Abstract
The biomass-derived activated carbons (ACs) have been prepared with high surface areas up to 793ām2āgā1 is by ZnCl2 activation at three different temperatures, viz. AC700, AC800 and AC900. The AC samples were characterized by a variety of analytical and spectroscopy techniques. The as-synthesized ACs were adopted for the simultaneous electrochemical detection of ascorbic acid (AA), dopamine (DA) and uric acid (UA). For comparison, reduced graphene oxide (RGO) was employed for the proposed sensor. The high surface area, modulated pore size and the presence of oxygen surface functional groups like heteroatoms (83.427% C, 1.085% N, 0.383% S and 0.861% H) in the biomass-derived AC is found to be responsible for the excellent catalytic activities of biomolecules. Fascinatingly, the facile sensor further used to detect biomolecules levels in the snail hemolymph and human blood serum. Notably, the obtained analytical parameters for the biomolecules detection over the AC modified GCE, outperforming several carbon-based modified electrodes in literatures.
Similar content being viewed by others
Introduction
Multidimensional (0, 1, 2 and 3D) carbon based materials have been extensively utilized for various applications, such as adsorbents, supercapacitors, batteries and electrodes1,2,3,4,5. Among them, graphene is a top candidate in various electrochemical aspects. However, its preparation from graphite is an intricate procedure which may lead to an explosion during the oxidation of graphite. Likewise, the preparation of carbon nanotubes (CNTs) also has practical difficulties because of their complicated instrumental setup. Besides, the preparation of activated carbons (ACs) from bio-wastes are simple, environmentally friendly and cost-effective. In evidence, ACs prepared from various bio-wastes have been widely used in numerous applications, owing to their unique properties, such as ultra high surface area, micro-mesopore volume, low toxicity, excellent chemical stability, electrical conductivity and presence of oxygen surface functional groups like heteroatoms5,6,7,8,9. Notably, the availability of literature reports on ACs for electrochemical sensor application is scarce. Moreover, the AC from pumpkin stems has not been explored much, a very few reports available on ACs prepared by using phosphoric acid activation towards the Phenol and Chlorophenol Adsorption10,11.
Ascorbic acid (AA) is a vital vitamin in the human diet and it is used as antioxidant and treatment of cancer, common cold, mental illness and AIDS12,13. Likewise, Dopamine (DA) is an important neurotransmitter which is widely distributed within the mammalian central nervous system (brain, renal, hormonal and cardiovascular systems, etc). Low levels of DA may lead to many diseases (Parkinsonās, schizophrenia, etc.)14,15,16,17. In addition, uric acid (UA) is the end product of primary purine metabolite and its abnormal concentration level in the human body symptomatic several diseases, such as hyperuricemia, leukemia and pneumonia18,19. Moreover, it is well known that the AA, DA and UA coexist in the central nervous system and serum. However, the simultaneous determination with selectivity and sensitivity is impossible by using solid electrodes due to their overlapping oxidation peak potentials20, insufficient surface area and also many research have been focused to separate their peak potentials21. In particular, carbon-based nanomaterials have been widely used for the simultaneous electrochemical detection of AA, DA and UA with enhanced sensitivity4,22,23.
Herein, we report a novel and efficient electrodes for the simultaneous and selective determination of AA, DA and UA with enormous catalytic activities by using biomass-derived ACs for the first time. Notably, the obtained analytical parameters of biomolecules detection over the as-synthesized ACs, overwhelming the several carbon-based electrodes.
Results and Discussion
Figure 1 shows the representative FE-SEM, FE-TEM, XRD and XPS pattern of the as-synthesized AC. As shown in Fig. 1a, the FE-SEM image of AC700 displays a bundle-like porous morphology, different from the structure of RGO (Figure S1a) and unactivated carbon (Figure S1b). Further FE-TEM (Fig. 1b) study revealed that as-synthesized AC700 contains the mesoscopic pores with short-range ordering, indicating the presence of multi-dimensional wormhole-like pore structure24,25. The XRD pattern of AC700 (Fig. 1a inset) shows two broad diffraction peaks at 23Ā° and 43Ā°, corresponding to the (002) and (101) plane reflection and reveals the amorphous behavior of the AC6. In addition, Fig. 1c shows the XPS survey spectra of AC700 exhibits the peaks corresponding to carbon and oxygen. Furthermore, CHNS elemental analysis was carried out to confirm the presence of heteroatoms in AC surface and they are determined to be 83.427% C, 1.085% N, 0.383% S and 0.861% H (see Table S1)1,5. Owing to the lower concentrations of heteroatoms, the XPS spectra has failed to show their corresponding peaks. However, the main advantage of the AC is the presence of heteroatoms like nitrogen and sulfur in nature without any doping, it may due to the biowaste precursors contain some small amounts of heteroatoms naturally, which may lead to the enhanced electrochemical behavior. Figure S1c and Figure S1d shows the N2 sorption studies of the ACs and unactivated carbon, respectively. The unactivated carbon provides a surface area of about 47.76ām2āgā1 was calculated by the BrunauerāEmmettāTeller (BET) model. Using the BJH model, the calculated pore volume was 0.06ācm3āgā1 as shown in Figure S1d. Besides, the ZnCl2 activated carbons provided the excellent surface areas of AC700, AC800 and AC900 are 793.2, 715.1 and 779.7, m2gā1 with pore volumes of 0.4, 0.35 and 0.36ācm3āgā1, respectively1,5. Furthermore, the pore size distribution curves (Figure S2a) designate the ACs are having well developed micro-mesopores. In order to investigate the structure of the as-prepared carbon materials, the Raman spectroscopy were performed. As shown in Fig. S2b, the activated carbons were showed the two sharp peaks at 1320 (D band) and 1592 (G band), which corresponds to the sp2 carbon and also the intensity of the D band is higher than G band, which designates the AC is amorphous in nature.
The voltammetric responses of different electrodes towards the simultaneous determination of AA, DA and UA mixture were performed by cyclic voltammetry (CV). As shown in Fig. 2, the bare GCE (curve d) fails to separate the three peaks, resulting in a broad and overlapped peak around 0.4āV containing a mixture of 30āĪ¼M AAā+ā10āĪ¼M DAā+ā20āĪ¼M UA concentrations in N2 saturated PBS at the scan rate of 50āmVāsā1. As evidenced, the peak potential separation of three biomolecules is impossible at the bare GCE. Besides, we obtained a well-defined oxidation peaks for AA, DA and UA at AC700 modified electrode (curve a), whereas no peaks observed for the blank measurement (curve b), which confirms the obtained peaks are corresponding to the three biomolecules. In order to optimize the suitable AC modified electrode towards AA, DA and UA, CVs were performed at UAC (unactivated carbon), AC700, AC800 and AC900, as shown in Fig. 2 inset. Among them, AC900 and AC800 displays enhanced peak currents, but possess with higher potentials than the AC700 electrode, which reveals the result with its high surface areas of ACs. However, AC700 exhibits a lower overpotentials with good peak to peak separations (AA-DAā=ā217, DA-UAā=ā129 and AA-UAā=ā346) of each analytes with more sufficient current intensities even at lower concentrations of biomolecules. By taking the advantage of the lower over the potentials of biomolecules, we choose the AC700 as an optimized electrode for further studies and possible reaction mechanism of the biomolecules as shown in Fig. 1d.
As shown in Fig. 2 (curve c), in comparison with RGO (AA-DAā=ā169, DA-UAā=ā143 and AA-UAā=ā312), our AC700-modified GCE exhibits a good peak to peak separation with several times larger current intensities of the three biomolecules (see Table-S2). Evidently, our AC700-modified GCE outperform all other electrodes due to their high surface area with micro/meso pores. The attributed results validates that the AC700-modified GCE possesses a good electrocatalytic activity towards AA, DA and UA. Figure S3 shows the corresponding cyclic voltammograms of AA, DA and UA the AC700-modified GCE with different scan rates in a pH 7 PBS buffer solution at the same concentrations of three molecules. Both peak potential (Ep) and peak current (Ip) is affected by varying the scan rates and the CVs clearly displays that the oxidation peak currents (Ipa) were increased with the increasing scan rates, whereas the peak potentials slightly shifts positively. For all of three biomolecules, the anodic currents were linear with the square root of the scan rate (inset to Figure S3) in the range of 50ā500āmVāsā1. The corresponding linear regression equations are, IPa (Ī¼A)ā=ā2.2157x - 10.592āV1/2 (mV/s) AA, IPa (Ī¼A)ā=ā1.6543x - 9.0433āV1/2 (mV/s) DA and IPa (Ī¼A)ā=ā1.6609x - 4.1972āV1/2 (mV/s) UA, with linear relative coefficients of 0.985, 0.9913 and 0.9915, respectively.
Hence, the kinetics of overall process were controlled by a diffusion process of AA, DA and UA on the surface of AC700-modified GCE. Moreover, the electrode reaction of DA and UA was quasi-reversible as the redox peak potentials vary with the scan rates. Moreover, while increasing the oxidation peaks of three biomolecules, the capacitances also increased, which can be attributed to the pseudocapacitive contribution from the oxygen surface functional groups and heteroatoms as shown in Table S1. These groups can improve the wettability and maximize the electroactive surface area23,26.
To investigate the sensitivity for the simultaneous determination of AA, DA and UA, differential pulse voltammetry (DPV) has been adopted which is more sensitive than the other techniques. DPV was carried out in the potential range of ā0.2 to 0.6āV at AC700-modified GCE in N2 saturated PBS (pH 7.0) solution. Fig. 3 shows the DPVs at different increasing concentrations of AA, DA and UA with well separated anodic peaks. Moreover, peak currents were increased with the increasing concentration of three biomolecules, corresponding linear response curves for three biomolecules are shown in Fig. 3 inset (concentration vs increasing current). The calculated sensitivity for AA, DA and UA are, 7.6, 6.3 and 6.1āĪ¼AāĪ¼Mā1ācmā2 and the obtained lower detection limits (LOD) were 2.3, 0.03 and 0.51āĪ¼M, respectively. The extraordinary analytical parameters of the reported biosensor at AC700-modified GCE surpassing the previously reported carbon based nanomaterials as shown in Table 1.
To investigate the selectivity and cross reactivity of each biomolecule, the DPVs were performed when the concentration of one biomolecule changed, whereas the other two biomolecules kept at constant as shown in Fig. 4. Figure 4a shows the DPVs of AC700-modified GCE at increasing concentrations of 30-95āĪ¼M AA in the presence of 10āĪ¼M DA and UA, indicating that AA holds good selectivity in the presence of DA and UA. The inset of Fig. 4a shows the corresponding calibration plots of the AA concentrations vs peak currents. Similarly, DPV experiments were conducted with DA and UA (Fig. 4b,c), in the presence of 33āĪ¼M AA and 20āĪ¼M UA or 30āĪ¼M AA and 10āĪ¼M DA, indicates the Ipa of DA and UA is well linear with their increasing concentrations as shown in the insets, respectively. As shown in Table S2, for selective analysis, the calculated detection limits and sensitivities of the three biomolecules are more similar to the simultaneous analyses, which evidenced that our AC modified GCE is more favorable for the simultaneous determination even at their lowest concentration. For the further evidence, as shown in Fig. 4dāf, we have performed the cross reactivity of each analytes, when the concentrations of two biomolecules changed, whereas the concentration of other biomolecule kept constant. Notably, Fig. 4dāf displays the DPVs at increasing concentrations of two biomolecules in the presence of one molecule, indicating that our AC-modified GCE is more feasible towards the selective and simultaneous determination of AA, DA and UA. The obtained results are indirectly indicates the good repeatability, reproducibility of our AC700-modified GCE towards the biomolecules determination in real sample analysis. The attributed results are due to the large surface area, more active sites and the shapes of isotherms suggest that the high-energy adsorption sites on AC, leading to improved sensitivity for the detection of biomolecules.
In addition, to compare the catalytic oxidation behavior of the as-synthesized AC700 material with RGO, DPVs were performed towards the selective determination of DA in N2 saturated PBS (pH 7.0) solution. As shown in Figure S4, for AC modified GCE, the oxidation peak current of DA was observed at 0.162āV and 0.182āV for RGO and the peak currents linearly increased with increasing concentrations of DA from 5āĪ¼M to 230āĪ¼M, while 5āĪ¼M to 115āĪ¼M for RGO. The linear equation of AC700-modified GCE is Ip/Ī¼Aā=ā0.1541 [DA]/Ī¼AĪ¼Mā1ā+ā4.1821 and for RGO is Ip/Ī¼Aā=ā0.068 [DA]/Ī¼AĪ¼Mā1 +0.294 and R2ā=ā0.9802. The calculated sensitivity of AC700-modified GCE is 2āĪ¼AāĪ¼Mā1ācmā2 and for RGO-modified GCE is 0.76āĪ¼AāĪ¼Mā1ācmā2. The calculated lower detection limit (LOD) for AC and RGO modified GCEs towards DA detection is 0.045āĪ¼M and 0.5āĪ¼M, respectively, according to the formula LODā=ā3 sb/S (where sb is the standard deviation of the blank signal and S is the sensitivity). The results clearly evidenced that the analytical parameters of the reported AC700-modified GCE in this study are more comparable with RGO-modified GCE (see Table S2). The attributed results are may because of the presence of oxygen surface functional groups and heteroatoms in the as-synthesized AC with high surface area and modulated micro/meso pore sizes. Hence, the AC modified GCE is more suitable for the highly sensitive determination of biomolecules.
In order to prove the real time application of the proposed sensor, snail hemolymph was collected from Taiwan, since it contains dopamine neurons level27,28,29. Interestingly, the 10āml of snail hemolymph extracts was analyzed by two DPV methods as shown in Fig. 5. First, we directly examined the snail hemolymph extracts without DA concentration. Fig. 5a displays the DPV curves at different concentrations (100ā600āĪ¼L) of snail hemolymph (as analyte) extracts containing in 0.1āM PBS solution (pH 7.0). Fascinatingly, we obtained the corresponding peak of DA with increasing oxidation peaks while increasing the concentration of snail hemolymph. Furthermore, we have diluted the average quantity of DA concentration in snail hemolymph.
As shown in Fig. 5b (experimental conditions are similar to Fig. 5a), the corresponding oxidation peak currents were increased linearly with increasing DA concentration. Remarkably, we achieved a higher sensitivity (4.9āĪ¼AāĪ¼Mā1ācmā2) and very lower detection limit (0.04āĪ¼M) and the obtained results on snail hemolymph extracts are more feasible when compared to the lab sample analysis. In addition, the AC700-modified GCE was further tested for detection of biomolecules in real samples in human serum, the good electrochemical response was observed with the recoveries ranged between 95.2 and 104.4%, as summarized in Table S3. The superior recovery observed for biomolecules in the presence of real samples, indicates the AC-modified electrode is more reliable in practical industrial applications.
In conclusions, the high surface areas of ACs were synthesized by using a simple ZnCl2 activation method and characterized by a variety of analytical and spectroscopy techniques is reported. The as-prepared AC sample showed a noteworthy performance for the reported biosensor. The AC700 outperform the other AC modified electrodes and RGO with excellent catalytic activities and quasi-reversible redox behaviors observed during the detection of biomolecules. Notably, the calculated low detection limits and ultra high sensitivity of the biomolecules detection over AC700-modified GCE, overwhelming the numerous carbon-based modified electrodes. In addition, the reported biosensor provides a remarkable performance in snail hemolymph and human blood serum.
Methods
Materials
Ascorbic acid, dopamine and uric acid were obtained from Sigma Aldrich, Zinc chloride (ZnCl2) from Wako. All solutions were prepared with deionized water with a resistivity of 18āMĪ©/cm Millipore. All chemicals were used as received without any further purification.
Instrumentation
The cyclic voltammetry (CV) and differential pulse voltammetry (DPV) studies were performed using a CHI900 electrochemical analyzer (CH instruments). A conventional three-electrode cell system was used with an AC-modified glassy carbon electrode (GCE) as the working electrode, an Ag/AgCl (saturated KCl) reference electrode and a platinum wire as the counter electrode. The elemental analysis was carried out using āelementar Vario EL cubeā (for CHNS, German). The surface morphology of the film was studied using JEOL field-emission scanning electron microscopy. X-ray diffraction was performed on a Rigaku, MiniFlex II instrument. The N2 adsorption-desorption isotherms and pore size distribution was analyzed by using āMicromeritics ASAP 2020ā.
Synthesis of ACs and RGO
The ACs were synthesized by using a simple and eco-friendly method reported elsewhere30. Briefly, pumpkin stems (Cucurbita pepo) was collected from Dharmapuri (Tamilnadu, India) and washed thoroughly, dried in an oven at 100āĀ°C. The dried pumpkin stems were pulverized and preheated at 150āĀ°C for 2 days. Then, desired amount of preheated sample was activated with 10% of ZnCl2 for 24āh under stirring in N2 atmosphere at 60āĀ°C, individually. Subsequently, the activated samples were carbonized at various temperatures of 700, 800 and 900āĀ°C for 2āh in N2 atmosphere at a heating rate of 10āĀ°Cāminā1 in a tube furnace separately. The carbonized AC powder washed with distilled water and 1āM HCl to remove the Zinc content and it was referred as pure AC. Finally, the carbonized samples were dried at 100āĀ°C overnight to remove moisture and ground well to get finest powder. For comparison, we have used the electrochemically reduced graphene oxide as reported earlier by us31.
Fabrication of the AC-modified electrode
For the electrochemical biosensor application, the as-synthesized ACs were dispersed in ethanol and sonicated for 2āhours to obtain the stable dispersion. Prior to modification, the GCE surface was carefully polished to a mirror finish with alumina slurry. Then, it was washed with distilled water and ultrasonicated in ethanol-containing water for a few minutes. The ca. 6āĪ¼l (optimized concentration) of AC dispersion was drop-cast on the pre-cleaned GCE and dried in air oven at 30āĀ°C. Then, the AC modified GCE was gently rinsed a few times with double distilled water to remove the loosely bound AC. The fabricated AC modified electrode was used for further electrochemical experiments and all the experiments were performed at room temperature in an inert atmosphere.
Additional Information
How to cite this article: Veeramani, V. et al. Biomass-derived functional porous carbons as novel electrode material for the practical detection of biomolecules in human serum and snail hemolymph. Sci. Rep. 5, 10141; doi: 10.1038/srep10141 (2015).
References
Sevilla, M., Mokaya, R. Energy Storage Applications of Activated Carbons: Supercapacitors and Hydrogen Storage. Energy Environ. Sci. 7, 1250ā1280 (2014).
Zhu, Y. et al. Carbon-Based Supercapacitors Produced by Activation of Graphene. Science 332, 1537ā1541 (2011).
Sun, C. L. et al. Microwave-assisted Synthesis of a Coreshell MWCNT/GONR Heterostructure for the Electrochemical Detection of Ascorbic acid, Dopamine and Uric acid. ACS Nano 5, 7788ā7795 (2011).
Futaba, D. N. et al. Shape-engineerable and Highly Densely Packed Single-Walled Carbon Nanotubes and Their Application as Supercapacitor Electrodes. Nature Materials 5, 987ā994 (2006).
Madhu, R., Vijaya Sankar, K., Chen, S. M., Selvan, R. K. Eco-friendly synthesis of activated carbon from dead mango leaves for the ultrahigh sensitive detection of toxic heavy metal ions and energy storage applications. RSC Adv. 4, 1225ā1233 (2014).
Madhu, R., Veeramani, V., Chen, S. M. Heteroatom-enriched and Renewable Banana-stem-derived Porous Carbon for the Electrochemical Determination of Nitrite in Various Water Samples. Sci. Rep. 4:4679 10.1038/srep04679 (2014).
Vernersson, T., Bonelli, P. R., Cerrella, E. G., Cukierman, A. L. Arundo donax Cane as a Precursor for Activated Carbons Preparation by Phosphoric acid Activation. Bioresour Technol. 83, 95ā104 (2002).
Bhattacharjya, D., Yu, J. S. Activated Carbon made from Cow Dung as Electrode Material for Electrochemical Double layer Capacitor. J. Power Sources 262, 224ā231 (2014).
Qian, W. et al. Human Hair-derived Carbon Flakes for Electrochemical Supercapacitors. Energy Environ. Sci. 7, 379ā386 (2014).
Ekpete, O. A., Horsfall, M. J., Tarawou, T. Evaluation of Activated Carbon from Fluted Pumpkin Stem Waste for Phenol and Chlorophenol Adsorption in a Fixed āBed Micro-Column. J Appl. Sci. Environ. Manage 15, 141ā146 (2011).
Ekpete, O. A., Horsfall, M. J. Preparation and Characterization of Activated Carbon derived from Fluted Pumpkin Stem Waste (Telfairia occidentalis Hook F). Res. J. Chem. Sci. 1, 10ā17 (2011).
Arrigoni, O., Tullio, C. D. Ascorbic acid: Much More Zhan Just an Antioxidant. Biochim. Biophys. Acta. 1569, 1ā9 (2002).
Noroozifar, M., Khorasani-Motlagh, M., Akbari, R., Parizi, M. B. Simultaneous and Sensitive Determination of a Quaternary Mixture of AA, DA, UA and Trp using a Modified GCE by Iron ion-Doped Natrolite Zeolite-Multiwall Carbon Nanotube. Biosens Bioelectron. 28, 56ā63 (2011).
Heien, M. L. A. V. et al. Real-Time Measurement of Dopamine Fluctuations after Cocaine in the Brain of Behaving Rats. Proc. Natl. Acad. Sci. USA 102, 10023ā10028 (2005).
Damier, P., Hirsch, E. C., Agid, Y., Graybiel, A. M. The Substantia Nigra of the Human Brain II. Patterns of loss of Dopamine-Containing Neurons in Parkinsonās Disease. Brain 122, 1437ā1448 (1999).
Carlsson, A., Lindqvist, M., Magnusson, T. 3,4-Dihydroxyphenylalanine and 5-Hydroxytryptophan as Reserpine Antagonists. Nature 180, 1200 (1957).
Savitt, J. M., Dawson, V. L., Dawson, T. M. Diagnosis and Treatment of Parkinson Disease: Molecules to Medicine. J. Clin. Invest. 116, 1744ā1754 (2006).
Zuo, Y., Yang, Y., Zhu, Z., He, W., Aydin, Z. Determination of Uric acid and Creatinine in Human Urine using Hydrophilic Interaction Chromatography. Talanta 83, 1707ā1710 (2011).
Dutt, V. V. S. E., Mottola, H. A. Determination of Uric acid at the Microgram level by a Kinetic Procedure Based on a Pseudo-induction Period. Anal. Chem. 46, 1777ā1781 (1974).
Sekli-Belaidi, F., Temple-Boyer, P., Gros, P. Voltammetric Microsensor using PEDOT-Modified Gold Electrode for the Simultaneous Assay of Ascorbic and Uric Acids. J. Electroanal. Chem. 647, 159ā168 (2010).
Chen, M., Li, H. Separation of Anodic Peaks of Ascorbic Acid and Dopamine at 4-Hydroxy-2-mercapto-6-methylpyrimidine Modified Gold Electrode. Electroanalysis 10, 477ā479 (1998).
Guo, S., Wen, D., Zhai, Y., Dong, S., Wang, E. Platinum Nanoparticle Ensemble-on Graphene Hybrid Nanosheet: One-Pot, Rapid Synthesis and Used as New Electrode Material for Electrochemical Sensing. ACS Nano 4, 3959ā3968 (2010).
Hall, P. J. et al. Energy Storage in Electrochemical Capacitors: Designing Functional Materials to Improve Performance. Enery Env. Sci. 3, 1238ā1251 (2010).
Elsayed, M. A., Hall, P. J., Heslop, M. J. Preparation and Structure Characterization of Carbons Prepared from Resorcinol-Formaldehyde Resin by CO2 Activation. Adsorption 13, 299ā306 (2007).
Wang, X., Lee, J. S., Tsouris, C., DePaoli, D. W., Dai, S. Preparation of Activated Mesoporous Carbons for Electrosorption of Ions from Aqueous Solutions. J. Mater. Chem. 20, 4602ā4608 (2010).
Wei, Y. et al. SnO2/Reduced Graphene Oxide Nanocomposite for the Simultaneous Electrochemical Detection of Cadmium(II), Lead(II), Copper(II) and Mercury(II): An Interesting Favorable Mutual Interference. J. Phys. Chem. C. 116, 1034ā1041 (2012).
Harris, S. J., Cottrell, G. A. Properties of an Identified Dopamine-Containing Neurone in Culture from the Snail Helisoma. Exp. Physiol. 80, 37ā51 (1995).
Chistyakova, M. V. Role of Dopamine and Serotonin in Modulation of Snail Defensive Behavior. Neurosci. Behav. Physiol. 20, 446ā452 (1990).
Emaduddin, M., Liu, G. J., Takeuchi, H. Effects of Dopamine on Snail Neurons. Eur. J. Pharmacol. 283, 113ā124 (1995).
R. Madhu, V. Veeramani, S.-M. Chen, J. Palanisamy & A. T. E. Vilian . Pumpkin stem-derived activated carbons as counter electrodes for dye-sensitized solar cells. RSC Adv., 4, 63917ā63921 (2014).
Devadas, B., Madhu, R., Chen, S-M., Veeramani, V., Rajkumar, M. Electrochemical Preparation of a Reduced Graphene Oxide/Ruthenium Oxide Modified Electrode and Its Application to the Simultaneous Determination of Serotonin and Melatonin. Sci. Adv. Mater. 6, 1ā9 (2014).
Du, J. et al. Novel Graphene flowers Modified Carbon Fibers for Simultaneous Determination of Ascorbic acid, Dopamine and Uric acid. Biosens. Bioelectron 53, 220ā224 (2014).
Yue, Y. et al. A Mesoporous Carbon Nanofiber-Modified Pyrolytic Graphite electrode used for the Simultaneous Determination of Dopamine, Uric acid and Ascorbic acid. Carbon 50, 107ā114 (2012).
Gai, P. et al. Simultaneous Electrochemical detection of Ascorbic acid, Dopamine and Uric acid based on Nitrogen Doped Porous Carbon Nanopolyhedra. J. Mater. Chem. B 1, 2742ā2749 (2013).
Cai, W., Lai, T., Du, H., Ye, J. Electrochemical Determination of Ascorbic acid, Dopamine and Uric acid based on an Exfoliated Graphite Paper Electrode: A High Performance Flexible Sensor. Sensor and Actuator B, 193, 492ā500 (2014).
Zhang, H. et al. Self-assembly Synthesis of a Hierarchical Structure using Hollow Nitrogen-Doped Carbon Spheres as Spacers to Separate the Reduced Graphene Oxide for Simultaneous Electrochemical Determination of Ascorbic acid, Dopamine and Uric acid. Anal. Methods 5, 3591ā3600 (2013).
Yang, L., Liu, D., Huang, J., You, T. Simultaneous Determination of Dopamine, Ascorbic acid and Uric acid at Electrochemically Reduced Graphene Oxide Modified Electrode. Sensor and Actuator B. 193, 166ā172 (2014).
Zhu, S., Li, H., Niu, W., Xu, G. Simultaneous Electrochemical Determination of Uric acid, Dopamine and Ascorbic acid at Single-Walled Carbon Nanohorn Modified Glassy Carbon Electrode. Biosens. Bioelectron. 25, 940ā943 (2009).
Acknowledgements
This work was supported by the National Science Council and the Ministry of Science and Technology, Taiwan (ROC). The authors thank Mr. Rajkumar Madhu (Department of English (MCAS), Periyar University, India) for helpful better language proficiency and biomass sample collection. The authors thank Prof. Marta Sevilla (CSIC, Spain) for helpful discussions.
Author information
Authors and Affiliations
Contributions
V.V. and R.M. conceived and synthesized the ACs from Pumpkin stem and they performed the structural, morphological characterizations and electrochemical experiments for biomolecules detection. R.M. wrote the paper. J.P. gave helps in experiments. The project was finalized by S.M.C., B.S.L. and V.S.V. All authors discussed the results and commented on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Supplementary Information
Supplementary Figures 1-6
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the articleās Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Veeramani, V., Madhu, R., Chen, SM. et al. Biomass-derived functional porous carbons as novel electrode material for the practical detection of biomolecules in human serum and snail hemolymph. Sci Rep 5, 10141 (2015). https://doi.org/10.1038/srep10141
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep10141
This article is cited by
-
Biomass-derived carbon for dye-sensitized solar cells: a review
Journal of Materials Science (2023)
-
Sensitive dual-mode detection of carbendazim by molecularly imprinted electrochemical sensor based on biomass-derived carbon-loaded gold nanoparticles
Microchimica Acta (2023)
-
Green and low-cost synthesis of N and P double doped porous carbon derived from Sonchus arvensis L for simultaneous electrochemical detection of ascorbic acid, dopamine and uric acid
Journal of Materials Science: Materials in Electronics (2023)
-
Preparation of Nitrate Bilayer Membrane Ion-Selective Electrode Modified by Pericarpium Granati-Derived Biochar and Its Application in Practical Samples
Electrocatalysis (2023)
-
Utilization of nitrogen self-doped biocarbon derived from soybean nodule in electrochemically sensing ascorbic acid and dopamine
Journal of Porous Materials (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.