Functional oxide interfaces based on transition metal oxides1 have been recognized for their new and exciting fundamental physics2,3 as well as for their potential as next-generation nanoelectronic materials. They are associated with a wide variety of interesting physical phenomena, such as superconductivity, ferroelectricity, ionic conduction and magnetism. Given the success that has been achieved in finding novel properties for technological applications in systems such as perovskite-type LaAlO3/SrTiO3 oxide interfaces4, it becomes important to also find further promising material combinations and structure types that may exhibit exotic properties. For example, a surprising lamellar ferromagnetic order at intergrowths of antiferromagnetic (AFM) haematite (Fe2O3) and para/antiferromagnetic (PM/AFM) ilmenite (FeTiO3) has been reported5,6. The charge imbalance at the interface has been identified as a source of this phenomenon, very often accompanied by local distortions. This can induce charge transfer processes and change the bond-angles between ions. These effects modify the competing ferromagnetic (FM) and AFM interactions (super–exchange and double exchange) in antiferromagnets as described by the so called Goodenough-Kanamori-Anderson (GKA) rules7. For instance a distortion (bond-angle change) and charge transfer can turn the AFM 180° magntic ion-oxygen-magnetic ion superexchange of partially filled 3d eg ( EquationSourcemath mrow msub mtextd mrow msup mtextz mn2 , math mrow msub mtextd mrow msup mix mn2 mo- msup miy mn2 ) or t2g (dxy, dyz, dxz) orbitals into ferromagnetic (double) exchange. Consequently, tuning the relative magnitudes of competing magnetic interactions via strain control at interfaces opens a promising route to create new types of magnets.

The interesting question arises if ferromagnetic order can be stabilized between two simple antiferromagnets like CoO and Co3O4, both of which are antiferromagnets with ordering temperatures TN = 291 K and 40 K, respectively8,9. In nanostructured AFM materials10 pairing of the two mutually compensating ferromagnetic sublattices is broken due to surface rearrangement, which leads to the presence of “uncompensated” and often “frustrated” surface moments and the consequent magnetic reconstruction11. Several examples of weak ferromagnetism in nanoparticulate CoO12,13,14 and Co3O415,16,17 materials have been reported in the literature based on these explanations, though the irregular shapes and the relatively wide size distributions of nanoparticles have made a detailed analysis of the origin of the observed ferromagnetic response very difficult. In contrast, nearly perfect antiferromagnetic CoO nanocrystals with octahedron shapes and different average sizes, as reported in Ref. 18, should allow the origin of the room temperature ferromagnetism to be identified. These crystalline CoO octahedra have eight (111) crystal facets stabilized by a thin Co3O4 shell, which forms naturally by surface oxidation in air19,20,21 and is thermodynamically more stable than CoO. The uncompensated magnetic moments in the ~3 nm thick AFM Co3O4 surface layer have been assumed as a likely source of the observed ferromagnetism. However, the origin of a quasi two-dimensional long-range ferromagnetic order persisting in a temperature range where the AFM CoO and Co3O4 bulk phases are paramagnetic is not understood.

Here, we demonstrate that the atomically sharp interface between the crystalline ~3 nm thick spinel-type Co3O4 surface layer and the crystalline CoO (rocksalt structure) is the source of the ferromagnetism observed up to 400 K. The octahedron-shaped nanocrystals with edge lengths between 40 and 150 nm, have a heavily strained epitaxial CoO/Co3O4 interface that forms at the eight (111) facets, offering quasi-2D ferromagnetic interfaces stable even in the paramagnetic regime of the antiferromagnetic CoO (T > 291 K). Using a combination of magnetometry, transmission electron microscopy and density functional theory (DFT) we obtain quantitative results confirming that an electronic reconstruction accompanied by a considerable interlayer compression of the CoO oxide (111) layer spacing at the interface to the Co3O4 surface coating explains the ferromagnetic order and its stability. One may note that such an enhanced TC in a quasi 2D interface is remarkable, since lower dimensionality in in general expected to lead to enhanced thermal fluctuations and a reduced ordering temperature22. Consequently, our results show that the occurrence of magnetic order in these octahedron-shaped nanocrystals can be attributed to the changes of bond-angles and valence states at the (111) CoO/Co3O4 interface, which modify the relative strengths of the inherent ferromagnetic double exchange and antiferromagnetic superexchange.

CoO crystallizes in the cubic rocksalt-structure, Fm3 m (Oh5), above the Néel temperature TN = 291 K, in which alternating layers of (111) Co planes with opposite magnetization directions are separated by oxygen planes. The Co2+ ions occupy the octahedral sites formed by the faced-centered-cubic (FCC) arranged O2− ions. Below TN the magnetic order induces a transition to a monoclinic phase (C2/m (C32h))23. This results in a distorted octahedral crystal field with a spin S = 3/2 and an unquenched orbital momentum of approximately L = 1 (L/S = 0.7)24 in the antiferromagnetically ordered state. AFM CoO has a very high magnetocrystalline anisotropy constant of ~2.7 × 107 J cm−3 25, which is comparable to that of the hard magnet samarium-cobalt26. In thin CoO layers the single ion magnetic anisotropy energy (MAE) density was found to change from 4.8 meV/atom to −1.6 meV/atom upon dilating or compressing along the CoO(100) plane and has been related to a large change of electronic occupation of the eg and t2g orbital states27. In principle, an ideal CoO crystal slab in a (111) orientation could show two contributions: a vanishing total magnetization for an even number of Co layers and the magnetization of a single Co2+ monolayer for an odd number of Co layers. On the other hand, the modified crystal field symmetry at the surface due to a missing or relaxed O2− surface layer changes the octahedral (Oh) symmetry dramatically, can unquench the orbital momentum and can consequently modify the spin only magnetic moment S = 3/2 with . Unfortunately, such ideal surface layers cannot be stabilized due to their high polarity. As shown for Co (111) films grown on Ir(100), nature circumvents the polarity problem by an appropriate surface reconstruction, that is, by switching from the rocksalt type to wurtzite-type stacking near the surface, which turns out to become metallic at the interface in ultrahigh vacuum28.

Co3O4 crystallizes in the normal spinel structure with the general formula [A]tet[B2]octO4, that is, [Co2+]tet[Co23+]octO2−4. Co3+ ions (“B” sites, 3d6, spin S = 0) occupy octahedral sites and Co2+ ions occupy the tetrahedral (“A”) sites formed by O2− species yielding an S = 3/2 state. The Co2+ ions on the A site are antiferromagnetically ordered below 40 K, namely, each ion at a tetrahedral site “A” is surrounded by four nearest neighbor A sites with an antiparallel magnetic moment. The [Co3+]oct ions on the B site are in the low spin (LS) S = 0 state, i.e., diamagnetic.

Cobalt oxide octahedron-shaped nanocrystals (Fig. 1a) prepared by colloidal chemistry (described in the Methods section) offer the possibility to study changes in interface structure, electronic properties and competing magnetic interactions. X-ray powder diffraction, neutron diffraction and X-ray photoemission spectroscopy measurements revealed that the major constituent of these nanocrystals was CoO with a rocksalt structure at room temperature and confirmed the absence of metallic (Co0) cobalt. High-resolution TEM measurements revealed the CoO-Co3O4 core-shell structure of the nanoparticles. Figure 1a shows a bright-field TEM image of the as-synthesized CoO nanocrystals deposited on an amorphous carbon support film. The observed morphologies of the nanocrystals, which take the form of hexagons, rectangles and rhombi in 2D projection, originate from 3D octahedral particle shapes (confirmed using electron tomography) whose crystal facets are determined by the underlying cubic crystallographic structure (see the scheme in Fig. 1b). The average edge lengths of the octahedron-shaped nanocrystals were determined to be 40 ± 8 nm and 75 ± 10 nm from bright-field TEM images. In the following, these samples are referred to as S-40 nm and S-75 nm, respectively.

Figure 1
figure 1

TEM and magnetic characterization of octahedral cobalt oxide nanocrystals.

(a), TEM bright-field image of octahedral cobalt oxide nanocrystals on an amorphous C support film. The particles exhibit patches of brighter contrast, which are likely to be related to the presence of voids inside the particles, as indicated by arrows in the inset. (b), Schematic representation of the octahedral particle shape, its projections and the corresponding crystallographic orientations for a cubic crystal structure. (c), ZFC and FC hysteresis loops, recorded at 300 K from samples S-75 nm and shown after subtraction of the linear paramagnetic (300 K) component. (d), As for c but at T = 5 K, the FC magnetization curve is shifted horizontally to the left relative to the ZFC curve. Values of HC, MR and MS (see text) are given in Tables T1 and T2.

Magnetic characterization of the CoO nanoctahedra was performed using a SQUID magnetometer under zero-field cooling (ZFC) and field cooling (FC) conditions. The measured field-dependent magnetization M(H) showed clear hysteresis loops (Fig 1c,d) at T = 300 K and 5 K, with characteristics of ferromagnetic behavior, superimposed on the expected paramagnetic (T = 300 K) and antiferromagnetic (T = 5 K) linear field-dependent response of CoO and Co3O4. The saturation magnetization MS = 1.58 Am2/kg (Co metal: 163.6 Am2/kg), the remanent magnetization MR = 0.261 Am2/kg and the coercivity HC = 35.7 mT measured at 300 K for the S-75 nm sample (Fig. 1c) unambiguously indicate a ferromagnetically ordered component in the nominally purely paramagnetic state above the Néel temperature TN = 291 K of CoO, which forms the core of every octahedron. Another unambiguous proof for the interfacial coexistence of FM and AFM components is the observation of an exchange bias field HEB at lower temperatures, seen as the horizontal and vertical shift of the hysteresis after field cooling (FC) relative to the ZFC M(H) loop (Fig. 1d). The temperature-dependence of the exchange bias field HEB and of the coercive field HC for samples S-40 nm and S-75 nm (Fig. S1) shows that HEB vanishes above TNCoO = 291 K as expected, while the coercive field μ0HC is still larger than about 30 mT. A detailed summary of the variation in MS, MR and HC with temperature for the ZFC and FC M(H) experiments is given in Supplementary Tables T1 and T2. In addition, K-edge X-ray absorption spectra, neutron diffraction studies and temperature dependent susceptibility measurements confirmed the absence of metallic cobalt and the existence of crystalline antiferromagnetic CoO with TNCoO = 291 K and a thin shell of Co3O4 with a finite-size-effect reduced TN = 20 K18.

The reduced – mass normalized - saturation magnetization MS measured for the smaller octahedra S-40 nm (2.81 Am2/kg at 5 K and 2.60 Am2/kg at 300 K) in comparison to the S-75 nm octahedra (1.72 Am2/kg at 5 K and 1.55 Am2/kg at 300 K) suggests that a surface or interface contribution is the origin of the ferromagnetic response. To support this analysis, we have calculated the expected magnetization of ferromagnetic single and double surface or interface layers of Co2+ ions. The number of these Co2+ cations at the apexes, edges, surfaces and interfaces was estimated for a given size and shell thickness of a CoO-Co3O4 core-shell octahedron, by making use of the geometrical relationship between the rocksalt-spinel crystal structures and the octahedral morphology. For an octahedral particle with eight 111 facets (Fig. 2b), where the number of atoms along the 111 facet is n, the number of Co2+ cations at the apexes is 6, at the edge is 12(n − 1), at the surfaces is 8[(n − 1)(n − 4)/2 + 1] and in the inside volume is (2n2 + 1)/3. Taking the typical magnetic moment μ = (4.8 ± 0.4)μB for Co2+29, we calculate the saturation magnetization MS for one layer (blue curves) of surface Co2+ cations (see Fig. 2a), while the red curves show the calculated values of MS for a double-layered interface of Co2+. The red curves intersect the measured MS (black solid and dashed lines for 300 K and 5 K) for the S-40 nm sample at a size range of 38–45 nm, while for S-75 nm the intersection occurs at a size range of 60–80 nm. The striking match between the measured and calculated saturation magnetization must therefore be associated with interfacial ferromagnetic long-range order and not surface-derived ferromagnetism.

Figure 2
figure 2

(a) Size dependence of experimentally measured (black solid (T = 5 K) and dashed (300 K) lines) and calculated saturation magnetization MS of CoO octahedra. A magnetic moment μ of (4.8 ± 0.4)μB per Co2+ ion and a shell thickness of 3 nm Co3O4 is assumed. MS arises only from the Co cations at the surfaces or interfaces of the octahedral nanocrystals, as indicated in the schematic in (b). The blue lines are calculated values assuming only effectively one layer of Co2+ cations at the Co3O4 surface, while the red lines correspond to a double layer of Co cations at the interface, as discussed in the text.

In order to understand the reason for the appearance of this interfacial long-range ferromagnetic order, we have also performed high-angle annular dark field (HAADF) imaging. Figure 3a shows an atomically resolved HAADF image of the edge of a typical cobalt oxide octahedron, oriented along the [110] direction. In HAADF imaging, the recorded contrast arises primarily from Rutherford and thermal diffuse scattering30. Under our experimental conditions, the HAADF intensity scales to a good approximation with the atomic number Z1.7 and the specimen thickness, since the area of interest is sufficiently thin. A distinct core-shell contrast variation with different atom-column configurations is appreciated. Figure 3b shows an enlargement of the interface area outlined by a dashed-square in Fig. 3a, in which a (111)-type interface and (002)-type interfaces between CoO and Co3O4 (delineated by dashed lines) can be identified. The core region (A) corresponds to a [110] atomic column projection of the rocksalt CoO structure, while the shell region (B) corresponds to a [110] atomic column projection of the normal spinel Co3O4 structure. The bright contrast corresponds to cobalt cation columns, whose scattering strength is greater than that of oxygen anions. For more precise atomic lattice information, we have analyzed the intensity variation and lattice spacing in different HAADF images. The rectangular a–b area shown in Fig. 3b was selected for intensity profile analysis (not shown) and indicates a clear intensity variation that reflects structure and chemistry differences across the interface boundaries. By using the CoO core as a reference, we measured variations of the (111)-plane lattice spacing in the CoO/Co3O4 interface region. The measurements (red data points in Fig. 3c) revealed a progressive decrease in lattice spacing from the core to the surface by as much as 8%, suggesting the presence of large strain in the interface region. Within experimental accuracy, we find that the Co3O4 plane spacing (235 pm) is bulk –like and stays unchanged. Only the CoO (111) spacing is strongly compressed at the interface and relaxes towards the core within three to four layers to its respective bulk value.

Figure 3
figure 3

STEM-HAADF image of a single octahedral cobalt oxide nanocrystal.

(a), Atom-column-resolved STEM-HAADF image of the edge of a [1–10]-oriented cobalt oxide nanocrystal acquired in STEM mode at 80 kV using a probe size of ~0.1 nm. The core region A and the shell region B exhibit contrast characteristic of [1–10]-oriented CoO and Co3O4 respectively. (b), Enlargement of the interface area: (111)-type interface between a CoO core and the Co3O4 shell. (c), Measured (111) (red dots) and calculated (blue dots) lattice plane spacings as a function of spacing number near the interface. “d0” denotes the spacing indicated by the dashed line in b. (d), Side view of the relaxed geometry of the CoO/Co3O4 (111) heterostructure obtained from the DFT + U calculations. The interface plane (dashed line) of O2 (red dots) connects octahedral Co ions (blue dots) in Co3O4 on the right to octahedral Co2+ ions in CoO on the left. Co2+ and Co3+ are denoted by blue/yellow polyhedra. As discussed in the text, electronic reconstruction in the interface Co3O4 layer reduces the S = 0 [Co3+]oct to low spin [Co2+]oct. (e), Spin density of the CoO/Co3O4 (111) heterostructure obtained from the DFT + U calculations. Red and blue contours denote antiparallel orientations of magnetic moments. Besides the antiferromagnetic alignment of octahedral Co2+ in CoO and tetrahedral Co2+ in Co3O4, note a considerable spin density at the Co3+ sites in the inner Co3O4 layers (not present in bulk Co3O4). A key feature is the significant spin polarization in the interface Co3O4 signaling the reduction of octahedral Co3+ to Co2+ sites in an unanticipated low spin state (S = 1/2) – the corresponding sites are emphasized by the arrow.

To shed more light on the underlying mechanisms DFT+$U$ calculations were performed considering two different terminations of Co3O4 at the interface: one with exclusively octahedral Co (named B-layer) and one with a mixed octahedral, tetrahedral layer. The calculated lattice spacings (blue data points in Fig. 3c) match very well the experimentally measured ones confirming that the interlayer distances on the CoO side of the interface are strongly reduced, while on the Co3O4 side it is close to the bulk-value. The very good agreement between the theoretical and experimental interlayer distances shown in Fig. 3d for theB-layer model unambiguously identifies that the latter is realized at the interface.

Below the side view of the relaxed structure from DFT+$U$ calculationsins Fig. 3d), Fig. 3e) shows the spin density and orbital polarization of the heterostructure. Red and blue contours denote antiparallel orientations of magnetic moments. Besides the antiferromagnetically ordered octahedral Co2+ in CoO and tetrahedral Co2+ in Co3O4, a striking feature is the noticeable spin density at the Co3+ sites (we note that no spin density is observed in bulk Co3O4 – not shown here). While the total contribution of the red and blue lobes at Co3+ in the inner layers sums up to a relatively small spin magnetic moment of 0.05 μB, individual octahedral Co-sites at the interface adopt a considerable magnetization of 0.4–0.8 μB (for details see Methods). This high magnetic moment signals a valence change from Co3+ towards Co2+ at the interface. Most importantly, these sites are in a low spin (LS) state, unlike Co2+ in the CoO part of the superlattice. The latter are in a high spin (HS) state with magnetic moments of 2.58 μB (close to the value of 2.64 μB in bulk CoO). Thus, the interface magnetism originates from a change in oxidation state at the octahedral sites with a LS state, which is clearly distinct from the HS state in bulk CoO.

By making use of the interfacial atomistic information obtained from the HAADF image analysis and the DFT + U calculations, it is possible to draw conclusion about the atomic interface structure of the two cobalt oxides. As mentioned above in bulk rocksalt CoO, Co2+ cations occupy octahedral sites in a lattice of FCC O2− ions. In contrast, in bulk normal spinel Co3O4, Co3+ cations populate half of the octahedral sites, while Co2+ cations populate one-eighth of the tetrahedral sites in an FCC lattice of O2− ions. The two structures can be epitaxially matched at the (111) facets of the FCC sublattice of host O2− ions, when the bulk lattice mismatch of about 5% (4.261 Å for CoO: JCPDS card no. 48-1719 and 8.084 Å for Co3O4: JCPDF card no. 42-1467) can be accommodated by strain. Such “flexible” accommodation of cobalt cations to form different oxides has also been observed in other transition metal oxide systems. Consequently, one can construct rocksalt/spinel (111)-type interfaces. In this model, the interfacial oxygen plane is adjacent to octahedral Co2+oct (S = 3/2) in CoO and octahedral Co3+oct (S = 0) in Co3O4. To understand the appearance of ferromagnetism we can compare the interface structure to an inverse spinel structure, which is typical for example for ferrimagnetic Fe3O4. The difference between ([Co2+]tet[Co23+]oct)O42− and ([Fe3+]tet[Fe2+ Fe3+]oct)O42− is the valence of the cobalt and iron cations in their respective tetrahedral and octahedral environments. In Fe3O4, magnetic super exchange (SE) and double exchange (DE) interactions between iron cations and their inequivalent neighbors proceed via the same oxygen anion. The Fe2+Oct and Fe3+Oct cations are coupled ferromagnetically through double exchange (DE). However, the two Fe3+Tet and Fe3+Oct cations are coupled antiferromagnetically through super exchange (SE), such that their moments of ±5 μB cancel. An unpaired moment of 4 μB on the Fe2+Oct cation site remains. Consequently, Fe3O4 exhibits ferrimagnetic behavior with a high Curie temperature TC = 858 K31. In Co3O4, on the other hand, the weak tetrahedral-tetrahedral (T-T) AFM interactions between the Co2+tet cations lead to antiferromagnetism9 with a low ordering temperature TN of ~20–40 K. Consequently, a ferromagnetic order with a high Curie temperature can be stabilized at the interface if magnetic moments are present at both the octahedral and the tetrahedral sites. Such a scenario was previously explained by a transition from a normal to inverse spinel in Co3O4 nanoparticles by Chen et al.32 and by Serrano et al.16 at the surfaces of nanoparticles on TiO2. On the other hand, our results demonstrate a rather different mechanism of formation of Co2+Oct at the interface with an unanticipated low spin state of S = 1/2. In the study of Serrano et al.16, a weak FM signal was attributed to surface reduction of Co3+Oct to Co2+Oct, whereby complex magnetic interactions involving T-T (Co2+Tet - Co2+Tet), O-O (Co3+Oct – Co2+Oct) and T-O could occur, in analogy to that in Fe3O4. Here, we suggest that it is possible to achieve long-range ferromagnetic order with a high Curie temperature due to the coupling of Co2+Oct (S = 3/2 and 1/2) and Co2+Tet cations on both sides of the epitaxial interface, as shown in Fig. 3d) and e). Our experimental and computational results indicate that robust ferromagnetic order can occur at (111) interfaces between CoO and Co3O4 above the highest Neel temperature of the antiferromagnets. To understand that such a behavior was not observed in previous Co oxide thin film studies, one may consider lateral size effects in the nanoctahedra. These may be important to prevent the formation of strain-releasing misfit dislocations at the interface – as has also been found in the growth of nanowires with heavily strained semiconductor heterostructures33. It will be interesting to investigate in the future, if defect-free CoO/Co3O4 interfaces could be stabilized in laterally extended epitaxial thin films despite the large strain observed in the CoO interface layers.

In summary, the present rocksalt/spinel-type system provides a fascinating oxide interface, in which electrostatic doping can induce changes of competing magnetic interactions (SE and DE) at the nanoscale level. We provide experimental and theoretical results to explain the appearance of a robust ferromagnetic order with a Curie temperature above 400 K at the epitaxial (111) interface of the two antiferromagnets CoO and Co3O4. We suggest that the electrostatic doping at the polar interface leading to an electronic reconstruction34 with a valence change, accompanied by an unanticipated spin state, is the origin of the effective long-range ferromagnetic order. As Co3O4 exhibits extraordinary catalytic activity for the oxidation of carbon monoxide and hydrocarbons and thus has the potential to at least partly replace noble metals or rare earth materials in technologically relevant processes, such ferromagnetic nano-octahedra with catalytic shell may become useful in technologies in which the particles can be recollected by magnetic gradient fields for reactivation.


CoO nanooctahedra were obtained using the hot-injection thermodecomposition of cobalt acetate (Sigma-Aldrich, 98%), (2.66 and 4 mmol) (dissolved in 5 mL of ethanol) in trioctylamine (Aldrich, 90%) (25 mL, 57.18 mmol) and oleic acid (Aldrich, 90%) (5.12 and 8 mmol) at 170°C and then left to reflux (at T = 300°C) for two hours. Once cooled to room temperature, the nanocrystals were obtained by centrifugation, washed several times and stored in ethanol. Repeated syntheses confirm the reproducibility of the final products.

Specimens for TEM analysis were prepared by dropping the diluted colloidal solution onto copper grids covered with a thin (~10 nm) amorphous carbon film and by allowing the solvent to evaporate. Structural and chemical characterization of the cobalt oxide nanocrystals was performed using several transmission electron microscopes. An FEI Titan 80–300 TEM operated at 200 kV was used for high-resolution TEM analysis (not shown here). An FEI Titan Ultimate 60–300 TEM operated at 80 kV was used for STEM EEL spectroscopy and atom-column-resolved STEM HAADF imaging. EEL spectra were acquired in STEM mode using a ~1 nm electron probe with an energy resolution of ~0.8 eV or better, as evaluated from the full-width at half-maximum of the zero-loss peak. Spectra were recorded using a dispersion of 0.3 eV/channel and acquisition time of 0.5 s for each spectrum image to minimize electron irradiation damage. The convergence and collection semi-angles were estimated to be 20 and 26.5 mrad, respectively. Magnetic characterization was performed using a SQUID magnetometer. Possible sources of error include sample preparation, post-treatment processing and sample storage. We also checked the possible ageing effect on magnetic properties of the samples and found negligible change in M(H) and M(T) for both samples kept under ambience conditions for a duration of six months.

First principles calculation

DFT calculations were performed using the all-electron full-potential linearized augmented plane wave (FP-LAPW) method, as implemented in the WIEN2k code35,36. For the exchange-correlation potential we used the generalized gradient approximation GGA37 with an on-site Coulomb repulsion term UCo = 5 eV (LDA/GGA + U method38). The muffin-tin spheres of the atoms were chosen as: 1.8 (Co) and 1.6 a.u. (O), respectively. The following cutoffs were used: Ry for the plane wave representation in the interstitial region; Gmax = 12 (a.u.)−1 for the plane wave expansion of the charge density and lmax = 10 for spherical harmonics inside the muffin-tin spheres. The integrals in reciprocal space were performed with 52 k-points in the irreducible part of the Brillouin zone (IBZ). The CoO/Co3O4 (111) heterostructure is modeled using six layers (and 2x2 lateral units) of CoO and one unit cell of Co3O4, using the lateral lattice parameter CoO (aCoO = 6.02 Å). The atomic positions are fully relaxed within hexagonal symmetry. Three different systems were considered, depending on the interface termination of Co3O4 with either an octahedral layer or a mixed octahedral/tetrahedral termination. The very good agreement in interlayer spacing between experiment and the B-layer model, identifies the latter as the preferred termination. The results for this interface are presented in Fig. 3d–e. Note that the heterostructure contains two B-layer interfaces on both sides of Co3O4. Because no symmetry constraints are imposed in the calculation and the stacking of layers is not identical at both sides we obtain a slight asymmetry of the interfaces, expressed in a difference of magnetic moments (0.4 and 0.8 μB) at the interfacial Co2+ oct sites, however the general mechanism of reduction of octahedral Co and a low spin state is present at both interfaces.