodenough, J. B. & Kim, Y. Challenges for rechargeable Li batteries. Chem. Mater. 22, 587–603 (2010).
Qian, J. et al. High rate and stable cycling of lithium metal anode. Nature Commun. 6, 6362 (2015).
Jie, X. L. & Nazar, L. F. J. Advances in L-S batteries. Mater. Chem. 20, 9821–9826 (2010).
Bruce, P. G., Freunberger, S. A., Hardwick L. J. & Tarascon, J. M. Li-O2 and Li-S batteries with high energy storage. Nat. Mater. 11, 19–29 (2012).
Verma, P., Maire, P. & Novak, P. A review of the features and analyses of the solid electrolyte interphase in Li-ion batteries. Electrochim. Acta 55, 6332–6341 (2010).
Ota, H., Wang. X. M. & Yasakuwa, E. Characterization of Lithium Electrode in Lithium Imides/Ethylene Carbonate and Cyclic Ether Electrolytes II. Surface Chemistry. J. Electrochem. Soc. 151, A427–A436 (2004).
Mogi, R. et al. Effects of Some Organic Additives on Lithium Deposition in Propylene Carbonate. J. Electrochem. Soc 149, A1578–A1583 (2002).
Aurbach, D., Zinigrad, E., Cohen, Y. & Teller, H. A short review of failure mechanisms of lithium metal and lithiated graphite anodes in liquid electrolyte solutions. Solid State Ionics 148, 405–416 (2002).
Matsuda, Y. Behavior of lithium/electrolyte interface in organic solutions. J. Power Sources 43, 1–7 (1993).
Ishikawa, M., Morita, M. & Matsuda, M. In situ scanning vibrating electrode technique for lithium metal anodes. J. Power Sources 68, 501–505 (1997).
Monroe, C. & Newman, J. Dendrite growth in lithium/polymer systems: A propagation model for liquid electrolytes under galvanostatic conditions. J. Electrochem. Soc. 150, A1377–A1384 (2003).
Zhang, Y. et al. Dendrite-free lithium deposition with self-aligned nanorod structure. Nano Lett. 14, 6889–6896 (2014).
Qian, J. et al. Dendrite-free Li deposition using trace-amounts of water as an electrolyte additive. Nano Energy 15, 135–144 (2015).
de Jonge, N. & Ross, F. M. Electron microscopy of specimens in liquid. Nat. Nanotechnol. 6, 695–704 (2011).
White, E. R. et al. In Situ transmission electron microscopy of lead dendrites and lead ions in aqueous solution. ACS Nano 6, 6308–6317 (2012).
Gu, M. et al. Demonstration of an electrochemical liquid cell for operando transmission electron microscopy observation of the lithiation/delithiation behavior of Si nanowire battery anodes. Nano Lett. 13, 6106–6112 (2013).
Abellán, P. et al. Probing the degradation mechanisms in electrolyte solutions for Li-ion batteries by in situ transmission electron microscopy. Nano Lett. 14, 1293–1299 (2014).
Sutter, E. et al. In-situ liquid cell electron microscopy of Ag-Pd galvanic replacement reactions on Ag nanoparticles. Nat. Commun. 5, 4946–4950 (2014).
Zeng, Z. et al. Visualization of electrode-electrolyte interfaces in LiPF6/EC/DMC electrolyte for lithium ion batteries via in situ. TEM Nano Lett. 14, 1745–1750 (2014).
Sacci, R. L. et al. Nanoscale imaging of fundamental Li battery chemistry: Solid-electrolyte interphase formation and preferential growth of lithium metal nanoclusters. Nano Lett. 15, 2011–2018 (2015).
Evans, J. E., Jungjohann, K. L., Browning, N. D. & Arslan, I. Controlled growth of nanoparticles from solution with in situ liquid transmission electron microscopy. Nano Lett. 11, 2809–2813 (2011).
Zheng, H. M. et al. Observation of single colloidal platinum nanocrystal growth trajectories. Science 324, 1309–1312 (2009).
Li, D. S. et al. Direction-specific interactions control crystal growth by oriented attachment. Science 336, 1014–1018 (2012).
Woehl, T. J. et al. Direct observation of aggregative nanoparticle growth: Kinetic modeling of the size distribution and growth rate. Nano Lett. 14, 373–378 (2014).
de Jonge, N., Peckys, D. B., Kremers, G. J. & Piston, D. W. Electron microscopy of whole cells in liquid with nanometer resolution. Proc. Nat. Acad. Sci. 106, 2159–2164 (2009).
Mehdi, B. L. et al. Observation and quantification of nanoscale processes in lithium batteries by operando electrochemical (S)TEM. Nano Lett. 15, 2168–2173 (2015).
Park, C., Woehl, T. J., Evans, J. E. & Browning, N. D. Minimum cost multi-way data association for optimizing multitarget tracking of interacting objects. IEEE TPAMI 37, 611–624 (2015).
Lu, D. et al. Failure mechanism of fast-charged lithium metal batteries in liquid electrolyte Adv. Energy Mater. 5, 1400993 (2014).
Chen, Z. et al. New class of nonaqueous electrolytes for long-life and safe lithium-ion batteries. Nature Commun. 4, 1513–1520 (2013).
Acknowledgements
This work was primarily supported by Joint Center for Energy Storage Research (JCESR), an Energy Innovation Hub funded by the Department of Energy, Office of Science, Basic Energy Sciences. The development of the operando stage was supported by the Chemical Imaging Initiative, a Laboratory Directed Research and Development Program at Pacific Northwest National Laboratory (PNNL). PNNL is a multi-program national laboratory operated by Battelle for the U.S. Department of Energy (DOE) under Contract DE-AC05-76RL01830. A portion of the research was performed using the Environmental Molecular Sciences Laboratory (EMSL), a national scientific user facility sponsored by the Department of Energy’s Office of Biological and Environmental Research and located at PNNL. The development of the multi-target tracking algorithm is supported by the National Science Foundation under NSF-1334012.
Author information
Authors and Affiliations
Contributions
B.L.M. and N.D.B. designed the experiments (performed by B.L.M.) and wrote the manuscript. J.Q. prepared the electrolyte. C.P. wrote the tracking algorithm, C.P. and A.S. performed the analysis. J.-G.Z. and W.A.H. assisted with the interpretation of the C.V. measurements. All authors discussed the results and commented on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Mehdi, B., Stevens, A., Qian, J. et al. The Impact of Li Grain Size on Coulombic Efficiency in Li Batteries. Sci Rep 6, 34267 (2016). https://doi.org/10.1038/srep34267
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep34267
This article is cited by
-
A Review of Solid Electrolyte Interphase (SEI) and Dendrite Formation in Lithium Batteries
Electrochemical Energy Reviews (2023)
-
A glimpse on all-solid-state Li-ion battery (ASSLIB) performance based on novel solid polymer electrolytes: a topical review
Journal of Materials Science (2020)
-
Monitoring chemical reactions in liquid media using electron microscopy
Nature Reviews Chemistry (2019)
-
Applying shot boundary detection for automated crystal growth analysis during in situ transmission electron microscope experiments
Advanced Structural and Chemical Imaging (2017)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.