The lack of new functional applications for metallic glasses hampers further development of these fascinating materials. In this letter, we report for the first time that the MgZn-based metallic glass powders have excellent functional ability in degrading azo dyes which are typical organic water pollutants. Their azo dye degradation efficiency is about 1000 times higher than that of commercial crystalline Fe powders and 20 times higher than the Mg-Zn alloy crystalline counterparts. The high Zn content in the amorphous Mg-based alloy enables a greater corrosion resistance in water and higher reaction efficiency with azo dye compared to crystalline Mg. Even under complex environmental conditions, the MgZn-based metallic glass powders retain high reaction efficiency. Our work opens up a new opportunity for functional applications of metallic glasses.
Decoloring (decomposing the -N = N- bond in azo dyes) is, in general, an undesirable phenomenon for decorating and furnishing. However, in order to remediate water with contaminants that contain various azo dyes, achieving high efficiency in decolorization is of considerable interest. Among the various methods of degrading the organic water contaminants, reduction by zero-valent (zero oxidation state) metals has been documented as a highly efficient and low cost process1,2,3,4. In contrast, bacterial degradation methods have limitation in degrading some toxic azo dyes especially in a complex environment containing various chemicals5,6 while a carbon sorbent absorption method only collects the contaminants via a physical process but cannot degrade them7. The zero-valent Mg (ZVM) is of special interest due to its high efficiency in degrading various organic water contaminants5. Corrosion of pure Mg in water, however, reduces its endurance since a large amount of Mg can be consumed by water. Moreover, the decoration by Pd and Pd compounds has also been applied to enhance the Mg performance5, but this approach is costly. Therefore, it is of high interest to suppress the water corrosion process of Mg at low cost while simultaneously increasing the reaction efficiency with the dye.
The solid solution alloying is an effective way of improving the corrosion behavior of crystalline Mg alloys, but, in many cases, this method is highly limited by the low solubility of the desired alloying elements8,9,10,11. The glassy alloys, which have a unique atomic structure and special physical and chemical properties12,13,14,15,16, are promising candidates for this purpose because they offer an enhanced solubility of the alloying elements thus improving the corrosion resistance. Furthermore, the amorphous phase itself has excellent ionic corrosion resistance owing to the homogeneous microstructure and absence of grain boundaries and other defects17,18,19.
On the other hand, metallic glasses are metastable and the constituent atoms do not reside at the thermodynamic equilibrium positions (corresponding to crystalline state) but locate in far-from-equilibrium states13,14,17. The metastable nature imparts many excellent properties to amorphous alloys that are unachievable for crystalline alloys, such as the good catalytic and chemical properties15,16,20,21,22,23,24. These properties can be widely tuned and optimized by controlling chemical composition, especially when the glass forming ability is not the major concern. In addition, the intrinsic brittleness of Mg- and Fe-based metallic glasses facilitates their communition into fine powders thus increasing their surface to volume ratio. The combination of their metastable nature, widely tunable compositions and intrinsic brittleness makes the metallic glasses very attractive materials for degrading the water contaminants.
Here we report that the ball-milled glassy Mg-based (BM G-Mg) alloy powders have excellent capability in degrading azo dyes in harsh environments at low temperatures. The glassy structure and high concentration of Zn are expected to improve the water corrosion resistance of the alloy and improve its reaction efficiency with azo dye.
Characterization of BM G-MgZn powders
The structure of the powders is verified by XRD, as is shown in Fig. 1(a). The initial powders, the powders reacted with azo dye solutions and the powders exposed in air for one week show an amorphous structure. The amorphous structure of the initial powders was further certified by high-resolution transmission electron microscopy (HRTEM) and nano-beam diffraction pattern, as is shown in Fig. 1(b). The morphology of the BM G-MgZn powders is shown in Fig. 1(c). It is evident that the particles are well dispersed without aggregation. The surface morphology of powder particles is characterized by high roughness and demonstrates the existence of corrugations. The particle size distribution shown in Fig. 1(d) provides an average diameter of 19.4 μm. Upon annealing at 300°C the powders crystallized to form Mg and MgZn intermetallics.
Azo dye degradation capability in aqueous solutions
The blue azo dye (Direct Blue 6, C32H20N6Na4O14S4) aqueous solution with concentration of 0.2 g/L was used for evaluating the degradation ability. The azo bonding of Direct Blue 6 solution has a wide light absorption peak around 580 nm corresponding to the wavelength scale of green and yellow color, which can be seen in Fig. 2(a). Along with the degradation process, the azo bond –N = N- breaks into two –NH225,26. The peak height in the absorption spectrum that is proportional to the concentration of azo dyes, will decrease and herein is used to characterize the Azo Dye concentration. The azo dye is degraded very fast in the first minute of exposure to BM G-MgZn powders. After 10 minutes of exposure, the color of the solution disappears denoting that the azo bonding is degraded completely. This degradation process takes place much faster than that for the commercial Fe powders and the Fe-based metallic glass powders27, as can be seen in Fig. 2(b). The intensity decay behavior with time can be fitted by an exponential decay function according to the pseudo-first-order kinetic model5,28, , where I is the normalized intensity of the absorption peak, I0 and I1 are fitting constants, t is the degradation time and t0 is the time when the intensity decreases to e−1 of the initial state derived by fitting the experimental data. The reaction efficiency can be estimated by the value of t0, as is shown in Fig. 2(c). The efficiency of G-MgZn powders (t0 = 0.78 min) is about 20 times faster than using the ball-milled Fe-based glass powders (BM G-Fe, t0 = 16 min) and 1000 times faster than using the gas-atomization Fe-based glass powders (GA G-Fe, t0 = 810 min) and commercial Fe powders (C-Fe), even though the Mg-based powders have a larger particle size and a reduced dosage is applied. After completion of the reaction, high-resolution SEM was used to examine the surface of the powder particles. The reaction products in form of nano-whiskers were observed to distribute uniformly and loosely on the surface of the G-MgZn particles, as is shown in Fig. 2(d). The uniform distribution without aggregation also denotes that the powder particles have high activity in this reaction. The loose structure of the reaction products on the surface cannot prevent further reaction and assures high reaction endurance.
Reaction efficiencies in complex environments
The reaction efficiency was evaluated at different environment temperatures ranging from 45°C to 7°C, as shown in Fig. 3(a). The reaction maintains a very high efficiency in the temperature range between 23 to 45°C, with a slight slow down at 7°C. The thermal activation energy barrier ΔE can be evaluated with the Arrhenius-type equation, t0 = τ0exp(ΔE/RT), where τ0 is a time pre-factor, R the gas constant. The ΔE is determined to be 51±23 kJ mol−1, where the large uncertainty is related to the very fast degradation speed for the initial one minute above 23°C so that resolving accurate t0 values is difficult. Even with the uncertainty, the ΔE is smaller than that of the G-Fe powders, i.e. 78 kJ mol−1 for ball-milled G-Fe powders and 114 kJ mol−1 for gas-atomized G-Fe powders27which indicates low temperature dependence for the degradation activity for G-Mg-Zn powders.
Slightly oxidized and the crystallized Mg-based powders were also examined. The degradation behavior of the absorption peak in comparison with the initial fresh powders can be found in Fig. 3(a). The degradation efficiency decreases after oxidation but the azo dyes can still be decomposed almost completely within 45 minutes, as shown in Fig. 3(b). The crystallized powders, which contain mostly crystalline Mg phase and MgZn intermetallics, have a much lower degradation efficiency, especially during the late stage of reaction. The fitting results give t0 = 10.2 min and 16.1 min for oxidized and crystallized powders, respectively. These values are about 12 and 20 times lower than that of the fresh BM G-MgZn powder.
To examine the effect of pH level we prepared the solution with pH = 3 by adding 0.1 M HCl solution and prepared the solution with pH = 10 by adding 0.1 M NaOH solution. For the initial one minute of the reaction, changing the acidity of the solution didn't change the reaction rate much, as is shown in Fig. 3(c). However, increasing the acidity can accelerate the degradation rate at the late stage. The azo dye can be degraded completely more quickly in solutions with low pH values.
The ability in degrading different azo dyes was also examined. Four other types of azo dyes with different characteristic absorption peaks were used for this evaluation, including Tartrazine (C16H9N4Na3O9S2, 534.36 g/mol), Methyl Orange (C14H14N3NaO3S, 327.34 g/mol), Sunset Yellow FCF (C16H10N2Na2O7S2, 452.37 g/mol) and Reactive Red 2 (C19H10Cl2N6Na2O7S2, 615.33 g/mol). The azo dyes were dissolved in deionized water with concentration of 0.1 g/L, separately. The UV absorption spectrum and the color image for each solution are shown in Fig. S1(a) and (b). The mixed solutions of the above 5 different azo dyes with the same amount and the same concentration (0.1 g/L) were used to evaluate the reaction activity of BM G-MgZn powders. The UV absorption spectrum of the mixed solutions measured before reaction exactly corresponds to that obtained by a simple addition of the spectrums obtained for each solution independently, as shown in Fig. S1(c). This fact indicates absence of chemical reaction between the azo dyes.
The UV absorption spectrums obtained during the degradation process are listed in Fig. S1(d). The change of the peak intensity around 470 nm was used to evaluate the degradation efficiency, as shown in Fig. 3(d). It decreases quickly, with t0 = 5.5 min, denoting a high reaction efficiency. Similarly, the reaction efficiency of the four azo dye solutions was studied separately, as shown in Fig. S2(a)–(h). The G-MgZn powders can degrade all of them in a short time. The Methyl Orange is the most difficult one to degrade with t0 value of 9.39 min, which is consistent with the degradation progress for the mixture of solutions. There is no clear relation between the degradation efficiency and the absorption peak wavelength, as shown in Fig. S2(i).
Corrosion resistance in water
Due to the low corrosion potential of Mg11, the fast corrosion by water can consume a significant amount of Mg and decrease its endurance, which is undesirable in the application of Mg in degrading the organic water contaminants. Thus, it is necessary to evaluate the water corrosion resistance of the present G-MgZn samples. The corrosion resistance of the G-MgZn alloy was examined using the polarization corrosion method. The open circuit potential (OCP) of both Mg ribbon samples and G-MgZn ribbon samples in water and azo dye solution (direct blue 6, 0.2 g/L) were measured, respectively, as is shown in Fig. 4(a). The OCP stabilized in 20 min. While the OCP in azo dye solution is slightly lower than that in water for both of the materials, the G-MgZn ribbon has a much higher OCP than that of crystalline Mg ribbon, −1.03±0.02 V for G-MgZn ribbon and −1.35±0.01 V for crystalline Mg ribbon. After the OCP stabilized, the potentiodynamic polarization behavior was measured for both materials in two liquids, which is shown in the form of log(i) versus the potential in Fig. 4(b), where i is the corrosion current density. The anode corrosion current density of G-MgZn sample in water is several times lower than that of Mg, which denotes that the G-MgZn sample has a better corrosion resistance to water than that of crystalline Mg. The inset in Fig. 4(b) shows the linear relation between corrosion current density and polarization potential. The slope of the plot yields the corrosion/reaction reactivity Δi/ΔV (reciprocal of corrosion resistance ΔV/Δi). In water, the reactivity is determined to be 0.014 and 0.033 m2/Ω for G-MgZn sample and Mg sample, respectively. In azo dye solution, the reactivity is determined to be 0.039 and 0.044 m2/Ω for G-MgZn sample and Mg sample, respectively. It should be noted that the reactivity in azo dye solutions includes two independent parts: one is the reactivity with water and the other is reactivity with azo dye. Thus, the reactivity with azo dye can be obtained by subtracting the water reactivity from the solution reactivity. The reactivity of G-MgZn ribbon with azo dye is then determined to be 0.025 m2/Ω, that is two times higher than that of Mg ribbon 0.011 m2/Ω, as shown in Fig. 4(c). These results certify that the G-MgZn has higher reactivity with azo dye but lower reactivity with water than the crystalline Mg.
To distinguish the difference in the reaction kinetics of the G-MgZn and crystalline Mg samples, the change of component elements on the surface was measured using energy-dispersive X-ray (EDX) spectroscopy after 1 hour reaction with water and azo dye solutions (Fig. 5). The EDX spectroscopy results for the initial sample, the sample reacted with water and the sample reacted with azo dye solution are shown in Fig. 5 (a), (b) and (c), respectively. As the penetration depth of electrons in EDX is about 1 μm, it is sensitive in detecting the change of the component elements on the surface. The relative change in the composition of the component elements is shown in Fig. 5(d), which is normalized by the initial state (the numerical values can be found in the Table S1 in supplementary files). After reaction with water, the concentration of Mg decreases while the concentration of Zn and Ca increases greatly. This is similar to the situation observed in biological environments8. In effect, the preferential dissolution of Mg provides a surface enrichment in Zn that also enables a self-passivation capability1,8. The increased Ca concentration may arise from the deposition of the reacted Ca(OH)2. After the reaction with azo dye solutions, however, no obvious changes of the composition were detected. This denotes that the G-MgZn powders react uniformly with azo dye without compositional alteration.
The degradation process of azo dyes, in general, usually follows the pseudo-first-order kinetic model that is based on that the reaction rate is proportional to the concentration5,28. However, we find that the degradation behavior by the BM G-MgZn powders does not follow the exponential decay function well. The reaction is very fast in the initial one minute, but relatively slow in the subsequent stage. The ball-milling procedure produces abundant nano-features on the surface of the powder particles, which gives a high effective surface area. The residual stress after ball milling further enhances the reactivity. These factors contribute to the ultra-fast reaction speed at the initial one-minute of the reaction. The decrease concentration of azo dyes, disappearance of the surface nano-features of powder particles and the deposition of the reaction products along with reaction should be responsible for the subsequent slow of the reaction speed at the late stage. So, the reaction kinetics is complex and may change along with reaction process. The fitting by exponential function used here is to get a general reaction speed to be comparable with other works but not to explain the reaction mechanism. It is worthy to study reaction kinetics in details in future.
The ball-milling procedure may produce some wear debris and contamination stemming from milling tools, even though we milled the powders at low jar-rotating speed and for a short time. The XRD pattern certifies that the amount of contaminants is too low to be detectable. As we used steel jar and balls, the main element of the wear debris and contaminants should be Fe. The crystalline Fe is also active in degrading the azo dyes but has low reaction efficiency. Thus, it should not be responsible for the high reaction efficiency observed in this work.
In summary, the present results clearly demonstrate that Mg-based glassy powders exhibit superior reaction efficiency in degrading azo dyes compared to Fe-based powders, their crystalline counterparts and crystalline Mg. The high reaction efficiency can be retained in complex environments, such as solutions with different pH values and containing various azo dyes, at low temperatures. The combination of the metastable nature and the ball-milling induced high roughness on the surface bestows the metallic glass powders with high reaction capability in degrading the azo dyes. The glassy structure of the sample allows for a high solubility of Zn, which improves the water corrosion resistance of the alloy and improves the reaction efficiency with azo dye. It is worthwhile to point out that the glassy MgZn-based powders are much more inert when exposed to the air, while the crystalline Mg powder easily undergoes autoignition which limits its applications. Generally, this functional application of Mg-Zn-Ca metallic glasses is not limited by their relatively low glass forming ability and their intrinsic brittleness is a favorable feature. This may open a new broad field for functional applications of metallic glasses.
Fabrication of BM G-MgZn-based powders
Pure elements with high purity (>99.9 wt.%) were designed with the nominal composition of Mg73Zn21.5Ca5.5 (at.%) and melted in BN crucible using an induction-melting furnace. The master alloy was polished and then remelted in a quartz tube followed by subsequent injection casting onto a rotating Cu wheel to obtain metallic glass ribbon samples with a thickness of about 40 μm. The ribbon samples were then put into an evacuated ball-milling jar for communition into powders. For the above 3 steps, the sample chambers were firstly pumped to high vacuum (<0.003 Pa) and then backfilled with high purity Ar gas for protection. The rotating speed of the jar upon ball-milling was 250 r/min. 1 min waiting interval was applied after each 5 min of milling to avoid the sample heating and then milled with inverse rotating direction. The total milling time was 2.5 hours. Some of the fresh powder samples were exposed in the air for one week to allow for oxidation. However, no detectable amounts of surface oxides can be observed using the XRD analysis. Some fresh powders were annealed under high vacuum (<0.003 Pa) at 300°C which is above the crystallization temperature determined by DSC9.
The azo dyes were purchased from Santa Cruz Biotechnology, Inc. The Direct Blue 6 azo dye solution was dissolved in deionized water forming a solution with concentration of 0.2 g/L (the same as in previous works23,27 to allow for comparison). The other four azo dyes solutions used in this work were 0.1 g/L. A decreased concentration was used to meet the maximum intensity of the UV measurement. Each time, 0.3 g of MgZn-base powders was added into 50 ml azo dye solutions. After the reaction, about 1.5 ml solution was taken out and filtered to measure the ultraviolet-visible (UV) absorption spectrum.
The atomic structure of both the ribbon and the powder samples was studied by X-ray diffractometry (XRD) (Bruker D8 Advance, Cu Kα X-ray) and high-resolution transmission electron microscopy (HRTEM) (JEOL 2010F). The powder morphology and size distribution was studied by SEM (Hitachi S-4800 Scanning Electron Microscope). The composition of the ribbon before and after reaction was determined by EDX equipped on the SEM machine. The UV absorption spectrum experiments were performed using Jasco V-650 Spectrophotometer. The OCP and polarization corrosion experiments were conducted using Hokuto Denko HZ-5000. The OCP was measured for more than 30 min to ensure its stabilization. The potential scanning rate used for polarization corrosion experiments was 2 mV/s.
Salter-Blanc, A. J. & Tratnyek, P. G. Effects of solution chemistry on the dechlorination of 1,2,3-Trichloropropane by zero-valent zinc. Environ. Sci. Technol. 45, 4073–4079 (2011).
Zhang, W. X. Nanoscale iron particles for environmental remediation: An overview. J. Nanoparticle Research 5, 323–332 (2003).
Arnold, W. A. & Roberts, A. L. Pathways of chlorinated ethylene and chlorinated acetylene reaction with Zn(0). Environ. Sci. Technol. 32, 3017–3025 (1998).
Fennelly, J. P. & Roberts, A. L. Reaction of 1,1,1-trichloroethane with zero-valent metals and bimetallic reductants. Environ. Sci. Technol. 32, 1980–1988 (1998).
Patel, R. & Suresh, S. Decolourization of azo dyes using magnesium-palladium system. .J. Hazard. Mater. 137, 1729–1741 (2006).
Kalme, S. D., Parshetti, G. K., Jadhav, S. U. & Govindwar, S. P. Biodegradation of benzidine based dye Direct Blue-6 by pseudomonas desmolyticum NCIM 2112. Bioresource Technology 98, 1405–1410 (2007).
Amin, N. K. Removal of direct blue-106 dye from aqueous solution using new activated carbons developed from pomegranate peel: Adsorption equilibrium and kinetics. J. Hazardous Materials 165, 52–62 (2009).
Zberg, B., Uggowitzer, P. J. & Löffler, J. F. MgZnCa glasses without clinically observable hydrogen evolution for biodegradable implants. Nature Mater. 8, 887–891 (2009).
Gu, X., Shiflet, G. J., Guo, F. Q. & Poon, S. J. Mg-Ca-Zn bulk metallic glasses with high strength and significant ductility. J. Mater. Res. 20, 1935–1938 (2005).
Scully, J. R., Gebert, A. & Payer, J. H. Corrosion and related mechanical properties of bulk metallic glasses. J. Mater. Res. 22, 302–313 (2007).
Song, G. L. & Atrens, A. Corrosion mechanisms of magnesium alloys. Adv. Eng. Mater. 5, 837–858 (2003).
Kumar, G., Tang, H. X. & Schroers, J. Nanomoulding with amorphous metals. Nature 457, 868–872 (2009).
Greer, A. L. Metallic glasses. Science 267, 1947–1953 (1995).
Johnson, W. L. Bulk glass-forming metallic alloys: science and technology. MRS Bull. 24, 42–56 (1999).
Inoue, A. & Takeuchi, A. Recently development and application products of bulk glassy alloys. Acta Mater. 59, 2243–2267 (2011).
Wang, W. H. Bulk metallic glasses with functional physical properties. Adv. Mater. 21, 4524–4544 (2009).
Inoue, A. Stabilization of metallic supercooled liquid and bulk amorphous alloys. Acta Mater. 48, 279–306 (2000).
Pang, S. J., Zhang, T., Asami, K. & Inoue, A. Synthesis of Fe-Cr-Mo-C-B-P bulk metallic glasses with high corrosion resistance. Acta Mater. 50, 489–497 (2002).
Peter, W. H. et al. Localized corrosion behavior of a zirconium-based bulk metallic glass relative to its crystalline state. Intermetallics 10, 1157–1162 (2002).
Baiker, A. Metallic glasses in heterogeneous catalysis. Faraday Discuss. Chem. Soc. 87, 239–251 (1989).
Katona, T. & Molnar, A. Amorphous alloy catalysis. J. Catal. 153, 333–343 (1995).
Carmo, M., Sekol, R. C., Ding, S., Kumar, G., Schroers, J. & Taylor, A. D. Bulk metallic glass nanowire architecture for electrochemical applications. ACS NANO 5, 2979–2983 (2011).
Zhang, C. Q., Zhang, H. F., Lv, M. Q. & Hu, Z. Q. Decolorization of azo dye solution by Fe-Mo-Si-B amorphous alloy. J. Non-Cryst. Solids 356, 1703–1706 (2010).
Lin, B., Bian, X., Wang, P. & Luo, G. Application of Fe-based metallic glasses in wastewater treatment. Mater. Sci. Eng. B 177, 92–95 (2012).
Agrawal, A. & Tratnyek, P. G. Reduction of nitro aromatic compounds by zero-valent iron metal. Environ. Sci. Technol. 30, 153–160 (1996).
Cao, J., Wei, L., Huang, Q., Wang, L. & Han, S. Reducing degradation of azo dye by zero-valent iron in aqueous solution. Chemosphere 38, 565–571 (1999).
Wang, J. Q. et al. Rapid degradation of azo dye by Fe-based metallic glass powder. Adv. Funct. Mater. 10.1002/adfm.201103015.
Shu, H. Y., Chang, M. C., Yu, H. H. & Chen, W. H. Reduction of an azo dye Acid Blue-24 solution using synthesized nanoscale zero-valent iron particles. J. Colloid Interface Sci. 314, 89–97 (2007).
The authors appreciate the help and discussions from Dr. T. Fujita, Dr. J.L. Kang and Dr. X.B. Ge. This work was supported by World Premier International Research Center Initiative (WPI), MEXT, Japan.
The authors declare no competing financial interests.
Electronic supplementary material
About this article
Cite this article
Wang, JQ., Liu, YH., Chen, MW. et al. Excellent capability in degrading azo dyes by MgZn-based metallic glass powders. Sci Rep 2, 418 (2012). https://doi.org/10.1038/srep00418
This article is cited by
The catalytic performance of Cu46Zr47-xAl7Yx amorphous ribbons in the degradation of AO II dye wastewater
Environmental Science and Pollution Research (2021)
Preparation, characterization and application of Fe72Cu1Co5Si9B13 metallic glass catalyst in degradation of azo dyes
Journal of Materials Science: Materials in Electronics (2021)
Co-Free High-Entropy Alloys Powders Immobilized by Electrospray and Microfluidics for Decolorization of Azo Dye
Acta Metallurgica Sinica (English Letters) (2020)
Excellent long-term reactivity of inhomogeneous nanoscale Fe-based metallic glass in wastewater purification
Science China Materials (2020)
International Journal of Minerals, Metallurgy, and Materials (2019)