At an initial pH of 2, while abiotic oxidation of aqueous Fe2+ was enhanced by a flux of H2O2 at micromolar concentrations, bio-oxidation of aqueous Fe2+ could be impeded due to oxidative stress/damage in Acidithiobacillus ferrooxidans caused by Fenton reaction-derived hydroxyl radical, particularly when the molar ratio of Fe2+ to H2O2 was low. When pyrite cubes were intermittently exposed to fluxes of micromolar H2O2, the reduced Fe2+-Fe3+ conversion rate in the solution (due to reduced microbial activity) weakened the Fe3+-catalyzed oxidation of cubic pyrite and added to relative importance of H2O2-driven oxidation in the corrosion of mineral surfaces for the treatments with high H2O2 doses. This had effects on reducing the build-up of a passivating coating layer on the mineral surfaces. Cell attachment to the mineral surfaces was only observed at the later stage of the experiment after the solutions became less favorable for the growth of planktonic bacteria.
Pyrite (FeS2) commonly occurs in the Earth's surface environments1. Great efforts have been made for the past decades to understand the mechanisms and kinetics of pyrite oxidation2,3,4,5,6,7,8,9,10,11,12,13,14, which is the driving force leading to the widespread ecological degradation caused by the formation of acid mine drainage (AMD) and acid sulfate soils (ASS)15,16,17. The established model to describe pyrite oxidation consists of the following overall chemical equations: Initially, oxidation of pyrite by molecular oxygen results in generation of sulfuric acid and ferrous sulfate (Equation 1). This process only completes the conversion of pyrite-S from S− to S6+. The aqueous Fe2+ of pyrite origin may further react with molecular oxygen to form Fe3+ (Equation 2), which subsequently acts as a more effective oxidant for pyrite oxidation (Equation 3) if the pH is sufficiently low to prevent Fe3+ hydrolysis. Abiotic oxidation of Fe2+ is very slow under acidic conditions but the process can be catalyzed by iron-oxidizing bacteria3.
Hydrogen peroxide (H2O2) is an aggressive oxidant and it is commonly present in rainwater18,19,20, especially during thunderstorms21. H2O2 can also be generated through radiolysis of water in geological formations or industrial wastes containing radioactive materials such as uranium ores, spent nuclear fuel etc22,23. Therefore, contacts between H2O2 and pyrite grain surfaces or/and aqueous Fe2+ are likely to occur in natural environments. Moreover, H2O2 has potential applications in hydrometallurgy for the extraction of base metals from sulfide ores24,25,26 and in desulfurization of coal27. There is therefore a possibility for the leaking/residual H2O2 to be in contact with pyrite in the non-target areas surrounding the heap leach piles. Furthermore, it was also suggested that H2O2 could be spontaneously generated when pyrite reacted with H2O in the absence of oxygen28 or during the oxidation of pyrite with molecular oxygen29,30. From a planetary perspective, the presence of atmospheric H2O2 in other planets such as Mars may represent an important factor that has been affecting the acid sulfate-producing processes in Martian environments31.
It is well established that powerful oxidative intermediates (free radicals) are generated as a result of the chain reactions initiated by contact between H2O2 and Fe2+ i.e. so-called Fenton reactions32,33. Therefore, H2O2 may have a dual role to play: (a) as a strong oxidant for abiotic oxidation of pyrite and aqueous Fe2+, and (b) as a toxicant (through the generation of free radicals) to cause oxidative stress in iron/sulfide-oxidizing bacteria and consequently affect their ability to catalyze Fe2+ oxidation.
Surface oxidation of pyrite by millimolar H2O2 (2–200 mmol L−1) in molecular oxygen-free conditions has been examined by Lefticariu et al34,35 in abiotic systems. The role of H2O2 spontaneously generated from oxidation of powdered pyrite by molecular oxygen was investigated by Schoonen et al30. In AMD and ASS scenarios, it is hardly possible that iron/sulfide-oxidizing bacteria are not involved in the process of pyrite weathering. Therefore, while the abiotic oxidation research provides a fundamental basis for understanding the role of H2O2 in pyrite oxidation, it has some limitations in explaining complex systems involving microbially mediated processes.
We previously examined the oxidation of pyrite cubes that were exposed to an Acidithiobacillus ferrooxidans strain (an iron- and sulfide-oxidizing bacterial species commonly present in natural environments), ambient dissolved oxygen and intermittent fluxes of H2O2 at micromolar levels under circumneutral (initial pH = 6.8). It was found that Equation 3 did not operate observably due to low Fe3+ solubility. The more aggressive nature of H2O2 as an oxidant (as compared to molecular oxygen) caused marked surface corrosion of the pyrite cubes. It was observed that cell colonization on the mineral surfaces was inhibited at high H2O2 levels (initial concentration of H2O2 >100 μmol L−1). However, at a H2O2 concentration of 50 μmol L−1, cell attachment was enhanced, as compared to the no-added H2O2 treatment36.
In this article, we report on the experimental results for the acidic scenario (initial pH = 2). This represents a step forward in simulating pyrite weathering involving H2O2 in field conditions e.g. pyrite grains in tailings dams, inundated mine waste impoundments and constructed wetlands that receive cyclic flux of micromolar H2O2 caused by intermittent rainfall events. Pyrite cubes instead of powdered pyrite were used in this study in order to minimize the possible interference from the spontaneously generated H2O2, as reported by Schoonen et al30, who found that it was a challenge to achieve quantitative measurements of the spontaneously generated H2O2. To obtain further insights into the response of planktonic Acidithiobacillus ferrooxidans to toxicity of Fenton reaction-derived free radicals and the resulting impacts on the oxidation rate of aqueous Fe2+, a separate experiment was also conducted to observe the evolution of cell population, aqueous Fe2+ and other relevant chemical parameters following a single H2O2 flux. The objective of this study was to examine the effects of micromolar H2O2 flux on the microbially involved oxidation of aqueous Fe2+ and cubic pyrite by comparison between the control (no added H2O2) and the treatments (with varying dosage levels of H2O2) under the same preset experimental conditions.
Aqueous Fe2+ oxidation experiments
For the abiotic experiments, the concentration of aqueous Fe2+ remained little change when exposed to molecular oxygen only (i.e. the control) for both the low and high Fe2+ scenarios. The injection of H2O2 (the treatments) caused a sudden decrease in Fe2+ within the first 5 min of the experiment. The aqueous Fe2+ then maintained at a stable level throughout the entire duration of the experiment after this initial drop. There was a tendency that the magnitude of Fe2+ drop increased with increasing dosage level of H2O2 (Fig. 1a and c).
In contrast with the abiotic experiment, the concentration of aqueous Fe2+ in the control (no added H2O2) rapidly decreased in the presence of Acidithiobacillus ferrooxidans for both the low and high Fe2+ scenarios (Fig. 1b and d). For the low Fe2+ scenario, the initial rapid drop in Fe2+ was observed for all the treatments. The aqueous Fe2+ evolution patterns in T3 and T4 were similar to those in T3 and T4 of the abiotic experiment, respectively. However, the aqueous Fe2+ in T1 and T2 continued to decrease after the initial drop with T1 showing a generally rapider rate of reduction, relative to T2 (Fig. 1b). When the initial concentration of Fe2+ in the solutions was increased to 558 mg L−1, there was no significant difference in the aqueous Fe2+ evolution pattern among the control, T1 and T2. T3 also had a very similar evolution pattern aqueous Fe2+ to the control except that it dropped much quickly during the first 5 min and took a slightly longer time to disappeared in the solution. T4 was the only treatment showing marked delay in aqueous Fe2+ depletion (Fig. 1d).
The curves of viable cell population during the incubation experiments for both the low and high Fe2+ scenarios are provided in Supplementary Fig. S1a and b. In general, the cell density decreased with increasing dosage level of H2O2. Fig. S2 is a selected SEM image showing the cellular damage in the affected microbes.
In the low Fe2+ scenario, there was a high degree of similarity in the curves of dissolved oxygen (DO) among the control, T1, T2 and T3. However, T4 showed much higher DO in the earlier stage of the incubation experiment, as compared to the others. This gap was closed at the 40th h of the experiment (Supplementary Fig. S3). The curves of DO were highly consistent among the control and all the treatments for the high Fe2+ scenario (data not shown).
Toxic response of Acidithiobacillus ferrooxidans to H2O2 under various conditions
Figure 2 shows that when the bacteria were exposed to 50 μmol L−1 H2O2 for 30 min (BH), the cell population in the solution significantly reduced, as compared to the control (BI, without added H2O2) and in the treatment (BHA) with a reactive oxygen species scavenger (ascorbic acid), which has the capacity to rapidly decompose H2O2. When comparing H2O2 only systems (i.e. BH and BIH) with H2O2-Fe2+ reaction systems (i.e. BIH and BIHA), it can be seen that the cell population was denser in a H2O2 only system than in its corresponding H2O2-Fe2+ system (Fig. 2), indicating that more severe oxidative stress in the cells in the latter than in the former.
Aqueous phase of the pyrite oxidation experiment
The viable cell count on the 6th day after inoculation of Acidithiobacillus ferrooxidans was lower than the number of cells added at the time when the inoculum was introduced into the solution for the control and all the treatments. The total number of viable planktonic cells was in the following decreasing order: CP > TP1 = TP2 > TP3 > TP4 on this occasion. Therefore, approximately 35% and 91% of the added bacteria disappeared from the solution for the control and the highest H2O2 dosage treatment (TP4), respectively. After this initial drop in planktonic cell population, the number of planktonic cells in various treatments fluctuated with different evolutionary patterns during the period of the incubation experiment. In general, the cell count was higher in CP and TP1 than in the treatments with higher H2O2 doses (TP2, TP3 and TP4). TP4 had the lowest cell count at any sampling occasion during the period of the experiment. The cell population in the control and the treatments consistently dropped to the lowest level on the 74th day and remained low until the end of the incubation experiment (Fig. 3a)
On the 3rd day of the experiment, the concentration of aqueous Fe2+ was in the following decreasing order: CP > TP4 > TP1 > TP2 > TP3. The Fe2+ concentration in TP1, TP2 and TP3 maintained at a level <5 mg L−1 during the entire period of the experiment. After the sudden drop from 9.6 mg L−1 on the 3rd day to 4.5 mg L−1 on the 6th day, the Fe2+ concentration in CP also maintained at a level <5 mg L−1 for the remaining period of the experiment. In contrast, TP4 exhibited a different Fe2+ variation pattern during the period of the experiment; the concentration of Fe2+ sharply increased from 8.3 mg L−1 on the 3rd day to 26.6 mg L−1 and 26.7 mg L−1 on the 12th and 15th day, respectively and then rapidly decreased to 4.6 mg L−1 on the 22nd day; after this, the Fe2+ concentration maintained at a level <6 mg L−1, with fluctuation, until the end of the experiment (Fig. 3b).
The aqueous Fe3+ had a similar temporal variation pattern for the control and all the treatments, showing a general trend to increase the concentration over time. However, Fe3+ concentration in TP4 was always much lower, relative to the control and other treatments on any sampling occasions, and no Fe3+ was detected during the initial 19 days of the experiment. In the early part of the experiment, the aqueous Fe3+ concentration tended to be markedly higher in CP and TP1 than in TP2 and TP3. However, this gap was gradually reduced in the latter part of the experiment (Fig. 3c).
There was a clear tendency that the aqueous sulfur concentration increased with increasing incubation time. This was accompanied by an opposite trend for the solution pH. Closer examination found that on most sampling occasions, TP4 had a higher pH and lower S concentration, as compared to the control and other treatments (Fig. 3d and e).
Scanning electron microscope (SEM) observations and X-ray photoelectron spectroscopy (XPS) analysis of the pyrite cube surfaces
No attached cells were observed on the surface of pyrite cubes that were taken on the 28th day of the experiment for the control and various treatments. Pitting corrosion was clearly observable for CP and TP1 but not for other treatments (Fig. 4a, d, g, j and m). The micro-morphological features of the reacted pyrite surfaces were markedly different at the end of the experiment, as compared with those observed on the 28th day. Except for TP4, all the treatments and the control exhibited marked surface cracking and partially flaking corrosion (Fig. 4b, e, h, k and n). Attached cells were clearly observed to occur on the flakes that were still tightly or loosely attached to the pyrite substrate for TP1, TP2 and TP3 (Fig. 4f, i and l). Scattered cell-shaped objects were also observed on the mineral surfaces for CP and TA4 (Fig. 4c and o), but they were not as clear as those observed for TP1, TP2 and TP3.
The XPS results showed that within a ~3–5 nm thick surface layer of the reacted mineral surface, oxygen accounted for a large proportion (52–79% on a molar basis) of the sum of iron, sulfur and oxygen. There was a trend that the oxygen percentage decreased with increasing dosage level of H2O2 in the solution (Fig. 5a). The Fe/S ratio of the reacted surfaces ranged from 0.183 to 0.257, which was much lower than the value (0.5) of the theoretical Fe/S ratio for pyrite. After treatment of the reacted pyrite cubes with the boiling HCl to remove the oxidized materials, the proportion of oxygen in the sum of iron, sulfur and oxygen markedly decreased for the outermost layer (top ~3–5 nm thick) of the corroded surface (Fig. 5b). The Fe/S ratio of the corroded surface ranged from 0.173 to 0.239, which was not markedly different from those prior to HCl treatment.
There was a trend that XPS peaks of Fe 2p3/2 and S 2p shifted to lower binding energies with increasing dosage level of H2O2, indicating that higher level of H2O2 resulted in increased proportion of lower-valence species of Fe and S on the reacted pyrite surfaces (Table 1). CP and TP1 exhibited the dominance of Fe3+ (in Fe-OH bond) in the surface Fe species. There was a trend that the percentage of Fe3+ decreased with increasing H2O2 level. Fe2+ (in Fe-S bond) was not detected for CP and TP1but dominated the surface Fe species for TP2, TP3 and TP4. In agreement with surface Fe speciation, S− dominated the surface S species for TP2, TP3 and TP4 while CP and TP1 only contained small amount of surface S−. The percentage of surface sulfate-S was greater in CP and TP1 than in TP2, TP3 and TP4. Small amount of thiosulfate-S was also detected for CP and TP1.
After HCl treatment, the chemical states of Fe and S were highly consistent among the control and the treatments, showing the predominant presence of surface Fe2+ and S− (in Fe-S bond). Polysulfides with varying valences (including the end product elemental S) were also present at significant amounts. Trace amounts of monosulfide (S2−) were also detected. Fe2+/Fe3+ (in Fe-O/Fe-S bonds) accounted for about 34% (±3%) (Table 2).
In the presence of dissolved oxygen alone (the control), no clear sign of Fe2+ oxidation was observed. This is consistent with the established theory that oxidation of aqueous Fe2+ by molecular oxygen under acidic pH was kinetically slow3. Consequently, the sudden drop in aqueous Fe2+ concentration for the treatments with the added H2O2 can be interpreted as the result of H2O2-driven oxidation of aqueous Fe2+. The “standstill” of aqueous Fe2+ level after this initial rapid oxidation indicates that the H2O2 was already depleted within a few minutes. The rapid consumption of H2O2 through Fe2+ oxidation can be expressed by the following chemical equations:
The decomposition of 1 mole of H2O2 leads to simultaneous oxidation of 1 mole of Fe2+ and generation of 1 mole of (Equation 4), which may further oxidize another mole of Fe2+ (Equation 5). If spontaneous decomposition of H2O2 takes place, elevated concentration of DO is expected according to the following equation: The trend lines showing the evolution of DO were very simular among the control and T1–T3 for the low Fe2+ scenario, indicating that spontaneous decomposition of H2O2, if any, was not significant for these treatments (Supplementary Fig. S3). The higher DO in T4 suggests that spontaneous decomposition of H2O2 did occur for this high-dose treatment. This is supported by the fact that the ratio of the converted Fe2+ to H2O2 was less than 1, indicating that over half of the added H2O2 was not consumed through Fe2+ oxidation.
By comparison with the abiotic oxidation results, it is evident that microbes played a crucial role in further oxidation of aqueous Fe2+ following the initial H2O2-driven oxidation in the corresponding biotic systems. However, the ability of microbes to catalyze the oxidation of aqueous Fe2+ was markedly affected by the initial concentration of aqueous Fe2+. When the initial concentration of aqueous Fe2+ was 55.8 mg L−1, the microbially mediated Fe2+ oxidation was impeded for all the treatments, as compared to the control. The oxidation rate of aqueous Fe2+ tended to decrease with increasing dose of H2O2. This was consistent with the observed decrease in cell population and cellular damage in the affected microbes (Supplementary Fig. S1a and Fig. S2) in response to the toxicity of hydroxyl radical that was generated through Fenton reaction (Equation 4). As shown in Fig. 2, H2O2 at an initial concentration of 50 μmol L−1 could cause marked oxidative stress in the cells. However, the presence of hydroxyl radical did increase the degree of oxidative stress in the cells.
In comparison with the low initial aqueous Fe2+ scenario (55.8 mg L−1), the microbial oxidation of aqueous Fe2+ was not retarded for the treatments except for T4 (H2O2 at 1000 μmol L−1) when the initial concentration of aqueous Fe2+ was increased to 558 mg L−1. The reduced microbial toxicity level due to the presence of higher initial concentration of aqueous Fe2+ can be attributed to the effect of excessive Fe2+ on scavenging , as shown in Equation 5.
Rapid disappearance of most added Acidithiobacillus ferrooxidans from the nutrient solution containing powdered pyrite was observed and attributed to the colonization of the bacteria on the pyrite mineral surfaces37,38. However, the lack of evidence showing the presence of attached cells and cell-shaped corrosion pits on the surfaces of pyrite cubes taken on the 28th day of the experiment suggests that this was not the case in this study. The general trend that the viable planktonic cell population decreased with increasing H2O2 dosage level suggests that the H2O2-derived resulted in the growth inhibition or even killing of some Acidithiobacillus ferrooxidans following inoculation. Ferrous ion was present in all the solutions at least after the 3rd day of the experiment. Consequently, free radical generation was possible.
However, it cannot be excluded that insufficient supply of Fe2+ to feed all the bacteria also contributed to the decrease in the viable planktonic cell population during the initial stage of the experiment39. This explains the initial drop in planktonic cell count for the control, which contained no added H2O2.
The marked recovery of the bacterial population after the initial drop for CP and TP1 can be attributed to (a) the adaptation of the bacteria to the H2O2-induced oxidative stress, (b) the increased supply of Fe2+ released from the mineral surfaces, and (c) possibly, the reduced concentration of free radicals as a result of the increased release rate of Fe2+, which alleviated the oxidative stress in Acidithiobacillus ferrooxidans, as discussed above.
The decreasing trend in cell density at the later stage of the experiment for CP and TP1 was likely to be caused by the reduced rate of Fe2+ release from the mineral surface during this period (the reasons for this have been discussed previously), as evidenced by the low concentration of aqueous Fe2+ and negative to very slow increase in aqueous Fe3+ during the period from the 28th day to the end of the experiment. This made the solutions become less and less favourable for the growth of the planktonic bacteria. Consequently, the bacteria had to seek alternative “food” sources by landing on the mineral surfaces and feeding on the sulfur-rich substrates. This is in contrast with the scenario at the earlier stage of the experiment (excluding the initial 6 days) when sufficient amount of Fe2+ was constantly released into the solution. The results obtained here indicates that the Acidithiobacillus ferrooxidans preferentially fed on free Fe2+ and possibly thiosulfate (S2O32−) in the solution rather than the structurally bound Fe2+ and reduced S species.
The absence of Fe3+ in TP4 until the 19th day of the experiment indicates that Fe2+ oxidation was negligible during this period. This resulted in the accumulation of Fe2+ in the solution. Clearly, the weak microbial activity resulting from the high dosage level of H2O2 was responsible for the inhibition of Fe2+ oxidation while the H2O2 itself as an oxidant had limited effect on the abiotic oxidation of the aqueous Fe2+ under the set experimental conditions. The aqueous Fe3+ concentration reflected the combined effect of the Fe3+ production from Fe2+ oxidation and the Fe3+ immobilization due to precipitation of iron compounds (precipitates were observed during the experiment but they were not produced in sufficient quantity to allow chemical and mineralogical analysis). Therefore, the steady increase in aqueous Fe3+ in CP and TP1 until the 28th day of the experiment indicates a higher rate of the Fe2+-Fe3+ conversion, relative to the rate of Fe3+ immobilization during this period. This more or less corresponded with a period when the bacterial population rapidly increased, reflecting an interdependency relationship between the Fe2+-Fe3+ conversion rate and the bacterial density. The subsequent plateau and decline phase of aqueous Fe3+ evolution was likely to represent a period of reduction in Fe3+ production as a result of reduced rate of Fe2+ release. This can be supported by the fact that the bacterial population tended to decrease during this period. The high similarity of Fe3+ evolutionary pattern between CP and TP1 suggests that a H2O2 level of 50 μmol L−1 was unlikely to cause a marked reduction in microbial oxidation of aqueous Fe2+ under the set experimental conditions. However, the increased dosage level of H2O2 tended to result in lower Fe3+ concentration in the solution. It is interesting to note that the Fe2+ concentration remained low during the entire period of the experiment for the H2O2 treatments except for the earlier stage of TP4. This indicates that the Fe2+-Fe3+ conversion rate more or less kept pace with the Fe2+ production rate. Therefore, the reduced rate of Fe2+ release from the mineral surface was a more upstream cause responsible for the lower solution Fe3+ concentration in these treatments.
The molar ratio of Fe to S in the solution ranged from 0.15 to 0.22, which were much smaller than the theoretical value of 0.5 assuming that equal amount of Fe and S was liberated from the pyrite cube surfaces during the experiment. In fact, it was likely that more Fe than S entered into the solution during the experiment, as evidenced by the presence of the Fe-deficient reacted pyrite surfaces (Fig. 5a). Therefore, much more Fe than S was removed from the solution through iron compound precipitation. Schwertmannite (Fe8O8(OH)6SO4) and jarosite (KFe3(OH)6(SO4)2) have a Fe/S molar ratio of 8 and 1.5, respectively. Therefore, the formation of basic sulfate minerals such as schwertmannite and jarosite explains the imbalance between Fe and S in the solution. This is consistent with the observed generation of H+ (as indicated by pH drop) as a result of Fe3+ hydrolysis leading to the formation of these minerals:
The Fe-deficient nature of the corroded surfaces (after HCl treatment to remove the coatings) indicates that the pyrite-Fe was preferentially liberated from the mineral surface, as compared to the pyrite-S. This can be explained by the relative easiness of the pyrite-Fe liberation reaction, as shown in the following chemical equations:
The completion of the above chemical reactions requires only one electron transfer from pyrite-Fe2+ to an electron acceptor (oxidant) in the solution, leaving structurally bound polysulfides (S2−) on the mineral surfaces. In contrast, the liberation of pyrite-S22− requires multiple steps of electron transfer from the pyrite surface to electron acceptors. The minimum number of electrons needed to be transferred to the external oxidants in order to liberate two pyrite-S atoms is 6 according to the equation below: Consequently, the oxidation of pyrite-S22− did not keep pace with the oxidation of pyrite-Fe2+, leaving sulfur species of intermediate oxidation states remained structurally connected with the pyrite substrate. The presence of a surfur-rich surface layer in oxidized pyrite crystals was also observed by others40,41.
The XPS results indicate the presence of oxidation products containing Fe3+ and SO42− within the ~3–5 nm thick outermost layer of the reacted pyrite surface. This suggests the formation of coating materials such as ferric (oxy)hydroxysulfates and (oxy)hydroxides. Xia et al42 observed the presence of jarosite in the microbially oxidized pyrite surfaces at acidic pH and suggested that the formation of surface-jarosite was the major cause responsible for the passivation of the sulfide mineral surfaces. The tendency that the proportion of surface-Fe3+ and -SO42− decreased with increasing dosage level of H2O2 appears to suggest that the presence of H2O2 affected the build-up of the ferric (oxy)hydroxysulfate-containing coating layer on the mineral surfaces although the exact mechanisms are not clear. Possibly, the differential composition of oxidants in the different H2O2-treated systems was an upstream factor that needs to be considered for the interpretation of the observed phenomena. From CP to TP4, the relative importance of H2O2-driven surface oxidation was likely to increase as a result of the increase in the H2O2 concentration and the simultaneous decrease in Fe3+ concentration. The weakened role of Fe3+ as a driving oxidant for mineral surface oxidation might reduce the frequency of Fe3+-SO42− contact at the solution-mineral interfaces, and consequently disfavour the formation of ferric (oxy)hydroxysulfate coatings, as described by the following H2O2-driven oxidation reaction: This is in contrast with the Fe3+-driven oxidation reaction, as shown in the following equation describing the formation of jarosite: Since no surface-S− was detected by XPS for CP and TP1, it is reasonable to believe that the thickness of the coating layer on the pyrite cube surfaces was >3–5 nm when the mineral crystals were exposed to H2O2 at a dosage level below 50 μmol L−1. The coating layer became thinner with increasing dosage level of H2O2, resulting in the occurrence of bulk pyrite-S (S−) within the ~3–5 nm thick outermost layer of the original reacted pyrite surfaces, which was consistent with the XPS results for the treatments with high H2O2 doses.
The research findings obtained from this study shed some light on the possible complication of the biogeochemical processes associated with the weathering of pyrite and other sulfide minerals due to the presence of H2O2 in the concentration range that may be encountered in field conditions. Our recent work43 also suggests that the Fe2+-H2O2 combinations that are likely to be encountered in natural waters resulted in significant degradation of agricultural herbicides. There is, therefore, a strong rationale for conducting additional laboratory-based investigations to obtain further insights into the exact chemical mechanisms and kinetics, and the subsequent field-scale study, which can be used to better evaluate the environmental risk of the toxic surface runoff from acid sulfate soils and sulfidic mine sites, and develop cost-effective management strategies and techniques to minimize its environmental impacts.
Pyrite specimens and pretreatment
The pyrite specimens used in this study were natural pyrite cubes purchased from the Anhui Tongling Siling Mineral Ltd. For this study, the purpose was to examine the effects of externally originated H2O2 on microbially involved oxidation of aqueous Fe2+ and pyrite grain surfaces. Therefore, powdered pyrite with high specific surface area was not appropriate due to its potential for causing the production of spontaneous H2O230. Pyrite cubes with similar size (approximately 1.5 × 1.5 × 1.5 cm3) were selected for the mineral-solution contact experiment. Pyrite surfaces are readily reactive when exposed to air. Pyrite oxidation products are expected to be present on the surfaces of any naturally occurring pyrite specimens. It is necessary to remove these coating materials prior to pyrite oxidation experiment. The surfaces of the mineral crystals were treated with a boiling 6 mol L−1 HCl solution to remove any oxides, (oxy)hydroxides and (oxy)hydroxysulfates of iron that were possibly present on the original mineral surfaces44. The “cleaned” pyrite cubes were immediately used for the experiment after washing with distilled water twice and acetone for three times to further remove elemental sulfur that is possibly present on the mineral surfaces.
Bacteria, culture conditions and inoculum preparation
A strain of Acidithiobacillus ferrooxidans was purchased from the China Marine Microbial Culture Collection Center (MCCC). The bacterial culture was maintained at 4°C in a 9 K nutrient medium39 containing 3.0 g of (NH4)2SO4, 0.01 g of Ca(NO3)2, 0.5 g of MgSO4.7H2O, 0.5 g of K2HPO4, 0.1 g of KCl and 44.3 g of FeSO4.7H2O in 1 L of distilled water with pH adjusted to 1.6 with a H2SO4 solution.
The inoculum was prepared prior to the experiment. An adequate amount of the bacteria required for the experiment was produced by facilitating bacterial growth in a sterile 9 K medium at 30°C, coupled with shaking (130 rpm) on a rotary shaker for 5–6 days. The cells in the enriched suspension were firstly separated from the iron precipitates (formed during the incubation) by centrifugation at 3000 rpm for 3 min to allow the settlement of the solid iron compounds. The cells remained in the suspension were then transferred into a new centrifuge tube and harvested by centrifugation at 5000 rpm for 10 min to allow the settlement of the cells. After washing twice with sterile distilled water (adjusted to pH 2 with a H2SO4 solution), the inoculum was formed by adding an appropriate amount of the same acidified distilled water into the centrifuge tube containing the cleaned cells. The cell concentration in the inoculum for each batch was determined by direct cell counting prior to addition of the inoculum into the experimental reactors in an experiment.
Aqueous Fe2+ oxidation experiment
Both biotic and abiotic experiments were conducted to observe the oxidation of Fe2+ following a single injection of H2O2. The abiotic experiment was to account for the effect of H2O2 as an oxidant on the chemical oxidation of aqueous Fe2+ while the biotic experiment was to examine the integrative effects of H2O2 (as an oxidant and a toxicant to iron-oxidizing bacteria) on Fe2+ oxidation. One control (C, without added H2O2) and four treatments with different initial H2O2 concentrations were established: (a) Treatment 1 (T1): 50 μmol L−1; (b) Treatment 2 (T2): 100 μmol L−1; (c) Treatment 3 (T3): 300 μmol L−1; and (d) Treatment 4 (T4): 1000 μmol L−1. For either biotic or abiotic experiment, two separate experiments with different initial levels of Fe2+ were conducted: (a) 55.8 mg L−1 and (b) 558 mg L−1.
For all the experiments, a Fe-free 9 K medium (without added FeSO4·7H2O) was used as the basal solution (i.e. the solution prior to the addition of various ingredients). A 150 mL conical flask was used as a batch reactor to contain 100 mL of a reacting solution with a pre-set H2O2-Fe2+ combination. The pH of the reacting medium was adjusted to 2 using a H2SO4 solution.
For the biotic experiments, the reacting medium was inoculated with Acidithiobacillus ferrooxidans at an initial cell concentration of 1.1 × 107 cells mL−1 for the lower Fe2+ treatments and 1.0 × 107 cells mL−1 for the higher Fe2+ treatments. All the conical flasks were loosely wrapped by aluminum foil to allow entry of air but not dust during the entire period of the experiment except at the time of sample collection. The reactors were shaken at 130 rpm on a rotary shaker with temperature set at 30°C. A small amount of sample was taken at different time to determine residual Fe2+ concentration, cell density and other relevant parameters. The experiment was performed in triplicate.
For the abiotic experiments, DO in the solutions was also monitored to examine whether marked spontaneous decomposition of H2O2 took place during the incubation experiment according to Equation 6.
Pre-experiment tests indicated that the added H2O2 was almost depleted within 5 min in the reaction systems investigated for the current study. Consequently, monitoring of H2O2 was not performed due to the following reasons: (a) the research objective (overall effects of H2O2 flux at the preset initial concentrations on the microbial oxidation of cubic pyrite and aqueous Fe2+) can be satisfactorily achieved without knowing the detailed evolution of H2O2 within the 5 min following the H2O2 injection; (b) the measured values of H2O2 for the different treatments are not reasonably comparable for such highly dynamic reaction systems since it is technically very difficult, if not impossible, to ensure the simultaneous analysis for the samples of all the treatments; and (c) there is a lack of highly reliable analytical methods for rapid measurements of micromolar level H2O230.
Pyrite oxidation experiment
The basal solution used was the same as the aqueous Fe2+ oxidation experiment. The “cleaned” pyrite cubes were exposed to H2O2 at various initial concentrations in the basal solution (with the pH adjusted to 2.0 by a H2SO4 solution) in the presence of the Acidithiobacillus ferrooxidans at an initial concentration of 2.7 × 107 cells mL−1. One control (CP, without added H2O2) and four treatments with different initial H2O2 concentrations were established: (a) Treatment1 (TP1): 50 μmol L−1; (b) Treatment 2 (TP2): 100 μmol L−1; (c) Treatment 3 (TP3): 300 μmol L−1; and (d) Treatment 4 (TP4): 1000 μmol L−1. A 250 mL conical flask was used as the reaction chamber. Five pyrite cubes were soaked in 90 mL of a respective solution for the control and each treatment. The conical flask was loosely wrapped using aluminium foil to allow entry of air but not dust and then kept in a biological incubator with the temperature set at 30°C during the entire period of the experiment except at the time of cyclic H2O2 injection and sample collection.
A time interval of 3–5 days was established for re-injection of H2O2, in-situ measurements of pH and solution sample collection for determinations of Fe2+, total Fe, S and cell density. After sampling, an equal amount of sterile Fe-free 9 K medium was added into the reactor to compensate the solution loss caused by the sample collection. To avoid markedly disturbing the solution equilibrium system, the volume of solution samples for chemical and microbial monitoring had to be minimized. Therefore only the above important parameters were measured for this experiment.
The experiment lasted for 86 days. On the 28th day of the experiment, two of the five pyrite cubes for the control and each treatment were taken for surface characterization analysis: one was used for observing the original oxidized surface and another was treated with a boiling 6 mol L−1 HCl solution to remove the oxidized materials for observing the corroded surface. At the end of the experiment, the pyrite cubes were harvested for surface characterization analysis to compare with those collected on the 28th day of the experiment.
Toxic response of Acidithiobacillus ferrooxidans to H2O2 under various conditions
Because both aqueous Fe2+ and cubic pyrite oxidation experiments indicated that Acidithiobacillus ferrooxidans experienced stress when exposed to H2O2, a supplementary toxic response experiment was conducted to determine whether the bacterial oxidative stress was caused by H2O2 alone or/and by its deriving hydroxyl radical as well. The basal solution used was the same as that in the aqueous Fe2+ and cubic pyrite oxidation experiments. Five treatments were established: (1) BI: without added H2O2; (2) BH: 50 μmol L−1 H2O2 only; (3) BIH: 50 μmol L−1 H2O2 and 55.8 mg L−1 Fe2+; (4) BHA: 50 μmol L−1 H2O2 and 50 μmol L−1 ascorbic acid (a scavenger of reactive oxygen species); and (5) BIHA: 50 μmol L−1 H2O2, 55.8 mg L−1 Fe2+ and 50 μmol L−1 ascorbic acid. Only one single injection of H2O2 was performed for the experiment. Acidithiobacillus ferrooxidans were inoculated into 100 mL of a respective solution in a conical flask. The initial pH was 2 and the initial cell concentration was 3.15 × 107 cells mL−1. The reactors were shaken at 130 rpm on a rotary shaker with temperature set at 30°C. Samples were taken for cell counting after shaking for 30 min.
In-situ measurement of pH and DO in the solution was made by a calibrated pH meter and DO meter, respectively. Fe2+ in the reacting solutions was measured by the potassium perchromate titration method45. Total Fe and S in the solution were determined by the inductively coupled plasma–atomic emission spectroscopy (ICP-AES). The concentration of viable planktonic cell in the reacting solutions was determined by direct cell counting using a Neubauer hemocytometer.
A FEI-XL30 environmental scanning electron microscope coupled with energy dispersive X-ray spectrometer (ESEM/EDS) was used for surface imaging and determining the surface chemical composition of the pyrite cubes. The observed surfaces were coated with a 20 nm thickness of gold. The accelerating voltage was 15 kV and the working distance was 4.9 to 6.3 mm.
XPS was employed to determine the chemical composition and element state of the mineral surfaces (to a depth of ~3–5 nm). XPS analyses were performed with a Kratos Axis UltraDLD spectrometer using a monochromatic Al Kα X-rays source. Broad scan was conducted using 160 eV pass energy, while narrow high-resolution spectra of all major lines were obtained using a resolution function with a width of 0.1 eV for a pass energy setting of 40 eV. The charge effect was corrected using C 1 s from contamination at 284.6 eV. Spectra were analyzed using the CasaXPS software (Version 2.2.19). Assignment of iron and sulfur species was made by referring to the published documents (Table S1 in the Supplementary Information).
The work related to this article was financially supported by the Natural Science Foundation of China (Project numbers: 40471067 and 40773058) and the Guangdong Bureau of Science and Technology (Project No. 2005A30402006).
About this article
Arsenic release from the abiotic oxidation of arsenopyrite under the impact of waterborne H2O2: a SEM and XPS study
Environmental Science and Pollution Research (2016)