Organic semiconductors combine optoelectronic properties with simple fabrication methods and the ability to tune the chemical structure to yield desired features, making them attractive candidates as laser materials1,2. Optically pumped lasers constructed from a broad range of conjugated polymers2 and oligomers3,4,5 have been reported. However, electrically pumped organic lasers have not yet been demonstrated due to serious luminescent efficiency roll-off under high current density. In organic light-emitting diodes, the maximum current density that allows for a high emission efficiency is approximately 1–10 A/cm2,6,7 which is considerably lower than the estimated current density necessary for electrically driven lasing (>10 kA/cm2)8,9. Therefore, a novel device structure that enables high current densities and reduces efficiency roll-off is required.

Recently, an extremely high current density greater than 30 kA/cm2 was observed in ambipolar single-crystal light-emitting transistors (SCLETs) of α,ω-bis(biphenylyl)terthiophene (BP3T, Fig. 1a)10 due to their excellent transfer properties. In this report, the current density at the roll-off point was improved to 1 kA/cm2,10 resulting from a reduced exciton quenching effect in the single-crystal transistor configuration. These results indicate that ambipolar SCLETs are promising devices for future organic lasers and reducing the lasing threshold below 1 kA/cm2 is the last remaining issue to be solved.

Figure 1
figure 1

Fabrication of a sub-micrometre one-dimensional (1D) grating structure.

(a) Molecular structure of α,ω-bis(biphenylyl)terthiophene (BP3T) and schematic fabrication steps for the soft ultraviolet (UV)-nanoimprint lithography (NIL) method. 1st step: BP3T single crystals were laminated onto a SiO2/Si substrate covered with poly(methyl methacrylate) (PMMA). A poly(dimethylsiloxane) (PDMS) mold with fine structure was also prepared. 2nd step: After spin coating UV-curable resist onto the BP3T crystal surface, the PDMS mold was pushed onto the resist film surface and irradiated with UV light, curing the resist film with the fine PDMS surface pattern. 3rd step: We completely etched the UV resist film with Ar plasma to copy the resist surface’s fine structure to the BP3T crystal surface. (b) Atomic force microscopic (AFM) images of the BP3T single crystal illustrating the 1D grating structure (350-nm period). (c) Fluorescence micrographs of BP3T single crystals without and with 1D grating.

An effective method for lowering the necessary exciton density for lasing is the application of optical resonators2. Although it is difficult to fabricate optical cavities with fragile organic single crystals, several attempts have been made. Examples include the Fabry-Pérot cavity11,12,13, microcavity14,15,16 and distributed feedback (DFB) resonator17,18,19,20,21. However, because of their relatively long cavity lengths (>2 μm), it is impossible for the Fabry-Pérot cavity and microcavity to demonstrate single-mode lasing, a property that is crucial for enhancing optical gain. In stark contrast to other cavities, the DFB structure is able to act as a single-mode resonator. However, because the sub-micrometer patterning of the organic single crystals that are necessary for the DFB cavity induces various problems, such as exciton-recombination centers and carrier traps, the fabrication of SCLETs with DFB structures is still a considerable challenge and a crucial milestone for the future development of organic lasers.

In this article, we demonstrate electroluminescence (EL) from SCLETs controlled by a sub-micrometer one-dimensional (1D) grating structure. BP3T single crystals were selected as the optical and electrical medium because of their excellent emission22, transport23 and solvent-tolerant properties24. We developed a soft UV-nanoimprint lithography (NIL) method25,26 and applied this technique to BP3T single crystals. We successfully observed modified EL from BP3T SCLETs with 1D grating structures. Additionally, the EL spectra that we obtained are well explained by Bragg diffraction and mode coupling resulting from the DFB system, enabling us to realize single-mode lasing.


Fabrication of grating resonators on fragile organic single crystals

As an initial attempt to apply the UV-NIL method, we recently succeeded in fabricating a 1D grating structure on the single-crystal surface of 2,5-bis[4-(5’-phenylthiophen-2’-yl)phenyl]thiophene and 2,5-di((E)-styryl)thieno[3,2-b]thiophene27. In this work, we have further elaborated the UV-NIL technique by largely improving fabrication processes and appropriately choosing a robust material. To this end, we selected BP3T as the material because of its excellent carrier mobilities (hole mobility >1 cm2/Vs and electron mobility > 0.1 cm2/Vs)23 and internal photoluminescence (PL) efficiency (quantum efficiency ~80%)22. We also measured an external PL efficiency of BP3T, which was 32% in powder and 13% in single crystals. A particularly important material property for high-quality UV-NIL is solvent tolerance, as the UV-NIL method requires the spin coating of photoresist on the crystal surface (Fig. 1a). BP3T crystals dissolve sparingly in most organic solvents24, so an improvement in fabrication quality is expected.

The UV-NIL process is schematically shown in Fig. 1a and explained in the Methods and Supplementary Information S1. BP3T single crystals were grown by physical vapor deposition23,28 and laminated onto a SiO2/Si substrate covered with poly(methyl methacrylate), which enabled the fabrication of SCLETs by reducing the effect of electron traps on the SiO2 surface29. A poly(dimethylsiloxane) (PDMS) mold with a fine structure was also prepared. After spin coating UV-curable resist onto the BP3T crystal surface, we pushed the PDMS mold onto the resist film surface and irradiated the resist film with the fine PDMS surface pattern using UV light curing. We completely etched the UV resist film with Ar plasma to copy the resist surface’s fine structure to the BP3T crystal surface. To obtain a superior structure to that reported previously27, we optimized several parameters, including the PDMS peeling-off conditions, UV exposure time, dry etching power and etching gas species (Supplementary Information S2).

The effectiveness of the modified method was examined by atomic force microscopy (AFM). We used Si substrates patterned by e-beam lithography and dry-etching techniques as master molds. We tested five different fine structures to judge the processing accuracy of our improved method: 1D grating patterns with periodicities of 1 μm, 350 nm and 270 nm and two-dimensional (2D) periodic pillars and holes. As shown in Fig. 1b (and Supplementary Information S3), we successfully fabricated all of these patterns on BP3T crystal surfaces. Surprisingly, the qualities of the structures were better by far than those reported previously27, indicating the improved patternability of BP3T crystals due to their excellent solvent tolerance24 and the optimized UV-NIL method. To gain further macroscopic information, we took PL images of the crystal before and after etching (Fig. 1c). The PL of BP3T single crystals is strongly confined due to the crystal’s self-waveguide effect, resulting in light emission from the crystal’s fringe only11,13,23. This light confinement is due to the perfect alignment of molecules within the crystal. In BP3T thin crystals, the transition dipoles are perpendicular to crystal surface. Therefore, PL light reveals TM polarization23. However, the PL image clearly exhibited a different color emission from the crystal surface for the BP3T single crystals with 1D grating (350 nm period), suggesting luminescence control by the DFB system.

Fabrication of ambipolar organic SCLETs with a grating resonator

Following our success in crystal patterning, we fabricated SCLETs using BP3T single crystals with DFB cavities according to the method described by Sawabe et al10. The structure of the SCLET with 1D grating structure is shown in Fig. 2a,b. Au and Ca asymmetric electrodes were used to match the metal-electrode work function to the highest- and lowest-occupied molecular orbitals of BP3T11,23. Moreover, we used cesium fluoride (CsF) thin films (thickness ~0.6 nm) as an electron injection buffer layer10. The output and transfer characteristics of this device revealed clear ambipolar transport (Fig. 2c,d). The estimated hole and electron mobilities from the transfer curve were 2.1 and 0.014 cm2/Vs, respectively. We observed clear light emission during ambipolar transport, even though the electron mobility of this device was considerably smaller than typical BP3T single crystal transistors (>0.1 cm2/Vs)23. Because the electron mobility of etched crystals was extremely sensitive to UV exposure time, we optimized this parameter and realized detectable light intensities (Supplementary Information S4).

Figure 2
figure 2

BP3T SCLETs with a DFB resonator.

(a) Schematic structure of the BP3T SCLET with the 1D grating. (b) Optical micrograph of the fabricated SCLET with CsF/Ca and Au asymmetric electrodes. (c) Output characteristics of a BP3T single-crystal ambipolar device with 350-nm-period 1D grating at various applied gate voltages (Vg). (d) Transfer characteristics of the device at VD = 200 V. (e) An EL spectrum from a BP3T single-crystal SCLET during ambipolar operation with 350-nm period 1D grating (red line) and a PL spectrum from the same device (blue line). A PL spectrum from a BP3T single crystal without grating is also shown by the black line.

Similar to that of PL, the EL from BP3T SCLET with a 350-nm 1D grating structure was from surface emission (Supplementary Information S5). To further confirm the effect of the grating structure, we measured both PL and EL spectra from patterned BP3T SCLET and compared these spectra with PL from BP3T SCLET without any grating structure (Fig. 2e). The emission spectra from SCLET with the DFB system are narrower than those from non-patterned BP3T single crystals, confirming the successful control of luminescent properties by the 1D structure.

We fabricated 6 BP3T SCLETs with a 1D grating structure to investigate the device statistics (Supplementary Information S6). Four of the six devices revealed ambipolar transport, whereas we observed only p-type behavior for the other two transistors. In stark contrast to the similar hole mobilities among the six devices (1.1 - 2.1 cm2/Vs ), the electron mobilities that we obtained were scattering (3.5 × 10−3 – 1.4 × 10−2 cm2/Vs), suggesting again that the electron mobility of patterned crystals is easily affected by UV irradiation. Although two of the six transistors showed unipolar characteristics, we observed obvious light emission from all devices and their wavelength was controlled by the DFB system. In particular, in the ambipolar BP3T SCLETs with a 1D grating structure, the light emitting zone was controlled by gate voltages, as reported in other ambipolar SCLETs (Supplementary Movie)30,31,32.

Moreover, we should compare the device performance of patterned BP3T SCLETs with BP3T SCLETs without etching (Supplementary Information S7). As we noted above, the hole mobilities of etched transistors (1.1 - 2.1 cm2/Vs) are close enough to those of normal transistors (0.2 - 1.64 cm2/Vs)10,13,23. However, the mobilities of electron transport in patterned BP3T SCLETs (3.5 × 10−3 – 1.4 × 10−2 cm2/Vs) are approximately one or two orders of magnitude smaller than those of reported BP3T SCLETs (0.17 – 0.2 cm2/Vs)10,13,23, indicating that there is still plenty room for improvement through optimizing the fabrication process and through the possibility of increasing the current density.

Interestingly, in Fig. 2e, both PL and EL spectra exhibited peak splitting in the SCLET with 1D grating. This splitting behavior might be explained by the Bragg scattering of propagated emission inside single crystals33 or by a photonic band gap34,35. It is very difficult to collect light emission that is exactly normal to the surface of crystals and in the DFB system, the slight difference from the normal leads to peak splitting that is due to the Bragg scattering of propagated light. Moreover, if there is a non-negligible photonic band gap in the photonic crystal of the DFB system, peak splitting will be observed even in spectra from the correct direction. Therefore, we cannot determine the origin of the peak splitting in Fig. 2e without taking angular dependent measurements.


To gain additional information about the peak splitting in the patterned BP3T crystal (Fig. 2e), we investigated the angular dependence of the PL spectra (Fig. 3a). As shown in Fig. 3b, PL spectra from BP3T crystals with DFB systems were narrower than from un-etched crystal and a clear angular dependence was observed, providing us with the opportunity to evaluate the grating structure in detail. In contrast to Fig. 2e, the resonance peak in Fig. 3a was a single peak, eliminating the possibility of peak splitting by a photonic band gap and suggesting that the effect of the Bragg scattering is caused by difficulties in running experiments from the normal direction. Additionally, we observed two resonant peaks at wavelengths of 565 and 706 nm. Assignment of these peaks is critical in designing superior resonators for laser applications. As a first step, we attempted to determine the waveguide mode using polarized PL measurements. In 1D diffractive gratings, light propagates parallel to the grating vector and the polarization direction is dependent on the guiding mode (transverse magnetic (TM) or transverse electric (TE)). Due to this relationship, the PL polarization direction is parallel to the grating vector in TM mode. The polarization direction is reversed in TE mode. As shown in Fig. 3c, the guiding mode in our BP3T single crystal with 1D diffractive grating was assigned to the TM mode because polarized PL emission was observed parallel to the grating vector. The TM mode is also reasonable because transition dipole moments in BP3T thin crystals are perpendicular to the crystal surface23.

Figure 3
figure 3

Optical properties of BP3T single crystals with a DFB resonator.

(a) Schematic representation of angular-dependent PL measurements in BP3T single crystals with grating. (b) Top: a PL spectrum from a BP3T single crystal without a grating structure. Bottom: Angular dependence of PL spectra from BP3T single crystals with 350-nm 1D grating. (c) Polarized PL spectra from a BP3T single crystal with 350-nm 1D grating. Red and black correspond to polarization directions that are parallel and perpendicular, respectively, to the grating vector of the 1D grating. (d) Surface profile of a BP3T single crystal with a 350-nm-pitch grating structure. The height, depth and grating period were determined to be approximately 363, 178 and 350 nm, respectively. (e) Refractive index dispersion of a BP3T single crystal. (f) Angular dependence of observed and predicted PL peak wavelength (Blue: TM0 mode, Red: TM1 mode).

Because lower-order TM modes are superior to higher-order TM modes as resonators, we next attempted to determine the order of each TM mode at wavelengths of 565 and 706 nm. For this analysis, we used the following simple equation to establish the 1D periodic structure:

where m is the Bragg diffraction resonated order; λ is the propagating light wavelength; neff is the effective refractive index of the grating layer; and Λ is the grating period2. From the PL spectra at 0° (Fig. 3b) and AFM observations (Fig. 1b), λ and Λ were experimentally determined to be 560 and 350 nm, respectively. Because the light emission that is normal to grating surface is cancelled out when m is odd33, the observed surface emission indicates that m is even (Fig. 1c).

Moreover, neff can be calculated for each TM mode on the basis of the crystal thickness, grating depth, grating structure and anisotropic refractive indices of the BP3T crystal36,37,38. Because the grating structure of BP3T is a dielectric composite that consists of BP3T line, space and air regions, the average refractive index of the grating layer neff can be estimated by

where f1, f2 and f3 are the volume fractions and n1, n2 and n3 are the refractive indices of the BP3T line, space and air regions, respectively (n3 = 1)37. From the AFM height profile of BP3T single crystals with a 350-nm-period grating, volume fractions were determined to be f1 = 0.51, f2 = 0.25 and f3 = 0.24 (Fig. 1b and 3d).

In addition, we estimated that the refractive index of BP3T crystals from the emission spectra’s interference modulation, which is caused by a pair of parallel crystal edges36,37. Figure 3e presents the refractive index dispersion of BP3T single crystals. The refractive indices of BP3T single crystals at 565 and 706 nm are 2.60 and 2.30, respectively. Based on these refractive indices of BP3T single crystals, we calculated n1 and n2 with a three-layer planar waveguide model (air/BP3T/SiO2) using refractive indices of air (nair = 1) and SiO2 (nSiO2 = 1.47). The effective refractive indices depend on the material thicknesses as well as the thicknesses of the line and space regions of the BP3T grating, which were 363 and 185 nm, respectively.

Profiles of the effective refractive indices were calculated using the eigenmode expansion method with electromagnetic wave analysis software (camfr). Table 1 presents the calculated refractive indices and DFB resonating mode m for each TM mode order. From this table and equation (1), we can uniquely determine the resonating mode (m = 2) and assign the two resonant peaks at 565 and 706 nm as TM1 and TM0, respectively. To verify our assignments, we calculated the predicted angular dependence and compared it with experimental results (Fig. 3f), in which the observation is qualitatively well explained by the prediction. The quantitative difference between observation and prediction might be caused by the volume fraction f, which is estimated from the AFM height profile. However, as shown in Fig. 3d, our etching accuracy is still insufficient and would lead to larger differences between observation and prediction at higher angles, which is revealed in Fig. 3f.

Table 1 Summary of effective refractive indices and DFB resonating mode.

Because the lower-order feedback of the TM mode is superior to higher-order feedback for stronger light confinement, it is critical for the resonant condition of the TM0 mode to be at the top of the PL spectrum peak for electrically driven lasers. However, first-order feedback requires a higher resolution to produce the periodic structure. A 1D grating structure with a periodicity of 270 nm is needed to match the DFB resonant peak to the maximum PL intensity of BP3T single crystals. Our improved UV-NIL method perfectly meets this requirement and successfully demonstrates peak matching between the maximum PL intensity and TM0 mode (Supplementary Information S3 and S8).

We should discuss the optoelectrical device parameters of the patterned BP3T SCLETs, which include external quantum efficiency (EQE) and maximum brightness. As shown in the PL emission, EL spectra also revealed strong angular dependency and without knowing the detail of the angular dependence of the EL emission, we cannot derive the EQE of BP3T SCLETs using the DFB system. However, it is very difficult to collect angular dependent EL spectra under constant voltage applications. To solve this problem, we applied the results of angular dependence in the PL spectra to the analysis of EL optoelectrical parameters. We thereby obtained a maximum brightness of 1.13 × 10−8 W and an EL EQE of 1.72 × 10−3%. Although the obtained EL EQE is much smaller than the single-crystal PL EQE (13%), our result is approximately one or two orders higher than in a previous report using similar materials, in which the reported EQEs in SCLET with and without the grating structure were 4.9 × 10−5% and 3.7 × 10−4%, respectively18.

To investigate the potential of BP3T crystals as electrically driven organic semiconductor lasers, the lasing properties of patterned BP3T crystals were examined through high-energy optical pumping. To match the BP3T single-crystal absorption band edge13, we selected a pump laser with a wavelength of 481 nm. Emission from the grating feedback structure was detected from the substrate’s surface. As shown in Fig. 4a, we observed single-peak emission under strong excitation, which can be attributed to the TM1 mode. Moreover, both the integrated intensity and emission line width exhibited threshold behavior (Fig. 4b), providing solid evidence of single-mode lasing.

Figure 4
figure 4

Single-mode lasing in BP3T single crystals with a DFB resonator.

(a) PL spectra from a BP3T single-crystal surface with a 1D grating structure (350-nm pitch). Black and red lines correspond to excitation under and over the lasing threshold, respectively. (b) Dependence of PL integrated intensity and full width at half maximum (FWHM) on pump fluence.

The estimated lasing threshold from Fig. 4b is 407 μJ/cm2, which is slightly smaller than the previously reported threshold of amplified spontaneous emission (ASE) in BP3T single crystals without a patterning process (520 μJ/cm2)13, suggesting that the optical gain due to the DFB system is not significant. Although one of the possible origins may be the effect of etching damage, this origin can be ruled out by comparing the ASE thresholds between single crystals with and without etching (Supplementary Information S9), which indicates that insufficient processing accuracy might be the reason for the relatively large lasing threshold.

Finally, we estimated the necessary current density for electrically pumped lasing from the optical threshold and compared it with our achievable current density. We obtained the lowest lasing threshold for a BP3T single crystal with a DFB grating of 407 μJ/cm2. This corresponds to a photon density of 9.8 × 1014/cm2 in the pump laser (excitation laser wavelength of 481 nm). Because the absorption coefficient of BP3T single crystals at 481 nm and the thickness of etched single crystals are 0.052 /μm39 and 363 nm, respectively, the excitation density at the lasing threshold (Nth) is approximately 5.1 × 1017 /cm3. This is the minimum exciton density necessary for lasing and must be generated electrically (by EL) to reach the threshold for electrically pumped laser. Importantly, our laser pulse (800 ps) is much shorter than the single exciton life time in the BP3T crystal (τ = 1.68 ns)22. Assuming that there are no other optical losses, e.g., from carrier-induced absorption, exciton-exciton annihilation and light losses during propagation inside single crystals, then the lasing threshold for the injection current can be estimated by the following equation

where q is the electrical charge, WRZ is the width of the recombination zone (typically 3 μm in BP3T SCLETs)40 and χ is the formation ratio of the singlet exciton (0.25). Moreover, the threshold current density is strongly dependent on the thickness of charge accumulation layer. To calculate the current densities, we assumed an accumulation layer thickness of 1 ML for the BP3T single crystal (3 nm) because it has been reported that carrier conduction occurs in only one or two molecular layers at the organic/dielectric interface10. Using the accumulation layer thickness, we estimated that the necessary current density is approximately 58 kA/cm2, which is 4 times as high as the maximum current density in BP3T SCLETs with the DFB grating (15 kA/cm2) and twice as high as the reported highest value among ambipolar BP3T SCLETs (33 kA/cm2)10. Note that the estimated necessary current density is a minimum estimation because we did not take into account any optical losses, such as carrier-induced absorption, exciton-exciton annihilation and light losses during propagation inside a single crystal. However, as we discussed above, there is still plenty of room for improvement through optimizing the fabrication process, which leads to a decrease in necessary current density for lasing and an increase in the achievable maximum current density in SCLETs.

In summary, we fabricated 1D and 2D grating structures with UV-NIL and dry-etching methods. We observed clear resonant effects that are caused by the 1D grating structure and more importantly, single-mode lasing was performed under strong photo excitation. Moreover, we succeeded in fabricating ambipolar SCLETs with DFB resonators. These results strongly indicate that the fabrication of photonic crystals with BP3T single crystals is a promising approach to creating new types of organic lighting and lasing devices because of their high refractive index,37 high luminescent efficiency,22 and high carrier mobility.23 The robustness of an organic crystal typified by B3PT underpins these approaches.


Crystal Growth and Substrate Preparation

Single crystals of BP3T were grown by physical vapor transport under an Ar gas stream, which was developed by Bisri et al.23 A highly doped silicon wafer with a 500-nm thermally oxidized SiO2 layer was spin-coated with poly(methyl methacrylate) (PMMA, Sigma Aldrich, St. Louis, Missouri, United States, CO., average Mw ~120,000). The substrate was annealed at 100 °C for 24 h under a N2 atmosphere.

UV-nanoimprint lithography (NIL)

UV-NIL is schematically shown in Fig. 1a and Fig. S1. A Si master mold was patterned by e-beam lithography. We fabricated poly(dimethylsiloxane) (PDMS) molds by pouring a mixture of PDMS precursor and curing agent (10:1 by weight) into the Si master mold. We used SIM-260 and CAT-260 as the PDMS precursor and curing agent, respectively, which were provided by Shin-Etsu Chemical Co., Ltd., Chiyoda, Tokyo, Japan. After thermal curing of the mixture at 70 °C for 1 h and 150 °C for 2 h, the PDMS mold was separated from the master mold. We also spin-coated UV-curable resist (NICT-82) provided by the Daicel Corp., Osaka, Osaka, Japan. (50 w % in 2-methoxy-1-methylethyl acetate) at a speed of 500 rpm for 5 s and 2,000 rpm for 10 s onto the SiO2/Si substrate with BP3T crystal. The thickness of the UV-curable resist film was approximately 1.5 μm, which was higher than that of BP3T single crystals (<<1 μm). The typical UV irradiation time was 40 min under a N2 atmosphere at ambient pressure. After rest curing, the sample was carefully separated from the PDMS mold. Finally, the UV-curable resist was etched by a SAMCO, Kyoto, Kyoto, Japan. 200iP Inductively Coupled Plasma (ICP) Etching System using Ar gas for 20 min. The ICP power and bias power were set to 90 and 25 W, respectively and the Ar flow rate was 22 sccm. The process chamber pressure was maintained at 2.0 Pa. The etching rate of the organic single crystal and the UV-curable resist were approximately 40 and 60 nm/min, respectively. The surface properties were measured by atomic force microscope (Bruker Corp., Billerica, Massachusetts, United States, Multimode 8).

SCLET fabrication

We fabricated SCLETs with the method described by Sawabe et al.10 The structure of the SCLET with a 1D-grating device is given in Fig. 2a,b. We laminated BP3T single crystals onto the PMMA layer to reduce electron traps and then introduced grating structures to the BP3T single crystal with UV-NIL. Au and Ca asymmetric electrodes were used to promote hole and electron injections. We considered energy level matching between the metal electrode work function and BP3T molecular levels, such as the highest-occupied molecular orbital (HOMO) and lowest-unoccupied molecular orbital (LUMO) levels. We also used cesium fluoride (CsF) thin films (thickness ~ 0.6 nm) as an electron-injection buffer layer. Electrical characterization of the device was performed inside a dark glove box using a semiconducting parameter analyzer (Agilent Technologies, Santa Clara, California, United States, B1505A).

Optical measurements of BP3T single crystals

EL and PL spectra were collected through an optical microscope (Keyence Corp., Osaka, Osaka, Japan, VH-Z100R) by spectrograph (Newport Corp., Irvine, California, United States, FIC-model 77440) with a Peltier-cooled detector (Andor Technology, Belfast, Contae Aontroma, Northern Ireland, DV401A-UVB). The angular dependence of the PL spectra was also collected by a rotatable optical microscope (Keyence Corp., Osaka, Osaka, Japan, VH-Z100R). Polarized PL spectra were measured through a polarizer that was mounted on an optical microscope (Olympus Corp., Shinjuku, Tokyo, Japan, BX51 M) and were collected by a Shamrock SR303i (Andor Technology, Belfast, Contae Aontroma, Northern Ireland). The photo-pumped laser spectra were collected by irradiating the BP3T samples with a pulsed laser beam and the lasing characteristics were observed normal direction to the crystal surface. The pump pulses were generated by a dye laser (Coumarin 481, Exciton Corp., Dayton, Ohino, United States) that was excited by a nitrogen gas laser (Optical Building Blocks Corp., Edison, New Jersey, United States, GL-3300 λ = 337 nm with a pulse width of 1ns). The pump pulses were generated at a wavelength of λ = 481 nm, chosen to match the BP3T absorption band edge and a pulse width of 800 ps. A neutral density filter was used to adjust the excitation intensities. The laser beam was focused on BP3T crystals with a size of 0.52 mm2 and an incident angle of 45 degree. The photo-pumped DFB laser emission from a BP3T single crystal was collected through the microscope (Nikon Corp., Chiyoda, Tokyo, Japan, eclipse) with a multichannel spectrograph (Lambda Vision Inc., Sagamihara, Kanagawa, Japan, SA-100C-HPCB/C). The photo-pumped laser measurements were performed under atmospheric conditions at room temperature.

Additional Information

How to cite this article: Maruyama, K. et al. Ambipolar light-emitting organic single-crystal transistors with a grating resonator. Sci. Rep. 5, 10221; doi: 10.1038/srep10221 (2015).