Footpads allow insects to walk on smooth surfaces. Specifically, liquid secretions on the footpad mediate adhesiveness through Van der Waals, Coulomb, and attractive capillary forces. Although the morphology and function of the footpad are well defined, the mechanism underlying their formation remains elusive. Here, we demonstrate that footpad hair in Drosophila is formed by the elongation of the hair cells and assembly of actin filaments. Knockdown of Actin5C caused a malformation of the hair structure, resulting in reduced ability to adhere to smooth substrates. We determined that functional footpads are created when hair cells form effective frameworks with actin filament bundles, thereby shaping the hair tip and facilitating cuticular deposition. We adapted this mechanism of microstructure formation to design a new artificial adhesive device—a spatula-like fiber-framed adhesive device supported by nylon fibers with a gel material at the tip. This simple self-assembly mechanism facilitates the energy-efficient production of low-cost adhesion devices.
Insects that can walk on smooth surfaces have specialized structures called footpads on their legs1,2. Previous studies have shown that footpads are composed of flexible hairs (setae), the tips of which have specific microstructures that are spatulate, discoidal, or pointed3,4,5. The footpad generates Van der Waals, Coulomb, and attractive capillary forces facilitating adhesion on to the substrate surface6. The footpad secretion is known to contain a non-volatile, lipid-like substance2,7,8. The bridge between the setal tip and the substrate, filled with the secreted liquid generates capillary forces that allow the insects to adhere to the substrate6. Although the morphology and function of the footpad are relatively understood2, the mechanism underlying its formation remains elusive. Drosophila melanogaster is a very useful model insect to study the mechanism of the development of footpads owing to the availability of several advanced genetic tools. The Drosophila melanogaster footpad houses many hairs, the tips of which have a spatula-like microstructure9,10. Recently, a mutant of the Polycomb group gene Su(z)2 with malformed adhesive pad structures was reported to affect the insect’s climbing ability10. However, the molecular and cellular mechanisms underlying footpad formation remain largely unknown.
In holometabolous insects such as Drosophila, footpads are newly formed during metamorphosis11,12. Here, we examine the formation of the footpad during the pupal stage. During the formation of the footpad hair, a hair cell elongated and actin filaments are assembled to make a framework providing a specific shape for the hair. Inhibition of cytoskeletal actin function through the RNAi-mediated knockdown of a gene Actin5C (Act5C) induced the malformation of the hair structure. The Act5C knockdown flies with malformed footpads demonstrated decreased ability to adhere to a smooth substrate. Therefore, the formation of the functional footpad involves hair cell elongation, supported by a framework of actin filament bundles that provides a specific shape and facilitates cuticular deposition. This mechanism of formation of the microstructures of footpad hair inspired us to design a new adhesive device. We propose a new fiber-framed adhesive device with a spatula-like structure supported by nylon fibers with gel materials at the tip. This simple procedure, using a self-assembly mechanism, enables us to reduce the cost of raw materials and energy required to produce useful adhesion devices.
Footpads in Drosophila
In the fruit-fly, Drosophila melanogaster, the tarsus (distal part of the leg) is divided into five segments, and the pretarsus is the structure that forms the tip of the leg. A pair of claws and a pair of footpads are present on the dorsal and ventral sides of the pretarsus, respectively9 (Fig. 1a). In addition, ~30 hairs (setae) are arranged in six or seven rows in the stalk of each footpad. The tip of each hair is ~1–2 μm in width, and has a spatulate shape (Fig. 1b). Cross-sectional images obtained using a transmission electron microscope (TEM) have shown that each hair is a flat tube composed of a cuticle (Fig. 1c). Flies secrete a viscous fluid between the footpad and the substrate and use attractive capillary forces to attach to the surface6 (Supplementary Fig. 1).
Footpad formation during metamorphosis
To examine the processes involved in the formation of these footpads during the pupal stage in Drosophila development, we first screened suitable GAL4 strains for the capacity to label footpad cells with a GFP expression marker (Supplementary Fig. 2). We determined that we could effectively label most of the footpad hair cells and some of the cells associated with the ventral aspect of the claws, in a seven-up (svp)-GAL4 line marked with GFP (svp > GFP). Then the svp-expressing cells were labeled with actin5C (Act5C: a gene encoding cytological actin in Drosophila)-GFP and nucleus-targeted with DsRed (svp > Act5C-GFP, nucDsRed) (Fig. 1d–g, d′–g′) and the formation of the footpad was monitored. At 20 h after puparium formation (AFP), we observed two clusters of GFP-expressing cells in ventral epidermal cells of the pupal pretarsus, which is formed from a simple sack of epidermal cells at this stage (Fig. 1d, d′). Each of these clusters of cells then began to extrude the processes outwards (Fig. 1e, e′). The cell bodies marked with magenta nuclei, in these footpad-forming cells, were seen to migrate proximally, while the tips remained in fixed positions (Fig. 1f, f′; Supplementary Movie 1). By 40 h APF, the cells had completed the construction of the framework for the footpad design (Fig. 1g, g′). Thus, the structural morphology of the svp-expressing cells was seen to dramatically change during the formation of the footpad during the first half of the pupal stage. Once the framework was completed, the process of depositing the cuticle began. To address whether a single cell forms a single hair or multiple hairs, we labeled only a limited number of svp-expressing cells, using the mosaic analysis with a repressible cell marker (MARCM) method13. Our results revealed that a single-labeled cell extended a fine process, which formed the tip of a single hair (Supplementary Fig. 3, Supplementary Movie 2), indicating that a single cell forms a single hair on the footpad. A similar mechanism was reported in the Stenus species4, suggesting that this process is conserved across insect species.
Cytoskeletal actin fiber involvement in footpad formation
It is well documented that cytoskeletal actin plays a vital role in morphological changes of cells14. Therefore, we next examined the role of cytoskeletal actin in the formation of footpads. To accomplish this, we stained the actin filaments in hair cells, using fluorescent phalloidin, which binds to fibrous actin molecules. Actin filaments were found to accumulate in the apical aspect of cells in the footpads at 24 h APF (Fig. 2a). Following 30 h APF, the cells began to extend the processes containing actin filaments stained with phalloidin (Fig. 2b; Supplementary Fig. 4); and at 40 h APF, actin filaments were observed to assemble and form the framework for a spatulate shape within the cell. Cytoskeletal actin filaments were, therefore, determined to have a role in the formation of the spatulate shape of the individual hair cells of the footpads (Fig. 2c–c″′).
To further elucidate the role of actin filaments, we examined the effects of RNAi-mediated knockdown of cytoskeletal actin (Act5C) on footpad formation. Act5C RNAi was induced in hair cells under the control of an svp-GAL4 driver. To avoid potentially lethal effects, Act5C RNAi was produced following the creation of the puparium, using the temperature-sensitive suppressor Gal80TS of GAL415 (svp > Act5C-RNAi, GAL80TS, Fig. 2d). Alternatively, in another group of flies, the effects of Act5C RNAi were inhibited in the nervous system by induction of pan-neuronal expression of elav-GAL8016 (svp > Act5C-RNAi, elav-GAL80, Fig. 2e). The flies survived to the adult stage of development, and thus, we could effectively observe the effect of Act5C knockdown on footpad formation. In both groups of flies, RNAi-mediated Act5C knockdown induced malformation of the hair shape, resulting in forked-shape tips rather than the normal spatulate shape (Fig. 2d–f). This abnormal shape should have been the result of the disrupted formation of the hair tip framework. No effects other than the malformed tips were seen in footpad morphology or the process of footpad formation in the Act5C knockdown flies under our experimental conditions (Supplementary Fig. 5, Supplementary Movie 3), probably because the level of knockdown was not high enough to induce other effects.
We next examined whether Act5C knockdown flies (svp > Act5C RNAi, elav-Gal80) with malformed footpads demonstrated defects in climbing ability on smooth substrates (Fig. 3; Supplementary Movies 4 and 5). We found that it took Act5C knockdown flies twice as long to climb the vertical wall of a Pasteur pipette, compared with the control flies with normal footpads (Fig. 3a, c, d). Moreover, the Act5C knockdown flies were seen to lose traction and slip down the pipette wall. They also struggled to effectively pass the constriction point on the pipette, resulting in their falling from the wall, while normal flies managed this obstacle with ease (Fig. 3b–d). Hence, the malformed footpads should reduce the active contact area between the tip of each hair and the substrate, resulting in decreased ability to adhere to smooth substrates. Taken together, these results demonstrate that cytoskeletal actin filaments are a mandatory component in the mechanism employed by Drosophila for the formation of the structural framework that determines the shape and thereby adhesiveness of the footpad hair. The footpad hair tips in insects show various shapes, such as filamentous, lanceolate, spatulate, and discoidal3,4,5,17. Our results suggest that insects with hairy pads employ this actin-based morphogenesis mechanism to provide distinct shapes to the microstructures of their footpad hair.
Biomimetic adhesive device inspired by the footpad formation
This mechanism employed by Drosophila in the formation of footpad microstructures provided insights into the designing of a new biomimetic device to improve adherence to substrates. Generally, the processes responsible for the establishment of the footpad microstructures in a fly are divided into two steps (Fig. 4a). First, a spatulate-shaped framework is formed by actin fibers at the tip of the hair. Secondly, cuticle materials are secreted, accumulated, and then solidified. We, therefore, propose a strategy for manufacturing adhesive structures using a similar two-step system (Fig. 4b). Step 1: design the structural framework with nylon fiber. Step 2: immerse the framework in resin and allow the spatulate-shaped structure to form via surface tension. The resulting adhesive structure contains a spatulate structure supported by nylon fibers, with a gel calcium alginate material forming the tip, which is the point of contact for a substrate (Fig. 4c). We evaluated the adhesive properties of the hair-like structures by performing a shear test. Since the setae of the fly are covered with a secreted fluid, we carried out the test after dipping our artificial hair structures in water (Fig. 4d). It was shown both in beetles18 and mimicked artificial systems19 that the amount of liquid at the hair tip could strongly influence the adhesion forces. This is the case in our devices also. The adhesion forces in the fibrillar system decreased with increasing amounts of water and increased with decreasing amounts of water. Immediately after dipping in water, the adhesive device had a high water content, and adhesive strength of 40 ± 15 mN (mean ± SE, n = 6). However, when the structure was almost dried after contact, the device exhibited a high average adhesive strength (779 ± 108 mN, mean ± SE, n = 11), which is equivalent to the force capable of suspending a 60-kg human being with an adhesive area of 9 cm2 (comparable with ~756 fibers), or a circle with a radius of ~17 mm. Figure 4e and f demonstrates that a single adhesive hair is capable of suspending a 52.8-g silicon board. Friction and adhesion of single pads were measured in beetles20, which suggested that the distal pads containing spatula-tipped hairs, for the most part, are mainly used for pulling and adhesion. So, comparison with the value of the shear stress of distal pads on a smooth surface showed that the shear stress of our device, 784 ± 144 kPa, is comparable with that of distal pads on a smooth surface, 642 ± 99 kPa in males and 613 ± 111 in females. Since our device is weak against peeling in a perpendicular direction, this adhesive ability is easily reversed by applying an opposite directional force or by simply twisting the fiber, similar to what is observed in insect footpads20,21,22. Importantly, this apparatus maintains its adhesive properties after repeated attachment and detachment cycles, even though it is necessary to dip it again in water before use when it dries up completely.
The attached area of our adhesive structure (1.2 mm2 ± 0.1, mean ± SE, n = 11) was about three orders of magnitude larger than that of the fly’s footpad hair (3 µm2 ± 0.1, mean ± SE, n = 5). Here, the adhesion mechanism in relation to the effect of size should be considered. In general, as the size of an object decreases, the object becomes affected more by the surface than the volume. Therefore, a small object can be lifted by the surface tension of a small droplet. In the case of the fly’s hair and the developed adhesive structure, the surface is larger than the volume in both cases because of the film shape. The mechanism of adhesion of such a structure via a low-viscosity liquid changes, depending on the amount of the liquid. Such a phenomenon is the same for living and artificial things. When the liquid volume is large, the distance between the adhesive and the adherend is large, and the capillary force is the main force responsible for adhesion. As the liquid volume decreases and the thickness of the interposed droplets become smaller than the radius of the contact portion, the Laplace pressure is responsible for adhesion. Further, when the amount of the droplet is small, and the solid surface is very close, the intermolecular forces come in play. When the contact area is the same, the adhesive force is smaller when the liquid amount is higher and vice versa. Therefore the adhesive force is determined by the surface to volume ratio, the amount of liquid present, and several interactive forces.
By examining the mechanism responsible for the development of footpad microstructures in flies, we biomimetically designed an effective adhesive agent. Since 2005, the development of biomimetic adhesive devices has been based on studies on biological dry hair adhesives, such as those found on geckos23,24,25,26. However, adhesion on a rough surface limits the true contact area between the adhesive structure and the deposition surface. Thus, to establish a larger contact area to improve the effectiveness of the adhesive surface, it is mandatory to incorporate flexible contact-forming hairs in the design. It is known that the stiffness of insect hair is not uniform, for example, a material composition gradient and subsequent Young’s modulus gradient in the longitudinal direction of the hairs is observed as in the ladybird beetle footpad27. The base of hair stalk is sufficiently hard to prevent clustering, and the contact surface of hair tips is sufficiently compliant to adapt to rough substrates. In addition, the bridge between the hair tip and the substrate is filled with the secreted liquid, which generates the capillary forces that adhere the insect to the substrate6. In the adhesive device, as in the biological setae, softness at the tip is important for adhesion. Through the use of a material with high moisture content, we designed highly flexible thin structures located at the device tip, thereby increasing the real contact area and improving the adhesive ability on rough surfaces. Furthermore, it is vital to incorporate hair-like fibers with high tensile strength capable of withstanding repeated attachments and detachments, which was achieved through the use of nylon fibers in our device. The compliance of the structure is known to strongly influence the adhesion force19. Further validation of our adhesive device, including quantification of the compliance, should be carried to compare the adhesiveness of the device with that of insect footpads. The use of an uncured liquid raw material such as sodium alginate in our design would serve to simplify the manufacturing process and reduce the cost of production associated with our device. Our approach effectively applied mechanisms employed in developmental biology in a mimetic approach (developmental biomimetics) for the design of new biology-inspired devices. We have, therefore, demonstrated developmental biomimetics as a strategy for developing new concepts in material science.
Fruit-flies, Drosophila melanogaster, were reared on cornmeal–yeast medium at 25 °C with constant illumination. CS flies were used as wild-type controls. For staging during metamorphosis, white prepupae were collected within 30 min after puparium formation (APF) and incubated at 25 °C until appropriate developmental stages were observed.
To determine which flies were suitable for labeling footpad cells, we crossed several GAL4 strains involved in pretarsus formation with UAS-mCD8::GFP strains and examined the expression pattern of GFP in the pretarsus region of the F1 pupal legs ~2 days APF. We examined bar-, ckm10-, spa-, neur-, dpp-, and svp-GAL4 Drosophila lines. Bar-GAL4 and dpp-GAL4 lines were generously donated by Dr. Kojima12 and the ckm10- GAL4 lines by Dr. C. Mirth28. The spa-, neur- and svp-GAL4 lines were obtained from the Kyoto Stock Center. Strains of FRTG13, UAS-mCD8::GFP, FRTG13, TubP-GAL80, UAS-nucDsRed, and TubP-Gal80TS (7019) were obtained from BDSC, and UAS-Act5C::GFP was obtained from the Kyoto Stock Center. A line of UAS-Act5C RNAi (7139) was obtained from VDRC. A line of elav-Gal80 was gifted by S. F. Goodwin.
Detailed genotypes and the abbreviations of all strains used in the paper are indicated in Supplementary Table 1.
Observation of footpad morphology
The footpad morphology was examined using a scanning electron microscope (SEM). Fly legs were fixed with 3.7% formaldehyde, washed in distilled water, and serially dehydrated with ethanol. After dehydration, ethanol was replaced with tert-butyl alcohol. The samples were then frozen at 4 °C and further dehydrated by freeze–drying (VFD-21S, Vacuum Device Inc). Specimens were then subjected to gold coating by an ion coater (Neo coater MP-19010 NCTR, JEOL), and observed with SEM (TM3000 Miniscope, Hitachi).
Legs were dissected from the body using fine scissors and prefixed overnight in 2% glutaraldehyde and 2% paraformaldehyde in 0.1 M cacodylate buffer (pH 7.2), following three washes for 10 min each in 0.1 M cacodylate buffer. Then, the specimens were postfixed for 2 h in 1% OsO4 in 0.1 M cacodylate buffer at room temperature. Dehydration through a graded ethanol series and substitution for propylene oxide were followed by embedding in Araldite and Quetol 812 resin (Nissin EM, Japan) mixture. Ultrathin sections were cut with an ultramicrotome (UCT; Leica, Germany) and stained with 2% uranyl acetate for 5 min and then in a lead-staining solution (Sigma-Aldrich, USA) for 3 min. The sections were observed by TEM (JEM-1220; JEOL, Japan), and the digital images were obtained with an attached cooled CCD camera (Gatan, USA).
Observation of footpad formation during metamorphosis
We employed svpNP5606-GAL4 and svpNP0724-GAL4 lines to assess the development of footpads in Drosophila, and since both strains demonstrated similar expression patterns of GAL4 in the footpad hair cells, we designated both as svp-Gal4. Furthermore, the hair cells in the footpads of pupae with the genotype spa > mCD8::GFP, nucDsRed, or svp > Act5C::GFP, nucDsRed were labeled with mCD8::GFP or actin5C-GFP or nucleus-targeted DsRed, and were dissected at appropriate developmental stages. Briefly, the legs were dissected, and the pupal cuticles were removed. The legs were then fixed with 3.7% formaldehyde for 30 min and washed with phosphate-buffered saline (PBS) containing 0.3% Triton-X (PBS-Tx). For immunochemical analysis, specimen preparations were incubated with anti-GFP primary antibodies (1:500, rabbit polyclonal; A6455, Molecular Probes, Eugene, OR) for over 6 h at 25 °C. After washing, the tissues were treated with Cy2-conjugated goat anti-rabbit IgG secondary antibodies (1:500, Jackson Immuno-Research) for over 6 h at 25 °C.
To visualize cytoskeletal actin filaments, the specimens were stained with TexasRed-X phalloidin (Invitrogen, T7471), Acti-stainTM 555 phalloidin (Cytoskeleton, Inc. PHDH1-A), and Alexa FluorTM 633 (Invitrogen, A22284) for over 2 h. Images of the footpad were obtained with a Leica TCS SPE confocal microscope (Wetzlar, Germany) using Leica application suite advanced fluorescence (LAS AF) software.
Somatic clones were produced using the mosaic analysis with a repressible cell marker (MARCM) method, which allows for single-cell labeling by inducing chromosomal recombination, enabling marker expression only in rare clones. White pupae of the y hs-flp; FRTG13, UAS-mCD8::GFP/ FRTG13, TubP-GAL80; svp-GAL4/+ genotypes were collected and maintained for 6 h. They were then subjected to a heat-shock at 37 °C for 30 min. At 42 h APF, the pupae were dissected, and the legs were fixed with 10% formalin for 30 min and stained for immunohistochemistry analysis as described above.
Live images of footpad development were obtained during the pupal stage in svp > mCD8::GFP, nucDsRed, svp > Act5C::GFP, nucDsRed, or svp > mCD8::GFP,Act5C RNAi, elav-Gal80 flies. At 20 h APF, following the removal of the puparium, pupae were attached to a glass coverslip. The coverslip was then glued to a tissue culture slide (Lab-Tek), with the pupae facing downwards, with wax, leaving a small space next to the coverslip to avoid condensation. To prevent the preparation from drying, distilled water was added to a chamber in the tissue culture slide. Time-lapse images for GFP and DsRed-labeled cells were obtained every 20 min using the Leica TCS SPE confocal microscope. Under these experimental conditions, pupae that are lacking puparium will develop into adults.
RNAi-mediated knockdown of cytoskeletal actin in flies
To examine the effects of RNAi-mediated knockdown of cytoskeletal actin (Actin5C) on footpad formation in flies, Act5C RNAi was introduced into hair cells under the control of an svp-GAL4 driver. To avoid lethal effects in svp-Gal4 > Act5C RNAi flies, Act5C RNAi was introduced by one of the two methods. The first involves treatment with the RNAi after the formation of the puparium, using a temperature-sensitive suppressor Gal80TS of GAL4. The flies of svp > Act5C RNAi, TubP-GAL80TS were reared at 18 °C during the larval stages. The prepupae obtained at 0–12 h APF were then transferred to 30 °C and maintained at a controlled temperature. Using these conditions, some adult flies were enclosed, and the morphology of their footpads was examined by SEM. The second method of introduction protects against the adverse effects of Act5C RNAi on the nervous system using elav-GAL80. Using this method, the flies of svp > Act5C RNAi, elav-Gal80 survived to adulthood, and we were able to observe the effects of Act5C knockdown on footpad formation. We counted the number of hairs with malformed tips among 15 hairs from three distal rows in one stalk of each footpad.
To assess the ability of knockdown flies to climb effectively, adults were collected within 24 h of being enclosed and maintained in vials containing Kimwipe paper soaked in 20 mM sucrose solution. Each female fly, at 24–48 h after having been enclosed, was placed in a Pasteur pipette, both sides of which were then plugged with cotton. The fly was gently tapped down to the bottom of the pipette and assessed for its climbing ability using a video recorder (Evrio JVC, Japan) for 1 min. The time required to climb the vertical glass wall of a Pasteur pipette from the bottom to its constriction site (8 cm) was recorded. In addition, the number of flies capable of overcoming the constriction point of the Pasteur pipette within 1 min was determined. Data from flies that were unable to reach the constriction point within 1 min were discarded to calculate the average times. The flies used were of genotypes+: + (CS strain), +/+; svp-GAL4/+, UAS-Act5C RNAi/+; elav-Gal80/+ as controls and svp > Act5C RNAi, elav-Gal80 for experimental strains.
Manufacturing the biomimetic fiber-framed adhesive structure
Nylon fibers with a diameter of 52 µm, sodium alginate solution (1 wt%), and calcium lactate solution (1 wt%) were prepared for the fabrication of the spatulate structure. At first, two nylon fibers at 2-mm intervals were fixed on a paper at one extremity. The fibers were then dipped in a sodium alginate solution and then lifted up from it. When the fibers were removed from the sodium alginate, a spatulate structure was formed owing to the surface tension of the solution29,30. The structures were then placed in a calcium lactate solution, where they solidified. After air-drying, the spatula was cut out from the paper substrate. The hair-like structures were hydrated prior to use. The area of the spatulate structure was 1.2 mm2 ± 0.1 (mean ± SE, n = 11). The whole process was carried out at 23 °C.
Shear force measurement
Adhesive testing of fly-mimetic hair structures was performed on a glass substrate at 23 °C using a load cell force transducer with a 980 mN capacity (World Precision Instruments, Sarasota, FL, USA). Before performing the assay, the glass substrate was cleaned in an ultrasonic bath with acetone, ethanol, and distilled water for 10 min. The test was carried out after dipping our artificial hair structures in water. The amount of water loaded on the structure during dipping was 560 ± 5 µg (mean ± SE, n = 6). Shear force measurements were performed by moving the glass substrate at a lateral speed of 24 mm/min.
Statistics and reproducibility
Statistical tests were performed in Microsoft Excel using BellCurve for Excel (version 3.20) software. The appearance of malformed (forked) hairs in Act5C knockdown flies was compared to that in the control in CS flies, using one-way ANOVA followed by Tukey–Kramer test. P-values are shown on the top of the graph. The evaluation of statistical significance of differences of the average times taken to climb the vertical glass wall was performed with one-way ANOVA and Tukey–Kramer test to compare wild-type and Act5C knockdown flies. Climbing assay to compare the percentage of flies capable of overcoming the constriction was analyzed using Kruskal–Wallis test, and post hoc pairwise comparisons were conducted using Scheff’s post hoc test. Measurements were acquired from distinct samples. Sample sizes for each experiment and P-values obtained from individual statistical analyses are indicated in the figures. The reproducibility in experimental qualitative data such as immunostaining or fluorescence-staining was verified by repeating the analyses in at least five biological samples, independently. All replication attempts were successful. Sample sizes for each measurement experiment concerning the biomimetic fiber-framed adhesive structure are also described in the texts and figure legends.
Further information on research design is available in the Nature Research Reporting Summary linked to this article.
The data that support the findings of this study are available from the corresponding author upon reasonable request. Source data underlying plots are provided in Supplementary Data 1.
West, T. The foot of the fly; its structure and action: elucidated by comparison with the feet of other insects. Trans. Linn. Soc. Lond. 23, 393–421 (1862).
Gorb, S. N. Attachment Devices of Insect Cuticle (Kluwer Academic Publishers, 2001).
Beutel, R. G. & Gorb, S. N. Ultrastructure of attachment specializations of hexapods (Arthropoda)-evolutionary patterns inferred from a revised ordinal phylogeny. J. Zool. Syst. Evol. Res. 39, 177–207 (2001).
Betz, O. Structure of the tarsi in some Stenus species (Coleoptera, Staphylinidae): external morphology, ultrastructure, and tarsal secretion. J. Morphol. 255, 24–43 (2003).
Voigt, D., Schuppert, J. M., Dattinger, S. & Gorb, S. N. Sexual dimorphism in the attachment ability of the Colorado potato beetle Leptinotarsa decemlineata (Coleoptera: Chrysomelidae) to rough substrates. J. Insect Physiol. 54, 765–776 (2008).
Langer, M. G., Ruppersberger, J. P. & Gorb, S. Adhesion forces measured at the level of a terminal plate of the fly’s seta. Proc. R. Soc. B Biol. Sci. 271, 2209–2215 (2004).
Ishii, S. Adhesion of a leaf feeding ladybird Epilachna vigintioctomaculata (Coleoptera: Coccinellidae) on a vertically smooth surface. Appl. Entomol. Zool. 22, 222–228 (1987).
Kosaki, A. & Yamaoka, R. Chemical composition of footprints and cuticula lipids of three species of lady beetles. Jpn. J. Appl. Entomol. Zool. 40, 47–53 (1996).
Ferris, G. F. External morphology of the adult. in Biology of Drosophila (ed Demerec, M.) 368–419 (Cold Spring Harbor Laboratory Press, 1950).
Hüsken, M. et al. Adhesive pad differentiation in Drosophila melanogaster depends on the Polycomb group gene Su(z)2. J. Exp. Biol. 218, 1159–65 (2015).
Whitten, J. M. Coordinated development in the fly foot: sequential cuticle secretion. J. Morph. 127, 73–104 (1969).
Kojima, T. The mechanism of Drosophila leg development along the proximodistal axis. Dev. Growth Differ. 46, 115–29 (2004).
Lee, T. & Luo, L. Mosaic analysis with a repressible cell marker for studies of gene function in neuronal morphogenesis. Neuron 22, 451–461 (1999).
Röper, K. Integration of cell-cell adhesion and contractile actomyosin activity during morphogenesis. Curr. Top. Dev. Biol. 112, 103–127 (2015).
McGuire, S. E., Le, P. T., Osborn, A. J., Matsumoto, K. & Davis, R. L. Spatiotemporal rescue of memory dysfunction in Drosophila. Science 302, 1765–1768 (2003).
Rideout, E. J., Dornan, A. J., Neville, M. C., Eadie, S. & Goodwin, S. F. Control of sexual differentiation and behavior by the doublesex gene in Drosophila melanogaster. Nat. Neurosci. 13, 458–466 (2010).
Gloyna, K., Thieme, T., Gorb, S. & Voigt, D. New results on the sexual dimorphism in tarsal adhesive setae of Diabrotica virgifera virgifera LeConte (Coleoptera, Chrysomelidae, Galerucinae). Eur. J. Environ. Sci. 4, 15–19 (2014).
Bullock, J. M., Drechsler, P. & Federle, W. Comparison of smooth and hairy attachment pads in insects: friction, adhesion and mechanisms for direction-dependence. J. Exp. Biol. 211, 3333–3343 (2008).
Gilet, T., Gernay, S. M., Aquilante, L., Mastrangeli, M. & Lambert, P. Adhesive elastocapillary force on a cantilever beam. Soft Matter 15, 3999–4007 (2019).
Bullock, J. M. & Federle, W. Division of labour and sex differences between fibrillar, tarsal adhesive pads in beetles: effective elastic modulus and attachment performance. J. Exp. Biol. 212, 1876–1888 (2009).
Niederegger, S. & Gorb, S. N. Tarsal movements in flies during leg attachment and detachment on a smooth substrate. J. Insect Physiol. 49, 611–620 (2003).
Gernay, S. M., Labousse, S., Lambert, P., Compère, P. & Gilet, T. Multi-scale tarsal adhesion kinematics of freely-walking dock beetles. J. R. Soc. Interface 14, 20170493 (2017).
Pattantyus-Abraham, A., Krahn, J. & Menon, C. Recent advances in nanostructured biomimetic dry adhesives. Front. Bioeng. Biotechnol. 1, 22 (2013).
Li, Y., Krahn, J. & Menon, C. Bioinspired dry adhesive materials and their application in robotics: a review. J. Bionic Eng. 13, 181–199 B (2016).
Eisenhaure, J. & Kim, S. A review of the state of dry adhesives: biomimetic structures and the alternative designs they inspire. Micromachines 8, 125 (2017).
Hosoda, N. The mechanisms of organisms as eco-materials design tools. in Handbook of Sustainable Engineering (eds Kauffman, J. & Lee, K. M.) 1249–1261 (Springer, 2013).
Peisker, H., Michels, J. & Gorb, S. N. Evidence for a material gradient in the adhesive tarsal setae of the ladybird beetle Coccinella septempunctata. Nat. Commun. 4, 1661 (2013).
Mirth, C. Ecdysteroid control of metamorphosis in the differentiating adult leg structures of Drosophila melanogaster. Dev. Biol. 278, 163–174 (2005).
Duprat, C. & Protière, S. Capillary stretching of fibers. EPL 111, 56006 (2015).
Duprat, C., Protière, S., Beebe, A. Y. & Stone, H. A. Wetting of flexible fibre arrays. Nature 482, 510–513 (2012).
We would like to thank T. Kojima, C. Mirth, S.F. Goodwin, the Kyoto Stock Center, VDRC (Vienna Drosophila Resource Center), and BDSC (Bloomington Drosophila Stock Center) for the various Drosophila strains. We would also like to thank A. Izumi, C. Sato, Y. Koizumi (HUE), H. Niu (National Institute for Materials Science: NIMS), and K. Koitabashi (NIMS) for their technical assistance. This work was supported by a Grant-in-Aid for Scientific Research on Innovative Areas from the Ministry of Education, Culture, Sports, Science, and Technology (MEXT) of Japan to K.-I.K. and T.H. (No. 24120004) and by “Seeds” Development Research Grants of NIMS to N.H.
The authors declare no competing interests.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Kimura, Ki., Minami, R., Yamahama, Y. et al. Framework with cytoskeletal actin filaments forming insect footpad hairs inspires biomimetic adhesive device design. Commun Biol 3, 272 (2020). https://doi.org/10.1038/s42003-020-0995-0