Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Deformation of the moving magnetic skyrmion lattice in MnSi under electric current flow


Topological defects are found ubiquitously in various kinds of matter, such as vortices in type-II superconductors, and magnetic skyrmions in chiral ferromagnets. While knowledge on the static behavior of magnetic skyrmions is accumulating steadily, their dynamics under forced flow is still a widely open issue. Here, we report the deformation of the moving magnetic skyrmion lattice in MnSi under electric current flow observed using small-angle neutron scattering. A spatially inhomogeneous rotation of the skyrmion lattice, with an inverse rotation sense for opposite sample edges, is observed for current densities greater than a threshold value jt ~ 1 MA m2 (106 A m2). Our result show that skyrmion lattices under current flow experience significant friction near the sample edges due to pinning, this being a critical effect that must be considered for anticipated skyrmion-based applications at the nanoscale.


Topological defects, i.e., defects that cannot be annihilated by continuous deformation, are found ubiquitously in various kinds of matter, such as screw dislocation in crystals1,2,3, defect in nematic liquid crystal4,5,6, and quantum vortices in superfluid and type-II superconductor7,8,9,10,11,12,13. A magnetic skyrmion, one of such topological defects, is a swirling spin texture characterized by a discrete topological number, called the skyrmion number. Such topologically nontrivial states of matter were first theoretically predicted in nonlinear field theory14,15, and subsequently in chiral magnets16. Experimentally, magnetic skyrmions often condense into triangular-lattice, observed as six-fold magnetic Bragg reflections in small-angle neutron scattering (SANS), first discovered by Mühlbauer et al. in the prototypical chiral magnet MnSi17. To date, triangular skyrmion-lattice structures are widely confirmed in various magnets ranging from metallic to insulating compounds18,19,20,21,22,23, and also by various techniques such as Lorentz transmission electron microscopy (TEM) and magnetic force microscopy24,25.

There are several prominent characteristics of magnetic skyrmions that make them quite intriguing for fundamental, as well as technological application viewpoints. One is its topological protection; once created, the skyrmion can hardly be annihilated18. Hence, there is a possibility for the magnetic skyrmion to be used as a robust information storage/carriage unit in future spintronics devices. In metallic skyrmion compounds, there is another important characteristic, namely its strong coupling to electric current flow. The electric current density required to realize the skyrmion-lattice motion is remarkably small at j ~ 1 MA m−2 (106 A m−2), compared to that required to move magnetic domain boundaries in conventional magnetic materials j ≥ 1 GA m−2 (109 A m−2)26,27,28,29. The potential for controlling magnetic skyrmions with such a low current density, together with their topologically protected nature, makes spintronics application promising30. Hence, magnetic skyrmions continue to attract strong attention, and remain under intense scrutiny for elucidating their dynamical behavior under electric current.

A number of reports have appeared to date on the motion of magnetic skyrmions under electric current flow. In the pioneering study of Jonietz et al. using SANS, a rotation of the skyrmion lattice in MnSi was detected for an electric current density greater than the threshold value jt ~ 1 MA m−231. There, it was argued that the electric current flow alone introduces translational motion only via spin transfer torques, which cannot be detected by SANS. Hence, a thermal gradient was intentionally applied in their experiment, which provides spatial inhomogeneity of the spin transfer torque. Indeed, the skyrmion-lattice rotation was observed only when both the current flow and thermal gradient were present. Nonetheless, by careful examination of the presented data, it can be seen that the skyrmion-lattice peaks are significantly broadened under the electric current flow, the origin of which was not discussed.

Skyrmion-lattice motion under thermally homogeneous conditions was studied in the other works. From Hall-resistivity measurements on MnSi, the skyrmions move in the direction of the electric current above a critical current density jt ~ 0.5 MA m−2, while the emergent electric field is transverse to the current32,33. From a Lorentz TEM study of FeGe, the skyrmion lattice was observed to ‘disappear’ as the electric current exceeded a threshold value, indicating the skyrmion lattice to move much faster than the Lorentz TEM time frame34. These studies show that the electric current flow induces the skyrmion-lattice motion. However, important microscopic information, such as the skyrmion-lattice deformation, under thermally homogeneous conditions remains largely unexplored.

Here, we investigate the deformation of the moving magnetic skyrmion lattice under an electric current flow using the SANS technique, paying careful attention towards keeping any thermal gradient as small as experimentally achievable. We observe clearly a broadening of the skyrmion-lattice-reflection peaks for j > jt, indicating the skyrmion lattice to deform considerably when the lattice starts to flow translationally. We further find that the peak broadening is due to a spatially inhomogeneous rotation of the skyrmion lattice; by measuring opposing-sample edges, we observed a counter-rotating behavior of the skyrmion lattice. The observed rotation appears to be not continuous but fixed angle in the SANS measurement time frame (20 min). While the rotation direction does not change under inversion of the external magnetic field, it does revert when the electric current direction is reversed. Finally, the peak broadening and corresponding lattice rotation remain finite even after the current is turned off, indicating a plastic deformation of the skyrmion lattice under the force exerted by the electric current.


Peak broadening of skyrmion reflection above j t

Representative SANS patterns measured at NG7 SANS instrument using the experimental setting in Fig. 1 are shown in Fig. 2a–d. They were measured by imaging an entire horizontal cross-section of the sample, as shown in Fig. 1c. A photograph of the sample mount and its schematic illustration are shown in Fig. 1a, b, respectively. Figure 2a, b show the skyrmion reflections observed at the two temperatures, T = 28.3 K and 28.6 K, respectively, under Bext = 0.2 T and j = 0. The six-fold magnetic reflections characteristic of the skyrmion lattice were observed in a temperature range of 28 K < T < 29.2 K at Bext = 0.2 T. These observations are identical to those in the earlier works17,31.

Fig. 1

Experimental setting of small angle neutron scattering (SANS) with keeping any thermal gradient as small as experimentally achievable. a, b Photograph (a) and schematic drawing (b) of the MnSi sample and sample mount for the NG7 experiment. The incident neutron beam was shaped to be 2.0 mm (width) × 1.0 mm (height) by an aperture. c, d Schematic illustration of the beam illumination area for investigating the peak broadening (c) and counter-rotating behavior at the sample edges (d) of the skyrmion-lattice peaks

Fig. 2

Small angle neutron scattering (SANS) data for investigating the peak broadening of the skyrmion reflection. ad SANS measured at Bext = 0.2 T. The skyrmion reflections were measured at T = 28.3 K (28.6 K) under j = 0 (2.7 MA m−2), respectively. All data were measured for 10 min. When the intensities of the six skyrmion reflections are not equivalent, the sample is slightly misoriented away from the Bragg position. The azimuthal width direction is indicated by the arrow in panel a. qx and qy stand for the reciprocal lattice space directions

Figure 2c, d show the SANS patterns obtained at j = 2.7 MA m−2 and Bext = 0.2 T. By comparing with the zero-current-flow counterparts in Fig. 2a, b, a considerable azimuthal broadening of the skyrmion-lattice peaks was observed. The peak broadening is temperature dependent at j = 2.7 MA m−2; the width is considerably larger at T = 28.3 K compared to that at T = 28.6 K. This result clearly indicates the significant deformation of the skyrmion lattice under large electric current. In stark contrast, no intrinsic peak broadening in radial direction was observed under the electric current.

To examine quantitatively the current dependence of the skyrmion-lattice peaks, in Fig. 3a, b, we show, respectively, the total scattered SANS intensity and azimuthal spot widths as functions of current density at three selected temperatures and Bext = 0.2 T. The spot width remains almost constant in the low current density region (j < jt ~ 1 MA m−2) for all measured temperatures. At T = 28.3 K, the width shows a steep increase for j > jt. This clearly confirms the existence of a threshold current density for skyrmion-lattice deformation. It may be noted that the value of jt is in good agreement with the current density above which skyrmion-lattice motion was detected in the earlier studies31,32. Hence, the peak broadening detected above jt in the present study is a direct consequence of skyrmion-lattice motion driven by the electric current. In stark contrast to the skyrmion-lattice peaks, we observed no peak broadening for the reflections in the helical phase at Bext = 0 up to 1.67 MA m−2, as shown by the open triangular symbol in Fig. 3b.

Fig. 3

Current-density and temperature dependences of the skyrmion reflections for investigating the peak broadening of the skyrmion reflection. ac, Current-density dependences of the total scattered small angle neutron scattering (SANS) intensity (a) and the azimuthal spot widths (b and c) of the skyrmion reflections measured at three temperatures. Here, we use 1σ standard deviation as error bar. The temperature used in ac is the sensor temperature, and therefore not the true temperature estimated from the ordering temperature of the helical phase. Thus, the increase (decrease) of the intensity at T = 28.3 K (29.0 K and 28.6 K) under the high electric current is due to sample heating. For the measurement of the negative current density, we reset the peak broadening of the skyrmion reflection at zero current density once by heating the sample above the phase transition temperature. In a and cf, data are measured at Bext = 0.2 T. In b the azimuthal width of the skyrmion (Bext = 0.2 T) and helical (Bext = 0) reflections at T = 28.6 K measured by the thicker sample are also shown. df Temperature dependences of the total scattered SANS intensity (d) and azimuthal widths (e, f) of the skyrmion reflections at each current density. In c and f additionally, the dependence of the width after applying j = 2.7 MA m−2 is shown. The broadening of the skyrmion reflection persisted for more than one hour after the applied current density was removed

Plastic deformation of skyrmion lattice

Once induced by the electric current, the broadening of the skyrmion-lattice peaks persists, even after the electric current is removed. In Fig. 3c, starting from the pristine state, the width increases monotonically up to j = 2.7 MA m−2 above jt, whereas when lowering the current, the width stays almost the same down to j = 0. This clearly indicates that the skyrmion lattice remembers the deformation generated in the driven state. In other words, the skyrmion lattice locally deforms like plastic matter when driven under electric current. This plastic deformation may be due to impurity pinning.

Figure 3d, e show the temperature dependences of, respectively, the total scattered SANS intensity and azimuthal spot widths at fixed current density. At j = 2.7 MA m−2, the width shows a significant temperature dependence below 28.5 K; it monotonically increases as temperature is decreased. Below jt, the width shows negligible temperature dependence. Figure 3f shows the temperature dependence of the width at j = 0, measured with decreasing temperature, after having applied the current density 2.7 MA m−2 at T = 28.6 K. Independent of the temperature, the spot widths remain broadened compared with the pristine state at j = 0 after the current ramping, confirming the robust memory effect for the skyrmion-lattice deformation.

Spatially inhomogeneous rotation of skyrmion lattice

To investigate the origin of the broadening of the skyrmion reflections, we performed SANS measurements on the left-edge (+) or right-edge (−) of the sample, as shown schematically in Fig. 1d. The size of the neutron illumination area is approximately 0.2 mm (width) × 1.0 mm (height). The SANS patterns obtained at T = 28.6 K and Bext = −0.2 T without electric current are shown in Fig. 4a, b for the left-edge and right-edge, respectively. The observed patterns are identical for the two edges, and in good agreement with the data shown in Fig. 2b. In marked contrast to the zero-current condition, under j = 2.7 MA m−2 the reflection patterns taken from the left-edge and right-edge parts exhibit counterclockwise and clockwise rotations, respectively, as shown in Fig. 4c, d.

Fig. 4

Small angle neutron scattering (SANS) data for investigating counter-rotating behavior at the sample edges of the skyrmion-lattice peaks. SANS measured from the left-edge (+) or right-edge (−) of the sample. ah, The skyrmion reflections at T = 28.6 K, respectively, measured at Bext = −0.2 (0.2 T), j = 0 (2.7 MA m−2), and at the left-edge (right-edge). All data were measured for 20 minutes. Dashed lines are guides to eye for the peak positions of the skyrmion reflections in pristine condition. i, j The current-density and magnetic-field dependences of the averaged rotation angles of the skyrmion reflections at T = 28.6 K at left-edges and right-edges. The circle and triangle denote the data at Bext = −0.2 and 0.2 T, respectively. The dashed lines are guides to eye. k Schematic illustration of the skyrmion-lattice rotation above jt. Blue and red circles stand for the pristine and moved skyrmions, respectively. Black arrows and vdom explain the velocity of the skyrmion-lattice domain near the sample edges

Next, the effect of inverting the current and magnetic-field directions was investigated. Figure 4e, f show data taken under an inverted magnetic field Bext = 0.2 T. Apparently, the rotation direction does not change by inverting Bext. On the other hand, the inversion of the current direction (from j = +2.7 to −2.7 MA m−2) results in a sign change of the rotation angle, as clearly seen by comparing Fig. 4g, h (j = −2.7 MA m−2) with Fig. 4c, d (j = +2.7 MA m−2). This indicates that the skyrmion-lattice rotation observed in the thermally homogeneous condition depends not on the magnetization direction, but only on the current direction. It should be noted that the transverse translational motion is due to the scalar spin chirality, which depends on the third order of the magnetization density \({\vec{\mathbf{M}}}({\vec{\mathbf{R}}})\), whereas the longitudinal translational mode along the electric current is due to the dissipative tensor which is in the second order in \({\vec{\mathbf{M}}}({\vec{\mathbf{R}}})\)35,36. The independence of the observed rotation angle to the magnetization direction thus indicates that the rotation effect should be attributed to the longitudinal translational motion of the skyrmions under the electric current. In the earlier study of Jonietz et al., the rotation of the magnetic skyrmion lattice was found under the electric current flow in the thermal gradient31. Zhang et al. recently found the continuous rotation of the magnetic skyrmion lattice by applying only the magnetic field gradient37. In these two studies, the gradient of either temperature or magnetic field is the key to induce skyrmion lattice rotation. In stark contrast, the rotation observed in the present study is induced solely by electric current without temperature nor magnetic-field gradient. It should be also emphasized that direction of the rotations detected in the earlier studies depend on the magnetic-field direction, indicating that the origin of the skyrmion lattice rotations are related to the time-reversal-variant scalar-spin chirality. On the other hand, independent rotation direction of the magnetic field direction observed in the present study indicates that the rotation is due to the time-reversal-invariant term, the dissipative tensor. Thus, we conclude that the origin of the skyrmion lattice rotation in this study is essentially different with those in the earlier studies. The averaged rotation angles for the six skyrmion reflections are plotted in Fig. 4i, j for the left-edge and right-edge parts, respectively. A counter-rotating behavior that is clearly antisymmetric around j = 0 is observed for the two edge positions with a rotation angle of approximately ±5 degrees for j = 2.7 MA m−2 at T = 28.6 K and Bext = ±0.2 T. Hence, we conclude that the peak broadening is mainly due to a spatially inhomogeneous rotation of the skyrmion lattice, with counter-rotating behavior for the left-edge and right-edge. It should be further noted that the sum of absolute rotation angle at each edge is in semiquantitative agreement with the overall broadening observed from imaging across the whole sample (Fig. 1c), supporting our conclusion.


Plausibly related to the present observation is a recent magneto-optical Kerr study of the motion of single skyrmions under current flow in a CoFeB-based trilayer, where the velocity of the skyrmion near the edge of the sample is reported to be 40% less than that at the center of the sample38. Assuming similar slow skyrmion flow near the edges of the bulk MnSi sample, we expect that a shear flow of the skyrmion-lattice domains may appear in our sample where the velocity of the skyrmion-lattice domains is faster in the middle region only for a short time after applying electric current. After some time, the rotational torque generated by the shear flow (Fig. 4k) will be balanced by the restoring force of the skyrmion lattice, and hence the lattice may be deformed, resulting in the counter-rotating behavior observed in the present study. In other words, the skyrmion lattice flows with a shear component plausibly due to significant friction near the edges. From the rotation direction of the skyrmion lattice relative to the direction of the electric current as shown in Fig. 4c–h, we can deduce that the skyrmion motion in MnSi is along the charge current not the electron current. This is in agreement with the conclusion based on the topological Hall resistivity measurement that macroscopically the skyrmions in MnSi drift in the same direction as the electric current flows (K. Everschor, private communication32).

As discussed above, the slower skyrmion flow, or in other words, friction effect, near the sample edges may be the key for the observed skyrmion-lattice rotation. We speculate that such slower flow of the skyrmions is related to the enhanced pinning near the edges. It has been reported that the magnetic skyrmions are confined inside the sample by the confining potential, resulting in stronger pining effect acting on the skyrmions near the edge, as discussed in ref. 39. We also expect that in reality the sample would have inevitable structural/chemical disorder at the sample edge induced by the cutting and polishing procedure, which results in larger number of pinning sites near the sample edge. Thirdly, as a more physical origin of enhanced pinning, we may expect an effect of additional Dzyaloshinskii-Moriya (DM) interactions originating from the lack of inversion symmetry at surface; for Bloch-type skyrmions, such as those in MnSi, the surface DM interaction would be added on the intrinsic (bulk) DM interaction, and hence the number of skyrmions might increase near sample edges, resulting in enhanced pinning effect. At present, however, we are not sure which of these effects, if any, are deterministic for the friction effect near edges inducing skyrmion lattice rotation observed in the present study. Further study, in particular from the theoretical viewpoint, is definitely necessary to elucidate this apparently interesting issue.

Another remaining issue is why the friction effect was seen in such a large (mm sized) region away from the sample edge. In the simple particle model, where skyrmions are dense and move randomly, this edge effect works only near the edge (~1 nm). We speculated that the lattice formation is the key to propagate the friction effect in the mm sized sample. For quantitative understanding of the generation of a shear stress deeper inside the sample, however, a numerical simulation including inter-skyrmion interactions that takes into account friction amongst the skyrmions, as well as the robustness of their formed triangular lattice, is required.

Lastly, we comment on the effect of the thermal gradient. Despite our effort to minimize the thermal gradient, a small but finite gradient remained along the electric-current direction. This thermal gradient was pointed out as the origin of the skyrmion-lattice rotation in ref. 31,40 However, since the rotational motion due to the spin transfer torque under the thermal gradient parallel to the electric current should depend on the macroscopic magnetization direction, one expects that the sign of the rotation angle is switched when the external magnetic field is reversed. We clearly found that the rotation angle at each edge does not change upon inversion of the magnetic-field direction, which excludes the possibility of the remaining thermal gradient giving rise to the skyrmion-lattice rotation in the present setup.

In summary, we have used SANS to study skyrmion-lattice motion in bulk MnSi under electric current flow in a thermally homogenous condition. The azimuthal width of the skyrmion-lattice peaks shows significant broadening above a threshold current density jt ~ 1 MA m−2. We show that this peak broadening originates from a spatially inhomogeneous rotation of the skyrmion lattice, that shows opposite senses of rotation at the sample edges. An intriguing memory effect was also observed for the peak broadening and the corresponding rotation of the skyrmion lattice, indicating that the driven skyrmion lattice considerably deforms due to the friction near the sample edges.


Single crystal growth and sample quality

MnSi single crystal was grown by the Czochralski method. The sample quality is checked by the electric resistivity measurement. The helical ordering anomaly was detected at ~29 K. The residual resistivity ratio R300K/R1.9K is ~53, which is the same order of magnitude as those of the samples used in the earlier works31,32. Details of electric resistivity measurement can be found in the Supplementary Note 1.

Small angle neutron scattering under electric current flow

SANS experiments were carried out at NG7 SANS instrument in National Institute of Standards and Technology and SANS-II SANS instrument in Paul Scherrer Institut. The single-crystal-MnSi samples were cut in a rectangular shape of 1.4 mm (width) × 7.5 mm (height) × 0.4 mm (thickness) for NG7. The incident neutron wavelength was λi = 6 Å with Δλ/λi = 14%. Full details of our experimental setting can be found in the Supplementary Note 2. The analysis methods of the SANS data and the other SANS data are shown in the Supplementary Note 3 and 4, respectively. To further limit any temperature inhomogeneity in the measured region, and also to check the sample position dependence, only a small part of the sample was illuminated by using a very narrow beam of 2.0 mm (width) × 1.0 mm (height). An electric current up to 2 A (j = 3.6 MA m−2) was applied along the [0 0 1] direction. For such a large electric current, the sample temperature deviates from the sensor temperature slightly due to self-heating. Hence, we estimated the sample temperature using the ordering temperature of the zero-field helical phase; the maximum difference between the sensor and sample temperatures was 0.16 K at j = 2.7 MA m−2. The temperature gradient along the current-flow direction was estimated by measuring the position dependence of the ordering temperature, and was confirmed to be less than 0.035 K mm−1 at the sample region investigated in the present study under j = 2.7 MA m−2. The thermal gradient perpendicular to the current-flow direction was also confirmed to be approximately 0.03 K mm−1 under j = 2.7 MA m−2. This is at least one order of magnitude smaller than in the previous experiment31. In Supplementary Note 5 and 6, the detailed methods how to determine the thermal gradient inside the sample are shown. The sample mount was installed into a horizontal-field magnet with the magnetic field applied along [1 –1 0] parallel to the incident neutron beam. Bext stands for the external magnetic field without correcting for the magnetic permeability of the MnSi sample.

Plastic deformation of the skyrmion lattice

From the peak width of the skyrmion reflection, the domain size is small with less than 10 skyrmion unit cells. It is expected that the skyrmion-lattice domain deforms with dislocation slipping along the domain boundary. This kind of deformation is called plastic deformation41. Thus, in this paper, we use the terminology of ‘plastic deformation’ to explain the observed shear distortion of the skyrmion lattice. Details of the model of the plastic deformation can be found in the Supplementary Note 7.


Certain commercial equipment, instruments, or materials are identified in this paper to foster understanding. Such identification does not imply recommendation or endorsement by the National Institute of Standards and Technology, nor does it imply that the materials or equipment identified are necessarily the best available for the purpose.

Data availability

The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.


  1. 1.

    Frank, F. C. Crystal growth and dislocations. Adv. Phys. 1, 91–109 (1952).

    ADS  Article  Google Scholar 

  2. 2.

    Griffin, L. J. Observation of unimolecular growth steps on crystal surfaces. Philos. Mag. 41, 196–199 (1950).

    Article  Google Scholar 

  3. 3.

    Ulvestad, A. et al. Topological defect dynamics in operando battery nanoparticles. Science 348, 1344–1347 (2015).

    ADS  Article  Google Scholar 

  4. 4.

    de Gennes, P. G. & Prost, J. The Physics of Liquid Crystals. (Oxford University Press, Oxford, 1995).

    Book  Google Scholar 

  5. 5.

    Tóth, G., Denniston, C. & Yeomans, J. M. Hydrodynamics of topological defects in nematic liquid crystals. Phys. Rev. Lett. 88, 105504 (2002).

    ADS  Article  Google Scholar 

  6. 6.

    Araki, T., Buscaglia, M., Bellini, T. & Tanaka, H. Memory and topological frustration in nematic liquid crystals confined in porous materials. Nat. Mater. 10, 303–309 (2011).

    ADS  Article  Google Scholar 

  7. 7.

    sOsborne, D. V. The rotation of liquid helium II. Proc. Phys. Soc. A 63, 909–912 (1950).

    ADS  Article  Google Scholar 

  8. 8.

    Abo-Shaeer, J. R., Raman, C., Vogels, J. M. & Ketterle, W. Observation of vortex lattices in Bose-Einstein condensates. Science 292, 476–479 (2001).

    ADS  Article  Google Scholar 

  9. 9.

    Brandt, E. H. The flux line lattice in superconductors. Rep. Prog. Phys. 58, 1465–1594 (1995).

    ADS  Article  Google Scholar 

  10. 10.

    Yaron, U. et al. Structural evidence for a two-step process in the depinning of the superconducting flux-line lattice. Nature 376, 753–755 (1995).

    ADS  Article  Google Scholar 

  11. 11.

    D’Anna, G., Gammel, P. L., Safar, H., Alers, G. B. & Bishop, D. J. Vortex-motion-induced voltage noise in Yba2Cu3O7−δ single crystals. Phys. Rev. Lett. 75, 3521–3524 (1995).

    ADS  Article  Google Scholar 

  12. 12.

    Pardo, F., de la Cruz, F., Gammel, P. L., Bucher, E. & Bishop, D. J. Observation of smectic and moving-Bragg-glass phases in flowing vortex lattices. Nature 396, 348–350 (1998).

    ADS  Article  Google Scholar 

  13. 13.

    Paltiel, Y. et al. Dynamic instabilities and memory effects in vortex matter. Nature 403, 398–401 (2000).

    ADS  Article  Google Scholar 

  14. 14.

    Skyrme, T. H. R. non-linear field theory. Proc. Roy. Soc. Lond. A 260, 127–138 (1961).

    ADS  MathSciNet  MATH  Google Scholar 

  15. 15.

    Derrick, G. H. Comments on nonlinear wave equations as models for elementary particles. J. Math. Phys. 5, 1252–1254 (1964).

    ADS  MathSciNet  Article  Google Scholar 

  16. 16.

    Bogdanov, A. N. & Yablonskii, D. A. Thermodynamically stable “vortices” in magnetically ordered crystals. The mixed state of magnets. Sov. Phys. LETP 68, 101–103 (1989).

    Google Scholar 

  17. 17.

    Mühlbauer, S. et al. Skyrmion lattice in a chiral magnet. Science 323, 915–919 (2009).

    ADS  Article  Google Scholar 

  18. 18.

    Nagaosa, N. & Tokura, Y. Topological properties and dynamics of magnetic skyrmions. Nat. Nanotechnol. 8, 899–911 (2013).

    ADS  Article  Google Scholar 

  19. 19.

    Neubauer, A. et al. Topological Hall effect in the A phase of MnSi. Phys. Rev. Lett. 102, 186602 (2009).

    ADS  Article  Google Scholar 

  20. 20.

    Bauer, A. & Pfleiderer, C. Magnetic phase diagram of MnSi inferred from magnetization and ac susceptibility. Phys. Rev. B 85, 214418 (2012).

    ADS  Article  Google Scholar 

  21. 21.

    Seki, S., Yu, X. Z., Ishiwata, S. & Tokura, Y. Observation of skyrmions in a multiferroic material. Science 336, 198–201 (2012).

    ADS  Article  Google Scholar 

  22. 22.

    Adams, T. et al. Long-wavelength helimagnetic order and skyrmion lattice phase in Cu2OseO3. Phys. Rev. Lett. 108, 237204 (2012).

    ADS  Article  Google Scholar 

  23. 23.

    Seki, S. et al. Formation and rotation of skyrmion crystal in the chiral-lattice insulator Cu2OseO3. Phys. Rev. B 85, 220406 (2012).

    ADS  Article  Google Scholar 

  24. 24.

    Yu, X. Z. et al. Real-space observation of a two-dimensional skyrmion crystal. Nature 465, 901–904 (2010).

    ADS  Article  Google Scholar 

  25. 25.

    Milde, P. et al. Unwinding of a skyrmion lattice by magnetic monopoles. Science 340, 1076–1080 (2013).

    ADS  Article  Google Scholar 

  26. 26.

    Myers, E. B., Ralph, D. C., Katine, J. A., Louie, R. N. & Buhrman, R. A. Current-induced switching of domains in magnetic multilayer devices. Science 285, 867–870 (1999).

    Article  Google Scholar 

  27. 27.

    Grollier, J. et al. Switching a spin valve back and forth by current-induced domain wall motion. Appl. Phys. Lett. 83, 509–511 (2003).

    ADS  Article  Google Scholar 

  28. 28.

    Tsoi, M., Fontana, R. E. & Parkin, S. S. P. Magnetic domain wall motion triggered by an electric current. Appl. Phys. Lett. 83, 2617–2619 (2003).

    ADS  Article  Google Scholar 

  29. 29.

    Yamanouchi, M., Chiba, D., Matsukura, F. & Ohno, H. Current-induced domain-wall switching in a ferromagnetic semiconductor structure. Nature 428, 539–542 (2004).

    ADS  Article  Google Scholar 

  30. 30.

    Fert, A., Cros, V. & Sampaio, J. Skyrmions on the track. Nat. Nanotechnol. 8, 152–156 (2013).

    ADS  Article  Google Scholar 

  31. 31.

    Jonietz, F. et al. Spin transfer torques in MnSi at ultralow current densities. Science 330, 1648–1651 (2010).

    ADS  Article  Google Scholar 

  32. 32.

    Schulz, T. et al. Emergent electrodynamics of skyrmions in a chiral magnet. Nat. Phys. 8, 301–304 (2012).

    Article  Google Scholar 

  33. 33.

    Zang, J., Mostovoy, M., Han, J. H. & Nagaosa, N. Dynamics of skyrmion crystals in metallic thin films. Phys. Rev. Lett. 107, 136804 (2011).

    ADS  Article  Google Scholar 

  34. 34.

    Yu, X. Z. et al. Skyrmion flow near room temperature in an ultralow current density. Nat. Commun. 3, 988 (2012).

    ADS  Article  Google Scholar 

  35. 35.

    Everschor, K., Garst, M., Duine, R. A. & Rosch, A. Current-induced rotational torques in the skyrmion lattice phase of chiral magnets. Phys. Rev. B 84, 064401 (2011).

    ADS  Article  Google Scholar 

  36. 36.

    Thiele, A. A. Steady-state motion of magnetic domains. Phys. Rev. Lett. 30, 230–233 (1972).

    ADS  Article  Google Scholar 

  37. 37.

    Zhang, S. L. et al. Manipulation of skyrmion motion by magnetic field gradients. Nat. Commun. 9, 2115 (2018).

    ADS  Article  Google Scholar 

  38. 38.

    Jiang, W. et al. Direct observation of the skyrmion Hall effect. Nat. Phys. 13, 162–169 (2017).

    Article  Google Scholar 

  39. 39.

    Iwasaki, J., Koshibae, W. & Nagaosa, N. Colossal spin transfer torque effect on skyrmion along the edge. Nano Lett. 14, 4432–4437 (2014).

    ADS  Article  Google Scholar 

  40. 40.

    Everschor, K. et al. Rotating skyrmion lattices by spin torques and field or temperature gradients. Phys. Rev. B 86, 054432 (2012).

    ADS  Article  Google Scholar 

  41. 41.

    Kaplan, W. D. The mechanism of crystal deformation. Science 349, 1059–1060 (2015).

    ADS  Article  Google Scholar 

Download references


The authors thank P. D. Butler, K. Everschor, M. Garst, A. Rosch, T. Hanaguri, W. Koshibae, J. Barker, A.P. Tsai, K. Yamauchi and T. Oguchi for the fruitful discussions. This work was in part supported by Grants-in-Aids for Scientific Research (No. 24224009, 26103006, 16H04007, 17K14327, 17K18744, and 18H03676) from the Ministry of Education, Culture, Sports, Science and Technology (MEXT), Japan and by the Research Program for CORE lab of “Dynamic Alliance for Open Innovation Bridging Human, Environment and Materials” in “Network Joint Research Center for Materials and Devices”. The Swiss National Science Foundation (SNF) Sinergia network “NanoSkyrmionics” (Grant No. CRSII5-171003), the SNF projects 153451 and 166298, and the European Research Council project CONQUEST. N.N. was supported by JST CREST Grant Number JPMJCR1874.

Author information




The small angle neutron scattering was carried out by D.O., M.Bl., J.S.W., Q.Y., J.K., G.N., Z.Q.I., I.Z., M.Ba., D.H., Y.N. and T.J.S. Experimental results were analyzed by D.O., M.Bl., J.S.W. and J.D.R. The growth of single crystal was performed by A.K. and Y.Ta. The theoretical discussion was done by D.O., J.S.W., H.M.R., S.H., J.I., N.N. and T.J.S. The paper was written by D.O., M.Bl., J.S.W., H.M.R., N.N., Y.Ta., Y.To., Y.N. and T.J.S. This study was planned by D.O., J.S.W., H.M.R., N.N., Y.Ta., Y.To., Y.N. and T.J.S.

Corresponding author

Correspondence to D. Okuyama.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Okuyama, D., Bleuel, M., White, J.S. et al. Deformation of the moving magnetic skyrmion lattice in MnSi under electric current flow. Commun Phys 2, 79 (2019).

Download citation


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing