Heterojunction Hybrid Devices from Vapor Phase Grown MoS2


We investigate a vertically-stacked hybrid photodiode consisting of a thin n-type molybdenum disulfide (MoS2) layer transferred onto p-type silicon. The fabrication is scalable as the MoS2 is grown by a controlled and tunable vapor phase sulfurization process. The obtained large-scale p-n heterojunction diodes exhibit notable photoconductivity which can be tuned by modifying the thickness of the MoS2 layer. The diodes have a broad spectral response due to direct and indirect band transitions of the nanoscale MoS2. Further, we observe a blue-shift of the spectral response into the visible range. The results are a significant step towards scalable fabrication of vertical devices from two-dimensional materials and constitute a new paradigm for materials engineering.


Molybdenum disulfide (MoS2), a semiconducting transition metal dichalcogenide (TMD), has drawn a lot of attention owing to its fascinating electronic and optical/optoelectronic properties1,2,3,4. Layered TMDs have a stacked two-dimensional (2D) lattice structure composed of an atomic plane of metal atoms sandwiched between two planes of chalcogen atoms. Recent studies on MoS2 thin film field effect transistors have shown that the MoS2 channel has very clear n-type characteristics with high mobility and good current on/off ratios5,6,7, which indicate that this layered material could be utilized in integrated circuits and logic circuit applications8,9. Further, it has been shown that monolayer MoS2 has a direct band gap of ~1.8 eV, whereas bulk MoS2 has an indirect band gap of ~1.3 eV2,10,11,12. The ability to tune the optical band gap of MoS2 by thickness modulation suggests a wide range of applications in optoelectronic devices including phototransistors and photodetectors10,13,14,15.

Even though the optoelectronic properties of MoS2 were the subject of intense research in the late 1960s16, scalable and reliable device production remains challenging, with most recent (opto-)electronic devices having been based on mechanically exfoliated MoS2 with e-beam defined contacts in a 3-terminal field effect transistor (FET) configuration. These investigations focused on field-induced charge carrier movements, however, photoconductivity measurements at the junction between layered MoS2 and conventional semiconducting substrates have rarely been conducted, which may be due to the lateral size limit of mechanically exfoliated flakes17. Additionally, exfoliation techniques have limited reproducibility and scalability1,2,18,19,20. Recently, large-area growth techniques based on vapor phase sulfurization of thin Mo films have been adopted for the synthesis of MoS2 thin films21,22. We have previously shown that vapor phase grown MoS2 thin films are electrically viable and can be employed to make sensors showing ultra-high sensitivity to ammonia23.

In this work, we introduce p-n heterojunction diodes fabricated by transferring vapor phase grown n-type MoS2 thin films onto p-type silicon (p-Si) substrates. Previously, we created high quality diodes by transferring monolayer graphene onto pre-patterned silicon substrates24,25. In a similar fashion, MoS2 layers of varying thicknesses are transferred forming a vertical hybrid device. This design allows the MoS2 film to be directly exposed to light. The effect of varying the incident light intensity, wavelength and MoS2 film thickness was investigated. The devices reported here display extraordinary sensitivity to changes in illumination. The spectral response showed a very broad spectrum with contributions from indirect and direct band gap transitions. Further, we report an extension of the spectrum into the visible range.

MoS2 thin films were synthesized by vapor phase sulfurization of Mo films of varying thickness. The thicknesses of the MoS2 films were found to be 4.17 ± 0.18, 8.26 ± 0.29, 12.52 ± 0.26 and 15.96 ± 0.16 nm, respectively, by spectroscopic ellipsometry (SE)26 (See the Supplementary Information for more details on the SE measurements). Raman spectra were used to assess the quality of the MoS2 films, as shown in Figure 1(a). The spectra all show the characteristic signal of 2H-MoS2 with no obvious contributions from carbon contamination, polymer residue or oxides. The positions of the (~383 cm−1) and A1g (~408 cm−1) peaks of the MoS2 films, which are related to in plane and out of plane vibrational modes, respectively, are labelled for clarity. Previous reports on mechanically exfoliated flakes have noted a divergence in these peaks for films progressing from few-layer (< 5) to bulk MoS212 In our case, all of the films resemble bulk MoS2 except for the 4.17 nm film, which displays a blue-shifted peak. The average thickness of 4.17 nm, as measured by spectroscopic ellipsometry, suggests an average number of layers of ~6. However, given that the films are polycrystalline, it is probable that the observed peak shift can be explained by the presence of some few-layer (< 5) crystals. For thicker films, the spectra are consistent over the entire film, indicating the homogeneity of the film synthesis (see Figure S1(a)–(d) of the Supplementary Information). High-resolution transmission electron microscopy (HRTEM) analysis of the 8.26 nm film transferred to a TEM grid is depicted in Figure 1(b), which indicates a polycrystalline structure in plane. Analysis of the selected area electron diffraction (SAED) pattern in various regions gave a Mo-Mo lattice spacing of ~0.32 nm which is in agreement with the literature value27,28,29,30. However, ~20% of SAED results showed lattice spacing values between 0.306–0.308 nm, which is 4% less than the reported literature value of 0.32 nm (See Figure S2(a)–(b) of the Supplementary Information for more details on the SAED pattern analysis). We note that such an assignment is preliminary, even though the greatest care was taken in ensuring the accuracy of these measurements.

Figure 1

(a) Raman spectra of the MoS2 thin films with various thicknesses grown by vapor phase sulfurization of Mo thin films. A slight shift of the E12g band is evident. (b) HRTEM image of a MoS2 thin film transferred to a TEM grid (Inset: a corresponding image at high magnification).

Large-scale MoS2 films were transferred using a polymer support technique leaving the films mechanically and electrically intact. In order to fabricate photodiodes, MoS2 films of ~1 cm2 area were transferred onto the pre-patterned p-Si substrates, as described in the methods section. The native oxide layer on the exposed silicon surface was removed with HF prior to deposition, ensuring good electrical contact between the MoS2 and the Si. As shown in Figure 2(a), one end of the transferred MoS2 film was placed on the p-Si surface without touching the metal electrode on the p-Si substrate, while the other end was connected to the Au pad on the SiO2 layer, forming an ohmic contact between them5,10,31. More details on the transfer process are presented in Figure S3(b) of the Supplementary Information.

Figure 2

(a) Schematic (left) and photograph (right) of the n-type MoS2/p-Si heterojunction diode. (b) J-V plot of the diode with 12.52 nm thick MoS2 on a linear scale (left) and semi-logarithmic scale (right) under dark (black) and illuminated (red) conditions. Inset of the left indicates open-circuit voltage (0.13 V) and short-circuit current (0.01 mA/cm2).

A plot of current-voltage (J-V) measurements of the diode device with 12.52 nm thick MoS2 is depicted in Figure 2(b). The MoS2 layers were fully electrically intact and well contacted by the gold pad as detailed above and therefore current transport was dominated by the MoS2/Si interface region. Clear rectifying behavior was observed in the dark. The forward J-V characteristics of a diode in dark conditions can be expressed using the diode equation32, the ideality factor (n ≥ 1) of a diode, which represents how closely the diode follows ideal diode behavior and has a value of unity in the ideal case, can be extracted from it. Considering the effect of the series resistance of the device, which is an additional secondary resistance component observed in the high forward bias region of practical diode devices, it gives an ideality factor value of 1.68 with a series resistance value of 7.3 kΩ, indicating good rectifying performance. Details of the diode parameter extraction are presented in the Supplementary Information.

The diodes exhibit obvious photoconductivity under illumination with a white light source as presented in Figure 2(b). While little variation in the current density is seen between dark and illuminated conditions under forward bias, there is an obvious distinction in the reverse bias region. In the dark the device is in the off state under reverse bias and there is low reverse leakage current, but while illuminated, an evident current increase is observed in the reverse bias region. A cross sectional view of the n-type MoS2/p-Si diode structure and its energy band diagram in reverse bias under illumination are shown in Figure 3(a). The n-type MoS2 and the p-Si substrate form a p-n heterojunction and the topside of the MoS2 film is exposed to the light source. Upon the incidence of photons, the valence band electrons are excited to the conduction band, generating electron-hole pairs in the n-type MoS2, depletion layer and p-type Si. In the depletion layer, the excited electrons and holes are accelerated to the n-type MoS2 and to the p-Si, respectively and they are then collected in the n-type MoS2 and p-Si region. When the electrodes of the p-Si substrate and n-type MoS2 thin film are connected to an external circuit, electrons will flow away from the n-type MoS2 film to the p-Si side and holes will flow away from the p-Si substrates to the n-type MoS2 side, generating a current.

Figure 3

(a) Cross sectional view of the n-type MoS2/p-Si diode structure (left) and its energy band diagram in reverse bias (right) under illumination, describing the movement of electrons () and holes (). Ec, EF, Ev, Eg and denote the conduction band, Fermi energy level, valence band, band gap and photon energy of the incident light, respectively. (b) J-V plot of the diode with the 12.52 nm thick MoS2 film on a semi-logarithmic scale under various incident light intensities (dark, 10, 30, 60 and 100% of full intensity) and (c) an associated photocurrent density (Jph) plot extracted from the J-V measurements in the reverse bias region. (d) A Jph plot with varying incident light intensity at reverse biases of V = −1 and −2 V. (e) A plot of Jph of the diode devices with different MoS2 thickness (4.17, 8.26, 12.52 and 15.96 nm) under reverse dc bias.

Figure 3(b) and 3(c) show a J-V plot of the diode with the 12.52 nm thick MoS2 film under various light intensities and a photocurrent density (Jph) plot extracted from the J-V measurements in the reverse bias region. The incident light intensity was controlled by a solid state dimmer and expressed using a relative value for the full intensity of the white light source. When the light intensity increased from 0 to 100%, the measured current density also showed an increasing trend in the reverse bias region proportional to the incident light intensity. From the photo response of the diode, which measures the output photocurrent for varying input light intensity, the relative responsivity of the diodes for the light can be compared. At reverse dc biases of V = −1 V and −2 V, the generated Jph shows a nearly linear increment giving a photocurrent value of 0.49 mA and 0.83 mA at the full intensity of the light source, respectively (Figure 3(d)). The larger responsivity at higher reverse dc biases can be attributed to the fact that the energy barrier height at the junction between n-type MoS2 and p-Si increases due to the increasing external electric field when a higher reverse bias is applied to the junction. This means the electrical potential difference across the depletion layer at the junction becomes much larger, which results in a stronger acceleration of electrons and holes in the depletion region and therefore a higher current.

In addition, the effect of modifying the MoS2 thickness on the photocurrent was investigated. The thickness values of MoS2 films, as measured by SE, were found to be 4.17, 8.26 and 15.96 nm. The J-V plots exhibit clear photoconductivity for all the devices when they are illuminated by the light source, as shown in Figure S5(a)–(c) of the Supplementary Information. The Jph values of the diodes with different MoS2 thicknesses under reverse bias are compared in Figure 3(e). It is clear from these results that when the same incident light intensity (50% of full intensity) is applied, the diode device with a thicker MoS2 thin film shows higher photocurrent values. This is because the volume of photon absorption in the n-type MoS2 thin film becomes larger with increased MoS2 film thickness. As more photons are absorbed in the thicker MoS2 layer more electron-hole pairs are produced, increasing the photocurrent of the device. This implies that it is possible to define the level of photoconductivity for MoS2/Si photodiode devices through modulation of the MoS2 film thickness.

The absolute spectral response was measured using a lock-in technique with a chopped photon flux over an investigated wavelength interval of 10 nm. Since the collimated incident light beam is bigger than the probe active area, a mask was used to define an illumination spot of 20 mm2 on the device, either on the MoS2 region or on the p-Si next to the MoS2 (Figure 4 (a)). This allows contributions from the blank p-Si substrate to the generated photocurrent to be eliminated. The spectral response of the diode device with an 8.26 nm thick MoS2 film for a reverse bias voltage between 0–2 V is plotted in Figure 4 (b). The multilayer MoS2 photodiode exhibits a wide spectral response, which increases with higher reverse bias voltages due to the increase of the external electrical field. The spectral responsivity of 1.4–8.6 mA/W at reverse dc biases of V = −2 V is achieved in the broad spectral range from visible to near-infrared. While this performance is inferior to that of recently reported monolayer (800 A/W) and multilayer MoS2 (thickness 30–60 nm, 120–210 mA/W) photodetectors14,33,34, it is better than previously reported monolayer MoS2 phototransistors (~7.5 mA/W)13 and graphene photodetectors (~0.5 mA/W)35. The underlying p-type silicon absorption peak is observed at approximately 1.07 eV (1158 nm) confirmed in a reference measurement where the illumination spot was moved to the p-Si (See Figure S6 in the Supplementary Information). Three additional peaks were identified through fitting in the spectrum at 1.43 eV, 2.15 eV and 2.48 eV. The first peak at 1.43 eV (867 nm) can be explained by the indirect band transition (Σmv) of multilayer MoS2 as indicated by the blue arrow in Figure 4(c). Moreover, there is a strong contribution from the direct band gap transition observed in nanoscale MoS2 films. This is an interesting observation considering the thickness of the film is 8.26 nm and therefore approximately 12 layers thick. The direct band gap contribution is split into light- (Km-Kv1) and heavy holes (Km-Kv2). Therefore, two distinct peaks in the spectral response are observed at energies of 2.15 eV (576 nm) and 2.48 eV (500 nm), illustrated by the red and green arrow in Figure 4(c).

Figure 4

(a) Schematic of the heterojunction diode with mask openings for MoS2 and p-Si indicated for spectral response measurements. (b) Absolute spectral response (Abs. SR) vs. wavelength (lower x-axis) and energy (upper x-axis) related to the diode device with an 8.26 nm thick MoS2 film at zero bias and reverse bias (VR) of 1 and 2 V with the mask opening on MoS2. The inset indicates the illumination of the diode. (c) Calculated energy bands for bulk MoS2. (d) Variation of the direct and indirect band gaps, with respect to the equilibrium case, as a function of the interlayer distance (expressed in %) and (e) variation of the direct and indirect band gaps, with respect to the equilibrium case, as a function of the lattice spacing (expressed in %).

Interestingly, we observe a blue-shift of 0.13 eV for the indirect transition and of approximately 0.4 eV for both direct transitions compared to the theoretical values for exfoliated MoS2 (i.e. 1.3 eV for the indirect band transition and 1.8 eV and 2.0 eV for light- and heavy holes for the direct band transition)2,33 and those observed experimentally20,26. This blue shift in the spectral response of bulk MoS2 compared with the absorption spectrum was previously mentioned by Wilson and Yoffe16.

Density functional theory (DFT) calculations were employed to investigate potential causes of the observed blue shift. In particular, the influence of both inter-layer spacing and lattice spacing on the band structure of multilayer MoS2 was studied. DFT calculations were performed to compute the electronic band structure of bulk MoS2. Computed bands are shown in Figure 4(c), where the maxima (Km, Σm) and the minima (Kv1, Kv2, Γv) of the conduction and valence bands, respectively, are highlighted. In Figure 4(d), we show the variations of the direct (Km-Kv1/Kv2) and indirect band gap (Σmv) with respect to the equilibrium case, as a function of the inter-layer distance (expressed in %). As soon as the interlayer distance is increased, the indirect band gap increases, while the direct band gap is negligibly affected. This is in agreement with recent simulations performed on bilayer MoS215. Γv are characterized by p-orbital wave-functions centered in correspondence of S atoms, while K minima are related to d-orbitals localized around Mo atoms. As a consequence, K points are less affected by increases in the interlayer distance, while the opposite holds for Γv minimum. In Figure 4(e), we show the same quantities as above, but as a function of lattice spacing variation. In this case, we qualitatively reproduce the larger shift of the direct band gaps with respect to the indirect band gap as soon as the lattice is compressed. From a quantitative point of view, a compression of 4% serves to explain the observed blue-shifted peak positions for both the indirect and direct transitions in the spectral response analysis of the device. Thus we tentatively assign the observed blue-shifted absorption peaks to the disordered lattice of our MoS2 films. This assumption is supported by our HRTEM analysis which shows slight compression in regions of our polycrystalline films. This could stem from the high temperature growth mechanism or could possibly be caused by the film transfer process. It must be noted here that a difference in the strain transfer and relaxation mechanism may exist when the MoS2 films are transferred onto different substrates, such as a TEM grid and a silicon substrate. Further, we cannot completely rule out the presence of dopants and contamination (e.g. oxygen) in the films, which could lead to lattice distortions. Nonetheless, the variation of the photo-response of 2D TMDs is an exciting and unexpected finding and will undoubtedly be the subject of further investigation, particularly as this variation in the spectral response of layered TMDs could present a wide range of opportunities in material design.

In summary, p-n heterojunction diodes were fabricated using n-type MoS2 films with varying thicknesses and p-Si substrates. MoS2 thin films are laterally in contact with p-Si substrates over the substrate area, allowing for direct exposure to incident light of varying intensity. Electrical measurements revealed that the n-type MoS2/p-Si diodes have good rectifying behavior as well as clear photoconductive characteristics. The photocurrent of the device has a strong dependence on the MoS2 film thickness whereby the thicker MoS2 films produce more photocurrent due to their increased volume for photon absorption. This demonstrates the potential to control the photocurrent of MoS2/Si diodes by modulating the thickness of the MoS2 layer. The spectral response of the device showed that there are contributions from direct and indirect band transitions in the multilayer MoS2 film. We further observed a substantially extended spectral range for our device into the visible range.

By employing a polymer support transfer process for the MoS2 thin films the MoS2/Si hybrid structure, which combines a semiconducting nanoscale TMD and a traditional semiconducting material, was realized. This approach could potentially be extended to various other semiconducting materials in such hybrid structures. Further comprehensive studies of such structures are required to improve device performance and engineer the properties of the interface. Nevertheless, this type of hybrid device demonstrates the benefits of using long developed semiconducting technology to take advantage of the novel properties of nanomaterials for future nano- and optoelectronic devices.


Commercially available lightly doped p-Si wafers with a thermally grown silicon dioxide (SiO2) layer (292 nm) were used as substrates. The p-Si wafer had a dopant (boron) concentration of 2.5 × 1015 cm−3 and <100> orientation. A part of the SiO2 layer was completely etched by immersing it in 3% diluted hydrofluoric acid (HF) for 20 minutes, resulting in a sloped sidewall at the Si/SiO2 boundary. Using a shadow mask, nickel (Ni) and gold (Au) metal electrodes (Ni/Au = 20/50 nm) were deposited on top of the remaining SiO2 layer and the exposed p-Si area. In order to achieve ohmic contacts between p-Si and Ni, the substrate was annealed at 400°C under N2 flow for 5 minutes.

MoS2 thin films were synthesized using a vapor phase sulfurization process similar to the method described previously22,23. Mo films of varying thickness were deposited on SiO2/Si substrates using a Gatan Precision Etching and Coating System (PECS), where the Mo film deposition rate (<0.1 nm/s) and thickness were monitored using a quartz crystal microbalance. Sulfurization of the Mo samples took place in a quartz tube furnace consisting of two different heating zones. The sputtered films were placed in a zone which was heated to 750°C and annealed for 30 minutes at a pressure of ~1 Torr under an argon (Ar) flow of 150 sccm (standard cubic centimeters per minute). Sulfur powder was heated to its melting point (113°C) in the inlet zone of the furnace and the generated sulfur vapor was supplied to the Mo films, where it reacted to produce MoS2. This technique yielded a continuous multilayer of MoS2. A schematic diagram of the process is shown in Figure S3(a) of the Supplementary Information.

The as-grown MoS2 thin films were transferred onto various substrates. A polymer support technique was employed for the transfer process, whereby polymethyl methacrylate (PMMA, MicroChem) was spin-coated onto the MoS2. The films were then floated on 2 M NaOH at room temperature until the SiO2 layer between the MoS2 and the Si substrates was completely etched away, leaving MoS2/PMMA films floating on the surface. After cleaning in deionized water the films were transferred onto arbitrary substrates. The PMMA support layer was then dissolved in acetone at room temperature for 20 minutes.

Thickness measurements of MoS2 thin films were carried out using a spectroscopic ellipsometry tool (Alpha SE, J. A. Woollam Co., Inc.) operating in the wavelength range of 380–900 nm at an angle of incidence of 70°. HRTEM analysis was performed in an FEI Titan transmission electron microscope at an acceleration voltage of 300 kV. Diffraction patterns were acquired at a camera length of 580 mm to expand the 100 diffraction ring; this increased the pixel count and improved the accuracy of the lattice measurements. MoS2 films were prepared for TEM characterization by floating the layers as described previously, then, from water dredging them onto a 300 mesh lacey carbon copper TEM grid (Agar Scientific). Raman spectra were obtained with a Witec Alpha 300 R confocal Raman microscope, using an excitation wavelength of 532 nm with a power of <1 mW and a spectral grating with 1800 lines/mm. Electrical measurements were conducted on a Suss probe station connected to a Keithley 2612A source meter unit under ambient conditions. The metal electrode on the p-Si substrate was positively biased and the electrode on the SiO2 layer was negatively biased. A white light source with a solid state dimmer for variable light intensity (ACE Light Source, SCHOTT: A20500, 150 watt halogen lamp) was used for photoconductivity measurements.

The spectral response was measured by a comparative method to a known spectral response of a reference detector using a Labview controlled setup. The light was generated by a tungsten-halogen and a deuterium-arc lamp and covered the wavelength range of 200–2000 nm. Specific wavelengths were selected by a monochromator (Acton Research Corporation, SP-555) using appropriate grids and filters. The light power density varied from 1 µW/cm2 at a wavelength of 200 nm up to 55 µW/cm2 at a wavelength of 1150 nm. A silicon photodiode was used to calibrate the setup. Due to the spectral limitation of the silicon photodiode, the spectral response measurement was limited to the range of 400 nm–1250 nm. The detector currents were measured by pre-amplifiers (Femto, DLPCA-200) and lock-in amplifiers (Princeton Applied Research Corporation, Model 5210) with 300 ms integration time and 0.4 Hz band width at 17 Hz optical chopper frequency for detection of ultra-low currents down to 10 pA. The measurement principle allows a wavelength dependent correction factor to be established for the probe spectral response calculation which takes into account variations of the preamplifiers, the difference between the reference detector area and the probe area as well as varying photo flux densities caused by the monochromator grids and filters.

Density functional theory (DFT) calculations were carried out to compute the electronic band structure of bulk MoS2. A Local density approximation (LDA) was assumed, adopting the exchange-correlation function by Perdew et al.36,37. An ultra-soft pseudo-potential description of the electron-electron interaction was used with valence electrons 4d5, 5s1 and 3s2, 3p4 of Mo and S atoms, respectively. An 80 Ry wave function and a 500 Ry charge density cut-off were taken into account. A Brillouin zone sampling was considered on a Gamma centered 11 × 11 × 2 grid. Geometry optimization was performed, relaxing both ions and lattices until the total energy variation was less than 10−6 eV. Once the optimized geometry was obtained, the band structure calculations were performed in order to gain insight into the role of inter-layer distance. All calculations were conducted exploiting the Quantum-ESPRESSO package38.


  1. Novoselov, K. S. et al. Two-dimensional atomic crystals. Proc. Natl. Acad. Sci. U. S. A. 102, 10451–10453 (2005).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  2. Mak, K. F., Lee, C., Hone, J., Shan, J. & Heinz, T. F. Atomically Thin MoS2: A New Direct-Gap Semiconductor. Phys. Rev. Lett. 105, 136805 (2010).

    Article  ADS  CAS  Google Scholar 

  3. Splendiani, A. et al. Emerging Photoluminescence in Monolayer MoS2 . Nano Lett. 10, 1271–1275 (2010).

    Article  ADS  CAS  Google Scholar 

  4. Korn, T., Heydrich, S., Hirmer, M., Schmutzler, J. & Schüller, C. Low-temperature photocarrier dynamics in monolayer MoS2 . Appl. Phys. Lett. 99, 102109 (2011).

    Article  ADS  CAS  Google Scholar 

  5. Radisavljevic, B., Radenovic, A., Brivio, J., Giacometti, V. & Kis, A. Single-layer MoS2 transistors. Nat. Nanotechnol. 6, 147–150 (2011).

    Article  ADS  CAS  Google Scholar 

  6. Radisavljevic, B. & Kis, A. Mobility engineering and a metal–insulator transition in monolayer MoS2 . Nat. Mater. 12, 815–820 (2013).

    Article  ADS  CAS  PubMed  Google Scholar 

  7. Wu, W. et al. High mobility and high on/off ratio field-effect transistors based on chemical vapor deposited single-crystal MoS2 grains. Appl. Phys. Lett. 102, 142106 (2013).

    Article  ADS  CAS  Google Scholar 

  8. Radisavljevic, B., Whitwick, M. B. & Kis, A. Integrated Circuits and Logic Operations Based on Single-Layer MoS2 . ACS Nano 5, 9934–9938 (2011).

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  9. Liu, L., Lu, Y. & Guo, J. On Monolayer MoS2 Field-Effect Transistors at the Scaling Limit. IEEE Trans. Electron Dev. 60, 4133–4139 (2013).

    Article  ADS  CAS  Google Scholar 

  10. Lee, H. S. et al. MoS2 Nanosheet Phototransistors with Thickness-Modulated Optical Energy Gap. Nano Lett. 12, 3695–3700 (2012).

    Article  ADS  CAS  PubMed  Google Scholar 

  11. Schlaf, R., Lang, O., Pettenkofer, C. & Jaegermann, W. Band lineup of layered semiconductor heterointerfaces prepared by van der Waals epitaxy: Charge transfer correction term for the electron affinity rule. J. Appl. Phys. 85, 2732–2753 (1999).

    Article  ADS  CAS  Google Scholar 

  12. Lee, C. et al. Anomalous Lattice Vibrations of Single- and Few-Layer MoS2 . ACS Nano 4, 2695–2700 (2010).

    Article  CAS  Google Scholar 

  13. Yin, Z. et al. Single-Layer MoS2 Phototransistors. ACS Nano 6, 74–80 (2012).

    Article  Google Scholar 

  14. Lopez-Sanchez, O., Lembke, D., Kayci, M., Radenovic, A. & Kis, A. Ultrasensitive photodetectors based on monolayer MoS2 . Nat. Nanotechnol. 8, 497–501 (2013).

    Article  ADS  CAS  PubMed  Google Scholar 

  15. Zhao, W. et al. Origin of Indirect Optical Transitions in Few-Layer MoS2, WS2 and WSe2 . Nano Lett. 13, 5627–5634 (2013).

    Article  ADS  CAS  PubMed  Google Scholar 

  16. Wilson, J. A. & Yoffe, A. D. The transition metal dichalcogenides discussion and interpretation of the observed optical, electrical and structural properties. Adv. Phys. 18, 193–335 (1969).

    Article  ADS  CAS  Google Scholar 

  17. Lopez-Sanchez, O. et al. Light Generation and Harvesting in a van der Waals Heterostructure. ACS Nano 8, 3042–3048 (2014).

    Article  CAS  PubMed  PubMed Central  Google Scholar 

  18. Coleman, J. N. et al. Two-Dimensional Nanosheets Produced by Liquid Exfoliation of Layered Materials. Science 331, 568–571 (2011).

    Article  ADS  CAS  PubMed  Google Scholar 

  19. Joensen, P., Frindt, R. F. & Morrison, S. R. Single-layer MoS2 . Mater. Res. Bull. 21, 457–461 (1986).

    Article  CAS  Google Scholar 

  20. Eda, G. et al. Photoluminescence from Chemically Exfoliated MoS2 . Nano Lett. 11, 5111–5116 (2011).

    Article  ADS  CAS  PubMed  Google Scholar 

  21. Lee, Y.-H. et al. Synthesis of Large-Area MoS2 Atomic Layers with Chemical Vapor Deposition. Adv. Mater. 24, 2320–2325 (2012).

    Article  CAS  Google Scholar 

  22. Zhan, Y., Liu, Z., Najmaei, S., Ajayan, P. M. & Lou, J. Large-Area Vapor-Phase Growth and Characterization of MoS2 Atomic Layers on a SiO2 Substrate. Small 8, 966–971 (2012).

    Article  CAS  Google Scholar 

  23. Lee, K., Gatensby, R., McEvoy, N., Hallam, T. & Duesberg, G. S. High Performance Sensors Based on Molybdenum Disulfide Thin Films. Adv. Mater. 25, 6699–6702 (2013).

    Article  CAS  PubMed  Google Scholar 

  24. Kim, H.-Y., Lee, K., McEvoy, N., Yim, C. & Duesberg, G. S. Chemically Modulated Graphene Diodes. Nano Lett. 13, 2182–2188 (2013).

    Article  ADS  CAS  PubMed  PubMed Central  Google Scholar 

  25. Yim, C., McEvoy, N. & Duesberg, G. S. Characterization of graphene-silicon Schottky barrier diodes using impedance spectroscopy. Appl. Phys. Lett. 103, 193106 (2013).

    Article  ADS  CAS  Google Scholar 

  26. Yim, C. et al. Investigation of the Optical Properties of MoS2 Thin Films Using Spectroscopic Ellipsometry. Appl. Phys. Lett. 104, 103114 (2014).

    Article  ADS  CAS  Google Scholar 

  27. Joensen, P., Crozier, E. D., Alberding, N. & Frindt, R. F. A study of single-layer and restacked MoS2 by X-ray diffraction and X-ray absorption spectroscopy. J. Phys. C: Solid State Phys. 20, 4043–4053 (1987).

    Article  ADS  CAS  Google Scholar 

  28. Ataca, C. & Ciraci, S. Functionalization of Single-Layer MoS2 Honeycomb Structures. J. Phys. Chem. C 115, 13303–13311 (2011).

    Article  CAS  Google Scholar 

  29. Ataca, C., Topsakal, M., Aktürk, E. & Ciraci, S. A Comparative Study of Lattice Dynamics of Three- and Two-Dimensional MoS2 . J. Phys. Chem. C 115, 16354–16361 (2011).

    Article  CAS  Google Scholar 

  30. Shi, Y. et al. van der Waals Epitaxy of MoS2 Layers Using Graphene As Growth Templates. Nano Lett. 12, 2784–2791 (2012).

    Article  ADS  CAS  Google Scholar 

  31. Lembke, D. & Kis, A. Breakdown of High-Performance Monolayer MoS2 Transistors. ACS Nano 6, 10070–10075 (2012).

    Article  CAS  PubMed  Google Scholar 

  32. Neamen, D. A. Semiconductor Physics and Devices : Basic Principles. 3rd edn, 269–304 (McGraw-Hill, 2003).

  33. Choi, W. et al. High-Detectivity Multilayer MoS2 Phototransistors with Spectral Response from Ultraviolet to Infrared. Adv. Mater. 24, 5832–5836 (2012).

    Article  CAS  PubMed  Google Scholar 

  34. Esmaeili-Rad, M. R. & Salahuddin, S. High Performance Molybdenum Disulfide Amorphous Silicon Heterojunction Photodetector. Sci. Rep. 3, 2345 (2013).

    Article  ADS  PubMed  PubMed Central  Google Scholar 

  35. Xia, F., Mueller, T., Lin, Y.-M., Valdes-Garcia, A. & Avouris, P. Ultrafast graphene photodetector. Nat. Nanotechnol. 4, 839–843 (2009).

    Article  ADS  CAS  PubMed  Google Scholar 

  36. Perdew, J. P. et al. Atoms, molecules, solids and surfaces: Applications of the generalized gradient approximation for exchange and correlation. Phys. Rev. B 46, 6671–6687 (1992).

    Article  ADS  CAS  Google Scholar 

  37. Perdew, J. P. & Wang, Y. Accurate and simple analytic representation of the electron-gas correlation energy. Phys. Rev. B 45, 13244–13249 (1992).

    Article  ADS  CAS  Google Scholar 

  38. Giannozzi, P. et al. QUANTUM ESPRESSO: a modular and open-source software project for quantum simulations of materials. J. Phys.: Condens. Matter 21, 395502 (2009).

    Google Scholar 

Download references


This work is supported by the SFI under Contract No. 12/RC/2278 and PI_10/IN.1/I3030. C.Y. and M.O. acknowledge an Irish Research Council scholarship via the Enterprise Partnership Scheme. N.M. acknowledges the EU under FP7-2010-PPP Green Cars (Electrograph No. 266391). M.C.L. acknowledges financial support through an ERC grant (InteGraDe, No. 307311) as well as the German Research Foundation, DFG (LE 2440/1-1 and GRK-1568). G.F. and G.I. gratefully acknowledge Quantavis s.r.l. through funds from FP7-GONEXTs project (Contract 309201). The authors thank the Advanced Microscopy Laboratory (AML) for their assistance in electron microscopy.

Author information




G.S.D. and C.Y. conceived and designed the experiments. M.O. and C.Y. fabricated the devices and performed the electrical measurements. C.Y. analyzed the data. N.M. carried out Raman spectroscopy measurements and analysis. M.O. and C.D. performed HRTEM analysis. S.R., H.S., A.B. and M.C.L. carried out the spectral response measurements and analysis. R.P., G.I. and G.F. performed the theoretical calculations. G.S.D. supervised the whole project. All authors contributed to the discussion of the results and improving the manuscript.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Electronic supplementary material

Rights and permissions

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by-nc-nd/4.0/

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Yim, C., O'Brien, M., McEvoy, N. et al. Heterojunction Hybrid Devices from Vapor Phase Grown MoS2. Sci Rep 4, 5458 (2014). https://doi.org/10.1038/srep05458

Download citation

Further reading

  • SnS2/Si vertical heterostructure for high-performance photodetection with large photocurrent and fast speed

    • Jianxiang Xu
    • , Hongbin Zhang
    • , Zelong Song
    • , Yancai Xu
    • , Qianqian Peng
    • , Xianwu Xiu
    • , Zhen Li
    • , Chonghui Li
    • , Mei Liu
    •  & Baoyuan Man

    Applied Surface Science (2020)

  • Highly Responsive Flexible Photodetectors Based on MOVPE Grown Uniform Few-Layer MoS2

    • Daniel S. Schneider
    • , Annika Grundmann
    • , Andreas Bablich
    • , Vikram Passi
    • , Satender Kataria
    • , Holger Kalisch
    • , Michael Heuken
    • , Andrei Vescan
    • , Daniel Neumaier
    •  & Max C. Lemme

    ACS Photonics (2020)

  • Direct growth of NbSe2 and TiSe2 thin flakes via deposited film selenization

    • Ren Hachiya
    • , Noriyuki Urakami
    •  & Yoshio Hashimoto

    Japanese Journal of Applied Physics (2020)

  • Electron Transport across Vertical Silicon/MoS2/Graphene Heterostructures: Towards Efficient Emitter Diodes for Graphene Base Hot Electron Transistors

    • Melkamu Belete
    • , Olof Engström
    • , Sam Vaziri
    • , Gunther Lippert
    • , Mindaugas Lukosius
    • , Satender Kataria
    •  & Max C. Lemme

    ACS Applied Materials & Interfaces (2020)

  • Production and processing of graphene and related materials

    • Claudia Backes
    • , Amr M Abdelkader
    • , Concepción Alonso
    • , Amandine Andrieux-Ledier
    • , Raul Arenal
    • , Jon Azpeitia
    • , Nilanthy Balakrishnan
    • , Luca Banszerus
    • , Julien Barjon
    • , Ruben Bartali
    • , Sebastiano Bellani
    • , Claire Berger
    • , Reinhard Berger
    • , M M Bernal Ortega
    • , Carlo Bernard
    • , Peter H Beton
    • , André Beyer
    • , Alberto Bianco
    • , Peter Bøggild
    • , Francesco Bonaccorso
    • , Gabriela Borin Barin
    • , Cristina Botas
    • , Rebeca A Bueno
    • , Daniel Carriazo
    • , Andres Castellanos-Gomez
    • , Meganne Christian
    • , Artur Ciesielski
    • , Tymoteusz Ciuk
    • , Matthew T Cole
    • , Jonathan Coleman
    • , Camilla Coletti
    • , Luigi Crema
    • , Huanyao Cun
    • , Daniela Dasler
    • , Domenico De Fazio
    • , Noel Díez
    • , Simon Drieschner
    • , Georg S Duesberg
    • , Roman Fasel
    • , Xinliang Feng
    • , Alberto Fina
    • , Stiven Forti
    • , Costas Galiotis
    • , Giovanni Garberoglio
    • , Jorge M García
    • , Jose Antonio Garrido
    • , Marco Gibertini
    • , Armin Gölzhäuser
    • , Julio Gómez
    • , Thomas Greber
    • , Frank Hauke
    • , Adrian Hemmi
    • , Irene Hernandez-Rodriguez
    • , Andreas Hirsch
    • , Stephen A Hodge
    • , Yves Huttel
    • , Peter U Jepsen
    • , Ignacio Jimenez
    • , Ute Kaiser
    • , Tommi Kaplas
    • , HoKwon Kim
    • , Andras Kis
    • , Konstantinos Papagelis
    • , Kostas Kostarelos
    • , Aleksandra Krajewska
    • , Kangho Lee
    • , Changfeng Li
    • , Harri Lipsanen
    • , Andrea Liscio
    • , Martin R Lohe
    • , Annick Loiseau
    • , Lucia Lombardi
    • , Maria Francisca López
    • , Oliver Martin
    • , Cristina Martín
    • , Lidia Martínez
    • , Jose Angel Martin-Gago
    • , José Ignacio Martínez
    • , Nicola Marzari
    • , Álvaro Mayoral
    • , John McManus
    • , Manuela Melucci
    • , Javier Méndez
    • , Cesar Merino
    • , Pablo Merino
    • , Andreas P Meyer
    • , Elisa Miniussi
    • , Vaidotas Miseikis
    • , Neeraj Mishra
    • , Vittorio Morandi
    • , Carmen Munuera
    • , Roberto Muñoz
    • , Hugo Nolan
    • , Luca Ortolani
    • , Anna K Ott
    • , Irene Palacio
    • , Vincenzo Palermo
    • , John Parthenios
    • , Iwona Pasternak
    • , Amalia Patane
    • , Maurizio Prato
    • , Henri Prevost
    • , Vladimir Prudkovskiy
    • , Nicola Pugno
    • , Teófilo Rojo
    • , Antonio Rossi
    • , Pascal Ruffieux
    • , Paolo Samorì
    • , Léonard Schué
    • , Eki Setijadi
    • , Thomas Seyller
    • , Giorgio Speranza
    • , Christoph Stampfer
    • , Ingrid Stenger
    • , Wlodek Strupinski
    • , Yuri Svirko
    • , Simone Taioli
    • , Kenneth B K Teo
    • , Matteo Testi
    • , Flavia Tomarchio
    • , Mauro Tortello
    • , Emanuele Treossi
    • , Andrey Turchanin
    • , Ester Vazquez
    • , Elvira Villaro
    • , Patrick R Whelan
    • , Zhenyuan Xia
    • , Rositza Yakimova
    • , Sheng Yang
    • , G Reza Yazdi
    • , Chanyoung Yim
    • , Duhee Yoon
    • , Xianghui Zhang
    • , Xiaodong Zhuang
    • , Luigi Colombo
    • , Andrea C Ferrari
    •  & Mar Garcia-Hernandez

    2D Materials (2020)


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Sign up for the Nature Briefing newsletter for a daily update on COVID-19 science.
Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing