Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Silicon etching using only Oxygen at high temperature: An alternative approach to Si micro-machining on 150 mm Si wafers


Using a combination of low-pressure oxygen and high temperatures, isotropic and anisotropic silicon (Si) etch rates can be controlled up to ten micron per minute. By varying the process conditions, we show that the vertical-to-lateral etch rate ratio can be controlled from 1:1 isotropic etch to 1.8:1 anisotropic. This simple Si etching technique combines the main respective advantages of both wet and dry Si etching techniques such as fast Si etch rate, stiction-free and high etch rate uniformity across a wafer. In addition, this alternative O2-based Si etching technique has additional advantages not commonly associated with dry etchants such as avoiding the use of halogens and has no toxic by-products, which improves safety and simplifies waste disposal. Furthermore, this process also exhibits very high selectivity (>1000:1) with conventional hard masks such as silicon carbide, silicon dioxide and silicon nitride, enabling deep Si etching. In these initial studies, etch rates as high as 9.2 μm/min could be achieved at 1150 °C. Empirical estimation for the calculation of the etch rate as a function of the feature size and oxygen flow rate are presented and used as proof of concepts.


There are two main types of chemical-based Si wafer micromachining; isotropic and anisotropic silicon etching1,2. Isotropic etching is where the etch rates is identical for all crystal orientation and is well-suited for processes such as structure release etch as well as to remove the sacrificial Si wafer after its use as a deposition template or mechanical support for device fabrication, is no longer needed1. Anisotropic etching is where the etch rates is dependent upon the crystal orientation of the etch direction. Anisotropic etching of Si is typically used when dimension control of the etching is critical, such as for formation of high aspect ratio features, deep Si trenches, or to exploit the anisotropy to precisely create specific patterns on wafers of particular crystal orientation, such as V grooves structures on Si(100) substrates2. Isotropic and anisotropic etching of Si have both wet and dry etching options, each with their own advantages and disadvantages. Wet etchants such as hydrofluoric:nitric:acetic acids (HNA) and potassium hydroxide (KOH) solutions are typically used for isotropic and anisotropic etching of Si, respectively2. While wet etchants are attractive due to the relatively simple setup requirements, they can suffer from drawbacks such as stiction, the handling of hazardous/toxic chemicals and expensive waste disposal management. Wet etching can also induce mechanical damage to the structures from liquid agitation and/or wafer drying processes that lead to yield and reliability variations2,3. The effect of stiction is particularly undesirable for the fabrication of micro-electromechanical systems (MEMS) as the thin structures can literally “stick” to the substrate, preventing safe release or operation.

On the other hand, common dry etchants such as xenon difluoride (XeF2), sulfur hexafluoride (SF6) alone or in combination with fluorocarbons (CxFx) (SF6 + CxFx), do not suffer from the detrimental stiction effect and can be easily calibrated and automated2,4. XeF2 is preferred over SF6 for isotropic etching of Si as XeF2 is a plasma-less process, whereas SF6 is a plasma process. A plasma-less process means that the etching gas is spontaneously reactive, whereas a plasma process requires external excitation to create reactive species, which requires additional costs to implement. By alternating CxFx with SF6, the etching turns from isotropic to anisotropic Si etching as at each cycle one alternates between sidewall passivation (with CxFx) and trench etching with SF6 (ie. the so-called Bosch process)5. SF6 + CxFx is currently preferred for anisotropic Si etching due to its ability to form extremely high aspect ratio trenches (with sidewall angle close to 90°)2, as there is currently no other alternative processes available that can achieve such characteristics. However, SF6 is a potent greenhouse gas6 and creates a toxic byproduct upon reaction with Si (ie. silicon tetrafluoride7). In addition, operating with dry etchants is usually more complex than wet etching and requires expensive equipment and the use of hazardous gas, which therefore requires appropriate waste abatement and disposal systems to be installed and maintained.

Ideally, the perfect Si etchant would be an etchant that does not cause additional damage to the wafer being processed, etch only in the pre-determined locations, has simple setup requirements, high etch rates and good uniformity over the entire wafer, high selectivity to common mask materials, uses easy-to-dispose chemicals and does not create environmental-unfriendly/toxic by-products. With these objectives in mind, we present here an alternative Si micromachining method using only oxygen (O2) at high temperatures. This process meets many of the aforementioned properties as we will show in this paper.

Most studies of the reaction of oxygen with Si are primarily focused on the oxidation of Si for the purpose of converting the Si surface (after initially lightly etching the Si) into silicon dioxide (SiO2)8,9. Two possible outcomes may occur upon reaction of Si with O2: Si etching via reaction (1) 2Si + O2(g) → 2SiO(g), or Si oxidation via reaction (2) Si + O2(g) → SiO2(s). More details on this mechanism are available in a thorough study by Smith and Ghidini10. At high temperatures and low oxygen partial pressures, Si reacts with O2 to form the volatile gas silicon monoxide (SiO) (reaction (1))8. Conversely, at high temperatures and high partial pressures, solid silicon dioxide (SiO2) is formed on the exposed Si surface instead8 (reaction (2)). While both processes etch the Si substrate to some degree, only reaction (1) will enable continual etching of Si as reaction (2) is self-limiting since the SiO2 formation rate reduces over time due to increasing difficulty for O2 to diffuse through the thick SiO2. Therefore we have optimised process parameters to favour reaction (1), enabling deep Si etching and therefore achieve controllable Si micro-machining.

In this paper, O2 etching of Si was optimised for Si micro-machining. It is demonstrated that this Si etching technique provides fast and uniform etching of large Si wafers and is compatible with multi-wafer batch processing. Furthermore, it is shown that isotropic and anisotropic etching can be obtained based on process conditions. In addition, this process is inherently stiction-free (being a dry etchant) and is safer than toxic halogen based dry etchants and so does not require expensive waste management systems. The main advantages and disadvantages of common Si etching techniques compared to our O2 based Si etching technique are summarised in Supplementary Table S11,2,5,11.

Here, we report the initial results of using this alternative Si etching technique with three different hard masks: silicon carbide (SiC), SiO2 and silicon nitride (SiN) thin films. As proof of concepts, we will also demonstrate the fabrication of single crystal SiC-based diaphragms, of MEMS-like structures and long Si stripes mimicking photonic waveguide structures. To the best of our knowledge, no such etching method (deep Si etching using only O2 at high temperatures for Si micro-machining) has been reported to date. Thanks to its many advantages, we believe that this alternative Si etching technique can become an attractive Si micro-machining process for a broad range of applications including MEMS and silicon photonics.

Results and Discussion

By increasing the etch temperature from 1100 °C to 1200 °C at an O2 flow rate of 20 sccm, the etch rate increased by 63% (from 1.9 μm/min to 3.1 μm/min). Importantly, etching at 1150 °C gives a reasonable etch rate (2.7 μm/min) and implies that a custom-built O2 etching equipment can use electronic grade quartz (maximum temperature ~1160 °C) in its construction. Hence 1150 °C is the etch temperature used for subsequent studies.

An Arrhenius plot displayed on Fig. 1 and plotting the etch rate versus inverse temperature (1/T) yields an activation energy of 0.86 eV for O2 etching, higher than the activation energy of Si(100) etching using XeF2 (0.26 eV above 410 K)4. A higher activation energy with O2 etching is expected in this process since the O2 molecules are converted into reactive O species at high temperatures10, whereas XeF2 is highly reactive at much lower temperatures2. The higher temperatures required for O2 etching of Si is therefore consistent with the higher activation energy. The etching behaviours for subsequent sections are examined in terms of etch rate, anisotropy, uniformity and mask selectivity.

Figure 1

Arrhenius plot showing the etch rate measured on a 600 μm wide square after etching with 20 sccm O2 at 1100 °C to 1200 °C.

The dash line indicates a linear least squares fit, with an adjusted coefficient of determination R2 of 0.87.

Firstly, we examine the effect of O2 flow rate on the Si etch rate. Due to the high aspect ratio of the test patterns, the vertical and lateral etch rates at various O2 flow rate were measured and compared using a combination of optical microscopy (OM) and scanning electron microscopy (SEM) imaging. Lateral and vertical etch rate results at various O2 flow rates are plotted on Fig. 2. They were found to be fairly similar for a flow rate of 10 sccm O2 at 1150 °C (ie. isotropic etching), but anisotropic outside 10 sccm O2, as shown in Fig. 2(a). However, Fig. 2(b) shows that both the vertical and lateral etch rates increase at a quasi-linear rate with O2 flow rate and so the saturation in the vertical-to-lateral etch rate ratio is not due to a vertical etch rate saturation at high O2 flow rates (>50 sccm).

Figure 2

(a) Ratio between the vertical and lateral etch rates as a function of O2 flow rates. The dashed line is a line guide to the eye. (b) Average vertical and lateral etch rates as a function of O2 flow rates. The error bars both (a,b) indicate the range of etch rates measured for all the different square opening widths at a given O2 flow rate. Dashed lines indicate least squares fit to a linear function for the plot in (b). All experiments were performed at 1150 °C with epitaxial SiC masks.

The anisotropic etching behaviours at different O2 flow rates is currently under investigation but might be related to various competing mechanisms such as chemisorption, surface diffusion, transition from molecular to viscous flow and changes to O2 sticking coefficients. A detailed study will be reported in another manuscript. Similar anisotropic behaviour has also been observed in XeF2 etching, where the degree of anisotropic was found to be dependent on exposed Si area, XeF2 charge pressure and number of etch cycles12. However, due to the approximately 3–4 orders of magnitudes pressure difference for XeF2 operation (~4 Torr operation pressure) compared to this O2 etching (10−3 to 10−4 Torr operation pressure), the anisotropy mechanism cannot be identical. For example, etch rate anisotropy in XeF2 is shown to be primarily caused by a short mean-free-path of ~20 μm13, but the mean-free-path during O2 etching operation is in the centimetre to metre range.

Nevertheless, Fig. 2(b) show that the general trend is that higher O2 flow rates leads to higher etch rates. The higher etch rate at higher O2 flow rates is expected as more O atoms are available for etching. The vertical etch rates achieved varied between ~0.7 to 9.2 μm/min for O2 flow rates from 5 to 100 sccm at 1150 °C, much faster than the typical reported wafer-level etch rates12 of 0.2–0.5 μm/min with XeF2 and is comparable with typical HNA and KOH14 etch rates (microns per minute). The 9.2 μm/min etch rate with O2 etching at 100 sccm O2 is also comparable with high etch rate, microwave enhanced KOH etching of ~10 μm/min14. It is worthwhile noting that etch rate is limited here by our equipment and that higher etch rate is expected for higher O2 flow rate, i.e higher O2 pressure. This illustrates that O2 etching combines advantage of fast etch rates of HNA with the stiction-free etching of dry etchants. Furthermore, an important issue with XeF2 etching is that the etch rate varies over the etching time. One cause of this is due to self-heating of the substrate during etching, which result in decreasing etch rates as etch time increases for etch temperatures below 400 K4,15. Another cause is due to increasing difficulty for XeF2 to diffuse into a cavity as its depth increases12. To evaluate this possible issue with the O2 etching, we compared two etching runs done at 1150 °C using 10 sccm O2 with etch times of 30 mins and 75 mins respectively and found that the etch rates were identical. This implies that O2 etching does not suffer from time-dependent etch rate changes as typically seen in XeF2 etching.

The variations in lateral etch rates as a function of mask opening area is plotted in Fig. 3. It was found that the experimental etch rates are well fitted by an empirical power law function given in Eq. (1), where ER is the lateral etch rate in μm/min, area is the mask opening area in μm2 and a,b and c are fitting variables that depend on the O2 flow rate (or partial pressure) (sccm) and etch tool design. The adjusted coefficient of determination R2 values are calculated to range between 0.89 and 0.99 for all power law function fits (see Fig. 3). The vertical etch rate can be deduced from the vertical-to-lateral etch rate ratio shown in Fig. 2(a).

Figure 3

Effect of the mask opening area on the lateral etch rate for Si(100) at different O2 flow rates.

The etch temperature was 1150 °C. The dashed lines represent a fit to an empirical power law function. The measurement error is at most 5%, based on the resolution of the optical microscope.

The etch rate variation is more pronounced for smaller feature areas, especially at high O2 flow rates, whereas the etch rate is mostly constant for larger features (>30 × 103 μm2). Such area dependent etch rate has also been observed with XeF2 etch process and is linked to the so-called microloading effect16. This effect occurs due to the diffusion-limited nature of etching and hence a small mask aperture results in less volume of reactants able to diffuse through the opening and etch the underlying Si substrate. In addition, the etch rate variation for different feature sizes is minimal at lower O2 flow rates (<10 sccm) or for large features (>30 × 103 μm2) at any O2 flow rate. Similarly, Sugano et al.17. have previously reported that a lower supply of XeF2 resulted in reduced etch rate variations with changes in feature size. Xu et al.12. have also reported that size dependent etch rate is minimised for large features, similar to that observed in Fig. 3. Appropriate design rules, similar to those created to handle the microloading effect in reactive ion etching (RIE)18 and XeF2 etching12, can be developed to overcome or even exploit this microloading effect, as in the case of RIE18. The etching behaviour as fitted by Eq. (1) can be used to assist in creating appropriate design rules.

In addition to the observation of O2 flow rates dependent microloading effects, we have also observed lateral etch rate anisotropy depending on the O2 flow rate. Figure 4 shows that the etch front faceting also varies depending on the O2 flow rate. For O2 flow rates of 30 sccm and below the under-etch region appears as a multi-sided polygon, direct evidence of an anisotropic etching. At O2 flow rate of 40 sccm and above, the number of sides reduces such that it is mostly a square with rounded corner, which better mirrors the original square opening.

Figure 4

Optical microscopy images of 80 μm square mask openings after etching at 1150 °C under O2 flow rates of (a) 5, (b) 10, (c) 20, (d) 30, (e) 40, (f) 50, (g) 80 and (h) 100 sccm. The mask is SiC and the substrate is Si(100). The etch time varies between 7.5 and 75 mins. Scale bar is shared. White arrows indicate examples of facets. The etch depth depends on the O2 flow rate and is given by Fig. 2. The etch depth for these features range from 40 μm to 94 μm deep.

For a passivated Si surfaces, Si voids have been known to spontaneously form after annealing the Si at high temperatures19. The formation of voids has been attributed to Si out-diffusion from the Si substrate due to Si vacancy diffusion and aggregating into larger Si voids20. The Si voids formed due to high temperatures are typically quite small and are at most tens of nm wide for every minute of annealing at 1100 °C19. In our O2 etching process, the void formation is controlled as the Si is only exposed in the mask openings and protected elsewhere by the mask. With the addition of O2, the Si void formation is accelerated through formation of volatile oxides (SiO) via reaction of O atoms with Si surface dangling bonds, in addition to the spontaneous void formation purely due to high temperatures, resulting in several orders of magnitudes difference in Si void formation and hence higher Si etch rates.

Figure 5 shows examples of cross-sectional SEM micrographs of Si that have been etched with 10 and 100 sccm O2 at 1150 °C, with a mask opening of 10 μm wide. The shape of the etched Si depends on the O2 flow rate, consistent with observation of lateral etch rate anisotropy in Fig. 4. The similarity in etched Si profile between Figure 5(a,b) confirm that that the etch profile depends on the O2 flow rate, as the specific profile only expands and not change shape, with a longer etch time. The appearance of several intermediate high indices, fast etching planes prior to being eventually bounded by the slowest etching planes has previously been observed in KOH etching of Si21. The difference between etch rates of the different planes have also been found to be dependent on the KOH concentration21. As the lateral etch rate anisotropy gradually reduces at higher O2 flow rates, the mechanism for facet formation is likely related to the supply of O atoms and available Si bonds for etching, behaving in a similar manner to KOH etching. The detailed physical process involved in lateral etch anisotropy formation mechanism is currently under investigation and will be reported in a later manuscript.

Figure 5

Cross-sectional SEM micrographs Si trenches formed from 10 μm wide mask openings after etching at 1150 °C under O2 flow rates of (a) 10 sccm for 30 mins, (b) 10 sccm for 75 mins and (c) 100 sccm for 7.5 mins. The mask is SiC and the substrate is Si(100).

However, in applications such as structure release and through-Si etch applications, faceting is not an issue. The faceting is also negligible when comparing it with the large features (channels may be centimetres long) that are typically used for microfluidic applications.

We have also observed that the O2 flow rate affects the etched Si surface roughness. Smooth etched Si surfaces appear as a bright, white colour and appear featureless under OM (cf. Fig. 6(g)). Figure 6 shows that from 80 sccm O2, the etched Si is rough and can be observed under OM, through appearance of grainy black coloured trenches due to light scattering from the rough surface (cf. Fig. 6(h)). Kosolobov et al.9 and Ross et al.22 have previously reported that low pressure oxygen etching of Si at high temperatures proceed in a step-flow mode, analogous to high quality thin film epitaxy. The roughness at high O2 flow rates may arise from insufficient surface atom diffusion, similar to the situation that occurs in thin film depositions where surface atoms diffusion is limited by high adatom arrival rates. Essentially at low O2 flow rates, the Si is removed monolayer-by-monolayer, preserving the smooth Si surface. However at high O2 flow rates, Si is unevenly removed and results in rough etched Si surfaces.

Figure 6

Optical microscopy images of 100 μm wide openings, 200 μm apart and 1 mm long, after etching in (a) 5, (b) 10, (c) 20, (d) 50, (e) 80 and (f) 100 sccm O2 at 1150 °C. Higher magnification, Normaski images of the Si trenches etched with (g) 10 and (h) 100 sccm O2 at 1150 °C. The mask is SiC and the substrate is Si(100). The etching time varies between 7.5 mins to 75 mins. Total Si lateral etch is similar for all O2 flow rates. Scale bar is shared for (a) to (f). The etch depth depends on the O2 flow rate and is given by Fig. 2. The etch depth for these features range from 48 μm to 84 μm deep. No clear SiC mask edges are observable in (g) and (h) due the difference in height between the bottom of the etched Si trench and the top of the SiC mask.

Another important characteristic of an etchant is its cross wafer etch uniformity, as high yield is important for large-scale manufacture. A patterned SiC mask with multiple duplicates of 100 μm wide, 1 mm long apertures spaced 4.5 mm apart across a 150 mm Si wafer, resulting in ~40% exposed Si area, was used to investigate the etch uniformity across the wafer for the etch parameter of O2 flow rate of 10 sccm at 1150 °C for 30 minutes. The etch rate was found to be highly uniform across the wafer for a given aperture size, with an average etch rate non-uniformity of 4% (Fig. 7). Furthermore, a two-inch wafer patterned with the same features (~23% exposed Si area) was also loaded during the same etching run. The etch rates between the 50.8 mm and 150 mm wafer had a difference of only 4%. It is estimated that approximately 10% of O2 atoms are consumed when etching 23% of a two-inch wafer using an O2 flow rate of 10 sccm, which is consistent with observation of minimal loading effects with multi-wafer runs. The consistent etch rate across the wafer and for multi-wafers is important for process control in manufacturing to enable high device yield.

Figure 7

Etch rate deviation of multiple 100 μm wide, 1 mm long apertures spaced 4.5 mm apart across a 150 mm Si wafers etched with an O2 flow rate of 10 sccm at 1150 °C for 30 mins.

The average etch rate is 1.23 μm/min.

Following on the theme of manufacturability, another important characteristic is mask selectivity. Mask materials consisting of SiO2, SiN and SiC were heated at 1150 °C under several different O2 flow rates and etch times. For all the tests, no mask degradation was observed under optical microscope. The selectivity is estimated to be greater than 1000:1 for all the samples which is more than sufficient for deep Si etch applications. This demonstrates that O2 etching is compatible with the common hard mask materials used for dry etching.

To demonstrate the capabilities of this new Si etching technique, we fabricated several building blocks typically found in Si-based applications such as MEMS and Si photonics (see Fig. 8). Firstly, we fabricated simple SiC cantilevers on a Si substrate (see Fig. 8(a)), which is a typical building block for MEMS2. The scanning electron microscope in Fig. 8(a) shows that the etched area is relatively smooth after 15 min etching using 5 sccm O2, unlike those typically seen after XeF2 etching, where the roughness is clearly visible under SEM3,12,17. The SiC cantilevers are also intact with no observable feature deformations. Next, we demonstrate fabrication of SiC bridges on a Si substrate, which mimics suspended SiC optical waveguides11. The bridges (Fig. 8(b)) show no obvious deformations and a smooth Si surface, indicating suitability as a building block for SiC-based Si photonics devices. Subsequently, we demonstrate formation of SiC diaphragms, which can be used as pressure sensor23. Figure 8(c) shows an array of 500 nm-thick SiC diaphragms that are ~8 mm in diameter formed from etching through the Si substrate from the backside. All SiC diaphragms survive the O2 etching process, leaving transparent SiC windows on the Si substrate. These examples show and ascertain the potential that O2 etching is suitable for creating a variety of structures for a broad range of applications.

Figure 8

(a) Scanning electron microscopy image of SiC cantilevers after etching underlying Si with 5 sccm O2 for 15 mins at 1150 °C (Etch depth ~ 9 μm). (b) Scanning electron microscopy image of suspended SiC bridges on Si. The SiC bridges are 25 μm wide and 1 mm (Etch depth ~ 44 μm). (c) Multiple 8 mm diameter etch-through openings evenly spaced across a 150 mm Si wafer that have been coated with 500 nm SiC. This wafer has been etched at 1150 °C for 4 hours at 50 sccm O2. The Si wafer thickness is 675 μm. All transparent SiC windows indicate areas where the Si has been completely etched away, leaving just the 500 nm SiC thin film.


A novel technique for deep etching of Si using pure O2 at high temperature is introduced and used to successfully demonstrate a variety of micron-scale structures. Effects of the etch temperature, O2 flow rate and mask aperture were investigated. Higher temperatures and higher O2 flow rates result in higher Si etch rates, although smooth etched Si surfaces is achieved only for O2 flow rates below 50 sccm. Vertical-to-lateral etch rate ratio varies depending on the O2 flow rate, with it being completely isotropic at 10 sccm O2. An interesting observation was that the lateral etch rate anisotropy can be controlled from anisotropic to isotropic by varying the O2 flow rate, with the transition to isotropic occurring at 30 sccm. High etch rate and high quality (smooth) etched Si surface coupled with the elimination of halogens (improves safety) and eliminating chemical waste hazards achieved in this initial study shows great potential for its use in large scale manufacturing.


Preparation of test wafers

2 inch and 150 mm Si(100) substrates were first coated on both sides with a thin film for etch mask purpose and consist of either ~300 nm thick single-crystal SiC using a customised low-pressure chemical vapour deposition (LP-CVD) tool24, ~100 nm thick SiN by reactive sputtering, or 100 to 1000 nm thick SiO2 formed either by using LP-CVD from SiH4 and O2 at 440 °C or thermally grown in a furnace by dry oxidation at 1000 °C. These three hard masks were tested for compatibility for this Si etching process but only the SiC mask was used for these studies for convenience as we had many SiC coated Si wafers already fabricated. Photoresist was then spin-coated onto the mask layers and then patterned using standard UV photolithography techniques, followed by dry etching to transfer the features of various shapes and dimensions between 2 to 600 μm wide and up to 1 mm long into the hard mask. The two inch wafers had an exposed Si area of approximately 23% and the 150 mm wafers had between 15% and 40% exposed Si areas.

O2 etching of test wafers

Si etching was performed using the same LP-CVD system used for the SiC thin film deposition24. Due to the batch reactor nature of this LP-CVD system, between two to four two-inch patterned wafers can be loaded at the same time. The samples were heated up to either 1100 °C, 1150 °C or 1200 °C and then exposed to oxygen flows varying from 5 to 100 sccm (maximum flow possible) and for different etch times, transferring the various patterns into the Si substrates. After etching, the samples were cooled down to room-temperature in vacuum.

Etched wafers characterisations

The lateral and vertical etch rate of the O2 etched samples were measured using an Olympus MX50 optical microscope (OM), a Jeol JSM-6510LV scanning electron microscope (SEM) and a Dektak 150 profilometer. The etch depth was determined using OM, SEM or a Dektak profilometer. Although OM measurements correlated to Dektak measurements for shallow etch depths, it should be noted that Dektak measurements were found to be unreliable for the narrower opening widths due to the difficulty for the relatively large stylus to reach the bottom of trenches which can be up to 100 μm deep. Hence OM was the predominant technique used to measure the etch depth. The lateral etch front anisotropy is studied using the OM. The etched Si roughness was evaluated using the OM and SEM. The mask selectivity was determined by measuring the mask thickness change before and after O2 etching using a Nanometrics Nanospec AFT 210 reflectometer.

Additional Information

How to cite this article: Chai, J. et al. Silicon etching using only Oxygen at high temperature: An alternative approach to Si micro-machining on 150 mm Si wafers. Sci. Rep. 5, 17811; doi: 10.1038/srep17811 (2015).


  1. Janse, H., Gardeniers, H., Ber, M. d., Elwenspoek, M. & Fluitman, J. A survey on the reactive ion etching of silicon in microtechnology. J. Micromech. Microeng. 6, 14 (1996).

    ADS  Article  Google Scholar 

  2. Kovacs, G. T., Maluf, N. I. & Petersen, K. E. Bulk micromachining of silicon. Proc. IEEE 86, 1536–1551 (1998).

    CAS  Article  Google Scholar 

  3. Easter, C. & O’Neal, C. B. Characterization of High-Pressure Vapor-Phase Silicon Etching for MEMS Processing. J. MEMS 18, 1054–1061 (2009).

    CAS  Article  Google Scholar 

  4. Williams, K. R. & Muller, R. S. Etch rates for micromachining processing. J. MEMS 5, 256–269 (1996).

    CAS  Article  Google Scholar 

  5. Laermer, F. & Schilp, A. Method of anisotropically etching silicon. USA patent US005501893A (1996).

  6. Dervos, C. T. & Vassiliou, P. Sulfur hexafluoride (SF6): Global environmental effects and toxic byproduct formation. J. Air Waste Manage. Assoc. 50, 137–141 (2000).

    CAS  Article  Google Scholar 

  7. Flamm, D. L. Mechanisms of silicon etching in fluorine-and chlorine-containing plasmas. Pure Appl. Chem. 62, 1709–1720 (1990).

    CAS  Article  Google Scholar 

  8. Lander, J. J. & Morrison, J. Low Voltage Electron Diffraction Study of the Oxidation and Reduction of Silicon. J. Appl. Phys. 33, 2089–2092 (1962).

    CAS  ADS  Article  Google Scholar 

  9. Kosolobov, S. S., Aseev, A. L. & Latyshev, A. V. In situ study of the interaction of oxygen with the Si(111) surface by ultrahigh-vacuum reflection electron microscopy. Semiconductors 35, 1038–1044 (2001).

    CAS  ADS  Article  Google Scholar 

  10. Smith, F. & Ghidini, G. Reaction of oxygen with Si (111) and (100): critical conditions for the growth of SiO2 . J. Electrochem. Soc. 129, 1300–1306 (1982).

    CAS  Article  Google Scholar 

  11. Vonsovici, A., Reed, G. T. & Evans, A. G. R. beta-SiC-on insulator waveguide structures for modulators and sensor systems. Mater. Sci. Semicond. Process. 3, 367–374 (2000).

    CAS  Article  Google Scholar 

  12. Xu, D. et al. Isotropic Silicon Etching With Gas for Wafer-Level Micromachining Applications. J. MEMS 21, 1436–1444 (2012).

    CAS  Article  Google Scholar 

  13. Bahreyni, B. & Shafai, C. Investigation and simulation of XeF2 isotropic etching of silicon. Journal of Vacuum Science & Technology a-Vacuum Surfaces and Films 20, 1850–1854 (2002).

    CAS  ADS  Article  Google Scholar 

  14. Walczak, R. & Dziuban, J. Fast wet anisotropic etching of silicon utilizing microwave treatment of KOH etchant. Meas. Sci. Technol. 17, 38 (2006).

    CAS  ADS  Article  Google Scholar 

  15. Chang, F. I. et al. Gas-phase silicon micromachining with xenon difluoride. Vol. 2641 [117–128] (Spie - Int Soc Optical Engineering, Bellingham, 1995).

  16. Madou, M. J. Fundamentals of Microfabrication: The Science of Miniaturization. Second edn, [107–108] (Taylor & Francis, 2002).

  17. Sugano, K. & Tabata, O. Effects of aperture size and pressure on XeF2 etching of silicon. Microsys. Technol. 9, 11–16 (2002).

    Article  Google Scholar 

  18. Bourouina, T., Masuzawa, T. & Fujita, H. The MEMSNAS process: microloading effect for micromachining 3-D structures of nearly all shapes. J. MEMS 13, 190–199 (2004).

    Article  Google Scholar 

  19. Kim, K. C., Park, C. I., Roh, J. I., Nahm, K. S. & Seo, Y. H. Formation mechanism of interfacial voids in the growth of SiC films on Si substrates. Journal of Vacuum Science & Technology A 19, 2636–2641 (2001).

    CAS  ADS  Article  Google Scholar 

  20. Jinschek, J., Kaiser, U. & Richter, W. Different void shapes in Si at the SiC thin film/Si(111) substrate interface. Journal of Electron Microscopy 50, 3–8 (2001).

    CAS  Article  Google Scholar 

  21. Pal, P., Sato, K. & Chandra, S. Fabrication techniques of convex corners in a (1 0 0)-silicon wafer using bulk micromachining: a review. J. Micromech. Microeng. 17, R111 (2007).

    CAS  ADS  Article  Google Scholar 

  22. Ross, F. M. & Gibson, J. M. The Etching of Silicon by Oxygen Observed by in situ Tem. Mater. Res. Soc. Symp. Proc. 222, 219 (1991).

    CAS  Article  Google Scholar 

  23. Young, D. J., Du, J. G., Zorman, C. A. & Ko, W. H. High-temperature single-crystal 3C-SiC capacitive pressure sensor. IEEE Sens. J. 4, 464–470 (2004).

    CAS  ADS  Article  Google Scholar 

  24. Wang, L. et al. Misorientation dependent epilayer tilting and stress distribution in heteroepitaxially grown silicon carbide on silicon (111) substrate. Thin Solid Films 564, 39–44 (2014).

    CAS  ADS  Article  Google Scholar 

Download references


This work was partly funded by the Queensland State Government grant entitled “Semiconductor Microfabrication Program”. This work was performed at the QMF - Queensland Node of the Australian National Fabrication Facility. A company established under the National Collaborative Research Infrastructure Strategy to provide nano- and microfabrication facilities for Australia’s researchers.

Author information




J.C. wrote the main manuscript text and prepared the figures. J.C, G.W. and A.I. designed the experiments and interpreted the data. J.C., L.W., G.W., K.C. and L.H. prepared the samples and conducted the O2 etching experiments. D.M. and S.H.T. assisted with interpretation of the results and structuring of the manuscript. All authors reviewed the manuscript.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Electronic supplementary material

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Chai, J., Walker, G., Wang, L. et al. Silicon etching using only Oxygen at high temperature: An alternative approach to Si micro-machining on 150 mm Si wafers. Sci Rep 5, 17811 (2016).

Download citation


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links