Rhenium diselenide (ReSe2) has recently garnered great research interest due to its distorted 1T structure, anisotropic physical properties, and applications in polarization-sensitive photodetectors. However, ReSe2 synthesized by chemical vapor deposition (CVD) is usually a multilayer/polycrystalline material containing numerous grain boundaries, thereby hindering its further applications. Here we describe the direct CVD growth of high-quality monolayer ReSe2 single crystals with a parallelogram shape arising from its anisotropic structure on a gold foil substrate. In particular, we use low-energy electron microscopy/diffraction combined with scanning tunneling microscopy/spectroscopy to determine the atomic-scale structure, domain orientation/boundaries, and band features of monolayer ReSe2 flakes grown directly on gold foils. This work may open new opportunities for the direct synthesis and in situ characterization of CVD-grown monolayer ReSe2.
Inspired by graphene research1,2,3, researchers in science and technology have recently shown increasing interest in two-dimensional (2D) monolayer transition metal dichalcogenides (TMDs, e.g., MoS2 and WS2) due to their rich physical, chemical, and electronic properties associated with the dimensionality effect4,5,6,7,8,9,10. Rhenium dichalcogenides (ReX2, X = S or Se) are an emerging class of TMDs which, unlike high-symmetry hexagonal TMDs, crystallize in a distorted CdCl2 structure with a triclinic symmetry due to charge decoupling from an additional valence electron in each Re atom11, 12. The distortion of the crystal structure affords weak interlayer coupling13,14,15, making bulk ReX2 behave as electronically and vibrationally decoupled monolayers. Accordingly, the transition from indirect to direct band gap is not observed in three-atom-thick ReX2, which is in sharp contrast with hexagonal semiconducting TMDs. More intriguingly, ReX2 exhibits a low-symmetry crystal lattice owing to its distorted structure, and the resulting anisotropic electrical and optical properties16,17,18,19,20 enable applications in polarization-sensitive photodetectors and integrated polarization controllers (such as wave plates)21,22,23.
Driven by such intriguing properties, researchers have devoted substantial efforts to synthesize monolayer or few-layer ReSe2 through various routes, including mechanical exfoliation12, 19, 20 and chemical vapor deposition (CVD)22, 24, 25. Notably, adhesive tape-based mechanical exfoliation yielded high-quality ReSe2 flakes from bulk crystals but suffered from unsatisfactory control of the domain size and thickness12, 19, 20. The facile CVD technique was then utilized to fabricate ReSe2 flakes on diverse dielectric substrates, rendering ReSe2 flakes with obvious thickness variations and polycrystalline domains22, 24, 25. Additionally, the current characterization routes for recognizing the grain boundaries (GBs) of polycrystalline ReSe2 are still limited to Raman spectroscopy or ex situ transmission electron microscopy (TEM)24, 26. Additional facile, high-throughput, and in situ identification routes that can evaluate materials from the atomic scale to the domain scale and can effectively achieve characterization of their morphological and electronic properties are still missing despite their importance for guiding the synthesis of samples with controlled orientations and properties.
A system for ReSe2 growth on a conductive substrate, which is distinct from its growth on insulating substrates, should hold fundamental promise considering its compatibility with powerful characterization techniques such as low-energy electron microscopy/diffraction (LEEM/LEED) and scanning tunneling microscopy/spectroscopy (STM/STS). Multi-scale structural details, as well as electronic properties, can be determined to provide insights into related systems27, 28. Coincidentally, a surface self-limited growth mechanism has recently been proposed by our group and other researchers for achieving high-quality monolayer MX2 (M: Mo, W; X: S, Se) on a unique Au foil substrate due to the low solubility of Mo, W, S and Se in Au29,30,31,32. The extremely low solubility (nearly 0.1 at.% at 1000 °C) of Re in Au33 may therefore be exploited to develop a new ReSe2/Au growth system.
Herein, we demonstrate direct synthesis of high-quality monolayer ReSe2 single crystals on a gold foil substrate via an ambient-pressure CVD (APCVD) route based on a surface self-limited growth mechanism. Using Raman spectroscopy, TEM, and LEEM/LEED, we correlate the lattice orientation and crystallinity with the specific domain shape, thereby establishing a common rule for identifying the single-crystal domain of the structurally anisotropic ReSe2 (e.g., to determine whether the parallelogram-shaped ReSe2 domain is monocrystalline). By virtue of high-resolution STM/STS, we also uncover the atomic-scale structures, defects (mainly GBs), and energy band feature of our high-quality monolayer ReSe2 on Au foils, none of which have been addressed to date, especially regarding CVD-grown ReSe2 samples.
APCVD synthesis and TEM characterization of monolayer ReSe2
The growth process of ReSe2 on the Au foil substrate is schematically displayed in Fig. 1a. Details on the growth methodology and experimental setup are provided in the Methods section and Supplementary Fig. 1, respectively. In brief, the ReO3 powder precursor (downstream) partially decomposes into highly volatile Re2O7 via a disproportionation reaction, and this product is subsequently transported by the Ar and H2 carrier gases and reacted with the Se precursor (upstream) to form ReSe2 flakes/films on the Au substrate. In this process, the Au surface is very inert towards the Se precursor, and surface reactions other than that involved in the ReSe2 synthesis should not occur.
X-ray photoelectron spectroscopy (XPS) was first employed to identify the formation of ReSe2 on Au foils. Five elements were observed in the full-range XPS spectrum (Supplementary Fig. 2). As also representatively shown in Fig. 1b, the Se 3d spectrum consists of two peaks located at binding energies of 55.8 and 54.9 eV, which correspond to Se 3d3/2 and Se 3d5/2, respectively, and the Re 4f spectrum possesses two peaks located at 44.2 and 41.8 eV, which are consistent with Re 4f5/2 and Re 4f7/2, respectively. The peak at 57.7 eV is attributed to Au 5p3/2, which arises from the Au substrate. The shifts to lower binding energies for Se 3d and Re 4f relative to those previously reported (Se 3d3/2: 56.0 eV; Se 3d5/2: 55.1 eV; Re 4f5/2: 44.4 eV; Re 4f7/2: 42.0 eV) for monolayer ReSe2 on SiO2/Si25 should result from the relatively strong electronic interaction of ReSe2/Au. In short, the XPS data provide tentative evidence for the evolution of ReSe2 on Au foils.
Scanning electron microscopy (SEM) images of the as-grown ReSe2 flakes on Au foils were then obtained, as shown in Fig. 1c,d and Supplementary Fig. 3. Uniform parallelogrammic shapes with a specific angle of ~119° are noticeable between the long and short edges, which is almost equal to the angle (118.91°) between the a-axis and b-axis of the ReSe2 crystal22. Moreover, the well-defined parallelogrammic shape can be preserved under different growth time (from 15 to 30 min), but with the long-edge lengths varying from ~2 to ~20 µm, as shown in Fig. 1c,d. In this regard, relatively good crystallinity and unique lattice orientation can be expected for such parallelogram-shaped flakes. More intriguingly, the ratio of the long/short edge length for the parallelogram-shaped ReSe2 can reach 5.5:1 (Fig. 1d), strongly suggesting anisotropic growth along different lattice orientations. Most of the ReSe2 domains displayed in Fig. 1c appear to have similar edge directions to each other, which is probably mediated by the steps of the crystalline facets of Au (mainly Au(100)28), i.e., the ReSe2 domains are aligned with one of their edges along the steps of the Au facets. More generally, the ReSe2 domains grown on a single Au domain/facet possess different orientations, as shown by the SEM image and its statistical analysis in Supplementary Fig. 3a, b. The lack of strict correlation between the crystal orientation of the ReSe2 domain and the underlying Au implies that there is no definite epitaxial relationship between the two. This phenomenon was also observed for monolayer MoS2 synthesized on Au foils29.
The transfer of APCVD-synthesized ReSe2 from Au foils to SiO2/Si substrates or TEM grids is highly important for further flake thickness and crystal structure characterization. In this study, a previously developed electrochemical bubbling method30 was exploited to transfer the as-grown sample because of its environmental friendliness. Atomic force microscope (AFM) images of ReSe2 flakes transferred onto SiO2/Si are presented in Fig. 1e and Supplementary Fig. 4, showing good maintenance of the initial parallelogrammic shape. The apparent flake height was measured as ~0.9 nm (inset of Fig. 1e), highly indicative of its monolayer nature according to previously published data12. More AFM data are supplied in Supplementary Fig. 4.
To clarify the detailed structure, TEM and spherical-aberration-corrected scanning transmission electron microscopy (STEM) analyses were also performed for a parallelogram-shaped ReSe2 flake transferred onto a copper TEM grid, as shown in Fig. 1f. A representative TEM image of the folded ReSe2 flake edge revealed a width of ~0.69 nm for the bright line, further indicating its monolayer feature (Supplementary Fig. 5). Specifically, monolayer ReSe2 crystalizes in a stably distorted 1T structure with a diamond-shape Re4 chain along the b direction, as shown from the high-resolution STEM image in Fig. 1g. The angle measured between the b and a axes was ~119°, and the lattice spacing between the two vicinal diamond-shaped chains in the respective directions were ~0.39 and ~0.35 nm, agreeing well with those of the exfoliated sample26. Selected-area electron diffraction (SAED) patterns of three typical locations of a transferred flake (marked 1 to 3 in Fig. 1f) were also collected to show the same crystallographic orientation (Fig. 1h–j).
The above characterization results indicate that the monolayer ReSe2 flakes universally observed with an ideal parallelogrammic shape should be single-crystalline domains. The monolayer thickness can be maintained until the complete coverage of the substrate by the ReSe2 film by extending the growth time to 60 min (Supplementary Fig. 3e). Similar to the mechanisms of monolayer graphene growth on Cu foils34 and of monolayer MoS2 or WS2 growth on Au foils29,30,31, a self-limited catalytic growth mechanism is thus proposed for ReSe2/Au foils for the following reasons: (1) the Au substrate is more catalytically active for the synthesis of high-quality ReSe2 than the inert insulating substrates, and (2) the solubility of Re in Au is extremely low (nearly 0.1 at.% at 1000 °C), which allows the surface-catalyzed growth of ReSe2 with a monolayer thickness.
Optical properties of single-crystal monolayer ReSe2 domains
Figure 2a shows representative Raman spectra obtained using a 532 nm laser for as-grown ReSe2 flakes on Au foils and transferred on SiO2/Si. More than 10 distinctive Raman peaks are visible in the range of 100−300 cm−1 owing to the low crystal symmetry of ReSe2. For the as-grown ReSe2 flake on Au foils, two obvious Raman peaks at ~122 and ~158 cm−1 were detected and assigned to Eg-like and Ag-like vibrational modes, respectively. Notably, the two peaks were redshifted by ~2 cm−1 compared with those (Eg-like and Ag-like vibrational modes at ~124 and ~160 cm−1, respectively) observed after transfer onto SiO2/Si and with previous results for CVD-grown ReSe2 on SiO2/Si22. This redshift is attributed to an enhanced adlayer-substrate interaction of ReSe2/Au according to previous work for MoS2/Au28, 35. To confirm the crystal quality of the monolayer ReSe2 flakes, Raman spectroscopy/mapping measurements were also carried out with a laser wavelength of 532 nm. A representative optical image and corresponding Raman intensity mapping image (the Eg-like vibrational mode) for the parallelogram-shaped ReSe2 transferred onto SiO2/Si are presented in Fig. 2b,c. Importantly, the Raman intensity is rather uniform across the whole domain, strongly indicating its rather high thickness homogeneity.
Figure 2d shows a series of polarized Raman spectra of the parallelogram-shaped ReSe2 flake transferred onto SiO2/Si that were collected at different sample rotation angles (from 0° to 360° with an interval of 10°) under the parallel polarization configuration with a 514 nm laser. Notably, the peak intensities of all the Raman modes are strictly dependent on the sample rotation angle, as clearly shown in the polar plot of the Eg-like mode intensity (Fig. 2e). These Raman data are well consistent with previous reports22, 24, thereby confirming the anisotropic nature of the single-crystal domain and denoting the specific edge orientations in the crystallization process, i.e., the alignments of the a-axis or b-axis along the short or long edges of the parallelogrammic ReSe2 domain22. Briefly, angle-resolved polarized Raman spectroscopy is suitable for identifying the optical in-plane anisotropy, as well as the crystalline orientation of our transferred monolayer single-crystal ReSe2.
LEEM and LEED characterization of monolayer ReSe2
Considering the in situ imaging ability and the complementary diffraction function of LEEM27, 36,37,38 and the conductivity of ReSe2/Au foils, bright-field LEEM (BF-LEEM) was then utilized to image the crystalline structure of the ReSe2 parallelogram, as shown in Fig. 3a. Corresponding micro-region LEED (µ-LEED) patterns were also collected from representative regions marked 1−3 in Fig. 3a (selected regions of 2 µm in diameter). Nearly identical lattice orientations can be observed in Fig. 3b, accordingly indicating the single-crystal feature of the monolayer parallelogram-shaped ReSe2 domains, in good agreement with the TEM and SAED results in Fig. 1. Additional LEEM/LEED characterization of the crystalline structure of the ReSe2 parallelogram is described in Supplementary Fig. 6.
For more evidence, representative BF-LEEM and corresponding LEED characterization of three discrete ReSe2 parallelograms was also performed (Supplementary Fig. 7a). Interestingly, the dark-field LEEM (DF-LEEM) image shown in Supplementary Fig. 7b reveals that the parallelogram-shaped ReSe2 flakes with parallel edges usually possess the same contrast and therefore have the same lattice orientation. Furthermore, BF-LEEM characterization of three merged ReSe2 parallelograms was also carried out (Fig. 3c). Corresponding LEED patterns recorded from the three domains (denoted 4−6 in Fig. 3c) display three sets of patterns possessing different orientations (Fig. 3d), thereby indicating their different lattice orientations. Surprisingly, the orientations of the LEED patterns are firmly related to the directions of the short edges of each ReSe2 parallelogram (see Fig. 3c, d), being positioned at approximately 11°, 142°, and 129° with regard to the horizontal direction. Further DF-LEEM image (Fig. 3e) exhibits clearly different contrasts among the three domains, and their merging boundaries are also clearly visible. Additional LEEM/LEED characterization of the orientation/boundary of the polygonal ReSe2 domains is described in Supplementary Fig. 7c, d. It is worthy of mentioning that this domain orientation/boundary imaging method of LEEM/LEED is distinguished from the commonly used dark-field TEM method, which usually involves a sample transfer process39,40,41. DF-LEEM accompanied with µ-LEED techniques is thus promising for serving as an in situ, nondestructive, and high-throughput method for determining the crystal structure of anisotropic 2D monolayer ReSe2 grown on conductive substrates. In addition, this identification method is also applicable to other 2D-layered materials synthesized on various conductive substrates.
Atomic and electronic structures of monolayer ReSe2
The CVD-grown monolayer ReSe2 on Au foil was also directly analyzed by high-resolution STM/STS to uncover its atomic-scale morphology and electronic properties in an as-grown state. Prior to the STM measurements, the CVD-grown ReSe2/Au was degassed overnight at ~400 °C in an ultrahigh-vacuum chamber to remove adsorbed impurities. Figure 4a shows a large-scale STM image of the sample surface, in which a large-area monolayer ReSe2 film is observed to extend over the flat Au terraces. The corresponding atomically resolved STM image (Fig. 4b) reveals perfect quasi-hexagonal surface lattices, indicating the relatively high crystal quality of the CVD-grown ReSe2 flakes. The unit cell, which is composed of the brightest neighboring spots, and the four adjacent spots, which are characterized by gradually increasing STM contrasts, are indicated by the black and red dashed parallelograms, respectively. According to the atomic model in Fig. 4c, the observed spot-like contrasts (e.g., the four typical spots in the red dashed parallelogram) correspond to the upper Se atoms (e.g., four Se atoms) of ReSe2. Additional sequential zoomed-in STM images are supplied in Supplementary Fig. 8 to show a ReSe2 film covering terraced Au and the coexistence of atomic lattices and the underlying terraces.
Notably, the STM contrast variations inside each unit cell (indicated by the black dashed parallelogram) can be visually observed in the corresponding 3D STM image (Fig. 4d), which is in sharp contrast with the honeycomb-like lattices of MoS2 possessing uniform spot-like contrasts inside each unit cell28, 42. This contrast fluctuation stems from the anisotropic structure of ReSe212, 43. Typically, ReSe2 crystallizes in a distorted 1T structure, and the four typical Re atoms are arranged into a diamond-shaped chain along the b-axis direction (along the red arrow in Fig. 4c). This structural distortion breaks the hexagonal symmetry and affords a doubled unit cell size (indicated by the black dashed parallelogram) compared to the configuration of the initial four Se atoms (marked by the red dashed parallelogram). The four Se atoms are not all in the same plane12, 43, which explains the varied contrasts in the STM image44.
It has been reported that the two principal crystal axes of ReSe2, corresponding to the shortest (b-axis) and second-shortest axis (a-axis) in the basal plane, have an angle of ~118.91° 22. Herein, the height profiles taken along these two typical lattice directions (a-axis and b-axis; marked in Fig. 4b, plotted in Fig. 4e) reveal two lattice constants of 7.05 ± 0.2 and 6.57 ± 0.1 Å, respectively, in line with the previous report45. Furthermore, low-temperature (~78 K) STS measurements were also conducted to explore the electronic structure of monolayer ReSe2/Au foils. As shown in Fig. 4f, the valence band maximum and conduction band minimum of ReSe2/Au are located at ~−0.70 and +0.50 V, respectively, indicating a slight n-doping effect of monolayer ReSe2 on Au foils. The quasiparticle band gap (Eg) of ReSe2/Au (~1.20 eV) is evidently much smaller than the theoretical value (~2.09 eV)43, probably due to the strong interfacial electronic interaction, which introduces metal-induced gap states to ReSe2 from the Au substrate, as similarly reported for MoS2 on Au foils with a reduced band gap46, 47. As a side evidence, the STS spectrum of the Au substrate shows an apparent tunneling contribution at a larger bias range than the band gap region of ReSe2.
Detailed structures of ReSe2 GBs
Current knowledge of the detailed structure of the GBs of structurally isotropic 2D materials, e.g., graphene and MoS2, is relatively comprehensive, revealing the existence of 4-membered-ring, 5-membered-ring, 7-membered-ring or 8-membered-ring types of defects39, 48,49,50,51,52. However, for ReX2, the large anisotropic interfacial energies imposed by their anisotropic structure make the structures of their GBs quite ambiguous, although efforts have been made using ex situ TEM characterization26, 53. In this work, detailed STM studies were first used to address such issues for the CVD-grown monolayer ReSe2/Au system.
A typical GB with a bright line-shaped contrast (marked by a blue dashed line) was captured between two neighboring domains (Fig. 5a and Supplementary Fig. 9). Since the STM morphology of the two composite domains (marked I and II) are quite similar, identifying the a-axis and b-axis of each is essential to distinguish their domain orientations. This can be realized by mapping the height profiles along the three different lattice directions (Supplementary Fig. 9) considering the inequivalence of the ReSe2 lattices12, 43. Consequently, domains I and II are revealed to have nearly the same lattice constants/orientations, and the a-axis and b-axis of the two domains are marked in Fig. 5b. Notably, in the further zoomed-in STM image in Fig. 5b, the bright line-shaped contrast at the GB almost disappears, and the patching interface becomes much clearer. The upper Se atoms imaged by STM are almost continuous at the GB but with a little distortion (as indicated by the fitted atomic model), which is free of apparent dislocation cores or defects. Accordingly, this patching behavior can be defined as two parallel domains with a dislocation, as also schematically shown in Fig. 5c for a clearer view.
Another typical GB is presented in Fig. 5d and Supplementary Fig. 10, wherein domains III and IV have apparently different STM contrasts even in the large-scale STM image. A perfect lattice coherence between the two adjacent domains is noticeable in the magnified STM image in Fig. 5e (as indicated by the fitted atomic model). A similar method was also used to identify the orientation of each domain (Supplementary Fig. 10). The results indicate that for domains III and IV, the b-axis directions are the same, whereas the a-axes are reversed. In this regard, this typical GB can be considered as a mirror twin boundary, as schematically shown in Fig. 5f. To illustrate the atomic bonding feature at the two typical GBs mentioned above, density functional theory (DFT) calculations were also performed, and the results coincide well with the STM observations (Supplementary Fig. 11 and Supplementary Discussion). More STM images of the twist GBs are provided in Supplementary Fig. 12, and the patching interfaces are similarly free of obvious defects.
Previous STEM studies revealed that the GBs in ReX2 evolved when the orientation of the Re-chain was changed by electron beam irradiation or the vacancy defects around the GBs26, 53. However, this ex situ characterization cannot avoid the artificial destruction induced by the transfer process and the effect of high-energy electron bombardment by TEM analysis. Accordingly, the intrinsic defect type of GBs may not be well resolved. In contrast, the CVD-grown ReSe2/Au foil synthesized in this work serves as an ideal platform for uncovering the intrinsic structures of GBs using in situ STM/STS characterization. To the best of our knowledge, this is the first report of an STM study on the GBs of ReSe2. Nevertheless, it is noteworthy that further theoretical and experimental efforts are still desirable for an in-depth understanding of the GBs.
In summary, we have accomplished the highly uniform synthesis of high-quality monolayer ReSe2 single crystals on Au foils using an APCVD method. We then identify the single-crystal nature of the parallelogram-shaped ReSe2 domains by using various methods, including Raman spectroscopy, TEM, and LEEM/LEED. The novel monolayer growth of ReSe2 on Au foils is directed by a self-limited catalytic growth mechanism, and the specific parallelogram shape is mainly mediated by its anisotropic structure. Direct growth on Au foil allows the atomic-scale morphology and intrinsic band feature of monolayer ReSe2 directly on Au foils to be analyzed using in situ STM/STS. We believe that this work should pave the way towards the direct synthesis and in situ characterization of anisotropic 2D-layered materials such as ReSe2 and propel their fundamental property investigations and practical applications in next-generation electronic and optoelectronic devices.
Synthesis of ReSe2
The synthesis of single-crystalline monolayer ReSe2 on Au foils was conducted in a multi-temperature-zone APCVD tube furnace equipped with a quartz tube (1 inch in diameter). Before growth, the Au foil (ZhongNuo Advanced Material Technology Co., Ltd., 30 μm thick, 99.99% purity) was annealed at 970 °C for 8 h to reduce its surface roughness. Five milligrams ReO3 powder (Alfa Aesar, 99.9% purity) and 1 g Se powder (Alfa Aesar, 99 + % purity) were utilized as the Re and Se precursors for the CVD growth. The Au substrate with an area of 1 cm × 1 cm was placed in a quartz boat at the center of the furnace. To expel air, the tube furnace was first flushed with ultra-high-purity Ar gas. The furnace was then heated to 750 °C over 30 min and maintained at 750 °C for 15, 30, or 60 min for growth under a constant flow rate of Ar gas of 50 sccm and H2 gas of 10 sccm at atmospheric pressure. After the synthetic procedure, the furnace was naturally cooled to room temperature.
Transfer of ReSe2
For sample transfer, the ReSe2/Au samples were first spin-coated with poly(methyl methacrylate) (PMMA) at 2500 rpm for 1 min, resulting in a uniform polymer film on the sample surfaces, and then were baked at 120 °C for 15 min. Next, the PMMA film, together with ReSe2 flakes, was detached from the Au substrate using an electrochemical bubbling method30. PMMA-supported ReSe2 was then washed with deionized water several times, transferred onto SiO2(300 nm)/Si substrates or TEM grids, and dried on a hot plate at 80 °C. Finally, the PMMA was removed using acetone and isopropanol.
Characterization of ReSe2
The synthesized ReSe2 flakes were systematically characterized using SEM (Hitachi S-4800, 2 kV), AFM (Bruker Dimension Icon), Raman spectroscopy (HORIBA iHR550, excitation light wavelengths of 514 and 532 nm), XPS (Kratos Analytical AXIS-Ultra with monochromatic Al Kα X-ray), TEM (FEI Tecnai F20, acceleration voltage of 200 kV), STEM (JEOL JEM-ARM200CF, acceleration voltage of 200 kV), and LEEM/µ-LEED (Elmitec LEEM-III system with ultrahigh vacuum of ~1 × 10−10 Torr). Ultrahigh-vacuum low-temperature STM/STS systems were also utilized for the atomic-scale structural characterization under a base pressure of better than 10−10 mbar. All the STM images were obtained at room temperature. The STS spectra were acquired at ~78 K by recording the output of a lock-in system with the manually disabled feedback loop. A modulation signal of 10 mV at 932 Hz was selected under a tunneling condition of 1.50 V and 210 pA.
DFT calculations were performed by the Vienna ab initio simulation package using the plane-wave basis set54 with an energy cutoff of 450 eV and the projector-augmented wave55 potentials and the generalized gradient approximation parameterized by Perdew, Burke and Ernzerhof for the exchange-correlation functional56.
The data reported by this article are available from the corresponding author upon reasonable request.
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Geim, A. K. Graphene: status and prospects. Science 324, 1530–1534 (2009).
Liao, L. et al. High speed graphene transistors with a self-aligned nanowire gate. Nature 467, 305–308 (2010).
Radisavljevic, B. et al. Single-layer MoS2 transistors. Nat. Nanotechnol. 6, 147–150 (2011).
Wang, Q. H. et al. Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 7, 699–712 (2012).
Voiry, D. et al. Enhanced catalytic activity in strained chemically exfoliated WS2 nanosheets for hydrogen evolution. Nat. Mater. 12, 850–855 (2013).
Chhowalla, M. et al. The chemistry of two-dimensional layered transition metal dichalcogenide nanosheets. Nat. Chem. 5, 263–275 (2013).
Mak, K. F. et al. The valley Hall effect in MoS2 transistors. Science 344, 1489–1492 (2014).
Sie, E. et al. Valley-selective optical Stark effect in monolayer WS2. Nat. Mater. 14, 290–294 (2015).
Lu, A.-Y. et al. Janus monolayers of transition metal dichalcogenides. Nat. Nanotechnol. 12, 744–749 (2017).
Tongay, S. et al. Monolayer behaviour in bulk ReS2 due to electronic and vibrational decoupling. Nat. Commun. 5, 3252 (2014).
Wolverson, D. et al. Raman spectra of monolayer, few-layer, and bulk ReSe2: an anisotropic layered semiconductor. ACS Nano 8, 11154–11164 (2014).
Hart, L. et al. Rhenium dichalcogenides: layered semiconductors with two vertical orientations. Nano Lett. 16, 1381–1386 (2016).
Zhang, Q. et al. Edge-to-edge oriented self-assembly of ReS2 nanoflakes. J. Am. Chem. Soc. 138, 11101–11104 (2016).
Zhang, Q. et al. Extremely weak van der Waals coupling in vertical ReS2 nanowalls for high-current-density lithium-ion batteries. Adv. Mater. 28, 2616–2623 (2016).
Liu, E. et al. Integrated digital inverters based on two-dimensional anisotropic ReS2 field-effect transistors. Nat. Commun. 6, 6991 (2015).
Chenet, D. A. et al. In-plane anisotropy in mono- and few-layer ReS2 probed by Raman spectroscopy and scanning transmission electron microscopy. Nano Lett. 15, 5667–5672 (2015).
Yang, S. et al. Tuning the optical, magnetic, and electrical properties of ReSe2 by nanoscale strain engineering. Nano Lett. 15, 1660–1666 (2015).
Lorchat, E. et al. Splitting of interlayer shear modes and photon energy dependent anisotropic raman response in n-layer ReSe2 and ReS2. ACS Nano 10, 2752–2760 (2016).
Arora, A. et al. Highly anisotropic in-plane excitons in atomically thin and bulklike 1T’-ReSe2. Nano Lett. 17, 3202–3207 (2017).
Liu, F. et al. Highly sensitive detection of polarized light using anisotropic 2D ReS2. Adv. Funct. Mater. 26, 1169–1177 (2016).
Zhang, E. et al. Tunable ambipolar polarization-sensitive photodetectors based on high-anisotropy ReSe2 nanosheets. ACS Nano 10, 8067–8077 (2016).
Yang, H. et al. Optical waveplates based on birefringence of anisotropic two dimensional layered materials. ACS Photonics 4, 3023–3030 (2017).
Hafeez, M. et al. Chemical vapor deposition synthesis of ultrathin hexagonal ReSe2 flakes for anisotropic Raman property and optoelectronic application. Adv. Mater. 28, 8296–8301 (2016).
Jiang, S. et al. Application of chemical vapor–deposited monolayer ReSe2 in the electrocatalytic hydrogen evolution reaction. Nano Res. https://doi.org/10.1007/s12274-017-1796-8 (2017).
Lin, Y.-C. et al. Single-layer ReS2: two-dimensional semiconductor with tunable in-plane anisotropy. ACS Nano 9, 11249–11257 (2015).
Shi, J. et al. Monolayer MoS2 growth on Au foils and on-site domain boundary imaging. Adv. Funct. Mater. 25, 842–849 (2015).
Zhou, X. et al. Periodic modulation of the doping level in striped MoS2 superstructures. ACS Nano 10, 3461–3468 (2016).
Shi, J. et al. Substrate facet effect on the growth of monolayer MoS2 on Au foils. ACS Nano 9, 4017–4025 (2015).
Gao, Y. et al. Large-area synthesis of high-quality and uniform monolayer WS2 on reusable Au foils. Nat. Commun. 6, 8569 (2015).
Yun, S. J. et al. Synthesis of centimeter-scale monolayer tungsten disulfide film on gold foils. ACS Nano 9, 5510–5519 (2015).
Gao, Y. et al. Ultrafast growth of high-quality monolayer WSe2 on Au. Adv. Mater. 29, 1700990 (2017).
Knook, B. et al. The electrical resistance of some dilute alloys of the noble metals and Re at low temperatures. Physica 30, 1124–1130 (1964).
Li, X. et al. Large-area synthesis of high-quality and uniform graphene films on copper foils. Science 324, 1312–1314 (2009).
Shi, J. et al. Controllable growth and transfer of monolayer MoS2 on Au foils and its potential application in hydrogen evolution reaction. ACS Nano 8, 10196–10204 (2014).
Gao, L. et al. Repeated growth and bubbling transfer of graphene with millimeter-size single-crystal grains using platinum. Nat. Commun. 3, 699 (2012).
Mu, R. et al. Visualizing chemical reactions confined under graphene. Angew. Chem. Int. Ed. 51, 4856–4859 (2012).
Ning, Y. et al. Applications of PEEM/LEEM in dynamic studies of surface physics and chemistry of two-dimensional atomic crystals. Acta Phys. Chim. Sin. 32, 171–182 (2016).
Van der Zande, A. M. et al. Grains and grain boundaries in highly crystalline monolayer molybdenum disulphide. Nat. Mater. 12, 554–561 (2013).
Najmaei, S. et al. Vapour phase growth and grain boundary structure of molybdenum disulphide atomic layers. Nat. Mater. 12, 754–759 (2013).
Ji, Q. et al. Unravelling orientation distribution and merging behavior of monolayer MoS2 domains on sapphire. Nano Lett. 15, 198–205 (2015).
Huang, Y. L. et al. Bandgap tunability at single-layer molybdenum disulphide grain boundaries. Nat. Commun. 6, 6298 (2015).
Zhong, H. X. et al. Quasiparticle band gaps, excitonic effects, and anisotropic optical properties of the monolayer distorted 1T diamond-chain structures ReS2 and ReSe2. Phys. Rev. B 92, 115438 (2015).
Parkinson, B. A. et al. Relationship of STM and AFM images to the local density of states in the valence and conduction bands of rhenium selenide (ReSe2). J. Am. Chem. Soc. 113, 7833–7837 (1991).
Lamfers, H.-J. et al. The crystal structure of some rhenium and technetium dichalcogenides. J. Alloys Compd. 241, 34–39 (1996).
Lee, S. et al. Statistical study on the schottky barrier reduction of tunneling contacts to CVD synthesized MoS2. Nano Lett. 16, 276–281 (2016).
Zhang, Z. et al. Direct chemical vapor deposition growth and band-gap characterization of MoS2/h-BN van der Waals heterostructures on Au foils. ACS nano 11, 4328–4336 (2017).
Yang, B. et al. Periodic grain boundaries formed by thermal reconstruction of polycrystalline graphene film. J. Am. Chem. Soc. 136, 12041–12046 (2014).
Zhang, Z. et al. Unraveling the sinuous grain boundaries in graphene. Adv. Funct. Mater. 25, 367–373 (2015).
Zhou, W. et al. Intrinsic structural defects in monolayer molybdenum disulfide. Nano Lett. 13, 2615–2622 (2013).
Zou, X. et al. Predicting dislocations and grain boundaries in two-dimensional metal-disulfides from the first principles. Nano Lett. 13, 253–258 (2013).
Huang, Y. L. et al. Gap states at low-angle grain boundaries in monolayer tungsten diselenide. Nano Lett. 16, 3682–3688 (2016).
Wu, K. et al. Domain architectures and grain boundaries in chemical vapor deposited highly anisotropic ReS2 monolayer films. Nano Lett. 16, 5888–5894 (2016).
Kresse, G. et al. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Kresse, G. et al. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Perdew, J. P. et al. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
The work was supported by the National Natural Science Foundation of China (Nos. 51290272, 51472008, 21688102, 61774003, and 21573004), the National Key Research and Development Program of China (2016YFA0200103, 2016YFA0200200, 2017YFA0304600, and 2017YFA0205700), and the Open Research Fund Program of the State Key Laboratory of Low-Dimensional Quantum Physics (Nos. KF201601 and KF201604).
The authors declare no competing interests.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Jiang, S., Hong, M., Wei, W. et al. Direct synthesis and in situ characterization of monolayer parallelogrammic rhenium diselenide on gold foil. Commun Chem 1, 17 (2018). https://doi.org/10.1038/s42004-018-0010-6
This article is cited by
Anisotropic monolayer of ReX2 on Au foils for exploring abnormal growth behavior and electronic properties
Nano Research (2023)
Nonlinear electronic and ultrafast optical signatures in chemical vapor-deposited ultrathin PtS2 ribbons
Nano Research (2022)
Present advances and perspectives of broadband photo-detectors based on emerging 2D-Xenes beyond graphene
Nano Research (2020)
Salt-assisted growth and ultrafast photocarrier dynamics of large-sized monolayer ReSe2
Nano Research (2020)
Step-confined thin film growth via near-surface atom migration
Nano Research (2020)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.