The reversal of the magnetization under the influence of a field pulse has been previously predicted to be an incoherent process with several competing phenomena such as domain wall relaxation, spin wave-mediated instability regions and vortex-core mediated reversal dynamics. However, there has been no study on the direct observation of the switching process with the aid of a microwave signal input. We report a time-resolved imaging study of magnetization reversal in patterned magnetic structures under the influence of a field pulse with microwave assistance. The microwave frequency is varied to demonstrate the effect of resonant microwave-assisted switching. We observe that the switching process is dominated by spin wave dynamics generated as a result of magnetic instabilities in the structures and identify the frequencies that are most dominant in magnetization reversal.
Magnetization reversal dynamics in patterned magnetic structures have been intensely studied in recent years due to their relevance in high speed switching applications1,2,3 and due to fundamental interests4,5,6,7,8,9. Long-range magnetostatic interactions due to shape effects become stronger as structural dimensions approach the sub-micron scale, giving rise to a rich composition of stationary and propagating magnetization dynamics, comprised of the fundamental and higher order precessional modes. The influence of competing forces such as the anisotropy, exchange and demagnetizing fields is evident from the creation of magnetic instability regions that precede the reversal process10,11 and are well supported by micromagnetic simulations12,13. Using magneto-optical techniques, experiments have shown that one way to speed up the switching process is to suppress the precessional motion, by tailoring the field pulses14. Time-resolved studies of pulse-induced switching in tapered sub-micrometer elements confirmed the observation of instability regions10 and interestingly switched at a lower magnetic field as compared to rectangular structures or structures with flux-closure domains15,16. However, the energy required in magnetization reversal by the use of static square current pulses makes it unsuitable to be considered for future applications in magnetization reversal devices.
To overcome this drawback, the idea of microwave assisted switching (MAS) has been proposed and researched widely over the past decade17,18,19,20,21,22. In MAS, a high frequency microwave current pulse is superimposed on the square current pulse, thereby driving the precessional switching dynamics at a higher frequency. Kerr microscopy studies12,23, in conjunction with micromagnetic simulations, of microwave assisted switching in large Py ellipsoids suggest that the reversal is initiated by the generation of inhomogeneous spin wave modes in confined structures leading to domain nucleation and magnetization reversal through domain wall propagation. MAS has also been explored by electrical techniques through ferromagnetic resonance (FMR) measurements17,18,19, or by using a microbridge superconducting interference device (SQUID)9. The scanning transmission X-ray microscopy (STXM) technique is an imaging technique that possesses the necessary spatio-temporal resolution to identify the physics behind the MAS process.
In this work, we present direct time-resolved images of the microwave assisted magnetization reversal process in a micron-sized Py (Ni78Fe22) element using STXM. The element is excited by a microwave signal superimposed on a pulse field due to a square current pulse. By varying the microwave excitation frequency, we identify the natural resonance frequency region of the magnetic element in which the switching is most efficient. Using micromagnetic simulations and subsequent analysis, we show that domains are formed around the foci of the elliptical element due to spin waves and couple with FMR frequencies at the edges of the element giving rise to further spin waves of edge modes and fundamental precession modes.
Direct dynamic imaging of MAS in patterned Py elements
The elements studied in this experiment are elliptical structures patterned on a film stack of Ta (2 nm)/Ni78Fe22 (Py, 30 nm). The elements were patterned in two different sizes such as a 4 × 0.4 μm2 element aligned at 45° to the current-carrying stripline (Figs. 1), and a 6 × 0.7 μm2 element aligned at 30° to the current-carrying stripline (Fig. 3). The ferromagnetic elements were fabricated beneath a 4 μm wide Ta (5 nm)/Cu (150 nm) stripline on a 75 nm thick silicon nitride (SiNx) membrane. The Py elements were patterned by standard electron-beam lithography and lift-off processing (see Methods). The current excitations in the stripline consist of a unipolar square pulse of 2 ns duration superimposed on a 4 ns long, 1.8 GHz sinusoidal microwave input pulse with a 1 ns offset in time, as seen in Fig. 1(b). The Oersted fields generated due to both the unipolar square pulse and the superimposed microwave signal are along the y-axis, therefore the initial state destabilizing magnetization dynamics is observed primarily along the y-axis. The pulse field applied during this process was -75 Oe and the microwave field was 30 Oe peak-to-peak. The microwave frequency was varied among four values, 1.5, 1.8, 2 and 2.5 GHz for both elements. At these fields, microwave-assisted switching was only successful at 1.8 GHz in the 4 × 0.4 μm2 element, but was less critical in the 6 × 0.7 μm2 element. The excitation frequency dependence of the switching process is discussed in greater detail later. The in-plane component of the magnetization was dynamically imaged employing time-resolved STXM by pump-and-probe technique (see Methods). Magnetic contrast is obtained by taking advantage of the X-ray magnetic circular dichroism (XMCD)24.
The black and white contrast in the inset of Fig. 1(b) corresponds to the direction of the magnetization along the x-axis of the element. Figures 1(c–h) show the time evolution of a typical reversal process in the element measured experimentally with both the square pulse and microwave fields. In the experiment, t = 0 is defined as the time of the onset of the 4 ns-long microwave pulse. The square pulse is turned on at t = 1 ns and reaches its maximum value at t = 1.3 ns. The irregular shape of the square pulse seen in Fig. 1(b) is due to imperfect reflection of the signals in the electrical circuitry. Figure 1(c) indicates the state of the element before switching at t = 1.27 ns, followed by domain nucleation at the foci of the elliptical element at t = 1.44 ns seen in Fig. 1(d). The formation and taper angle of the domains is influenced by both the shape-dependent demagnetizing field in the element and the consequent instability regions formed as a result of spin wave creation and propagation10,11. These domains gradually undergo relaxation and expansion processes as seen at t = 1.77 ns in Fig. 1(e). The sequence of the domain expansion processes seen in Figs. 1(e–g) indicates that the element does not follow a uniform, coherent precession switching model. The edges of the element remain unswitched until t = 2.43 ns (Fig. 1(g)) and reverse only at the end of the square pulse. This is attributed to the significantly higher demagnetizing field at the edges of the element (see Supplementary Information Fig. S1). Even though micromagnetic simulations cannot include magnetic and surface defects that contribute to domain pinning effects and other non-uniformities in the switching sequence, we have performed simulations using the object oriented micromagnetic framework (OOMMF) to confirm a reversal process that is largely similar to that of experiment (Fig. 4(a–f); see Methods for further details). The applied field direction in simulations is the same as that of experiments as shown in the inset of Fig. 1(b). The simulation results will be discussed in further detail later.
Influence of microwave assist fields in magnetization reversal
In order to demonstrate that the assistance of the microwave pulse is significant in switching the element, a set of control experiments were performed. In the first control experiment, only the square pulse excitation was applied to the stripline without the microwave excitation. The current pulse flows along the x-axis (from left to right) and the Oersted field is generated along the −y-axis. Figures 2(a–f) show the time-resolved images of the magnetic element at different time instants after the application of the square pulse at t = 1 ns. Clearly, the element undergoes partial switching along the foci of the element. However, once the pulse excitation is removed, the domains gradually annihilate and the element relaxes back to its initial state. In the second control experiment, only the microwave excitation was applied to the stripline and we see that a very weak excitation is generated in the element as shown in Fig. 2(g–i). A full switching was not possible in this case, either. These control experiments confirm that a full switching is only possible with the help of a microwave pulse on top of a square pulse field.
Influence of microwave excitation frequency on magnetization reversal process
The control experiments established the necessary contribution of a microwave field in magnetization reversal studies. However, the frequency of microwave excitation also determines the probability of successful switching. To investigate further, the 6 × 0.7 μm2 elements were subjected to microwave current pulses of four different frequencies varying from 1.5–2.5 GHz. Time-resolved images of the switching attempts at these frequencies are shown in Fig. 3(a). Complete magnetization reversal is observed at frequencies f = 1.8 GHz, 2.0 GHz and 2.5 GHz through different switching evolution processes, however, at f = 1.5 GHz partial magnetization reversal of the element is followed by relaxation to the initial state. It is well-known that the absorption of microwave energy is most efficient at the natural resonance frequency of the element and results in more abrupt and uniform switching of the element. This behavior is well corroborated by the switching sequences observed for f = 1.8 GHz and f = 2.5 GHz, which in turn suggests that the range of 1.8–2.5 GHz falls within the natural resonance frequency region of the element. The majority of the element has completed magnetization reversal at both f = 1.8 GHz and f = 2.5 GHz by t = 1.61 ns, except for the tapered regions at the edges of the element. However, the propagation of the reversed domains to the edges of the element and complete magnetization reversal occur over differing time scales for the two excitation frequencies. For example, at f = 1.8 GHz complete switching is achieved within 2.93 ns, while at f = 2.5 GHz the switching is complete only by 4.42 ns. As the demagnetizing field profiles at the element edges are the same in both cases, this observation may be attributed to the different precession angles at the two microwave excitation frequencies. As a result, the component of the applied microwave field along the hard axis of the magnetization in these regions is different for each frequency.
Another local anomaly in the switching characteristic is observed at f = 2.0 GHz, where the switching sequence by domain nucleation at the foci and subsequent propagation is similar to that of the element in Fig. 1(c–h). In fact, the domain evolution up till t = 1.77 ns at f = 2.0 GHz is similar to the non-successful switching attempt at f = 1.5 GHz. Beyond t = 1.77 ns, the element undergoes domain annihilation and gradual relaxation to its initial state at f = 1.5 GHz, but complete magnetization reversal happens within 4 ns at f = 2 GHz. Thus, the success of magnetization switching for fixed values of applied microwave and static fields depends on the frequency of the microwave excitation. Similar dependence of the switching field on the microwave frequency has been reported in micromagnetic simulations25 on elements of dimensions 1024 × 128 × 20 nm3. To confirm these similarities in switching behavior, we performed micromagnetic simulations (see Methods) to estimate the effective resonance strength across microwave excitation frequencies. As the precession angle varies with microwave excitation frequency, the standard deviation (ΔMeff) of the simulated magnetization is assumed to be a measure of the effective resonance strength. Figure 3(b) shows the variation of ΔMeff as a function of the applied microwave excitation frequency. Analogous to the experimental data, we observe larger resonances at frequencies in the range of 1.8 – 2.5 GHz as compared to that at f = 1.5 GHz. We find that spatially-varying demagnetizing field profiles and edge pinning field profiles can lead to a range of precessional frequencies and in turn cause spin wave generation.
The initiation of the switching has been previously attributed in literature to the formation of instability regions as mentioned earlier and the origin of these instabilities comes from spin wave generation. However, it is unclear to what extent spin wave generation assists in nucleation and magnetization reversal. To substantiate the influence of high-frequency spin waves in the switching process, Fourier analysis of the simulated data has been carried out in the time domain to identify the dominant frequencies. Figures 4(a–f) show the simulated magnetization profiles of the element at different stages in the reversal process, in a color scale similar to that of the experimental time-resolved images in Fig. 1(c–h). It is important to note that while the reversal stages in experiment and simulation match well, the overall process occurs at a faster rate in simulations due to the lack of any material and physical deformities, such as patterning defects. To identify the dominant frequency modes in the bulk of the magnetic element, the Fourier analysis was performed on the points along the easy axis, as indicated in the inset of Fig. 4(g). The analyzed locations pass through the magnetically-soft central regions of the element where the in-plane demagnetizing field is the lowest. Therefore, any disturbance or dynamics would be maximized along this line. Figure 4(g) shows the FFT for the mx data for a total simulation time of 6 ns. The regions between points 75–125 and 225–275 represent the foci of the elliptically-shaped element, where the internal field is at a minimum and the observed FFT spectra is at its highest intensity. This spectra exactly matches the domain nucleation and switching behavior experimentally seen in the 4 × 0.4 μm2 element shown in Fig. 4(h) at t = 1.44 ns. Clear correlation can be seen between the yellow and red dotted regions in Fig. 4(g,h). Thus, the high intensity peaks in the simulated data at a frequency of ~5.6 GHz should correspond to the local resonance frequency within these domains, as reported earlier8,26. This result confirms that spin waves may be a critical factor in a microwave assisted magnetization switching process.
In conclusion, we have directly imaged the magnetization switching dynamics under the influence of a microwave-assisted field pulse in patterned elements for the first time with sub-nanosecond temporal resolution. Excitation with a varying frequency of the microwave pulse reveals the natural resonance frequency range of the element and confirms the influence of a microwave assist field in magnetization reversal. The Fourier analysis in the time domain reveals the presence of higher local resonant frequencies at the foci of the elliptical element and matches the switching sequence observed in experimental results. This, in turn, shows that magnetization reversal depends on the spatial variation of the demagnetizing field.
Sample preparation details
The Py elements studied in this work were prepared by standard electron beam lithography, sputtering and liftoff processes. Elliptically-shaped elements of dimensions 4 × 0.4 μm2 and 6 × 0.7 μm2 were patterned using a 200 nm-thick Polymethyl methacrylate (PMMA) resist mask. A film stack of Ta (2 nm)/Ni78Fe22 (Py, 30 nm) was then deposited in a sputtering chamber with a base chamber pressure of 2 × 10−9 Torr. Following lift-off, conventional linear striplines were defined by photolithography using a 2 μm-thick Sumitomo PFI-D81B8 resist. The Ta/Cu pads were sputter-deposited followed by lift-off processing.
Time-resolved scanning transmission X-ray microscopy
The time-resolved imaging data were obtained by magnetic soft X-ray transmission microscopy at the MAXYMUS microscope (Beam-line UE46 PGM-2 at BESSY II synchrotron in Berlin, Germany), maintained by the MPI for Intelligent Systems. X-ray energy was tuned to the Ni L3 absorption edge (852.7 eV), where the XMCD effect yields the largest magnetic contrast for Py. The sample was tilted by 60° with respect to the X-ray beam to measure the mx and mz components of the magnetization with a spatial resolution of 25 nm. A fast digital pulse generator and a signal generator in combination with a frequency mixer were used to inject rectangular pulses (pulse of 2 ns duration and rising & falling times of ~300 ps), superimposed with sine wave burst pulses (pulse width of 4 ns) through a strip line to generate the in-plane magnetic field burst pulses. The field strengths are calculated from the currents and have an estimated systematic error of ~10%. In order to increase the signal-to-noise ratio and yield reasonable dynamic contrast, a stroboscopic pump-and-probe technique that averages several million excitations per imaged pixel was used. We set the repetition rate of the excitation to 12 MHz and accumulated the information of the magnetic state every 166 ps, thereby providing good temporal resolution during the reversal process. The multi bunch mode of the synchrotron was synced with the experiment to gain the complete temporal information per measured pixel simultaneously, before moving to the next pixel and so on, thus mapping the temporospatial magnetic state of the sample in one single scan. Beam-time periods at synchrotron facilities are very limited and are also known to present significant challenges in setting up an initial, successful proof-of-concept experiment. As a result, the switching experiments that we could study were constrained. For these reasons, we only present the data of MAS at two angles of rotation (30° and 45° to the –x axis) of the ferromagnetic element.
Micromagnetic simulations and Fourier analysis
The micromagnetic simulations were carried out with the object oriented micromagnetic framework (OOMMF, OOMMF User’s Guide, Version 1.0, Interagency Report NISTIR 6376 (National Institute of Standards and Technology, 1999)). We performed the simulations at cell sizes of (5 × 5 × 30) nm3 and (2 × 2 × 30) nm3 and similar results were obtained in both cases. The exchange interaction length in Py is known to be (~5 nm). Standard material parameters for Py are used in the simulations such as the saturation magnetization Ms = 860 × 103 A/m, exchange stiffness A = 1.3 × 10−11 J/m, zero magnetocrystalline anisotropy and a damping constant α = 0.01.
How to cite this article: Rao, S. et al. Time-resolved imaging of pulse-induced magnetization reversal with a microwave assist field. Sci. Rep. 5, 10695; doi: 10.1038/srep10695 (2015).
Devolder, T., Chappert, C., Katine, J. A., Carey, M. J. & Ito, K. Distribution of the magnetization reversal duration in subnanosecond spin-transfer switching. Phys. Rev. B 75, 064402 (2007).
Hui, Z. et al. Sub-200 ps spin transfer torque switching in in-plane magnetic tunnel junctions with interface perpendicular anisotropy. J. Phys. D. Appl. Phys. 45, 025001 (2012).
Liu, H. et al. Ultrafast switching in magnetic tunnel junction based orthogonal spin transfer devices. Appl. Phys. Lett. 97, 242510 (2010).
Choi, B. C., Belov, M., Hiebert, W. K., Ballentine, G. E. & Freeman, M. R. Ultrafast Magnetization Reversal Dynamics Investigated by Time Domain Imaging. Phys. Rev. Lett. 86, 728–731 (2001).
Gerrits, T., van den Berg, H. A. M., Hohlfeld, J., Bar, L. & Rasing, T. Ultrafast precessional magnetization reversal by picosecond magnetic field pulse shaping. Nature 418, 509–512 (2002).
Kovalenko, O., Pezeril, T. & Temnov, V. V. New Concept for Magnetization Switching by Ultrafast Acoustic Pulses. Phys. Rev. Lett. 110, 266602 (2013).
Paul, P. H. et al. Ultra-fast ballistic magnetization reversal triggered by a single magnetic field pulse. J. Phys. D. Appl. Phys. 42, 245007 (2009).
Stoll, H. et al. High-resolution imaging of fast magnetization dynamics in magnetic nanostructures. Appl. Phys. Lett. 84, 3328–3330 (2004).
Thirion, C., Wernsdorfer, W. & Mailly, D. Switching of magnetization by nonlinear resonance studied in single nanoparticles. Nature Mater. 2, 524–527 (2003).
Han, X. et al. Magnetic Instability Regions in Patterned Structures: Influence of Element Shape on Magnetization Reversal Dynamics. Phys. Rev. Lett. 98, 147202 (2007).
Grimsditch, M. et al. Magnetic stability of nano-particles - The role of dipolar instability pockets. Europhys. Lett. 54, 813–819 (2001).
Yanes, R. et al. Modeling of microwave-assisted switching in micron-sized magnetic ellipsoids. Phys. Rev. B 79, 224427 (2009).
Hiebert, W. K., Ballentine, G. E., Lagae, L., Hunt, R. W. & Freeman, M. R. Ultrafast imaging of incoherent rotation magnetic switching with experimental and numerical micromagnetic dynamics. J. Appl. Phys. 92, 392–396 (2002).
Bauer, M., Lopusnik, R., Fassbender, J. & Hillebrands, B. Suppression of magnetic-field pulse-induced magnetization precession by pulse tailoring. Appl. Phys. Lett. 76, 2758–2760 (2000).
Gadbois, J., Zhu, J. G., Vavra, W. & Hurst, A. The effect of end and edge shape on the performance of pseudo-spin valve memories. IEEE Trans. Magn. 34, 1066–1068 (1998).
Zhang, W. L. et al. Magnetization reversal simulation of diamond-shaped NiFe nanofilm elements. IEEE Trans. Magn. 41, 4390–4393 (2005).
Nozaki, Y., Ishida, N., Soeno, Y. & Sekiguchi, K. Room temperature microwave-assisted recording on 500-Gbpsi-class perpendicular medium. J. Appl. Phys. 112, 083912 (2012).
Nozaki, Y., Narita, N., Tanaka, T. & Matsuyama, K. Microwave-assisted magnetization reversal in a Co/Pd multilayer with perpendicular magnetic anisotropy. Appl. Phys. Lett. 95, 082505 (2009).
Nozaki, Y. et al. Microwave-assisted magnetization reversal in 0.36-μm-wide Permalloy wires. Appl. Phys. Lett. 91, 122505 (2007).
Zhu, J. G. & Wang, Y. Microwave Assisted Magnetic Recording Utilizing Perpendicular Spin Torque Oscillator With Switchable Perpendicular Electrodes. IEEE Trans. Magn. 46, 751–757 (2010).
Zhu, J. G., Zhu, X. & Tang, Y. Microwave Assisted Magnetic Recording. IEEE Trans. Magn. 44, 125–131 (2008).
Woltersdorf, G. & Back, C. Microwave Assisted Switching of Single Domain Ni80Fe20 Elements. Phys. Rev. Lett. 99, 227207 (2007).
Martín Pimentel, P., Leven, B., Hillebrands, B. & Grimm, H. Kerr microscopy studies of microwave assisted switching. J. Appl. Phys. 102, 063913 (2007).
Schütz, G. et al. Absorption of circularly polarized X rays in iron. Phys. Rev. Lett. 58, 737–740 (1987).
Laval, M., Bonnefois, J. J., Bobo, J. F., Issac, F. & Boust, F. Microwave-assisted switching of NiFe magnetic microstructures. J. Appl. Phys. 105, 073912 (2009).
Park, J. P., Eames, P., Engebretson, D. M., Berezovsky, J. & Crowell, P. A. Imaging of spin dynamics in closure domain and vortex structures. Phys. Rev. B 67, 020403 (2003).
This work is supported by the Singapore Ministry of Education Academic Research Fund Tier 1 (R-263-000-A46-112).
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Rao, S., Rhensius, J., Bisig, A. et al. Time-resolved imaging of pulse-induced magnetization reversal with a microwave assist field. Sci Rep 5, 10695 (2015). https://doi.org/10.1038/srep10695
This article is cited by
Tunable microwave susceptibility of thin truncated conical permalloy nanodisks : a micromagnetic investigation
Journal of Nanoparticle Research (2023)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.