Outstanding supercapacitive properties of Mn-doped TiO2 micro/nanostructure porous film prepared by anodization method

Scientific Reports volume 6, Article number: 22634 (2016) | Download Citation

Abstract

Mn-doped TiO2 micro/nanostructure porous film was prepared by anodizing a Ti-Mn alloy. The film annealed at 300 °C yields the highest areal capacitance of 1451.3 mF/cm2 at a current density of 3 mA/cm2 when used as a high-performance supercapacitor electrode. Areal capacitance retention is 63.7% when the current density increases from 3 to 20 mA/cm2, and the capacitance retention is 88.1% after 5,000 cycles. The superior areal capacitance of the porous film is derived from the brush-like metal substrate, which could greatly increase the contact area, improve the charge transport ability at the oxide layer/metal substrate interface, and thereby significantly enhance the electrochemical activities toward high performance energy storage. Additionally, the effects of manganese content and specific surface area of the porous film on the supercapacitive performance were also investigated in this work.

Introduction

Supercapacitors, as electrical energy storage devices (generally called electrochemical capacitors) have attracted much attention owing to their longer cycle life, more rapid charging/discharging rates, and higher power, compared with conventional dielectric capacitors and batteries1,2,3,4. Such outstanding performance largely satisfies the higher requirements of practical applications in portable electronics, hybrid electric vehicles, and large industrial equipments, etc.5,6. The electrode material is a crucial factor affecting the performance of a supercapacitor7. Active electrode materials are mainly categorised into three types: carbon materials, conductive polymer materials, and transition metal oxides8,9. Transition metal oxides are of great interest nowadays due to their higher energy density and better reliability compared with others10.

Among the frequently-used transition metal oxides, manganese oxide is generally considered as one of the most promising candidates due to its high theoretical capacitance derived from reversible oxidation state changes during charging/discharging process11,12,13,14. However, it suffers from shortcomings of low specific surface area15, poor electrical conductivity14, and easy dissolution16,17, etc. To overcome these problems, efforts have been focused on further improvement of its capacitive properties by combining MnO2 with carbon18, TiO219,20, Co3O421, ZnO22,23, Fe2O324, etc.

TiO2 is an important semiconductor material with good chemical stability, low cost, low toxicity, and environmentally friendly nature25,26. Whereas, when TiO2 is used as electrode material alone, its capacitance is relatively low, and compositing TiO2 with manganese oxides could considerably improve its capacitive performance. For example, the composite of TiO2 and MnO displays significantly higher capacity than that of TiO227; the TiO2@MnO2 nanobelts and the Mn-doped TiO2 nanosheet-based spheres exhibits superior rate capability and outstanding cycling performance28,29.

Fabrication approaches of the composites affect their capacitance performance significantly. For instance, the hybrid electrode material, prepared through depositing MnO2 onto TiO2 nanotube arrays, obtains an areal capacitance of 213.2 mF/cm2,7,30,31,32,33. Whereas, such composite structure could not completely overcome the easily-dissolving disadvantage of MnO2. Mn-doped TiO2 nanotube arrays, prepared by anodizing of Ti-Mn alloys, could address that issue because manganese can be uniformly doped into the tubular structure, nonetheless, the Mn-doped nanotube arrays suffer from very small capacitance value34. In order to further improve the capacitance properties of composite oxide of manganese and titanium, in the present study, Mn-doped TiO2 micro/nanostructure porous film was prepared through anodizing a Ti-Mn alloy containing 10.0 wt% Mn under suitable conditions and superior capacitive properties with high areal capacitance of 1451.3 mF/cm2 and excellent cycling performance were achieved.

Results and Discussion

SEM images of the sample prepared through anodization of a Ti-Mn alloy in aqueous solution containing 0.25 wt% NH4F and 30 wt% ethylene glycol at 30 °C and 40 V for 3 h are shown in Fig. 1. The top view of the as-prepared sample displays a surface with criss-crossed gaps (Fig. 1a). The gaps extend from the surface to the alloy substrate, which divide the oxide into cylindrical structures at the micron-scale (Fig. 1b). Many fibrillar substances are left at the exposed surface of alloy substrate where cylindrical structures were peeled off (Fig. 1c), indicating that the oxide layer is closely connected to the substrate. Numerous nanopores were found on the surface of these cylindrical structures (Fig. 1d). In brief, under this condition, a type of micro/nanostructure porous film with micron-scale cylinders, whose surface is full of nanoporous structures, is obtained. This kind of micro/nanostructure porous film will be referred to as porous film hereinafter.

Figure 1: SEM images of the sample.
Figure 1

(a) top view, (b) cross-sectional view, (c) interface between the oxide layer and alloy substrate, (d) nanoporous structure at the cylinder surface.

Based on Fig. 1, formation mechanism of the micro/nanostructure porous film was proposed (Fig. 2). The microstructure of the alloy surface is irregular, thus, a non-uniform anodizing reaction and electrical breakdown occur at the early stage of anodization, which result in the formation of tiny gaps at the alloy surface (Fig. 2a). During the anodization process, the current density is as large as 100 mA/cm2. The larger curvature results in the higher charge density and faster reaction rate at the top of gaps (Fig. 2b, point A) than that at the side position (Fig. 2b, point B). Along with the increasing anodization time, the alloy surface becomes uneven due to the different reaction rates at the top and side of the gaps. Reactions at the top position lead to the formation of gaps, and reactions at the side position lead to the formation of nanoporous structures. Eventually, the porous film structure as shown in Fig. 2c is formed. On account of the faster reaction rate at point A than that at point B in Fig. 2b, there is unreacted metal (fibrillar substances as seen in Fig. 1c) inside the cylindrical structures after the reaction. The fibrillar substances are connected with the underneath metal and form the brush-like metal substrate (Fig. 2c).

Figure 2
Figure 2

Schematic formation mechanism of Mn-doped TiO2 micro/nanostructure porous film (a) formation of tiny gaps, (b) state of the reaction in the tiny gaps, (c) structure of the oxide film.

To study the crystal structure of the oxide film, XRD analyses were conducted (Fig. 3a). When the sample was annealed at 100 °C and 200 °C, only those diffraction peaks of the titanium substrate (PDF card 44–1294) were detected, indicating that the oxides are amorphous. When the sample was annealed at 300 °C, 400 °C, and 500 °C, rutile TiO2 (PDF card 78–1510) is obtained. At 300 °C, rutile TiO2 was newly detected with weak characteristic diffraction peaks, indicating the formation of a small amount of TiO2 microlite in the oxide film. When annealed at 400 °C and 500 °C, the crystallinity of rutile TiO2 is improved. No characteristic peaks of manganese oxide can be seen in Fig. 3a, indicating that elemental Mn is scattered in the TiO2 matrix. To study the elemental valence of the oxides, XPS measurement results are given in Fig. 3b. The characteristic peaks of Ti2p3/2 and Ti2p1/2 are located at about 458.5 eV and 464.0 eV, respectively, confirming that Ti element is in Ti4+ state2,35. The peaks of Mn2p3/2 and Mn2p1/2 appears at about 641.6 eV and 653.3 eV, indicating that Mn element is in its +4 oxidation state (Fig. 2c)10,36.

Figure 3
Figure 3

XRD patterns of Mn-doped TiO2 micro/nanostructure porous film annealed at different temperatures (a), XPS Ti2p and Mn2p spectra of the porous film (b).

The cyclic voltammetry (CV) curves of the porous film annealed under different temperatures ranging from 100 to 500 °C are shown in Fig. 4A. Along with the increasing annealing temperatures, the integrated area of the CV curves first increases and then decreases. The integrated area is maximised at 300 °C, and the area is minimised at 500 °C. The influence of annealing temperature is manifested in two ways: along with the increasing annealing temperature, on the one hand, improved atomic order degree and the formation of rutile TiO2 would lead to the enhanced conductivity and the increased utilisation rates of active materials, therefore, the capacitive value would increase accordingly2; on the other hand, mutual condensation reaction of hydroxyl groups would result in the reduced specific surface area37,38 and the decreased hydrophilicity, hence, the capacitive value would decrease accordingly. The two opposite effects of annealing temperatures on the capacitive properties result in that the highest capacitive value appears when the samples were annealed at 300 °C (Fig. 4A). Therefore, the porous film annealed at 300 °C is chosen for subsequent measurements.

Figure 4
Figure 4

CV curves of the porous film at different annealing temperatures (scan rate: 50 mV/s) (A) and scan rates (annealing temperature: 300 °C) (B); Areal capacitance as a function of current density (the inset shows the GCD curves at different current densities) (C) and cycling performance at a current density of 10 mA/cm2 over 5,000 cycles (D).

Figure 4B shows the CV curves of the porous film annealed at 300 °C under different scan rates. According to Fig. 4B, the areal capacitance is 188.2, 169.5, 108.0, and 71.5 mF/cm2 at scan rates of 5, 10, 50, and 100 mV/s, respectively. The galvanostatic charge-discharge (GCD) measurements and corresponding areal capacitance are shown in Fig. 4C. At a current density of 3 mA/cm2, the highest areal capacitance of 1451.3 mF/cm2 was obtained. The retention of capacitance is 85.3%, 76.7%, 67.2%, and 63.7% at current densities of 6, 10, 15, and 20 mA/cm2 respectively. The charge curve is nearly symmetrical to the discharge curves, and the corresponding IR drop is 0.03 V when the current density is 3 mA/cm2 (inset, Fig. 4C). Figure 4D shows the continuous GCD curves of porous film at a current density of 10 mA/cm2 over 5,000 cycles. The capacitance retention is 90.3% after 2,000 cycles, and 88.1% after 5,000 cycles.

From Fig. 4C, Mn-doped TiO2 porous film obtains the highest areal capacitance of 1451.3 mF/cm2 at a current density of 3 mA/cm2. For comparison, the recently reported areal capacitance values obtained from the composites of MnO2 and TiO2 at the same current density are summarised in Table 1. Moreover, the value is also higher than those previously reported areal capacitances at lower current densities. For example, the MnO2-TiN nanotube7 achieves its highest areal capacitance of 213.2 mF/cm2 at a current density of 0.25 mA/cm2 and TiO2@MnO2 nanowall arrays31 achieves their highest specific capacitance of 15.5 mF/cm2 at a current density of 0.01 mA/cm2.

Table 1: Areal capacitance (mF/cm2) of the composites of MnO2 and TiO2 as a function of the current density (I, mA/cm2).

In order to compare the properties of this porous film with that of the frequently studied nanotube arrays, by changing the experimental conditions, Mn-doped TiO2 nanotube arrays were prepared through anodizing the same Ti-Mn alloy in ethylene glycol electrolyte containing 0.25 wt% NH4F and 5 wt% H2O at 30 °C and 40 V for 3 h. The SEM images are shown in Fig. 5. The nanotube arrays have an outer diameter of about 110 nm, a wall thickness of about 20 nm and a length of about 3.5 μm. The CV curves of Mn-doped TiO2 nanotube arrays tested under same conditions are shown in Fig. 6. The calculated areal capacitances are 0.63, 0.32, 0.24, and 0.21 mF/cm2 at scan rates of 5, 10, 50, and 100 mV/s, respectively. According to Figs 4B and 6, the areal capacitance of the porous film is about 300 times higher than that of the Mn-doped TiO2 nanotube arrays.

Figure 5
Figure 5

SEM images of Mn-doped TiO2 nanotube arrays (a) cross-sectional view; (b) top view.

Figure 6: CV curves of Mn-doped TiO2 nanotube arrays at different scan rates (annealing temperature: 300 °C).
Figure 6

In order to study the reason why the porous film possesses such a high areal capacitance, manganese content and specific surface area of Mn-doped TiO2 porous film and Mn-doped TiO2 nanotube arrays were analyzed (Table 2). Results show that the specific surface area of the porous film and nanotube arrays is similar, while the manganese content differs a lot. Manganese content of porous film is about 2.25 times higher than that of nanotube arrays, which might be due to the different solubility of manganese oxide and titanium oxide in different electrolytes. The different manganese content would lead to different capacitance value, however, the fairly high capacitance value of porous film which is about 300 times of that of nanotube arrays could not be only ascribed to its nearly doubled manganese content.

Table 2: Manganese content, specific surface area (SSA) and capacitance of the samples.

Electrochemical impedance spectroscopy (EIS) analysis is an effective method of explaining the capacitance performance of materials. Impedance Nyquist plots and equivalent circuits of porous film and nanotube arrays are shown in Fig. 7. The simulation data, according to the equivalent circuits, matches the experimental data very well. The semicircular arc in the EIS plot is observed for porous film at high-frequency and is followed by a sloping line at low-frequency. A sloping line is also observed for the nanotube arrays, but they lack the corresponding semicircular arc. The difference in EIS results indicates that the electrochemical processes in porous film are controlled by a combination of ion diffusion and electrochemical reaction, and the electrochemical processes in nanotube arrays is mainly controlled by ion diffusion. According to the simulation results, the charge transfer resistance and diffusion resistance admittance coefficient (Y0) of porous film are 0.23 Ω/cm2 and 0.17 S•sec0.5/cm2, respectively. Whereas, for nanotube array film, the diffusion resistance admittance coefficient (Y0) is 0.00060 S•sec0.5/cm2. The diffusion resistance admittance coefficient of porous film is about 283.3 times of that of nanotube arrays. Consequently, small diffusion resistance might be the main reason for the high areal capacitance of porous film.

Figure 7: Impedance Nyquist plot of samples and the fitted results using a ZVIEW electrochemical software.
Figure 7

The diffusion resistance is closely related with the morphology and structure of the hybrid electrode. According to Figs 1 and 2, the brush-like alloy substrate of the porous film would greatly improve the contact area and conductive ability between oxide layer and the metal substrate, and therefore, significantly reduce the charge transfer resistance, increase the utilisation rate of the active materials and consequently result in the outstanding areal capacitance value. For nanotube arrays film (Fig. 5), only the tube bottom is connected with metal substrate and the charge transfer resistance along with the nanotube wall is very large, resulting in the worse capacitance properties for the nanotube arrays in comparison with the porous film.

In summary, Mn-doped TiO2 micro/nanostructure porous film was successfully prepared by a simple anodization method. The annealing temperature exerts a significant influence on the capacitive performance of the porous film. The film annealed at 300 °C yields the highest areal capacitance of 1451.3 mF/cm2 at a current density of 3 mA/cm2. Areal capacitance retention is 63.7% when the current density increases from 3 to 20 mA/cm2, and the capacitance retention is 88.1% after 5,000 cycles. The capacitance performance of porous film is much better than that of the nanotube arrays film. The enhanced capacitance properties of the porous film might be mainly ascribed to specific preparation method and unique morphology structure. The brush-like alloy substrate of the porous film would greatly improve the contact area and conductive ability between oxide layer and the metal substrate, and therefore, significantly reduce the charge transfer resistance and increase the utilisation rate of the active materials. Additionally, manganese content and specific surface area of porous film also have a certain influence on its performance.

Methods

Ti-Mn (Mn: 10.0 wt%) alloy prepared using a power metallurgical method was cut into 20 mm × 40 mm × 2 mm foils, and then polished with metallographic abrasive paper, and ultrasonically washed in twice-distilled water and ethanol before use. Anodization was performed using a program-controlled DC source (Dahua Coop., Beijing, China). The anodization set-up consisted of a two-electrode configuration with Ti-Mn alloy foil as the anodic electrode and platinum foil (30 mm × 50 mm × 0.1 mm) as the cathodic electrode. All anodization experiments were conducted in aqueous solution containing 0.25 wt% NH4F and 30 wt% ethylene glycol at 30 °C and 40 V for 3 h. After anodization, the samples were rinsed in deionised water, air-dried, and characterised.

Morphologies, structures, elemental valence state, manganese content, and specific surface area of the samples were investigated using a scanning electron microscope (SEM, Hitachi, S-4800), an X-ray diffractometer (XRD, Rigaku, D/MAX-2500), an X-ray photoelectron spectroscope (XPS, ULVAC-PHI, PHI-5000 VersaProbe), and an inductively coupled plasma optical emission spectrometer (ICP-OES, Leemon, Prodigy Xp), and specific surface area analyser (BET, Quantachrome Corportion, Autosorb Iq), respectively. The electrochemical properties of the samples were investigated by cyclic voltammetry (CV) and galvanostatic charge-discharge (GCD) testing using an electrochemical analyser (CH Instruments, Inc. USA, CHI660E). The electrochemical measurements were conducted in a standard three-electrode configuration comprising the sample as the working electrode, a platinum foil as the counter-electrode, a saturated calomel electrode (SCE) as the reference electrode, and 0.5 M Na2SO4 as the electrolyte. The analysis of the capacitive performance of each sample was based on the geometric area of the working electrode2,14. EIS measurements were tested in the range of frequencies from 0.01 Hz to 100 kHz at open potential and an alternating current (AC) voltage amplitude of 5 mV. Figure 8 shows the corresponding equivalent circuit model.

Figure 8: The corresponding equivalent circuit model.
Figure 8

Additional Information

How to cite this article: Ning, X. et al. Outstanding supercapacitive properties of Mn-doped TiO2 micro/nanostructure porous film prepared by anodization method. Sci. Rep. 6, 22634; doi: 10.1038/srep22634 (2016).

References

  1. 1.

    & Materials for electrochemical capacitors. Nat. Mater. 7, 845–854 (2008).

  2. 2.

    et al. Hydrogenated TiO2 nanotube arrays for supercapacitors. Nano Lett. 12, 1690–1696 (2012).

  3. 3.

    , & Influence of microstucture on the charge storage properties of chemically synthesized manganese dioxide. Chem. Mater. 14, 3946–3952 (2002).

  4. 4.

    et al. Crystalline MnO2 as possible alternatives to amorphous compounds in electrochemical supercapacitors. J. Electrochem. Soc. 153, A2171–A2180 (2006).

  5. 5.

    , , & Laser scribing of high-performance and flexible graphene-based electrochemical capacitors. Science 335, 1326–1330 (2012).

  6. 6.

    , , , & Printable thin film supercapacitors using single-walled carbon nanotubes. Nano Lett. 9, 1872–1876 (2009).

  7. 7.

    & Electrochemical flexible supercapacitor based on manganese dioxide-titanium nitride nanotube hybrid. Electrochim. Acta 120, 273–283 (2014).

  8. 8.

    et al. Fabrication of Ni(OH)2 coated ZnO array for high-rate pseudocapacitive energy storage. Electrochim. Acta 109, 252–255 (2013).

  9. 9.

    & Fabrication of nanoporous nickel oxide by de-zincification of Zn–Ni/(TiO2-nanotubes) for use in electrochemical supercapacitors. Electrochim. Acta 100, 133–139 (2013).

  10. 10.

    et al. High-capacitance MnO2 nanoflakes on preformed C/TiO2 shell/core nanowire arrays for electrochemical energy storage. Electrochim. Acta 120, 416–422 (2014).

  11. 11.

    , & Flexible Zn2SnO4/MnO2 core/shell nanocable-carbon microfiber hybrid composites for high-performance supercapacitor electrodes. Nano Lett. 11, 1215–1220 (2011).

  12. 12.

    , & Charge storage mechanism of MnO2 electrode used in aqueous electrochemical capacitor. Chem. Mater. 16, 3184–3190 (2004).

  13. 13.

    et al. Facile synthesis of large-area manganese oxide nanorod arrays as a high-performance electrochemical supercapacitor. Energy Environ. Sci. 4, 2915–2921 (2011).

  14. 14.

    et al. H-TiO2@MnO2//H-TiO2@C core-shell nanowires for high performance and flexible asymmetric supercapacitors. Adv. Mater. 25, 267–272 (2013).

  15. 15.

    et al. Multilayered films of cobalt oxyhydroxide nanowires/manganese oxide nanosheets for electrochemical capacitor. J. Power Sources 195, 680–683 (2010).

  16. 16.

    , , , & Investigation on capacity fading of aqueous MnO2·nH2O electrochemical capacitor. J. Power Sources 177, 660–664 (2008).

  17. 17.

    , , & Preparation and electrochemical characterization of cobalt-manganese oxide as electrode materials for electrochemical capacitors. J. Phys. Chem. Solids 69, 1733–1739 (2008).

  18. 18.

    et al. Manganese dioxide nanorod arrays on carbon fabric for flexible solid-state supercapacitors. J. Power Sources 239, 64–71 (2013).

  19. 19.

    et al. Engineering of three dimensional (3-D) diatom@TiO2@MnO2 composites with enhanced supercapacitor performance. Electrochim. Acta 190, 159–167 (2016).

  20. 20.

    et al. High-performance and renewable supercapacitors based on TiO2 nanotube array electrodes treated by an electrochemical doping approach. Electrochim. Acta 116, 129–136 (2014).

  21. 21.

    et al. Co3O4 nanowire@MnO2 ultrathin nanosheet Core/Shell Arrays: A new class of high-performance pseudocapacitive materials. Adv. Mater. 23, 2076–2081 (2011).

  22. 22.

    , , & Three-dimensional ZnO@MnO2 core@shell nanostructures for electrochemical energy storage. Chem. Commun. 49, 4456–4458 (2013).

  23. 23.

    et al. Facile electrochemical synthesis of ZnO/ZnS heterostructure nanorod arrays. J. Electrochem. Soc. 158, E84–E87 (2011).

  24. 24.

    , , & High-performance pseudocapacitor electrodes based on α-Fe2O3/MnO2 core–shell nanowire heterostructure arrays. The Journal of Physical Chemistry C 117, 15523–15531 (2013).

  25. 25.

    et al. Electrochemical doping of anatase TiO2 in organic electrolytes for high-performance supercapacitors and photocatalysts. J. Mater. Chem. A 2 (2014).

  26. 26.

    , , , & Titanium dioxide nanotube films for electrochemical supercapacitors: Biocompatibility and operation in an electrolyte based on a physiological fluid. J. Electrochem. Soc. 162, A5065–A5069 (2015).

  27. 27.

    et al. Enhancing the comprehensive electrochemical performance by compositing intercalation/deintercalation-type of TiO2 with conversion-type of MnO. J. Alloys Compd. 640, 15–22 (2015).

  28. 28.

    et al. Hierarchical TiO2 nanobelts@MnO2 ultrathin nanoflakes core–shell array electrode materials for supercapacitors. RSC Advances 3, 14413–14422 (2013).

  29. 29.

    et al. Mn-doped TiO2 nanosheet-based spheres as anode materials for lithium-ion batteries with high performance at elevated temperatures. ACS Appl. Mater. Interfaces 6, 7292–7300 (2014).

  30. 30.

    et al. Dramatically improved energy conversion and storage efficiencies by simultaneously enhancing charge transfer and creating active sites in MnOx/TiO2 nanotube composite electrodes. Nano Energy 20, 254–263 (2016).

  31. 31.

    & Hierarchically structured TiO2@MnO2 nanowall arrays as potential electrode material for high-performance supercapacitors. Int. J. Hydrogen Energy 39, 12201–12212 (2014).

  32. 32.

    & Enhanced electrochemical performance of manganese dioxide spheres deposited on a titanium dioxide nanotube arrays substrate. J. Power Sources 272, 866–879 (2014).

  33. 33.

    et al. Electrochemical properties of MnO2-deposited TiO2 nanotube arrays 3D composite electrode for supercapacitors. Int. J. Hydrogen Energy 40, 14331–14337 (2015).

  34. 34.

    , , , & Preparation and capacitance properties of Mn-doped TiO2 nanotube arrays by anodisation of Ti–Mn alloy. J. Alloys Compd. 658, 177–182 (2016).

  35. 35.

    et al. TiO2@C core–shell nanowires for high-performance and flexible solid-state supercapacitors. J. Mater. Chem. C 1, 225–229 (2013).

  36. 36.

    Some notes on XPS Mn2p and Ce3d spectra of MnOx-Ceria catalysts. Catal. Today 185, 319–321 (2012).

  37. 37.

    et al. Effect of calcination temperature on the activity and structure of MnOx/TiO2 adsorbent for Hg0 removal. Fuel Process. Technol. 135, 25–33 (2015).

  38. 38.

    , , & Effect of initial water content and calcination temperature on photocatalytic properties of TiO2 nanopowders synthesized by the sol–gel process. Ceram. Int. 41, 12788–12797 (2015).

Download references

Acknowledgements

This work is supported by National Natural Science Foundation of China (51272064 and 51401074), Key Basic Research Program of Hebei Province of China (No. 12965135D), Natural Science Foundation of Hebei Province of China (E2013202032), the Talent Training Project of Hebei Province (2013) and the Program for Changjiang Scholars and Innovative Research Team in University (IRT13060).

Author information

Affiliations

  1. School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300130, China

    • Xuewen Ning
    • , Xixin Wang
    • , Xiaofei Yu
    • , Jianling Zhao
    • , Mingli Wang
    •  & Haoran Li
  2. Nanoscience Technology Center, Department of Materials and Engineering, University of Central Florida, Orlando, Florida 32826, US

    • Yang Yang

Authors

  1. Search for Xuewen Ning in:

  2. Search for Xixin Wang in:

  3. Search for Xiaofei Yu in:

  4. Search for Jianling Zhao in:

  5. Search for Mingli Wang in:

  6. Search for Haoran Li in:

  7. Search for Yang Yang in:

Contributions

X.W.N., X.X.W. and X.F.Y. fabricated the samples, analysed the results and wrote the manuscript. M.L.W. and H.R.L. conducted characterizations and tests work. J.L.Z. and Y.Y. conceived the experiment. J.L.Z. was responsible for the project and foundation. All authors reviewed the manuscript.

Competing interests

The authors declare no competing financial interests.

Corresponding authors

Correspondence to Jianling Zhao or Yang Yang.

About this article

Publication history

Received

Accepted

Published

DOI

https://doi.org/10.1038/srep22634

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.