Chemical reduction of graphene oxide (GO) is the main route to produce the mass graphene-based materials with tailored surface chemistry and functions. However, the toxic reducing circumstances, multiple steps, and even incomplete removal of the oxygen-containing groups were involved, and the produced graphenes existed usually as the assembly-absent precipitates. Herein, a substrate-assisted reduction and assembly of GO (SARA-GO) method was developed for spontaneous formation of 3D graphene network on arbitrary conductive substrates including active and inert metals, semiconducting Si, nonmetallic carbon, and even indium-tin oxide glass without any additional reducing agents. The SARA-GO process offers a facile, efficient approach for constructing unique graphene assemblies such as microtubes, multi-channel networks, micropatterns, and allows the fabrication of high-performance binder-free rechargeable lithium-ion batteries. The versatile SARD-GO method significantly improves the processablity of graphenes, which could thus benefit many important applications in sensors and energy-related devices.
Graphene, an atomic-thick layer of carbon atoms with unique properties such as high electrical conductivity, large surface area, good chemical, environmental and mechanical stability, has drawn extensive attention from both the experimental and theoretical communities due to its promising applications in energy, environment, biology, and electronics1,2,3,4,5,6.
For preparation of graphenes, chemical reduction of graphene oxide (GO) is one of the most important routes owing to its feasibility for mass production of graphene-based materials with tailored surface chemistry and functions7. However, chemical treatment of GO was usually carried out in reducing circumstances such as hydrazine (N2H4)8, H2/Ar with alcohol under high temperatures9, strong alkaline sodium/potassium hydroxide10,11, sodium borohydride/sulfuric acid12, hydriodic acid13, sodium-ammonia solution14. Besides that the reduction reactions are often involved in the toxicity of the reducing agents, multiple steps, long reaction time, and even incomplete removal of the oxygen-containing groups15, the produced graphenes are usually collected as random precipitates or agglomeration lacking of well-confined organization such as three-dimensional (3D) graphene assembles16,17,18,19, which largely limit their applications in energy-related devices.
The recent findings that GO can be directly reduced by active metals (e.g., Al, Fe, Cu)20,21,22 open the new possibility for controlled assembly of graphenes on conductive substrates. Herein, we demonstrate a powerful, facile but efficient substrate-assisted reduction and assembly of GO (SARA-GO) (Figure 1). The spontaneous reduction of GO and its well-organized assembly into 3D network on arbitrary conductive surfaces such as the active metals of Zn, Fe, and Cu, inert metals of Ag, Pt, and Au, semiconducting Si wafer, nonmetallic carbon-based film, and even indium-tin oxide (ITO) glass are achieved readily without any additional reducing agents. As we shall see later, the versatile SARD-GO method offers an efficient approach for constructing a variety of unique graphene assemblies such as microtubes, four-way pipes, spiral tubes, multi-channel networks, and micropatterns, and allowing the fabrication of high-performance binder-free rechargeable lithium-ion batteries (LIBs) by spontaneously deposition of 3D graphene network on Cu foil as anode. The SARD-GO method significantly improves the versatile process of graphenes, which could thus benefit many important applications of graphenes in sensors and energy-related devices.
SARA-GO on active metal surface
As one example, the Cu foil has been standing in the aqueous 1 mg/mL GO suspension with a pH = 4.0 for several hours without any additives, a black layer of reduced GO (RGO) covers its whole surface (Fig. 2a and Supplementary Fig. S1), which is composed of the 3D network of RGO sheets (Fig. 2b and Supplementary Fig. S2). The amount of deposited RGO on Cu foil can be modulated conveniently by the reaction time (Supplementary Fig. S3).
TEM investigation reveals that the as-prepared RGO sheets are decorated with nanoparticles (Fig. 2c), which are easily removed after washing with aqueous HCl solution (Fig. 2d, and Supplementary Fig. S4). Electron diffraction pattern of the RGO sheets presents clear diffraction spots without halation (Fig. 2d, inset), implying the highly crystalline graphene structure.
X-ray diffraction (XRD) further confirms that the representative peak of GO (2θ = ca. 11°, the bottom curve in Fig. 2e) has completely disappeared in the as-prepared RGO samples, accompanied with a new broad peak centered at around 24° and a series of sharp peaks (the middle curve in Fig. 2e). The peaks at 2θ = ca. 40°, 47°, 68°, 82°, and 86° correspond to the (111), (200), (220), (311) and (222) planes of face-centered cubic (fcc) structure of Cu2O (JCPDS ICDD card NO. 01-1194). After washed with aqueous HCl solution, the RGO presents a dominant peak centered at 2θ = ca. 24° (the upper curve in Fig. 2e), corresponding to the (002) plane of stacked graphene sheets with an interlayer spacing of about 0.37 nm. It is larger than the d-spacing (0.336 nm) of graphite, suggesting the incompact stacking of as-produced graphenes in the sample.
The chemical structure of the RGO deposited on Cu foil was also studied by Raman and X-ray photoelectron spectroscopy (XPS). Raman spectrum indicates that GO sheets were reduced and their conjugated structures were partly restored (Supplementary Fig. S5). XPS analysis shows that the intensity of O peak for RGO has decreased drastically in comparison with GO (Fig. 2f). A Cu peak appears on the as-prepared RGO (the middle curve in Fig. 2f) and on the residues in the GO suspension (Supplementary Fig. S6), suggesting the Cu has been involved in the reduction reaction of GO. The Cu related peaks vanished in the RGO sample with aqueous HCl treatment (Fig. 2f, the upper curve) in consistent with the XRD observation. Fig. 2g shows the high resolution Cu2p spectrum, which reveals that Cu exists in an oxidized form with two peaks at around 932.2 and 951.9 eV assigned to Cu 2p3/2and Cu 2p1/2 of Cu+, respectively23,24. The XPS also indicates the presence of Cu2+, suggesting that the surfaces of the Cu2O nanoparticles were partially oxidized to CuO. The results are consistent with other observations of copper oxidation at the nanoscale25,26,27. Combined with the fact that no diffractions from CuO were detected in XRD pattern (the middle curve Fig. 2e), it can be concluded that only a small amount of Cu2O was oxidized and/or the formed CuO might be amorphous.
High resolution C1s peak of the final RGO proves that oxygen-containing groups have been removed significantly. The C1s spectrum of the original GO (Fig. 2h) reveals four types of carbon bonds: C = C/C–C (∼284.8 eV), C–O (hydroxyl and epoxy, ~286.6 eV), C = O (carbonyl, ~287.5 eV) and O–C = O (carboxyl, ~288.7 eV)25. For the RGO formed on Cu foil, however, the majority of oxygen functional groups have been removed and the C–C bonds become dominant (Fig. 2h). The C/O atomic ratio of RGO is ca. 9.1 (Table S1), which, although not the best, is much higher than that of RGO synthesized by other typical reduction process (Table S2).
Through the extensive investigation mentioned above, we conclude that, based on the SARA-GO in Fig. 1a, GO has been spontaneously reduced to graphene (also called RGO in this work) in a 3D network form, while the Cu substrate is oxidized into the Cu oxide. Other active metals such as Al, Zn, Fe, Co also play well for direct formation the 3D graphene network on their foils (Fig. 2i–l and Supplementary Fig. S7–S16).
SARA-GO on inert metal surface
Although the spontaneous reduction of GO induced by active metals is impressive as demonstrated in current work and others22,23,24, it is not yet applicable to the inert metals such as Ag, Pt and Au (Supplementary Fig. S16), not to mention the nonmetallic conductive substrates. The reduction of GO and the oxidation of metal substrates are associated with the electron harvest of GO and the electron loss of metal (Fig. 1a), which provides the opportunity to reduce GO onto arbitrary conductive surfaces via SARA-GO process in Fig. 1b. This concept is inspired by the substrate-enhanced electroless deposition (SEED) we developed previously26. As schematically shown in Fig. 1b, by simply supporting the inert metals or other conductive surfaces (Target) with an active metal substrate (Sub0), GO could be reduced and deposited on the Target surface via a process analogous to the galvanic displacement reaction26. The inert conductive substrate acts as a “cathode” for GO reduction and deposition of RGO from its suspension, while the active metal foil serves as an “anode” where Sub0 is oxidized into Subn+. Therefore, the SARA-GO process should allow the assembly of RGO on any conducting substrate as long as a proper base substrate is defined.
To demonstrate this concept, we supported the inert Au sheet (purity: 99.9%) with the Cu foil (Au/Cu) and exposed them to the aqueous GO suspension. As can be seen in Fig. 3b, the Au surface is covered with graphene network just like the porous structure on Cu foil (Fig. 2b), while the Au sheet without Cu support remains clear regardless of the reaction time (Fig. 3a). These results confirm the effective deposition of RGO network on inert metal surface via the SARA-GO.
TEM investigation reveals the transparent RGO sheet with clear electron diffraction spots (Fig. 3c and inset) characteristic of the highly crystalline graphene structure. XRD further confirms that the representative peak of GO (2θ ≈ 11°) has completely disappeared in the RGO samples, accompanied with a new broad peak centered at around 23° for loosely stacked graphenes (Fig. 3d). Accordingly, the C 1s XPS spectra of GO and RGO (Fig. 3e) reflect that most of the oxygenated functional groups of GO have been removed. The C/O ratio for the RGO on Au surface is 7.8, in consistent with that of RGO mentioned above (Fig. 2h). These characterizations demonstrate the deposited RGO network on Au surface has a feature of high-quality graphene similar to that on Cu, indicating the feasibility of SARA-GO.
Apart from the Au, the SARA-GO process also works well on such inert metals as Pt and Ag when their sheets were supported by Cu layers (Fig. 3f&g, and Supplementary Fig. S17). Similarly, RGO network can also be deposited on the Cu covered inert metals, such as Pt, Ag and Au (Supplementary Fig. S18).
To further demonstrate the effectiveness of SARA-GO process on the nanostructures of inert metals, we have put the Au, Ag, and Pt nanostructures with different sizes and shapes on Cu foil into the aqueous GO suspension (Supplementary Fig. S19). As expected, they behavior as the good substrates to reduce the GO and assemble 3D RGO network on them (Supplementary Fig. S20–S22), indicating the morphology-independent feature of the practicable SARA-GO. Fig. 3h shows the deposited RGO network on Ag nanoleaves.
SARA-GO on nonmetallic surface
More importantly, the SARA-GO process allows the RGO spontaneously deposited on any conductive surfaces such as semiconducting Si (Fig. 3i and Supplementary Fig. S23&24), ITO glass (Fig. 3j&k and Supplementary Fig. S25), carbon (Fig. S26) and graphene films (Fig. 3l and Supplementary Fig. S27&28), indicating the versatile SARA-GO method is universal for formation of graphene network on conductive surfaces for various applications. Specially, the RGO network formed on ITO surface can have no obvious influence on the transparency with a proper reaction time (Fig. 3j&k and Supplementary Fig. S25).
Fabrication of graphene microtubes, four-way pipe, multi-channel network and graphene micropatterns via SARA-GO process
The SARA-GO process allowing the spontaneous reduction of GO on various conductive surfaces offers a facile but efficient method for construction of unique graphene assemblies of practical importance. As exemplified in Fig. 4a&b, the reduction of GO along a Cu wire will lead to the formation of graphene microtube (μGT)27,28. The Cu wire will act as the support for aggregation of RGO network, and meters of μGTs with a diameter depending on the used Cu wire are collected after Cu etching in aqueous FeCl3/HCl solution (Fig. 4b, Supplementary Fig. S29–S31). Further, specifically defined configurations such as spiral tubes (Fig. S32), four-way pipe (Fig. 4c, Supplementary Fig. S33), and multi-channel network of graphenes (Fig. 4f, Supplementary Fig. S34) with tunable length and diameter in large scale can be done readily.
Fig. 4c displays the as-prepared four-way pipe, and the inserts in Fig. 4c are the SEM images for the four nozzles, indicating the characteristics of hollow interior as the schematic diagram in Fig. 4d. Similarly, Cu mesh (Fig. 4e), as well as the Fe mesh (Supplementary Fig. S34), will induce the woven fabric of μGTs (Fig. 4f–h, Supplementary Fig. S34).
The region-defined patterns of RGO network are also available through the powerful SARA-GO. As presented in Fig. 4i and Supplementary Fig. S35, by pressing a Cu grid (200 μm in side length) on Pt foil and exposing them to the GO suspension, we can achieve the RGO patterns on Pt foil after removing the Cu grid. The region-confined 3D graphene network remains well with freeze-drying (Fig. 4j). Depending on the Cu masks, a variety of specific patterns on nonconductive substrates can also be designed for various applications (Supplementary Fig. S36&37).
SARA-GO for construction of binder-free lithium-ion batteries (LIBs)
Apart from the construction of unique graphene configurations of practical importance mentioned above, the SARA-GO method enabling the self-organization of 3D graphene network on various conductive substrates will largely facilitates the fabrication of graphene electrodes, and thus benefits the device applications.
As one of the important energy storage devices, rechargeable LIBs have drawn worldwide interest2,3. However, graphite, the most commonly used commercial anode material, encounters serious disadvantages such as low theoretical specific capacity (372 mAh g−1) and limited rate capability. As a result, great efforts are being devoted to developing new electrode materials for high performance LIBs. Graphene is expected to be a good candidate as a high-power and high-energy electrode material due to its intrinsically superior electrical conductivity, excellent mechanical flexibility, remarkable thermal conductivity, high surface area29,30, and high chemical diffusivity of Li, ~10−7–10−6 (cm2 s−1)31,32. Herein, the SARA-GO method provides a straightforward route to assemble graphene network on the Cu foil in the form of 3D pore-interconnected structure, which can be directly used as anode electrode in LIBs without need of any ancillary materials such as binders and conductive additives required for the conventional LIB fabrication.
The cropped Cu foil (Fig. 5a) was first deposited with RGO network on one side via SARA-GO (Fig. 5b). After slightly washing with aqueous HCl to remove the Cu oxides, the freeze-dried sample (Fig. 5c) as anode was directly assembled in a coin battery (Fig. 5d).
As shown in Fig. 5e, the RGO/Cu electrode shows typical cyclic voltammogram (CV) curves (1 to 5 cycles) of the carbonaceous anode materials at a scan rate of 0.5 (mV s−1). The peak at around 0.8 V can be ascribed to the decomposition of the electrolyte on the surface of RGO, leading to the formation of the solid electrolyte interphase (SEI) layer33,34. The CV curves of the second to the fifth cycle almost overlap, implying an excellent cycling ability of the RGO/Cu electrode.
Fig. 5f shows the galvanostatic charge/discharge profiles of the RGO/Cu electrode between 0.01–3 V at a current density of 0.1 A g−1. The initial discharge and charge specific capacities are 2472 and 1605 mAh g−1, respectively. The irreversible capacity loss is generally attributed to the formation of SEI33,34. The RGO/Cu electrode becomes stable at the ninth cycle with a capacity of 1076 mAh g−1, which is about 2.9 times higher than the theoretical one of graphite (372 mAh g−1).
Fig. 5g shows the cycling performance and the corresponding coulombic efficiency at a current of 0.3 A g−1 after aging at 0.1 A g−1 for 10 cycles. The discharge capacity stabilizes at 725 mAh g−1 for 60 cycles, which is about 2 times higher than the theoretical capacity of graphite, superior to that of many other carbon materials (Table S3) including carbon nanosprings35, carbon nanocages36, carbon nanofibers (CNF)37, carbon nanotubes (CNT)38, CNF/CNT39, N-doped graphene40 and N,S-codoped porous graphene41, as well as metal oxides of CoMn2O4 microspheres42, and their composites such as MnO2/CNT43 and Fe3O4/RGO44. At the meanwhile, the coulombic efficiency of the battery retained at nearly 100% during the cycling, showing an excellent reversibility. Furthermore, the 3D RGO/Cu-based battery has also a great rate behavior as tested under variable rates from 0.1 A g−1 to 20 A g−1 (Fig. 5h). Even at 20 A g−1, the reversible capacity is still 231 mAh g−1, which is closed to the highly N-doped carbon materials with excellent performance34,45. Remarkably, after the high-rate measurements, the specific capacities of the RGO/Cu electrode almost recover to the initial values cycled at 100 mA g−1. A long-term cycling stability has also been carried out at a high current density of 2 A g−1. As shown in Fig. 5i, the anode material shows stable cycling behavior, and the reversible capacity of up to about 500 mAh g−1 is achieved for 300 cycles, which is still ca. 134% of the theoretical capacity of graphite. On the other hand, the electrochemical impedance spectra of the RGO/Cu electrode before and after cycling at 0.3 A g−1 for 100 cycles indicate the activated and improved reaction kinetics upon cycling, and the good contact between the RGO/Cu electrode and the current collector (Supplementary Fig. S38).
As we know, GO can be reduced by strong reduction reagents such as hydrazine8. However, GO as a strong oxidant is paid the little attention. In fact, GO has the capability to oxidize Fe2+ to Fe3+ in despite of the relatively high redox potential of +0.77 V (vs. standard hydrogen electrode, SHE) for (Fe2+/Fe3+)46. Example also includes the oxidation of iodic ions (I-) into neutral iodine (I2) (+0.54 V vs. SHE for I-/I2) by GO suspension47. Therefore, it is reasonable to observe that GO was reduced by active metals such as Al, Fe, Cu20,21,22.
By curve fitting analysis of the XPS results (Fig. 2h), we can find that the hydroxyl, epoxy and carbonyl groups decrease drastically, while the carboxylic acid groups remain relatively stable. Considering that the epoxy and hydroxyl groups are the main active oxide groups of GO for the typical reduction process48,49, and epoxy group can also convert to hydroxyl group in aqueous acidic solution, we proposed the reaction mechanism via an electron transfer process of GO with hydroxyl groups as exemplified model in Figure 6. The hydrions are easy to form the complex with the oxygen-related groups in GO, which could induce a dehydration process and allow the positively charged GO system to receive the electrons from the active metals20,21,22. Accordingly, metal ions produced by electron-lost metals could combine the hydroxide (OH-) ions to balance hydrogen (H+). These metastable metal hydroxides then further performed a dehydration process to form metal oxides as we have experimentally observed the formation of such metal oxides as Cu2O (Fig. 2c), ZnO (Supplementary Fig. S7–S9), and Fe3O4 (Supplementary Fig. S10&S11) during SARA-GO.
Besides, we also performed the first principle calculation to compare the electron properties of metal surfaces on the basis of the work functions. The work function is the minimum energy required to release electrons from the reactive surface, which should give some clues why different metals have the quite different performances for reducing GO. In our calculation the generalized gradient approximation with the Perdew-Burke-Ernzerhof functional50 was used, the basis set contains plane waves up to an energy cutoff of 380 eV and the structure is relaxed until the force on each atom is less than 0.03 eV/Å in the Vienna ab initio software package (VASP)51,52. We performed the calculation on several metal slabs of Zn (0001), Al (111), Cu(111), Pt (111) and Au (111) surfaces with seven layers as examples using Periodic Boundary Conditions (PBC) (Supplementary Fig. S39). The work functions of these metals are 4.02 eV, 4.13 eV, 4.73 eV, 5.85 eV and 5.01 eV, respectively. These results indicate the capacity to lose electrons of the different metals. Obviously, the active metals like Zn, Al and Cu are much more active than Pt and Au for GO reduction in consistent with the experimental observation. Although the difficulty to directly reduce GO on inert metals of Pt and Au, the SARA-GO (Figure 1b) developed in this study provide the solution.
It is also notable that the SARA-GO method will generate the graphene assemblies with easy in-situ functionalization. As can be seen in Fig. 2c and Supplementary Fig. S7–S11, the functional components such as Cu2O, ZnO and Fe3O4, if not washed away by aqueous HCl, could be spontaneously attached on the graphene sheets during the SARA-GO process. Therefore, new functions could be expected due to these incorporated components. As an example shown in Supplementary Fig. S40, the as-prepared ZnO-containing graphene film presents the fast photocurrent response with good repeatability upon exposure to a daylight lamp (100 W).
In conclusion, a general method of substrate-assisted reduction and assembly of graphene oxide has been developed for spontaneous deposition of 3D graphene network on arbitrary conductive substrates without any additional reducing agent. The SARA-GO process offers a facile, but efficient approach for constructing a variety of unique graphene assemblies of practical importance. For examples, graphene microtubes, four-way pipes, spiral tubes, multi-channel networks, and micropatterns have been conveniently manufactured by using Cu or Fe wires and meshes as templates. The SARA-GO enabling the self-organization of 3D graphene network on various conductive substrates largely facilitates the fabrication of graphene electrodes. The binder-free LIBs using spontaneously deposited 3D graphene network on Cu foil as anode materials have been demonstrated, which exhibit high capacity, cycling stability and rate performance superior to many other carbon-based materials and metal oxide composites. The versatile SARD-GO method with significantly improved processability of graphenes will benefit a variety of applications beyond those specifically demonstrated in this preliminary study.
Synthesis of Graphene Oxide (GO)
Spontaneous deposition of 3D RGO network on Al, Zn, Fe, Co, Cu foils
Zn, Fe, Cu, Co and Al foils were exposure to 1 mg/mL GO solution for a certain time (e.g, 1–12 h) at ambient condition (Supplementary Fig. S1), and RGO was spontaneously assembled on the metal foils. The metal oxides on RGO were carefully washed away with over 2 M HCl aqueous solution, followed with deionized water. The lyophilization was carried out to get the 3D RGO network. All the metal foils were purchased from Alfa Aesar with a purity of >99.9%. To accelerate the reaction and prevent the passivation effect due to the coating of the produced nonconductive metal oxides, a mild temperature of 60°C is also applied on demand.
Spontaneous deposition of RGO network on the surfaces of inert metals of Au, Ag, Pt and semiconducting Si (N-type)
We first deposited a layer of Cu on one sides of Au, Ag, Pt foils, and Si wafer by vacuum sputtering, which were then exposure to 1 mg/mL GO solution for several hours. Apart from the Cu sides, RGO network was also spontaneously deposited on the Cu-free sides of Au, Ag, Pt foils and Si wafer. The alternative method for depositing RGO network on the surface of inert metals and Si is covering them by Cu foil partly, followed by directly immersing them in 1 mg/mL GO solution for a certain time.
Spontaneous deposition of RGO network on the surfaces of Au, Ag, Pt nanostructures
The preparation of Au, Ag, Pt nanostructures with different size shape on Cu foils were carried out as described in our previous publications26,55. Briefly, on sides of the Cu foils were contacted with aqueous 0.01 M HAuCl4, 0.02 M AgNO3, and 0.01 M H2PtCl6 solutions for 1 min, respectively, for the deposition of the nanostructured Au, Ag or Pt with different sizes and shapes on Cu foils as shown in Supplementary Fig. S19–S22. Subsequently, Cu foils were washed with HCl solution and deionized water several times carefully before further experiments. For the formation of RGO network on the nanostructures, the Cu foils with nanostructured Au, Ag, Pt were exposed to 1 mg/mL GO solution for 8 h, which were then washed by HCl solution, deionized water several times, characterized after lyophilization.
Spontaneous deposition of RGO network on indium-tin oxide (ITO) surface
ITO glass was half covered with Cu layer by vacuum sputtering, which was then exposed to 1 mg/mL GO solution for 12 h at room temperature (Supplementary Fig. S25). After that, the ITO was washed with deionized water slightly before lyophilization. Finally, the remained Cu was removed from the ITO glass carefully, and the region of RGO on ITO was still transparent due to the short reaction time.
Spontaneous deposition of RGO network on carbon film
We used the carbon film coated Cu-based TEM grid as an example to demonstrate the effective deposition of RGO on carbon film. A carbon-coated Cu TEM grid was immersed in the 1 mg/mL GO solution for 10 h, which was then washed with aqueous HCl and deionized water, followed by lyophilization before characterization.
Spontaneous deposition of RGO network on graphene film
A two step deposition of RGO was devised for this purpose (Supplementary Fig. S27&28). The graphene film supported by Cu was first prepared by exposure of Cu foil to the 0.5 mg/mL GO solution for 10 h, which was washed with HCl solution and deionized water several times carefully, followed by naturally drying to form a graphene film on Cu. This Cu supported graphene film was then immersed in 1 mg/mL GO solution for 10 h for the further deposition of RGO on the preformed graphene film. The RGO on graphene film could be directly peeled off from the Cu foil or separated from the Cu foil by 1 M FeCl3 treatment for 0.5 h. Finally, the 3D RGO assembled on graphene film was collected after washing with deionized water and lyophilization.
Preparation of graphene microtubes (μGTs)
The formation of μGTs is schematically shown in Supplementary Fig. S29. A Cu wire was immersing into 1 mg/mL GO solution for 10 h to allow the assembly of RGO along the Cu wire. Then the wet graphene enwrapped Cu wire was taken out from the solution, and densely packed graphene layer surrounding Cu wire was formed after drying naturally. Subsequently, μGTs with a diameter depending on the supporting Cu wire were collected after etching Cu wire in an aqueous 2.5 M FeCl3 solution containing 0.5 M HCl and thoroughly washing with distilled water. The Cu wire can not only reduce the GO to RGO, but also act as the support during the drying process. The μGTs with diameters of ca. 100 (Supplementary Fig. S30) and 40 μm (Fig. 4b) were produced by choosing the Cu wires with corresponding diameters as supporting core.
The preparation of Y-shaped μGT with spiral structure, four-way pipe and multi-channel network of graphenes
Based on the formation of μGTs mentioned above, different configurations of Cu wires (Supplementary Fig. S32&33), and Cu or Fe meshes (Supplementary Fig. S34) were exposed to the 1 mg/mL GO solution to allow the formation of Y-shaped μGT with spiral structure, four-way pipe and multi-channel network of graphenes.
The preparation of RGO pattern on Pt foil
As presented in Supplementary Fig. S35, by pressing a Cu grid (200 μm in side length) on Pt foil and then exposing them to the 1 mg/mL GO suspension for 12 h, we can achieve the RGO patterns on Pt foil after removing the Cu grid. The region-confined 3D graphene network remains well with freeze-drying (Fig. 4i& j).
The preparation of region-defined pattern of RGO on SiO2
Cu islands on SiO2 were first obtained by vacuum sputtering with a Cu grid (400 μm in side length) as mask (Supplementary Fig. S36), which was then immersed in 1 mg/mL GO for 12 h to assembly the RGO on the Cu deposited regions. 3D porous RGO patterns on SiO2 ware produced by freeze-drying procedure. The patterns of RGO film were obtained with naturally drying.
Fabrication of 3D RGO/Cu electrode
Firstly, the trimmed Cu foil with circular shape was immersed in 1 mg/mL GO solution for 10 h for the spontaneous assembly of RGO on Cu foil. After slightly washing with aqueous HCl, the sample was freeze-dried to keep 3D pore-interconnected graphene structure on Cu, which was directly used as working electrode in LIBs without need of any ancillary materials such as binders and conductive additives required for the conventional LIB fabrication.
The as-obtained sample was directly used as working electrode without any ancillary materials for cell assembly. A lithium foil was used as the counter electrode and a solution of 1 M LiPF6 in ethylene carbonate (EC)/dimethyl carbonate (DMC)/diethyl carbonate (DEC) (1:1:1 in volume) was used as electrolyte. The assembly of the cells was performed in an argon-filled glove box. The cells were then aged for 8 h before measurement. The cycling tests were charged and discharged using an LAND CT2001A test station. The impendence spectra were obtained by applying a sine wave with amplitude of 5 mV over the frequency range from 100 kHz to 0.01 Hz. The weights of graphenes on Cu foil were determined by measuring more than 10 parallel samples under the same condition. A mean value was used in this study.
The morphology of the samples was determined by FET TECNAI F30 high resolution transmission electron microscopy (HR-TEM) at an acceleration voltage of 200 kV. Field-emission scanning electron microscope (FE-SEM) images and EDS data of the samples were taken on JSM-7001F SEM unit. X-ray diffraction (XRD) patterns were obtained by using a Netherlands 1,710 diffractometer with a Cu Kα irradiation source (λ = 1.54 Å), and a self-calibration process was performed with a SiO2 internal standard sample prior to target measurement. X-ray Photograph electron spectroscopy (XPS) data were obtained with an ESCALab220i-XL electron spectrometer from VG Scientific using 300 W AlKα radiation. The base pressure was about 3 × 10−9 mbar. The binding energies were referenced to the C 1 s line at 284.8 eV from adventitious carbon.
This work is sponsored by National Basic Research Program of China (2011CB013000), NSFC (No. 21004006, 21174019, 51161120361), Fok Ying Tong Education Foundation (No. 131043), the 111 Project B07012, and research foundation for the doctoral program of higher education of China (20101101120036).
About this article
Scientific Reports (2015)