Rechargeable magnesium batteries are poised to be viable candidates for large-scale energy storage devices in smart grid communities and electric vehicles. However, the energy density of previously proposed rechargeable magnesium batteries is low, limited mainly by the cathode materials. Here, we present new design approaches for the cathode in order to realize a high-energy-density rechargeable magnesium battery system. Ion-exchanged MgFeSiO4 demonstrates a high reversible capacity exceeding 300 mAh·g−1 at a voltage of approximately 2.4 V vs. Mg. Further, the electronic and crystal structure of ion-exchanged MgFeSiO4 changes during the charging and discharging processes, which demonstrates the (de)insertion of magnesium in the host structure. The combination of ion-exchanged MgFeSiO4 with a magnesium bis(trifluoromethylsulfonyl)imide–triglyme electrolyte system proposed in this work provides a low-cost and practical rechargeable magnesium battery with high energy density, free from corrosion and safety problems.
Rechargeable batteries have become quintessential energy conversion devices, that are widely used in portable electronic devices and hybrid electric vehicles. However, their energy density and safety still require improvement, particularly considering their future demand as larger power sources for electric vehicles and smart grid communities1. Rechargeable magnesium metal batteries are one potential solution. As an anode, magnesium metal provides two electrons per atom, giving it an attractive volumetric capacity of 3837 mAh·cm−3, which is approximately five times higher than that of the conventional graphite anodes in lithium ion batteries (LIBs). In addition to the high capacity, the relatively high negative reduction potential of magnesium metal can provide high energy density. Moreover, the terrestrial abundance and melting point of elemental magnesium by far surpass that of lithium, translating to a cheap and safe battery system. These advantages of magnesium metal anodes have been previously recognized2,3 and a rechargeable magnesium battery cell was first proposed in 20004. In this system, sulfide clusters in Chevrel-type Mo6S8 were used as cathodes and a magnesium organohaloaluminate salt in tetrahydrofuran (THF) was used as the electrolyte. However, the energy density remained rather constrained by the cathode material and the narrow potential window, corrosion and safety problems posed by the electrolyte have hampered the commercial realization of these batteries. Recently, magnesium deposition and dissolution obtained by using magnesium bis(trifluoromethylsulfonyl)imide (Mg(TFSI)2) with glyme–diglyme have been reported5. The anodic stability of this electrolyte is higher than 3.0 V vs. Mg2+/Mg and high-voltage cathode materials can be used in this electrolyte. Even though extensive research has been performed on cathode materials6, breakthroughs are awaited for the development of practically usable rechargeable magnesium batteries. In this study, we have attempted to address the problems related to cathode materials by using an ion-exchanged polyanion cathode (i.e., MgFeSiO4) and constructed a rechargeable magnesium battery using this high-energy-density cathode material.
The choice of cathode materials for magnesium battery is extremely limited because divalent Mg2+ insertion/extraction in host compounds is difficult, apparently due to the stronger ionic interaction and harder charge redistribution of magnesium compared to lithium ions7. For decades, various cathode materials have been proposed, including the molybdenum chalcogenides4,7, V2O58, TiS2 nanotubes9, graphene-like MoS210, todorokite-type/hollandite-type MnO211,12 and sulfur13. Nevertheless, these candidates cannot achieve high capacity, high voltage and excellent cyclability in parallel. Orthosilicates such as olivine-type MgMSiO4 (M = Fe, Mn, Co) are another group of promising candidates, because the theoretical capacities of MgMSiO4 exceed 300 mAh·g−1 and the operating voltages are expected to be higher than that of conventional magnesium battery cathode materials14. These silicate frameworks possess tetrahedral polyanions (SiO44−) which are expected to afford lattice stabilization for magnesium (de)intercalation through the presence of strong Si–O bonds. Amongst this family of silicates, MgFeSiO4 is expected to be inexpensive because its constituent elements are abundant; in fact, the mineral olivine, (Mg, Fe)2SiO4 occurs naturally in significant amounts. The utilization of olivine-type MgFeSiO4 as a cathode material for rechargeable Mg batteries has previously been reported15. However, its innate electrochemical properties have not been adequately examined owing to the contribution of the electrochemical reaction from the copper current collector with the electrolyte, as reported recently16.
In olivine compounds such as LiFePO4, the lithium cation is located in a distorted octahedral site such that its diffusion pathway is one-dimensional (1D)17,18; in this case, the mobility of the carrier ions is easily impeded once defects are generated in the pathway (Fig. S1)19. The thermodynamically stable phase of MgFeSiO4 with the olivine-type structure possesses some degree of mixing between different octahedral Mg and Fe crystallographic sites20 and a similar limitation imposed by low dimensionality may occur. We therefore attempted to improve electrode kinetics by preparing a meta-stable phase of MgFeSiO4 via the electrochemical ion exchange of Li2FeSiO4, rather than by the conventional solid state synthesis. In Li2FeSiO4, the SiO4 tetrahedra are arranged in the same way as in the MgMSiO4 olivine structure, but with slightly different spacings, so that Li and Fe are in tetrahedral rather than octahedral coordination, providing a 2D network (Fig. 1a, left).
The preparation of MgFeSiO4 involves, two electrochemical processes, namely, 2Li+ extraction from Li2FeSiO4 followed by Mg2+ insertion. Details regarding the characterization of as-prepared Li2FeSiO4 are shown in Supporting Information (Figs. S2, S3, S4 and Table S1). The complete extraction of Li+ from Li2FeSiO4 is performed in a Li-ion battery cell (as demonstrated previously21,22) and then Mg2+ is inserted into FeSiO4 after changing the electrolyte to one containing a Mg salt. The voltage profiles for the Li extraction and the Mg insertion processes are shown in Fig. 1b. To extract two Li+ from Li2FeSiO4, the cells are charged to the theoretical capacity of Li2FeSiO4 (i.e., 331 mAh·g−1) within an appropriate voltage range. The subsequent discharge processes in the Mg salt electrolyte deliver a capacity of approximately 330 mAh·g−1, demonstrating for the first time the ability to insert Mg2+ into FeSiO4. In this measurement, to improve electronic conduction path in the electrodes, an appreciable amount of carbon was used, which might cause side reactions without the contribution of the active materials. However, the composite electrode without the active materials exhibits little charge–discharge capacity (as shown in Fig. S5). Therefore, the obtained charge and discharge capacity emanates mainly from reaction of active materials.
Remarkably, MgFeSiO4 prepared via ion exchange undergoes reversible electrochemical charge-discharge processes. The charge-discharge profiles in a magnesium battery cell of the electrochemically prepared MgFeSiO4 are shown in Fig. 1c. The charge–discharge reaction was limited to within 330 mAh·g−1 to prevent the contribution of other reactions such as electrolyte decomposition. Considering the electrochemical window of magnesium (trifluoromethylsulfonyl)imide (Mg(TFSI)2) in acetonitrile (0.5 M), which is shown in Fig. S6 in Supporting Information, it can be concluded that the electrolyte was stable in our experiments. Although the charge-discharge potential appears slightly shifted, a reversible reaction is attainable with almost one Mg2+ insertion and extraction. The achieved discharge capacity of MgFeSiO4 is approximately twice that of conventional LIB cathodes such as LiCoO2 and LiFePO4. The average charge-discharge potential is −0.1 V vs. Ag+/Ag, which corresponds to 2.4 V vs. Mg2+/Mg according to the literature23. The energy density is estimated to be 746 Wh·kg−1, which far exceeds that of the Chevrel phases of Mo6S8 (~135 Wh·kg−1)4 and other cathode materials reported to date, such as V2O5 (~400 Wh·kg−1)6 and α-MnO2 (~560 Wh·kg−1)11.
Structural changes were investigated by X-ray diffraction using a synchrotron source. Rietveld refinement of Li2FeSiO4 (Fig. S2 and Table S1) resulted in a P21/n monoclinic structure comprising of the 2D network of SiO4 and FeO4 tetrahedra, which agrees well with the literature24. It is predicted that Li2–xFeSiO4 has various polymorphs with 2D and 3D networks upon electrochemical reaction25. Indeed, our recent XRD study demonstrated that the initial 2D monoclinic (P21/n) structure in Li2FeSiO4 is converted to a 3D orthorhombic (Pnma) structure in LiFeSiO426. In this study, we performed further delithiation from LiFeSiO4 and found that the Pnma orthorhombic 3D structure is retained in FeSiO4 (Figs. S7 and S8 and Tables S2 and S3 in Supporting Information). Namely, the 2D network in Li2FeSiO4 (Fig. 1a, left) is transformed to a 3D network in FeSiO4 (Fig. 1a, center). Note that satisfactory refinement could not be obtained when structural models with the original Li2FeSiO4-type 2D network were used.
After the subsequent Mg2+ insertion and extraction processes, the XRD patterns reversibly change (Fig. S9), while the orthorhombic crystal structure is maintained as shown in Table 1. The lattice parameters of Mg1–xFeSiO4 appear to follow the Vegard's law. Although refinement of MgFeSiO4 and Mg0.5FeSiO4 was difficult because of poor data quality, these observations strongly indicate that the 3D network in FeSiO4 is retained upon the Mg2+ insertion/extraction (Fig. 1a, right). The cell volume reduction by Mg2+ insertion can be explained by the reduced repulsion between Fe and Si cations (Fe2+-Si4+ in MgFeSiO4vs. Fe4+-Si4+ in FeSiO4), consistent with recent theoretical reports14. Such a 3D network can be beneficial in terms of the stability of cathode materials upon Mg2+ insertion/extraction.
The full de-intercalation of Li2FeSiO4 or MgFeSiO4 would presumably result in Fe4+, therefore the charge compensation mechanism was investigated using Fe K-edge X-ray absorption near edge structure (XANES), as shown in Fig. 2a. The higher and lower energy shifts of the XANES spectra at the Fe K-edge correspond, respectively, to increase and decrease in the oxidation state of the Fe ions, as confirmed in previous iron silicate systems22,27. During the lithium extraction process, a significant shift is observed from Li2FeSiO4 to LiFeSiO4. This corresponds to the oxidation of divalent Fe ions to the trivalent state, which is dominated by the outermost orbital of the Fe-3d band. Between LiFeSiO4 and FeSiO4, only a small shift is observed, as has also been noted by others upon a more than one lithium extraction from Li2FeSiO422. The small edge shift suggests that other charge compensation mechanisms should be occurring between LiFeSiO4 and FeSiO4. In the subsequent Mg2+ (de)insertion processes, reversible shifts in the absorption energies are observed as shown in Fig. 2b. While the energy shift in the XANES spectrum is small from FeSiO4 to Mg0.5FeSiO4 (similar to what was observed in the LiFeSiO4–FeSiO4 regime), a significant shift is observed from Mg0.5FeSiO4 to MgFeSiO4. A similar trend was also observed during the magnesium extraction process, as is apparent in Fig. 2c.
O K-edge X-ray absorption spectroscopy (XAS) measurements give further insight for FeSiO4 (Fig. 2d). The pre-edge peak intensity at 529 eV increases as Fe is oxidized; this indicates the degree of hybridization between the Fe 3d states and O 2p states28. Such a strong hybridization between the metal and ligand can lead to creation of ligand holes, suggesting this process as the redox mechanism during the charge-discharge reaction of ion-exchanged MgFeSiO4. In general, anion redox processes can contribute to large capacities, as has recently been revealed in the lithium (de)intercalation of Li2(Ru,Sn)O329. The charge compensation process dominantly occurs within the Fe 3d orbital in the Mg0.5FeSiO4–FeSiO4 regime. Conversely, the O 2p orbital plays an important role in the oxidation/reduction process between the Mg0.5FeSiO4 and FeSiO4 regimes by creating holes at ligand sites. Such different electronic structural changes influence the charge–discharge potential profiles (shown in Fig. 1c), in which two-stage sloping profiles are observed. The theoretical potential based on DFT calculations carried out using the experimental XRD data (shown in Fig. S7 and S8 in Supporting Information) is in good agreement, particularly between the MgFeSiO4 and Mg0.5FeSiO4 regimes. However, there is a discrepancy between the experimental and theoretical potential values in the Mg0.5FeSiO4–FeSiO4 regime, where the contribution of O 2p orbital states is more dominant. This discrepancy should not come as a surprise, considering that DFT calculations in this study do not fully take into account the exchange–correlation interaction for oxygen states.
For a working magnesium battery based on ion-exchanged MgFeSiO4, further improvement in the electrolyte is pivotal because magnesium deposition/dissolution cannot be achieved using (Mg(TFSI)2) in acetonitrile as a solvent. Previously proposed electrolytes such as magnesium organohaloaluminates and hexamethyldisilazide magnesium chloride in THF13,23 have narrow potential windows due to the use of chloride and THF. Additionally, these electrolytes suffer from corrosion (due to the halide) and also pose safety problems with regard to flammability (due to the volatility of THF). An alternative electrolyte, employing a different magnesium salt dissolved in a less volatile solvent, would therefore be desirable. Here, we present our results using magnesium bis(trifluoromethylsulfonyl)imide (Mg(TFSI)2) dissolved in triglyme. Cyclic voltammograms of a platinum working electrode in the Mg(TFSI)2–triglyme electrolyte at 100°C are shown in Fig. 3a. The cathodic and anodic peaks correspond to magnesium deposition and dissolution, respectively. The anodic stability in this electrolyte is higher than 3.5 V vs. Mg2+/Mg. This value is higher than that of the wide potential window of organohaloaluminates, etc., in THF, recently reported by Muldoon and co-authors30. The deposited product was characterized by XRD and scanning electron microscopy (SEM) (Figs. 3b and 3c). The diffraction pattern of the deposited product is fully indexed to the P63/mmc space group, consistent with the formation of Mg metal. Particles approximately 5 μm thick were deposited on the platinum working electrode without dendrite formation. Most recently, magnesium deposition and dissolution obtained using Mg(TFSI)2 with glyme–diglyme as a solvent have been reported5. The boiling point of triglyme is higher than that of the glyme–diglyme solvent, which is favorable for stable battery operation under various temperatures. Our results validate that the Mg(TFSI)2–triglyme system, in addition to the reported glyme–diglyme system5, can be used in rechargeable magnesium batteries in combination with high-voltage cathode materials.
As a proof-of-concept, we therefore propose a novel rechargeable magnesium battery system as shown in Fig. 4a, where ion-exchanged MgFeSiO4 and Mg metal are used as the cathode and anode, respectively and Mg(TFSI)2–triglyme as the electrolyte. These materials would be highly beneficial for increasing the energy density of the electrode materials in magnesium batteries without imposing significant constraints on available resources. The chemical and thermal stabilities afforded by the polyanion moieties are also suitable for cathode materials. The Mg(TFSI)2–triglyme electrolyte does not contain Cl-, Br- or THF-based solvents. This enables the safe operation of rechargeable magnesium batteries without corrosion and low flammability. Using ion-exchanged MgFeSiO4 and Mg(TFSI)2–triglyme, charge–discharge measurements for the magnesium rechargeable battery full cell were performed at 100°C; the obtained results are shown in Fig. 4b. A reversible charge–discharge capacity of 166 mAh·g−1 was obtained, which was calculated on the basis of the mass of the active material (viz., ion-exchanged MgFeSiO4 cathode), despite the effect of anode polarization on this profile. When Mg(TFSI)2–triglyme is used as the electrolyte, only half of the theoretical capacity of the cathode material could be obtained owing to the high polarization and elevated temperature operation needed (Fig. S11). The high polarization might presumably be arising from the low Mg2+ cation flux in the triglyme solvent. In a Li(TFSI)–triglyme system, high polarization was also reported31. Further improvements in the electrolyte and morphology control of the composite electrodes are essential.
This study demonstrates ion-exchanged MgFeSiO4 as a feasible cathode material for use in rechargeable magnesium batteries. The application of ion-exchanged MgFeSiO4 polyanion compounds as rechargeable magnesium battery cathode materials provides a capacity of more than 300 mAh·g−1 at an average potential of 2.4 V vs. Mg2+/Mg, with good retention upon cycling. The electronic and crystal structure of ion-exchanged MgFeSiO4 changes during the charging and discharging processes, which demonstrates the (de)insertion of magnesium in the host structure. Batteries using a combination of ion-exchanged MgFeSiO4 and the Mg(TFSI)2–triglyme electrolyte represent a prototype for a low-cost, high-energy-density rechargeable magnesium battery in which no toxic or explosive components are used.
Cathode materials were synthesized using a solid-state reaction. Amorphous SiO2 (99.9%), FeC2O4·2H2O (99%) and Li2CO3 (99%) powders were weighed in a molar ratio of 1:1:1. The powders were mixed using a ball mill in acetone. 10 wt% Ketjen carbon black was added to improve the electronic conductivity. Mixing was performed using a plenary ball mill (Fritsch LP-6) at 400 rpm for 6 h. The obtained slurry was dried at room temperature under vacuum. The dried powder was pelletized and calcined at 800°C for 6 h under Ar flow. The obtained powder was thereafter transferred to an argon-filled glove box, owing to the inherent sensitivity of the material upon air exposure.
The products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Conventional XRD measurements were performed at room temperature on a Rigaku Rint-2200 diffractometer using Cu Kα radiation. The diffraction data were collected in a 2θ range of 10° to 60° with a step size of 0.04°. SEM micrographs were recorded with a JSM-890 (JEOL) operated at 15 kV. TEM measurements were performed with an HR-9000 (Hitachi) operated at 200 kV, taking care not to expose the samples to air.
Electrodes were prepared from the basic active material (Li2FeSiO4), to which carbon (acetylene black) was added and ball-milled at 400 rpm for 30 minutes. Polytetrafluoroethylene (PTFE) binder was thereafter added to obtain a final weight ratio of 40:50:10. Two-electrode cells were prepared using metallic lithium as the counter electrode. The electrolyte was 1 M LiClO4 in propylene carbonate. Cells were charged at 55°C to a capacity commensurate with the extraction of two Li+ (theoretical capacity of ca. 331 mAh·g−1). After the charge processes, the cells were dismantled in an Ar-filled glove box. The working electrode was rinsed several times with dimethyl carbonate and dried in vacuum. The dried active electrodes were pressed on Pt mesh as the working electrode. Three-electrode cells were used for Mg battery measurements. The electrolyte consisted of 0.5 M magnesium (trifluoromethylsulfonyl)imide (Mg(TFSI)2) in acetonitrile. A Mg ribbon was used as the anode. As the reference electrode, a silver wire was inserted into a solution of 0.01 M AgNO3 and 0.1 M Mg(TFSI)2 in acetonitrile. This solution, contained in an additional glass tube, was brought into contact with the Mg(TFSI)2/acetonitrile solution via a microporous glass membrane. The galvanostatic charge–discharge measurements were carried out at 55°C. The cells were cycled at a C/50 rate within the capacity ranges of one Mg2+ per Fe. The upper and lower cut-off potentials were set at 1.0 V vs. Ag+/Ag and −1.0 V vs. Ag+/Ag, respectively.
Mg deposition and dissolution test
Three-electrode cells were used. A platinum sheet and a Mg rod were used as the working and the counter electrodes, respectively. Mg(TFSI)2/triglyme (1:5 molar ratio) was used as the electrolyte. As a reference electrode, a silver wire was inserted into a solution of 0.01 M AgNO3 and 0.1 M Mg(TFSI)2 in triglyme. Cyclic voltammetry was performed in the potential range of −3.75–1.5 V at a potential sweep rate of 1.0 mV s−1 at 100°C.
Mg rechargeable battery test
Two-electrode cells were used. Ion-exchanged MgFeSiO4 and Mg metal were used as the cathode and anode, respectively. The galvanostatic charge–discharge measurements were performed at a C/50 rate at 100°C. The capacity range was limited to 0.5 Mg2+ per Fe. The upper and lower cut-off voltages were set at 1.0 V vs. Mg2+/Mg and −1.0 V vs. Mg2+/Mg, respectively.
After the electrochemical measurements, the charged/discharged electrodes were rinsed several times with acetonitrile. Powder samples were then loaded into a glass capillary and sealed in an argon-filled glove box to eliminate the exposure of the samples to air. Synchrotron X-ray diffraction patterns were collected at the beam line BL02B2 of SPring-8, Japan, equipped with a large Debye-Scherer camera. The wavelength of the incident X-ray beam was set to 0.5 Å using a double-crystal silicon (111) monochromator, which was calibrated with a CeO2 standard. Full pattern matching and Rietveld refinements were performed with the JANA2006 program package. The backgrounds were interpolated by a Chebyshev function and the peak shapes were described by a pseudo-Voigt function.
For the Fe K-edge XAS measurements, charged/discharged Mg1–xFeSiO4 electrodes were intimately mixed with boron nitride powder and pressed into pellets. The pellets were sealed in laminated packets in an argon-filled glove box. The XAS spectra were measured in the energy region of the Fe K-edge at room temperature in transmission mode at the beam line of the SPring-8 synchrotron radiation facility (BL01B1 and BL14B2) in Hyogo, Japan. Treatment of the raw X-ray absorption data was performed with the Athena package, allowing for alignment and normalization. As for the O K-edge XAS measurements, the electrodes were transferred to the measurement chamber without exposing the samples to air. The spectra were measured at BL-2 of the SR center at Ritsumeikan University (Japan). The spectra were collected in fluorescence yield mode.
Armand, M. & Tarascon, J. M. Building better batteries. Nature 451, 652–657 (2008).
Novak, P. & Desilvestro, J. Electrochemical Insertion of Magnesium in Metal Oxides and Sulfides from Aprotic Electrolytes. J. Electrochem. Soc. 140, 140–144 (1993).
Gregory, T. D., Hoffman, R. J. & Winterton, R. C. Nonaqueous Electrochemistry of Magnesium Applications to Energy Storage. J. Electrochem. Soc. 137, 775–780 (1990).
Aurbach, D. et al. Prototype systems for rechargeable magnesium batteries. Nature 407, 724–727 (2000).
Ha, S.-Y. et al. Magnesium(II) Bis(trifluoromethane sulfonyl) Imide-Based Electrolytes with Wide Electrochemical Windows for Rechargeable Magnesium Batteries. ACS Appl. Mater. Interfaces 6, 4063–4073 (2014).
Yoo, H. D. et al. Mg rechargeable batteries: an on-going challenge. Energy Environ. Sci. 6, 2265–2279 (2013).
Levi, E., Gofer, Y. & Aurbach, D. On the Way to Rechargeable Mg Batteries: The Challenge of New Cathode Materials. Chem. Mater. 22, 860–868 (2010).
Le, D. B. et al. Intercalation of polyvalent cations into V2O5 aerogels. Chem. Mater. 10, 682–684 (1998).
Tao, Z. L., Xu, L. N., Gou, X. L., Chen, J. & Yuan, H. T. TiS2 nanotubes as the cathode materials of Mg-ion batteries. Chem. Commun. 2080–2081 (2004).
Liang, Y. L. et al. Rechargeable Mg Batteries with Graphene-like MoS2 Cathode and Ultrasmall Mg Nanoparticle Anode. Adv. Mater. 23, 640–643 (2011).
Zhang, R. et al. alpha-MnO2 as a cathode material for rechargeable Mg batteries. Electrochem. Commun. 23, 110–113 (2012).
Kumagai, N., Komaba, S. & Sakai, H. Preparation of todorokite-type manganese-based oxide and its application as lithium and magnesium rechargeable battery cathode. J. Power Sources 97–8, 515–517 (2001).
Kim, H. S. et al. Structure and compatibility of a magnesium electrolyte with a sulphur cathode. Nature Commun. 2, 427 (2011).
Ling, C., Banerjee, D., Song, W., Zhang, M. & Matsui, M. First-principles study of the magnesiation of olivines: redox reaction mechanism, electrochemical and thermodynamic properties. J. Mater. Chem. 22, 13517–13523 (2012).
Li, Y., Nuli, Y., Yang, J., Yilinuer, T. & Wang, J. MgFeSiO4 prepared via a molten salt method as a new cathode material for rechargeable magnesium batteries. Chin. Sci. Bull. 56, 386–390 (2011).
Lv, D. et al. A Scientific Study of Current Collectors for Mg Batteries in Mg(AlCl2EtBu)2/THF Electrolyte. J. Electrochem. Soc. 160, A351–A355 (2013).
Nishimura, S. et al. Experimental visualization of lithium diffusion in LixFePO4 . Nature Mater. 7, 707–711 (2008).
Morgan, D., Van der Ven, A. & Ceder, G. Li conductivity in LixMPO4 (M = Mn, Fe, Co, Ni) olivine materials. Electrochem. Solid State Lett. 7, A30–A32 (2004).
Axmann, P. et al. Nonstoichiometric LiFePO4: Defects and Related Properties. Chem. Mater. 21, 1636–1644 (2009).
Redfern, S. A. T. et al. Octahedral cation ordering in olivine at high temperature. II: an in situ neutron powder diffraction study on synthetic MgFeSiO4 (Fa50). Phys. Chem. Miner. 27, 630–637 (2000).
Rangappa, D., Murukanahally, K. D., Tomai, T., Unemoto, A. & Honma, I. Ultrathin Nanosheets of Li2MSiO4 (M = Fe, Mn) as High-Capacity Li-Ion Battery Electrode. Nano Lett. 12, 1146–1151 (2012).
Lv, D. P. et al. Understanding the High Capacity of Li2FeSiO4: In Situ XRD/XANES Study Combined with First-Principles Calculations. Chem. Mater. 25, 2014–2020 (2013).
Lu, Z., Schechter, A., Moshkovich, M. & Aurbach, D. On the electrochemical behavior of magnesium electrodes in polar aprotic electrolyte solutions. J. Electroanal. Chem. 466, 203–217 (1999).
Armstrong, A. R., Kuganathan, N., Islam, M. S. & Bruce, P. G. Structure and Lithium Transport Pathways in Li2FeSiO4 Cathodes for Lithium Batteries. J. Am. Chem. Soc. 133, 13031–13035 (2011).
Saracibar, A., Van der Ven, A. & Arroyo-de Dompablo, M. E. Crystal Structure, Energetics, And Electrochemistry of Li2FeSiO4 Polymorphs from First Principles Calculations. Chem. Mater. 24, 495–503 (2012).
Masese, T. et al. Relationship between Phase Transition Involving Cationic Exchange and Charge–Discharge Rate in Li2FeSiO4 . Chem. Mater. 26, 1380–1384 (2014).
Dominko, R. et al. On the Origin of the Electrochemical Capacity of Li2Fe0.8Mn0.2SiO4 . J. Electrochem. Soc. 157, A1309–A1316 (2010).
Augustsson, A. et al. Electronic structure of phospho-olivines LixFePO4(x = 0,1) from soft-x-ray-absorption and -emission spectroscopies. J. Chem. Phys. 123, 184717 (2005).
Sathiya, M. et al. Reversible anionic redox chemistry in high-capacity layered-oxide electrodes. Nature Mater. 12, 827–835 (2013).
Muldoon, J. et al. Electrolyte roadblocks to a magnesium rechargeable battery. Energy Environ. Sci. 5, 5941–5950 (2012).
Yoshida, K. et al. Correlation between battery performance and lithium ion diffusion in glyme-lithium bis(trifluoromethanesulfonyl)amide equimolar complexes. J. Electrochem. Soc. 159, A1005–A1012 (2012).
This work was supported by Core Research for Evolutional Science and Technology (CREST) under the auspices of the Japan Science and Technology Agency (JST). Synchrotron radiation experiments were performed at beam lines BL01B1, BL14B2 and BL02B2 of SPring-8 with the approval of the Japan Synchrotron Radiation Research Institute (JASRI) (proposal nos. 2012B1018, 2012A1022, 2011B1029 and 2011A1021).
The authors declare no competing financial interests.
Electronic supplementary material
About this article
Cite this article
Orikasa, Y., Masese, T., Koyama, Y. et al. High energy density rechargeable magnesium battery using earth-abundant and non-toxic elements. Sci Rep 4, 5622 (2015). https://doi.org/10.1038/srep05622
Advanced Energy Materials (2020)
Noncrystalline Nanocomposites as a Remedy for the Low Diffusivity of Multivalent Ions in Battery Cathodes
Chemistry of Materials (2020)
Boosting electrochemical reactivity of tin as an anode for Mg ion batteries through introduction of second phase
Journal of Power Sources (2020)
Improved Non-Grignard Electrolyte Based on Magnesium Borate Trichloride for Rechargeable Magnesium Batteries
Scientific Reports (2020)
Spinel–rocksalt transition as a key cathode reaction toward high-energy-density magnesium rechargeable batteries
Current Opinion in Electrochemistry (2020)