Office Paper Platform for Bioelectrochromic Detection of Electrochemically Active Bacteria using Tungsten Trioxide Nanoprobes


Electrochemically active bacteria (EAB) have the capability to transfer electrons to cell exterior, a feature that is currently explored for important applications in bioremediation and biotechnology fields. However, the number of isolated and characterized EAB species is still very limited regarding their abundance in nature. Colorimetric detection has emerged recently as an attractive mean for fast identification and characterization of analytes based on the use of electrochromic materials. In this work, WO3 nanoparticles were synthesized by microwave assisted hydrothermal synthesis and used to impregnate non-treated regular office paper substrates. This allowed the production of a paper-based colorimetric sensor able to detect EAB in a simple, rapid, reliable, inexpensive and eco-friendly method. The developed platform was then tested with Geobacter sulfurreducens, as a proof of concept. G. sulfurreducens cells were detected at latent phase with an RGB ratio of 1.10 ± 0.04 and a response time of two hours.


Electrochemically active bacteria (EAB) transfer electrons outside their cells toward insoluble electron acceptors during their respiration1,2. These organisms can be found in diverse environments, such as oceans, lakes and river sediments as well as domestic and industrial wastewater streams3. The most common application of EAB is the production of electrical current from the bacterial metabolism in microbial fuel cells (MFCs)1,2. Nevertheless, significant optimization of MFCs is still required. Besides electricity production, other applications of EAB include wastewater treatment, hydrogen production and in situ monitoring of microbial respiration4,5. Further research into the physiology and ecology of EAB is essential to design microorganisms with improved electron transfer capabilities6,7. Nowadays, the available screening methods are based on MFC principles, such as, voltage-based screening assay8, microfabricated MFC array4 and U-tube-shaped MFC9. However, these methods are relatively slow (~ 5 to 6 days) and expensive. The development of rapid and simple screening methods using low cost and available materials is today a key issue to identify EAB. The use of electrochromic materials has emerged recently as an attractive mean for colorimetric identification and characterization of EAB, making use of their reducing ability. Yuan et al.10 have described an optical probe method for the detection of EAB in solution using an electrochromic (EC) material, tungsten trioxide (WO3). EC materials change their optical properties (between two coloration states) with the appliance of a sufficient electrochemical potential. In this work, the bioelectrochromic response is achieved by an electron-transfer (redox) process of the EAB11,12. The electrochemical reaction that results in the chromic response of WO3 can be described considering the injection of an equimolar amount (x) of positive ions (M+) and electrons (e) as depicted in Equation 1 :

Typical cations are H+, Li+ and Na+, with a stoichiometry that can vary between zero and one13. In this work, nanostructures of WO3 were synthesized through a microwave assisted hydrothermal synthesis, which offers significant advantages, such as control over the crystal growth, shape and size, low number of impurities, improved product yield, low processing temperature, high homogeneity, very rapid heating to treatment temperature, low cost and easy synthesis14,15,16,17,18. The WO3 nanoparticles were integrated in a wax-printed office paper platform as an active layer for EAB detection. The fabrication of the paper-based sensor comprises two main steps: (i) wax printing of the hydrophobic patterns on the office paper and (ii) drop casting of the WO3 nanoparticles dispersion. Wax printing is a micropatterning method proposed by G. M. Whitesides' group for paper-based microfluidics19. Initially, a wax printer deposits a layer of wax onto the paper's surface that is then fused to penetrate throughout the paper thickness rendering it hydrophobic20,21,22,23,24. This method represents nowadays the fastest and simplest paper patterning process, allowing the formation of well-defined, sub millimeter-sized hydrophilic wells surrounded by hydrophobic barriers19,22. The proposed paper-based sensor was successfully used to test the presence of electrochemically active Geobacter sulfurreducens25 cells. The presence of these cells in the sample induces tungsten bronze formation displaying a deep blue color that highly contrasts with the white background provided by the paper platform. The color discrepancy between a positive (deep blue) and negative (white) result can be easily scrutinized by visual comparison or RGB analysis performed onto a digital photograph. Here, is reported for the first time the use of a low cost paper-based sensor to optically detect the presence of a well-known and deeply studied EAB, Geobacter sulfurreducens26,27,28.

Results and discussion

Tungsten trioxide synthesis

The crystallographic structure of the synthesized WO3 nanoparticles was determined by X-ray diffraction (XRD) ( Figure 1 ) and corroborated by Fourier transform infrared spectroscopy (FT-IR) ( Fig. S1 ). Tungsten oxides follow a well-known ReO3-type structure built up of layers containing distorted corner-shared WO6 octahedra. The growing process of WO3 nanostructures can be described in three major steps: (i) formation of the tungstic acid (H2WO4), (ii) formation of WO3 clusters by decomposition of H2WO4 and (iii) growth of WO3 crystal nucleus29. In the synthesis with sodium tungstate dihydrate (Na2WO4·2H2O) as precursor and NaCl as structure-directing agent (SDA) (Figure 1A), WO3 nanoparticles grow in a monoclinic (m-WO3) crystallographic structure (ICDD #00-043-1035) at pH 0.0 and orthorhombic (o-WO3·0.33H2O) (ICDD #01-072-0199) at pH 1.8. At pH 0.4 the WO3 nanoparticles are a mixture of the two phases, monoclinic and orthorhombic, together with the precursor (marked with *) and tungstic acid (marked with ♦). Using Na2SO4 as SDA (Figure 1B), orthorhombic and hexagonal (h-WO3) (ICDD #01-075-2187) phases were obtained at pH 0.4 and pH 1.8, respectively. At pH 0.4 the sample also shows a peak assigned to the acid tungstic (♦) and two unidentified peaks (Δ) that are due to lattice distortions of the crystallographic structure, as previously reported for WO3 nanoparticles prepared by hydrothermal synthesis30. Finally, using peroxopolytungstic acid (PTA) as precursor (Figure 1C), the crystallographic structure of the synthesized nanopowder is monoclinic for the lowest and higher pH values, which is in agreement with previous reports, although with different crystallographic plane intensities29. For the intermediate pH value, the WO3 nanoparticles present an orthorhombic phase. The FT-IR analysis is in accordance with the crystallographic structures attributed by XRD. However, the samples prepared with PTA precursor also revealed the presence of a W = O vibration bond that are assigned to some impurities. In general, the formation of nanoparticles is favourable for pH values lower that 2.0, however at pH 0.4 tend to form bundle structures and a mixture of phases and/or impurities31.

Figure 1

XRD diffractograms of the WO3 nanoparticles.

(A) WO3 nanoparticles synthesized from Na2WO4·2H2O, NaCl solutions; (B) WO3 nanoparticles synthesized from Na2WO4·2H2O, Na2SO4 solutions; (C) WO3 nanoparticles synthesized from PTA solutions. The peaks marked as * and ♦ are characteristic of Na2WO4·2H2O and H2WO4 structures. The peaks marked as Δ are non-identified. The crystalline structures were produced with the CrystalMaker software (Centre for Innovation & Enterprise, Oxford).

Figure 2 shows the morphological analysis performed by scanning electron microscopy (SEM). The WO3 nanoparticles synthesized with Na2WO4·2H2O show different morphologies: (i) nanocubes assigned to m-WO3, (ii) nanosheets assigned to o-WO3·0.33H2O, (iii) nanowires assigned to h-WO3 and (iv) bundle structures. Regarding the WO3 nanoparticles synthesized with PTA, the obtained structures present well-defined edges with nanosheet-like morphology at pH 0.0, a mixture of nanowires and nanocubes at pH 0.4 and single nanocubes at pH 1.8.

Figure 2

SEM images of the synthesized WO3 nanoparticles.

The images are false colored (GIMP software) for better understanding. The different colors are related with the XRD diffractograms for each crystalline structure.

The sulphate ions added to the synthesis process, act as capping agents covering some facets of WO3 crystal nuclei. At pH 1.8 a faster growth rate along c-axis is observed, yielding to one-dimensional wire/rod-like structures. In the meantime, a certain amount of sodium cations is required as stabilization ions for the hexagonal and triangular tunnels in the formation of h-WO315,31,32,33. When chloride ions are added it is believed that a similar process occurs prompting the growth of the nanoparticles in a specific direction34.

Additionally, electrochemical impedance spectroscopy (EIS) was performed in all the samples, in order to compare the conductivity of the nanostructures, since this affects its electron transfer ability during the electrochromic process. The Bode plots represented in Fig. S2 display, in general, lower impedances values for the orthorhombic and hexagonal crystallographic structures, which is in accordance with the literature35,36,37. The results obtained for hexagonal crystallographic structure ( Table S1 ) are explained by its high surface area and tunnel structure.

Office paper as a platform for EAB identification

The above described WO3 nanoparticles were used as an active layer in a regular office paper substrate in order to develop a colorimetric electrochemical device for EAB detection. This paper is optimized for printing and therefore has a more uniform surface, lower porosity and higher hydrophobicity (water-contact angle of 106°) when compared to chromatography paper (water-contact angle of 12°)22, the most common type employed in paper-based devices. Office paper allows a superficial adhesion of the WO3, which facilitates the interaction of EAB with the electrochromic nanoparticles, promoting an intense and uniform coloration of the test well. SEM-EDS and XRD analysis ( Figure 3A–C ) revealed a high-density structure of intertwined cellulose fibers with a cylindrical and flat shape and the presence of agglomerates, especially calcium carbonate, as confirmed by a FT-IR analysis ( Fig. S3 ).

Figure 3

Office paper characterization.

(A) SEM image and EDS map; (B) EDS spectrum; (C) XRD diffractogram; (D) Hydrophobic barriers formation; (E) Photograph of a positive result in the developed paper-based sensor with WO3 nanoprobes for the colorimetric detection of EAB (Geobacter sulfurreducens cells in yellow and hexagonal WO3 nanoparticles in blue). The images are false-colored (GIMP software) for better understanding of the different materials.

The sensor layout was designed to resemble a conventional microplate ( Figure 4A ) for parallel assays and prototyped into single-use sensors containing only a test and a control wells ( Figure 3D–E ). The layout was then patterned by wax printing, a method previously optimized by M. N. Costa et al.22, that increases the surface hydrophobicity (water-contact angle of 119°) ensuring no cross contamination between adjacent samples as well as the confinement of the WO3 nanoparticles dispersion to one particular area. A thermal analysis of the office paper ( Fig. S4 ) was also performed in order to guarantee that the material could withstand the heating process. The patterned office paper was then impregnated with the synthetized WO3 nanoparticles by a drop casting process. A drop was spotted on each well delimited by the hydrophobic pattern, in order to create the electrochromic layer.

Figure 4

EAB detection.

(A) Paper-based sensor photograph of the Colorimetric assays of all synthesized WO3 nanoparticles at 5 g/L; (B) RGB analyses for all the samples in contact with Geobacter sulfurreducens (Gs) cells. (Results recorded after 4 hours) The horizontal line represents the threshold of 1 considered for discrimination between positive and negative and the results represent the average of three independent measurements with the respective error bars indicative of the standard deviation.

Colorimetric assays

A screening colorimetric assay of all the synthesized WO3 nanoparticles was performed in the developed paper-based sensor ( Figure 4A ) and in the conventional 96-well plate ( Fig. S5 ). For the paper platform, an RGB analysis of the results was carried out using ImageJ software and the ratio of the average intensities in blue and red channels was recorded ( Figure 4B ). An electrochromic response translated by the deep blue color of the tungsten bronze (Equation 1) was achieved with sample 6, which corresponds to the synthesized hexagonal WO3 nanowires. The h-WO3 nanoparticles has attracted much attention due to its well-known tunnel structure where openness degree is higher when compared to the layered structure of orthorhombic or monoclinic geometries. This feature results in an easier intercalation of cations to form tungsten bronzes and concomitant enhancement of the electrochromic properties14,38. Moreover, the one-dimensional nanowire shape originates a structure with a high surface area and increased surface atom density that can easily interact with the EAB. Additionally, the electrochromic response was also observed in the conventional assay with other crystallographic WO3 structures, due to the higher concentration of the nanoparticles and enhanced interaction with EAB (Fig. S5).

For the fabricated paper-based sensor, the bioelectrochromic response is conditioned by the time that the cell suspension drops (V = 50 µL) take to dry (approximately 4 hours). Therefore, an equal scale down on the well's diameter (d = 3.38 mm) and in the sample volume (V = 20 µL) was carried out, with a reduction (2.5 times smaller) from the first paper-based sensor (Figure 4A). Additionally, an optimization assay was carried out ( Figure 5A ) to evaluate the influence of the h-WO3 nanoparticles concentration in the detection of EAB. Figure 5B represents the RGB analysis of the resulting color of the Geobacter sulfurreducens cells in contact with h-WO3 nanoparticles. From this analysis it is possible to conclude that 15 g/L and 20 g/L h-WO3 nanoparticles dispersion renders higher RGB ratios when compared to the other studied concentrations. Moreover, 15 g/L nanoparticles dispersion presents a linear response to the increasing G. sulfurreducens cells concentration. Therefore, henceforward the sensors were produced with h-WO3 nanoparticles dispersion at 15 g/L, with the same ratio nanoparticles per area than the first sensor (0.014 g/mm2). With the described scale-down the response time decreased to half the time (approximately 2 hours).

Figure 5

EAB detection.

(A) Paper-based sensor photograph of the Colorimetric assays of h-WO3 nanoparticles at different concentrations; (B) RGB analyses of h-WO3 nanoparticles at 15 g/L in contact with G. sulfurreducens cells, with the negative control E. coli and a blank test. (Results recorded after 2 hours) The horizontal line represents the threshold of 1 considered for discrimination between positive and negative and the results represent the average of three independent measurements with the respective error bars indicative of the standard deviation.

Figure 5C represents an RGB analysis of a positive control (Geobacter sulfurreducens), a negative control (Escherichia coli) and a blank well (no sample) for background information. Geobacter sulfurreducens cells in a late-exponential phase of growth (Abs600 nm ~ 0.5) display an RGB ratio of 1.33 ± 0.005, while the negative control, Escherichia coli under the same conditions and blank sample display an equal ratio of 0.99 ± 0.001/0.004. This result reveals a clear statistically significant difference between a positive and negative sample (P < 0.0001), proving the specificity of the developed paper-based device ( Table S2 ). Moreover, it was also possible to detect EAB at latent phase (Abs600 nm ~ 0.1), with an RGB ratio of 1.10 ± 0.040, thus confirming that the sensor here described is sensitive for low concentrations of EAB.


Electrochemically active bacteria are ubiquitous in nature and have the ability to transfer electrons outside their cells, a feature that can be applicable in electricity production, which is of the outmost importance in an energy dependent world.

However, the number of identified species is still very limited and their electron transfer mechanisms are feebly understood, caressing of feasible techniques to allow the detection of these bacteria as well as to facilitate the study of their physiology and electron transfer mechanisms.

This work reports a paper-based sensor with WO3 nanoprobes to optically detect the presence of these bacteria.

In order to study and optimize the electrochromic response to EAB cells, three different WO3 crystallographic structures (monoclinic, orthorhombic and hexagonal) were synthetized with the use of different precursors (Na2WO4·2H2O and PTA) and structure-directing agents (NaCl and Na2SO4) as well as by varying solution pH.

The performance of the produced structures as electrochromic material for EAB detection was evaluated in a screening colorimetric assay both in the conventional method, using a 96-well microplate and in an office paper platform, with the same dimensions and produced through wax-printing method. Both assays achieved a successful detection of EAB Geobacter sulfurreducens with a high color contrast for the h-WO3 nanowires. This enhanced bioelectrochromic response is in accordance with mentioned above that this structure presents an increased surface area and surface atom density proving to be the ideal material for EAB electrochromic detection.

The conventional assay performed in a solution based reaction also demonstrated a mild colorimetric response with other WO3 structures, due to the easier contact with G. sulfurreducens cells.

Aiming to reduce the response time, sample and reagents volume necessary for the test, a scale down paper-based device was tested with a 2.5 × reduction of wells diameter. The mentioned scale down allowed a reduction in the response time for 4 hours to 2 hours.

The described paper-based sensor showed a RGB ratio above 1 for a sample of Geobacter sulfurreducens cells at latent phase, thus providing a reliable, inexpensive, eco-friendly and simple approach to identify EAB. Moreover, this method can also be used in screening assays to aid in the understandings of the influence of certain proteins in the electron transfer chain, thus allowing further refining in the performance of the mentioned applications.

Experimental section

Tungsten trioxide synthesis

Several types of nanoparticles were synthesized through a microwave assisted hydrothermal method. Two different precursors were used (0.8 g): sodium tungstate dehydrated (Na2WO4·2H2O), (Fluka, 99%) and peroxopolytungstic acid (PTA), prepared by oxidation of tungsten (W) with hydrogen peroxide (H2O2), previously described39,40.

Two different salts were used as structure directing agents (SDA): NaCl (0.3 g) (Panreac, 99.5%) and Na2SO4 (0.72 g) (Panreac, 99%) with the Na2WO4·2H2O precursor. For each set of precursor, 3 M hydrochloric acid (Sigma-Aldrich, 37% by weight) was added to the solutions thus forming the acid tungstic (H2WO4) intermediate and the final pH values were set as 0.0, 0.4 and 1.8. In the samples produced from PTA precursor the influence of SDA was not studied.

The solutions were then transferred into a 35 mL vessel, sealed and heated in a microwave reactor (Discover SP, CEM Corporation, Matthews, NC, USA) at a constant power of 100 W for 1 h. All nine nanopowders were collected by centrifugation (4000 rpm, ~ 30 min) and dried (80°C, ~ 12 h). Solids were then grounded in a mortar to obtain fine powders and stored for further characterization.

Paper sensor fabrication

A4 (210 × 297 mm) sheets of an office paper (300%, Portucel Soporcel, Setúbal, Portugal) were fed to the manual feed tray of a commercial solid ink printer (Xerox ColorQube 8570, Xerox Corporation, Norwalk, CT, USA) designed to print a wax-based ink. All the prototypes used in this work were designed in Adobe Illustrator (Adobe Systems Software, Ireland). The prototypes were projected to resemble 96 and 384-well plates with d = 0.7 and 0.38 cm, respectively.

The printed patterns were placed on a hot plate (Heidolph MR HeiTec, Schwabach, Germany) at 140°C for 2 min, allowing the wax to melt and spread vertically through the whole thickness of the paper, creating the desired hydrophobic pattern. Each well was functionalized with 40 µL and 10 µL of WO3 nanoparticles dispersion for the sensor with d = 0.7 cm and d = 0.38 cm, respectively. The papers were allowed to dry at room temperature overnight. The final paper sensors were stored at room temperature in a dark box with no light interferences.

Bacterial growth

Geobacter sulfurreducens (strain ATCC 51573/DSM 12127/PCA) was inoculated under strict anaerobic conditions in NBAF medium with the following composition: 0.04 g/L CaCl2·2H2O, 0.1 g/L MgSO4·7H2O, 1.8 g/L NaHCO3, 0.5 g/L Na2CO3·H2O, 0.19 mg/L Na2SeO4, DL vitamins, 100X NB salts and NB mineral elixir, with 10 mM sodium acetate as the electron donor and 40 mM sodium fumarate as the electron acceptor. To remove oxygen, the NBAF medium was placed in 10 mL pressure tubes and gassed with an 8:2 mix of N2:CO2. After the NBAF medium deaeration and sterilization, 2% of yeast extract, 1% of 100 mM pH 7.0 cysteine and 1% of Geobacter sulfurreducens cells from a frozen stock were added to the culture medium under an anaerobic atmosphere. Cultures were grown at 30°C. The bacterial growth was followed through absorbance readings at 600 nm (Fig. S6). Escherichia coli (strain BL21 (DE3)), used as a negative control on the colorimetric assays, was inoculated in LB medium (10 g/L tryptone, 5 g/L yeast extract and 10 g/L NaCl) and incubated at 37°C, 200 rpm.

EAB-WO3 colorimetric assay

An anaerobic chamber (LABstar Glove Box Workstation, MBRAUN, Garching, Germany, O2 < 0.1 ppm) was used to perform all the colorimetric assays. Geobacter sulfurreducens, grown until late-exponential phase and Escherichia coli, in the same conditions, were collected by centrifugation at 6000 rpm for 5 min and then suspended in a buffer (30 mM Na2HPO4·2H2O, 30 mM KCl and 30 mM CH3COONa, pH 6.53). Cell cultures (50 µL and 20 µL for the sensor with d = 0.7 cm and d = 0.38 cm, respectively) were added to the respectively well and the drops were allowed to dry at room temperature.

Data acquisition and analysis

The colorimetric paper-based results were recorded with a digital scanner (All-in-One Printer 1050A HP, Hewlett-Packard Development Company, L.P., Palo Alto, CA, USA) with a 300 dpi resolution. Color development analysis was performed with ImageJ software (National Institutes of Health, Bethesda, Maryland, USA) through an RGB control. A one-way ANOVA analysis, with Tukey's multiple comparison test, using GraphPad (San Diego, CA) was used to validate the results. The one-way analysis of variance was used to test for differences between two groups of data (positive and negative results). Additional statistical analysis of the differences was carried out using Tukey's multiple comparison procedures.


The crystallographic structure of the WO3 nanoparticles and the office paper were determined by XRD (X'Pert Pro, PANalytical, Almelo, Netherlands) with CuKα target and wavelength of 1.5406 Å. The nanoparticles' morphology and paper was characterized by SEM-EDS (Carl Zeiss AURIGA Crossbeam SEM-FIB, Oberkochen, Germany) and their chemical structure by FT-IR (Nicolet 6700 FT-IR, Thermo Electron Corporation, Waltham, MC, USA) with a diamond crystal attenuated total reflectance (ATR) accessory. The electrochemical impedance spectroscopy was performed in a potentiostat (600TM Gamry Instruments) with WO3 powders in a form of pellets made at a pressure of 8 tons, with a diameter of approximately 1 cm and a thickness of 1–3 mm. The electrochemical cell consisted in two stainless steel electrodes in each side of the pellet compacted in a homemade cell.

Scanning electron microscopy of biological samples

Geobacter sulfurreducens cells alone and in contact with WO3 nanoparticles were imaged using SEM. Before imaging, the mixture was fixed in 3% glutaraldehyde in a 0.2 M cacodylate buffer solution for 2 h, rinsed two times with 0.1 M cacodylate buffer solution and dehydrated through graded ethanol (70, 95 and 100%, respectively, for 20 min each).


  1. Strycharz-Glaven, S. M., Snider, R. M., Guiseppi-Elie, A. & Tender, L. M. On the electrical conductivity of microbial nanowires and biofilms. Energy Environ. Sci. 4, 4366 (2011).

    CAS  Article  Google Scholar 

  2. Bretschger, O. et al. Current production and metal oxide reduction by Shewanella oneidensis MR-1 wild type and mutants. Appl. Environ. Microbiol. 73, 7003–12 (2007).

    CAS  Article  Google Scholar 

  3. Ringeisen, B. R. et al. Single Cell Isolation of Bacteria from Microbial Fuel Cells and Potomac River Sediment. Electroanalysis 22, 875–882 (2010).

    CAS  Article  Google Scholar 

  4. Hou, H., Li, L., Cho, Y., Figueiredo, P. & Han, A. Microfabricated microbial fuel cell arrays reveal electrochemically active microbes. PLoS One 4, 6570 (2009).

    ADS  Article  Google Scholar 

  5. Erable, B., Duţeanu, N. & Ghangrekar, M. Application of electro-active biofilms. Biofouling 26, 57–71 (2010).

    CAS  Article  Google Scholar 

  6. Lovley, D. R. Microbial fuel cells: novel microbial physiologies and engineering approaches. Curr. Opin. Biotechnol. 17, 327–32 (2006).

    CAS  Article  Google Scholar 

  7. Nevin, K. P. et al. Anode biofilm transcriptomics reveals outer surface components essential for high density current production in Geobacter sulfurreducens fuel cells. PLoS One 4, 5628 (2009).

    ADS  Article  Google Scholar 

  8. Biffinger, J. et al. Characterization of electrochemically active bacteria utilizing a high-throughput voltage-based screening assay. Biotechnol. Bioeng. 102, 436–44 (2009).

    CAS  Article  Google Scholar 

  9. Zuo, Y., Xing, D., Regan, J. M. & Logan, B. E. Isolation of the exoelectrogenic bacterium Ochrobactrum anthropi YZ-1 by using a U-tube microbial fuel cell. Appl. Environ. Microbiol. 74, 3130–7 (2008).

    CAS  Article  Google Scholar 

  10. Yuan, S.-J. et al. A photometric high-throughput method for identification of electrochemically active bacteria using a WO3 nanocluster probe. Sci. Rep. 3, 1315 (2013).

    Article  Google Scholar 

  11. Lee, S.-H. et al. Crystalline WO3 Nanoparticles for Highly Improved Electrochromic Applications. Adv. Mater. 18, 763–766 (2006).

    CAS  Article  Google Scholar 

  12. Mortimer, R. J. Electrochromic Materials. Annu. Rev. Mater. Res. 41, 241–268 (2011).

    ADS  CAS  Article  Google Scholar 

  13. Zheng, H. et al. Nanostructured Tungsten Oxide - Properties, Synthesis and Applications. Adv. Funct. Mater. 21, 2175–2196 (2011).

    CAS  Article  Google Scholar 

  14. Ha, J.-H., Muralidharan, P. & Kim, D. K. Hydrothermal synthesis and characterization of self-assembled h-WO3 nanowires/nanorods using EDTA salts. J. Alloys Compd. 475, 446–451 (2009).

    CAS  Article  Google Scholar 

  15. Rajagopal, S. et al. Controlled Growth of WO3 Nanostructures with Three Different Morphologies and Their Structural, Optical and Photodecomposition Studies. Nanoscale Res. Lett. 4, 1335–42 (2009).

    ADS  CAS  Article  Google Scholar 

  16. Song, X. C., Zheng, Y. F., Yang, E. & Wang, Y. Large-scale hydrothermal synthesis of WO3 nanowires in the presence of K2SO4 . Mater. Lett. 61, 3904–3908 (2007).

    CAS  Article  Google Scholar 

  17. Komarneni, S., Rajha, R. K. & Katsuki, H. Microwave-hydrothermal processing of titanium dioxide. Mater. Chem. Phys. 61, 50–54 (1999).

    CAS  Article  Google Scholar 

  18. Pimentel, A. et al. Synthesis of Long ZnO Nanorods under Microwave Irradiation or Conventional Heating. J. Phys. Chem. C 118, 14629–14639 (2014).

    CAS  Article  Google Scholar 

  19. Martinez, A. W., Phillips, S. T., Butte, M. J. & Whitesides, G. M. Patterned paper as a platform for inexpensive, low-volume, portable bioassays. Angew. Chem. Int. Ed. Engl. 46, 1318–20 (2007).

    CAS  Article  Google Scholar 

  20. Martinez, A.. W.., Phillips, S.. T.., Whitesides, G.. M.. & Carrilho, E.. Diagnostics for the Developing World: Microfluidic Paper-Based Analytical Devices. Anal. Chem. 82, 3–10 (2010).

    CAS  Article  Google Scholar 

  21. Jokerst, J. C. et al. Development of a paper-based analytical device for colorimetric detection of select foodborne pathogens. Anal. Chem. 84, 2900–7 (2012).

    CAS  Article  Google Scholar 

  22. Costa, M. N. et al. A low cost, safe, disposable, rapid and self-sustainable paper-based platform for diagnostic testing: lab-on-paper. Nanotechnology 25, 094006 (2014).

    ADS  CAS  Article  Google Scholar 

  23. Liana, D. D., Raguse, B., Gooding, J. J. & Chow, E. Recent advances in paper-based sensors. Sensors (Basel). 12, 11505–26 (2012).

    CAS  Article  Google Scholar 

  24. Veigas, B. et al. Gold on paper-paper platform for Au-nanoprobe TB detection. Lab Chip 12, 4802–8 (2012).

    CAS  Article  Google Scholar 

  25. Lovley, D. R. et al. Geobacter: the microbe electric's physiology, ecology and practical applications. Advances in microbial physiology. 59, 1–100 (2011).

    CAS  Google Scholar 

  26. Morgado, L. et al. Revealing the structural origin of the redox-Bohr effect: the first solution structure of a cytochrome from Geobacter sulfurreducens. Biochem. J. 441, 179–87 (2012).

    CAS  Article  Google Scholar 

  27. Bond, D. & Lovley, D. Electricity production by Geobacter sulfurreducens attached to electrodes. Appl. Environ. Microbiol. 69, 1548–1555 (2003).

    CAS  Article  Google Scholar 

  28. Reguera, G. et al. Biofilm and nanowire production leads to increased current in Geobacter sulfurreducens fuel cells. Appl. Environ. Microbiol. 72, 7345–8 (2006).

    CAS  Article  Google Scholar 

  29. Wang, J., Lee, P. S. & Ma, J. Synthesis, growth mechanism and room-temperature blue luminescence emission of uniform WO3 nanosheets with W as starting material. J. Cryst. Growth 311, 316–319 (2009).

    ADS  CAS  Article  Google Scholar 

  30. Santos, L. et al. WO3 Nanoparticle-Based Conformable pH Sensor. ACS Appl. Mater. Interfaces 13, 12226–12234 (2014).

    Article  Google Scholar 

  31. Gu, Z. et al. Large-scale synthesis of single-crystal hexagonal tungsten trioxide nanowires and electrochemical lithium intercalation into the nanocrystals. J. Solid State Chem. 180, 98–105 (2007).

    ADS  CAS  Article  Google Scholar 

  32. Huang, K. et al. Controllable synthesis of hexagonal WO3 nanostructures and their application in lithium batteries. J. Phys. D. Appl. Phys. 41, 155417 (2008).

    ADS  Article  Google Scholar 

  33. Shi, J., Hu, G., Cong, R., Bu, H. & Dai, N. Controllable synthesis of WO3·nH2O microcrystals with various morphologies by a facile inorganic route and their photocatalytic activities. New J. Chem. 37, 1538 (2013).

    CAS  Article  Google Scholar 

  34. Phuruangrat, A., Ham, D. J., Hong, S. J., Thongtem, S. & Lee, J. S. Synthesis of hexagonal WO3 nanowires by microwave-assisted hydrothermal method and their electrocatalytic activities for hydrogen evolution reaction. J. Mater. Chem. 20, 1683 (2010).

    CAS  Article  Google Scholar 

  35. Santos, L. et al. Structure and Morphologic Influence of WO3 Nanoparticles on the Electrochromic Performance of Dual-Phase a -WO3/WO3 Inkjet Printed Films. Adv. Electron. Mater. 1, 1400002 (2015).

    Article  Google Scholar 

  36. Li, Y. M., Hibino, M., Miyayania, M. & Kudo, T. Proton conductivity of tungsten trioxide hydrates at intermediate temperature. Solid State Ionics 134, 271–279 (2000).

    CAS  Article  Google Scholar 

  37. Orsini, G. & Tricoli, V. Mesoporous, high-surface-area tungsten oxide monoliths with mixed electron/proton conductivity. J. Mater. Chem. 20, 6299 (2010).

    CAS  Article  Google Scholar 

  38. Kharade, R. R., Patil, K. R., Patil, P. S. & Bhosale, P. N. Novel microwave assisted sol–gel synthesis (MW-SGS) and electrochromic performance of petal like h-WO3 thin films. Mater. Res. Bull. 47, 1787–1793 (2012).

    CAS  Article  Google Scholar 

  39. Wojcik, P. J. et al. Microstructure control of dual-phase inkjet-printed a-WO3/TiO2/WOX films for high-performance electrochromic applications. J. Mater. Chem. 22, 13268 (2012).

    CAS  Article  Google Scholar 

  40. Wojcik, P. J., Santos, L., Pereira, L.., Martins, R.., Fortunato, E. Tailoring nanoscale properties of tungsten oxide for inkjet printed electrochromic devices. Nanosc. 5, 1696–708 (2015).

    ADS  Article  Google Scholar 

Download references


This work was partially supported by the Portuguese Science Foundation (FCT-MEC) through the projects EXCL/CTM-NAN/0201/2012, Pest-C/CTM/LA0025/2013-14, Pest-C/EQB/LA0006/2013-14, PTDC/BBB-BEP/0753/2012 and the ERC Advanced Grant (INVISIBLE, contract number 228144). Geobacter sulfurreducens cells were kindly provided by Prof. Derek Lovley from University of Massachusetts (USA). We would like to thank to Dr. Daniela Nunes for the SEM images.

Author information




A.C.M., L.S., M.N.C., J.M.D., P.D. and A.G. contributed equally to the work and R.M., C.A.S. and E.F. supervised the work. All authors reviewed the manuscript.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Electronic supplementary material

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Marques, A., Santos, L., Costa, M. et al. Office Paper Platform for Bioelectrochromic Detection of Electrochemically Active Bacteria using Tungsten Trioxide Nanoprobes. Sci Rep 5, 9910 (2015).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.