Abstract
We demonstrate multilevel data storage in organic ferroelectric resistive memory diodes consisting of a phase-separated blend of P(VDF-TrFE) and a semiconducting polymer. The dynamic behaviour of the organic ferroelectric memory diode can be described in terms of the inhomogeneous field mechanism (IFM) model where the ferroelectric components are regarded as an assembly of randomly distributed regions with independent polarisation kinetics governed by a time-dependent local field. This allows us to write and non-destructively read stable multilevel polarisation states in the organic memory diode using controlled programming pulses. The resulting 2-bit data storage per memory element doubles the storage density of the organic ferroelectric resistive memory diode without increasing its technological complexity, thus reducing the cost per bit.
Similar content being viewed by others
Introduction
There is currently significant research interest in resistive polymer switching driven by the desire for non-volatile, reprogrammable memory for ubiquitous, low-cost computing systems. Ferroelectric polymers such as poly(vinylidene fluoride) (PVDF) and its copolymers with trifluoroethylene (TrFE), P(VDF-TrFE), can be switched by an external electric field between two polarisation states with a relatively large remanent polarisation of 0.05–0.1 C/m2. Many groups have studied the ferroelectric properties of these materials in thin-film capacitors1,2,3,4,5,6,7 and transistors8,9,10,11,12,13,14,15 for memory applications. In 2008, Asadi et al. used phase-separated blends of P(VDF-TrFE) and semiconducting polymers to realise a bistable resistive memory diode16,17,18. In this diode, the semiconducting polymer forms a resistive pathway from one electrode to the other that can be modulated via the ferroelectric polarisation of P(VDF-TrFE). This diode combines the appealing features of P(VDF-TrFE) with those of a memory diode (i.e., rectification and non-destructive resistive readout), thereby enabling simple yet high-density crossbar array integration16,17,18,19,20. Recently, a 32 × 32 crossbar array has been fabricated using these bi-stable diodes21. In this 1-kb array, each crossing of electrode lines defines a memory cell that can store a single bit of information.
The inherent problem with low-cost processing is the resulting relatively low areal density. This drawback can be partially mitigated by exploiting the fact that ferroelectric materials generally offer the capability of partial switching, enabling the storage of multiple bits per memory element22,23,24. However, multilevel data storage generally requires either complex addressing methods, in the form of voltage or current modulation, or additional complex processing steps13,22,23,24. This study presents a novel multi-bit scheme that allows for non-destructive readout and simple pulsed writing; this is made possible via a thorough characterisation of the dynamic response. The switching time depends exponentially on the applied electric field, and the coercive fields are found to depend on the polarising time. We demonstrate that the ferroelectric response is primarily controlled by a statistical distribution of the local electric field rather than by a temporal law of local polarisation switching, i.e., the electric-field dependence can be explained in terms of the inhomogeneous field mechanism (IFM) model that has been established for a wide range of disordered ferroelectrics24,25,26. These insights introduce the possibility of multilevel polarisation (MLP) states, which are demonstrated in the diodes investigated in this study. Four stable polarisation states can be programmed and read out repeatedly in a single memory diode. The resulting 2-bit data storage per memory element doubles the storage density of the organic ferroelectric resistive memory diode without increasing its technological complexity, thus reducing the cost per bit.
Results & Discussion
Figure 1a schematically illustrates the structure of our organic ferroelectric resistive memory device and the materials used. Poly(9,9-di-n-octylfluorene-alt-benzothiadiazole), F8BT, is an ambipolar semiconductor whose charge transport has been well characterised in diodes and transistors27,28,29. P(VDF-TrFE) is a wide band-gap insulator, and its ferroelectric properties have been well described1,2,3,4,5,6,30,31,32,33. A 1:9 (w/w) polymer blend solution of F8BT and P(VDF-TrFE) was spin coated onto glass substrates with patterned Mo/MoO3 electrodes; these substrates were subsequently annealed at 135 °C for 1 hour to enhance the crystallinity of the ferroelectric phase. For more processing details, see the Experimental section and previously published works16,17,18,19,20. Figure 1b presents an AFM topography image of a 200-nm-thick continuous film. Circular domains of F8BT with diameters of 200–600 nm are surrounded by a P(VDF-TrFE) matrix. Similar phase-separated morphologies have been reported by several groups20,34,35,36. In these studies, a wide range of different polymers and small-molecule semiconductors have been used, illustrating that this type of lateral phase-separated morphology, which is key to device operation, is not specific to any one type of semiconductor7,36. When such a thin film is sandwiched between two metal electrodes, the transport of charge carriers is possible via the semiconducting phase. The work function(s) of the metal contact(s) is (are) purposely chosen to yield substantial injection barrier(s) into the semiconductor. F8BT forms a (hole) injection barrier of ~0.3 eV with Mo/MoO3 if the work function for MoO3 is taken to be ~5.6 eV and the HOMO level of F8BT is taken to be 5.9 eV26,30,31. The work function of the other Ba/Al electrode (2.8 eV) matches the LUMO energy of F8BT (3.3 eV); an ohmic contact for electron injection is thus expected21. When the ferroelectric material is polarised in the correct direction, the polarisation field of the ferroelectric material lowers the injection barrier at the semiconductor-metal interface, and a higher device current is observed7,34; however, when the ferroelectric material is poled in the other direction, the current is low. A bi-stable resistive switch is thus obtained. A representative quasi-static current versus voltage hysteretic sweep of the ferroelectric memory diodes is presented in Fig. 1c. In the forward voltage scan, the electron (i.e., minority) current is low despite the ohmic contact, whereas the hole (i.e., majority) current is initially limited by the Schottky barrier between MoO3 and F8BT, and thus, a relatively low current of 0.52 nA at 5 V is measured. When the applied voltage exceeds the coercive electric field of the ferroelectric P(VDF-TrFE) layer, the injection barrier of MoO3/Mo is lowered, and the hole current is significantly increased; the current then reads 0.24 μA at 5 V. Thus, the current ratio for the two polarisation states is ~450, which is sufficiently large for crossbar integration.
(a) Chemical structures of F8BT (red) and P(VDF-TrFE) (blue) and a schematic illustration of a polymer ferroelectric resistive memory cell; (b) AFM topological image of a P(VDF-TrFE):F8BT (9:1 (w/w)) blended film on an MoO3/Mo electrode, and (c) static I-V characteristics and (d) dynamic characteristics of the ferroelectric memory diodes. The colour scale indicates the device ON current measured at 5 V after switching pulses of different pulse widths (i.e., times) and pulse heights (i.e., voltages).
To enable controlled partial switching, additional knowledge of the switching kinetics is required. To accomplish this goal, pulsed switching studies were performed (Fig. 1d), during which the duration and magnitude of the programming pulse were varied. Before each programming pulse, the memory was reset to the OFF state by applying a negative pulse of −20 V for 50 ms. Figure 1d presents the results obtained when switching the memory from the OFF to the ON state. The memory remained in the OFF state when short pulses of insufficient amplitude were applied. For large pulses of 20 V, switching to the ON state occurred within 0.2 ms, whereas for lower voltages (i.e., ~14 V), the switching time was near 10 ms. Such a strong electric-field dependence has been previously reported for P(VDF-TrFE) capacitors3,4,5.
Figure 2a presents the measured currents as functions of the applied field for both the ON-to-OFF transition and the OFF-to-ON transition. The ON-to-OFF transient arises at slightly lower electric fields (i.e., is ‘faster’) than the OFF-to-ON switching transient. We note that symmetric behaviour is not expected a priori, as this would imply a nearly linear relationship between the actual device current and the remanent polarisation. Figure 2b displays the derivative of the memory current vs. the electric field (i.e., ΔI/ΔE) for the OFF-to-ON transition as a function of the applied field for various pulse durations. If the switching time is defined as the time at which ΔI/ΔE peaks, then the switching times can be fit using the following empirical formula37:
(a) Measured currents of the ferroelectric memory diode at 5 V after switching from OFF to ON (i.e., curves starting low) or ON to OFF (i.e., curves starting high) vs. the applied electric field at various pulse widths. (b) Scaled derivatives versus the applied field at various pulse widths. (c) Normalised curves of (b) on an appropriately scaled electric-field axis at the maximum position, Emax (t). (d) Currents through the organic ferroelectric memory diode after switching from OFF to ON vs. the programming pulse time under various applied fields. The scattered points were measured at 5 V after programming, and the solid lines represent fits to the IFM model. (e) Normalised logarithmic derivative curves versus pulse widths at a fixed programming voltage of 18.5 V (Ec = 0.93 MV/cm), where the solid line represents the fitted master curve. (f) Device currents attributable to the cumulative effect of successive programming pulses (OFF to ON) at a constant electric field value (Ec = 0.93 MV/cm).
![](http://media.springernature.com/lw182/springer-static/image/art%3A10.1038%2Fsrep24407/MediaObjects/41598_2016_Article_BFsrep24407_Equ1_HTML.gif)
where τ0 is the characteristic time parameter and Ea is the activation field. The obtained fit values were τ0 = ~6.7 ns and Ea = 11.37 (±0.32) MV/cm (please refer to Figure S3 in the Supporting Information for more information). The extracted value of Ea of 11.37 (±0.32) MV/cm is comparable to the value of ~10 MV/cm that has been previously measured in P(VDF-TrFE) capacitors24, indicating that the field dependence in both types of memory devices is similar. The longer switching times measured for our devices are related to the exponential pre-factor. The τ0 value of ~6.7 ns in the diodes is somewhat larger than the previously reported value of ~1 ns in the capacitor structure26. Typically, the τ0 parameter is associated with the accumulation of screening charges at the interfaces between non-ferroelectric and ferroelectric layers. Hence, a larger τ0 value suggests that charge carriers flow via the non-ferroelectric regions of the film (e.g., the amorphous phase of the grain boundaries in the P(VDF-TrFE) matrix or the polymer semiconductor pillars interfacing with the P(VDF-TrFE) matrix) and form an interfacial charge layer at the phase boundaries26.
Strikingly, all ΔI/ΔE curves display a similar shape, with a characteristic width and height. This observation can be explained by the IFM model24,25,26. In this model, a ferroelectric material is considered to consist of randomly distributed regions with independent polarisation kinetics governed by a switching-time-dependent local field. In other words, the time-dependent local field depends on the domains that have and have not switched before. Therefore, if the kinetic process is deterministic, the various domains will always switch in the same order, and their transients can be expected to exhibit a universality that can be expressed as a master curve. Indeed, the properties of the derivatives presented in Fig. 2b allow us to extract such a master curve through the Gaussian fitting of the normalised data points, as shown in Fig. 2c. Details regarding the extraction of the IFM master curve are provided in the Supporting Information.
Until recently, the applications of this new type of device have been restricted to only the two saturated values. In principle, it is possible to obtain an intermediate current between the saturated values by adjusting the ratio of upward to downward polarisation. However, the achievement of an intermediate state with the desired polarisation value is challenging because of the stochastic and complex nature of ferroelectric polarisation switching and possible depolarisation effects. Our devices, however, can be well described in the framework of the IFM model, and hence, we attempted to store multiple bits in a single memory cell by polarising only certain ferroelectric regions instead of all of them13,22,24. Figure 2d presents the transient current curves as a function of the switching pulse time, where the scattered points represent measured data and the lines represent fits to the IFM model. The shape of the fitted transient curve vs. the logarithm of the switching pulse time is similar to that of the transient current curves vs. the electric field, as observed in Fig. 2a. This observation suggests that it may be informative to differentiate the fitted transient curves with respect to the logarithm of the pulse time; the resulting Gaussian distribution is presented in Fig. 2e. The kinetics of the independent local polarisation in P(VDF-TrFE) ferroelectrics follow a stretched exponential dependence on the switching pulse time24,25. Therefore, conceptually, partial polarisation in a ferroelectric matrix can be modulated by adjusting both the switching time and the electric field. Figure 2f illustrates the feasibility of pulse-modulated multilevel data storage in organic ferroelectric memory, where intermediate current states can be reliably programmed. The curves highlight that adjustments to the switching time and electric field are, to a large degree, interchangeable, as the same state can be achieved in multiple ways.
For the actual demonstration of 2-bit data storage in an organic ferroelectric diode cell, we selected two intermediate states with programming times of 0.2 ms and 1 ms in addition to the complete OFF and complete ON states, each of which had a programming time of 50 ms (see Figure S4 in the Supporting Information). The measured currents at 5 V after programming pulses of different durations and equal electric field strength took on discrete values for corresponding pulse durations. Furthermore, the readout current after a number of successive programming pulses was less than that after a single pulse of the corresponding cumulative duration because the memory current is exponentially related to the pulse duration.
The memory reliability of pulse-modulated multilevel data storage in the organic ferroelectric memory switch was examined in terms of both time-dependent data retention and endurance over multiple instances of data programming/erasing. Data retention was evaluated by independently measuring four data storage levels controlled by different pulse-switching times at a fixed programming voltage of 18.5 V (Ec = 0.93 MV/cm). Figure 3a reveals reasonably reliable data retention of all four states for up to approximately 103 s. It should be noted that the charge retention of this multilevel ferroelectric memory device is relatively short, which may be attributable to the partial depolarisation of ferroelectric components interfacing with semiconducting polymer pillars; this behaviour is significantly different from that of capacitance-type organic ferroelectric memory, and thus, further improvements should be sought to increase the retention time, including the optimisation of semiconducting components and/or a more careful selection of electrodes. However, it is notable that the retention of the intermediate states is comparable to or even better than that of the normal operation mode (cf. the upper ‘ON’ curve). Next, for measurements of endurance under multiple data-writing cycles, we consecutively erased/wrote each of the four levels of data storage (i.e., ‘00,’ ‘01’, ‘10’, and ‘11’ states) and read the current after n iterations of this programmed endurance cycle (n = 1, 2, 5, 10, … 500, 1000). Very consistent and reliable rewritability of all four levels was observed for over 1000 cycles, as shown in Fig. 3b. The results indicate that the degree of ferroelectric polymer domain switching was precisely controlled and remained unchanged when a proper combination of pulse duration and voltage was repeatedly applied.
Finally, to demonstrate the feasibility of doubling the information density of a real memory device using pulse-modulated MLP states, we tested a simple 1 × 4 organic ferroelectric crossbar memory diode array, wherein the word line (WL) was common and the bit line (BL) was separated (Fig. 4a). To write an example state of ‘11010010’ into the 1 × 4 crossbar memory array, different programming pulse widths of 50 ms, 0.2 ms, 0 ms, and 1 ms at a fixed programming voltage of 18.5 V, corresponding to ‘11’, ‘01’, ‘00’, and ‘10’, respectively, were sequentially applied to each bit line. Then, in the same sequence in which the data were written, a fixed current-measuring voltage of 5 V was applied to non-destructively read the stored multilevel data. Figure 4b clearly reveals that discrete and distinct current levels corresponding to the specific pulse widths in each memory cell could be read out. In a similar manner, we wrote and read the 8-bit state ‘00100111’ into the 1 × 4 crossbar memory array, as shown in Fig. 4c. Both examples successfully demonstrated that the memory density of the simple organic ferroelectric crossbar memory diode array could be reliably doubled by the controlled programming pulse width, as intended.
Conclusion
In summary, we demonstrated the capability of pulse-modulated multilevel data storage in organic ferroelectric resistive memory diodes. The principle can be understood based on an investigation of the dynamic operating principles of the organic memory device. The dynamic switching mechanism of our organic resistive memory can be explained by the IFM model, in which the ferroelectric components are regarded as an assembly of randomly distributed regions with independent polarisation kinetics governed by a time-dependent local field. Therefore, we could reliably partially polarise the ferroelectric material using tuned programming pulses to achieve 2-bit data storage in a single organic ferroelectric diode cell with stable retention and endurance. We believe that these findings lay the foundations for organic ferroelectric memory devices that offer higher storage density without increased technological complexity.
Methods
For device fabrication, the bottom anode layers were initially formed on glass substrates through the e-beam evaporation of Mo, the subsequent deposition of MoO3, and finally, patterning using standard photolithography. Next, a 200-nm-thick continuous film of a 1:9 (w/w) blend of F8BT and P(VDF-TrFE), with 77 mol% VDF, was spun in an initially homogeneous evaporative solution, followed by thermal annealing at 135 °C for 1 hour to facilitate the growth of the ferroelectric ß phase. The decomposition of the mixed polymer gave rise to a dispersed phase consisting of pillar-like semiconductor domains embedded in a ferroelectric matrix. The Ba/Al top cathodes were evaporated through a shadow mask, and finally, the devices were encapsulated with a conformable SiNx barrier layer to avoid charge trapping at the interfaces between the electrodes and the polymer semiconductors, which can affect the multilevel resistive switching phenomenon. A schematic illustration of this organic ferroelectric resistive memory device is presented in Fig. 1a. A commercial AFM system (Veeco MultiMode NS-IIIA) with Al-coated Si tips (Nanosensors, spring constant k = 12.5 N/m) was used to characterise the blend structure at the nanoscale. Electrical measurements were performed at room temperature in ambient conditions using an Agilent 33120A function generator (i.e., the source) in combination with an external voltage amplifier, a Keithley 6485 picoammeter (i.e., the sensor), and two Keithley 2612A source meters controlled by a homebuilt “FerrOrgan” switching box.
Additional Information
How to cite this article: Lee, J. et al. Pulse-modulated multilevel data storage in an organic ferroelectric resistive memory diode. Sci. Rep. 6, 24407; doi: 10.1038/srep24407 (2016).
References
Lovinger, A. J. Ferroelectric polymers. Science 220(4602), 1115–1121 (1983).
Horiuchi, S. & Tokura, Y. Organic ferroelectrics. Nat Mater 7(5), 357–366 (2008).
Furukawa, T., Nakajima, T. & Takahashi, Y. Factors governing ferroelectric switching characteristics of thin VDF/TrFE copolymer films. IEEE T Dielect El In 13(5), 1120–1131 (2006).
Jung, H. J. et al. Shear-induced ordering of ferroelectric crystals in spin-coated thin poly (vinylidene fluoride-co-trifluoroethylene) films. Macromolecules 42(12), 4148–4154 (2009).
Ling, Q. D. et al. Polymer electronic memories: Materials, devices and mechanisms. Prog Polym Sci 33(10), 917–978 (2008).
Ng, T. N. et al. Scalable printed electronics: an organic decoder addressing ferroelectric non-volatile memory. Sci. Rep. 2, 585, doi: 10.1038/srep00585 (2012).
Kemerink, M., Asadi, K., Blom, P. W. & de Leeuw, D. M. The operational mechanism of ferroelectric-driven organic resistive switches. Org electron 13(1), 147–152 (2012).
Naber, R. C. et al. High-performance solution-processed polymer ferroelectric field-effect transistors. Nat Mater 4(3), 243–248 (2005).
Naber, R. C. et al. An Organic Field‐Effect Transistor with Programmable Polarity. Adv Mater 17(22), 2692–2695 (2005).
Sekitani, T. et al. Organic nonvolatile memory transistors for flexible sensor arrays. Science 326(5959), 1516–1519 (2009).
Lee, K. H. et al. High‐Mobility Nonvolatile Memory Thin‐Film Transistors with a Ferroelectric Polymer Interfacing ZnO and Pentacene Channels. Adv Mater 21(42), 4287–4291 (2009).
Kang, S. J. et al. Non‐volatile Ferroelectric Poly (vinylidene fluoride‐co‐trifluoroethylene) Memory Based on a Single‐Crystalline Tri‐isopropylsilylethynyl Pentacene Field‐Effect Transistor. Adv Funct Mater 19(10), 1609–1616 (2009).
Hwang, S. K., Bae, I., Kim, R. H. & Park, C. Flexible Non‐Volatile Ferroelectric Polymer Memory with Gate‐Controlled Multilevel Operation. Adv Mater 24(44), 5910–5914 (2012).
Baeg, K. J. et al. High‐Performance Top‐Gated Organic Field‐Effect Transistor Memory using Electrets for Monolithic Printed Flexible NAND Flash Memory. Adv Funct Mater 22(14), 2915–2926 (2012).
Kim, R. H. et al. Non-volatile organic memory with sub-millimetre bending radius. Nat Comm 5 (2014).
Asadi, K., De Leeuw, D. M., De Boer, B. & Blom, P. W. Organic non-volatile memories from ferroelectric phase-separated blends. Nat Mater 7(7), 547–550 (2008).
Asadi, K., de Boer, T. G., Blom, P. W. & de Leeuw, D. M. Tunable Injection Barrier in Organic Resistive Switches Based on Phase‐Separated Ferroelectric–Semiconductor Blends. Adv Funct Mater 19(19), 3173–3178 (2009).
Asadi, K., Li, M., Stingelin, N., Blom, P. W. & de Leeuw, D. M. Crossbar memory array of organic bistable rectifying diodes for nonvolatile data storage. Appl Phys Lett. 97(19), 193308 (2010).
Naber, R. C., Asadi, K., Blom, P. W., de Leeuw, D. M. & de Boer, B. Organic nonvolatile memory devices based on ferroelectricity. Adv. Mater 22(9), 933–945 (2010).
Khan, M. A. et al. High‐Performance Ferroelectric Memory Based on Phase‐Separated Films of Polymer Blends. Adv Funct Mater 24(10), 1372–1381 (2014).
van Breemen, A. J. et al. Crossbar arrays of nonvolatile, rewritable polymer ferroelectric diode memories on plastic substrates. Appl Phys Express 7(3), 031602 (2014).
Lee, D. et al. Multilevel data storage memory using deterministic polarization control. Adv Mater 24(3), 402–406 (2012).
Khikhlovskyi, V. et al. Multi-bit organic ferroelectric memory. Org electron 14(12), 3399–3405 (2013).
Genenko, Y. A. et al. H. Universal polarization switching behavior of disordered ferroelectrics. Adv Funct Mater 22(10), 2058–2066 (2012).
Zhukov, S. et al. Dynamics of polarization reversal in virgin and fatigued ferroelectric ceramics by inhomogeneous field mechanism. Phys Rev B 82(1), 014109 (2010).
Schütrumpf, J., Zhukov, S., Genenko, Y. A. & Von Seggern, H. Polarization switching dynamics by inhomogeneous field mechanism in ferroelectric polymers. J Phys D Appl Phys 45(16), 165301 (2012).
He, Y., Gong, S., Hattori, R. & Kanicki, J. High performance organic polymer light-emitting heterostructure devices. Appl Phys Lett, 74(16), 2265–2267 (1999).
Chua, L. L. et al. General observation of n-type field-effect behaviour in organic semiconductors. Nature 434(7030), 194–199 (2005).
Zaumseil, J., Donley, C. L., Kim, J. S., Friend, R. H. & Sirringhaus, H. Efficient Top‐Gate, Ambipolar, Light‐Emitting Field‐Effect Transistors Based on a Green‐Light‐Emitting Polyfluorene. Adv Mater 18(20), 2708–2712 (2006).
Legrand, J. F. Structure and ferroelectric properties of P (VDF-TrFE) copolymers. Ferroelectrics 91(1), 303–317 (1989).
Ducharme, S. et al. Intrinsic ferroelectric coercive field. Phys Rev Lett. 84(1), 175 (2000).
Greiner, M. T. et al. Universal energy-level alignment of molecules on metal oxides. Nat Mater 11(1), 76–81 (2012).
Meyer, J. et al. Transition metal oxides for organic electronics: energetics, device physics and applications. Adv Mater 24(40), 5408–5427 (2012).
Asadi, K. et al. Spinodal decomposition of blends of semiconducting and ferroelectric polymers. Adv Funct Mater 21(10), 1887–1894 (2011).
Michels, J. J., van Breemen, A. J., Usman, K. & Gelinck, G. H. Liquid phase demixing in ferroelectric/semiconducting polymer blends: An experimental and theoretical study. J Polym Sci Polym Phys 49(17), 1255–1262 (2011).
Khikhlovskyi, V. et al. Nanoscale organic ferroelectric resistive switches. J Phys Chem C 118(6), 3305–3312 (2014).
Merz, W. J. Domain Formation and Domain Wall Motions in Ferroelectric BaTiO3 Single Crystals. Phys Rev 95(3), 690 (1954).
Acknowledgements
This work was supported by a Research Grant of Pukyong National University in 2015 (CD20151148).
Author information
Authors and Affiliations
Contributions
J.L., A.B. and G.G. conceived the initial idea and designed the experiments. J.L. and V.K. fabricated the devices and performed measurements, J.L., A.B., G.G. and R.J. and analyzed the data. J.L., G.G. and M.K. wrote this article. All authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Lee, J., van Breemen, A., Khikhlovskyi, V. et al. Pulse-modulated multilevel data storage in an organic ferroelectric resistive memory diode. Sci Rep 6, 24407 (2016). https://doi.org/10.1038/srep24407
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep24407
This article is cited by
-
Interfacial preparation of ferroelectric polymer nanostructures for electronic applications
Polymer Journal (2021)
-
Local ferroelectric studies on interconnected PVDF nano-dot thin films using piezo force microscopy
Journal of Materials Science: Materials in Electronics (2019)
-
High-voltage transition studies from rectification to resistive switching in Ag/PVDF/Au capacitor-like structures
Polymer Bulletin (2018)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.