In many technical applications crystallization proceeds in the presence of stresses and flows, hence the importance to understand the crystallization mechanism in simple situations. We employ molecular dynamics simulations to study the crystallization kinetics of a nearly hard sphere liquid that is weakly sheared. We demonstrate that shear flow both enhances and suppresses the crystallization kinetics of hard spheres. The effect of shear depends on the quiescent mechanism: suppression in the activated regime and enhancement in the diffusion-limited regime for small strain rates. At higher strain rates crystallization again becomes an activated process even at densities close to the glass transition.
The making of a material is a process that often involves phase transformations. How a material transforms from one stable phase to another has wide-spread consequences: for technological applications such as metal alloys1, colloids2,3,4 and the graphite-diamond transition of carbon5; but also for the nucleation of ice in clouds6 affecting our climate. Phase transformations have been studied primarily after a sudden change of thermodynamic conditions but with dynamics that obey detailed balance. More realistically however, such transformations proceed away from thermal equilibrium and in the presence of external mechanical stresses and flows, for example when preparing colloidal crystals through spin-coating7. To study the basic physical mechanisms, here we consider as a model system a supersaturated liquid of hard spheres8,9,10 and generate a non-vanishing stress through constantly shearing the liquid.
Hard spheres (or more generally, hard particles11) are a paradigm for a wide range of soft materials in which entropy dominates over energetic forces and is one of the best-studied model systems in statistical mechanics. Moreover, many aspects of liquids are dominated by the packing of atoms. In the absence of shear, even though there are no direct forces between particles, hard spheres crystallize at sufficiently high packing fractions ϕ > ϕf with ϕf ≃ 0.492 when the entropy of the crystal has become higher than that of the disordered liquid. Experimentally, the limit of true hard spheres can be approached using colloidal suspensions12, which allow the direct observation of nucleation events3,13. The exact microscopic pathway from liquid to solid remains the focus of intensive research. The classical picture has been that of a one-step processes in which a rare fluctuation leads to densification and the emergence of a nucleus with the same symmetry as the solid14. More recent work has observed different pre-cursors during the initial stage that have a different symmetry than the final solid. This leads to a picture of crystallization as a two-step9,15, or even three-step3, process. Increasing the density, the entropic barrier to nucleation shrinks with dynamics that effectively become arrested on experimental time scales for packing fractions ϕ > ϕg with ϕg ≃ 0.58. How the crystallization pathway then changes is currently under investigation16.
Weakly sheared liquids still crystallize but with kinetics that are significantly altered. Understanding and controlling these kinetics at least qualitatively is of technological importance in the search of new protocols to process materials. For example, growing crystals without defects requires a small growth rate once the critical nucleus has formed. Typically this implies conditions close to coexistence2, where, however, the nucleation time (the time for the critical nucleus to appear) becomes prohibitively large. No consensus has emerged so far regarding the role of shear in numerical17,18,19,20 and experimental studies21,22,23 with and without attractive interactions. On one hand the suppression of crystallization has been reported for weak, moderate and high strain rates17,19,22, which is characterized by a decrease of the structural order in the sheared crystal22, larger critical nuclei and nucleation barriers compared to the quiescent case17 and finally the break-up and melting of solid clusters19. On the other hand, weak shear can induce crystallization in the disordered liquid and glassy state18,23. To complicate matters, an optimal strain rate has been reported19,20,21, where at first crystallization is promoted but hampered at larger strain rates. We will show that all of these features are reproduced in a sheared hard sphere liquid.
As has been done in previous studies9,10, we do not simulate true hard spheres but particles interacting pairwise via the Weeks-Chandler-Andersen potential, which is mapped onto hard spheres through an effective diameter d (see Methods). We calculate the crystallization rate density k (in Brownian units τBd3) for different values of the packing fraction ϕ and strain rate . To this end we bracket the crystallization time (the spread is included in the error estimation) by the two times such that the size n of the largest cluster obeys n < ns (n > ns) for all . The exact value nc < ns ≪ N of the threshold ns is not important as long as it is larger than the critical nucleus size nc and much smaller than the system size. We found that ns = 200 is a convenient value, which in the following is used for all packing fractions studied. For the lowest density we have performed a committor analysis24,25 and checked that the probability to commit to the solid state is unity for n ≥ 200. For the highest density n ≃ 200 roughly corresponds to the onset of the linear growth regime. From 100 independent runs, the crystallization rate is then determined as k = (V〈τx〉)−1, where V is the volume of the simulation box.
In the quiescent case () the rate is a non-monotonic function of the packing fraction, see Fig. 1a: It has a maximum around ϕ ≃ 0.56 and is decreasing fast when going to lower densities (lower supersaturation). The calculated rates agree well with previous simulation results9,10 and within errors also with experimental data (for a detailed discussion see ref. 12. Note that densities even closer to freezing can be studied using rare-event sampling methods8,10 but predict absolute rates that are several orders of magnitude too small compared to experimental results12. A comprehensive explanation of this discrepancy is still an open issue.
The crystallization rate also decreases at higher densities due to two competing factors: going to higher densities the free energy barrier against nucleation decreases while at the same time the diffusivity of particles also decreases. The non-monotonicity thus reflects the turnover from an activated process at lower densities, where a sufficiently large solid cluster has to be nucleated to overcome interfacial tension, to a crystallization process that is limited by diffusion26. In colloidal suspensions and complex fluids it is the mobility of particles that is rate-limiting, while in atomistic fluids it is the conduction of the released latent heat.
We now apply a steady shear flow leading to a non-vanishing stress. The shear flow is weak so that for the range of strain rates studied the system remains in the linear response regime and the temperature is approximately constant, see Supplementary Figure 1. Since we consider a non-equilibrium situation we require a thermostat in order to remove the dissipated heat. We have been particularly careful in selecting this thermostat in order to minimize the deviation of the kinetic energy from the bath temperature while not perturbing collective dynamics. Supplementary Figure 2 demonstrates that the kinetic energy remains unperturbed also during crystallization, indicating that the latent heat is removed sufficiently fast by the thermostat. Note that the strain rates studied here are much smaller than what is required for shear-induced ordering27.
In Fig. 1b, we observe for packing fractions ϕ ≤ 0.56 a strong suppression of crystallization. The rate decreases as a function of the square of the strain rate,
where k0 is the quiescent rate. Such a quadratic dependence to lowest order is expected from symmetry considerations alone since the rate should be invariant under the inversion of the flow profile. Moreover, the fitted expansion coefficients A < 0 for the lowest densities are well described by a linear function A ∝ (ϕ − ϕ0) with ϕ0 ≃ 0.56 well below the glassy regime. Given the strong dependence of the quiescent rate k0 on density, this simple result is somewhat surprising. The density ϕ0 approximately indicates the crossover from a regime where crystallization is suppressed by shear flow to a regime where it is enhanced with A > 0 (at least for weak shear). The location of this crossover agrees with the location for the qualitative change from activated to diffusion-limited.
We now analyze in more detail the lowest density ϕ ≃ 0.539 studied to gain some insights into the transition state ensemble, which comprises the configurations at the top of the free energy barrier separating the liquid from the solid. To this end we perform a committor analysis24,25 computing the probability PB to commit to the solid state, which is a good reaction coordinate to unambiguously describe the process of crystallization. Specifically, PB is computed from several (20 in our case) fleeting trajectories – short runs of length τf – for every configuration along a stored trajectory with randomized velocities. The fleeting time is much shorter than the nucleation time τx with mean , but large enough to allow the system to unambiguously reach the threshold (ns = 200). The committor for one configuration is calculated as the ratio between the number of fleeting trajectories that reach the solid divided by the total number of trials fired from that configuration. Such an analysis can also be performed in a driven system. Some care has to be taken regarding the initial velocities, which here are taken from the equilibrium Maxwell-Boltzmann distribution. Due to the small strain rates, the perturbation of the steady state is negligible compared to the fleeting time τf (cf. Supplementary Figure 3).
Figure 2(a) shows for ϕ ≃ 0.539 that the correlations between PB and the cluster size n are similar for both the quiescent and the sheared liquid. For the latter, equal PB typically have larger cluster sizes which indicates that smaller clusters are more likely to break up under shear. This intuitively agrees with the observation of a suppression of nucleation. Of particular interest are configurations for which PB ~ 0.5, i.e., for which the chances to fall back to the liquid or to surmount the barrier are equal. These configurations constitute the transition state ensemble, for which the distribution of cluster sizes are shown in the inset of Fig. 2(a). The mean values nc ≃ 36 for and nc ≃ 68 for are estimates of the critical cluster sizes for the quiescent and sheared liquid, respectively. Moreover, PB ≃ 1 for n ≥ ns, which shows that the threshold is sufficiently large. For higher densities critical cluster sizes are smaller and we use the same threshold for all densities.
Effective chemical potential
Classical nucleation theory predicts a crystallization rate k0 = κexp(−ΔG/kBT) with two contributions: a kinetic pre-factor κ and an exponential free energy barrier ΔG ∝ |Δμ|−2. Here, T is the temperature, kB is Boltzmann’s constant and Δμ < 0 is the difference in chemical potential of the solid and the liquid. The proportionality depends on the interfacial tension and geometric factors due to the average shape of the critical nuclei.
Both contributions to the rate are affected when turning on the shear flow. The pre-factor is determined by the fluctuations and correlations between solid-like particles in the meta-stable liquid, the reduction of which is not strong enough to explain the observed exponential reduction of the crystallization rate. Alternatively, it has been proposed that the suppression can be accounted for through an effective free energy with an increased barrier17. To test this idea, we convert packing fractions to chemical potential differences using a linear fit to the data of ref. 10. Indeed, plotting the rates as a function of an effectively reduced chemical potential difference
(while keeping the interfacial tension constant) with constant α ≃ −15, all rates for different strain rates collapse onto a single curve as shown in Fig. 2(b). This demonstrates that nucleation under shear remains a rare, collective fluctuation to overcome a single barrier. Interestingly, Butler and Harrowell have argued for the non-equilibrium coexistence of a sheared liquid and the solid that the magnitude of the chemical potential difference is likely to increase28,29. This would imply that under shear there are two effective chemical potentials: one determines the nucleation of the new phase and one determines the final coexistence in the steady state. Both cannot be the same, which is in striking contrast to the quiescent liquid.
We finally study the regime ϕ ≥ 0.56. In Fig. 3a the mean crystallization time 〈τx〉 is plotted for the largest packing fraction ϕ ≃ 0.587, which indeed shows an enhancement of crystallization for weak shear flow. For consistency, we maintain the same criteria for determining the crystallization time although now multiple solid clusters appear and grow. While at low supersaturation the distinction between the actual nucleation time (random waiting time to reach the critical cluster size) and crystallization time (random waiting time τx to reach ns) is negligible, this is no longer the case. At this density, the solidification process is limited by the rate with which additional particles “attach” (there are no direct attractive forces but arranging into ordered structures locally increases the entropy). Shear flow increases the diffusion both parallel and perpendicular to the direction of the shear flow30 and thus speeds up the attachment while the barrier to nucleate small solid clusters is still small. However, we observe that increasing the mean crystallization time reaches a minimum before it again increases for higher strain rates.
In Fig. 3b the evolution of the largest cluster is shown for ϕ ≃ 0.587. To separate the effects of nucleation and growth, the single trajectories have been shifted by τx before averaging. In the quiescent liquid, the growth of the largest nucleus is gradually and slow before 〈n〉 becomes an approximately linear function of time for 〈n〉 > ns. Hence, the value ns = 200 is also a good estimate for the beginning of the linear growth regime. In the presence of shear flow, the initial increase of 〈n〉 is less gradual and the following growth is more rapid. Interestingly, for both non-zero strain rates the curves lie on top of each other while the crystallization rates differ by a factor of two. The reason is revealed in Fig. 3c, which shows that the distribution of the single crystallization times τx is strongly affected by the shear flow. In the quiescent liquid the barrier to nucleation has basically vanished and we observe multiple nuclei (see snapshot Fig. 3d). The mean nucleation time 〈τx〉 ≃ 16.5τB is small (compare 〈τx〉 ≃ 750τB for ϕ ≃ 0.539) while the distribution is approximately Gaussian, which qualitatively agrees with a diffusive evolution under a constant force given by the chemical potential difference between liquid and solid. Going to a small strain rate , the distribution of nucleation times remains a Gaussian but becomes more narrow with a smaller mean. At this strain rate solid clusters thus appear more frequently and grow faster compared to the quiescent liquid (see Fig. 3e). At higher strain rate the distribution of τx becomes very broad with a pronounced tail, which implies a delayed induction of solid clusters and the qualitative change to activated behavior. Once these have formed, however, clusters grow faster than in the absence of shear flow (Fig. 3f).
The effect of weakly shearing a hard sphere liquid on crystallization strongly depends on the density: At low supersaturation the driving force of crystallization, the difference of the chemical potential between liquid and solid, is also small. Here the forces exerted by the shear flow might overcome the gain of entropy and lead to a larger probability for small solid clusters to lose particles (or even break up). Larger clusters are not affected, which, in combination, leads to a shift of the critical cluster size that can be interpreted as an effectively larger barrier to nucleation. No enhancement of crystallization occurs in this regime. This result might also shed some light onto the controversy regarding the discrepancy between experimental and simulation results at low supersaturations. As pointed out by Russo et al.31, sedimentation of not fully density-matched colloidal particles has an influence on the crystallization rate. However, the actual mechanism is not known and combined with the suppression of crystallization found here seems to rule out shear-induced effects.
At high supersaturation there is a combination of two effects: (i) The diffusion of particles in the surrounding liquid is increased. This enhanced exploration of configuration space accelerates the growth of solid clusters. (ii) The shear flow disrupts the subtle order in the liquid and thus suppresses the formation of small solid clusters. At larger strain rates this suppression is so strong that crystallization again becomes an activated process comparable to crystallization at lower supersaturation in the quiescent liquid. We expect that these physical mechanisms are valid beyond hard spheres also in the presence of short-ranged interactions.
We study a model liquid composed of N = 5000 monodisperse, nearly hard spheres in a periodic box with volume V employing standard NVT molecular dynamics32. Particles interact via the Weeks-Chandler-Andersen potential (WCA) for r < 21/6σ. The temperature is held constant via the stochastic Lowe-Andersen thermostat33, which is characterized by the bath collision frequency Γ. This thermostat has desirable properties, in particular it is Galilean invariant and conserves angular momentum. The WCA potential can be mapped onto hard spheres by means of an effective diameter d10, which we compute from with freezing packing fraction of hard spheres and freezing density of the WCA liquid10. The packing fraction is . As time scale we employ the Brownian time τB = d2/D0, where D0 is the bare diffusion coefficient in the infinitely dilute system. The system is driven through Lees-Edwards periodic boundary conditions leading to a linear flow profile .
Random configurations of dense hard spheres without preformed structures were created with the algorithm by Clarke and Wiley34, where the non-overlapping distance between particles was chosen to be equal to the effective diameter d. These configurations are thermalized in a short run without shear at high collision frequency Γ ≃ 100 before the production runs at given strain rate with Γ ≃ 10.
To distinguish between liquid-like and solid-like particles, we follow ref. 10. We employ the local bond order parameter35
for particle i, where Yl,m(θ, ϕ) are spherical harmonics and Nn is the number of neighbors within distance rij < 1.5σ. We construct a bond network through the scalar product
using l = 6 with d(i, j) ≥ 0.7 defining a bond. A particle is defined as “solid-like” (“pre-structured”) if the number of bonds is ≥9 (≥6) and clusters are constructed from mutually bonded solid-like particles.
How to cite this article: Richard, D. and Speck, T. The role of shear in crystallization kinetics: From suppression to enhancement. Sci. Rep. 5, 14610; doi: 10.1038/srep14610 (2015).
Porter, D. A., Easterling, K. E. & Sherif, M. Phase Transformations in Metals and Alloys (CRC Press, 2008).
Anderson, V. J. & Lekkerkerker, H. N. W. Insights into phase transition kinetics from colloid science. Nature 416, 811–815 (2002).
Tan, P., Xu, N. & Xu, L. Visualizing kinetic pathways of homogeneous nucleation in colloidal crystallization. Nat. Phys. 10, 73–79 (2014).
Peng, Y. et al. Two-step nucleation mechanism in solid-solid phase transitions. Nature Mater. 14, 101–108 (2015).
Khaliullin, R. Z., Eshet, H., Kühne, T. D., Behler, J. & Parrinello, M. Nucleation mechanism for the direct graphite-to-diamond phase transition. Nature Mater. 10, 693–697 (2011).
Virtanen, A. et al. An amorphous solid state of biogenic secondary organic aerosol particles. Nature 467, 824–827 (2010).
Jiang, P. & McFarland, M. J. Large-scale fabrication of wafer-size colloidal crystals, macroporous polymers and nanocomposites by spin-coating. J. Am. Chem. Soc. 126, 13778–13786 (2004).
Auer, S. & Frenkel, D. Prediction of absolute crystal-nucleation rate in hard-sphere colloids. Nature 409, 1020–1023 (2001).
Kawasaki, T. & Tanaka, H. Formation of a crystal nucleus from liquid. Proc. Natl. Acad. Sci. USA. 107, 14036–14041 (2010).
Filion, L., Ni, R., Frenkel, D. & Dijkstra, M. Simulation of nucleation in almost hard-sphere colloids: The discrepancy between experiment and simulation persists. J. Chem. Phys. 134, 134901 (2011).
Damasceno, P. F., Engel, M. & Glotzer, S. C. Predictive self-assembly of polyhedra into complex structures. Science 337, 453–457 (2012).
Palberg, T. Crystallization kinetics of colloidal model suspensions: recent achievements and new perspectives. J. Phys.: Condens. Matter 26, 333101 (2014).
Gasser, U., Weeks, E. R., Schofield, A., Pusey, P. N. & Weitz, D. A. Real-space imaging of nucleation and growth in colloidal crystallization. Science 292, 258–262 (2001).
Becker, R. & Döring, W. Kinetische behandlung der keimbildung in übersättigten dämpfen. Ann. Phys. 24, 719–752 (1935).
Schilling, T., Schöpe, H. J., Oettel, M., Opletal, G. & Snook, I. Precursor-mediated crystallization process in suspensions of hard spheres. Phys. Rev. Lett. 105, 025701 (2010).
Sanz, E. et al. Avalanches mediate crystallization in a hard-sphere glass. Proc. Natl. Acad. Sci. USA. 111, 75–80 (2014).
Blaak, R., Auer, S., Frenkel, D. & Löwen, H. Crystal nucleation of colloidal suspensions under shear. Phys. Rev. Lett. 93, 068303 (2004).
Mokshin, A. V. & Barrat, J.-L. Shear-induced crystallization of an amorphous system. Phys. Rev. E 77, 021505 (2008).
Cerdà, J. J., Sintes, T., Holm, C., Sorensen, C. M. & Chakrabarti, A. Shear effects on crystal nucleation in colloidal suspensions. Phys. Rev. E 78, 031403 (2008).
Lander, B., Seifert, U. & Speck, T. Crystallization in a sheared colloidal suspension. J. Chem. Phys. 138, 224907 (2013).
Holmqvist, P., Lettinga, M. P., Buitenhuis, J. & Dhont, J. K. G. Crystallization kinetics of colloidal spheres under stationary shear flow. Langmuir 21, 10976–10982 (2005).
Wu, Y. L., Derks, D., van Blaaderen, A. & Imhof, A. Melting and crystallization of colloidal hard-sphere suspensions under shear. Proc. Natl. Acad. Sci. USA. 106, 10564–10569 (2009).
Shao, Z. et al. Shear-accelerated crystallization in a supercooled atomic liquid. Phys. Rev. E 91, 020301 (2015).
Bolhuis, P. G., Chandler, D., Dellago, C. & Geissler, P. L. Transition path sampling: Throwing ropes over rough mountain passes, in the dark. Annual Review of Physical Chemistry 53, 291–318 (2002).
Jungblut, S. & Dellago, C. Heterogeneous crystallization on tiny clusters. EPL (Europhysics Letters) 96, 56006 (2011).
Harland, J. L., Henderson, S. I., Underwood, S. M. & van Megen, W. Observation of accelerated nucleation in dense colloidal fluids of hard sphere particles. Phys. Rev. Lett. 75, 3572–3575 (1995).
Vermant, J. & Solomon, M. J. Flow-induced structure in colloidal suspensions. J. Phys.: Condens. Matter 17, R187 (2005).
Butler, S. & Harrowell, P. Factors determining crystal–liquid coexistence under shear. Nature 415, 1008–1011 (2002).
Butler, S. & Harrowell, P. Simulation of the coexistence of a shearing liquid and a strained crystal. J. Chem. Phys. 118, 4115 (2003).
Lander, B., Seifert, U. & Speck, T. Mobility and diffusion of a tagged particle in a driven colloidal suspension. EPL 92, 58001 (2010).
Russo, J., Maggs, A. C., Bonn, D. & Tanaka, H. The interplay of sedimentation and crystallization in hard-sphere suspensions. Soft Matter 9, 7369–7383 (2013).
Allen, M. P. & Tildesley, D. J. Computer Simulation of Liquids (Clarendon Press, New York, NY, USA, 1989).
Koopman, E. A. & Lowe, C. P. Advantages of a lowe-andersen thermostat in molecular dynamics simulations. J. Chem. Phys. 124, 204103 (2006).
Clarke, A. S. & Wiley, J. D. Numerical simulation of the dense random packing of a binary mixture of hard spheres: Amorphous metals. Phys. Rev. B 35, 7350 (1987).
Steinhardt, P. J., Nelson, D. R. & Ronchetti, M. Bond-orientational order in liquids and glasses. Phys. Rev. B 28, 784–805 (1983).
We acknowledge financial support by DFG through collaborative research center TRR 146 and ZDV Mainz for computing time on the MOGON supercomputer.
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Richard, D., Speck, T. The role of shear in crystallization kinetics: From suppression to enhancement. Sci Rep 5, 14610 (2015). https://doi.org/10.1038/srep14610
This article is cited by
Materials, assemblies and reaction systems under rotation
Nature Reviews Materials (2022)
Hydrochemical and operational parameters driving carbonate scale kinetics at geothermal facilities in the Bavarian Molasse Basin
Geothermal Energy (2020)
On the effect of flow restrictions on the nucleation behavior of molecules in tubular flow Nucleators
Journal of Flow Chemistry (2020)
Hydrodynamic assembly of two-dimensional layered double hydroxide nanostructures
Nature Communications (2018)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.