Abstract
Research on composite materials is facing, among others, the challenging task of incorporating nanocrystals and their superstructures, in polymer matrices. Electron microscopy can typically image nanometre-scale structures embedded in thin polymer films, but not in films that are micron size thick. Here, X-ray Ptychography was used to visualize, with a resolution of a few tens of nanometers, how CdSe/CdS octapod-shaped nanocrystals self-assemble in polystyrene films of 24 ± 4 μm, providing a unique means for non-destructive investigation of nanoparticles distribution and organization in thick polymer films.
Introduction
Hybrid materials fabricated by mixing metal chalcogenide semiconducting nanocrystals (NCs) with polymers have received particular attention in the last decade, triggered by their potential functionalities in the fields of electronics, optics, photovoltaics1,2,3,4,5, among others. The achievements in the synthesis of NCs in terms of control over their size and geometry6,7,8,9,10,11 have represented a step forward in the research of nanocomposites. As part of this field, scientists have been working on controlling the dispersion of NCs in polymer films and on correlating the formation of their ordered aggregates with the final properties of the nanocomposite12,13,14,15. The NCs organization in the polymer is expected to strongly influence the properties of the resulting material. For instance, the optical16, surface wettability14, stress sensing17 and transport18 properties of polymer nanocrystal-composites are strongly influenced by the NCs distribution and orientation in the polymer film. However, the presence of the polymer affects the way NCs interact during film fabrication and additionally makes it difficult to directly visualize the NCs in the polymer, especially in μm-thick films, thus preventing the assessment of their distribution, orientation and formation of ordered aggregates. Therefore, a reliable non-destructive high resolution imaging technique with the capability to penetrate μm-thick samples and with the necessary resolution to visualize nanometre-scale structures is needed. This stringent requirement rules out electron-based microscopic techniques, as they are not suited for imaging μm-thick films. Hard X-rays on the other hand ensure full penetration in thick polymer foils (even when they are several tens of μm thick), but the non-periodic organization of the NCs in polymers requires a coherent X-ray beam, if a diffractive imaging approach is to be used.
In the last decade, Coherent Diffractive Imaging (CDI) has been developed and optimized for nanostructural analysis of complex materials, regardless of their degree of crystallinity, thanks to significant advances in synchrotron source brilliance, efficiency of focusing optics and detectors19. CDI has been developed as a very promising tool for materials investigation at the nanoscale. In this technique, a coherent X-ray beam, scattered by an ensemble of objects (without any spatial correlation), freely propagates until it reaches a 2D detector, where its diffraction pattern is registered20,21,22.
With respect to imaging techniques that exploit an image forming lens, CDI has the advantage of avoiding any objective lens which would limit the final image spatial resolution. In CDI the ultimate spatial resolution is determined, in principle, by the wavelength of the radiation. In reality, it is limited by the largest angle at which scattered light can be reliably detected, by the mechanical precision and stability of the entire setup and by the sample radiation damage. As a drawback, CDI data have to be phase retrieved a posteriori with specific algorithms23,24,25 to reconstruct quantitatively the complex-valued exit wavefield after propagation through the object.
An interesting technique is ptychography, considered as the scanning mode version of CDI, which allows the analysis of extended specimens. In ptychography, the sample is scanned across a coherent and finite-sized illumination function-the probe-in such a way that the latter partially overlaps at adjacent scanning positions26,27,28. A diffraction pattern is recorded at each scanning position and it is then used in the phase retrieval algorithms to reconstruct the object transmission function29,30,31. The redundancy in the ptychography data, introduced by the overlapping illuminated regions, provides a higher robustness in the phase reconstruction algorithms. This technique has been employed with success in the last years, for example for the first tomographic reconstruction of a bone specimen32, as a label-free bioimaging method to investigate weakly scattering objects33,34 or biological cells35,36,37, as well as in Bragg projection for the visualization of strain fields of extended crystals38,39 or to image nanoscale ferroelectric domains40. The combination of ptychography with scanning X-ray fluorescence microscopy has also been explored41,42. Advantages of ptychography over the other X-ray based microscopy techniques can be listed as follows: i) it can probe matter at the nanoscale; ii) radiation damage problems are limited33,34,35,36,37, since it is a phase contrast imaging technique; iii) it is compatible with specific sample environments for in situ and in operando studies38,39,40; and iv) it can be combined with other types of microscopies41,42.
Here, ptychography was used to investigate the distribution of octapod-shaped NCs (made of a CdSe core and eight CdS arms)10,43 embedded in polystyrene (PS) μm-thick films. In nm-thick polymer films, octapods tended to either segregate to the bulk boundaries or to cluster into short linear arrays when the polymer content was increased, as revealed by transmission electron microscopy (TEM) in a previous work14. However, when the octapods were embedded in free-standing PS films, several μm thick, they could not be imaged through standard imaging techniques (such as TEM), which prevented us from drawing any conclusion on whether chain-like assemblies were still formed in polymers in such circumstances. Ptychography was therefore the technique of choice in this case. Phasing of the raw data, performed here using a difference map algorithm27, was combined with deblurring and denoising algorithms to improve signal-to-noise ratio and reduce the background contribution of the original data and ultimately led to an enhancement of the object visibility. In this way, we were able to retrieve a high contrast octapod density map that enabled us to visualize the NCs organization in such thick polymer films.
Results
Figure 1 shows: a TEM image of a CdSe/CdS octapod-shaped NC synthesized as reported in previous works10,43 (panel a); the nanostructures formed by the addition of polystyrene (panel b); a scheme of the preparation process of the free-standing nanocomposite films for the ptycography studies (panel c). Details are given in the Supplementary Information (Fig. S1) and in the Methods section. The final thickness of the free-standing films was 24 ± 4 μm. For comparison purposes, additional samples from both repeatedly-washed octapod solutions and octapod/PS mixtures were also prepared by drop casting (15 μl) on Si3N4 membranes and were allowed to dry under the same conditions as for the free-standing films. The resulting nanocomposite films, prepared with this approach, presented a thickness of 307 ± 10 nm. The following specimens were structurally investigated: i) a sample made from a repeatedly-washed octapod solution (no polymer), drop-casted on top of a Si3N4 membrane (OCT sample); ii) two thin octapod/PS films, prepared with two different batches of PS having molecular weights (Mw) of 190 and 350 kg/mol, respectively and deposited on top of Si3N4 membranes (named PS190_thin and PS350_thin); iii) two free-standing octapod/PS films, named PS190 and PS350, using the same two polymer batches as for the films deposited on the Si3N4 membranes.
(a) Close-view TEM image showing a single octapod standing on a carbon-coated Cu grid with four pods. The cartoon highlights its orientation. Scale bar: 50 nm. (b) 45°-tilt-SEM image demonstrating the presence of a linear ordered aggregate of octapods after the removal of the PS by oxygen plasma in a thinner nanocomposite film standing on a SiO2 substrate. Scale bar: 500 nm. (c) Overview of the fabrication process by mould casting: vials containing the octapod solutions after the addition of the polymers evidencing no visible changes in transparency; the sketches show the injection of the nanocomposite solution into Al moulds to produce the free-standing thick films.
The first structural characterization was carried out by grazing incidence small angle X-ray scattering (GISAXS) on the named OCT sample and the thin octapod-PS films, PS190_thin and PS350_thin. Data were recorded at the XRD2 beamline of the LNLS synchrotron in Campinas. Fig. S2a–c are the GISAXS data registered on the OCT sample at incidence angles αi of 0.17°, 0.27° and 0.37°, respectively. The coherent scattering features detectable in the data are fingerprints of the organization of the octapods in ordered arrays, as already reported by us in a previous work44. In order to better appreciate these features, GISAXS data collected on the OCT sample at αi = 0.27° are displayed in Fig. S3 where the two dotted lines identify the position of intensity maxima associated to the presence of the arrays of octapods44. Conversely, GISAXS data collected, at the same incidence angles, from the PS190_thin and PS350_thin films (see Fig. S2d–i), did not reveal any scattering feature directly related to any possible assembly of the octapods into periodic arrays.
PS350_thin, PS190 and PS350 free-standing films were therefore imaged through ptychography to inspect the configuration of the octapods in the PS thin/thick films, as a function of the polymer molecular weight Mw (comparison between the PS190 and PS350 films) and of the film thickness (comparison between the PS350_thin and PS350 films). The experiments, described in detail in the Methods section, were performed at the cSAXS beamline of the Swiss Light Source in Villigen. For the free-standing films (PS190 and PS350), two different areas (labelled as pos1 and pos2 in Table S1) distant 7 mm from each other were explored. A single area was investigated for the PS350_thin and the OCT samples. For each area we acquired data from five regions (named A, B, C, D, E as displayed in the scheme in Fig. S4). Each region was 4 × 4 μm2 large and the regions were located at relative distances of 50 μm from each other. The same region was scanned five times consecutively by repeating the procedure described in the Methods, producing a matrix of images , with i = 1 to 5. An example of the five phased maps acquired from sample PS190 in the region A of pos2 is shown in Fig. S5a–e. In all these images the structural features visibility is affected by noise and contrast. Consequently, averaging, denoising and deblurring were useful to reduce the noise level in the polymer background, to enhance the image contrast and therefore, to visualize the nanoscale structure of the sample at the experimentally achievable spatial resolution (see details in the Methods section). The image obtained after the averaging/denoising/deblurring process for sample PS190 is reported in Fig. S5f. Given the clear improvement that was observed, we proceeded to average, denoise and deblur all the phased images, after sub-pixel alignment. The results are presented in Fig. 2a for the OCT sample (region E), Fig. 2c for the PS350_thin (region A) and in Fig. 3a and Fig. 3c for the PS190 (region A, pos2) and PS350 (region B, pos2) free-standing films, respectively. These images represent the phase of the recovered complex-valued exit wavefield, after propagation through the object25 or, in other words, the images are correlated to the actual arrangement of the octapods inside the polymer thick-films. The full dynamical colour range was used in the images to enhance object visibility. The presence of the NCs produces an additional phase shift Δϕ with respect to the reference value corresponding to the bare polymer (background level). For each region and area, here explored, we computed and summarized in Table S1: i) the percentage (S%) of the 4 × 4 μm2 region where the phase Δϕ exceeds the background level, which is a direct indication of the sample portion containing nanocrystals; ii) the mean phase (<Δϕ>) averaged over S% and iii) the maximum phase retardation (Δϕmax). The error in the phase shifts is about 0.002.
Ptychography results for the OCT
(a,b) and PS350_thin (c,d) samples. Displayed in colors (a,c) and black and white (b,d) is the phase retardation (Δϕ) of the recovered complex-valued exit wavefield. Area of the images in panels (a,c) is 2.5×2.5 μm2, area of the images in panels (b,d) is 870×870 nm2 and corresponds to the square marked in blue in (a,c). Scale bar is 200 nm. Sketch in Fig. 2b depicts octapods in pod-to-pod contact visible in the square marked in white; sketch in Fig. 2d shows more intricate 3D aggregates with stronger interconnected octapods visible in the square marked in white.
Ptychography results for the PS190
(a,b) and PS350 (c,d) free-standing samples. Displayed in colors (a,c) and black and white (b,d) is the phase retardation (Δϕ) of the recovered complex-valued exit wavefield. Area of the images in panels (a,c) is 2.5 × 2.5 μm2, area of the images in panels (b,d) is 870 × 870 nm2 and corresponds to the square marked in blue in (a,c). Scale bar is 200 nm.
To evidence the effect of the molecular weight and thickness of the polymer on the octapod arrangement we conducted a quantitative comparison among the four samples. In Table 1 we report the mean phase shifts <Δϕ>, extracted from Table S1 and the polymer thickness (tPS). We found that is larger than
and
is larger than
. Thus, the average phase shift increases both by reducing the polymer thickness tPS, for the same molecular weight and by reducing the polymer molecular weight, for the same tPS. As a result, the octapod aggregation appears to be dependent on the molecular weight and thickness of the polymer film.
Table 1 summarizes also the image resolution values (ρ). Considering the adopted experimental conditions described in the Methods section, the expected spatial resolution was ρ27 nm. In order to estimate the actual spatial resolution of the phased images (before and after the averaging and filtering procedure), we adopted the Fourier shell correlation (FSC) criterion, as described in the Supplementary Information (section Resolutions, Fig. S6)45,46. The error in the FSC resolution depends on the indetermination in the sub-pixel alignment procedure46. By changing the alignment by ±1 subpixel (Δdet/3), the resolution was found to vary within ±1 nm.
Close up views of the regions framed in blue in Figs 2 a,c and 3a,c, are displayed in Figs 2b,d and 3b,d, which allow to better elucidate the arrangement of octapods, both alone and embedded in a thick-free-standing polymer film. In the case of the octapods without polymer, the NCs are standing with four pods in contact with the Si3N4 membrane and forming linear arrays in some areas, where the octapods present a pod-to-pod contact with neighboring ones (as highlighted by the sketch in Fig. 2b which shows possible ways of NCs contact), while the octapods form more intricate 3D aggregates when they are embedded in the polymer films-with stronger interconnection-as depicted by the sketch in Fig. 2d. This can be also appreciated from the changes of the <Δϕ> values, that are the smallest in the case of octapods that form mainly 2D structures (see Fig. 2a,b and in Table 1) and they become larger when the octapods are embedded in the polymer, which is an indication of their 3D organization. Note that our images present features that cannot be exclusively attributed to the sample structures, as they can be residual artifacts of the reconstruction process, most probably due to a not entirely accurate knowledge of the probe translation positions47. However, the unavoidable presence of residual artifacts in the images does not impact significantly our conclusion of being able to visualize the NCs in the thick-polymer films. Thus, our results highlight the potential use of the ptycography for the analysis of nanostructures in polymer matrices.
Conclusions
To summarize, the major results which can be drawn from this analysis are the following:
-
1
GISAXS investigation ruled out any possible organization of the octapods into ordered arrays for the thin polymer films; periodic arrays were found only for the sample made from a repeatedly-washed octapod solution (no polymer), drop-casted on top of a Si3N4 membrane.
-
2
Ptychography allowed visualizing the self-assembly of octapods into linear and interconnected structures, both in the thin polymer films and in the free-standing polymer films. This result is in agreement with the octapod configuration observed by TEM/SEM on nanometric thin polymer samples, but never experimentally demonstrated for free-standing thick films.
-
3
Averaging/deblurring/denoising allowed improving image contrast and reducing noise level in the background between octapod nanostructures. This consented to visualize the sample structures at a resolution close to the nominal one (27 nm).
-
4
Ptychographic data were used to explore the effect on the octapod aggregation of: i) different polymer film thickness for the same polymer molecular weight in the PS350_thin and PS350 samples; and ii) different molecular weights, for the same thickness of the polymer film in the PS350 and PS190 samples. The results from the analysis suggest that the octapod distribution in the polymer films is influenced by the molecular weight of the polymer and the thickness of the resulting composite film.
-
5
The resolution of the phase maps acquired in the free-standing composite films was not affected by the film thickness in the range here studied, up to 24 μm. This finding indirectly confirms that the projection and product approximations hold for our experiment. Actually, both film thickness and molecular weight do not impact the quality of the resulting images. This finding could have interesting implications for other imaging experiments and sample preparations.
In conclusion, we have imaged through ptychography the aggregation of CdSe/CdS octapod-shaped nanocrystals in 24 ± 4 μm thick free-standing polystyrene films. This X-ray-based microscopy technique allowed imaging, with a resolution of a few tens of nanometers, the aggregation of the octapods in interconnected architectures. Our work demonstrates the potential of ptychography to enhance the imaging of complex structures embedded in thick free-standing films, thus helping to fill the gap from nanometer to micrometer scale.
Methods
Preparation of the octapod-polystyrene nanocomposite films
The nanocomposite solutions were prepared by first dissolving polystyrene polymer from Sigma-Aldrich (Mw = 190.000 g/mol; Mw = 350.000 g/mol; Tg = 94 °C) at 5% vol in toluene; the polymer solutions were kept under strong shaking for 5 hours prior to use and then sonicated for 5 min. Octapods/polystyrene mixtures were prepared by adding 200 μl of sonicated polystyrene solutions to 300 μl of the sonicated octapod solution (10−8 M) for a final polymer concentration in the mixture of 2% vol. The mixtures were magnetically stirred rigorously for 15 min and cleared of air bubbles. In the first series of experiments the mixture solution was cast on a SiO2 substrate. Then we proceeded to prepare the free standing films: 350 μl of the mixture prepared with the higher Mw polymer and and 450 μl of the mixture prepared with the lower Mw polymer were injected each mixture solution into an open Aluminum mould of 30 × 10 × 3 mm3 previously polished, cleaned and coated with Marbocote 227 CEE release agent from Marbo Italia SPA. The samples were allowed to dry at room temperature inside the glove box for 12 hours. Finally, the samples were released from the mould and cut in prismatic shapes of ca. 20 × 8 mm2.
Bright field transmission electron microscopy (TEM) analyses
Bright field transmission electron microscopy (TEM) analyses were conducted on a 100 kV JEOL JEM 1011 microscope. Scanning electron microscopy (JEOL JSM-7500FA) was conducted on both carbon-coated film on TEM grids and SiO2 substrates with a 10 nm sputtered carbon coating. All substrates were cleaned before depositing the drops using 10 minutes of ultrasonic bath in acetone, distilled water and isopropanol. After cleaning they were carefully dried with pressurized air. A plasma reactor (Gambetti Tucano Multipurpose Plasma System) with an oxygen flow was used for the removal of the polymer from the SiO2 substrate. The plasma exposure time was 5 min at room temperature with a bias power level of 200 W. The thickness of the thinner films supported by the membranes was measured by an AMBiOS XP-2 Technology optical profilometer. A micrometer gauge was used to measure the thickness of the free-standing films.
Grazing Incidence Small Angle X-ray Scattering Experiment
GISAXS measurements were performed at the XRD2 beamline at LNLS (Brazilian Synchrotron Light Laboratory) in Campinas (Brazil). A Pilatus 100 K detector was used, with 487 × 195 pixels and 172 μm × 172 μm pixel size. The sample-to-detector distance was equal to 2.3 m; the radiation energy was E = 8.0 keV.
Ptychographic Coherent Diffractive Imaging Experiment
The experiments were performed at the cSAXS beamline of the Swiss Light Source, at the Paul Scherrer Institut in Villigen, Switzerland. The energy of the incident beam was set to 6.2 keV (wavelength, λ = 0.2 nm). An Au Fresnel zone plate (FZP) with a diameter of 200 μm, fabricated on a 200 nm thick silicon nitride membrane, was used to define a coherent illumination onto the sample. The outermost zone width and the thickness of the FZP were 50 nm and 500 nm, respectively. The focal distance was 50 mm with a depth of focus of 50 μm. Coherent illumination of the entire lens aperture was ensured by using a horizontal aperture close to the source48. The sample was mounted on a piezoelectric stage allowing positioning with nanometer resolution in the two directions transversal to the beam propagation. Coherent diffraction patterns were recorded with a Pilatus 2M detector with Δdet-pixel = 172 μm pixel size49 placed at z = 2.236 m from the sample with a flight tube in between, filled with He to reduce air scattering and absorption. Optics-sample distance was z1 = 270 μm.
We first obtained ptychographic images on a test specimen with large phase contrast features in order to obtain an initial probe for subsequent ptychographic imaging of the samples, as described for ptychography on weak scattering objects34. For the investigated samples, we placed the specimen at z1 = 270 μm from the focal plane of the lens, in such a way that the beam had a size of d = 450 nm at the sample position. For each sample we collected 5 repeated scans of the sample area. Each scan was realized by moving the sample along concentric circles34 with a radial step size of 0.2 μm and 5 points in the first circle. A diffraction pattern with 0.2 s exposure time was collected at each scanning point. The total scanned area was 4 × 4 μm2 with a total of 324 scanning points (see Fig. S7 in the Supplementary Information), which took about 2 minutes including the time required for sample positioning. Polymers are expected to suffer from radiation damage. Therefore, we preferred the strategy of acquiring 5 datasets, with 0.2 s exposure time per scanning point, in order to fractionate the dose among datasets. This choice allowed us to measure a-posteriori the correlation between consecutive phase maps and to average only those with the highest correlation (equal or larger than 97%), i.e. unaffected by radiation damage.
Ptychographic reconstructions were performed for each scan with 200 iterations of the difference map algorithm50 and 100 iterations of a maximum likelihood optimization algorithm used as a refinement51,52. In the ptychographic reconstructions we used the probe previously retrieved with the test specimen as the initial probe, which was then updated in each iteration50. The effective area of the detector used for phasing was Ndet × Ndet = 192 × 192 pixels, determining a pixel size of the phased image of nm. The expected spatial resolution was
nm, being the numerical aperture
Concerning the procedure followed for denoising and deblurring the averaged images, image contrast enhancement was realized by means of a standard MATHEMATICA deblurring routine, based on the Total Variation approach, which deconvolves a point spread box function, one pixel large. Denoising was performed by a bilateral filter, which reduces noise, preventing edge smoothing.
Additional Information
How to cite this article: De Caro, L. et al. Ptychographic Imaging of Branched Colloidal Nanocrystals Embedded in Free-Standing Thick Polystyrene Films. Sci. Rep. 6, 19397; doi: 10.1038/srep19397 (2016).
References
Kao, J., Thorkelsson, K., Bai, P., Rancatore, B. J. & Xu, T. Toward functional nanocomposites: taking the best of nanoparticles, polymers and small molecules. Chem. Soc. Rev. 42, 2654–2678 (2013).
Herzog, G. et al. Influence of Nanoparticle Surface Functionalization on the Thermal Stability of Colloidal Polystyrene Films. Langmuir 28, 8230–8237 (2012).
Morgenstern, F. S. F. et al. Ultrafast Charge- and Energy-Transfer Dynamics in Conjugated Polymer: Cadmium Selenide Nanocrystal Blends. ACS Nano 8, 1647–1654 (2014).
Li, Z., Gao, F., Greenham, N. C. & McNeill, C. R. Comparison of the Operation of Polymer/Fullerene, Polymer/Polymer and Polymer/Nanocrystal Solar Cells: A Transient Photocurrent and Photovoltage Study. Adv. Funct. Mater. 21, 1419–1431 (2011).
Dayal, S., Kopidakis, N., Olson, D. C., Ginley, D. S. & Rumbles, G. Photovoltaic Devices with a Low Band Gap Polymer and CdSe Nanostructures Exceeding 3% Efficiency. Nano Lett. 10, 239–242 (2009).
Paik, T. & Murray, C. B. Shape-directed binary assembly of anisotropic nanoplates: a nanocrystal puzzle with shape-complementary building blocks. Nano Lett. 13, 2952–2956 (2013).
Li, H. et al. Synthesis of Uniform Disk-Shaped Copper Telluride Nanocrystals and Cation Exchange to Cadmium Telluride Quantum Disks with Stable Red Emission. J. Am. Chem. Soc. 135, 12270–12278 (2013).
Zanella, M. et al. Self-Assembled Multilayers of Vertically Aligned Semiconductor Nanorods on Device-Scale Areas. Adv. Mater. 23, 2205–2209 (2011).
Miszta, K. et al. Hierarchical self-assembly of suspended branched colloidal nanocrystals into superlattice structures. Nature Mater. 10, 872–876 (2011).
Deka, S. et al. Octapod-Shaped Colloidal nanocrystals of Cadmium Chalcogenides via “One-Pot” Cation Exchange and Seeded Growth. Nano Lett. 10, 3770–3776 (2010).
Kostiainen, M. A. et al. Electrostatic assembly of binary nanoparticle superlattices using protein cages. Nat Nano 8, 52–56 (2013).
Shenhar, R., Norsten, T. B. & Rotello, V. M. Polymer-Mediated Nanoparticle Assembly: Structural Control and Applications. Adv. Mater. 17, 657–669 (2005).
Modestino, M. A., Chan, E. R., Hexemer, A., Urban, J. J. & Segalman, R. A. Controlling Nanorod Self-Assembly in Polymer Thin Films. Macromolecules 44, 7364–7371 (2011).
Arciniegas, M. P. et al. Self-Assembly of Octapod-Shaped Colloidal Nanocrystals into a Hexagonal Ballerina Network Embedded in a Thin Polymer Film. Nano Lett. 14, 1056–1063 (2014).
Zhang, H., Liu, Y., Yao, D. & Yang, B. Hybridization of inorganic nanoparticles and polymers to create regular and reversible self-assembly architectures. Chem. Soc. Rev. 41, 6066–6088 (2012).
Roskov, K. E., Kozek, K. A., Wu, W.-C., Chhetri, R. K., Oldenburg, A. L., Spontak, R. J. & Tracy, J. B. Long-Range Alignment of Gold Nanorods in Electrospun Polymer Nano/Microfibers. Langmuir 27, 13965–13969 (2011).
Raja, S. N., Olson, A. C. K., Thorkelsson, K., Luong, A. J., Hsueh, L., Chang, G., Gludovatz, B., Lin, L., Xu, T., Ritchie, R. O. & Alivisatos, A. P. Tetrapod Nanocrystals as Fluorescent Stress Probes of Electrospun Nanocomposites, Nano Lett. 13, 3915–3922 (2013).
Vercelli, B., Zotti, G., Berlin, A. & Natali M. Self-Assembled Structures of Semiconductor Nanocrystals and Polymers for Photovoltaics. (3) PbSe Nanocrystal−Polymer LBL Multilayers. Optical, Electrochemical, Photoelectrochemical and Photoconductive Properties. Chem. Mater. 22, 2001–2009 (2010).
Holt, M., Harder, R., Winarski, R. & Rose, V. Nanoscale Hard X-Ray Microscopy Methods for Materials Studies, Annu. Rev. Mater. Res. 43, 183–211 (2013).
van der Veen, J. F. & Pfeiffer, F. Coherent x-ray scattering. J. Phys. Condens. Mat. 16, 5003–5030 (2004).
Nugent, K. A. Coherent methods in the X-ray sciences. Adv. Phys. 59, 1–100 (2010).
De Caro, L., Carlino, E., Siliqi, D. & Giannini, C. Coherent Diffractive Imaging – from nanometric down to picometric resolution. In Handbook of Coherent-Domain Optical Methods: Biomedical Diagnostics, Environmental Monitoring and Material Science,(ed. Tuchin, V. ) p. 291–314 (Springer: New York,, 2012).
Gerchberg, R. W. & Saxton, W. O. A practical algorithm for the determination of the phase from image and diffraction plane pictures. Optik 35, 237–250 (1972).
Fienup, J. R. Phase retrieval algorithms: a comparison. Appl. Opt. 21, 2758–2769 (1982).
Fienup, J. R. Phase retrieval algorithms: a personal tour, Appl. Opt. 52, 45–56 (2013).
Rodenburg, J. M. et al. Hard-X-Ray Lensless Imaging of Extended Objects, Phys. Rev. Lett. 98, 034801 (2007).
Thibault, P. et al. High-Resolution Scanning X-ray Diffraction Microscopy. Science 321, 379–382 (2008).
Maiden, A. M., Humphry, M. J., Zhang, F. & Rodenburg, J. M. Superresolution imaging via ptychography. J. Opt. Soc. Am. A 28, 604–612 (2011).
Faulkner, H. M. L. & Rodenburg, J. M. Movable Aperture Lensless Transmission Microscopy: A Novel Phase Retrieval Algorithm Phys. Rev. Lett. 93, 023903 (2004).
Rodenburg, J. M. & Faulkner, H. M. L. A phase retrieval algorithm for shifting illumination. Appl. Phys. Lett. 85, 4795–4797 (2004).
Maiden, A. M. & Rodenburg, J. M. An improved ptychographical phase retrieval algorithm for diffractive imaging. Ultramicroscopy 109, 1256–1262 (2009).
Dierolf, M. et al. Ptychographic X-ray computed tomography at the nanoscale. Nature 467, 436–439 (2010).
Giewekemeyer, K. et al. Quantitative biological imaging by ptychographic x-ray diffraction microscopy, Proc. Natl. Acad. Sci. USA. 107, 529–534 (2010).
Dierolf, M. et al. Ptychographic coherent diffractive imaging of weakly scattering specimens. New J. Phys. 12, 035017 (2010).
Jones, M. W. M. et al. Whole-cell phase contrast imaging at the nanoscale using Fresnel Coherent Diffractive Imaging Tomography. Sci. Rep. 3, 2288, doi: 10.1038/srep02288 (2013).
Marrison, J., Lotta, R., Marriott, P. & O’Toole, P. Ptychography – a label free, high-contrast imaging technique for live cells using quantitative phase information. Sci. Rep. 3, 2369, doi: 10.1038/srep02369 (2013).
Lima, E. et al. Cryo-scanning x-ray diffraction microscopy of frozen-hydrated yeast, J. Microsc. 249, 1–7 (2013).
Takahashi, Y. et al. Bragg x-ray ptychography of a silicon crystal: Visualization of the dislocation strain field and the production of a vortex beam. Physical Review B 87, 121201(R) (2013).
Godard, P. et al. Three-dimensional high-resolution quantitative microscopy of extended crystals. Nat. Comm. 2, 568 (2011).
Hruszkewycz, S. O. et al. Imaging Local Polarization in Ferroelectric Thin Films by Coherent X-Ray Bragg Projection Ptychography. Phys. Rev. Lett. 110, 177601 (2013).
Vine, D. J. et al. Simultaneous X-ray fluorescence and ptychographic microscopy of Cyclotella meneghiniana. Opt. Express 20, 18287–96 (2012).
Deng, J. et al. Simultaneous cryo X-ray ptychographic and fluorescence microscopy of green algaeProc. Natl. Acad. Sci. USA. 112, 2314–2319 (2015).
Kim, M. R. et al. Influence of Chloride Ions on the Synthesis of Colloidal Branched CdSe/CdS Nanocrystals by Seeded Growth. ACS Nano 6, 11088–11096 (2012).
De Caro, L. et al. A superbright X-ray laboratory microsource empowered by a novel restoration algorithm. J. Appl. Cryst. 45, 1228–1235 (2012).
Nieuwenhuizen, R. P. J. et al. Measuring image resolution in optical nanoscopy, Nat. Meth. 10, 557–562 (2013).
van Heel, M. & Schatz, M. Fourier shell correlation threshold criteria. J. Struct. Biology 151, 250–282 (2005).
Zhang, F. et al. Translation position determination in ptychographic coherent diffraction imaging. Opt. Express 21, 13592–13606 (2013).
Vila-Comamala, J. et al. Characterization of high-resolution diffractive X-ray optics by ptychographic coherent diffractive imaging. Opt. Express 19, 21333–21344 (2011).
Kraft, P. et al. Characterization and Calibration of PILATUS Detectors. Ieee T Nucl Sci 56, 758–764 (2009).
Thibault, P., Dierolf, M., Bunk, O., Menzel, A. & Pfeiffer, F. Probe retrieval in ptychographic coherent diffractive imaging. Ultramicroscopy 109, 338–343 (2009).
Guizar-Sicairos, M. & Fienup, J. R. Phase retrieval with transverse translation diversity: a nonlinear optimization approach. Opt. Express 16, 7264–7278 (2008).
Thibault, P. & Guizar-Sicairos, M. Maximum-likelihood refinement for coherent diffractive imaging, New J. Phys. 14, 063004 (2012).
Acknowledgements
The authors acknowledge financial support from the European Commission under the Seventh Framework Program by means of the grant agreement for the Integrated Infrastructure Initiative N. 262348 European Soft Matter Infrastructure (ESMI) and from the CNR/CNpQ Italian-Brazilian bilateral agreement (X-ray meso-crystallographic studies of self-assembled 3D nanocrystal superlattices). Ana Diaz and Andreas Mendzel are greatly acknowledged for setting up the experiment at the cSAXS beamline and for providing beamtime for the measurements. The staff of the XRD2 beamline at LNLS-Campinas, in particular Leide Cavalcanti, Douglas Henrique Caetano de Araujo and Henrique Ferreira Canova, are acknowledged for their technical support during GISAXS data acquisition. One of the author (C.G.) is indebted with Ian Robinson for useful discussions.
Author information
Authors and Affiliations
Contributions
C.G., D.A. and D.S. conceived and realized the ptychography experiment at cSAXS-PSI; M.R.K., M.A. and L.M. prepared the nanocrystals/polymers, D.A. and T.S. collected the GISAXS data; L.D.C. and D.S. transformed the ptychographic data into quantitative microscopies. L.D.C. realized the algorithms to improve the resolution of the PIE phased maps, C.G., M.A., L.M., D.A. and L.D.C. discussed the results and wrote the paper in close collaboration with all the authors.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
De Caro, L., Altamura, D., Arciniegas, M. et al. Ptychographic Imaging of Branched Colloidal Nanocrystals Embedded in Free-Standing Thick Polystyrene Films. Sci Rep 6, 19397 (2016). https://doi.org/10.1038/srep19397
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep19397
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.