Abstract
Lithium-ion batteries connected in series are prone to be overdischarged. Overdischarge results in various side effects, such as capacity degradation and internal short circuit (ISCr). However, most of previous research on the overdischarge of a cell was terminated when the cell voltage dropped to 0 V, leaving the further impacts of overdischarge unclear. This paper investigates the entire overdischarge process of large-format lithium-ion batteries by discharging the cell to −100% state of charge (SOC). A significant voltage platform is observed at approximately −12% SOC and ISCr is detected after the cell is overdischarged when passing the platform. The scanning electron microscopy (SEM) and X-ray diffraction (XRD) results indicate that the overdischarge-induced ISCr is caused by Cu deposition on electrodes, suggesting possible Cu collector dissolution at the voltage platform near −12% SOC. A prognostic/mechanistic model considering ISCr is used to evaluate the resistance of ISCr (RISCr), the value of which decreases sharply at the beginning of ISCr formation. Inducing the ISCr by overdischarge is effective and well controlled without any mechanical deformation or the use of a foreign substance.
Similar content being viewed by others
Introduction
Lithium-ion batteries are currently used as power sources for electronic devices due to their high energy density and extended lifespan among comparable battery technologies1. However, the safety of lithium-ion batteries must be guaranteed before widespread application2,3,4,5.
The safety of lithium-ion batteries exposed to extreme conditions has been analyzed in previous studies in terms of thermal runaway6,7, overcharge8, overdischarge9,10 and internal short circuit (ISCr)11,12,13. Overdischarge is a common type of abuse that may lead to safety problems, such as ISCr9. Batteries are increasingly subjected to the conditions of overdischarge as greater numbers of cells are connected in series for a system requiring high voltage, such as electric vehicles14. Therefore, overdischarge and its impact on batteries must be investigated.
Several previous studies have cast light on the overdischarge mechanisms of lithium-ion batteries9,15,16,17. The anode potential increases abnormally during overdischarge; thus, the Cu current collector of the cell is oxidized to Cu2+ 9,14. Simultaneously, over-deintercalation of lithium at the anode during overdischarge causes decomposition of the solid electrolyte interface (SEI) and the decomposition of SEI generates gases, including carbon dioxide15. New SEI films form on the anode when the cell is recharged. The growth of the SEI films can lead to degradation of the electrochemical charge transfer processes in the electrodes17, as indicated by the impedance increment at low frequency9,18. Moreover, the morphology of the cathode materials also changes during overdischarge. The side reactions that occur during extreme overdischarge result in the solid-state amorphization of the transition metal compounds16. The changes in the morphology of the components within the lithium ion battery lead to capacity degradation. The dissolution of the Cu collector also affects the lifespan of the battery17.
Researchers have proposed several approaches to diminish the consequences of overdischarge. Three-electrode measurement was introduced for overdischarge testing to monitor the over-potential at the anode. Lee et al. avoided the high-level potential at the anode by adopting an Li2NiO2-added cell, which exhibits a near-cathode-limiting configuration14. Moreover, Kim et al. used succinonitrile as an electrolyte additive, which can form a passive layer on the Cu collector, to avoid Cu dissolution during overdischarge19.
However, most tests in the literature were terminated when the cell voltage dropped to 0 V, leaving the further influences of overdischarge unclear. Cells are connected in series in actual battery packs and a cell voltage lower than 0 V can occur when a cell is overdischarged. Overdischarge can lead to ISCr, which may cause thermal runaway during cycling. For example, Maleki et al. reported incidental ISCr after the cell was overdischarged and cycled9. Brand et al. studied the process of overdischarge and inferred the occurrence of ISCr from the temperature10. The possible hazards of ISCr remain unknown due to the insufficient number of studies to reveal the entire overdischarge process.
ISCr in lithium-ion batteries is under intensive study because of its significant impact on the batteries’ safety. Several approaches have been proposed to induce or simulate ISCr; however, most include mechanical deformation or the introduction of a foreign substance. Maleki et al.20, Cai et al.21 and Zhang et al.22,23 created ISCr by mechanical deformation and structural changes. Orendorff et al.24, Santhanagopalan et al.25 and Stringfellow et al.26 induced ISCr by introducing a foreign substance into the lithium-ion battery. The current study found that ISCr can be induced through deep overdischarge without mechanical destruction or foreign substances.
This work studies the mechanisms of forced overdischarge for large-format lithium-ion batteries. The overdischarge process is divided into three stages according to the characteristics of the entire voltage curves during overdischarge. The impact of overdischarge on the lithium-ion batteries at different stages is analyzed. Severe overdischarge, i.e., SOC < −12%, results in variant levels of ISCr caused by Cu foil dissolution and deposition. The resistance of ISCr (RISCr) quantitatively reflects the level of ISCr; therefore, RISCr is analyzed by recharging the battery after the overdischarge tests.
RISCr is evaluated using a prognostic/mechanistic model8,27,28 combined with ISCr29 by fitting the observed open circuit voltage (OCV) data during self-discharge. Furthermore, SEM and XRD experiments are conducted to study the surface morphology and characterization of the materials on electrodes. The results supported the notion that Cu deposition occurs during the overdischarge of lithium-ion batteries, which in turn causes ISCr.
Results
Voltage curve during overdischarge
The voltage during overdischarge is shown in Fig. 1(a). The overdischarge profile can be approximately divided into 3 stages according to the characteristics of the voltage variations. In Stage I (−11% < SOC ≤ 0%), the voltage dropped rapidly from 3.4 V to the minimum voltage of approximately −2.19 V, following a clear platform at approximately 1 V. In Stage II (−20% < SOC ≤ −11%), the voltage stopped declining and rebounded gradually with several fluctuations. In Stage III (−100% < SOC ≤ −20%), the voltage underwent a monotonic gradual increase asymptotically to 0 V without fluctuations.
The voltage drop in Stage I is caused by the increasing potential of anode and the decreasing potential of cathode; because overdischarge leads to deintercalation of Li+ from the anode and insertion into the cathode. In Stage II, when the anode potential reaches approximately 3.4~3.5 V15,19, anodic corrosion of the Cu collector is triggered; the anode potential thus enters an electrochemical reaction platform for the Cu dissolution. Copper ions dissolved in the electrolyte can travel through the separator and deposit on the cathode; the cathode potential thus increases due to the reduction of copper ions. The overpotential for Cu dissolution can account for the voltage valley at approximately −11% SOC. In Stage III, the electrochemical reactions of Cu dissolution and deposition continue and the internal short becomes more severe, with a decrease of RISCr. Therefore, the absolute value of the voltage, which is the product of the overdischarge current and RISCr, decreases and approaches zero.
The cells under overdischarge that were terminated in Stage I exhibited no discernible changes in properties, whereas in Stage III, the voltage increased slowly asymptotically to 0 V, suggesting the occurrence of severe ISCr. However, in Stage II, the properties of the voltage curve were more complex because the results varied at different terminal conditions. To detail the variations in voltage and its influence on overdischarge, the voltage curve of stage II was analyzed by incremental capacity analysis30, as shown in Fig. 1(b); the peaks and valleys of the incremental capacity curve indicate the inflection points of the voltage curve, denoted as MIN, A, B, C, D and E in Fig. 1(c). The terminal conditions in Stage II were chosen to be near the inflection points according to the voltage curve analysis above. Inflection point B in Fig. 1(b) is located at a significant peak of incremental capacity, representing the electrochemical reaction platform where Cu collector dissolution is inferred. Figure 2 illustrates the process of Cu dissolution during overdischarge and the formation of the ISCr induced by overdischarge. The internal short caused by Cu deposition occurs after the cell is overdischarged to SOC < −12% and becomes more severe during the overdischarge process.
Recharging after different degrees of overdischarge
Cells were recharged with 8.33 A (1/3C) current after the overdischarge tests terminated under different conditions (see Supplementary Table S1). The recharge experiments were separated into two categories (with and without ISCr) according to the occurrence of ISCr.
Cells 2, 3 and 4 did not exhibit ISCr after being overdischarged to MIN, A and B (Fig. 1(c)), respectively, as they could be fully recharged and cycled without any signs of ISCr or significant capacity loss. The results of the non-ISCr cells suggest that if the overdischarge is terminated before point B at approximately −12% SOC (the first platform after the occurrence of the minimum voltage), the cell can be fully charged back and reused with only minor side effects.
The other samples (with ISCr) overdischarged over point B showed evident characteristics of ISCr with different resistances (RISCr). Cells 5 and 6, overdischarged to −13.0% and −13.7% respectively, could be fully recharged with 8.33 A (1/3C) current (Fig. 3(a)). After the recharge, cells 5 and 6 displayed significant self-discharge and the depleting OCV of cells 5 and 6 is shown in Fig. 3(b). It was more difficult to fully charge cell 6 compared to cell 5, as the charging time was longer for cell 6. Moreover, the OCV of cell 6 depletes more rapidly than that of cell 5. This phenomenon suggests that cells 5 and 6 both suffered from ISCr and the RISCr of cell 6 was lower than that of cell 5.
Cells that had been overdischarged to SOC < −14.5% could not be fully recharged to 4.2 V with 8.33 A (1/3C) current. During the recharge process, their voltages increased once the recharge began but soon reached a stable value. The stable voltage during the recharge process becomes lower as the overdischarge increased further, suggesting a lower RISCr.
Estimation of RISCr using a prognostic/mechanistic model
RISCr can be quantitatively evaluated by analyzing the depleting OCV after the cell is fully recharged. The RISCr of cells 5 and 6 are estimated using prognostic/mechanistic model8,27,28 combined with an equivalent circuit model of a battery with ISCr29, as shown in Fig. 4(b). According to the equivalent circuit model, the simulated OCV, denoted as Vsim(t) in Eqn. (1), is equal to the voltage caused by RISCr.
The current I(t) is a constant 0 because the voltage of the battery is observed at an open circuit, as shown in Eqn. (2). Combining Eqn. (2) with Kirchhoff’s current law in Eqn. (3), we obtain Eqn. (4), which indicates that the current through RISCr and internal resistance R should be the equivalent at any given time.
Eqn. (5) is written according to Kirchhoff’s voltage law, where E(t) denotes the electromotive force given by the prognostic/mechanistic model in Eqn. (6). Vp(y(t)) and Vn(x(t)) denote the cathode potential and anode potential, respectively. y(t) is defined as a customized variable in the half-cell tests instead of the stoichiometric lithium content in the cathode8. Furthermore, x(t) refers to the value x in LixC631. Half-cells with LiyNi1/3Co1/3Mn1/3O2(NCM)/Li and graphite/Li were made and cycled at C/20 current at 25 °C to acquire Vp(y) and Vn(x) (see Supplementary Fig. S1).
Eqn. (7), which is derived from Eqns (4, 5, 6), determines the current during self-discharge. By combining Eqn. (7) with Eqn. (1), we obtain the expression of Vsim(t) in Eqn. (8).
The cathode potential Vp(y(t)) and anode potential Vn(x(t)) change over time during the self-discharge process because y(t) and x(t) are functions of time, as shown in Eqns (9, 10), where y0 (x0) denotes the initial value of y (x), Cp (Cn) represents the capacity of the cathode (anode) and is the integral of the self-discharge current. The cathode potential and anode potential during self-discharge can be determined by combining y(t) and x(t) with the separated half-cell quasi-equilibrium voltage curve, as shown in Supplementary Fig. S1.
Therefore, the OCV during self-discharge can be simulated from Eqns (7, 8, 9, 10) by choosing appropriate settings for [R, RISCr, y0, x0, Cp, Cn] using an optimization method, such as a genetic algorithm, as in refs 8,28. The root mean squared error (RMSE) between the simulated open circuit voltage Vsim(t) and the observed open circuit voltage is calculated to evaluate the degree of coincidence, as shown in Eqn. (11). n is the length of data used for the simulation and represents the time points.
Figure 3(b) compares the simulated OCV with the observed OCV for cells 5 and 6. The simulated voltage curves fit the experimental observations well, indicating that the model and identified parameters approximately reflect the ISCr of the overdischarged cells.
The of the cells that could not be fully recharged with 8.33 A (1/3C) current is estimated simply dividing the stable voltage by the charging current, because all of the charging current is entirely bypassed by RISCr.
Figure 5 shows the relationship between the estimated RISCr and the overdischarge SOC. The results suggest that ISCr occurs after the inflection point B at approximately −12% SOC, where the first platform after the minimum voltage is located. The RISCr declines with a lower overdischarge SOC. This method of inducing ISCr by overdischarge is effective and can be well controlled.
SEM and XRD results
The SEM and XRD results reveal the surface morphology and structural characterization of ISCr induced by overdischarge. Digital photographs of the electrodes dissembled from cells 1 and 10, which were dismantled after the overdischarge test, are shown in Fig. 6(g–j). Both the cathode and anode of cell 10 are stained with Cu deposition, which is irregularly observed throughout the entire electrodes.
The SEM morphologies of the materials on the electrodes from cells 1 and 10 are compared in Fig. 6(a–f). Figure 6(a,d) show normal graphite and LiyNi1/3Co1/3Mn1/3O2 materials on the anode and cathode, respectively. The surface of the graphite anode of cell 1 is smooth and the cathode is flat with a porous structure. However, after overdischarge to −20% SOC (as in cell 10), the smooth graphite anode is dotted with small spherical depositions, as shown in Fig. 6(b,c), whereas the cathode of cell 10 is also contaminated by larger spherical depositions on the cathode materials, as shown in Fig. 6(e,f).
The XRD results in Fig. 7 suggest that Cu deposition increases gradually on both the anode and cathode during the entire overdischarge process. The emerging peaks of Cu support the previous assumption that Cu foil dissolution and deposition occur on the electrodes during overdischarge.
The SEM and XRD results, in combination with the previous analysis of ISCr induced by overdischarge, demonstrate that the Cu foil dissolution is caused by overdischarge and that the subsequent deposition of cupric ion on the electrodes results in ISCr when Cu deposition penetrates the separator and bridges the two electrodes. As the duration of overdischarge increases, Cu becomes further dissolved and deposited between the electrodes, resulting in more severe ISCr with a lower RISCr.
Discussion
This research investigates the entire overdischarge process and overdischarge-induced ISCr of large-format Li-ion batteries with an LiyNi1/3Co1/3Mn1/3O2 (NCM) cathode and graphite anode. The voltage of the overdischarged battery decreases to the minimum value at approximately −11% SOC and then increases with several inflection points, eventually asymptotically approaching 0 V. A significant peak of incremental capacity which represents the electrochemical reaction platform of Cu collector dissolution is observed at approximately −12% SOC.
Neither ISCr nor capacity fading occurs if the overdischarge is terminated before −12% SOC, where the first platform after the minimum voltage is located. However, if the terminal SOC is lower than −12%, then the battery suffers from ISCr, which is the result of Cu foil dissolution and deposition on electrodes according to the SEM and XRD results.
The RISCr induced by overdischarge is evaluated using an equivalent circuit model with ISCr and a prognostic/mechanistic model. RISCr sharply decreases, from −12% to −15% SOC, at the beginning of internal short formation, after which RISCr continues to decrease, albeit more gradually.
The overdischarge-induced ISCr is likely to occur when lithium-ion batteries are connected in series with great inconsistency. Moreover, the ISCr induced by overdischarge is well controlled without any mechanical deformation or foreign substance.
The authors wish to note that the capacity ratios of negative to positive electrode have impact on the electrochemical reaction of Cu oxidation. To be specific, given an increased capacity ratio of negative and positive electrode, i.e. more active materials on the negative electrode, the occurrence of the potential of Cu dissolution at the negative electrode will be delayed, thereby postponing the Cu collector dissolution to an SOC more negative than −12% (−15%, −20% etc.).
Methods
Performance test
A 25 Ah commercial pouch Li-ion cell with a hard steel case was tested in this study. The cathode material of the battery was NCM and the anode was graphite; the capacity ratio of negative to positive electrode is 1.18. The performance tests were conducted before the overdischarge tests. The battery was cycled between the voltage limits of 4.2 V and 2.75 V with C/3 current at 25 °C, as listed in Supplementary Table S2. The discharge capacity measured in Step 7 is regarded as the original discharge capacity of the battery.
Overdischarge test
The overdischarge tests were performed in an explosion-proof chamber using a battery test bench manufactured by Digatron® (Digatron Power Electronics GmbH, Tempelhofer Str. 12–14, 52068 Aachen, Germany). In the test, a fully discharged battery was connected in series with 4 auxiliary batteries and the voltages were monitored. Figure 8 illustrates how the batteries were connected and placed in the overdischarge tests. Supplementary Table S1 summarizes the experimental settings of the 16 batteries. The overdischarge tests covered a wide range of terminal SOCs. Experiments 12–16 were performed to investigate the overall voltage variation of the battery during overdischarge and a typical voltage curve was drawn (Fig. 1(a)). In experiments 2–9, the terminal conditions were chosen according to the analysis of the overall voltage variation during overdischarge (Fig. 1(c)).
Recharge test
The recharge tests were conducted on the battery after the overdischarge tests to analyze the impact of overdischarge and estimate the RISCr induced by overdischarge. After being overdischarged once, cells were recharged with 8.33 A (1/3C) current and cycled, if possible. If the cell could be fully recharged and exhibited stable static OCV without self-depleting, then the cell was cycled with the same profile as the performance test listed in Supplementary Table S2 to analyze the capacity degradation. If the cell was successfully recharged to 4.2 V but exhibited a significant decrease in OCV, then the cell was considered to have ISCr and its OCV was further investigated. If the cell could not be charged to 4.2 V, then the recharging was held until its voltage reached a stable value.
SEM test
Cells were dismantled after the overdischarge test and the surface morphology of the electrodes was analyzed by an SEM manufactured by JEOL® (3-1-2 Musashino, Akishima, Tokyo 196-8558, JAPAN). The tested cells included cells 1 and 10. Cell 1 was not overdischarged as a control experiment and cell 10 was overdischarged to −20% SOC.
XRD test
Cells 1, 5 and 10 were studied using an XRD manufactured by Bruker® (Bruker AXS GmbH, Östliche Rheinbrückenstr. 49, 76187 Karlsruhe, Germany) to analyze the structural characterization of the active materials on both electrodes.
Half-cell test
The electrochemical properties of electrodes were investigated by half-cell tests. Half-cells with NCM/Li and graphite/Li were made from pieces cut from the electrodes of the battery used in this work. The half-cells were cycled at C/20 current at 25 °C to simulate quasi-equilibrium electrochemical conditions. No significant differences in capacity and electrochemical property were observed between the electrode materials of cell 1 (not overdischarged) and cell 3 (overdischarged to −11%). The OCV of the cathode/anode (Supplementary Fig. S1) is defined as the average of low current charge and discharge curves.
Additional Information
How to cite this article: Guo, R. et al. Mechanism of the entire overdischarge process and overdischarge-induced internal short circuit in lithium-ion batteries. Sci. Rep. 6, 30248; doi: 10.1038/srep30248 (2016).
References
Tarascon, J. M. & Armand, M. Issues and challenges facing rechargeable lithium batteries. Nature 414, 359–67 (2001).
Lu, L., Han, X., Li, J., Hua, J. & Ouyang, M. A review on the key issues for lithium-ion battery management in electric vehicles. J. Power Sources 226, 272–288 (2013).
Goodenough, J. B. & Kim, Y. Challenges for rechargeable Li batteries. Chem. Mater. 22, 587–603 (2010).
Armand, M. & Tarascon, J.-M. Building better batteries. Nature 451, 652–657 (2008).
Zhang, G. et al. Reaction temperature sensing (RTS)-based control for Li-ion battery safety. Sci. Rep. 5, 18237 (2015).
Feng, X. et al. Thermal runaway features of large format prismatic lithium ion battery using extended volume accelerating rate calorimetry. J. Power Sources 255, 294–301 (2014).
Huang, P., Wang, Q., Li, K., Ping, P. & Sun, J. The combustion behavior of large scale lithium titanate battery. Sci. Rep. 5, 7788 (2015).
Ouyang, M. et al. Overcharge-induced capacity fading analysis for large format lithium-ion batteries with LiyNi1/3Co1/3Mn1/3O2+LiyMn2O4 composite cathode. J. Power Sources 279, 626–635 (2015).
Maleki, H. & Howard, J. N. Effects of overdischarge on performance and thermal stability of a Li-ion cell. J. Power Sources 160, 1395–1402 (2006).
Brand, M. et al. Electrical safety of commercial Li-ion cells based on NMC and NCA technology compared to LFP technology. 1–9 (2013).
Feng, X., Weng, C., Ouyang, M. & Sun, J. Online internal short circuit detection for a large format lithium ion battery. Appl. Energy 161, 168–180 (2016).
Xu, J., Liu, B. & Hu, D. State of Charge Dependent Mechanical Integrity Behavior of 18650 Lithium-ion Batteries. Sci. Rep. 6, 21829 (2016).
Wu, H., Zhuo, D., Kong, D. & Cui, Y. Improving battery safety by early detection of internal shorting with a bifunctional separator. Nat. Commun. 5, 5193 (2014).
Lee, H. et al. Li2NiO2 as a novel cathode additive for overdischarge protection of li-ion batteries. Chem. Mater. 20, 5–7 (2008).
Li, H.-F., Gao, J.-K. & Zhang, S.-L. Effect of Overdischarge on Swelling and Recharge Performance of Lithium Ion Cells. Chinese J. Chem. 26, 1585–1588 (2008).
Shu, J. et al. A comparative study of overdischarge behaviors of cathode materials for lithium-ion batteries. J. Solid State Electrochem. 16, 819–824 (2012).
Zhang, L. et al. Capacity fading mechanism during long-term cycling of over-discharged LiCoO2/mesocarbon microbeads battery. J. Power Sources 293, 1006–1015 (2015).
Erol, S., Orazem, M. E. & Muller, R. P. Influence of overcharge and over-discharge on the impedance response of LiCoO2|C batteries. J. Power Sources 270, 92–100 (2014).
Kim, Y. S. et al. Succinonitrile as a corrosion inhibitor of copper current collectors for overdischarge protection of lithium ion batteries. ACS Appl. Mater. Interfaces 6, 2039–2043 (2014).
Maleki, H. & Howard, J. N. Internal short circuit in Li-ion cells. J. Power Sources 191, 568–574 (2009).
Cai, W., Wang, H., Maleki, H., Howard, J. & Lara-Curzio, E. Experimental simulation of internal short circuit in Li-ion and Li-ion-polymer cells. J. Power Sources 196, 7779–7783 (2011).
Ramadass, P., Fang, W. & Zhang, Z. (John). Study of internal short in a Li-ion cell I. Test method development using infra-red imaging technique. J. Power Sources 248, 769–776 (2014).
Fang, W., Ramadass, P. & Zhang, Z. (John). Study of internal short in a Li-ion cell-II. Numerical investigation using a 3D electrochemical-thermal model. J. Power Sources 248, 1090–1098 (2014).
Christopher, J. & Orendorff Ganesan Nagasubramanian, E. P. R. Experimental triggers for internal short circuits in lithium-ion cells. J. Power Sources 196, 6554–6558 (2011).
Santhanagopalan, S., Ramadass, P. & Zhang, J. (Zhengming). Analysis of internal short-circuit in a lithium ion cell. J. Power Sources 194, 550–557 (2009).
Stringfellow, R., Ofer, D., Sriramulu, S. & Barnett, B. Lithium-Ion Battery Safety Field-Failure Mechanisms. Meet. Abstr. MA2010–02, 322 (2010).
Feng, X. et al. Characterization of large format lithium ion battery exposed to extremely high temperature. J. Power Sources 272, 457–467 (2014).
Han, X., Ouyang, M., Lu, L. & Li, J. A comparative study of commercial lithium ion battery cycle life in electric vehicle: Capacity loss estimation. J. Power Sources 268, 658–669 (2014).
Ouyang, M. et al. Internal short circuit detection for battery pack using equivalent parameter and consistency method. J. Power Sources 294, 272–283 (2015).
Feng, X. et al. Using probability density function to evaluate the state of health of lithium-ion batteries. J. Power Sources 232, 209–218 (2013).
Ohzuku, T. Formation of Lithium-Graphite Intercalation Compounds in Nonaqueous Electrolytes and Their Application as a Negative Electrode for a Lithium Ion (Shuttlecock) Cell. J. Electrochem. Soc. 140, 2490 (1993).
Acknowledgements
This work was supported by the National Natural Science Foundation of China under the contract of No. U1564205 and by the US-China Clean Energy Research Center–Clean Vehicle Consortium (CERC-CVC). The Chinese side of the CERC-CVC is supported by the MOST (Ministry of Science and Technology) of China under the contract of No. 2014DFG71590. The first author is also supported by Tsinghua University Initiative Scientific Research Program and Tsinghua University Student Research Training Program No. 1521T0086.
Author information
Authors and Affiliations
Contributions
R.G. designed and carried out the experiment, processed the data, performed simulations, prepared all the figures and wrote the manuscript. L.L. and X.F. assisted in simulations and interpretation of the data. M.O. supervised the project. All authors revised the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Guo, R., Lu, L., Ouyang, M. et al. Mechanism of the entire overdischarge process and overdischarge-induced internal short circuit in lithium-ion batteries. Sci Rep 6, 30248 (2016). https://doi.org/10.1038/srep30248
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep30248
This article is cited by
-
An experimental study on the failure behaviors of hybrid supercapacitors under overdischarge conditions
Ionics (2024)
-
A phenomenological and quantitative view on the degradation of positive electrodes from spent lithium-ion batteries in humid atmosphere
Scientific Reports (2023)
-
Surface chemical heterogeneous distribution in over-lithiated Li1+xCoO2 electrodes
Nature Communications (2022)
-
Studies on the deposition of copper in lithium-ion batteries during the deep discharge process
Scientific Reports (2021)
-
Challenges and recent progress in thermal management with heat pipes for lithium-ion power batteries in electric vehicles
Science China Technological Sciences (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.