Abstract
The development of organic semiconducting nanowires that act as charge carrier transport pathways in flexible and lightweight nanoelectronics is a major scientific challenge. We report on the fabrication of fullerene nanowires that is universally applicable to its derivatives (pristine C60, methanofullerenes of C61 and C71 and indene C60 bis-adduct), realized by the single particle nanofabrication technique (SPNT). Nanowires with radii of 8–11 nm were formed via a chain polymerization reaction induced by a high-energy ion beam. Fabrication of a poly(3-hexylthiophene) (P3HT): [6,6]-phenyl C61 butyric acid methyl ester (PC61BM) bulk heterojunction organic photovoltaic cell including PC61BM nanowires with precisely-controlled length and density demonstrates how application of this methodology can improve the power conversion efficiency of these inverted cells. The proposed technique provides a versatile platform for the fabrication of continuous and uniform n-type fullerene nanowires towards a wide range of organic electronics applications.
Similar content being viewed by others
Introduction
Currently, efforts to construct one-dimensional nanostructures of conjugated polymers1,2 and molecules are implemented using techniques such as templating3, electrodeposition4 and self-assembly5,6. Fullerenes, which have spherical shapes, electron accepting and transport capability, have occupied an important place in photochemistry7 and organic electronics8. They are electron and energy acceptors with rigid spherical π-conjugation, which provides an attractive avenue to applications in cosmetics, fluid lubrication, lightweight hard plastics and organic electronics9,10,11,12. Recently, the emerging field of organic semiconductors has cast a prominent spotlight on fullerene derivatives, because they possess deep-lying lowest unoccupied molecular orbitals (LUMO) and consequently, a negative (n)-type semiconducting nature13,14,15. Bulk heterojunction (BHJ) organic photovoltaic cells (OPV) are a notable application, which consist of positive (p)-type conjugated polymers and n-type fullerene derivatives that provide a promising framework, allowing the formation of a bi-continuous network with a large p/n interface, so that high power conversion efficiency (PCE) can be achieved16,17. Although the soluble fullerenes represent major advances in BHJ architecture, the thermal instability of BHJs, due partly to the diffusive motion of molecular fullerenes, must be addressed to realize the practical application of OPV18. Therefore, fullerene nanowires with a robust structure, which secure a large interface of p/n junctions and electron transport to the cathode, would contribute to the realization of stable BHJs.
The single particle nanofabrication technique (SPNT)19,20,21,22 was specifically designed to construct organic nanowires by irradiating a polymer thin film with high-energy charged particles, where “one” ion particle can deposit kinetic energy along the nanospace trajectory sufficient for the production of high-density radicals, with gelation resulting via cross-linking reactions. The subsequent development process dissolves the unexposed area and isolates the nanowires from the film material. Figure 1a shows a schematic of the procedure for nanowire formation. It is noteworthy that SPNT has universal applicability to various polymers; not only conventional polymers such as poly(styrene)20, but also conjugated polymers such as poly(silane), poly(thiophene) and poly(fluorene)21,22. The prerequisite for nanowire formation is a higher efficiency for cross-linking than main-chain scission.
Although most p-type conjugated polymers have been successfully converted to nanowires by SPNT, the formation of conjugated molecule nanowires has remained elusive, because small molecules require a large number of cross-linking reactions to ensure insolubility against the developer. Thus, we have examined small n-type molecules, such as the fullerene derivatives shown in Fig. 1b.
Results
Nanowire formation of fullerene derivatives
SPNT was applied to films of C6023, [6,6]-phenyl C61 butyric acid methyl ester (PC61BM)16, [6,6]-phenyl C71 butyric acid methyl ester (PC71BM) and indene-C60 bis-adduct (ICBA)24,25, according to the procedure illustrated in Fig. 1a. The latter three fullerenes are typical, soluble fullerenes used in BHJs. PC61BM nanowires were successfully formed, as evidenced by the scanning electron microscopy (SEM) and atomic force microscopy (AFM) images shown in Fig. 1c and 1d. The density of the nanowires can be easily scaled up by simply increasing the ion beam fluence, as shown in Fig. 1e and 1f. The lengths of the nanowires are almost equivalent to the thickness of the original film (ca. 1 μm) and are independent of the ion fluence.
The respective dependence of the PC61BM nanowire length and density on the film thickness and ion fluence was examined. The lengths of the nanowires were always equivalent to the film thickness for various film thicknesses of 0.1, 0.5 and 4 μm (Supplementary Fig. S1). Furthermore, the number of nanowires observed in a 2×2 μm2 AFM image area coincided with the number of incident ions calculated from the corresponding fluence (1.0, 3.0 and 5.0×108 ions cm−2) as shown in Supplementary Fig. S2. These results indicate that (1) nanowires are formed for each ion trajectory, (2) the terminus of a substrate-side nanowire is strongly connected to the bottom surface without separation during the development process and (3) the fullerene nanowires do not swell in the longitudinal direction by contact with the development solvent.
The AFM images shown in Fig. 2a demonstrate that SPNT affords nanowires for all of the C60, PC61BM, PC71BM and ICBA fullerene derivatives. The histogram below each micrograph indicates the distribution of the nanowire radius, obtained using an ellipsoidal model and the measurement of one hundred points of height and width (see supplementary information). The averaged radii are summarized in Table 1. ICBA, which has a slightly larger radius (11 nm) than the other fullerenes (8–9 nm) and bears two bulky indene units, has been extensively utilized in BHJs in combination with regioregular poly(3-hexylthiophene) (P3HT), because the high LUMO of ICBA achieves a high open-circuit voltage (Voc) for the OPV24. The bis-adduct fullerene has many regioisomers, which ensures good solubility, but may disrupt three-dimensional crystallization25. This could lead to increased radius and flexibility of the nanowires that reflects the packing in the fullerene film and its solubility. This presumption is strongly corroborated by the topography of the 2 μm-length nanowires made of bare C60, whereas they are obviously rigid with a complete straight shape, in contrast to substituted fullerenes (Fig. 2b).
The scanning tunneling microscopy (STM) image of a C60 nanowire (Fig. 2c) reveals that the surface is covered by closely packed fullerene molecules. Dimerization and polymerization reactions of C60 have been reported with light exposure26,27, high temperature and pressure28 and γ-ray irradiation29. The 2+2 cycloaddition reaction (Fig. 2d) has been proposed for the photopolymerization reaction, as studied by Raman spectroscopy27. The STM images of the C60 nanowires on a Si substrate were also collected in a variety of bias voltage applied to the substrate (Supplementary Fig. S3). The optimized bias voltage was set at −1 ~ −1.2 V for the clear visualization of the outer cage of C60 molecules (Fig. S3(d) ~ (f)), which was the considerably higher bias voltage required for the visualization of C60 molecules not polymerized into the nanowires and distributed on the surface (Fig. S3(a)~(c)). This is suggestive that the polymerization reaction at the surface of the nanowires causes lowering of the energy levels of LUMO orbital of C60 molecules bound into the nanowires. Taking account of these reports and the good mechanical strength of the nanowires, a similar polymerization reaction is also expected to occur for SPNT, in which nanowire formation is successful, regardless of the substituents.
Chain polymerization reaction
To produce a complete picture of the polymerization reaction, the cross-linking efficiency G(x), was estimated and is defined by the number of reactions per 100 eV of absorbed ion dose. From the theoretical model, G(x) is expressed as20:
where ρ is the density of the material, NA is Avogadro's number, r is the observed radius of the nanowire, LET is the linear energy transfer along the ion trajectory30, M is the molecular weight, rc and rp are the respective radii of the core and penumbra areas given by the theoretical equation for collisions of charged particles with matter and e is the elementary charge. This equation has been proven to be valid for many types of polymers20,21,22. G(x) obtained for the fullerene nanowires are listed in Table 1 and range from 29 to 55 (100 eV)−1, which is approximately two orders of magnitude larger than that of synthetic polymers such poly(4-bromostyrene), which has the highest G(x) of 0.30–1.6 (100 eV)−1 among polymers31. Furthermore, G(x) for the fullerene nanowires exceeds the initial ionization yield (ca. 5 (100 eV)−1)32, which reveals that the polymerization reaction proceeds via a chain reaction.
p/n heterojunction of PC61BM and polyfluorene nanowires
Nanowire fabrication is facile in the direction perpendicular to the substrate; therefore, we attempted to form p/n junction nanowires comprising a p-type poly(9,9′-n-dioctylfluorene) (PFO) and n-type PC61BM bilayer. A bilayer without significant inter-mixing was successfully prepared by spin-coating a PFO layer from toluene solution onto a drop-cast PC61BM layer. Figure 3a shows a schematic of the procedure, where the bilayer is exposed to 450 MeV Xe ions and developed using toluene. The AFM image in Fig. 3b indicates nanowire formation, the length of which corresponds to the bilayer thickness. A magnified image of the nanowire (Fig. 3c) shows that the nanowire consists of two components; a straight, thick portion and a thin, winding portion. The size and morphology of the former portion are consistent with that observed for a PC61BM nanowire and the latter portion appears identical to an individual PFO nanowire (Fig. 3d). There also appears to be an inflection point at the p/n heterojunction for several nanowires, which results from the difference in the mechanical strength of the PFO and PC61BM nanowires, as represented by the bottom right schematic in Fig. 3a. Furthermore, the rigidity of fullerene nanowires is evident from the low aspect ratio (width/height) of the PC61BM nanowire cross section, which is as small as 2.3, while that of PFO nanowires is 7.3. The PFO nanowires are flattened by either their own weight or by adhesive interaction with the surface. It should be noted that SPNT can be used to produce any type of semiconducting heterojunction with two dissimilar materials if a bilayer can be prepared. This toleration of SPNT towards materials is underlined by critical requisite for the formation of self-assembled nano-heterojunctions through synthetic procedure33.
Photovoltaic application of PC61BM nanowires
The p/n heterojunction demonstrated is expected to be applied for ideal charge separation and transport in OPV, or as a nanoscale diode for molecular switching, although integration of the p/n nanowires into the device still requires considerable development. Therefore, the hybridization of PC61BM nanowires with BHJ-type OPV was examined. Figures 4a and 4b show schematics for the fabrication of PC61BM nanowires on glass/ indium tin oxide (ITO)/ poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) and glass/ITO/TiOx substrates for normal and inverted cell structures34. The PC61BM nanowires were confirmed to be in contact with both substrate types. The active layer of P3HT:PC61BM = 1:1 w/w was spin-coated from o-dichlorobenzene (oDCB) solution in a nitrogen glove box, followed by solvent removal in a petri dish and thermal annealing at 150°C for 10 min. A PEDOT:PSS/Au anode and Ca/Al cathode layers were formed for the inverted and normal cells, respectively. The OPV performance was measured under illumination from an AM 1.5 G solar simulator. Figure 4c shows current density-voltage (J-V) curves for P3HT:PC61BM devices with and without PC61BM nanowires. The impact of nanowire length (LNW = 40, 120 and 200 nm) and density (ρNW = 109, 1010 and 1011 cm−2) on the OPV performance was investigated. The PCE, Voc, short-circuit current density (Jsc) and fill factor (FF) are listed in Table 2 (see Supplementary Fig. S4 for all J-V curves). When the nanowires are integrated with normal cells, the PCE was decreased from 3.68% without nanowires to 3.06% at ρNW = 109 cm−2 and to 1.44% at ρNW = 1011 cm−2. The negative effect of the nanowires on the normal device is due to the connection of the n-type PC61BM nanowires to the anode ITO/PEDOT:PSS layer, so that electrons in the nanowires have a higher recombination rate with holes, which results in a significant drop of Jsc and FF. In contrast, the inverted cell with LNW = 120 nm and ρNW = 109 cm−2 nanowires exhibited an approximate 7% improvement of the PCE over that without the nanowires (from 2.73 to 2.91%), due to an increase of Jsc (from 8.15 to 8.92 mA cm−2) despite a slight decrease of the FF (59.3 to 57.7%). The segregation of PC61BM nanowires on the cathode ITO/TiOx layer is beneficial for electron collection, which leads to an increase in the overall device performance (Fig. 4b).
Discussion
In the OPV devices, calculating the area that the nanowires with LNW = 120 nm and ρNW = 109 cm−2 can cover gives a small value of only 2%. This may be an unprecedented finding that the nanowires act as seeds to promote the vertical segregation of PC61BM during the formation of active layer. The TEM images of BHJ with PC61BM nanowires reveals that the nanowire structures are preserved, although they seem larger than those before formation of the BHJ layer (Fig. 4e and 4f), which suggests the selective aggregation of PC61BM onto the seed nanowires. However, a high density of nanowires (ρNW > 1011 cm−2) caused an abrupt decease in PCE, even for the inverted cells (Fig. 4d), which suggests the nanowires have a negative effect.
The LUMO of PC61BM is considered slightly lowered in comparison with normal PC61BM along with narrowing of the band gap, on the basis of density functional theory results of C60 dimer35,36. In the characterization of photovoltaic devices (Table 2), Voc is decreased with increasing the number density and length of PC61BM nanowires in the inverted cells, while it does not change significantly in the normal cells. This is the case giving that LUMO of PC61BM nanowires is also shifted downward as observed in C60 nanowires, because the electron energy level drops from the upper-lying LUMO of normal PC61BM domain to the lower-lying LUMO of PC61BM nanowires which are concentrated on the anode in the inverted cells.
It is difficult to yield bulk materials of PC61BM nanowires on the scale of a few milligrams for characterization of the electrical properties for devices such as field-effect transistors; therefore, electrode-less flash-photolysis time-resolved microwave conductivity (FP-TRMC)37 was employed. The photoconductivity maxima of films exposed to fluences of 1010 and 1011 cm−2 were decreased by approximately 14 and 30%, respectively (Supplementary Fig. S5). Thus, the electron transport capability of the nanowires is worse than that of the pristine film due to the randomly-polymerized network, which is consistent with the results for the OPV, where too many nanowires resulted in degradation of the PCE. This result is, nonetheless, contradictory to that reported for a C60 film irradiated with 55–120 MeV ions and the formation of conductive pathways perpendicular to the substrate measured by conducting AFM38. However, the conditions used were different from the present study (conductive direction, method, ion beam energy, material and development process) and thus more detailed investigations are highly anticipated. The negative effect on the OPV was found to manifest more in the normal P3HT:PC61BM cell with P3HT nanowires (LNW = 200 nm, ρNW = 1011 cm−2), of which the PCE was 0.53% with an extremely low FF of 27.1% (Supplementary Fig. S6), despite the preservation of the P3HT backbone and cross-linking of the side-chain, which are mainly responsible for the gelation.
The advantage of rigid fullerene nanowires over the bulk state is the thermal stability. The surface morphologies of PC61BM nanowires before and after thermal annealing at 160°C for 10 min were compared (Supplementary Figs. S7 and S8). The almost perfect conservation of the nanowire structure demonstrates the feasibility and stability of these organic electronics. State-of-the-art low bandgap copolymers comprising donor and acceptor units sometimes require fine-tuning of the side-chains and the incorporation of solvent additives such as 1,8-diiodeoctane to form an ideal BHJ network39, whereas the present fullerene nanowires could pave the way towards the facile construction of BHJs with high thermal stability.
In spite of the relatively high mechanical strength of fullerene nanowires, they still lay down on the surface in the development process. Some uprisings are expected during the active layer coating; however, excessive long nanowires result in their bending and knocking down, which might be one of the reasons for the decrease of OPV performance observed in the long nanowires. Further investigations are on the way to making the nanowires stand on the surface by performing dry development process instead of the present wet process.
The simple concept of the present approach (a particle produces a corresponding nanowire) provides control of the number density of nanowires on a substrate and the nanowires can be successfully applied as a versatile platform of continuous and uniform organic n-type semiconducting nanowires. The extremely high efficiency of the polycondensation reactions in fullerene derivatives may launch the single particle nanofabrication technique onto the industrial stage for application in the fabrication of electronic nanomaterials.
Methods
Formation of nanowires by SPNT
All reagents and chemicals were purchased from Nacalai Tesque, Inc. and Aldrich Chemical Co., Ltd. unless otherwise stated. The Si substrates were subjected to UV-ozone treatment. C60 was deposited on Si substrates by thermal evaporation in a vacuum chamber. PC61BM, PC71BM and ICBA were dissolved in chlorobenzene (CB) and drop-cast on the Si substrate. Film thickness was measured using a stylus surface profiler (Ulvac, Dektak 150). Films were irradiated using 450 MeV Xe or 490 MeV Os particles from the cyclotron accelerator at the Takasaki Advanced Radiation Research Institute (TIARA) of the Japan Atomic Energy Agency. The number density of incident particles was controlled from 1.0×108 to 1.0×1011 ions cm−2. The irradiated C60 and fullerene derivative films were developed in oDCB and CB for 10 min, respectively. The loss of kinetic energy of particles due to penetration through the fullerene films was estimated using the SRIM 2010 calculation code30.
Morphology observations
The size and shape of the nanowires were observed by atomic force microscopy (AFM; Seiko Instruments Inc., Nanocute OP and Nanonavi II) and scanning electron microscopy (SEM; Jeol Ltd., JSM-7001F). The surface structures of the C60 nanowires were measured using a scanning tunneling microscope (STM; Jeol Ltd., JSPM-5200). Transmission electron microscopy (TEM) observation was carried out using a Jeol Ltd. JEM-1400 microscope. The BHJ samples for TEM were prepared by exfoliation of a thin film layer after ultrasonication of a normal cell in water, which dissolves the bottom PEDOT:PSS layer and allows lift-off of the active layer with the nanowires.
OPV devices
Materials: Poly(3-hexylthiophene) (P3HT; >98% head-to-tail regioregularity, 99.995% trace metals basis, Mn = 3−6×104 g mol−1, Mw/Mn < 2.5) and PC61BM (purity >99.5%) were purchased from Aldrich and Frontier Carbon, Inc., respectively. Solvents were purchased from Kishida Kagaku Corp. unless otherwise noted and were used as-received without further purification. PEDOT:PSS (Baytron P VP AI 4083) and ITO-coated glass substrates (<15 Ω square−1) were purchased from H. C. Stark and Sanyo Shinku Corp., respectively. The ITO glass substrates were successively cleaned in tetrahydrofuran, detergent, de-ionized water, acetone and isopropyl alcohol for 10 min each with ultrasonication. The dried ITO glass substrates were subjected to UV-ozone treatment.
Normal OPV: A PEDOT:PSS layer was cast onto the ITO layer by spin-coating after passing through a 0.2 μm filter. The substrate was annealed on a hot plate at 150°C for 30 min. A 2 wt% chloroform (CF) solution of PC61BM or 1.5 wt% CB solution of P3HT were cast on top of the PEDOT:PSS buffer layer in a nitrogen glove box by spin-coating or drop-casting after passing through a 0.2 μm filter. The films were then irradiated with 490 MeV Os particles. The number density of incident particles was controlled from 1.0×109 to 1.0×1011 ions cm−2. The irradiated films were developed in CB for 15 min in a nitrogen glove box. A 1.5 wt% oDCB solution of P3HT: PC61BM = 1:1 (w/w) was heated at 60°C with stirring for at least 4 h to achieve complete dissolution. The active layer was cast, immediately after development, on top of the PEDOT:PSS buffer layer in a nitrogen glove box by spin-coating at an optimized rotation speed and time after passing through a 0.2 μm filter. The films were annealed on a hot plate at 150°C for 10 min. A cathode consisting of 20 nm Ca and 100 nm Al layers was sequentially deposited through a shadow mask on top of the active layers by thermal evaporation in a vacuum chamber. The resulting device configuration was ITO (120–160 nm)/PEDOT:PSS (45–60 nm)/active layer (ca. 220 nm)/Ca (20 nm)/Al (100 nm) with an active area of 7.1 mm2. Current-voltage (J-V) curves were measured using a source-measure unit (ADCMT Corp., 6241A) under AM 1.5 G solar illumination at 100 mW cm−2 (1 sun) using a 300 W solar simulator (SAN-EI Corp., XES-301S).
Inverted OPV: The TiOx precursor (Koujundo Kagaku Corp.) was cast on the ITO layer by spin-coating after passing through a 0.2 μm filter. The layers were annealed on a hot plate at 150°C for 10 min. A 2 wt% CF solution of PC61BM was cast onto the TiOx layer in a nitrogen glove box by spin-coating after passing through a 0.2 μm filter. The films were irradiated with 490 MeV Os particles, developed with CB and the P3HT:PC61BM active layer was cast in a similar fashion to that for the normal OPV. An aqueous solution of PEDOT:PSS with 1 wt% poly(ethylene)glycol as a surfactant was dropped onto the active layer after passing through a 0.2 μm filter and immediately spin-coated. The layers were annealed on a hot plate at 150°C for 10 min. The anode consisted of a 50 nm Au layer that was deposited through a shadow mask on top of the active layers by thermal evaporation in a vacuum chamber. The resulting device configuration was ITO (120–160 nm)/TiOx (ca. 10 nm)/active layer (ca. 220 nm)/PEDOT:PSS (50–100 nm)/Au (50 nm) with an active area of 7.1 mm2. The J-V curves were measured in the same way as that for the normal OPV.
References
Zhao, Y. S., Wu, J. & Huang, J. Vertical Organic Nanowire Arrays: Controlled Synthesis and Chemical Sensors. J. Am. Chem. Soc. 131, 3158–3159 (2009).
Ahn, J. -H., Kim, H. –S., Lee, K. J., Jeon, S., Kang, S. J., Sun, Y., Nuzzo R, G. & Rogers, J. A. –Heterogeneous Three-Dimensional Electronics by Use of Printed Semiconductor Nanomaterials. Science 314, 1754–1757 (2006).
O'Carroll1, D., Lieberwirth, I. & Redmond, G. Microcavity effects and optically pumped lasing in single conjugated polymer nanowires. Nature Nanotech. 2, 180–184 (2007).
Ramanathan, K., Bangar, M. A., Yun, M., Chen, W., Mulchandani, A. & Myung, N. V. Individually Addressable Conducting Polymer Nanowires Array. Nano Lett. 4, 1237–1239 (2004).
Bullock, J. E., Carmieli, R., Mickley, S. M., Vura-Weis, J. & Wasielewski, M. R. Photoinitiated Charge Transport through π-Stacked Electron Conduits in Supramolecular Ordered Assemblies of Donor-Acceptor Triads. J. Am. Chem. Soc. 131, 11919–11929 (2009).
Matsuo, Y., Sato, Y., Niinomi, T., Soga, I., Tanaka, H. & Nakamura, E. Columnar Structure in Bulk Heterojunction in Solution-Processable Three-Layered p-i-n Organic Photovoltaic Devices Using Tetrabenzoporphyrin Precursor and Silylmethyl[60]fullerene. J. Am. Chem. Soc. 131, 16048–16050 (2009).
Imahori, H., Guldi, D. M., Tamaki, K., Yoshida, Y., Luo, C., Sakata, Y. & Fukuzumi, S. Charge Separation in a Novel Artificial Photosynthetic Reaction Center Lives 380 ms. J. Am. Chem. Soc. 123, 6617–6628 (2001).
Chuvilin, A., Bichoutskaia, E., Gimenez-Lopez, M. C., Chamberlain, T. W., Rance, G. A., Kuganathan, N., Biskupek, J., Kaiser, U. & Khlobystov, A. N. Self-assembly of a sulphur-terminated graphene nanoribbon within a single-walled carbon nanotube. Nature Mater. 10, 687–692 (2011).
Isaacson, C. W., Kleber, M. & Field, J. A. Quantitative Analysis of Fullerene Nanomaterials in Environmental Systems: A Critical Review. Environ. Sci. Technol. 43, 6463–6474 (2009).
Sun, Y., Welch, G. C., Leong, W. L., Takacs, C. J., Bazan, G. C. & Heeger, A. J. Solution-processed small-molecule solar cells with 6.7% efficiency. Nature Mater. 11, 44–48 (2012).
Chen, H.-Y., Hou, J., Zhang, S., Liang, Y., Yang, G., Yang, Y., Yu, L., Wu, Y. & Li, G. Polymer solar cells with enhanced open-circuit voltage and efficiency. Nature Photo. 3, 649–653 (2009)
Babu, S. S., Mohwald, H. & Nakanishi, T. Recent progress in morphology control of supramolecular fullerene assemblies and its applications. Chem. Soc. Rev. 39, 4021–4035 (2010).
He, Z., Zhong, C., Huang, X., Wong, W.-Y., Wu, H., Chen, L., Su, S. & Cao, Y. Simultaneous Enhancement of Open-Circuit Voltage, Short-Circuit Current Density and Fill Factor in Polymer Solar Cells. Adv. Mater. 23, 4636–4643 (2011).
Beaujuge, P. M. & Fréchet, J. M. J. Molecular Design and Ordering Effects in π-Functional Materials for Transistor and Solar Cell Applications. J. Am. Chem. Soc. 133, 20009–20029 (2011).
Clarke, T. M. & Durrant, J. R. Charge Photogeneration in Organic Solar Cells. Chem. Rev. 110, 6736–6767 (2010).
Yu, G., Gao, J., Hummelen, J. C., Wudi, F. & Heeger, A. J. Polymer Photovoltaic Cells: Enhanced Efficiencies via a The device structure consisted of a Network of Internal Donor-Acceptor Heterojunctions. Science 270, 1789–1791 (1995).
Service, R. F. Outlook Brightens for Plastic Solar Cells. Science 332, 293-293 (2011).
Hishikawa, Y., Warta, W. & Dunlop, E. D. Solar cell efficiency tables (version 39). Progress in Photovoltaics 20, 12–20 (2012).
Seki, S., Maeda, K., Tagawa, S., Kudoh, H., Sugimoto, M., Morita, Y. & Shibata, H. Formation of Nanowires along Ion Trajectories in Si Backbone Polymers. Adv. Mater. 13, 1663–1665 (2001).
Seki, S., Tsukuda, S., Maeda, K., Matsui, Y., Saeki, A. & Tagawa, S. Inhomogeneous Distribution of Crosslinks in Ion Tracks in Polystylene and Polysilanes. Phys. Rev. B 70, 144203/1–8 (2004).
Seki, S., Tsukuda, S., Maeda, K., Tagawa, S., Shibata, H., Sugimoto, M., Jimbo, K., Hashitomi, I. & Koyama, A. Effects of Backbone Configuration of Polysilanes on Nanoscale Structures Formed by Single-Particle Nanofabrication Technique. Macromolecules 38, 10164 (2005).
Tsukuda, S., Seki, S., Sugimoto, M. & Tagawa, S. Customized Morphologies of Self-Condensed Multisegment Polymer Nanowires. J. Phys. Chem. B 110, 19319–19322 (2006).
Kroto, H. W., Heath, J. R., O'Brien, S. C., Curl, R. F. & Smalley, R. E. C60: Buckminsterfullerene. Nature 318, 162–163 (1985).
Zhao, G., He, Y. & Li, Y. 6.5% Efficiency of Polymer Solar Cells Based on poly(3-hexylthiophene) and Indene-C60 Bisadduct by Device Optimization. Adv. Mater. 22, 4355–4358 (2010).
Kang, H., Cho, C.-H., Cho, H.-H., Kang, T. E., Kim, H. J., Kim, K.-H., Yoon, S. C. & Kim, B. J. . . Controlling Number of Indene Solubilizing Groups in Multiadduct Fullerenes for Tuning Optoelectronic Properties and Open-Circuit Voltage in Organic Solar Cells. ACS Appl. Mater. Interfaces 4, 110–116 (2012).
Rao, A. M., Zhou, P., Wang, K.-A., Hager, G. T., Holden, J. M., Wang, Y., Lee, W.-T., Bi, X.-X., Eklund, P. C., Cornett, D. S., Duncan, M. A. & Amster, J. Photoinduced Polymerization of Solid C60 Films. Science 259, 955 (1993).
Zhou, P., Dong, Z. –H., Rao, A. M. & P. C., Eklund. Reaction mechanism for the photopolymerization of solid fullerene C60 . Chem. Phys. Lett. 211, 337–340 (1993).
Iwasa, Y., Arima, T., Fleming, R. M., Siegrist, T., Zhou, O., Haddon, R. C., Rothberg, L. J., Lyons, K. B., Carter Jr, H. L. Hebard, A. F., Tycko, R., Dabbagh, G., Krajewski, J. J., Thomas, G. A. & Yagi, T. New Phases of C60 Synthesized at High Pressure. Science 264, 1570–1572 (1994).
Malik, S., Fujita, N., Mukhopadhyay, P., Goto, Y., Kaneko, K., Ikeda, T. & Shinkai, S. Creation of 1D [60]fullerene superstructures and its polymerization by γ-ray Irradiation. J. Mater. Chem. 17, 2454–2458 (2007).
The G(x) was obtained from each radius, molecular weight, density (1.5–1.7 g cm−3) and linear energy transfer (LET) of 490 MeV Os (ca. 17–18 keV nm−1) calculated by SRIM 2010 simulation code (http://www.srim.org/).
Burlant, W., Neerman, J. & Serment, V. γ-radiation of p-substituted polystyrenes. .J. Polym. Sci. 58, 491–500 (1962).
Hatano, Y., Katsumura, Y., & Mozumder, A. Charged Particle and Photon Interactions with Matter, -Recent Advances, Applications and Interfaces; CRS Press (2011).
Zhang, W., Jin, W., Fukushima, T., Saeki, A., Seki, S. & Aida, T. Supramolecular Linear Heterojunction Composed of Graphite-Like Semiconducting Nanotubular Segments. Science 334, 340–343 (2011).
Park, S. H., Roy, A., Beaupré, S., Cho, S., Coates, N., Moon, J. S., Moses, D., Leclerc, M., Lee, K. & Heeger, A. J. Bulk heterojunction solar cells with internal quantum efficiency approaching 100%. Nature Photo. 3, 297–303 (2009).
Bihlmeier, A., Samson, C. C. M. & Klopper, W. DFT Study of Fullerene Dimers. ChemPhysChem 6, 2625 2632– (2005).
Ren, T., Sun, B., Chen, Z., Qu, L., Yuan, H., Gao, X., Wang, S., He, R., Zhao, R., Zhao, Y., Liu, Z. & Jing, X. Photochemical and Photophysical Properties of Three Carbon-Bridged Fullerene Dimers: C121 (I, II, III). J. Phys. Chem. B 111, 6344–6348 (2007).
Saeki, A., Tsuji, M. & Seki, S. Direct Evaluation of Intrinsic Optoelectronic Performance of Organic Photovoltaic Cells with Minimizing Impurity and Degradation Effects. Adv. Energy Mater. 1, 661–669 (2011).
Kumar, A., Avasthi, D. K., Tripathi, A., Kabiraj, D., Singh, F. & Pivin, J. C. Synthesis of confined electrically conducting carbon nanowires by heavy ion irradiation of fullerene thin film. J. Appl. Phys. 101, 014308/1–5 (2007).
Lee, J. K., Ma, W. L., Brabec, C. J., Yuen, J., Moon, J. S., Kim, J. Y., Lee, K., Bazan, G. C. & Heeger, A. J. Processing Additives for Improved Efficiency from Bulk Heterojunction Solar Cells. J. Am. Chem. Soc. 130, 3619–3623 (2008).
Acknowledgements
This work was supported by the Japan Society for the Promotion of Science (JSPS) Funding Program for Next-Generation World-Leading Researches (NEXT Program), the Precursory Research for Embryonic Science and Technology (PRESTO) program of the Japan Science and Technology Agency (JST) and a KAKENHI grant from the Ministry of Education, Culture, Sports, Science and Technology (MEXT) of Japan. TEM measurements were conducted in the Research Hub for Advanced Nano Characterization, the University of Tokyo, supported by MEXT of Japan.
Author information
Authors and Affiliations
Contributions
A.S. and S.Se. conceived and designed the research. Y.M. and S.Su. performed experiments and H. M., A. A., M.O., S.T. and M.S. helped with experiments of ion beam irradiations. A.K. and K.K. conducted TEM experiments. Y.M., A.S. and S.Se. analysed the data and wrote the manuscript. All authors read and discussed it extensively.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Supplementary Information
Supplementary information for Fullerene nanowires as a versatile platform for organic electronics
Rights and permissions
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareALike 3.0 Unported License. To view a copy of this license, visit http://creativecommons.org/licenses/by-nc-sa/3.0/
About this article
Cite this article
Maeyoshi, Y., Saeki, A., Suwa, S. et al. Fullerene nanowires as a versatile platform for organic electronics. Sci Rep 2, 600 (2012). https://doi.org/10.1038/srep00600
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep00600
This article is cited by
-
Ubiquitous organic molecule-based free-standing nanowires with ultra-high aspect ratios
Nature Communications (2021)
-
Evolution of SPR in 120 MeV silver ion irradiated Cu (18%) C60 nanocomposites thin films
Journal of Materials Science: Materials in Electronics (2019)
-
Fabrication of enzyme-degradable and size-controlled protein nanowires using single particle nano-fabrication technique
Nature Communications (2014)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.