Abstract
A model binary hybrid system composed of a randomly distributed rare-earth ferromagnetic (Gd) part embedded in an s-wave superconducting (Nb) matrix is being manufactured to study the interplay between competing superconducting and ferromagnetic order parameters. The normal metallic to superconducting phase transition appears to be very sensitive to the magnetic counterpart and the modulation of the superconducing properties follow closely to the Abrikosov-Gor’kov (AG) theory of magnetic impurity induced pair breaking mechanism. A critical concentration of Gd is obtained for the studied NbGd based composite films (CFs) above which superconductivity disappears. Besides, a magnetic ordering resembling the paramagnetic Meissner effect (PME) appears in DC magnetization measurements at temperatures close to the superconducting transition temperature. The positive magnetization related to the PME emerges upon doping Nb with Gd. The temperature dependent resistance measurements evolve in a similar fashion with the concentration of Gd as that with an external magnetic field and in both the cases, the transition curves accompany several intermediate features indicating the traces of magnetism originated either from Gd or from the external field. Finally, the signatures of magnetism appear evidently in the magnetization and transport measurements for the CFs with very low (<1 at.%) doping of Gd.
Similar content being viewed by others
Introduction
A coupled superconductor (SC) - ferromagnet (FM) hybrid system can provide a model platform to study the interaction between two fundamentally contrasting many body ground state problems in one system where the conflicts appear due to the incompatible nature of the order parameters of its individual components. One of such existing experimentally accessible electronic hybrid systems is SC-FM based composite thin film (CF) with controllable parameters tuned by its composition. For an s-wave SC is in contact with a FM as in a CF, a modulation of the superconducting order parameter is the most pronounced effect which occurs mostly due to the proximity effect at the SC-FM interfaces, exchange interaction and stray fields originated from FM1. In addition, varieties of other interesting physical phenomena like coexistence of magnetism and superconductivity2, enhancement of superconductivity due to magnetic interaction3,4, domain wall superconductivity5,6, high critical current for power electronic application7, significant pinning enhancement due to the integration of FM particles into the SC matrix8,9, existence of long-range spin-polarized supercurrents10,11 etc. have been observed in SC-FM based hybrid systems. Besides, being real multicomponent percolating physical systems, CFs also offer to study the fundamental aspects of electronic, transport and magnetic properties of individual percolating networks and understand the quantum phase transitions12,13.
To construct the CFs, we employ one of the commonly explored rare-earth magnets, Gd, which has also been used to impact the superconducting properties while coupled to a superconductor14,15. As per the SC material is considered, Nb offers the highest critical temperature for an elemental superconductor. Combination of these two would possibly leads to one of the simplest selection of SC-FM based systems. Since 1960s, NbGd based hybrid systems in various geometries have been used to study the interplay between s-wave superconductivity in Nb and ferromagnetism mediated by 4f localized electrons in Gd8,16,17,18,19,20,21. Recently, we have demonstrated that phase slip processes can be triggered by introducing magnetic Gd particles into superconducting Nb matrices22. Here, we study the modulation of the superconducting properties together with an investigation for the existence of any characteristic magnetic properties in the limit of very dilute magnetic doping in NbGd based CFs.
The CFs were grown at room temperature with thicknesses in the range between 50 to 110 nm directly on Si (100) substrate. We observe a strong pair breaking effect induced by magnetic Gd and the modulation of the superconducting critical temperature Tc closely follows the AG theory related to the magnetic impurity induced pair breaking mechanism for an s-wave superconductor23. Our results clearly demonstrate that Gd is strongly detrimental to restoring the superconductivity in the CFs and a critical concentration (ccr) of about 1.3 at.% of Gd can completely destroy the superconductivity. This is in very much contrast to a recently reported result where the authors claimed to have superconductivity sustained for up to ~40 at.% of Gd incorporation with a Nb buffer layer (50 nm)8. To avoid any contribution from the buffer layer and hence to directly probe the superconducting properties of CFs we do not use any SC buffer layer. Furthermore, the present findings support some of the earlier works reporting no clear superconducting transitions for the CFs having Gd more than about 5 at.%18,24.
As a true interplay between SC and FM, the signatures of magnetism have been also observed by the paramagnetic Meissner effect (PME)25,26,27 in the temperature dependent DC magnetization measurements (M-T) for the CFs while only diamagnetic Meissner effect is observed in pure Nb films. With increasing Gd above the ccr, a paramagnetic transition occurs and the related transition temperature Tm behaves linearly with Gd concentration, c. Besides, we observe a non-trivial resistive-superconducting transition curve featured with several intermediate structures initiated and modulated by the Gd incorporation in R-T measurements. These distinct features modulate additively with the applied magnetic field. Thus even with a very dilute magnetic doping of less than 1at.%, the characteristics of magnetic properties are evident in the magnetization as well as in the transport measurements. Finally, we have constructed a compositional phase diagram where the region related to the PME is included in addition to the other phases and have established the magnetic phase diagram for varying composition.
Results
The X-ray diffraction (XRD) patterns of as-deposited CFs having different compositions are shown in Fig. 1(a). Pure Nb film shows a body-centered cubic (bcc) structure with lattice parameter, a = 3.31 Å. All the samples with relatively low c, the Gd concentration, up to 15 % reveal similar bcc patterns. With increasing c, the peak positions shift to lower 2θ values indicating an increase of the lattice parameter due to Gd inclusions. Further, for c ≥ 25 at.%, appearance of broad features, marked with rectangular blocks in Fig. 1, leads to either the presence of both cubic (fcc) and hexagonal phases of Gd8 or could be a signature of a typical amorphous solids as reported earlier24. Pure Gd yields a hexagonal close-packed (hcp) structure with lattice parameters, ahcp = 3.64 Å and chcp = 5.88 Å. Fig. 1(b) presents the variation of the lattice parameter a for the Nb-rich bcc state with c up to 40 %. The inclusion of Gd with larger metallic radius (1.87 Å) than that of Nb (1.43 Å) clearly influences and increases the lattice parameter of the Nb-rich bcc phase.
An atomic force microscope (AFM) is used to study the surface topography of the CFs. Figure 1(c–f) represents the morphological evolution of the CFs with increasing c. The morphology of a Nb film of about 100 nm thickness is shown in Fig. 1(c) while (d–f) of Fig. 1 represent the same for NbGd films grown in a single batch but having variation in Gd concentration. The changes in the grain size for different c-values are evident in the AFM images. The grain size for the Nb samples are about 20–30 nm as reported earlier also22 whereas, with increasing c the lateral size of the grains becomes larger and the grain boundaries get blunter. Further, it is visible that the grains start to merge and to form clusters type of morphology for higher concentration of Gd [Fig. 1(f)].
The temperature dependent resistance (R-T) measurements are carried out on CF based devices in conventional 4-terminal geometry. The Device geometry and the electrical connections are shown in the inset of Fig. 2(b). A set of normalized R-T curves with varying c are shown in Fig. 2(a). The resistance is normalized with the normal state resistance measured at 10 K. The superconducting transition temperature Tc is defined as the temperature corresponding to the maximum value of dR/dT and is shown by the dotted black vertical line for the device with c = 0.3 (the red curve). The black open squares in Fig. 2(a) present the R-T characteristic for a pure Nb film which shows a sharp transition with an extent of about 0.1 K in temperature and with a Tc ~ 8.85 K. With increasing c, the normal metal (NM) – superconductor transition curves move towards lower temperature. At c = 0.95, the resistance reduced to ~1 % of its normal state value. Further, the transitions get broader and hence an increase in transition width with increasing c as manifested in the R-T measurements. For c ≥ 1, the devices do not show a complete zero-resistance transition from its normal state down to the temperature limit of the measurement setup of ~2 K. Within this narrow range of Gd concentration we observe a crossover between superconducting to non-superconducting states as well as an obvious modulation of the superconducting transition width mediated by the magnetic contribution in the CFs.
The suppression of the Tc is consistent with the pair breaking picture introduced by Abrikosov and Gor’kov (AG) for an s-wave superconductor in the presence of magnetic impurities. As described by the AG theory23, the normalized Tc can be denoted as:
where, Tc0 is the critical temperature of pure Nb film, is the pair breaking parameter with τ as the quasi-particle lifetime controlled by the scattering from magnetic impurities . Assuming isotropic scattering in the limit of very low impurity, τ can be related to the impurity concentration c as28,29, where c is in at.%. ψ is the digamma function and can be expressed as,
In the limit of very dilute doping with equation (1) can be rewritten as,
Now from equation (3) if we neglect the quadratic term for a very low range of impurity concentration, a linear dependence is expected for the critical temperature to the impurity concentration. From equation (1) we note that for a critical value of α, αcr, Tc vanishes. This implies that the superconductivity can sustain up to a critical impurity concentration ccr.
To envisage experimentally the dependence of the Tc on c, we have extracted Tc values from each R-T data for ~30 samples varying in c. Each Tc is normalized by Tc0, the critical temperature of Nb and the normalized Tc is plotted against c in Fig. 2 (b). The black squares represent the experimental results whereas the red solid curve is a fit using equation (3). The black stars represent the Tc of measured samples showing partial/no transition down to 2 K. For these samples the Tc values are placed at the 0 K line in Fig. 2(b). The critical concentration ccr is considered at the base temperature of the measurement setup as indicated in Fig. 2(b) and is about 1.2 at.%.
As the Meissner effect is another hallmark of superconductivity we have verified the dependence of Tc on c through DC M-T measurements also. Figure 3(a) displays a set of M-T curves measured on CFs with different c values. The black squares represent the M-T behaviour of a Nb film with a Tc ~ 8.7 K as shown by the arrow in Fig. 3(a). Here, the Tc is defined as the temperature at which a CF starts to show negative magnetization. The measured Tc values for Nb from both R-T and M-T measurements are close to its bulk value (Tc0bulk = 9.2 K).
Similar to the R-T measurements, the M-T transition curves show a general trend to shift towards lower temperature with increasing c [Fig. 3(a)]. Likewise, we have extracted the Tc values from each M-T curves with different c and the related dependence is shown in Fig. 3(b). Up to a value of c ~1.4%, the variation of Tc on c follows an analogous trend as that is observed from R-T measurements in Fig. 2(b). A fit using equation (3) shown by the red curve in Fig. 3(b) follows closely to the experimental points in this range of c. However, above c ~1.4%, the diamagnetic transitions (black circles) occur irregularly for some of the samples and for the rest we observe no transition (black stars) and the related modulation in Tc with c is shown by the dotted curve in Fig. 3(b). A representative M-T curve is shown in the inset of Fig. 3(b) with c = 4.7% which is marked with pink dotted circular region in the main panel. Here, we observe a clear diamagnetic transition at ~6.2 K. However, the amplitude of the magnetization is ~50 times smaller than that for the samples presented in Fig. 3(a). This might be a weak transition originated locally through any percolated path but not through the whole sample and can be treated as an incomplete transition. Incomplete/partial transitions are observed in R-T measurements (Figure S3 in the supporting material) also for the devices with higher values of c.
It is apparent from the M-T and R-T measurements that the superconducting Tc collapses rapidly to the base temperature limit with increasing c from 0 to ~1.3 %. The close agreement between experimental results and the fit using the AG theory indicates the pair breaking mechanism induced by the magnetic doping as the origin of this suppression of superconductivity. The critical concentration ccr of Gd provides a crossover from superconducting to normal state in these CFs. Indeed, the values of ccr from the R-T (~1.2 % at 2 K) and M-T measurements (~1.4 % at 1.8 K) are very close.
It is clear that the magnetic doping is detrimental for the superconducting properties in the CFs and the Tc gets degraded with increased magnetic constituents. However, the detail mechanism behind the degradation of the superconductivity might be understood from the evolution of the SC-NM transition with the concentration of the FM part. To obtain an insight into the transition region of the R-T characteristics we display the R-T data shown in Fig. 2(a) in a semi-logarithmic scale in Fig. 4(a). As seen earlier, the Nb device adheres a sharp transition down to its complete superconducting state. In contrast, NbGd devices expose some distinct features described by kink/shoulder type of broadenings which get prominent with increasing c. The colored arrows in Fig. 4(a) indicate the formation of the features along with their evolution with increasing c. Hence, the question arises whether the featured kinks in the NbGd devices imply any trace of magnetism appearing from the Gd content.
Further, we emphasize a closer look onto the M-T data measured in both the field cooled (FC) and zero field cooled (ZFC) conditions for a few representative samples presented separately in Fig. 4(b). For clarity, we shifted the M-T curves in the y-direction with the order of increasing c values and the dotted baselines attached to each individual curve represent the zero-magnetization state obtained by subtracting the background magnetization. The bottom black circles represent the M-T measurements for a Nb sample with a Tc ~ 8.7 K. The similar behaviour is observed for the next sample (the red circles) while moving upward in Fig. 4(b) except for a very little fluctuation in the related FC data close to its Tc. Moving to the next sample in upward direction with a little higher c value (blue circles), we witness a very different behaviour in ZFC M-T characteristic which shows a crossover from a positive to negative magnetization while decreasing the temperature. Unlike the former two samples, the FC data for this sample shows a strong positive magnetization and the temperature Tm for the onset of positive magnetization appears to be the same at which the positive magnetization appears for the ZFC M-T data. This scenario is very similar to the paramagnetic Meissner effect (PME) observed in earlier studies30,31,32,33. We highlight the region of paramagnetic to diamagnetic transition by the orange dotted rectangular region in Fig. 4(b). With increasing c the PME is still observed for next couple of samples in Fig. 4(b), however, the amplitude of the paramagnetic signal gets reduced and the PME disappears for the sample with c = 1.3 %. From the M-T measurements with further increasing c, we mostly observe an onset of a positive magnetization and the related temperature Tm increases linearly with c. We note that due to a smaller paramagnetic signal, Tm values are not distinguishable from the background in the same scale for all the individual samples presented in Fig. 4(b). However, their individual data clearly exhibit the transition to paramagnetic state over the background signal (see Figure S4 in the supporting material).
There are two most common and well accepted arguments behind the PME, namely, the d-wave symmetry of quasiparticle pairing and the flux compression25. The former is not relevant in our case since we observe a strong suppression of Tc with the concentration of magnetic impurities indicating the SC is of s-wave symmetry as described in the AG theory23. The latter, i.e., the magnetic flux compression is possible due to the inhomogeneity present in these CFs34. The PME effect has been observed in SC-FM based hybrid systems where the effect is attributed to the flux compression due to spontaneous vortex formation35 and also to the interplay between SC and FM in the hybrids36. Recently, we also have shown that the magnetic doping may lead to the vortex formation22. Further, according to the Ginzburg-Landau (GL) theory, the presence of vortices inside a thin superconducting sample can cause the PME by the compression of the flux trapped inside the vortices37,38. The kink types of features in R-T characteristics [Fig. 4(a)] can be of support to the picture of vortex formation39 and hence the flux compression. However, for better understanding of the origin of the PME one needs to study the field dependence magnetization behaviour which is out of the scope of this study. Here, we emphasize that the traces of magnetism are evident in both the DC magnetization and the R-T measurements for these NbGd based CFs with less than 1 at.% of Gd in it.
For further support in favor of the signatures of the magnetic characteristics we have performed the R-T measurements under an external magnetic field applied perpendicular to the plane of the samples and their evolution with the B-field is presented in Fig. 5. Figure 5(a) shows a set of field dependent R-T measurements data for a Nb device. We observe a sharp transition from the resistive state to its superconducting state under low applied field with a reduced Tc for increased B-field. At relatively higher B-field, the sharpness of the transition gets distorted and it becomes wider. For example at B = 500 mT, the transition curve accompanies a kink type of structure (shown by an arrow) indicating an intermediate state possibly due to the vortex formation under the magnetic field for a type-II superconductor39. Thus the applied B-field above a threshold value causes similar types of features/kinks in the R-T characteristics for the Nb film as they appeared for the NbGd samples under no external field. The Field dependent R-T measurements are being carried out for NbGd composite devices also and the results for a few illustrative devices with c = 0.3, 0.5, 0.65 are presented in Fig. 5(b–d), respectively. In Fig. 5(b) with c = 0.3 and for the fields up to 100 mT, the transition curves look broader compared to that of the Nb device. However, this device with an applied field of about 200 mT facilitates the shouldering effect which was absent under no external field. At B = 200 mT, a small kink starts to appear in the transition characteristic and it gets prominent with increasing the field. Similar type of features appears for devices with higher values of c [Fig. 4(a)] under no external field as clearly manifested in Fig. 5(c,d). In addition to the broadening of the transition width with increasing c, the shouldering features are getting wider and stronger and they are observed to modulate in a similar fashion with the external field.
It is apparent from Fig. 4(a) and Fig. 5 that the kinks/shouldering features appeared in the R-T characteristics originate either from the magnetic particles embedded in the CF or from the external magnetic field suggesting their origin to be related with the magnetism. The features start to appear at higher field for the devices with lower c and vice versa. This is a clear indication that the applied field and the concentration of the magnetic counterpart in the CFs supplement each other. Hence it is straightforward that the magnetic component of the CFs generates an effective magnetic field which probably is originated from the exchange interaction and/or the stray field associated with the magnetic particles39. The magnetic contribution of Gd in the CFs is also evident by the appearance of positive magnetization in ZFC and the occurrence of the PME in the M-T measurements as shown in Fig. 4(b). Further, Nb is a type-II superconductor and the vortex states are expected to play an important role while studying the interaction between the superconductivity and the ferromagnetism in Nb-Gd based hybrid systems. The incorporation of magnetic Gd into the Nb matrix can lead to vortex state due to its internal field and also it can act as the pinning centers under an applied magnetic field. The shouldering type of features appearing in the R-T curves open up a possibility to have spontaneous vortices in the CFs having the Gd concentration above a threshold value. In this study, the features start to appear for c = 0.5% which could be the threshold value of c to observe the features at zero external B-field.
Discussion
Based on the detailed experimental investigations, we have formulated (i) a compositional phase diagram and (ii) a magnetic phase diagram for selected compositions. The dependence of the characteristic transition temperatures on the concentration of magnetic impurities leads to the compositional phase diagram as shown in Fig. 6(a). The black squares and the green circles represent the superconducting critical temperatures measured through R-T and M-T measurements, respectively. The red solid curve (in the left), representing the best fit to the experimental points using the AG theory, illustrates the phase boundary of the SC state (the shaded area in dark green). Above a certain minimum value of the Gd concentration, both the FC and ZFC M-T measurements show a positive magnetization indicating a paramagnetic phase of the CFs under consideration. The paramagnetic transition temperature Tm is the temperature related to the onset of the positive magnetization. The Tm is observed to depend linearly to the concentration of the magnetic component and the purple spheres in Fig. 6(a) represent the experimental values of Tm while the attached red curve in right is a linear fit. The region below this line in the phase diagram indicates the PM phase. However, For a few NbGd samples with c-values in the range of 0 < c < ccr, a crossover from paramagnetic to diamagnetic state has been observed in the ZFC M-T measurements while their M-T characteristics in FC condition show positive magnetization down to the measurement limit of 1.8 K [Fig. 4(b)]. This phenomenon is known as the PME. The yellow region, between the SC and the PM states illustrates the region related to the PME. The rest part of the phase diagram obviously represents the NM phase of the CFs. This is noteworthy to mention that the electronic states are very sensitive to the magnetic impurity as revealed in the phase diagram through the appearance of the PME region.
For constructing the magnetic phase diagram we have extracted the Tc values from the R-T measurements performed under externally applied magnetic field as previously shown in Fig. 5. For each device with particular c-values, we map the B-Tc phase diagram. Figure 6(b) contains a set of B-Tc phase diagram for a few representative samples with different c-values. The shaded areas represent the SC state while the solid lines connect the experimental values. The dotted lines are the extrapolations to the base temperature, 2K. We have used a gradient in the color for the shaded area to indicate the inclusion and variation of the magnetic constituent. The region of superconducting area in the phase diagram decreases with increasing c which is consistent with the pair breaking mechanism discussed previously. The experimental data along with their linear fits for the same set of devices are shown in Fig. 6(c). From the GL theory near the Tc, a linear dependence of Tc on the B-field is expected for a dirty superconductor40,41. We have extracted the Bc2(T*) value for each device at T* = T/Tc = 0.75 from the linear fit and its dependence on c is displayed in the left axis of Fig. 6(d). As expected, Bc2(T*) decreases with increasing c since the concentration of the magnetic part and the external magnetic field behave in a complimentary fashion. From the GL theory the coherence length ξGL(0) can be obtained by the slope of the linear fit of the B-Tc data as42,
Where, ϕ0 is the flux quantum. We have calculated the values of ξGL(0) for different Gd concentration in the range between 0 to 0.8 % and the related variation is shown by the red stars in Fig. 6(d). ξGL(0) increases with c and this is consistent with the dependence of Bc2 on c. However, with increasing c the mean free path gets reduced due to increased scattering and hence the coherence length should also be reduced42. Also note that the ξGL(0) for the Nb sample is much lower than that of a pure bulk Nb. This is because the Nb films were grown in the same chamber where NbGd samples were prepared and it is quite likely that our Nb films are in the dirty limit with a low residual resistivity (R300 K/R10 K ~ 2.78). Another reason could be the grain size of the Nb films which are in the range of 20–30 nm22. The similar value of the ξGL(0) has been reported for Nb with grain sizes ~20 nm43. Further, the enhancement of the ξGL(0) with Gd concentration is not only related to the grain size since at this low range of Gd concentration the variation in the grain sizes are not detectable from the AFM studies. The enhancement can be related to the interaction between SC and FM and further study is needed for clear understanding.
Finally, we have demonstrated a pronounced and controlled modulation of the superconducting properties in NbGd based CFs for Gd concentration in the range between 0 to 1.4 at.% by performing M-T and R-T measurements. A critical concentration of Gd ~ 1.3 at.% is found above which superconductivity disappears. Besides, the traces of magnetism with less than 1 at.% Gd in the CFs have been appeared evidently through the PME in M-T measurements and the shouldering effect in R-T measurements. However we do observe a non-monotonous oscillatory dependence of Tc on c from M-T measurements for the samples with c ≥ 1.4 at.%. With high c-value, diamagnetic transition can occur partially through any percolating path or due to in-homogeneities mediated by possible Gd clustering. Also the AFM images in Fig. 1(d–f) indicate of possible Gd clustering at high Gd concentration. There could be other effects like the formation of the triplet states originating from the interaction between SC and FM which could lead to an oscillatory behaviour in the Tc as reported earlier20. Nevertheless, the R-T measurements did not show similar behaviour except for the partial transitions (Figure S3 in the supporting material). Hence we can assume that the non-monotonous behaviour is related to the partial transition.
Methods
We fabricated NbGd based CFs by co-sputtering of Gd (99.95 %) and Nb (99.99 %) using an ultra-high vacuum (UHV) DC magnetron sputtering system. CFs are grown on Si (100) substrate with a top layer of 300 nm thick thermally oxidized SiO2 as the dielectric. The sputtering chamber was evacuated to less than 5 × 10−9 Torr before each deposition and the co-sputtering was performed in an Ar (99.9999 % purity) environment at about 3 x 10-3 mBar. The deposition rates for Nb and Gd were 3 Å/sec and 1–2 Å/sec, respectively. Apart from the determination of the sputtering rate, we had performed an extensive optimization process with respect to the relative position of the samples from the sputtering targets and the open area for the shutter of Gd target in order to obtain a gradient in the Gd concentration with respect to the relative position of the samples from the targets. Using this technique we have been able to manufacture samples with varying Gd concentration but keeping the Nb part unaltered from one single sputtering run. For different deposition runs we tried to maintain the relevant parameters very closely so that the results could be comparable from samples fabricated in different sputtering runs. On this context, we prepared 2 batches with thicknesses ~60 nm and ~110 nm, respectively and each batch contained 6 devices with variation in Gd concentration. Devices from both the batches follow the AG theory independently and the related ccr values remained very close (see the supporting material). This confirms that the devices prepared from different batches with similar conditions can be comparable.
We mainly prepared two types of samples, namely, CFs with dimensions 3.5 mm × 3.5 mm × 100 nm for DC M-T measurements and NbGd based patterned devices for transport studies. CFs, studied in this report, were grown at room temperature with thickness varying in the range of 50–110 nm. A Si capping layer of about 10 nm thickness was sputtered on top of the CFs for both types of samples to avoid any oxidation while exposed to the atmosphere. We employed shadow mask to fabricate multi-terminal devices for conventional 4-terminal transport measurements. Current and voltage leads were designed with Au (100 nm)/Ti (20 nm) layers followed by the fabrication of about 100 micron wide and about 1300 micron long channel of NbGd based CFs. Careful measurements were done for the estimation of the concentration by energy dispersive spectroscopy (EDS) analysis using a field emission scanning electron microscope by Zeiss. For each sample, EDS measurements were performed at 5–10 different places and the average value was considered for the analysis along with the uncertainty range estimated from the measured composition at different places. Structural characterization of CFs with varying c was done by grazing incidence X-ray diffraction (GIXRD) using a θ-2θ x-ray diffractometer (Philips X’pert pro X-ray diffractometer) with Cu-kα radiation operating at 40 kV and 20 mA and the morphological studies were performed by an atomic force microscopy (AFM). A SQUID magnetometer from Quantum Design was used to perform the M-T measurements. The transport measurements were carried out in a Physical Properties Measurement System (PPMS) by Quantum Design. The devices were mounted on a puck and soldered for the electrical measurements.
Additional Information
How to cite this article: Bawa, A. et al. Ultrasensitive interplay between ferromagnetism and superconductivity in NbGd composite thin films. Sci. Rep. 6, 18689; doi: 10.1038/srep18689 (2016).
References
Buzdin, A. I. Proximity effects in superconductor-ferromagnet heterostructures. Rev. Mod. Phys. 77, 935 (2005).
Aladyshkin, A. Y., Silhanek, A. V., Gillijns, W. & Moshchalkov, V. V. Nucleation of superconductivity and vortex matter in superconductor-ferromagnet hybrids. Supercond. Sci. Technol. 22, 053001 (2009).
Wei, T. C., Pekker, D., Rogachev, A., Bezryadin, A. & Goldbart, P. M. Enhancing superconductivity: Magnetic impurities and their quenching by magnetic fields. Europhys. Lett. 75, 943 (2006).
Stamopoulos, D., Pissas, M., Karanasos, V., Niarchos, D. & Panagiotopoulos, I. Influence of randomly distributed magnetic nanoparticles on surface superconductivity in Nb films. Phys. Rev. B 70, 054512 (2004).
Yang, Z., Lange, M., Volodin, A., Szymczak, R. & Moshchalkov, V. V. Domain-wall superconductivity in superconductor-ferromagnet hybrids. Nat. Mater. 3, 793 (2004).
Linder, J. & Halterman, K. Superconducting spintronics with magnetic domain walls. Phys. Rev. B 90, 104502 (2014).
Stamopoulos, D., Manios, E., Pissas, M. & Niarchos, D. Modulation of the properties of a low-Tc superconductor by anisotropic ferromagnetic particles. Physica C 437–38, 289 (2006).
Palau, A. et al. Hysteretic Vortex Pinning in Superconductor-Ferromagnet Nanocomposites. Phys. Rev. Lett. 98, 117003 (2007).
Togoulev, P. N., Suleimanov, N. M. & Conder, K. Pinning enhancement in MgB2-magnetic particles composites. Physica C 450, 45 (2006).
Bergeret, F. S., Volkov, A. F. & Efetov, K. B. Odd triplet superconductivity and related phenomena in superconductor-ferromagnet structures. Rev. Mod. Phys. 77, 1321 (2005).
Eschrig, M. Spin-polarized supercurrents for spintronics. Phys. Today 64, 43–49 (2011).
Strelniker, Y. M., Frydman, A. & Havlin, S. Percolation model for the superconductor-insulator transition in granular films. Phys. Rev. B 76, 224528 (2007).
Liu, X., Panguluri, R. P., Huang, Z.-F. & Nadgorny, B. Double Percolation Transition in Superconductor-Ferromagnet Nanocomposites. Phys. Rev. Lett. 104, 035701 (2010).
Matthias, B. T., Suhl, H. & Corenzwit, E. Spin Exchange in Superconductors. Phys. Rev. Lett. 1, 92 (1958).
Kim, H. et al. Effect of magnetic Gd impurities on the superconducting state of amorphous Mo-Ge thin films with different thickness and morphology. Phys. Rev. B 86, 024518 (2012).
Strunk, C., Sürgers, C., Paschen, U. & Löhneysen, H. v. Superconductivity in layered Nb/Gd films. Phys. Rev. B 49, 4053 (1994).
Koch, C. C. & Love, G. R. Superconductivity in Niobium Containing Ferromagnetic Gadolinium or Paramagnetic Yttrium Dispersions. J. Appl. Phys. 40, 3582 (1969).
Scholten, P. D. & Moulton, W. G. Effect of ion-implanted Gd on the superconducting properties of thin Nb films. Phys. Rev. B 15, 1318 (1977).
Strunk, C., Paschen, U., Surgers, C. & Vonlohneysen, H. Pair-breaking mechanisms in Nb/Gd/Nb films. Physica B 194, 2403 (1994).
Jiang, J. S., Davidović, D., Reich, D. H. & Chien, C. L. Oscillatory Superconducting Transition Temperature in Nb/Gd Multilayers. Phys. Rev. Lett. 74, 314 (1995).
Strunk, C., Surgers, C., Rohberg, K. & Vonlohneysen, H. Transition-temperature and critical fields of Nb/Gd layers Physica B 194, 2405 (1994).
Bawa, A., Jha, R. & Sahoo, S. Tailoring phase slip events through magnetic doping in superconductor-ferromagnet composite films. Sci. Rep. 5, 13459 (2015).
Abrikosov, A. A. & Gor’kov, L. P. Contribution to the theory of superconducting alloys with paramagnetic impurities. Sov. Phys. JETP 12, 1254 (1961).
Sommer, R. L., Xiao, J. Q. & Chien, C. L. Magnetic and magneto-transport properties of metastable GdxNb1-x alloys. IEEE Trans. Magn. 34, 1135 (1998).
Li, M. S. Paramagnetic Meissner effect and related dynamical phenomena. Phys. Rep. 376, 133 (2003).
Braunisch, W. et al. Paramagnetic Meissner effect in high-temperature superconductors. Phys. Rev. B 48, 4030 (1993).
Braunisch, W. et al. Paramagnetic Meissner effect in Bi high-temperature superconductors. Phys. Rev. Lett. 68, 1908 (1992).
Kim, Y.-J. & Overhauser, A. W. Theory of impure superconductors: Anderson versus Abrikosov and Gor’kov. Phys. Rev. B 47, 8025 (1993).
Powell, B. J. & McKenzie, R. H. Dependence of the superconducting transition temperature of organic molecular crystals on intrinsically nonmagnetic disorder: A signature of either unconventional superconductivity or the atypical formation of magnetic moments. Phys. Rev. B 69, 024519 (2004).
Fang, Y., Yazici, D., White, B. D. & Maple, M. B. Enhancement of superconductivity in La1−xSmxO0.5F0.5BiS2 . Phys. Rev. B 91, 064510 (2015).
Thompson, D. J., Minhaj, M. S. M., Wenger, L. E. & Chen, J. T. Observation of Paramagnetic Meissner Effect in Niobium Disks. Phys. Rev. Lett. 75, 529 (1995).
Yuan, S., Ren, L. & Li, F. Paramagnetic Meissner effect in Pb nanowire arrays. Phys. Rev. B 69, 092509 (2004).
Papadopoulou, E. L., Nordblad, P., Svedlindh, P., Schöneberger, R. & Gross, R. Magnetic Aging in Bi2Sr2CaCu2O8 Displaying the Paramagnetic Meissner Effect. Phys. Rev. Lett. 82, 173 (1999).
Das, P. et al. Surface superconductivity, positive field cooled magnetization and peak-effect phenomenon observed in a spherical single crystal of niobium. Phys. Rev. B 78, 214504 (2008).
Xing, Y. T., Micklitz, H., Baggio-Saitovitch, E. & Rappoport, T. G. Controlled switching between paramagnetic and diamagnetic Meissner effects in superconductor-ferromagnet Pb-Co nanocomposites. Phys. Rev. B 80, 224505 (2009).
López de la Torre, M. A. et al. Paramagnetic Meissner effect inYBa2Cu3O7/La0.7Ca0.3MnO3 superlattices. Phys. Rev. B 73, 052503 (2006).
Moshchalkov, V. V., Qiu, X. G. & Bruyndoncx, V. Paramagnetic Meissner effect from the self-consistent solution of the Ginzburg-Landau equations. Phys. Rev. B 55, 11793 (1997).
Zharkov, G. F. Paramagnetic Meissner effect in superconductors from self-consistent solution of Ginzburg-Landau equations. Phys. Rev. B 63, 214502 (2001).
Xing, Y. T. et al. Spontaneous vortex phases in superconductor-ferromagnet Pb-Co nanocomposite films. Phys. Rev. B 78, 224524 (2008).
Vicent, J. L., Hillenius, S. J. & Coleman, R. V. Critical-Field Enhancement and Reduced Dimensionality in Superconducting Layer Compounds. Phys. Rev. Lett. 44, 892 (1980).
Tinkham, M. Introduction to Superconductivity. 2nd edn, (McGraw-Hill, 1996).
Orlando, T. P., McNiff, E. J., Foner, S. & Beasley, M. R. Critical fields, Pauli paramagnetic limiting and material parameters of Nb3Sn and V3Si. Phy. Rev. B 19, 4545 (1979).
Bose, S., Raychaudhuri, P., Banerjee, R. & Ayyub, P. Upper critical field in nanostructured Nb: Competing effects of the reduction in density of states and the mean free path. Phys. Rev. B 74, 224502 (2006).
Acknowledgements
We thank Prof. R.C. Budhani for his fruitful discussions and we are thankful to Dr. Ranjana Mehrotra for her support in carrying out this work. We are indebted to Dr. K.K. Maurya for his support in carrying out the GIXRD characterization. The technical help for FESEM imaging, EDS characterization and thickness optimization using the central facilities at CSIR-NPL are highly acknowledged. We are thankful to Mr. M.B. Chhetri for his assistance in building the UHV sputtering unit. We gratefully acknowledge Dr. Sudhir Husale for critical reading of the manuscript and helping us with the invaluable discussions. We are thankful to Mr. Sachin Yadav and Mr. Bikash Gajar for their help and support during the revision of the manuscript. A.B. acknowledges financial support from CSIR-NPL for the research internship. The work was supported by CSIR network project ‘AQuaRIUS’ (Project No.: PSC 0110).
Author information
Authors and Affiliations
Contributions
A.B. and S.Sa. designed and fabricated the devices and participated in the measurements. A.G. performed the magnetization measurements in MPMS. S.Si. conducted the AFM measurements. V.P.S.A. participated in the transport measurements using PPMS. S.Sa. analyzed and interpreted the data and wrote the manuscript. All the authors read and reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Bawa, A., Gupta, A., Singh, S. et al. Ultrasensitive interplay between ferromagnetism and superconductivity in NbGd composite thin films. Sci Rep 6, 18689 (2016). https://doi.org/10.1038/srep18689
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep18689
This article is cited by
-
Effect of Gd magnetic impurities on the superconducting properties of highly disordered molybdenum nitride microstrips
Applied Physics A (2023)
-
A robust nitridation technique for fabrication of disordered superconducting TiN thin films featuring phase slip events
Scientific Reports (2021)
-
Substrate mediated nitridation of niobium into superconducting Nb2N thin films for phase slip study
Scientific Reports (2019)
-
Proximity-induced supercurrent through topological insulator based nanowires for quantum computation studies
Scientific Reports (2018)
-
Light Induced Electron-Phonon Scattering Mediated Resistive Switching in Nanostructured Nb Thin Film Superconductor
Scientific Reports (2017)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.