Abstract
A new method for magnetic field mapping based on the optical response of organized dense arrays of flexible magnetic cantilevers is explored. When subjected to the stray field of a magnetized material, the mobile parts of the cantilevers deviate from their initial positions, which locally changes the light reflectivity on the magnetooptical surface, thus allowing to visualize the field lines. While the final goal is to be able to map and quantify nonuniform fields, calibrating and testing the device can be done with uniform fields. Under a uniform field, the device can be assimilated to a magneticfieldsensitive diffraction grating, and therefore, can be analyzed by coherent light diffraction. A theoretical model for the diffraction patterns, which accounts for both magnetic and mechanical interactions within each cantilever, is proposed and confronted to the experimental data.
Introduction
Magnetic field mapping techniques have continuously been developed due to the necessity for determining the spatial components of local magnetic fields in many industrial applications and fundamental research^{1,2,3,4}. A wellestablished tool for obtaining the spatial distribution of magnetic fields is the magnetooptical imaging (MOI) method, which makes use of socalled MOI films such as ferrite garnet films with uniaxial or planar anisotropy^{5,6}, and nanoparticle Bitter films^{7,8,9,10,11}. A MOI film placed on a magnetized surface will have its magnetic domain structure reorganized in accordance with the local intensity of the magnetization or stray field produced by the analyzed material. However, the method is nonquantitative and depositing a MOI film is an invasive process that leaves traces after removal. Other field mapping techniques are based on scanning, such as superconducting quantum interference device (SQUID)^{12,13}, Hall bar^{14,15,16}, magnetic force^{17,18}, and scanning magnetoresistive microscopy^{19}. Despite being highly sensitive, scanning techniques are slow and each of them has its own drawback. For instance, SQUID microscopy operates at low temperatures, and magnetoresistive sensors operate with dc currents, thus possibly introducing heat and magnetic fields that can alter the sample. Due to their long spin coherence time, negatively charged nitrogenvacancy centers in diamond are also promising for magnetometry^{20,21,22,23}. However, nanometer scale proximity to the surface of the diamond film is necessary and is limited by the charge stability of the surface state acceptors. Several factors are considered for sensors^{12} such as spatial resolution, sensitivity, linear response, required proximity to the sample, as well as the ability to filter noise and to measure without bringing in any perturbations to the sample. The existing techniques usually combine several of the desired features and in many cases they are found to be complementary. In this paper, we report magnetic field mapping by use of a structure based on organized arrays of closepacked mobile magnetic elements. Each element is a magnetic cantilever with microscopic length and nanometer scale thickness. When placed in proximity to magnetized materials, the cantilevers are deflected depending on the intensity and direction of the stray fields. Due to a local change of reflectivity induced by the stray field, the field lines generate a contrast, which is even visible to the naked eye on the surface of the mapping device. Such magnetooptical surface offers the advantage of being a passive and easytouse device, since neither power source nor sample preparation is required. It is also directly sensitive to magnetic torques rather than magnetic field gradients. The goal of such device is to map nonuniform fields by extracting from each cantilever the local intensity and direction of the field. Uniform magnetic fields can however be used to calibrate and quantify the sensitivity of the mapping device. Since all cantilevers deflect the same way in a uniform magnetic field, the device is optically equivalent to a magneticfieldsensitive diffraction grating. The field mapping technique presented here opens up possibilities for applications such as microcracks detection by measuring current distributions in metals or detection of ferromagnetic pigments used in security applications.
Results
Visualizing field lines with organized arrays of magnetic cantilevers
The magnetooptical surfaces are developed by a topdown technique on silicon (Si) substrates. A MaN 2403 negative tone photoresist layer is deposited by spincoating and patterned after the rectangularsection beam shape of the microelements by UV lithography. Then, a 100 nm layer of permalloy (Ni_{81}Fe_{19}) is deposited by sputtering on a 3 nm titanium (Ti) layer. The purpose of the Ti layer is to promote the adhesion of the permalloy layer on Si. Different lengths and spacings between each beam can be achieved with different types of masks. The remaining photoresist is then liftedoff and the Si substrate is isotropically etched by reactive ion etching using a sulfur hexafluoride (SF_{6}) plasma, which liberates the beams. The beams have one end, which is patterned with wider dimensions to ensure that the SF_{6} plasma does not entirely etch the Si underneath, so that the anchor contact (Fig. 1a) can be formed. Once the substrate is removed, the freestanding part of the cantilevers bends because of the residual stress^{24,25} due to the elevated deposition temperature (~100 °C) and the difference of thermal expansion coefficients between Si (2.56 × 10^{−6} K^{−1}), Ti (8.6 × 10^{−6} K^{−1}) and permalloy (12 × 10^{−6} K^{−1}). Once liberated, the magnetic microelements are free to be actuated by an external magnetic field. Typical scanning electron microscope (SEM) images of arrays of magnetic cantilevers are shown in Fig. 1b,c. Optical microscopy coupled with a highspeed camera system allows to observe the realtime spontaneous motion of the beams when they are exposed to a magnetic field (Fig. 1d,e). In our case, the permalloy layers are vacuumdeposited. So, to ensure the stability of the magnetic cantilevers against oxidation when exposed to the air, a 1 or 2 nm layer of a metal that gets passivated in the air (Al, Ta) can be grown before taking the permalloy film out of the vacuum chamber. Such thin film does not significantly alter the Young’s modulus of the cantilever.
To test this concept of field mapping, an experiment is first conducted at macroscopic scale. A test device (Fig. 2a) is placed over a NdFeB permanent magnet (Fig. 2b). A striking result is that the field lines produce contrasted regions that are visible to the naked eyes on the magnetooptical surface (Fig. 2c,d). The surface of the device recovers its initial state after the field is removed, so the effect is reversible. The white light reflects differently depending on the local deflection of each cantilever caused by the stray field, thus giving rise to the dark regions that recreate the shape of the magnet. In a second step, in order to quantify the strength of the observed stray field, we employ optical diffraction by coherent light in a uniform magnetic field.
Theoretical model using Hamiltonian mechanics
Considering the arrays of microcantilevers as an actuable diffraction grating, we establish a theoretical model that relates the diffraction pattern to the deflection caused by a magnetic field with a certain magnitude and direction. Expressing the shape of the deflected cantilevers by an adequate function is required to obtain the diffraction patterns analytically. The coordinate system and the notations related to the array of cantilever are defined in Fig. 3. For the theoretical model, the deformation occurs in the (zOx) plane, and the cantilevers are considered to be long and slender beams that are made of isotropic materials. Those conditions being met, the model accounting for the internal stress caused by the action of an external magnetic field on the magnetic cantilever can be developed in the frame of the EulerBernoulli beam theory^{26}. Here, we choose an energy approach to describe the interplay between the magnetic and the mechanical properties of the materials. The total energy per unit length of the beam, expressed as a function of the curvilinear coordinate s, includes the bending energy E_{c}(s), and the magnetic energy E_{m}(s), which contains the Zeeman term due to the external field and the shape anisotropy term. α and β are the local angles between the neutral axis of the beam and the x–axis, and between the magnetization and the x–axis, respectively. Since the beams are made of permalloy, the magnetocrystalline anisotropy and the effects of magnetostriction are negligible. Therefore, the uniaxial shape anisotropy along the neutral axis of the beam is the dominant form of magnetic anisotropy. The influence of the exchange and dipolar interactions on the deformation are neglected. For a given external load on the cantilevers, the functional minimization of the total energy with respect to the function α(s) leads to the relation between ds and dα.
where and are characteristic lengths that are related to the external magnetic field and the uniaxial anisotropy, respectively. M_{s} is the saturation magnetization of permalloy, K_{u} is the uniaxial anisotropy energy coefficient, θ_{B} is the magnetic field angle, E is the combination of the Young’s moduli of both permalloy and Ti layers according to the Reuss rule of mixture^{27}, is the centroidal bending stiffness. In order to account for the initial bending of the cantilevers, a homogeneous residual stress is included in the bending energy term by giving a constant initial radius of curvature R to the beam. From equation (2), one can express the shape of the beam with a parametric curve (see the Methods section). For the calculations, R and θ_{B} are fitting parameters.
The values of α and β at the free end of the cantilever are noted as and , respectively. A consequence of this model is that α and β are singlevalued functions of s. Thus, for a given length of the beam, applying an external applied magnetic field with a certain magnitude B and a certain angle θ_{B} will result in a unique set of values for the pair .
Equation (1) implies that the external field applies a torque on the magnetization of the material, which in turn exerts a torque on the easy axis of the ferromagnet, thus causing the beam to bend. Although the uniaxial shape anisotropy would normally favor an alignment of the magnetization along the neutral axis of the cantilever, the combined presence of both bending and Zeeman energies can, in principle, allow the magnetization to be oriented in directions nonparallel to the tangent to the beam. To verify this hypothesis, the equilibrium angle of the magnetization with respect to the neutral axis of the beam is determined at each point on the cantilever by minimizing the magnetic energy with respect to β, i.e. ∂E_{m}/∂β = 0, which results in the following relation:
Equation (3) can also be seen as an equilibrium between the torque exerted by the external field on the magnetization and that exerted by the magnetization on the easy magnetization axis. The calculations are done with M_{s} = 800 emu.cm^{−3}, K_{u} = 43000 erg.cm^{−3}, values for permalloy thin films^{28,29,30} at 300 K, and the beams have a length μm and width w = 2 μm. Figure 4 represents the shape of a 100 μm long beam deflected under a magnetic field of 700 Oe, with a field angle θ_{B} = 1.36 rad, and the stable equilibrium orientation of the magnetization calculated at several positions on the beam. It is clear from Fig. 4 that the magnetization vectors slightly point out of the beam. The effect becomes weaker as one approaches the free end, which is consistent with a decreasing bending torque as x increases, since β gets closer to θ_{B}.
Discussion
The magnetomechanical model computes the cantilever shape that best fits the intensity profile of the coherent light diffraction patterns measured experimentally in the Fraunhofer conditions. The theoretical wave diffraction patterns are obtained by calculating the total diffracted intensity for a given curvature. The total intensity of the diffracted light, at coordinates (x_{M}, y_{M}) on the observation plane, is the product of the interference grating term by the Fraunhofer diffraction term , which is adjusted to account for the curvature. Using the notations in Fig. 3, the phase difference between the waves diffracted at O(0, 0, 0) and P(x, y, z(x)) is given by , for an incidence quasinormal to the magnetooptical surface:
where f is the focal length of the converging lens that forms the diffraction pattern in the observation plane, and are the incident and diffracted wave vectors, respectively, and λ = 533 nm is the wavelength of the laser.
The spacing of the grating and the number of cantilevers are S_{x} = 112 μm, N_{x} = 20 and S_{y} = 4 μm, N_{y} = 100 in the x and y directions, respectively. When the cantilevers are flat, the array gives an optical response corresponding to a symmetric pattern (Fig. 5a,b). When the structure is bent, the diffraction pattern becomes asymmetric because the envelope of the optical signal, determined by , changes when the magnitude of the external field varies (Fig. 5a,c,d). The results in Fig. 4 are obtained with the fitting parameters R = 155 μm and θ_{B} = 1.36 rad. Then, by incorporating the mathematical expression of the shape of the cantilevers in equation (6), we found a relatively good match between the measured optical signals and the calculated diffracted intensities. The data fittings in Fig. 5c,d yield the magnitude of the magnetic field B: 700 Oe and 800 Oe, respectively. A gaussmeter is placed under the sample to confirm the value of the field. Consequently, the abovementioned theoretical approach appropriately models the shape of the beams bent under the influence of a certain stray field. In addition, this model can also be used to predict the most optimal cantilever dimensions to improve the sensitivity and the resolution for magnetic field mapping. The quantity is the highest value of α(s) for a given length , hence it measures how much a cantilever can be deflected by a field. Shorter beams make it possible to build denser arrays for better spatial resolution but reduce the ability of the beam to deflect. However, thinner beams can be deflected more easily, therefore at an equal amplitude of external field, they have a higher sensitivity than thicker beams (Fig. 5e,f). A possible way to enhance the sensitivity of the device is to fabricate cantilevers with nonuniform thicknesses: smaller thicknesses around the clamped end will reduce the overall stiffness, while higher thicknesses near the free end will increase the magnetic torque. The fabrication process would nonetheless be more complexe. Tuning the centroidal stiffness I by changing the geometry of the cantilevers in the y direction can be a more feasible alternative.
In summary, we have shown that a magnetooptical surface made up of organized arrays of magneticfieldactuable cantilever beams can react to the direction and the magnitude of a stray field emanated from a magnetized material. At the macroscopic scale, the effects can be visible to the naked eye, but they can also be visualized at the microscopic scale by optical microscopy, which allows a realtime twodimensional imaging of the magnetic field distribution. The arrays of magnetic cantilevers are directly sensitive to magnetic torques, rather than magnetic field gradients. This property is attractive because measuring the deflection of the cantilevers is equivalent to measuring the magnetic torque applied on it, hence magnetic fields can be quantified. An interesting challenge is to further improve the spatial resolution and the sensitivity by changing the dimensions or the geometry of the beams. Beam thicknesses of a few tens of nanometers offer higher sensitivity, while lengths as short as a few microns stiffen the beams, which goes against optimizing the sensitivity. Augmenting the sensitivity of the device by changing the geometry of the cantilevers and in particular by using beams of nonuniform thickness is a path to explore. The upper and lower limit depends on the mechanical properties of the cantilevers. A quantitative description of the relationship between applied field and cantilever deflection is given in relation to Fig. 5e,f. With the geometry described in this paper, fields in the range 0.1 to 2 kOe can be detected and mapped. In principle, the sensitivity of this approach could be much increased by using vertically suspended magnetic cantilevers, which would hang below the substrate. In this case, the cantilever could be made much thinner since they would not have to support their own weight. As a result, they would react to much lower field than those described in Fig. 3. In this case, magnetic fields of the order of the earth field could be detected. For the type of foreseen applications, there is no interest in trying to further enhance the sensitivity of the cantilevers since they are expected to be used in presence of the earth field. The drawback of this technique is however its sensitivity to vibrations and the volume required not for the device itself but for the optical readout setup.
Methods
Distributed magnetic torque on the magnetic beams
The magnetomechanical model is developed in the frame of Hamiltonian mechanics. The total energy per unit length of the beam corresponds to a Lagrangian given in terms of generalized coordinate α and generalized velocity . For a given external load imposed by the applied magnetic field, the Legendre transform of is invariant along the beam:
The equation above leads to the following first order differential equation:
Solving the equation analytically is not trivial because the variable s is contained in both functions α and β. Since , equation (3) allows to isolate the variables α and β, which eliminates α in the expression of ds in equation (2): ds = Λ_{K}g(β)dβ, with
where and . The shape of the cantilever is given by a parametric curve by calculating and , where β_{0} = β(s = 0) is found with equation (3) using the boundary condition at the clamped end α(s = 0) = 0. Since s is a singlevalued function of β, β(s) is found by inverting s(β). By inserting the values of β(s) in equation (2), α(s) is determined, thus allowing to calculate the difference of angles β(s) − α(s) along the beam.
Additional Information
How to cite this article: Truong, A. et al. Magnetooptical micromechanical systems for magnetic field mapping. Sci. Rep. 6, 31634; doi: 10.1038/srep31634 (2016).
References
 1
Freeman, M. R. & Choi, B. C. Advances in magnetic microscopy. Science 294, 1484 (2001).
 2
Budker, D. & Romalis, M. Optical magnetometry. Nat. Phys. 3, 227 (2007).
 3
Rondin, L. et al. Nanoscale magnetic field mapping with a single spin scanning probe magnetometer. Appl. Phys. Lett. 100, 153118 (2012).
 4
Lee, H., Yang, N. & Cohen, A. E. Mapping nanomagnetic fields using a radical pair reaction. Nano Lett. 11, 5367 (2011).
 5
Helseth, L. E., Hansen, R. W., Il’yashenko, E. I., Baziljevich, M. & Johansen, T. H. Faraday rotation spectra of bismuthsubstituted ferrite garnet films with inplane magnetization. Phys. Rev. B, 64, 174406 (2001).
 6
Helseth, L. E. et al. Faraday rotation and sensitivity of (100) bismuthsubstituted ferrite garnet films. Phys. Rev. B, 66, 064405 (2002).
 7
Bitter, F. On inhomogeneities in the magnetization of ferromagnetic materials. Phys. Rev. 38, 1903 (1931).
 8
Bitter, F. Experiments on the nature of ferromagnetism. Phys. Rev. 41, 507 (1932).
 9
Dahlberg, E. D. & Proksch, R. Magnetic microscopies: the new additions. J. Magn. Magn. Mater. 200, 720 (1999).
 10
Hartmann, U. & Mende, H. H. The strayfieldinduced birefringence of ferrofluids applied to the study of magnetic domains. J. Magn. Magn. Mater. 41, 244 (1984).
 11
Rice, P. & Moreland, J. A new look at the Bitter method of magnetic imaging. Rev. Sci. Instr. 62, 844 (1991).
 12
Kirtley, J. R. & Wiskwo, J. P. Jr. Scanning SQUID microscopy. Annu. Rev. mater. Sci. 29, 117 (1999).
 13
Kirtley, J. R. et al. Highresolution scanning SQUID microscope. Appl. Phys. Lett. 66, 1138 (1995).
 14
Chang, A. M. et al. Scanning Hall probe microscopy. Appl. Phys. Lett. 61, 1974 (1992).
 15
Oral, A., Bending, S. J. & Henini, M. Scanning Hall probe microscopy of superconductors and magnetic materials. J. Vac. Sci. Technol. B 14, 1202 (1996).
 16
Oral, A., Bending, S. J. & Henini, M. Realtime scanning Hall probe. Appl. Phys. Lett. 69, 1324 (1996).
 17
Martin, Y. & Wickramasinghe, H.K. Magnetic imaging by “force macroscopy” with 1000 Å resolution. Appl. Phys. Lett. 50, 1455 (1987).
 18
Sáenz, J. J. et al. Observation of magnetic forces by the atomic force microscope. J. Appl. Phys. 62, 4293 (1987).
 19
Mitin, D., Grobis, M. & Albrecht, M. Scanning magnetoresistive microscopy: an advanced characterization tool for magnetic nanosystems. Rev. Sci. Instrum. 87, 023703 (2016).
 20
Ohashi, K. et al. Negatively charged nitrogenvacancy centers in a 5 nm thin ^{12}C diamond film. Nano Lett. 13, 4733 (2013).
 21
Toyli, D. M. et al. Measurement and control of single nitrogenvacancy center spins above 600 K. Phys. Rev. X 2, 031001 (2012).
 22
Balasubramanian, G. et al. Ultralong spin coherence time in isotopically engineered diamond. Nat. Mater. 8, 383 (2009).
 23
Fang, K. et al. Highsensitivity magnetometry based on quantum beats in diamond nitrogenvacancy centers. Phys. Rev. Lett. 110, 130802 (2013).
 24
Schöngrundner, R. et al. Critical assessment of the determination of residual stress profiles in thin films by means of the ion beam layer removal method. Thin Solid Films 564, 321 (2014).
 25
Fang, W. & Wickert, J. R. Determining mean and gradient residual stress in thin films using micromachined cantilevers. J. Micromech. Microeng. 6, 301 (1996).
 26
Antman, S. S. Nonlinear Problems of Elasticity (Springer, New York, 2005).
 27
Reuss, A. Calculation of the flow limit of mixed crystals on the basis of the plasticity of monocrystals. J. Appl. Math. Mech. 9, 49 (1929).
 28
Miltat, J., Albuquerque, G. & Thiaville, A. Spin Dynamics in Confined Magnetic Structures I, Chap. An Introduction to Micromagnetics in the Dynamic Regime (Springer, Berlin Heidelberg, 2002).
 29
EncinasOropesa, A. & Nguyen Van Dau, F. Origin of magnetic anisotropy in thin films deposited on stepbunched substrates. J. Magn. Magn. Mater. 256, 301 (2003).
 30
Miyajima, H., Sato, K. & Mizoguchi, T. Simple analysis of torque measurement of magnetic thin films. J. Appl. Phys. 47, 4669 (1976).
Acknowledgements
This work was funded in part by the European grant ABIOMATER 665440, and in part by P2N NANOSHARK (ANR11NANO001).
Author information
Affiliations
Contributions
B.D. and H.J. designed the research. B.D. and P.S. optimized the method for sample preparation. T.D. and M.M. participated in fabricating samples. A.T., G.O. and I.J. established the experimental setup for physical optics. A.M. and A.T. developed the theoretical model. A.T. collected and analyzed the data, and wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Truong, A., Ortiz, G., Morcrette, M. et al. Magnetooptical micromechanical systems for magnetic field mapping. Sci Rep 6, 31634 (2016). https://doi.org/10.1038/srep31634
Received:
Accepted:
Published:
Further reading

Magnetomechanically actuated microstructures to efficiently prevent bacterial biofilm formation
Scientific Reports (2020)

Optomechanically Actuated Microcilia for Locally Reconfigurable Surfaces
Advanced Materials (2020)

Fabrication of nanotweezers and their remote actuation by magnetic fields
Scientific Reports (2017)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.