High performance non-precious cathodic catalysts for oxygen reduction reaction (ORR) are vital for the development of energy materials and devices. Here, we report an noble metal free, Fe5C2 nanoparticles-studded sp2 carbon supported mesoporous material (CNTHb-700) as cathodic catalyst for ORR, which was prepared by pyrolizing the hybrid adduct of single walled carbon nanotubes (CNT) and lyophilized hemoglobin (Hb) at 700 °C. The catalyst shows onset potentials of 0.92 V in 0.1 M HClO4 and in 0.1 M KOH which are as good as commercial Pt/C catalyst, giving very high current density of 6.34 and 6.69 mA cm−2 at 0.55 V vs. reversible hydrogen electrode (RHE), respectively. This catalyst has been confirmed to follow 4-electron mechanism for ORR and shows high electrochemical stability in both acidic and basic media. Catalyst CNTHb-700 possesses much higher tolerance towards methanol than the commercial Pt/C catalyst. Highly efficient catalytic properties of CNTHb-700 could lead to fundamental understanding of utilization of biomolecules in ORR and materialization of proton exchange membrane fuel cells for clean energy production.
The essential role of ORR in proton exchange membrane fuel cells (PEMFC) and metal air batteries for enhanced industrial demand of high energy efficacy has increased its technological importance1,2,3. Despite being exorbitant and less abundant, noble metals like platinum and gold and its alloys have been long relied on for development of cathodic catalysts for ORR on account of their low overpotential and fast reduction kinetics4,5,6,7. However, due to high cost of these noble metals, there have been many attempts to develop non-precious metal-nitrogen/carbon (M-N/C) composites in which these pricey metals are replaced with cheap but electrochemically active transition metals like Fe and Co and their alloys8,9,10,11,12,13,14. Nitrogen, on the other hand, enhances the polarization of porous surface due to its basic nature, which results in high degree of surface adsorption of oxygen and thus assists ORR. As such, the development of commercially viable catalysts with high ORR properties, derived from inexpensive and naturally abundant precursors, has been a great challenge in the field of clean energy production. In this regard, use of selective transition metal carbide nanoparticles as catalytic sites on conductive carbon materials with high surface area can be envisioned as promising materials due to high surface activity and high durability.
Recently, the development of nanomaterials using metalloproteins with good electron transfer capabilities has attracted particular interest15,16,17. Among various transition metal compounds, metal carbides have been widely studied for their application as electrochemical catalysts due to their high conductivity and high resistance for corrosion18,19. The accumulation of appropriate portion of carbon can effectively modify the electron distribution in a metal to change its electronegativity in favor of its catalytic properties20. Herein, we have synthesized an sp2 carbon supported mesoporous material CNTHb-700 uniformly decorated with iron carbide (Fe5C2) nanoparticles by pyrolyzing the hybrid adduct of most common metalloprotein Hb and oxidized CNTs in the presence of ammonia gas. Hb with a quaternary structure, plays a dual role in synthesis of carbonized M-N/C material; (i) inherent Fe2+ ions located in each of four heme groups of a Hb molecule serve as a source of ORR active Fe5C2 nanoparticles-based catalytic sites and (ii) polypeptide chains and pyrrolic units of heme group behave as precursors for nitrogen doped sp2 carbon support. We observed that these Fe5C2 (510) nanoparticles behave as efficient oxygen reduction sites, showing the onset potential as good as commercial catalyst (20% Pt/C), while highly conducting Fe5C2 nanoparticles lead to efficient charge transfer responsible for high current density. We discuss the outstanding electrochemical features of the cost effective catalyst showing remarkable stability in its current density even after 10000 voltammetric cycles.
Earlier, blood powder has been used to generate nitrogen doped carbonized supporting material for oxygen reduction properties in only basic medium21. Due to relatively very low percentage of Fe (heme groups) in blood than in pure hemoglobin, main catalytic sites are either ‘doped heteroatoms’ generated by carbonized proteins of blood plasma like albumins, globulins and fibrinogens or/and extrinsically incorporated metal based nanoparticles21. In CNTHb-700, Hb molecules are self sufficient to generate Fe5C2 catalytic sites without any need of extrinsic addition of metal based nanoparticles for ORR properties in both acid and base. To best of our knowledge, this is the first report on synthesis of Fe5C2 nanoparticles appended CNTs from Hb/CNT adduct for the development of cathodic electrode for excellent oxygen reduction reaction in both acidic as well as in basic media.
The single walled CNT (SWCNT) was oxidized to oxidized CNT (o-CNT) in the presence of piranha according to a previous report22. To the well dispersed o-CNT in distilled water (60 mg/50ml), an aqueous solution of 40 mg of lyophilized Hb was added dropwise at 4 °C to avoid early denaturation of protein. The dispersion was allowed to be stirred for overnight at room temperature. The dispersion was centrifuged and washed with water 4–5 times. The solid part was dried and then placed in quartz pyrolysis tube and heated at 700 °C for 2 h with a rate of temperature increase 9 °C/min in NH3 atmosphere to give nitrogen doped carbonized composite CNTHb-700. The product was leached for 3 h in 0.1M sulfuric acid to remove inactive metal particles. Other catalysts (CNTHb1, CNTHb-II and CNTHb-III) were synthesized using same procedure by varying the amount of Hb in o-CNT. A schematic diagram shows the stepwise procedure for the synthesis of composite CNTHb-700 (Fig. 1a).
The scanning electron microscopy (SEM) of CNTHb-700 shows the formation of Fe5C2 nanoparticles over CNTs (Fig. 1b). High resolution (HR) transmission electron microscopic (TEM) (HRTEM) images of CNTHb-700 confirm the uniform adsorption of Fe5C2 nanoparticles along with carbonized sheets over CNTs (Fig. 1c). The distribution of Fe5C2 nanoparticles was supported by TEM-mapping of electronic image of catalyst CNTHb-700 (Supporting Information Fig. S1). The nanoparticles in HRTEM image possess lattice spacing of 0.205 nm (Fig. 1d) which clearly corresponds to Fe5C2 (510)23, whereas the carbonized part of Hb with lattice spacing of 0.31 nm corresponds to lattice fringes of C (002) planes, confirming the sp2 character24. The crystallanity of Fe5C2 nanoparticles was confirmed by fast Fourier transform (FFT) pattern (Inset, Fig. 1d) which exhibits the C3 symmetric structure of nanoparticles. The nanoparticles size-distribution study of a wider TEM image (Supporting Information Fig. S2a) with ~130 nanoparticles showed that ~63% of these particles lie below the range of 5 nm of diameter at the surface, whereas approximately 35% particles have diameter in the range of 2.0–4.0 nm (Supporting Information Fig. S2b). Such ultrafine nanoparticles are the reason of good dispersion of nanoparticles and more uniform adsorption over the carbon material.
Being a metalloprotein, Hb irreversibly adsorbs at the oxidized surface of oxidized CNTs (o-CNTs) due to hydrophobic interactions which further results in direct electron transfer (DET) interactions between protein and carbon materials to give oxidized CNTHb (o-CNTHb) hybrid adduct25. The UV-vis spectral study (Supporting Information Fig. S3) shows the interactions between oxidized SWCNT and Hb.
The o-CNT shows an undefined absorption band at 200–250 nm range, whereas the Hb in its aqueous solution shows the characteristic Soret band at 405 nm. Upon addition of aqueous solution of aqueous hemoglobin to aqueous dispersion of o-CNT, a defined band at 209 nm was observed along with another band at 405 nm which indicates the interactions between o-CNT with Hb in o-CNTHb adduct (Supporting Information Fig. S3). However, no change in characteristic Soret band corresponding to Hb at 405 nm was observed which means that secondary structure of protein is unperturbed26. Besides, the addition of Hb to CNT leads to immediate precipitation of otherwise soluble o-CNT and Hb solutions due to alteration in surface morphology of material by strong interactions between them (Supporting Information Fig. S3, Inset).
The electron transfer between Hb and o-CNT was further confirmed by comparing Raman spectra of o-CNT and o-CNTHb (Supporting Information Fig. S4). The G band corresponding to o-CNT is observed at 1596 cm−1 which shifts to the lower value of 1580 cm−1 upon addition of Hb, confirming the electron transfer. In addition to this, the 2D or G’ band in o-CNTHb is observed at higher wavenumber as compared to that in o-CNT, which indicates the separation of CNTs due to the increased negatively charged electron density on CNTs upon adsorption of Hb molecules on their surfaces. The decreased intensity of D band in o-CNTHb is possibly due to the denaturation of Hb molecules adsorbed on o-CNT. However, the Raman spectrum of CNTHb-700 shows enhancement in intensity of D band, thus leading to high ID/IG ratio which indicates the increased numbers of surface defect attributed to adsorbed iron carbide nanoparticles and nitrogen doping on the CNT surfaces27.
In powder X-ray differaction (XRD) pattern of CNTHb-700, the prominent peak at 26.69° can be attributed to the sp2 C(002) of CNT. Other small peaks at 2θ value 44.12° 51.45° and 75.66° correspond to sp2 carbons C(100), C(004) and C(110). Same diffraction peaks can also be observed in the XRD spectrum of oxidized o-CNT. In comparison to o-CNT, much stronger diffraction peak can be observed at 44.17° in the case of CNTHb-700 due to Fe5C2 nanoparticles with the lattice planes Fe5C2 (510) (Supporting Information Fig. S5)23.
FT-IR spectrum of CNTHb-700 shows broad stretching bands at 1137 cm−1 and 1564 cm−1 are characteristic features of C-N bond and C=O/C=N bonds, which indicates the high extent of nitrogen doping in material (Supporting Information Fig. S6). No significant band corresponding to C-N and C=N was observed in IR spectrum of o-CNT. The band at 2914 cm−1 corresponds to C-H bond stretches.
The key elements (C, N, O and Fe) in CNTHb-700 were determined by wide scan XPS spectra (Supporting Information Fig. S7). The C1s peak is unraveled into three peaks at 284.69 eV, 285.84 eV and 289.88 eV. The peak at 284.69 eV is a merged signal corresponding to sp2 carbon and C-Fe bond, whereas peaks at 285.84 eV and 289.88 eV are attributed to sp3 carbon and π − π* interactions, respectively (Fig. 2a)28. The N1s peak shows pyridinic, pyrrolic and graphitic nitrogen at 398.78 eV, 400.88 eV and 402.01 eV, respectively (Fig. 2b)29. In the case of Fe (2p) (Fig. 2c), the peaks at 706.11 eV and 719.25 eV confirms the formation of Fe5C2 nanoparticles, whereas the peak at 711.26 eV can be assigned to the binding energy of 2p3/2 orbital of Fe3+ moieties23,30. This result corroborates with the XRD results. For O1s, two peaks at 531.73 eV and 533.02 eV were observed due to C-O and C=O, respectively (Fig. 2d)31. However, the composition of the material was confirmed by elemental analysis (for C, N and O) and ICP-OES analysis (for Fe) which showed the weight % of C, N, O and Fe to be 78.48%, 7.25%, 8.2% and 5.8%, respectively.
The magnetic hysteresis loop of CNTHb-700 was recorded at 300 K to confirm the formation of Fe5C2 nanoparticles. The magnetization value was calculated with respect to per gram of Fe5C2 nanoparticles. It shows saturation magnetization value of 105 emu g−1 (Fig. 2e) which is very close to that of the characteristic value of soft ferro/ferrimagnetic Fe5C2 nanoparticles23. The magnetic intensities are little lower than bulk Fe5C2 due to the presence of CNTs and carbonized sp2 material.
The Brunauer-Emmett-Teller (BET) study of adsorption-desorption isotherm resulted in the curve supporting mesoporous phase in CNTHb-700 (Fig. 2f) with surface area of 459.25 m2g−1 and average volume of 105.51 cm3g−1. The pore size distribution in CNTHb-700 was studied by the Barrett-Joyner-Halenda (BJH) algorithm for approximation using nitrogen desorption branch at 77 K which revealed that most of the pores have diameter of 3.75 nm making the material highly mesoporous (Fig. 2f, Inset). The mesoporous material with such high surface area provides a plenty of catalytic surface for ORR, which also justifies the high catalytic performance of CNTHb-700 catalyst.
The electrochemical activity of CNTHb-700 as a cathodic material for ORR was studied by cyclic voltammetry (CV) and linear sweep voltammetry (LSV) using rotator disc electrode (RDE) in acidic and basic media. The CVs of CNTHb-700 in nitrogen saturated 0.1 M HClO4 and 0.1 M KOH solutions do not show any significant oxygen reduction peak which can be easily observed when same solutions were saturated with oxygen by purging it for 30 mins (Supporting Information Fig. S8a,b). It exhibits the ORR catalytic activity of CNTHb-700 as cathode in both acidic and basic media. However, oxygen reduction capabilities of this material were studied in detail by LSV measurements on RDE at 1600 rpm and compared with commercial 20% Pt/C at scan rate 10 mV s−1 in oxygen saturated 0.1 M HClO4 and 0.1 M KOH solutions. In acidic medium, the polarization curve of CNTHb-700 at 1600 rpm shows the onset potential of 0.92 V which is comparable to that of commercially available Pt/C under same conditions (Fig. 3a). Its half wave potential is just 75 mV lower than that of Pt/C. In basic medium under similar conditions, the onset potential of 0.92 V was observed (Supporting Information Fig. S9a). However, its half wave potential is ~55 mV lower than that of Pt/C. The material shows very high limiting current density of 6.34 and 6.69 mA cm−2 at 0.55 V (Fig. 3a, Supporting Information Fig. S9a) for acidic and basic media, respectively.
This catalytic performance of CNTHb-700 can be attributed to (a) uniformly adsorbed small Fe5C2 nanoparticles on the surface of CNTs which provide the metal based catalytic site for ORR, (b) polarizing nitrogens doped in carbon matrix of CNTs, which enhance the binding ability of neighboring carbon towards molecular oxygen to facilitate ORR and dramatically increase the conductivity of material by providing favorable channel for electron transfer and (c) high surface area of mesoporous M-N/C material which endows the system with highly available catalytic surface.
The oxygen reduction activity of CNTHb-700, in acidic medium, was compared with other CNT-Hb materials i.e. CNTHb-I, CNTHb-II and CNTHb-III which were prepared by same synthetic route but with different ratio of starting materials i.e. CNT:Hb (6:2, 6:3, 6:5, respectively). Interestingly, by changing the ratio of CHT:Hb from 6:4, the decrease in onset potentials as well as half wave potential was observed which certainly indicates that CNTHb-700 shows best catalytic performance (Supporting Information Fig. S9b). The decrease in amount of Hb in o-CNT perceptibly decreases the metal based catalytic sites, resulting in low catalytic activity. On the other hand, increasing the amount of Hb presumably leads to enveloped binding sites of N-doped CNTs by a larger number of Fe5C2 particles to decrease oxygen binding and ORR activity. Relatively, no significant ORR properties were observed in the case of activated isolated precursors o-CNT-700 and Hb-700 and unactivated hybrid adducts o-CNTHb (Supporting Information Fig. S9b).
The rotator ring disc electrode (RRDE) experiment was performed to calculate number of electrons involved in oxygen reduction and percentage of H2O2 production during the process in acidic and basic media. The hydrogen peroxide yield and number of electrons involved in ORR were calculated from disk currents and ring currents (Fig. 3b and Supporting information Fig. S10) in 0.1 M HClO4 and 0.1 M KOH, repsectively. In acidic medium, the yield of H2O2 is less than 1% and average number of electrons is 3.99, whereas in basic medium, the yield of H2O2 is less than 2% and average number of electrons is 3.98 (Supporting Information Fig. S10). To further confirm the 4-electron process, the ORR polarization curves at different rotation speeds from 300 to 1600 rpm were recorded in 0.1 M HClO4 (Supporting Information Fig. S11a) and 0.1 M KOH (Supporting Information Fig. S12a). Using Koutecky-Levich equation and J−1 versus ω−1/2 plots at different voltages (0.75, 0.73, 0.70, 0.67, 0.65, 0.63 and 0.60 V) drawn from ORR polarization curves, the number of electrons were calculated (Supporting Information Figs S11b and S12b) which corroborates with results of RRDE calculations to confirm the 4 e− mechanism of oxygen reduction in acidic as well as basic medium.
Generally, the activation at low temperature is helpful in better nitrogen doping of carbon matrix, whereas the high temperature activation results in better catalytic activation of material. Therefore, we optimized the pyrolysis temperature of o-CNTHb adduct by observing the effect of different activation temperatures (500, 600 and 800 °C) on ORR properties of material in 0.1 M HClO4. The CNTHb-700 gives the best ORR properties among CNTHb-500/600/700/800 (Supporting Information Fig. S13).
The chronoamperometric study of CNTHb-700 catalyst shows much higher stability in its current density than the Pt/C catalyst at 0.55 V (vs. RHE) in 0.1 M HClO4 (Fig. 4a). The accelerated degradation test (ADT) on cyclic voltammetry shows that CNTHb-700 exhibits a high long term stability between 0–1.2 V in 0.1 M HClO4 (Fig. 4b). After 10000 cycles, no significant change in cyclic voltammogram of CNTHb-700 was observed. In ORR polarization curve, after 10000 cycles, a small decrease of 30 mV in half wave potential was observed along with very small decrease in current density (Fig. 4c). However, no significant change in onset potential was observed. Likewise, CNTHb-700 also exhibits very high stability in 0.1 M KOH (Supporting Information Figs S14 and S15). The referred very small decrease in limiting current and half wave potential is supposedly due to limited Ostwald ripening which results in redeposition of small Fe5C2 nanoparticles to form relatively bigger Fe5C2 nanoparticles, thus relatively reducing the number of metal based catalytic sites. This proposed hypothesis is supported by the particle size distribution calculation from HRTEM image of CNTHb-700 which demonstrates that most of nanoparticles attain the diameter 10–15 nm after 10000 voltammetric cycles in 0.1M HClO4 (Supplementary Information, Fig. S16a,b). The XPS spectra of CNTHb-700 after 10000 voltammetric cycles shows a relatively smaller but broader peak at 705.87 eV corresponding to the Fe-C bond, which confirms the stability of Fe5C2 nanoparticles (Supporting Information Fig. S16c).
Moreover, to study the practical utility of catalyst, the methanol tolerance of CNTHb-700 was compared with that of Pt/C in acid and base. Upon adding 1 M of methanol in 0.1M of HClO4, no considerable change in current density was observed at 0.55 V (vs. RHE) for 80000 sec in the case of CNTHb-700, whereas a sudden drop in current density was observed in the case of Pt/C under similar conditions (Fig. 4d). Furthermore, no significant change in cyclic voltammogram and oxygen reduction polarization curve was observed in the case of CNTHb-700 (Fig. 4e,f), whereas an intense inverse methanol oxidation peak was observed in ORR curve of Pt/C (Supporting Information Fig. S17) in acid. The catalyst CNTHb-700 shows equally high methanol tolerance in 0.1 M KOH (Supporting Information Figs S18–S20), which is much superior to commercial Pt/C catalyst under similar conditions (Supporting Information Fig. S20a,b). These studies confirm much stable and selective catalytic behavior of CNTHb-700 over commercial Pt/C.
Furthermore, to have a better insight of the role of heme groups in Hb in consequential high ORR activity by CNTHb-700, we synthesized two model cathodic materials CNTCyt-700 and CNTMy-700 by using other heme proteins with single heme group i.e. cytochrom-C and myoglobin, respectively, in place of hemoglobin. As per our anticipation, both materials show inferior ORR catalytic activity than CNTHb-700 (Supporting Information Fig. S21) which is clearly due to the lesser available Fe5C2 based catalytic sites on nitrogen doped CNTs. FT-IR of CNTMy-700 and CNTCC-700 show much weaker stretching bands at 1197.98 and 1598.36 cm−1 and 1126.48 and 1553.62 cm−1, respectively, corresponding to C-N and C=N (Supporting Information Fig. S6). In addition to that, very weak diffraction peaks for Fe5C2 (510) can be observed in XRD spectra of CNTMy-700 and CNTCC-700, which confirms the lesser available metal based catalytic sites (Supporting Information Fig. S5) and thus explains the low-grade ORR properties. This approach evidently confirms the role of heme groups and the proposed mechanism of oxygen reduction by CNTHb-700 as cathodic electrode. Thus, the Hb carrying four heme groups plays a pivotal role in providing uniformly distributed metal based catalytic sites on the surfaces of CNTs, whereas CNTCC-700 and CNTMy-700 carry single heme group each show inferior oxygen reduction properties, thus confirming the role of heme groups in synthesis of efficient catalyst.
The Fe5C2 nanoparticles have been generated by thermally activating commercially available lyophilized hemoglobin to prepare a metal coordinating nitrogen doped carbon supported highly mesoporous material CNTHb-700. This material behaves as an excellent cathodic catalyst for ORR with onset potential as good as the commercial catalyst Pt/C with much higher current density of 6.34 and 6.69 mA cm−2 at 0.55 V (vs. RHE) in 0.1 M HClO4 and 0.1 M KOH, respectively. The catalyst exhibits quite high stability as it retains its current density for 80000 sec at 0.55 V (vs. RHE) in chronoamperometric study in acidic as well as basic media. CNTHb-700 exhibits much superior methanol tolerance than commercially available Pt/C which makes this catalyst a viable material for fuel cells.
Single walled carbon nanotubes were purchased from ILJIN Nanotech. Lyophilized hemoglobin (from human blood), myoglobin (from equine heart) and cytochrom C were purchased from Sigma Aldrich. The chemicals were used as such without any pretreatment. Double distilled water was used for synthesis and for electrochemical studies.
General Synthesis of catalyst
The oxidized CNT (o-CNT) was synthesized by following the reported procedure22. To the aqueous dispersion of o-CNT (60 mg/50ml) was dropwise added the aqueous solution of desired ratio of hemoglobin Hb at 4 °C. The mixture was allowed to be stirred for 15 h at room temperature. The dispersed reaction mixture was centrifuged at 10000 rpm for 10 min. The resulting solid adduct o-CNTHb was washed several times with distilled water and dried. The o-CNTHb adduct was pyrolysed at desired temperature (9°/min) for 2h under NH3 gas. This activated material was leached by sonicating it in 0.1 M sulfuric acid for 3 h to give resulting catalyst.
Field-emission SEM (FE-SEM) measurements were carried out on Hitachi S-4800. HRTEM was performed on JEOL, JEM-2100F with an acceleration voltage of 200 kV. TEM samples were prepared by placing a drop of the colloidal solution on a carbon-coated copper grid and dried overnight at room temperature. Normal X-ray diffractometer (Normal-XRD) measurements were performed on a D8 advance (Bruker AXS). Raman spectroscopy was measured on WITec, Alpha-300R. Fourier transform infrared spectroscopy (FTIR) was measured on a VARIAN, 670/620. Inductively coupled plasma-optical emission spectrometer (ICP-OES) was carried out on VARIAN-700ES. Element analyzer (EA) measurements were performed on Flash 2000 (Thermo scientific, Netherlands). Magnetic measurements were performed on powder samples using a Quantum Design MPMS-XL SQUID magnetometer. XPS was measured on K-alpha (thermos fisher, UK). Brunauer-Emmett-Teller (BET) measurements were carried out on BELSORP-miniII (BEL Japan, inc).
All CVs were recorded by scanning the electrode potential from 0 to 1.2 V (vs. RHE) at a scan rate of 50 mV s−1. The VSP-Modular 2 Channels Potentiostat/Galvanostat/EIS (Bio-Logic Science Instruments) was calibrated with respect to an Ag/AgCl electrode. CV measurements were carried out in an N2-saturated 0.1 M HClO4 solution at room temperature. Rotating-disk electrode measurements were carried out in an O2-saturated 0.1M HClO4 solution at room temperature using a rotating-disk electrode system for ORR calibration. Linear sweep voltammograms were recorded by scanning the disk potential from 1.2 to 0.2 V (vs. RHE) at a scan rate of 10 mVs−1. For CV and rotating-disk electrode experiments, a three electrode configuration was used, consisting of a modified glassy carbon electrode (geometric area of 0.0707 cm2) as the working electrode, Ag/AgCl as reference electrode and Pt wire as a counter electrode. The voltammetric results were later converted with respect to standard hydrogen electrode. A 300 μg cm−2 of each synthesized catalysts and 250 μg cm−2 of Pt/C were loaded on glassy carbon electrode for all voltammetric analyses.
How to cite this article: Vij, V. et al. Hemoglobin-carbon nanotube derived noble-metal-free Fe5C2-based catalyst for highly efficient oxygen reduction reaction. Sci. Rep. 6, 20132; doi: 10.1038/srep20132 (2016).
Vayssilov, G. N. et al. Support nanostructure boosts oxygen transfer to catalytically active platinum nanoparticles. Nat. Mater. 10, 310–315 (2011).
Wu, G., More, K. L., Johnston, C. M. & Zelenay, P. High-performance electrocatalysts for oxygen reduction derived from polyaniline, iron and cobalt. Science 332, 443–447 (2011).
Dewi, E. L., Oyaizu, K., Nishide, H. & Tsuchida, E. Electrocatalysis for dioxygen reduction by a m-oxo decavanadium complex in alkaline medium and its application to a cathode catalyst in air batteries. J. Power Sources 130, 286–290 (2004).
Dai, U. & Chen, S. Oxygen Reduction Electrocatalyst of Pt on Au Nanoparticles through Spontaneous Deposition. ACS App. Mater. Interfaces 7, 823–829 (2015).
Strmcnik, D. et al. Enhanced electrocatalysis of the oxygen reduction reaction based on patterning of platinum surfaces with cyanide Nat Chem 2, 880–885 (2010).
Tiwari, J. N. et al. Stable platinum nanoclusters on genomic DNA–graphene oxide with a high oxygen reduction reaction activity. Nat. Commun 4, 2221 (2013).
Tiwari, J. N. et al. Interconnected Pt-nanodendrite/ DNA/reduced-graphene-oxide hybrid showing remarkable oxygen reduction activity and stability. ACS Nano 7, 9223–9231 (2013).
Tang, H. et al. Molecular architecture of cobalt porphyrin multilayers on reduced graphene oxide sheets for high-performance oxygen reduction reaction. Angew. Chem. Int. Ed. 52, 5585–5589 (2013).
Lin, L., Zhu, Q. & Xu, A. W. Noble metal free Fe−N/C catalyst for highly efficient oxygen reduction reaction under both alkaline and acidic conditions. J. Am. Chem. Soc. 136, 11027−11033 (2014).
Strickland, K. et al. Highly active oxygen reduction non-platinum group metal electrocatalyst without direct metal–nitrogen coordination. Nat. Commun 6, 7343 (2014).
Rigsby, M. L., Wasylenko, D. J., Pegis, M. L. & Mayer, J. M. Medium effects are as important as catalyst design for selectivity in electrocatalytic oxygen reduction by iron-porphyrin complexes. J. Am. Chem. Soc. 137, 4296–4299 (2015).
Holewinski, A., Idrobo, J. C. & Linic, S. High-performance Ag–Co alloy catalysts for electrochemical oxygen reduction. Nat. Chem. 6, 828–834 (2014).
Wu, G. & Zelenay, P. Nanostructured nanoprecious metal catalysts for oxygen reduction reaction. Acc. Chem Res. 46, 1878–1889 (2013).
Wu, G., More, K. L., Johnston, C. M. & Zelenay. P. High-performance electrocatalysts for oxygen reduction derived from polyaniline, iron and cobalt. Science 332, 443–447 (2011).
Lu, Y., Yeung, N., Sieracki, n & Marshall, N. Design of functional metalloproteins Nature 460, 855–862 (2009).
Eddowes, M. J. & Hill, H. A. O. Novel method for the investigation of the electrochemistry of metalloproteins : cytochrome c. J. Chem. Soc., Chem. Commun. 771b–772, 10.1039/c3977000771b (1977).
Guo, J., Yao, X., Ning, L., Wang, Q. & Liu, H. The adsorption mechanism and induced conformational changes of three typical proteins with different secondary structural features on graphene. RSC Adv. 4, 9953–9962 (2014).
Yang, W., Liu, X., Yue, X., Jia, J. & Guo, S. Bamboo-like Carbon Nanotube/Fe3C Nanoparticle Hybrids and Their Highly Efficient Catalysis for Oxygen Reduction. J. Am. Chem. Soc. 137, 1436–1439 (2015).
Chen, M., Liu, J., Zhou, W., Lin, J. & Shen, Z. Nitrogen-doped graphene- supported transition-metals carbide electrocatalysts for oxygen reduction reaction. Sci. Rep. 5, 10389–10398 (2015).
Levy, R. B. & Boudart, M. Platinum like behavior of tungsten carbide in surface catalysis. Science 181, 547–549 (1973).
Zhang, C., Antonietti, M. & Fellinger, T. P. Blood Ties: Co3O4 Decorated Blood Derived Carbon as a Superior Bifunctional Electrocatalyst. Adv. Funct. Mater. 24, 7655–7665 (2014).
Datsyuka, V. et al. Chemical oxidation of multiwalled carbon nanotubes. Carbon 46, 833–840 (2008).
Huang, G. et al. Highly magnetic iron carbide nanoparticles as effective T2 contrast agents. Nanoscale, 6, 726–730 (2014).
Zhao, Z., Dai, Y., Ge, G., Guo, X. & Wang, G. Facile simultaneous defect production and O, N-doping of carbon nanotubes with unexpected catalytic performance for clean and energy-saving production of styrene. Green Chem. 17, 3723–3727 (2015).
Cai, C. & Chen, J. Direct electron transfer and biocatalysis of hemoglobin at a carbon nanotube. Anal. Biochem. 325, 285–292 (2004).
Gupta, S & Irihamye, A. Probing the nature of electron transfer in metalloproteins on graphene-family materials as nanobiocatalytic scaffold using electrochemistry. AIP advaces 5, 037106 (2015).
Liu, J., Webster, S. & Carroll, D. L. Temperature and Flow Rate of NH3 Effects on Nitrogen Content and Doping Environments of Carbon Nanotubes Grown by Injection CVD Method. J. Phys. Chem. B 109, 15769–15774 (2005).
Yang, X. H. et al. A free radical assisted strategy for preparing ultrasmall Pt decorated CNTs as a highly efficient counter electrode for dye-sensitized solar cells. J. Mater. Chem. A 2, 614–619 (2014).
Tang, L., Ji, R., Li, X., Teng, K. S. & Lau, S. P. Energy-level structure of nitrogen-doped graphene quantum dots. J. Mater. Chem. C 1, 4908–4915 (2013).
Yang, C., Zhao, H., Hou, Y. & Ma, D. Fe5C2 Nanoparticles: A facile bromide-induced synthesis and as an active phase for fischer−tropsch synthesis. J. Am. Chem. Soc. 134, 15814−15821 (2012).
Titirici, M. M., Thomas, A., Yu, S. H., Muller, J. & Antonietti, M. A direct synthesis of mesoporous carbons with bicontinuous pore morphology from crude plant material by hydrothermal carbonization. Chem. Mater. 19, 4205–4212 (2007).
This work was supported by NRF (National Honor Scientist Program: 2010-0020414).
The authors declare no competing financial interests.
Electronic supplementary material
About this article
Cite this article
Vij, V., Tiwari, J., Lee, WG. et al. Hemoglobin-carbon nanotube derived noble-metal-free Fe5C2-based catalyst for highly efficient oxygen reduction reaction. Sci Rep 6, 20132 (2016). https://doi.org/10.1038/srep20132
This article is cited by
Rational design of Fe-N-C electrocatalysts for oxygen reduction reaction: From nanoparticles to single atoms
Nano Research (2022)
In situ trapped high-density single metal atoms within graphene: Iron-containing hybrids as representatives for efficient oxygen reduction
Nano Research (2018)
Heavily Graphitic-Nitrogen Self-doped High-porosity Carbon for the Electrocatalysis of Oxygen Reduction Reaction
Nanoscale Research Letters (2017)