Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Magnetic coupling at rare earth ferromagnet/transition metal ferromagnet interfaces: A comprehensive study of Gd/Ni


Thin film magnetic heterostructures with competing interfacial coupling and Zeeman energy provide a fertile ground to study phase transition between different equilibrium states as a function of external magnetic field and temperature. A rare-earth (RE)/transition metal (TM) ferromagnetic multilayer is a classic example where the magnetic state is determined by a competition between the Zeeman energy and antiferromagnetic interfacial exchange coupling energy. Technologically, such structures offer the possibility to engineer the macroscopic magnetic response by tuning the microscopic interactions between the layers. We have performed an exhaustive study of nickel/gadolinium as a model system for understanding RE/TM multilayers using the element-specific measurement technique x-ray magnetic circular dichroism, and determined the full magnetic state diagrams as a function of temperature and magnetic layer thickness. We compare our results to a modified Stoner-Wohlfarth-based model and provide evidence of a thickness-dependent transition to a magnetic fan state which is critical in understanding magnetoresistance effects in RE/TM systems. The results provide important insight for spintronics and superconducting spintronics where engineering tunable magnetic inhomogeneity is key for certain applications.


Modified magnetic interaction at the interfaces between different ferromagnetic materials can be utilised to engineer materials with magnetic properties that are significantly different from the bulk. A classical example of such a system is a rare-earth/transition-metal (RE/TM) ferromagnetic multilayer since in the presence of an external magnetic field the layers couple parallel, but the antiferromagnetic coupling between the layers can lead to novel magnetic states and phase transitions between them. Ferrimagnetic alloys and multilayers (antiparallel alignment between layers) are of great interest fundamentally and from an applied point of view. Ferrimagnetic alloys were until very recently the only magnetic system that showed ultrafast magnetisation switching induced by a femtosecond laser pulse1,2,3,4, and engineered magnetic multilayers are key components of superconducting spin valves5,6,7,8.

The theoretical groundwork of RE/TM systems was established by Camley and Tilley9,10; they modelled RE/TM multilayers and found that due to the different Curie temperatures (TC) of the RE and TM layers several phases occur as the effects of temperature and applied magnetic field are incorporated. At temperatures far below the TC of the RE, the RE aligns with the applied field while the TM aligns antiparallel to both the RE and the applied field. This is called the RE-aligned state. At higher temperatures, the magnetisation of the RE decreases and a second-order phase transition to the TM-aligned state occurs in which the TM aligns parallel to the applied field and the RE aligns antiparallel to both the TM and the applied field. This simple picture was later confirmed experimentally11,12; however, the existence of a twisted state at the interface between bulk Fe and a thin layer of Gd (five atomic layers) was also predicted by Camley for certain values of the applied field13, but this has not been conclusively demonstrated.

Due to the interface-driven nature of RE/TM systems it is difficult to measure the exact magnetic structures of the individual layers using standard measurement techniques such as vibrating sample magnetometry or magnetoresistance measurements14,15,16. Additionally, at low temperatures the magnetisation of a RE layer in a RE/TM bilayer will be far larger than that of the TM layer, meaning it can be extremely difficult to deconvolute the two signals. Therefore, an element specific measurement technique such as x-ray magnetic circular dichroism (XMCD) is essential for investigating RE/TM systems. The energy of the x-rays used can be tuned to the absorption edges of particular elements, meaning only the magnetic response of specific layers is measured at any one time. Previous studies using XMCD have mainly confirmed the predictions of Camley and Tilley9,10: Barth et al. observed evidence of the transition between the RE- and TM-aligned state as a function of temperature in a Ni/Gd bilayer (7.5 nm and 5 nm thick, respectively)12, while Koizumi et al. observed the same behaviour in a Gd/Fe (2 nm/2 nm)50 superlattice measured at 20 K and room temperature17.

In this study we present extensive XMCD results of Ni/Gd/Ni films allowing us to fully map the magnetic states as a function of applied field and temperature for a wide range of different Ni and Gd thicknesses (Fig. 1). Our results demonstrate the full richness of the magnetic state diagram of RE/TM systems and shed new light on previous work that interpreted results based on an incomplete picture of RE/TM behaviour14,18.

Figure 1
figure 1

(a) Diagram of experimental setup showing the structure of the samples, the direction of the incident x-rays, and the position of the measuring photodiodes (I0 and I). (b) Examples of XMCD spectra taken at ~6 K for Ni (i) and Gd (ii). The XMCD was measured at the Ni L3 and Gd M5 absorption edges, respectively, marked by dotted lines. The two signals μ+ and μ are from positive and negative saturation, while Δμ is the difference between the two, vertically offset for clarity. (c) Hysteresis loops measured between 5 and 10 K (low T), and 45 and 65 K (high T), that are representative of the three observed behaviours (N.B. Axis on all plots identical). The (total) Ni and Gd thicknesses of each of the samples are (from left to right): 5 nm Ni and 4.5 nm Gd, 6 nm Ni and 8 nm Gd, and 8 nm Ni and 6 nm Gd. The last sample is the same as that from which the XMCD spectra are shown in (b).


We measured 15 polycrystalline samples by XMCD, each with different layer thicknesses, throughout a range of temperatures between 6 K and room temperature. Since the magnetic signal that is detected by XMCD is the projection of the magnetic moment onto the wavevector of the x-ray, the magnet coils are placed such that the applied magnetic field is parallel to the propagation direction of the x-rays. The easy-axis of the thin films is in-plane, so for effective measurement of the magnetic moment of the samples as small an angle as possible is desirable between the plane of the samples and the x-ray propagation; here we used an angle of 30 degrees as the films are measured in transmission.

The measured samples displayed one of three behaviours as illustrated in Fig. 1(c) which shows element-specific magnetisation versus applied field (M(H)) hysteresis loops at high and low temperatures for three different samples that are characteristic of each behaviour. In the first behaviour the Ni layers follow the applied magnetic field (positive magnetisation in positive field) while the Gd layer remains antiparallel to the Ni and the magnetic field. This does not change as the temperature is increased. The hysteresis loops shown are from a sample with total Ni thickness of 5 nm, and Gd thickness of 4.5 nm (Note that the multilayers are of the form Ni/Gd/Ni, with equal Ni thicknesses either side of the Gd. This means that the thicknesses of the individual Ni layers will be half that of the total Ni thickness, and it is the total Ni thickness which is measured and stated in the text and figure captions.) In the second behaviour, the opposite is observed at lower temperatures: the Ni is antiparallel to the field while the Gd is parallel. Above a transition temperature, this state is reversed to the same as that in behaviour 1. The thicknesses of the Ni and Gd in this sample are 6 nm and 8 nm, respectively. The third behaviour is more complex: the Ni M(H) loops at low temperature displays a distinctive “N”-shape, indicative of significant magnetic inhomogeneity, in this case probably a fan-like state, in Ni during magnetisation reversal; the Gd layer undergoes a gradual transition over a temperature range of tens of kelvins from aligned parallel to the Ni to antiparallel. The sample displaying this behaviour in the figure had Ni and Gd thicknesses of 8 nm and 6 nm, respectively, and is the same sample as that for which the XMCD spectra are shown in Fig. 1(b).


A simple model exploring the competition between the different energies in the system allows us to confirm our explanation of the observed behaviour and illustrate possible micromagnetic structures within the samples which can reproduce the measured hysteresis loops. The model uses the Stoner-Wohlfarth framework by Mauri et al.19, and that of Camley and Tilley, wherein an iterative process is used to find the ground state of a stack of Ni and Gd atomic layers. We solve the following equation to find the angle of one magnetic moment at which the energy is a minimum:

where g is the Landé g-factor, μB is the Bohr magneton, μ0 is the permeability of free space, M is the average magnetisation of the layer (in our case M is equal to the value of the magnetic moment of the atom for a perfectly ordered material), ϕ is the angle of a magnetic moment with respect to the applied magnetic field direction, K is the magnetocrystalline anisotropy energy, θ is the direction of the magnetic easy axis, n is the number density of the material of the layer, J is the exchange constant of the layer, and S is the magnitude of the magnetic moment of an atom in units of the Bohr magneton. We then iterate through the stack at each magnetic field value using the output of one iteration as the input for the next, until the difference between two iterations is less than a specified value. This process is repeated for each magnetic field value. Figure 2 shows a comparison between the results of the model and the temperature dependence of the third type of behaviour, which match very closely despite the simplicity of the model.

Figure 2: Comparison between the hysteresis loops measured by XMCD and those produced by the model, as well as detailed view of the micromagnetic structure of the sample at certain temperatures and field values extracted from the model.
figure 2

(a,c) Hysteresis loops, experimental and theoretical for Ni and Gd, respectively. The magnetisation has been normalised by the highest and lowest values of magnetisation within the loop to ease comparison. Shaped markers on some theoretical loops show the temperature and field values of the vector diagrams in (b). (b) Vector diagrams showing the direction of magnetisation of each atomic layer in the model system used to produce the hysteresis loops. The magnitude of the magnetisation is not shown. Black arrows represent Ni layers, red Gd, as labelled in the top left. The experimental hysteresis loops are from the same sample as that shown in Fig. 1(b,c) (behaviour 3), and has (total) Ni and Gd thicknesses of 8 nm and 6 nm, respectively.

The model we use allows us to extract the micromagnetic structure from the system that produced the hysteresis loops since the modelled system is a one-dimensional stack of magnetic moments. The sum of the projections of the magnetic moments of each of the elements onto the direction of the applied field gives the total magnetisation at each field value, as shown in the hysteresis loops. The original angles of the each magnetic moment can also be plotted individually to give magnetic vector diagrams that show the inhomogeneity in the system at particular field values (Fig. 2(b)).


The first two observed behaviours can be understood in terms of the variation in the influence of the interfacial layers in the multilayer compared to that of the bulk. In the thinnest samples, the interfacial coupling will dominate and if the ratio between the Ni and Gd thicknesses favors the Ni, the Ni will control the behaviour of the Gd despite the higher magnetic moment of the Gd at lower temperatures (behaviour 1). For slightly thicker Gd layers, although the interfacial coupling still dominates the behaviour of the system, the Gd will dominate the Ni while its magnetic moment is not suppressed by the increasing temperature (behaviour 2).

We can now use the model to examine in detail the third observed behaviour. Magnetic vector diagrams produced by the model are shown in Fig. 2(b) and help illustrate our interpretation of the experimental results. They show the angles of the magnetisation for each atomic layer calculated by the model at a particular field value and temperature; the field values are indicated on the corresponding hysteresis loops. Figure 2(a,c) show the experimental and modelled hysteresis loops as a function of temperature. At 6 K and high fields, we expect the majority of moments in the both the Ni and Gd layers to be aligned parallel with the applied field direction. However, if the interfacial antiparallel coupling is maintained, there must be some moments canted away from this direction (seen in the vector diagrams marked with a square). Indeed, the model enforces strict antiparallel coupling at the interface, and the fact that the magnetisation at the maximum applied field is not the highest magnetisation measured in both the Ni and Gd loops supports this experimentally. The angle of the moments canting away from the applied field direction are highest at the interface, and due to the intra-layer exchange energies the angle changes continuously to allow the moments to align with the bulk further away from the interface. As the applied field is lowered the exchange energies dominate over the Zeeman energy and the change in angle of moments as a function of the distance from the interface is reduced (seen in the vector diagrams marked with a circle). This means that either the Ni or Gd are forced to align mostly antiparallel to the applied field due to the influence of the interfacial coupling. At low temperatures the Gd couples more strongly to the field and so forces the Ni to align antiparallel to both the Gd and the field. This is reflected in the hysteresis loops; as the field strength is decreased the magnetisation of the Ni decreases to negative saturation as the bulk Ni moments are forced by the intra-layer exchange energy to follow the Ni moments which are closest to the interface with the Gd. Then, as the field crosses zero, the Gd moments flip, following the field, and the Ni moments also all flip as shown by the sudden reversal in the hysteresis loop from negative to positive saturation (shown in the vector diagrams marked with a triangle).

As the temperature increases, the reversal of Ni becomes less pronounced due to a lowered influence of the Gd (Gd has a Curie temperature less than half that of Ni), and vanishes altogether by 50 K. Correspondingly, the Gd begins to display similar signs to those that the Ni displayed at low temperature; sudden magnetisation reversals that do not follow the direction of the applied field. This indicates that more of the Ni moments will be aligned with the field at high fields and higher temperatures, and we can see from the corresponding Gd loops that the Gd is for the most part completely under the influence of the Ni and remains antiparallel to both the Ni and the applied field for the majority of the applied field range. Any magnetic inhomogeneity that was present at the interface at lower temperatures has vanished for the most part.

The novel behaviour described above is reproducibly observed in multiple samples and so is a general behaviour. The measured samples were grown in four different growth runs, but we are confident that the observed effects are due to thickness dependence, and not stochastic variations in the growth conditions. This is because, firstly, samples from different growth runs display the same types of behaviours. Secondly, imaging the magnetic landscape on a micron-scale for three samples using a scanning SQUID microscope20, a sensitive probe of magnetic flux, shows consistent resolution-limited domain structure and uniform magnetisation strength for a variety of locations in each sample.

The measurement setup limits prevented us from applying a high enough field to observe true saturation. For example, we can see in the Ni loop at 6 K that the highest magnetisation in the loop is not the saturation magnetisation of the Ni at high fields. However, another factor influencing the saturation magnetisation is the measurement geometry; as previously mentioned, the magnetic field is necessarily applied at a 30 degree angle out of the plane of the samples.

Figure 3 shows a magnetic state diagram for a particular sample that has been extracted from the experimental data as an illustration of how such a comprehensive study could help use the understanding gained about the RE/TM system to design new experiments and devices. To construct the figure, the Ni and Gd hysteresis loops are first normalized, so the maximum of the modulus of the difference is 2 (ΔMs = 2); this corresponds to the Ni and Gd having oppositely saturated magnetisations, while ΔMs = 0 corresponds to parallel Ni and Gd. We know that when the Ni and Gd layers are antiparallel there is no inhomogeneity at the interfaces, but the inhomogeneity will nucleate at the interfaces as the angle between the layers changes. Such a magnetic state diagram can also be constructed from the output of the model which could then be used to pick parameters that maximise magnetic inhomogeneity in devices in fields such as spintronics and superconducting spintronics where the manipulation of such magnetic structures is desirable.

Figure 3: Phase diagram showing the degree of inhomogeneity present in an experimental multilayer as a function of applied field and temperature.
figure 3

The phase diagram is constructed from experimental hysteresis loops by taking the difference between the normalised magnetisation of Ni and Gd at each field value in a loop. This is then repeated for every temperature.

In summary, we have performed a comprehensive experimental study of the RE/TM system using an extremely powerful measurement technique (XMCD). The use of the simple model allows a detailed view of the micromagnetic structure that is responsible for any of the three behaviours that were observed. The strict antiferromagnetic exchange coupling between RE and TM ferromagnets and its competition with the intralayer exchange energy and the Zeeman energy has been shown to lead to significant inhomogeneity in the system. The relative strengths of these energies, and thus the behaviour of the system can be tuned by varying the thickness of the individual layers within the multilayer, and our characterisation of the necessary thicknesses should enable the design of a new generation of devices that can utilise the magnetic inhomogeneity present at RE/TM interfaces including spintronics and superconducting spintronics. Our work will help to reinterpret the results of previous studies, and has consolidated our knowledge of another otherwise simple system that can be engineered to yield not only fundamentally interesting behaviours, but behaviours that have the potential to influence future technologies based on spintronics and superconducting spintronics21,22,23,24.


D.C. magnetron sputtering

The samples were grown at room temperature by d.c. magnetron sputtering in a system with a base pressure better than 10−8 mbar. The growth rate was 2.1 nm min−1 for Ni and 9.8 nm min−1 for Gd in argon at a pressure of 1.5 Pa.


XMCD was performed at beam line 13-1, SSRL at SLAC National Accelerator Laboratory. The geometry of the measurement setup is sketched in Fig. 1(a). Photodiodes measure the photon count before and after the x-rays pass through the sample. This allows a relative transmission to be measured while allowing for corrections to be made in fluctuations in the synchrotron beam. An electromagnet was mounted parallel to the x-ray propagation direction allowing applied fields in that direction of up to 250 mT, and a helium cryostat could cool the samples to approximately 6 K.

Data Availability

The data supporting this paper is available open access at

Additional Information

How to cite this article: Higgs, T. D. C. et al. Magnetic coupling at rare earth ferromagnet/transition metal ferromagnet interfaces: A comprehensive study of Gd/Ni. Sci. Rep. 6, 30092; doi: 10.1038/srep30092 (2016).


  1. Mentink, J. H. et al. Ultrafast spin dynamics in multisublattice magnets. Phys. Rev. Lett. 108, 057202 (2012).

    ADS  CAS  Article  Google Scholar 

  2. Kirilyuk, A., Kimel, A. V. & Rasing, T. Ultrafast optical manipulation of magnetic order. Rev. Mod. Phys. 82, 2731–2784 (2010).

    ADS  Article  Google Scholar 

  3. Graves, C. et al. Nanoscale spin reversal by non-local angular momentum transfer following ultrafast laser excitation in ferrimagnetic gdfeco. Nature materials 12, 293–298 (2013).

    ADS  CAS  Article  Google Scholar 

  4. Radu, I. et al. Transient ferromagnetic-like state mediating ultrafast reversal of antiferromagnetically coupled spins. Nature 472, 205–208 (2011).

    ADS  CAS  Article  Google Scholar 

  5. Eschrig, M. Spin-polarized supercurrents for spintronics. Physics Today 64, 43–49 (2011).

    ADS  CAS  Article  Google Scholar 

  6. Robinson, J. W. A., Halász, G. B., Buzdin, A. I. & Blamire, M. G. Enhanced supercurrents in josephson junctions containing nonparallel ferromagnetic domains. Phys. Rev. Lett. 104, 207001 (2010).

    ADS  CAS  Article  Google Scholar 

  7. Bergeret, F. S., Volkov, A. F. & Efetov, K. B. Odd triplet superconductivity and related phenomena in superconductor-ferromagnet structures. Rev. Mod. Phys. 77, 1321–1373 (2005).

    ADS  CAS  Article  Google Scholar 

  8. Wang, X. L. et al. Giant triplet proximity effect in superconducting pseudo spin valves with enigneered anisotropy. Phys. Rev. B 89, 140508 (2014).

    ADS  Article  Google Scholar 

  9. Camley, R. E. & Tilley, D. R. Phase transitions in magnetic superlattices. Phys. Rev. B 37, 3413–3421 (1988).

    ADS  CAS  Article  Google Scholar 

  10. Camley, R. E. Properties of magnetic superlattices with antiferromagnetic interfacial coupling: Magnetization, susceptibility, and compensation points. Phys. Rev. B 39, 12316–12319 (1989).

    ADS  CAS  Article  Google Scholar 

  11. Baczewski, L., Kalinowski, R. & Wawro, A. Magnetization and anisotropy in fe/gd multilayers. J. Magn. Magn. Mater. 177–181, Part 2, 1305–1307 (1998). International Conference on Magnetism (Part II).

    ADS  Article  Google Scholar 

  12. Barth, A. et al. Magnetic coupling in Gd/Ni bilayers. J. Phys.: Condens. Matter 20, 395232 (2008).

    ADS  Google Scholar 

  13. Camley, R. E. Surface spin reorientation in thin gd films on fe in an applied magnetic field. Phys. Rev. B 35, 3608–3611 (1987).

    ADS  CAS  Article  Google Scholar 

  14. Prieto, J. L., Blamire, M. G. & Evetts, J. E. Magnetoresistance in a constricted domain wall. Phys. Rev. Lett. 90, 027201 (2003).

    ADS  Article  Google Scholar 

  15. McGrath, O. F. K. et al. Observation and interpretation of a partial gd twisted spin state in an epitaxial gd/fe bilayer. Phys. Rev. B 54, 6088–6091 (1996).

    ADS  CAS  Article  Google Scholar 

  16. Takanashi, K., Kamiguchi, Y., Fujimori, H. & Motokawa, M. Magnetization and magnetoresistance of fe/gd ferrimagnetic multilayer films. J. Phys. Soc. Jpn. 61, 3721–3731 (1992).

    ADS  CAS  Article  Google Scholar 

  17. Koizumi, A., Takagaki, M., Suzuki, M., Kawamura, N. & Sakai, N. Anomalous magnetic hysteresis of gd and fe moments in a gd/fe multilayer measured by hard x-ray magnetic circular dichroism. Phys. Rev. B 61, R14909–R14912 (2000).

    ADS  CAS  Article  Google Scholar 

  18. Robinson, J. W. A., Chiodi, F., Egilmez, M., Halász, G. B. & Blamire, M. G. Supercurrent enhancement in bloch domain walls. Sci. Rep. 2, 699 (2012).

    ADS  CAS  Article  Google Scholar 

  19. Mauri, D., Siegmann, H. C., Bagus, P. S. & Kay, E. Simple model for thin ferromagnetic films exchange coupled to an antiferromagnetic substrate. J. Appl. Phys. 62, 3047–3049 (1987).

    ADS  Article  Google Scholar 

  20. Huber, M. E. et al. Gradiometric micro-squid susceptometer for scanning measurements of mesoscopic samples. Rev. Sci. Instrum. 79, 053704 (2008).

    ADS  Article  Google Scholar 

  21. Linder, J. & Robinson, J. W. Superconducting spintronics. Nature Physics 11, 307–315 (2015).

    ADS  CAS  Article  Google Scholar 

  22. Bergeret, F. S., Volkov, A. F. & Efetov, K. B. Josephson current in superconductor-ferromagnet structures with a nonhomogeneous magnetization. Phys. Rev. B 64, 134506 (2001).

    ADS  Article  Google Scholar 

  23. Volkov, A. F., Bergeret, F. S. & Efetov, K. B. Odd triplet superconductivity in superconductor-ferromagnet multilayered structures. Phys. Rev. Lett. 90, 117006 (2003).

    ADS  CAS  Article  Google Scholar 

  24. Houzet, M. & Buzdin, A. I. Long range triplet josephson effect through a ferromagnetic trilayer. Phys. Rev. B 76, 060504 (2007).

    ADS  Article  Google Scholar 

Download references


T.D.C.H. and J.W.A.R. acknowledge funding from the EPSRC [EP/I038047/1], the EPSRC Programme grant “Superconducting Spintronics” [EP/N017242/1] and the Leverhulme Trust [IN-2013-033]. S.B. acknowledges support from the Knut and Alice Wallenberg Foundation. X.L.W. and J.H.Z. acknowledge support from the MOST of China [2015CB921500]. Research at SLAC and Stanford was supported through the Stanford Institute for Materials and Energy Sciences (SIMES) which like the SSRL user facility and the scanning SQUID microscopy is funded by the Office of Basic Energy Sciences of the U.S. Department of Energy.

Author information

Authors and Affiliations



J.W.A.R. conceived the experiment and supervised the project. The X-ray magnetic circular dichroism (XMCD) experiments were performed by T.D.C.H., H.O. and S.B. Local scanning superconducting quantum interference (scanning SQUID) measurements were undertaken by A.R.J. and K.A.M. Bulk magnetic measurements were performed using a Quantum Design MPMS SQUID Magnetometer by X.L.W. and J.H.Z. The XMCD data was jointly analysed by T.D.C.H., J.W.A.R., N.B., S.B. and H.O. The manuscript was written by T.D.C.H. along with J.W.A.R., and all authors commented on the manuscript.

Corresponding author

Correspondence to J. W. A. Robinson.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Higgs, T., Bonetti, S., Ohldag, H. et al. Magnetic coupling at rare earth ferromagnet/transition metal ferromagnet interfaces: A comprehensive study of Gd/Ni. Sci Rep 6, 30092 (2016).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing