In this work, we study the lithiation behaviours of both porous silicon (Si) nanoparticles and porous Si nanowires by in situ and ex situ transmission electron microscopy (TEM) and compare them with solid Si nanoparticles and nanowires. The in situ TEM observation reveals that the critical fracture diameter of porous Si particles reaches up to 1.52 μm, which is much larger than the previously reported 150 nm for crystalline Si nanoparticles and 870 nm for amorphous Si nanoparticles. After full lithiation, solid Si nanoparticles and nanowires transform to crystalline Li15Si4 phase while porous Si nanoparticles and nanowires transform to amorphous LixSi phase, which is due to the effect of domain size on the stability of Li15Si4 as revealed by the first-principle molecular dynamic simulation. Ex situ TEM characterization is conducted to further investigate the structural evolution of porous and solid Si nanoparticles during the cycling process, which confirms that the porous Si nanoparticles exhibit better capability to suppress pore evolution than solid Si nanoparticles. The investigation of structural evolution and phase transition of porous Si nanoparticles and nanowires during the lithiation process reveal that they are more desirable as lithium-ion battery anode materials than solid Si nanoparticles and nanowires.
With ever-growing demands for high-performance power sources, especially in portable electronics and electrical vehicles (EV), tremendous research interests have been stimulated toward developing the next generation of lithium-ion batteries (LIBs) with high capacity, long cycle life and low cost1,2. Compared with carbonaceous anodes (372 mAh/g for LiC6) used in commercial LIBs, silicon (Si) has a large theoretical gravimetric capacity of ~4200 mAh/g and volumetric capacity of ~8500 mAh/cm3 and therefore has been considered as one of the most promising anode materials for the next-generation LIBs3,4. However, Si experiences a dramatic volume change (>300%) during the lithium alloying/dealloying processes and for crystalline Si (c-Si) this large volume expansion is accompanied with dramatic anisotropic expansion5,6,7. This change not only causes severe pulverization of the material but also induces electrical disconnection of the active material from the current collector, resulting in performance degradation of the battery if Si is used as the anode. To minimize the extent of volume change, tremendous efforts have been made on the synthesis of novel nanostructured Si materials, such as nanowires8,9, nanotubes10,11,12, hollow spheres and core-shell structures13,14. Recently, three-dimensional porous structured Si has attracted significant attention. The pre-formed nanopores in the Si can provide a large space to accommodate the volume expansion and therefore help to maintain the structure integrity when lithium alloys with Si. Moreover, this three-dimensional porous structure provides large surface area of the material to be accessible to the electrolyte and thus a short diffusion length for lithium ions to transport from electrolyte to Si, which facilitates the lithium alloying/dealloying processes at high current rates15,16,17,18,19,20.
To understand the lithiation/delithiation process of Si, it is of importance to directly observe the structural and chemical evolution during the process and thus correlate with the battery properties. Over the past few years, tremendous progress has been made toward developing methodologies for in situ observation of structural and chemical evolution of electrodes used for LIBs. Among them, in situ transmission electron microscopy (TEM) has been particularly informative and has revealed important features of the lithiation/delithiation process of Si nanoparticles and nanowires on phase transition, structural evolution and lithiation kinetics6,7,21,22,23,24,25,26,27,28. Specifically, both c-Si nanoparticles and nanowires are reported to transform to amorphous LixSi (a-LixSi) via electrochemical-driven solid-state amorphization. With further lithiation, a-LixSi transforms to crystalline Li15Si4 (c-Li15Si4)7,21,22,26. The fracture behaviour of c-Si nanoparticles during the first lithiation is reported to be particle-size-dependent. The critical fracture diameter is 150 nm, below which cracks do not form and above which surface cracking and particle fracture takes place upon lithiation7. In comparison, the critical fracture diameter of amorphous Si (a-Si) particles is reported to be up to 870 nm. In addition, the lithiation reaction velocity of a-Si is approximately constant and does not slow as in c-Si, which suggests different stress evolution during lithiation and implies that a-Si may be a more desirable active material than c-Si27. These studies have led to fundamental understanding of the lithiation/delithiation process of Si nanoparticles and nanowires; however, these studies cannot provide direct explanation of better electrochemical performance achieved by newly reported nanostructured Si than solid Si nanoparticles and nanowires. Moreover, most studies only focus on the first several lithiation/delithiation cycles of Si, but do not look into post-cycling analysis of the structural evolution of Si. In this work, we study the phase transition and structural evolution of both porous Si nanoparticles and porous Si nanowires by in situ and ex situ TEM. The in situ TEM observation of lithiation process of porous Si nanoparticles reveals that the lithiation proceeds in an end-to-end manner, which is different from the surface-to-center manner for solid Si nanoparticles under the same experimental condition. In addition, much larger critical fracture diameter is achieved in porous Si particle than previously reported for c-Si and a-Si particles. Another interesting feature in the lithiation process of porous Si nanoparticles and nanowires is that a-LixSi does not transform to c-Li15Si4 even after full lithiation, which is distinct from that of solid Si nanoparticles and nanowires. The distinct lithiation behaviours of porous Si nanoparticles and nanowires are attributed to their interconnected three-dimensional porous structure, which is built up by numerous small domains. First-principle molecular dynamic simulation was conducted to investigate the effect of domain size on the phase stability of c-Li15Si4, which confirms the effect of nanostructure on phase transition. Moreover, structural evolution of porous and solid Si nanoparticles under successive lithiation/delithation cycles are compared through ex situ TEM, which confirms that porous Si is a more desirable anode material for LIBs than solid Si.
In this work, the porous Si nanoparticles and nanowires were prepared according to our previous reports15,18. To prepare porous Si nanoparticles, metallurgical Si was used as the starting material. After milling to submicron particles, the Si was etched in Fe(NO3)3/HF etchant to obtain porous structure. To prepare porous Si nanowires, a boron-doped Si wafer was used as the starting material and AgNO3/HF was used as the etchant to obtain the porous structure. To prepare Si nanowires without pores, a pure Si wafer without doping was used as the starting material. After etching by AgNO3/HF, Si nanowires without pores were obtained. For comparison, both Si nanoparticles with and without pores and Si nanowires with and without pores are characterized by in situ TEM. The in situ TEM nanobattery setup is schematically shown in Fig. 1a. Figure 1b–g and Supplementary Movie 1 show the lithiation process of a ball-milled Si particle with largest diameter of ~950 nm and smallest diameter of ~630 nm. The ball-milled Si was prepared by ball-milling metallurgical Si and then being washed with HF and deionized water (DI-H2O) to remove the surface oxide layer (Supplementary Fig. 1a,b). After the Li2O/Li electrode contacted the ball-milled Si, a potential of −2 V was applied to the Cu electrode with respect to Li2O/Li electrode to initiate the lithiation process. As shown in Fig. 1c, a bump (indicated by the red arrow) comes out from the particle after lithiation for only 28 s, which is due to anisotropic expansion of Si particles. Further lithiation results in the change of contrast of the particle as shown in Fig. 1d. The gray LixSi shell and dark Si core indicates that lithium ions flow from surface to center of the particle in the radial direction. As the particle size is well above the reported critical fracture diameter of c-Si (150 nm), cracks (indicated by the blue arrows) start to form in the particle after lithiation for only 120 s (Fig. 1d). After 468 s of lithiation, the particle fractures into several pieces (Fig. 1g). The selected area electron diffraction (SAED) pattern in Fig. 1h exhibits rings made up of discrete spots, indicating nanosized polycrystalline nature of the ball-milled Si particle before lithiation. The ball-milled Si particle is made up of nanosized single crystalline Si particles, which results in the anisotropic expansion of the ball-milled Si particle during lithiation process. After full lithiation, the particle transforms to polycrystalline Li15Si4 as indicated by Fig. 1i. The Li2O phase in Fig. 1i is from the Li2O/Li electrode in contact with the particle.
Figure 2 shows the lithiation behaviour of a typical porous Si particle. As illustrated in Fig. 2a and Supplementary Fig. 1c,d, numerous pores distribute uniformly throughout the whole porous Si particle after electroless etching of the ball-milled Si. To investigate the fracture behaviour of porous Si particle during the lithiation process, we chose a large particle with diameter up to 1.52 μm for in situ TEM observation. Figure 2b–f demonstrate the TEM images of the porous Si particle during the lithiation process. From the TEM images and Supplementary Movie 2, the volume expansion of the particle initiates in the lower right corner and then proceeds to the top left corner of the particle. This indicates that the lithium ions flow in an end-to-end manner, which is distinct from the surface-to-center lithiation manner observed in both crystalline and amorphous Si particles7,27. To clarify the lithium propagation manner of porous Si particle, the lithiation behaviour of another porous Si particle was characterized by in situ TEM with higher magnification as shown in Supplementary Fig. 2a–d and Supplementary Movie 3. The lithiation front is marked by the red dotted line in Supplementary Fig. 2b–d, which propagates from lithium source to the other end of the particle. This observation is consistent with Fig. 2 and confirms the end-to-end lithiation manner of porous Si particle. After lithiation for 1121 s, the volume expansion of the particle almost ended (Fig. 2e). To ensure full lithiation of the particle, the −2 V potential was applied to the Cu electrode for another ~200 s and no obvious volume expansion of the particle was observed during this period. After lithiation for 1335 s, no crack was observed in the particle and the diameter of the particle increased to 2.05 μm, corresponding to a volume expansion of 145% (Fig. 2f). The volume expansion is far less than the theoretical 300% for solid Si particles after full lithiation. This is attributed to the porous structure of the particle, which provides large space to accommodate the volume expansion by possible inward expansion during the lithiation process. The SAED patterns of the particle were obtained before lithiation and after full lithiation as shown in Fig. 2g,h, respectively. Before lithiation, the porous Si particle is polycrystalline as shown in Fig. 2g. After full lithiation (Fig. 2h), the SAED pattern indicates that a-LixSi (marked by the blue arc) and c-Li15Si4 (indicated by the green arrow) coexist6,29. The rings from Li2O/Li electrode are marked by the yellow arcs. This observation contrasts the SAED pattern of the fully lithiated ball-milled Si, which exhibits only c-Li15Si4 phase as shown in Fig. 1i. We note that the porous Si and ball-milled Si particles are prepared from the same starting material. Taking into account that the most distinguishable difference between the porous Si and the ball-milled Si is their microstructures, we believe that the porous structure helps to prevent the formation of c-Li15Si4 phase during the first lithiation process and we will discuss it in detail later.
A brief summary of the lithiation behaviours of solid and porous Si particles reveal that lithiation proceeds in a surface-to-center manner for solid Si particles while in an end-to-end manner for porous Si particles. Figure 3 schematically illustrates the different lithiation manners of solid and porous Si particles. As lithium diffuses faster in the surface of Si than that in the bulk, a-LixSi shell will form in ball-milled Si particle once lithiation occurs (Fig. 3b). As the a-LixSi shell thickens, cracks will form on the surface of the particle (Fig. 3c), which lead to final pulverization of the ball-milled Si particle as shown in Fig. 3d. The situation is different in porous Si particle, which is made up of numerous small domains (Fig. 3e) and possesses complex surface topological feature. The large and complex surface of porous Si lags the propagation of lithium in the whole particle. As a result, lithium tends to proceed from the lithium source and propagate through the whole particle in an end-to-end manner, even though lithium may proceed in a surface-to-center manner in each domain as shown in Fig. 3f,g. Because each domain in porous Si is in several nanometers, which is much smaller than the critical fracture diameter of solid Si, no crack will form during lithiation process (Fig. 3h). In addition, the porous structure provides large space to accommodate the volume expansion by possible inward expansion of each domain, leading to smaller volume change of the porous Si particle than solid Si particle.
To further characterize the structural evolution of ball-milled Si and porous Si, ex situ TEM images and corresponding SAED patterns of the two samples were obtained before cycling and after being charge-discharged for 1 cycle, 10 cycles and 50 cycles in Li-Si cells in the voltage window of 0.01–2 V (vs. Li/Li+) at a current density of 400 mA/g as shown in Fig. 4a–h. According to previous reports, the cutoff voltage range plays an important role to induce pore evolution in Si. Specifically, a large voltage window of 0.05-1 V would lead to porous structure of Si while Si cycled in a small voltage window of 0.17-0.6 V retains its original structure well after cycling30. In this work, we cycled the Li-Si cells in large voltage window of 0.01–2 V (vs. Li/Li+) so that we can study the capability of porous Si and ball-milled Si to suppress pore evolution during the cycling process. Before cycling, both ball-milled Si and porous Si are polycrystalline as indicated by the inset SAED patterns in Fig. 4a,e, respectively. After being charge-discharged for different cycles, both ball-milled Si and porous Si transform to amorphous structure as indicated by the inset SAED patterns in Fig. 4b–d,f–h. To quantitatively investigate the pore evolution processes of the two samples, pore size distributions were obtained based on statistical analysis of TEM images. Before cycling, the surface of ball-milled Si is smooth as shown in Fig. 4a. For porous Si particles, the pores are clearly resolved by the contrast in the image in Fig. 4e and the mean diameter is 9.9 ± 0.1 nm based on the pore size distribution diagram in Fig. 4i. After being charge-discharged for only 1 cycle, nanopores are observed to form on the periphery of the ball-milled Si as indicated by the dark/light contrast in Fig. 4b, which is due to inelastic deformation of Li/Si during the lithiation/delithiation process30. On the contrary, the porous Si particle retains its original porous structure well as shown in Fig. 4f. This is confirmed by the pore size distribution diagram of two samples in Fig. 4j. The mean diameter of newly-formed pores in the ball-milled Si is 3.8 ± 0.1 nm. While for porous Si, the mean diameter of pores is 10.9 ± 0.1 nm, which is close to its original value before cycling. After cycling for 10 cycles, the surface of the ball-milled Si particles gets much rougher (Fig. 4c), while the pore size increase of porous Si is still not significant (Fig. 4g). As shown in Fig. 4k, the mean diameter of the pores in the ball-milled Si increases drastically to 20.1 ± 0.1 nm, corresponding to a 429% increase compared with that after 1 cycle. Similar to Ostwald ripening in which particles agglomerate to reduce surface energy, this increase of pore size with cycling is equivalent to agglomeration of pores so that the surface energy of the particle can be reduced31. In contrast to the significant pore size increase in ball-milled Si, the mean diameter of pores in porous Si is only 12.8 ± 0.1 nm after 10 charge-discharge cycles, corresponding to only 29% increase compared with that before cycling. After cycling for 50 cycles, pores in both ball-milled Si and porous Si increase in size as shown in Fig. 4d,h. According to Fig. 4l, the mean diameter of pores for ball-milled Si is 41.8 ± 0.1 nm. However, the mean diameter of pores for porous Si is 36.0 ± 0.1 nm, which is still smaller than that of ball-milled Si. As the pore evolution is due to inelastic deformation of Li/Si during lithiation/delithiation process, for solid Si nanoparticles, the inelastic deformation is severe due to its large volume change during lithiation/delithiation process. For porous Si nanoparticles, however, the domains of the particle are observed to expand into the void space in the particle based on the observation in Supplementary Fig. 2a–d that the contrast of the particle from the porous structure becomes obscure and uniform during the lithiation process. This lithiation behaviour of porous Si particle results in smaller volume change of the particle and stress relaxation in each domain. The stress relaxation prevents the stress in porous Si nanostructures from exceeding the elastic limit of Si and thus suppresses the pore evolution in porous Si nanostructures.
The formation and size increase of pores in ball-milled Si particles would cause significant volume expansion of particles as they transform from solid particles to totally porous structure. However, with pre-formed pores, the volume change of porous Si particles before and after cycling is much less significant than that of ball-milled Si particles. This difference in particle volume change during cycling results in the different cycling performance of the two electrodes. Figure 4m shows the cycling performances of ball-milled Si and porous Si electrodes tested in the voltage window of 0.01–2 V (vs. Li/Li+) at a current density of 400 mA/g. As shown in the figure, the capacity of ball-milled Si decays rapidly in the initial 10 cycles and then decreases in constant rate. This corresponds to the TEM observation that pore formation in ball-milled Si particles takes place in early cycles, which causes the particles to lose electrical contact from the current collector and thus leads to loss of active materials for capacity contribution. The volume change of porous Si during cycling is much less than that of ball-milled Si; however, the relatively large surface area of porous Si as compared to ball-milled Si would lead to more severe solid electrolyte interface (SEI) formation on porous Si particles, which would also cause capacity decay in the initial cycles. For this reason, it is essential to apply coating on porous Si particles (e.g. carbon coating) to mitigate the SEI formation and thus to further improve the cyclability of porous Si electrodes17,18,19.
In order to further demonstrate whether the microstructure or the starting material of porous Si would affect its lithiation behaviour, we prepared solid Si nanowires and porous Si nanowires according to our previous report using Si wafers as the starting material15. Figure 5 and Supplementary Movie 4 show the lithiation behaviour of a typical solid Si nanowire with diameter of ~120 nm and length of ~600 nm. The Si nanowire before lithiation is shown in Fig. 5a and Supplementary Fig. 3a,b. After lithiation for 103 s (Fig. 5d), the gray shell and dark core of the nanowire reveal that the lithiation of Si nanowire occurs through the formation of a-LixSi shell and Si core structure, which is due to the faster lithium diffusion rate on the nanowire surface than that in the center. After lithiation for 150 s, the volume expansion of the nanowire almost ended (Fig. 5e). To ensure full lithiation of the nanowire, the −2 V potential was applied to the Cu electrode for another ~130 s and no obvious volume expansion of the nanowire was observed during this period. After lithiation for 285 s, no crack was observed in the nanowire (Fig. 5f). This is in agreement with a previous report, which demonstrates that the critical diameter for pulverization of Si nanowire is in the regime of 220–260 nm32. The SAED pattern of the Si nanowire before lithiation (Fig. 5g) reveals its polycrystalline nature. After lithiation for 285 s, the SAED pattern of the nanowire (Fig. 5h) indicates that it has transformed to the c-Li15Si4 phase, which is similar to the result of the ball-milled Si particle in Fig. 1i.
The lithiation behaviour of a porous Si nanowire bundle consisting of several porous Si nanowires was also examined by in situ TEM as demonstrated in Fig. 6 and Supplementary Movie 5. As shown in Fig. 6a and Supplementary Fig. 3c,d, the nanowires obtain highly porous structure with pore diameter and wall thickness of ~8 nm before lithiation. The single nanowire beside the nanowire bundle in Fig. 6a acts as the lithium diffusion path during the lithiation process. Figure 6b–g demonstrate the lithiation process of the porous Si nanowire bundle, from which we can find that the contrast of the nanowires from the porous structure becomes obscure and uniform during the process. This indicates that the a-LixSi expands into the void space in the nanowires, which helps to minimize the volume expansion of the nanowires. The lithiation front is marked by the red dotted line in Fig. 6b–e, which also indicates the end-to-end lithiation manner similar to that of porous Si particle. This observation demonstrates that the explanation of porous Si particle lithiation manner in Fig. 3 also applies to porous Si nanowires. After lithiation for 823 s, lithium was observed to diffuse out of the nanowire bundle as indicated by the red arrow in Fig. 6f, indicating that the lithiation process was complete. To ensure full lithiation, the −2 V potential was applied to the Cu electrode for another ~140 s and no obvious volume expansion of the nanowire bundle was observed during this period. After lithiation for 964 s, no crack was observed in the nanowire bundle (Fig. 6g). Figure 6h shows the SAED pattern of the nanowire bundle before lithiation, which reveals its polycrystalline nature. After lithiation for 964 s, the SAED pattern of the porous Si nanowire bundle (Fig. 6i) demonstrates that it has transformed to a-LixSi (marked by the blue arc). This observation contrasts the SAED pattern of the fully lithiated solid Si nanowire, which exhibits only c-Li15Si4 phase as shown in Fig. 5h.
A brief summary of the lithiation behaviours of porous Si and solid Si nanostructures reveal that after full lithiation, solid Si nanostructures transform to c-Li15Si4 while porous Si nanostructures transform to a-LixSi. The porous Si nanostructures are made up of small Si domains as shown in Supplementary Figs 1d and 3d, while the domain of solid Si nanoparticle or solid Si nanowire is the whole nanoparticle or whole nanowire due to their solid structures. We believe that the different sizes of the domains of porous Si and solid Si lead to their different phase transition behaviours. To further illustrate the effect of domain size on the resultant phase after lithiation, first-principle molecular dynamic simulation was performed to study the structure stability of nanosized c-Li15Si4 particle. The simulated nanoparticle was constructed by 2 × 2 × 2 Li15Si4 crystalline supercells, which is composed of 128 Si atoms and 480 Li atoms and corresponds to the size of 2 nm in three dimensions. Periodic boundary condition is applied in the simulation and the empty space between Li15Si4 particles is set larger than 1 nm to exclude the mutual interaction of atoms from neighbouring particles. First-principle calculations were performed using the VASP code density functional theory (DFT) calculations in generalized gradient approximation (GGA) with the Perdew-Burke-Ernzerhof (PBE) function used to calculate the force among atoms33,34. Molecular dynamic simulation was carried out at 300 K with a time step of 1 fs interval.
Figure 7a–e show the structural evolution of Li15Si4 nanoparticle from the initial crystal to a disordered structure after 400 fs simulation. The yellow atoms are Si and blue atoms are Li. At the early stage of the simulation (e.g. 100 fs), it is clear to see that the surface atoms are the first to deviate from their original positions due to the lack of symmetric force potential at the particle surface (Fig. 7b). In the following simulation, cascaded breakdown of the periodic force potential leads to the structure disordering from outer surface to the inner part of particle. After 400 fs simulation, the particle turns to an amorphous structure (Fig. 7e). To semi-quantify the structure amorphization, the radial distribution function (RDF) of Si-Si pairs was calculated and shown in Fig. 7f. At the initial stage (0–100 fs), the sharp peaks in RDF illustrate the well-defined crystal structure. However, after 400 fs simulation, peaks at large Si-Si distance are largely smoothed, indicating the disappearance of ordered atomic arrangement. The small peak showing up at 2.5 Å corresponds to the distance of Si-Si in the amorphous Si structure, which further demonstrates the destroying of crystalline Li15Si4 structure.
Due to the constrained computation resource for first-principle molecular dynamic simulation of large-size particles, we adopted classical molecular dynamic simulation to characterize the structure stability of c-Li15Si4 particles with the same initial crystal structure as 2 nm particle (Fig. 7a) while with larger diameter of 6 nm, 8 nm, 10 nm and 12 nm. After 400 fs simulation, the atomic structures and morphologies of the Li15Si4 particles are illustrated in Supplementary Fig. 4. The yellow atoms are Si and blue atoms are Li. Periodic boundary condition was used with particle-to-particle distance larger than 5 nm to eliminate the mutual interaction. Simulation were conducted by using the LAMMPS software code35 and a second nearest neighbour (2NN) modified embedded atom method (MEAM) potential was used to account for the atomic interaction in Li-Si system36. Based on the comparison of enlarged images in Supplementary Fig. 4a–d, it is found that in 6 nm Li15Si4 particle (Supplementary Fig. 4a), the surface of the particle is in amorphous structure and the core atoms have lost their initial crystalline arrangement. In 8 nm particle, however, the crystallinity of the core increases compared with that of 6 nm particle even though the surface atoms in the 8 nm particle still rearrange in amorphous structure (Supplementary Fig. 4b). Similar trend is observed in 10 nm particle (Supplementary Fig. 4c) and when particle size increases to 12 nm, the crystallinity of the core is the highest and the crystalline volume is the largest among four particles even though the surface of 12 nm particle still tends to be amorphous (Supplementary Fig. 4d). Generally speaking, the trend is that as the particle size increases, the crystallinity in the core of the particles and the crystalline volume in the particles also increase. However, due to lack of symmetric force potential in the surface, the surface atoms in the particles always tend to deviate from their original positions and thus rearrange in amorphous structure. This simulation result further supports our conclusion that the small domains in porous Si nanostructures help to suppress c-Li15Si4 formation during the first lithiation process. Besides, this explains why some diffraction spots of c-Li15Si4 show up in Fig. 2h, which may be due to the formation of c-Li15Si4 in the cores of some large-size domains in the porous Si particle after full lithiation. For porous Si nanowire, however, only a-LixSi forms after full lithiation (Fig. 6i), which is possibly due to the smaller size of domains in porous Si nanowires than that in porous Si nanoparticles as we compare the domains marked in Supplementary Figs 1d and 3d. The formation of c-Li15Si4 during the first lithiation process is reported to be detrimental to the cycle life of Si-based LIBs and a cutoff voltage higher than 0.05 V is usually selected to suppress the formation of c-Li15Si4 at low potential37. Here, we report that in addition to the low cutoff voltage, the nanoporous structure can also suppress the formation of c-Li15Si4 during first lithiation process due to the effect of domain size, which helps to achieve the excellent cycling performances of porous Si nanostructures.
In conclusion, we have applied in situ and ex situ TEM to study the structural evolution and phase transition of porous Si nanoparticles and nanowires and have compared their behaviours with solid Si nanoparticles and nanowires. The critical fracture diameter of porous Si particles reaches up to 1.52 μm, which reveals its better capacity to accommodate volume expansion during the lithiation process. In addition, the porous Si nanoparticles and nanowires transform to the a-LixSi phase after full lithiation in contrast to the c-Li15Si4 phase for solid Si nanoparticles and nanowires, which is due to small Si domains in porous Si nanoparticles and nanowires as revealed by the first-principle molecular dynamic simulation. Finally, ex situ TEM observation of porous Si nanoparticles and solid Si nanoparticles reveal that porous Si nanoparticles obtain better capability to suppress pore evolution than solid Si nanoparticles during the cycling process. The better capabilities of porous Si nanostructures to accommodate volume expansion, to suppress c-Li15Si4 formation during the first lithiation process and to suppress pore evolution during cycling make them more desirable lithium-ion battery anode materials than solid Si nanostructures.
Synthesis of porous Si particles: Porous Si particles were synthesized according to our previous report18. Specifically, metallurgical Si particles were ground to fine powder using ball-milling operated at grinding speed of 1200 rpm for 5 hours. After that, the Si particles were soaked in a ferric etchant containing 0.03 M Fe(NO3)3 and 5 M HF under continuous stirring for 2 hours. The precipitates containing porous Si particles were then collected and washed with ethanol and DI-H2O. After drying at 90 °C in air for 6 hours, the particles were collected for further use.
Synthesis of ball-milled Si particles: Metallurgical Si particles were ground to fine powder using ball-milling operated at grinding speed of 1200 rpm for 5 hours. The Si powder was then washed with HF and DI-H2O successively to remove surface oxide layer. After drying at 90 °C in air for 6 hours, the particles were collected for further use.
Synthesis of porous Si nanowires: Porous Si nanowires were synthesized according to our previous report15. Specifically, boron-doped Si wafers (resistivity <5 mΩ·cm) were immersed in an etchant solution containing 0.02 M AgNO3 and 5 M HF for 3 h. After being washed with DI-H2O, concentrated HNO3 and DI-H2O again, sequentially, porous Si nanowires were collected by scratching the wafers using a blade.
Synthesis of solid Si nanowires: Si wafers without doping were immersed in an etchant solution containing 0.02 M AgNO3 and 5 M HF for 3 h. After being washed with DI-H2O, concentrated HNO3 and DI-H2O again, sequentially, solid Si nanowires were collected by scratching the wafers using a blade.
Preparation of Si-based electrodes: The active material can be either porous Si nanoparticles or ball-milled Si nanoparticles. To prepare electrodes, active Si material was first mixed with carbon black and alginic acid sodium salt with mass ratio of 7:2:1 in water to form uniform slurry. The slurry was coated on copper foil and then dried at 90 °C in air for 6 hours.
For battery measurements, CR2032 coin cells were assembled using lithium foil as counter/reference electrode and Celgard 2400 as separator. The prepared Si-based electrodes were used as working electrodes. The electrolyte was 1 M LiPF6 in dimethyl carbonate (DMC)/fluoroethylene carbonate (FEC), 1:1 by volume. The galvanostatic charge-discharge test was carried out in the voltage window of 0.01–2 V (vs. Li/Li+) at a current density of 400 mA/g.
In situ TEM characterization
The experimental setup is schematically illustrated in Fig. 1a. The in situ TEM characterization was conducted using a nanobattery configuration with Si (ball-milled Si nanoparticles, porous Si nanoparticles, solid Si nanowires, or porous Si nanowires) as the working electrodes, Li as the reference electrode and Li2O as the solid electrolyte. All the in situ electrochemical tests were conducted in a Titan 80–300 scanning transmission electron microscope (STEM) operated at 300 kV with a Nanofactory TEM scanning tunneling microscopy (STM) holder. To assemble the nanobattery, a Cu rod and a W rod were firstly cut to produce clean and fresh cross section. Si was randomly attached to Cu rod as the working electrode by directly touching Si powder with the Cu rod. After that, the holder was transferred to Ar-filled glovebox, in which the W rod was used to scratch the Li metal surface to fetch some fresh Li. A conformal coating layer of Li on one end of the W rod served as the reference electrode and lithium source. The W rod was then mounted onto the holder by a screw for reliable mechanical and electrical connection. The entire assembly was then transferred to the microscope column within a sealed plastic bag. The lithium metal was only exposed to air during the insertion of the TEM holder into the microscope column, which is typically about 2 s. During this short period of air exposure, the surface of the lithium metal was oxidized to Li2O, which acts as the solid electrolyte for the function of the nanobattery. To initiate lithiation process, a bias of −2 V was applied on the Si electrode against the Li electrode to promote Li ion transport through the Li2O layer.
Ex situ TEM characterization
To characterize the structural evolution of ball-milled Si nanoparticles and porous Si nanoparticles after different charge-discharge cycles, the Li-Si cells were cycled in the voltage window of 0.01–2 V (vs. Li/Li+) at a current density of 400 mA/g and were then disassembled at delithiated state after different cycles inside Ar-filled glovebox. The active materials from the electrodes were then washed with acetonitrile and 0.5 M H2SO4 to remove the residual electrolyte and lithium salts. After that, the active materials were washed with DI-H2O and ethanol and finally dried at 90 °C in air for 6 hours before ex situ TEM characterization. Transmission electron microscope (JEOL, JEM-2100F) was used for ex situ TEM characterization in the paper. The pore size distributions were obtained based on statistical analysis of TEM images. For each sample, 200 pores were selected from TEM images and the largest diameter of each pore was measured for statistical analysis.
How to cite this article: Shen, C. et al. In Situ and Ex Situ TEM Study of Lithiation Behaviours of Porous Silicon Nanostructures. Sci. Rep. 6, 31334; doi: 10.1038/srep31334 (2016).
Tarascon, J. M. & Armand, M. Issues and challenges facing rechargeable lithium batteries. Nature 414, 359–367 (2001).
Goodenough, J. B. & Kim, Y. Challenges for Rechargeable Li Batteries. Chem. Mater. 22, 587–603 (2010).
Boukamp, B. A., Lesh, G. C. & Huggins, R. A. All-Solid Lithium Electrodes with Mixed-Conductor Matrix. J. Electrochem. Soc. 128, 725–729 (1981).
Larcher, D. et al. Recent findings and prospects in the field of pure metals as negative electrodes for Li-ion batteries. J. Mater. Chem. 17, 3759–3772 (2007).
Lee, S. W., McDowell, M. T., Choi, J. W. & Cui, Y. Anomalous Shape Changes of Silicon Nanopillars by Electrochemical Lithiation. Nano Lett. 11, 3034–3039 (2011).
Liu, X. H. et al. Anisotropic Swelling and Fracture of Silicon Nanowires during Lithiation. Nano Lett. 11, 3312–3318 (2011).
Liu, X. H. et al. Size-Dependent Fracture of Silicon Nanoparticles During Lithiation. ACS Nano 6, 1522–1531 (2012).
Chan, C. K. et al. High-performance lithium battery anodes using silicon nanowires. Nat. Nanotechnol. 3, 31–35 (2008).
Cui, L. F., Ruffo, R., Chan, C. K., Peng, H. & Cui, Y. Crystalline-Amorphous Core-Shell Silicon Nanowires for High Capacity and High Current Battery Electrodes. Nano Lett. 9, 491–495 (2009).
Park, M. H. et al. Silicon Nanotube Battery Anodes. Nano Lett. 9, 3844–3847 (2009).
Song, T. et al. Arrays of Sealed Silicon Nanotubes As Anodes for Lithium Ion Batteries. Nano Lett. 10, 1710–1716 (2010).
Hertzberg, B., Alexeev, A. & Yushin, G. Deformations in Si-Li Anodes Upon Electrochemical Alloying in Nano-Confined Space. J. Am. Chem. Soc. 132, 8548–8549 (2010).
Yao, Y. et al. Interconnected Silicon Hollow Nanospheres for Lithium-Ion Battery Anodes with Long Cycle Life. Nano Lett. 11, 2949–2954 (2011).
Liu, N. et al. A Yolk-Shell Design for Stabilized and Scalable Li-Ion Battery Alloy Anodes. Nano Lett. 12, 3315–3321 (2012).
Ge, M., Rong, J., Fang, X. & Zhou, C. Porous Doped Silicon Nanowires for Lithium Ion Battery Anode with Long Cycle Life. Nano Lett. 12, 2318–2323 (2012).
Ge, M., Fang, X., Rong, J. & Zhou, C. Review of porous silicon preparation and its application for lithium-ion battery anodes. Nanotechnology 24, 422001–422010 (2013).
Li, X. et al. Mesoporous silicon sponge as an anti-pulverization structure for high-performance lithium-ion battery anodes. Nat. Commun. 5, 4105 (2014).
Ge, M. et al. Large-Scale Fabrication, 3D Tomography and Lithium-Ion Battery Application of Porous Silicon. Nano Lett. 14, 261–268 (2014).
Lu, Z. et al. Nonfilling Carbon Coating of Porous Silicon Micrometer-Sized Particles for High-Performance Lithium Battery Anodes. ACS Nano 9, 2540–2547 (2015).
Shen, C. et al. Silicon(lithiated)-sulfur full cells with porous silicon anode shielded by Nafion against polysulfides to achieve high capacity and energy density. Nano Energy 19, 68–77 (2016).
Liu, X. H. et al. Ultrafast Electrochemical Lithiation of Individual Si Nanowire Anodes. Nano Lett. 11, 2251–2258 (2011).
Wang, C. M. et al. In Situ TEM Investigation of Congruent Phase Transition and Structural Evolution of Nanostructured Silicon/Carbon Anode for Lithium Ion Batteries. Nano Lett. 12, 1624–1632 (2012).
Gu, M. et al. In Situ TEM Study of Lithiation Behavior of Silicon Nanoparticles Attached to and Embedded in a Carbon Matrix. ACS Nano 6, 8439–8447 (2012).
McDowell, M. T. et al. Studying the Kinetics of Crystalline Silicon Nanoparticle Lithiation with In Situ Transmission Electron Microscopy. Adv. Mater. 24, 6034–6041 (2012).
McDowell, M. T., Lee, S. W., Wang, C. & Cui, Y. The effect of metallic coatings and crystallinity on the volume expansion of silicon during electrochemical lithiation/delithiation. Nano Energy 1, 401–410 (2012).
Gu, M. et al. Electronic Origin for the Phase Transition from Amorphous LixSi to Crystalline Li15Si4 . ACS Nano 7, 6303–6309 (2013).
McDowell, M. T. et al. In Situ TEM of Two-Phase Lithiation of Amorphous Silicon Nanospheres. Nano Lett. 13, 758–764 (2013).
Luo, L., Wu, J., Luo, J., Huang, J. & Dravid, V. P. Dynamics of Electrochemical Lithiation/Delithiation of Graphene-Encapsulated Silicon Nanoparticles Studied by In-situ TEM. Sci. Rep. 4, 3863 (2014).
Liu, X. H. et al. In situ atomic-scale imaging of electrochemical lithiation in silicon. Nat. Nanotechnol. 7, 749–756 (2012).
Hu, L. et al. Silicon-Carbon Nanotube Coaxial Sponge as Li-Ion Anodes with High Areal Capacity. Adv. Energy Mater. 1, 523–527 (2011).
Choi, J. W. et al. Stepwise Nanopore Evolution in One-Dimensional Nanostructures. Nano Lett. 10, 1409–1413 (2010).
Ryu, I., Choi, J. W., Cui, Y. & Nix, W. D. Size-dependent fracture of Si nanowire battery anodes. J. Mech. Phys. Solids 59, 1717–1730 (2011).
Kresse, G. & Furthmuller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Perdew, J. P. et al. Atoms, molecules, solids and surfaces: Applications of the generalized gradient approximation for exchange and correlation. Phys. Rev. B 46, 6671–6687 (1992).
Plimpton, S. Fast Parallel Algorithms for Short-Range Molecular Dynamics. J. Comput. Phys. 117, 1–19 (1995).
Cui, Z., Gao, F., Cui, Z. & Qu, J. A second nearest-neighbor embedded atom method interatomic potential for Li-Si alloys. J. Power Sources 207, 150–159 (2012).
Chan, C. K., Ruffo, R., Hong, S. S., Huggins, R. A. & Cui, Y. Structural and electrochemical study of the reaction of lithium with silicon nanowires. J. Power Sources 189, 34–39 (2009).
A portion of the TEM images used in this article were generated at the Center for Electron Microscopy and Microanalysis, University of Southern California. M.G. finished the research reported in this paper at University of Southern California and contributed to discussions after he joined Brookhaven National Laboratory. M.G. acknowledged the support of Brookhaven National Laboratory, which was supported by the U.S. Department of Energy, Office of Science, Office of Basic Energy Sciences, under Contract No. DE-SC0012704. C.W. was supported by the Assistant Secretary for Energy Efficiency and Renewable Energy, Office of Vehicle Technologies of the U.S. Department of Energy under Contract No. DE-AC02-05CH11231, Subcontract No. 6951379 under the Batteries for Advanced Battery Materials Research (BMR). The in situ TEM work was conducted in the William R. Wiley Environmental Molecular Sciences Laboratory (EMSL), a national scientific user facility sponsored by DOE’s Office of Biological and Environmental Research and located at PNNL.
The authors declare no competing financial interests.
About this article
Cite this article
Shen, C., Ge, M., Luo, L. et al. In Situ and Ex Situ TEM Study of Lithiation Behaviours of Porous Silicon Nanostructures. Sci Rep 6, 31334 (2016). https://doi.org/10.1038/srep31334
Capacity fading mechanism of Li2O loaded NiFe2O4/SiO2 aerogel anode for lithium-ion battery: Ex-situ XPS analysis
Applied Surface Science (2021)
Materials Research Express (2021)
Recent Tactics and Advances in the Application of Metal Sulfides as High‐Performance Anode Materials for Rechargeable Sodium‐Ion Batteries
Advanced Functional Materials (2021)
Morphological evolution of a single crystal silicon battery electrode during lithiation and delithiation: An operando phase-contrast imaging study
Energy Storage Materials (2020)