Carrier mobility and chemical doping level are essential figures of merit for graphene and large-scale characterization of these properties and their uniformity is a prerequisite for commercialization of graphene for electronics and electrodes. However, existing mapping techniques cannot directly assess these vital parameters in a non-destructive way. By deconvoluting carrier mobility and density from non-contact terahertz spectroscopic measurements of conductance in graphene samples with terahertz-transparent backgates, we are able to present maps of the spatial variation of both quantities over large areas. The demonstrated non-contact approach provides a drastically more efficient alternative to measurements in contacted devices, with potential for aggressive scaling towards wafers/minute. The observed linear relation between conductance and carrier density in chemical vapour deposition graphene indicates dominance by charged scatterers. Unexpectedly, significant variations in mobility rather than doping are the cause of large conductance inhomogeneities, highlighting the importance of statistical approaches when assessing large-area graphene transport properties.
Graphene1 is being targeted for an increasing number of commercially oriented applications2,3,4,5,6,7,8,9 and industrial development10,11,12, merited by its combination of exceptional electronic, optical and mechanical properties as well as the increasing availability of synthesized large-area graphene films. In particular, there is a profound interest in the commercial adaptation of large-area graphene of high electrical quality for electronics applications, including high frequency terahertz (THz) electronics13,14,15 and transparent, flexible and durable electrodes for graphene-based touch-screens, displays and solar cells14. There have been several demonstrations of THz time-domain spectroscopy (THz-TDS) for rapid and contact-free conductance measurements of large-area graphene16,17,18, making practical implementations of in-line spatial mapping of graphene sheet conductance on a large scale possible19,20,21. For typical electronic applications22, however, the conductance of a graphene film in itself gives an incomplete picture in terms of the expected performance. For many scientific as well as commercial applications, the carrier mobility and the background carrier density originating from intentional23,24 or unintentional25,26 chemical doping are the essential figures of merit27,28 and the most straightforward way to obtain this information is through the electric field effect, which requires a variable gate potential. Such characterization in contacted graphene devices ultimately results in the dissection and processing of the sample, if any kind of spatial or statistical information is required. This is a destructive process, where the question as to whether the final devices truly represent the initial state of the unprocessed film of graphene, is difficult to answer.
Here we demonstrate quantitative mapping of the field-effect carrier mobility in a large-area monolayer CVD graphene film based on in-situ electrically gated THz-TDS imaging. In contrast to prior electrically gated THz spectroscopy experiments performed on graphene29,30,31,32 we employ a low-mobility, high carrier concentration gate-electrode material, in this case p+ boron-doped, nano-crystalline silicon, to ensure a negligible THz response from free carriers injected into the gate-electrode. This allows for isolation of the graphene sheet conductance from non-contact THz-TDS transmission measurements and thus a quantitative extraction of the graphene field-effect mobility.
Experiment and substrate design
To avoid THz absorption from free carriers in the substrate, to obtain a voltage-independent gate capacitance and to ensure an insignificant gate-differential THz response from free carriers injected into the gate-electrode, we employ a low-mobility, high carrier density thin film gate-electrode. This allows for isolation of the gate-induced conductance of the graphene and a quantitative extraction of the graphene field-effect mobility. To this end, we use a substrate comprised of 525 μm ρ > 10,000 Ωcm high resistivity silicon (Si), 50 nm boron-doped poly-crystalline Si (poly-Si) and 165 nm Si nitride (Si3N4). The THz response of the poly-Si/Si3N4 stack is found to be negligible with a frequency-independent transmission of 100% ± 1% and a diminishing phase-shift of 2 ° (see Supplementary information), which is attributed to slight differences in high resistivity Si substrate thickness between the positions of the reference and sample measurements. In accordance, the 2-point contact DC sheet conductance of the poly-Si thin film was measured to be below σs,poly-Si = 0.1 mS, which is at the limit of sensitivity of the THz spectrometer. Combined with a Boron doping concentration of npoly-Si = 2.6 × 1019 cm−3, measured by secondary ion mass spectroscopy, the sheet conductance value is consistent with an expected carrier mobility below μpoly-Si = 10 cm2/Vs.33,34,35
A large-area graphene film is grown on commercially available Cu foil by means of a standard catalytic chemical vapour deposition (CVD) and is subsequently transferred onto the layered substrate, as shown in Fig. 1(a), by a standard polymer-assisted technique, involving complete sacrificial etching of the Cu substrate in (NH4)2S2O8. Figure 1(b) and (c) shows a tiled, high-resolution optical image and Raman analysis characteristics of the final sample, respectively.
Back-gated terahertz conductance mapping
THz maps of the CVD graphene on Si3N4/poly-Si/Si were recorded at 21 different gate voltages between 0V and 40V, a selection of which are shown in Fig. 2(a), where the data is represented by images showing the total transmitted THz power and corresponding THz sheet conductance. Since the CVD graphene film is heavily p-doped, the conductance and therefore the THz response of the graphene film are lowest in the Vg =24 V THz map. The complex, frequency-dependent sheet conductance can be directly obtained in each pixel of the maps from the measured amplitude and phase change upon transmission through the sample (see Methods section). As shown in Fig. 2(b) the THz sheet conductance exhibits a real part of the conductance which rises very slightly with increasing frequency and exhibits a strong dependence on the applied gate voltage. The imaginary part of the conductance, which is subject to a relatively high uncertainty due to substrate thickness variations on the order of 200 nm across the 2 cm sample (see Supplementary information), is close to 0 in the accessible frequency range of 0.25–1.2 THz and it exhibits a weak dependence on both frequency and applied gate voltage. The slightly rising real conductance along with an imaginary conductance which decreases slightly towards more negative values with increasing frequency is consistent with the Drude-Smith model and may suggest a small degree of preferential back-scattering of charge carriers in this particular graphene film, as we recently reported on36. For frequencies significantly below the scattering rate (2πf≪1/τ), the Drude-Smith and Drude models, expected for the THz response of pristine graphene, dictates that the real part of is constant and near its DC value while the imaginary part is close to zero. Our spectrally resolved measurement can thus be replaced by a single, real-valued quantity reflecting the DC conductance of the graphene film.
In Fig. 2(a) we have used this approach to form maps of the graphene sheet conductance, represented by the average value of between 0.5–0.9 THz, from here on referred to as σs. The evolution of σs with varying Vg in the series of images in Fig. 2(a) is a result of the electric field effect in graphene and thus provides vital information on the carrier mobility and chemical doping of the film.
Field-effect mobility mapping
Figure 2(c) shows σs as a function of Vg for three distinct areas in the map with highly conducting graphene, less conducting graphene and no graphene coverage. The measured of σs shows a linear dependence on the applied gate voltage in the range 0V < Vg < 18 V with different slopes throughout the extent of the graphene film, reflecting the local field-effect mobility for hole carriers. This observation is found to be representative throughout the graphene film area. For gate voltages 24 V < Vg < 40 V a plateau with slowly increasing σs is found. This observation indicates that electron-conduction is greatly impaired in this particular graphene film with electron mobilities that are more than an order of magnitude lower than the observed hole mobilities. Application of a gate voltage, Vg, between the poly-Si thin film and the graphene film induces a proportional change in the free carrier density, Δns, in the poly-Si and graphene films, as Throughout the extent of the film, a highly consistent minimum is found in the sheet conductance close to Vg = 24 V. This minimum represents the charge-neutrality-point (CNP), indicating a constant and homogeneous presence of residual absorbates with a density of approximately 5 × 1012 cm−2, which p-dopes the entire graphene film. Within the regime of long-range, charged impurity scattering, the added free graphene carriers result in a roughly linear change in the graphene sheet conductance, σs, with the field effect mobility being a proportionality factor. The sheet conductance, σs, of the graphene film is thus described by the relations37:
where Cg is the gate capacitance, e is the electronic charge, ε0 is the vacuum permittivity, εSiN = 7.5 is the relative permittivity of Si nitride, t is the thickness of Si nitride gate dielectric and μFE is the field-effect mobility of the graphene film.
The gate-induced conductance in the gate electrode can be neglected because of the insignificant carrier mobility (μpoly-Si < 10 cm2/Vs) of our poly-Si thin film relative to the hole mobility of the investigated graphene film, which is approximately two orders of magnitude higher. Because of the choice of a low-mobility, high carrier concentration gate material, the experiments presented here provide a direct and reliable measure of the gate-induced conductance evolution of the graphene film with an insignificant contribution from gate-induced carriers in the substrate. Following equation (2), the field effect mobility of the graphene film can thus be obtained in each pixel of the mapped area by retrieving the slope |Δσs/ΔVg| in the high density-region well below the CNP. Based on this central result we are able to show a spatially resolved field-effect hole mobility map for the large-area CVD graphene film in Fig. 2(d), resulting from the application of equation (2) to the entire dataset. The slope |Δσs/ΔVg| was found in each pixel by a linear fitting routine to σs vs. Vg from 0 V to +18 V. Similarly, the carrier density due to chemical doping of the graphene film at zero gate bias, can be evaluated across the map from the determined hole mobilities and the sheet conductance at Vg = 0, by utilizing the relation σs = ensμhole. Figure 2(e) shows a map of ns (ns is set to 0 in pixels where μhole < 100 cm2/Vs). We note that carrier mobility measured using this technique is affected by the coverage of graphene, because equations (3) and (4) assume full areal coverage within the measurements area. In case of less than full coverage, mobilities are underestimated by a factor proportional to the convolution of the THz spot profile and the local graphene coverage landscape.
In contrast to recent back-gated THz spectroscopy investigations of CVD graphene29,31, our measurement of σs shows a linear dependence on the applied gate voltage, reflecting the local field-effect mobility for hole carriers. The linear dependence of σs on Vg is expected for graphene films where long-range, charged impurity scattering dominates over short-range neutral defect scattering37,38 and is typically observed in DC transport measurements of samples with field effect mobility μ < 5.000 cm2/Vs.1,23,39,40 Our findings of a spatially homogeneous doping level of approximately 5 × 1012 cm−2, as well as strongly suppressed electron mobility are consistent with transport measurements on graphene in atmospheric conditions. It is well known that a presence of O2 and H2O adsorbates on graphene causes a strong p-doping on the monolayer, which is particularly relevant in samples not annealed and exposed to atmospheric conditions40,41, as is our case. In addition, this unintentional p-doping inhibits the mobility of electrons relative to that of holes. The latter effect was predicted as a unique property of massless fermions42,43 and has been verified several times in conventional DC transport measurements23,40. The relatively high chemical doping density further supports the notion that the electronic transport is dominated by long-range scattering on charged impurities37.
Unexpectedly, Fig. 2 (d) and (e) reveal that the large-scale spatial variations in the sheet conductance of the graphene film, observed in Fig. 2(a), are primarily due to spatial variations in the carrier mobility, rather than variations in doping level. The chemical doping level, shown in Fig. 2(e) presents only small spatial fluctuations. In contrast, we find that even on a scale of a few mm, the carrier mobility varies by up to a factor 2, highlighting the importance of techniques that either facilitate a statistical approach for assessing transport properties in CVD graphene or allow spatial mapping of graphene transport properties such as that presented here. This fact is quantified in Fig. 3, which shows histograms of μhole and ns(0V) from the central region of the graphene film, marked by dashed, black rectangles in Fig. 2(d) and (e). The fitted Gaussian distributions plotted along with the distributions, have peak values of μhole = 1174 cm2/Vs and ns(0 V) = 6.2 × 1012 cm−2 and relative standard deviations of std(μhole)/avg(μhole) = 14.0% and std(ns)/avg(ns) = 4.8%.
We find that the procedure presented here gives far more comprehensive information than the typical convention of relying on a few representative electrical measurements from random or selected areas of a large graphene film. We also note that the features and inhomogeneities in the field effect mobility in Fig. 2(d) were not observed in a typical Raman analysis of the amplitude-ratio of the the D- and G-bands, which can be found in the Supplementary information.
We anticipate that quantitative, non-contact mapping of graphene carrier mobility as presented in this work will have a significant technological importance for the advancement of production and implementations of large-area graphene in commercial electronic applications and that it can contribute to the fundamental insight into charge carrier dynamics of the graphene solid-state-system by paving the way for investigations of transport dynamics with unprecedented statistical basis.
In conclusion, we have presented non-contact, quantitative mapping of graphene field effect mobility in a 10 × 10 mm2 large-area CVD film by in-situ electrically gated THz-TDS measurements. While THz-TDS is non-contact, optical characterization, the frequency range is well below the inverse scattering time of the graphene charge carriers, making the obtained conductance directly comparable the DC value. The technique thus opens up the possibility for assessment of fundamental electrical transport properties such as carrier mobility and chemical doping level on basis of large statistical ensembles, or large-area spatial mapping. Far from the charge-neutrality-point, our measurements show a linear dependence of the THz sheet conductance on carrier density, which is interpreted as a signature of electrical transport limited by long-range, charged impurity scattering, also observed in most DC transport measurements on graphene. Unexpectedly, we find that the mobility varies by up to a factor of 2 on a scale of just few mm and that significant conductance variations in the investigated CVD graphene are due to mobility rather doping variations, which highlights the importance of techniques that facilitate highly statistical or spatially resolved approaches for assessing transport properties in large-area graphene.
Terahertz time-domain spectroscopy
The experiments are carried out using a Picometrix© T-ray™ 4000 fiber-coupled THz time-domain spectrometer relying on photoconductive switches for THz generation and detection, which is detailed elsewhere21. The sample is placed in the THz focal plane formed between 2 aspheric polymer lenses, each with a working distance of 25.4 mm, producing a focused spot size of approx. 0.6 mm at 0.5 THz and 0.3 mm at 0.9 THz21. By raster-scanning the graphene sample in steps of 0.2 mm in the THz focus, pulse waveforms are recorded in every pixel of a spatially resolved map with close to 7500 pixels covering the full extent of the 10 × 10 mm2 graphene film. Through utilization of the electric field effect in graphene, THz maps are recorded at different carrier densities by applying voltages, Vg, in the range from 0 V to 40 V between poly-Si thin film and graphene film. The full acquisition time for each map is 16 minutes and Vg is increased in discrete steps of 2 V between each map.
The sheet conductance of the graphene film was extracted in each pixel of the THz maps based on an approach described previously21. The complex-valued transmission coefficient, in each pixel of the map can be directly related to the complex sheet conductance, , of the graphene film according to equation , which is derived from Fresnel coefficients for the boundaries in the sample geometry, modeled as an infinitely thin conducting surface of sheet conductance, 44,45 on a thick high resistivity Si dielectric medium with refractive index nSi = 3.41746. is calculated as the ratio of the Fourier transform of the transmitted sample THz waveform, , (transmission through graphene/Si3N4/poly-Si/Si) to that of a reference waveform, (transmission through Si3N4/poly-Si/Si-substrate) and can be related to real and imaginary parts of the sheet conductance as
where Z0 = 377 Ω is the vacuum impedance.
How to cite this article: Buron, J. D. et al. Graphene mobility mapping. Sci. Rep. 5, 12305; doi: 10.1038/srep12305 (2015).
Novoselov, K. S. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197–200 (2005).
Bao, Q. et al. Atomic-Layer Graphene as a Saturable Absorber for Ultrafast Pulsed Lasers. Adv. Funct. Mater. 19, 3077–3083 (2009).
Su, F.-Y. et al. Flexible and planar graphene conductive additives for lithium-ion batteries. J. Mater. Chem. 20, 9644 (2010).
Eda, G., Fanchini, G. & Chhowalla, M. Large-area ultrathin films of reduced graphene oxide as a transparent and flexible electronic material. Nat. Nanotechnol. 3, 270–4 (2008).
Liao, L. et al. High-speed graphene transistors with a self-aligned nanowire gate. Nature 467, 305–308 (2010).
Li, X. et al. Transfer of Large-Area Graphene Films for High-Performance Transparent Conductive Electrodes. Nano Lett. 9, 4359–4363 (2009).
Lin, Y.-M. et al. Operation of Graphene Transistors at Gigahertz Frequencies. Nano Lett. 9, 422–426 (2009).
Xia, F., Mueller, T., Lin, Y., Valdes-Garcia, A. & Avouris, P. Ultrafast graphene photodetector. Nat. Nanotechnol. 4, 839–843 (2009).
Lin, Y.-M. et al. Wafer-Scale Graphene Integrated Circuit. Science (80-.). 332, 1294–1297 (2011).
Bae, S. et al. Roll-to-roll production of 30-inch graphene films for transparent electrodes. Nat. Nanotechnol. 5, 574–578 (2010).
Kim, K. S. et al. Large-scale pattern growth of graphene films for stretchable transparent electrodes. Nature 457, 706–710 (2009).
www.investorintel.com. Game Changer: Grafoid’s new patent-pending MesoGrafTM technology sets the standard for high-energy-density graphene -.
Schwierz, F. Graphene transistors. Nat. Nanotechnol. 5, 487–496 (2010).
Novoselov, K. S. et al. A roadmap for graphene. Nature 490, 192–200 (2012).
Zheng, J. et al. Sub-10 nm Gate Length Graphene Transistors: Operating at Terahertz Frequencies with Current Saturation. Sci. Rep. 3, (2013).
Dawlaty, J. M. et al. Measurement of the optical absorption spectra of epitaxial graphene from terahertz to visible. Appl. Phys. Lett. 93, 131905–131905–3 (2008).
Choi, H. et al. Broadband electromagnetic response and ultrafast dynamics of few-layer epitaxial graphene. Appl. Phys. Lett. 94, 172102 (2009).
Liu, W., Valdés Aguilar, R., Hao, Y., Ruoff, R. S. & Armitage, N. P. Broadband microwave and time-domain terahertz spectroscopy of chemical vapor deposition grown graphene. J. Appl. Phys. 110, 083510–083510–5 (2011).
Tomaino, J. L. et al. Terahertz imaging and spectroscopy of large-area single-layer graphene. Opt. Express 19, 141–146 (2011).
Paul, M. J. et al. Terahertz imaging of inhomogeneous electrodynamics in single-layer graphene embedded in dielectrics. Appl. Phys. Lett. 101, 091109 (2012).
Buron, J. D. et al. Graphene Conductance Uniformity Mapping. Nano Lett. 12, 5074–5081 (2012).
Avouris, P. & Xia, F. Graphene applications in electronics and photonics. MRS Bull. 37, 1225–1234 (2012).
Chen, J.-H. et al. Charged-impurity scattering in graphene. Nat. Phys. 4, 377–381 (2008).
Khrapach, I. et al. Novel highly conductive and transparent graphene-based conductors. Adv. Mater. 24, 2844–9 (2012).
Martin, J. et al. Observation of electron–hole puddles in graphene using a scanning single-electron transistor. Nat. Phys. 4, 144–148 (2007).
Caridad, J. M. et al. Effects of particle contamination and substrate interaction on the Raman response of unintentionally doped graphene. J. Appl. Phys. 108, 084321 (2010).
Li, X. et al. Large-Area Synthesis of High-Quality and Uniform Graphene Films on Copper Foils. Science (80-.). 324, 1312–1314 (2009).
Mayorov, A. S. et al. Micrometer-scale ballistic transport in encapsulated graphene at room temperature. Nano Lett. 11, 2396–9 (2011).
Horng, J. et al. Drude conductivity of Dirac fermions in graphene. Phys. Rev. B 83, 165113 (2011).
Ren, L. et al. Terahertz and Infrared Spectroscopy of Gated Large-Area Graphene. Nano Lett. 12, 3711–3715 (2012).
Maeng, I. et al. Gate-Controlled Nonlinear Conductivity of Dirac Fermion in Graphene Field-Effect Transistors Measured by Terahertz Time-Domain Spectroscopy. Nano Lett. 12, 551–555 (2012).
Jnawali, G., Rao, Y., Yan, H. & Heinz, T. F. Observation of a transient decrease in terahertz conductivity of single-layer graphene induced by ultrafast optical excitation. Nano Lett. 13, 524–30 (2013).
Kamins, T. I. Hall Mobility in Chemically Deposited Polycrystalline Silicon. J. Appl. Phys. 42, 4357 (1971).
Seto, J. Y. W. The electrical properties of polycrystalline silicon films. J. Appl. Phys. 46, 5247 (1975).
Dimitriadis, C. A. et al. Effect of pressure on the growth of crystallites of low-pressure chemical-vapor-deposited polycrystalline silicon films and the effective electron mobility under high normal field in thin-film transistors. J. Appl. Phys. 73, 8402 (1993).
Buron, J. D. et al. Electrically continuous graphene from single crystal copper verified by terahertz conductance spectroscopy and micro four-point probe. Nano Lett. 14, 6348–55 (2014).
Das Sarma, S., Adam, S., Hwang, E. H. & Rossi, E. Electronic transport in two-dimensional graphene. Rev. Mod. Phys. 83, 407–470 (2011).
Ando, T. Screening Effect and Impurity Scattering in Monolayer Graphene. J. Phys. Soc. Japan 75, 074716 (2006).
Tan, Y.-W. et al. Measurement of Scattering Rate and Minimum Conductivity in Graphene. Phys. Rev. Lett. 99, 246803 (2007).
Wang, H., Wu, Y., Cong, C., Shang, J. & Yu, T. Hysteresis of electronic transport in graphene transistors. ACS Nano 4, 7221–8 (2010).
Gammelgaard, L. et al. Graphene transport properties upon exposure to PMMA processing and heat treatments. 2D Mater. 1, 035005 (2014).
Novikov, D. S. Numbers of donors and acceptors from transport measurements in graphene. Appl. Phys. Lett. 91, 102102 (2007).
Robinson, J., Schomerus, H., Oroszlány, L. & Fal’ko, V. Adsorbate-Limited Conductivity of Graphene. Phys. Rev. Lett. 101, 196803 (2008).
Glover, R. & Tinkham, M. Conductivity of Superconducting Films for Photon Energies between 0.3 and 40kTc. Phys. Rev. 108, 243–256 (1957).
Lui, K. P. H. & Hegmann, F. A. Ultrafast carrier relaxation in radiation-damaged silicon on sapphire studied by optical-pump–terahertz-probe experiments. Appl. Phys. Lett. 78, 3478 (2001).
Grischkowsky, D. R., Keiding, S., Vanexter, M. & Fattinger, C. Far-infrared time-domain spectroscopy with terahertz beams of dielectrics and semiconductors. J. Opt. Soc. Am. B-Optical Phys. 7, 2006–2015 (1990).
We acknowledge valuable conversations with Ole Hansen, as well as technical assistance from Morten Møller. We acknowledge financial support from the EC Graphene FET Flagship, contract no 604391, Center for Nanostructured Graphene (CNG), sponsored by the Danish National Research Foundation, Project DNRF58, the Villum Foundation, project no. VKR023117 and the Gladiator Project, funded from the European Union Seventh Framework Programme (FP7/2007-2013) under grant agreement no. 604000.
The authors declare no competing financial interests.
Electronic supplementary material
About this article
Cite this article
Buron, J., Pizzocchero, F., Jepsen, P. et al. Graphene mobility mapping. Sci Rep 5, 12305 (2015). https://doi.org/10.1038/srep12305
Fabrication and spectroscopic characterization of graphene transparent electrodes on flexible cyclo-olefin substrates for terahertz electro-optic applications
Cobalt (II) Phthalocyanine Sulfonate Supported on Reduced Graphene Oxide (RGO) as a Recyclable Photocatalyst for the Oxidation of Aldehydes to Carboxylic Acids
Catalysis Letters (2020)
Applied Sciences (2020)
Through-substrate terahertz time-domain reflection spectroscopy for environmental graphene conductivity mapping
Applied Physics Letters (2020)