Abstract
Magnetocapacitance (MC) effect has been observed in systems where both symmetries of time-reversal and space-inversion are broken, for examples, in multiferroic materials and spintronic devices. The effect has received increasing attention due to its interesting physics and the prospect of applications. Recently, a large tunnel magnetocapacitance (TMC) of 332% at room temperature was reported using MgO-based (001)-textured magnetic tunnel junctions (MTJs). Here, we report further enhancement in TMC beyond 420% at room temperature using epitaxial MTJs with an MgAl2O4(001) barrier with a cation-disordered spinel structure. This large TMC is partially caused by the high effective tunneling spin polarization, resulted from the excellent lattice matching between the Fe electrodes and the MgAl2O4 barrier. The epitaxial nature of this MTJ system sports an enhanced spin-dependent coherent tunneling effect. Among other factors leading to the large TMC are the appearance of the spin capacitance, the large barrier height, and the suppression of spin flipping through the MgAl2O4 barrier. We explain the observed TMC by the Debye-Fröhlich modelled calculation incorporating Zhang-sigmoid formula, parabolic barrier approximation, and spin-dependent drift diffusion model. Furthermore, we predict a 1000% TMC in MTJs with a spin polarization of 0.8. These experimental and theoretical findings provide a deeper understanding on the intrinsic mechanism of the TMC effect. New applications based on large TMC may become possible in spintronics, such as multi-value memories, spin logic devices, magnetic sensors, and neuromorphic computing.
Similar content being viewed by others
Introduction
Magnetocapacitance (MC) effect has been getting much attention due to the fascinating spin physics and potential applications1,2,3,4. MC effect appears in a system with broken time-reversal and space-inversion symmetry, such as in multiferroic materials5,6 and spintronic devices2,3,4,7,8,9,10. More recently, it has been observed in magnetic supercapacitors11,12, organic heterojunctions13,14, graphene-based two-dimensional (2D) materials15,16, and three-dimensional (3D) topological insulators17,18. These materials or devices have prospects for applications in high-performance magnetic sensors, memory devices, and data storage systems2,3,4,5,6,7,8,9,11,12,13,14.
Magnetic tunnel junctions (MTJs)4,8,19 are a common spintronic device and can exhibit a large MC effect at room temperature, often referred to as tunnel magnetocapacitance (TMC)2,3,4,7,8,9. MTJs are also known to show a large tunnel magnetoresistance (TMR) effect20,21,22,23,24,25,26. TMC’s unique properties include a relative larger TMC (measured in percentage) over TMR at some specific frequencies4, good thermal stability in TMC19, and robustness of TMC against a bias voltage as opposed to a bias-induced TMR drop8. Recently, by optimizing appropriate frequencies and bias voltages, a large TMC of 332% was achieved in MgO-based MTJs at room temperature27. The core structure of MTJs is Co40Fe40B20/MgO/Co40Fe40B20, leading to a textured CoFe/MgO/CoFe(001) interfacial structure promoted by an annealing process. Based on the Debye-Frölich (DF) modelled calculation, the spin polarization which contributes to TMC is 47.7% in this MTJ system.
The lattice-mismatch between rock-salt MgO and bcc ferromagnetic (FM) electrodes (Fe, CoFe, etc.) prevents further improvement in the properties of MgO-based MTJs. An alternative barrier, a spinel MgAl2O4 (MAO), is a good candidate for MTJs, as the new barrier maintains the Δ1-preferential coherent tunneling effect, which is necessary acquiring a large TMC effect28,29,30,31,32,33,34,35. The crystalline MAO barrier is superior to MgO in in-plane lattice matching with bcc-electrodes—~ 0.404 nm in MgAl2O4(200) versus ~ 0.421 nm in MgO(100)29,30. However, the first-principle band calculation predicts that an effective dc-tunneling spin polarization through Fe/MgAl2O4/Fe(001) is much smaller than that through Fe/MgO/Fe(001) due to the appearance of additional Δ1 conduction channels in minority spin states originating from a band-folding effect of Fe36. Introducing cation site disordering into the spinel structure that accompanies the crystal symmetry change from \(Fd\overline{3} m\) to \(Fm\overline{3} m\) or \(F\overline{4} 3m\) (cation-disordered spinel structure) reduces the lattice unit size to half of the primitive MgAl2O4, which effectively suppresses the band-folding effect30,37; a TMR ratio of Fe/cation-disordered MAO/Fe(001) reaches ~ 436% at low temperature (245% at room temperature)32, which is far beyond the calculated upper limit of ~ 160% in Fe/cation-ordered MAO/Fe(001). Since the corresponding dc spin polarization is over ~ 60%, a giant TMC beyond conventional values could be observed.
In this work, we report the largest TMC of 426% in MTJs with cation-disordered spinel MAO barriers at room temperature. The frequency characteristics and voltage dependence of TMC can be well explained by the calculations based on modified DF model combined with Zhang formula, sigmoid function, parabolic barrier approximation (PBA), and spin-dependent drift–diffusion (SDD) mechanism. This means that the large TMC is attributed to the spin capacitance appeared in Fe/MAO interfaces, the formation of MAO high barrier and the suppression of spin flipping through an MAO barrier. The calculation also predicts that TMC could reach 1000% in MTJs with a high spin polarization of 80%. Our findings open a new avenue to the development of spintronics applications.
Results and discussion
Device structures
Figure 1a shows the device structure prepared by a high vacuum dc/rf magnetron sputtering system, in a base pressure of 5 × 10−7 Pa, with the following layer sequence: MgO(001) single-crystal substrate/Cr (40)/Fe (30)/Mg (0.45)/Mg19Al81 (dMgAl ~ 1.22–1.25)/ oxidation/Fe (7)/Ir20Mn80 (IrMn) (12)/Ru (12) (unit: nm). Details of the device fabrication procedure are described in the Experimental Section. After the growth of the multilayer stack, the MTJ structures were patterned into a junction area of 5 × 10 μm2 with an elliptical shape using typical microfabrication processes including photolithography and Ar ion-beam etching.
The current–voltage (I-V) characteristics and TMR curves in MTJs were measured using a dc four-probe method at room temperature. The magnetic field was applied along Fe[100] || MAO[110] up to 300 Oe. A typical TMR curve is shown in Fig. 1b. A large TMR ratio of 180% is observed, indicating the achievement of optimum oxidation of the MAO interfaces. Here, the TMR ratio is defined by \((R_{{\rm{AP}}} - R_{\rm{P}} )/R_{\rm{P}}\), where RP(AP) is the resistance in the parallel (anti-parallel) magnetization states of both FM layers. The corresponding dc tunneling spin polarization is 68.8%. The large TMR also indicates the formation of an epitaxial MAO barrier30. In this study, two MTJs with a TMR ratio of 174% (sample A, dMgAl = 1.25 nm) and 183% (sample B, dMgAl = 1.22 nm) were used for TMC measurements.
Frequency characteristics of TMC under no bias voltage
Figure 2 shows the TMC and TMR curves at 60 Hz, 140 Hz, 40 kHz, and 1 MHz for samples A and B, respectively. The bias voltage is ~ 0 V. Positive TMC and TMR effects are observed at each frequency. TMR ratios are independent of the frequency, and are 174% and 183% for samples A and B, respectively. Here, the TMC ratio is defined by \((C_{\rm{P}} - C_{{\rm{AP}}} )/C_{{\rm{AP}}}\), where CP(AP) is the capacitance in the parallel (anti-parallel) magnetization states for both FM layers. The TMC ratio increases with increasing the frequency in the low frequency region, and it reaches 227% (223%) at 140 Hz for sample A (B). The TMC of 227% (223%) is larger than the conventional value of 172%, which is observed in MgO-based MTJs27. As increasing the frequency, the TMC decreases to 10.5% (10.3%) at 40 kHz, and it slightly increases to 13.2% (16.1%) for sample A (B). Here we note that the TMC and TMR curves are slightly different with different frequency. Although the reason is not clear at the present stage, the TMC and TMR are sensitive to the magnetization states of Fe layers in Fe/MAO interfaces. The magnetization states of Fe layers slightly change depending on the interfacial structures, magnetic pinning, domain wall motion, etc. These factors could cause the slight changes in TMC and TMR curves. As is well known, the spin transfer torque (STT) switching is observed in MTJs with a junction area of smaller than a few 100 nm scale (single domain scale for in-plane magnetized films) and with a thin free layer (less than a few nm). For examples, it is observed in CoFe/MgO/CoFe MTJs with a junction area of 100 × 150 nm2, 100 × 200 nm2, or 100 × 300 nm2 and with a free-layer thickness of 1.8–2.6 nm38, and in CoFe/MgO/CoFe MTJ pillars with a diameter of 40 or 100 nm and with a free-layer thickness of 1.0 − 1.7 nm39. In contrast, the junction area of the MTJs fabricated in this study is as large as 5 × 10 μm2 and the thickness of the Fe free layer is 30 nm. Therefore, it is considered that STT switching cannot be expected in our MTJs. The voltage-controlled magnetic anisotropy (VCMA) can be observed in MTJs with an FM layer thickness of less than a few nm. For examples, it is demonstrated in Fe/MgO structures with 2 − 4 Fe monolayers with strong perpendicular magnetic anisotropy40, and in Fe(0.5)/Ir(0.1)/CoFe(0.1)/MgO (numbers are nominal thicknesses in nanometers) MTJs41. Therefore, it is considered that VCMA cannot be significant in our MTJs that have thicker Fe layers and in-plane anisotropy. The frequency characteristics of TMC, TMR, and CP(AP) are shown in Fig. 3. CP(AP) at frequency f is calculated by the following DF model:
where \(C_{{\infty ,\rm{P(AP)}}}\) and \(C_{{0,\rm{P(AP)}}}\) are the high-frequency and DC capacitances, τP(AP) is the relaxation time, and βP(AP) is the exponent showing the distribution of relaxation time, respectively, for the P (AP) configuration. The relation between τP and τAP is given by
where PTMC is the spin polarization, contributing to TMC, inside the FM layer4,42. TMR is calculated using the Julliere formula43. As shown in Fig. 3, the calculation results of TMC, CP(AP), and TMR fit to the experimental data well. The parameters obtained in the fitting calculation are shown in Table S1. We obtain PTMC of 0.594 (0.627) and PTMR, contributing to TMR, of 0.682 (0.691) for sample A (B) by the fit. Here we note that PTMC is lower than PTMR for samples A and B. The difference between PTMC and PTMR is attributed to the different penetration lengths of spin-dependent carriers (electrons or holes inside Fe) for TMC and TMR. The penetration length of TMC is considered to be longer than that of TMR4. The spin polarization of the interfacial FM atoms between FM/insulator layers is higher than that of inner atoms from the interface atoms due to the two-dimensional effect44,45,46,47. In our cases, the spin polarization of the interfacial atoms in Fe layers is also considered to be higher than that of inner atoms from the Fe/MAO interface. Therefore, PTMC(TMR) is low (high) for a long (short) penetration length. Our calculation also indicates that higher PTMR generally gives higher PTMC. Since the spin polarizations PTMC and PTMR of sample B are larger than that of sample A, the bias voltage dependences of TMC and TMR in sample B are investigated (as for sample A, see the supplementary information).
Observation of a large TMC by biasing dc voltage
Figure 4 shows the bias voltage dependence of TMC and TMR curves at 140 Hz in sample B. TMR decreases from 183% to 116% with increasing the voltages up to 500 mV in the positive bias region. The same tendency can be seen in the negative region. The reduction of TMR can be attributed to spin flipping process in the AP configuration by interface magnetic excitation48 in addition to the effect of the Fe band structure49. In contrast, the TMC ratio increases with increasing the voltage in the positive bias region, and it reaches 426% at 325 mV. A TMC of 426% is the largest value ever reported for MTJs. As increasing the voltage higher than 325 mV, the TMC ratio decreases to 203% at 500 mV. In the negative bias region, the TMC ratio decreases with the increase of bias voltage. Figure 5 shows the bias dependence of TMC, TMR, and CP(AP) at 60 Hz, 140 Hz, and 40 kHz. The TMC and TMR curves at 60 Hz and 40 kHz are shown in Fig. S1. As described above, at 140 Hz, the TMC reaches 426% at 325 mV in the positive bias region, and then it rapidly drops at a higher voltage of 325 mV. In the negative bias region, the TMC shows plateau behavior from 0 to − 150 mV, and then it drops sharply. After that, it slightly decreases. At 60 Hz, in contrast, the TMC shows the almost the same behavior as the TMR. At 40 kHz, the TMC tends to increase with increasing the voltage in the bipolar bias regions. The model calculation of the bias dependence of the TMC and CP(AP) is performed using SDD model and DF model combined with PBA and Zhang-sigmoid formula. In the modified DF model, the capacitance based on PBA and Zhang-sigmoid formula for the P (AP) configuration under the bias voltage V can be expressed by
Here, the coefficient of the real part of the capacitance in Eq. (3) is determined by PBA, which describes the bias voltage dependence of the effective barrier thickness50. ϕ0,P(AP) is the barrier height in the absence of the bias voltage for the P (AP) configuration, \(e\) is the electron charge, and κ is the parameter determined by the contributing ratio of the dynamic capacitance to the overall capacitance. \(C_{{\infty ,\rm{P(AP)}}}\), \(C_{{0,\rm{P(AP)}}}\), and βP(AP) in the real part of the capacitance are the same parameters in Eq. (1). The relaxation time can be expressed by
Here KP(AP), which is appeared in Zhang model, is the parameter determined by Curie temperatures of FM layers, the density of states of itinerant electrons in FM layers, and direct and spin-dependent transfers and spin quantum number within the framework of the transfer Hamiltonian in the system of FM/insulator/FM. τP(AP),0 is the relaxation time for the P (AP) configuration under no bias voltage. The sigmoid function under the application of bias voltage can be expressed by
where αP(AP) is the broadening of the contributing rate of dynamic capacitance to the overall capacitance in the P (AP) configuration and V0,P(AP) is the voltage for spin flipping. Thus, the Zhang-sigmoid formula gives the bias voltage dependence of the relaxation time27. Based on the SDD model for the static case, the spin capacitance can be given by
where S is a junction area, λ is a characteristic screening length and en0,P(AP) is a screening charge density at the interface. Therefore, the total capacitance \(C_{{\rm{P(AP),}V}} (f)\) at the bias voltage V is given by
The bias voltage dependence of the TMC ratio at frequency f can be calculated using Eqs. (3)−(7). As can be seen in Fig. 5, the experimental data provide an excellent fit to the calculation results in the entire bias region at each frequency. The parameters obtained in the fitting calculation are shown in Table S2. Here we discuss the mechanism of a large TMC based on the fitting analysis. As shown in Fig. 5b, since both the CP and CAP decrease with increasing the voltage from 0 to 325 mV, the large TMC is observed in this region. Based on the PBA, a biasing voltage reduces the effective barrier thickness of the insulating layer, resulting in the increase of CP(AP). Also, based on the Zhang-sigmoid model, the relaxation time becomes shorter with increasing the voltage, and it rapidly shortens near the spin-flipping voltage V0,P(AP). This results in the gradual increase of CP(AP) including the rapid increase at the threshold voltage V0,P(AP). Since the observed CP and CAP decrease with increasing the voltage, the PBA and Zhang-sigmoid model do not mainly contribute to the capacitance. In contrast, the SDD model describes the spin capacitance that appears in the FM/insulator interface due to the deference in chemical potential between both the FM layers. Since the spin capacitance can be expressed by Eq. (7), the CP(AP) decreases with increasing the voltage. The decrease of capacitance by biasing agrees with the observed results. This means that the SDD model is dominant in the bias region from 0 to 325 mV, indicating that the large TMC originates from the appearance of spin capacitance (See Fig. 6).
We also note that the asymmetry behavior can be seen in the bias dependences of TMC and CP(AP). The CP and CAP increase with increasing the voltage in the negative bias region. This means that the PBA mainly contributes to the observed capacitance (See Fig. 6a). This is consistent with the fitting analysis that the barrier height ϕ0,P(AP) in the negative bias region is lower than that in the positive bias region as shown in Table S2. As the barrier height is low, the effective barrier thickness becomes thin with applying the voltage. Moreover, we notice that the jump-up of CAP can be seen at around + 325 mV and − 175 mV. This indicates that the spin flipping occurs at a higher than + 325 mV and − 175 mV in the positive and negative bias regions, respectively. This is also consistent with the fitting results that the spin-flipping voltage V0,AP is + 310 mV and − 153 mV in the positive and negative bias regions, respectively. Therefore, Zhang model contributes to the observed capacitance in addition to the SDD model in the positive bias region and PBA in the negative bias region (See Fig. 6a). Although the method to control the threshold bias Vth is not clear at the present stage, it could depend on materials; Vth = ~ 100 mV for CoFe/MgO/CoFe MTJs27 and Vth = ~ 300 mV for Fe/MAO/Fe MTJs in this study. The threshold bias could be controlled by changing materials, thicknesses and crystal structures of MTJ layers. As shown in Fig. 5a,c, there is also an excellent agreement between theory and experimental results for the TMC in the entire voltage regions at 60 Hz and 40 kHz. This means that the mechanism of TMC properties can be explained by the fitting analysis in the same manner. As for sample A, the experimental data are also in good agreement with calculation results, as shown in Figs. S2 and S3. The parameters obtained in the fitting calculation are shown in Tables S1 and S2.
Prediction of an extremely large TMC and high-frequency shift
Successful modelling allows us to predict an extremely large TMC by the development of MTJs with a higher spin polarization. Figure 7a shows the calculated voltage dependence of TMC with varying the spin polarization of FM layers. The main parameters used in the calculation are the same as that in the calculation of TMC in sample B at 140 Hz (See Tables S1 and S3, 140 Hz). As can be seen from Fig. 7a, even though the spin polarization PTMC only increases from 0.627 to 0.8, the maximum TMC ratio is expected to increase from 393% to 892%. Figure 7b shows the frequency characteristics assuming TMC at VDC = 325 mV and PTMC = 0.8 with different relaxation times τP. The other parameters are the same as in Tables S1 and S3 (140 Hz). The maximum TMC is 1060% at 230 Hz, 23 kHz, and 2.3 MHz for τP of 3.9 ms, 39 μs, and 0.39 μs, respectively. This indicates that the peak of TMC is shifted to a high frequency region on the order of MHz when a short τP in the sub-μs scale is achieved. The DF model suggests that the relaxation time is determined by the oscillation speed of electric dipoles formed near the interfaces between an FM layer and an insulator. The relaxation time is short in a high oscillation speed. For a short relaxation time, the thickness of the insulator should be thinner. Therefore, the formation of a thinner MAO layer is necessary for high-frequency operation. In fact, recently reported papers demonstrate a high-frequency operation of ~ 100 MHz, corresponding to a relaxation time of sub ns, in FeCo-MgF and Co-MgF nanogranular tunneling systems, respectively9,51. The high-frequency shift of TMC will be of great importance for future spintronic applications, such as magnetic read heads and memory devices.
In summary, we observed a large TMC of up to 426% in Fe/MAO/Fe MTJs at room temperature, which is the largest value in MTJs. The large TMC originates from a high spin polarization of 62.7% due to the reduced spin scattering process under bias voltage application by excellent lattice matching between Fe and MAO and the appearance of spin capacitance in Fe/MAO interfaces. Additionally, the high barrier height of MAO (1.8–2.0 eV) and the spin flipping suppressed in the low bias region from 0 to 325 mV are important features. These physical pictures can be understood by the static SDD model and dynamic DF model incorporating PBA and Zhang-sigmoid model. This model predicts that the TMC could potentially exceed 1000% in MTJs when a spin polarization reaches 80%. Our theoretical and experimental findings provide new insights into the exact mechanism of the TMC effect in MTJs. The prospect of increasingly larger TMC opens exciting opportunities for new spintronics applications. MTJs endowed with a giant TMR and TMC are superior magnetic and spintronic devices rich in spin-dependent physics and ready for unexplored electrical engineering designs over a wide frequency range.
Methods
Preparation of the samples
The MTJs were prepared by using a high vacuum magnetron sputtering system in a base pressure of 5 × 10−7 Pa, with the following layer sequence: MgO(001) single-crystal substrate/Cr (40)/Fe (30)/Mg (0.45)/Mg19Al81 (dMgAl = 1.22 and 1.25 nm)/oxidation/Fe (7)/IrMn (12)/Ru (12) (unit: nm). We deposited the Cr, Fe, Mg, IrMn, and Ru layers in DC mode and the MgAl layer in radio frequency (RF) mode with magnetron sputtering under an Ar gas pressure of 0.1 Pa. An MAO barrier was formed by direct inductively coupled plasma (ICP) oxidation of the Mg/MgAl bilayer. The ICP oxidation used an input RF power density of 0.24 W/cm2 under an O2 + Ar mixture gas (total 6 Pa) for 45 s. The detailed condition is described in Ref.30. After the growth of the multilayer stack, the MTJ structures were patterned into a junction area of 5 × 10 μm2 with an elliptical shape by using photolithography, Ar ion-beam etching, and SiO2 insulation sputtering. The MTJs were annealed at 175 °C in a vacuum furnace (base pressure: ~ 10−5 Pa) under a 5 kOe magnetic field for an hour along Fe[100] to induce exchange bias for the top Fe layer.
Measurements of the voltage-induced TMC
The frequency characteristics and the bias voltage dependence of the TMC and TMR for MTJs were measured by an AC four-probe method using the Agilent Technologies 4284A LCR meter at room temperature. The frequency ranged from 60 Hz to 1 MHz and the bipolar bias voltage was applied up to 500 mV. The AC voltage was set at 50 mVrms. The magnetic field was applied along Fe[100] || MAO[110] up to 300 Oe.
Data availability
All data generated or analyzed during this study are included in this published article and its supplementary information files.
References
Rondinelli, J. M., Massimiliano, S. & Nicola, A. S. Carrier-mediated magnetoelectricity in complex oxide heterostructures. Nat. Nanotechnol. 3, 46–50 (2008).
Kobayashi, N., Masumoto, H., Takahashi, S. & Maekawa, S. Giant dielectric and magnetoelectric responses in insulating nanogranular films at room temperature. Nat. Commun. 5, 4417 (2014).
Lee, T. H. & Chen, C. D. Probing spin accumulation induced magnetocapacitance in a single electron transistor. Sci. Rep. 5, 13704 (2015).
Kaiju, H. et al. Large magnetocapacitance effect in magnetic tunnel junctions based on Debye-Fröhlich model. Appl. Phys. Lett. 107, 132405 (2015).
Kimura, T. et al. Magnetic control of ferroelectric polarization. Nature 426, 55–58 (2003).
Wang, J. et al. Epitaxial BiFeO3 multiferroic thin film heterostructures. Science 299, 1719 (2003).
Kaiju, H. et al. Inverse tunnel magnetocapacitance in Fe/Al-oxide/Fe3O4. Sci. Rep. 7, 2682 (2017).
Kaiju, H. et al. Robustness of voltage-induced magnetocapacitance. Sci. Rep. 8, 14709 (2018).
Ikeda, K., Kobayashi, N., Arai, K.-I. & Yabukami, S. Magnetoelectric effect in nanogranular FeCo-MgF films at GHz frequencies. J. Magn. Magn. Mater. 446, 80–86 (2018).
Hong, J. Y., Chen, S. H., Chiang, W. C. & Lin, M.-T. High-frequency magnetocapacitance effect in organic spin valve with a 3,4,9,10-perylene-teracarboxylicdianhydride spacer. SPIN 4, 1440015 (2014).
Zhu, J. et al. Magnetocapacitance in magnetic microtubular carbon nanocomposites under external magnetic field. Nano Energy 6, 180–192 (2014).
Pal, S. et al. Magnetic field induced electrochemical performance enhancement in reduced graphene oxide anchored Fe3O4 nanoparticle hybrid based supercapacitor. J. Phys. D: Appl. Phys. 51, 375501 (2018).
He, L., Li, M., Urbas, A. & Hu, B. Optically tunable magneto-capacitance phenomenon in organic semiconducting materials developed by electrical polarization of intermolecular charge-transfer states. Adv. Mater. 26, 3956 (2014).
Luan, L., Wang, K. & Hu, B. Sign reversal of magneto-capacitance in an organic heterojunction based opto-spintronic system. J. Mater. Chem. C 6, 4671 (2018).
Tahir, M. & Schwingenschlögl, U. Magnetocapacitance of an electrically tunable silicene device. Appl. Phys. Lett. 101, 132412 (2012).
Zibrov, A. A. et al. Even-denominator fractional quantum Hall states at an isospin transition in monolayer graphene. Nat. Phys. 14, 930 (2018).
Tahir, M., Sabeeh, K. & Schwingenschlögl, U. Quantum capacitance of an ultrathin topological insulator film in a magnetic field. Sci. Rep. 3, 1261 (2013).
Kozlov, D. A. et al. Probing quantum capacitance in a 3D topological insulator. Phys. Rev. Lett. 116, 166802 (2016).
Parui, S. et al. Frequency driven inversion of tunnel magnetoimpedance and observation of positive tunnel magnetocapacitance in magnetic tunnel junctions. Appl. Phys. Lett. 109, 052401 (2016).
Miyazaki, T. & Tezuka, N. Giant magnetic tunneling effect in Fe/Al2O3/Fe junction. J. Magn. Magn. Mater. 139, L231–L234 (1995).
Moodera, J. S., Kinder, L. R., Wong, T. M. & Meservey, R. Large magnetoresistance at room temperature in ferromagnetic thin film tunnel junctions. Phys. Rev. Lett. 74, 3273–3276 (1995).
Butler, W. H., Zhang, X.-G., Schulthess, T. C. & MacLaren, J. M. Spin-dependent tunneling conductance of Fe|MgO|Fe sandwiches. Phys. Rev. B 63, 054416 (2001).
Mathon, J. & Umerski, A. Theory of tunneling magnetoresistance of an epitaxial Fe/MgO/Fe(001) junction. Phys. Rev. B 63, 220403R (2001).
Yuasa, S., Nagahama, T., Fukushima, A., Suzuki, Y. & Ando, K. Giant room-temperature magnetoresistance in single-crystal Fe/MgO/Fe magnetic tunnel junctions. Nat. Mater. 3, 868–871 (2004).
Parkin, S. S. P. et al. Giant tunnelling magnetoresistance at room temperature with MgO (100) tunnel barriers. Nat. Mater. 3, 862 (2004).
Ikeda, S. et al. Tunnel magnetoresistance of 604% at 300K by suppression of Ta diffusion in CoFeB/MgO/CoFeB pseudo-spin-valves annealed at high temperature. Appl. Phys. Lett. 93, 082508 (2008).
Ogata, K., Nakayama, Y., Xiao, G. & Kaiju, H. Observation and theoretical calculations of voltage-induced large magnetocapacitance beyond 330% in MgO-based magnetic tunnel junctions. Sci. Rep. 11, 13807 (2021).
Shan, R. et al. Demonstration of half-metallicity in fermi-level-tuned Heusler alloy Co2FeAl0.5Si0.5 at room temperature. Phys. Rev. Lett. 102, 246601 (2009).
Sukegawa, H. et al. Tunnel magnetoresistance with improved bias voltage dependence in lattice-matched Fe/spinel MgAl2O4/Fe(001) junctions. Appl. Phys. Lett. 96, 212505 (2010).
Sukegawa, H. et al. Enhanced tunnel magnetoresistance in a spinel oxide barrier with cation-site disorder. Phys. Rev. B 86, 184401 (2012).
Tao, B. S. et al. Long-range phase coherence in double-barrier magnetic tunnel junctions with a large thick metallic quantum well. Phys. Rev. Lett. 115, 157204 (2015).
Belmoubarik, M., Sukegawa, H., Ohkubo, T., Mitani, S. & Hono, K. MgAl2O4(001) based magnetic tunnel junctions made by direct sputtering of a sintered spinel target. Appl. Phys. Lett. 108, 132404 (2016).
Ikhtiar, et al. Giant tunnel magnetoresistance in polycrystalline magnetic tunnel junctions with highly textured MgAl2O4(001) based barriers. Appl. Phys. Lett. 112, 022408 (2018).
Yakushiji, K., Sugihara, A., Nakano, T. & Yuasa, S. Fully epitaxial magnetic tunnel junction on a silicon wafer. Appl. Phys. Lett. 115, 202403 (2019).
Coll, M. et al. Towards oxide electronics: A roadmap. Appl. Surf. Sci. 482, 1–93 (2019).
Miura, Y., Muramoto, S., Abe, K. & Shirai, M. First-principles study of tunneling magnetoresistance in Fe/MgAl2O4/Fe (001) magnetic tunnel junctions. Phys. Rev. B 86, 024426 (2012).
Sukegawa, H., Inomata, K. & Mitani, S. Post-oxidized Mg-Al-O (001) coherent tunneling barrier in a wide range of resistance-area products. Appl. Phys. Lett. 105, 092403 (2014).
Hayakawa, J. et al. Current-induced magnetization switching in MgO barrier magnetic tunnel junctions with CoFeB-based synthetic ferrimagnetic free layers. IEEE Trans. Magn. 44, 1962 (2008).
Ikeda, S. et al. A perpendicular-anisotropy CoFeB-MgO magnetic tunnel junction. Nat. Mater. 9, 721 (2010).
Maruyama, T. et al. Large voltage-induced magnetic anisotropy change in a few atomic layers of iron. Nat. Nanotechnol. 4, 158 (2009).
Nozaki, T. et al. Voltage-controlled magnetic anisotropy in an ultrathin Ir-doped Fe layer with a CoFe termination layer. APL Mater. 8, 011108 (2020).
Kobayashi, N., Iwasa, T., Ishida, K. & Masumoto, H. Dielectric properties and magnetoelectric effects in FeCo-MgF insulating nanogranular films. J. Appl. Phys. 117, 014101 (2015).
Julliere, M. Tunneling between ferromagnetic films. Phys. Lett. 54A, 225–226 (1975).
Fullerton, et al. Structure and magnetism of epitaxially strained Pd(001) films on Fe(001): Experiment and theory. Phys. Rev. 51, 6364 (1995).
Fujii, Y., Komine, T., Kai, T. & Shiiki, K. A theoretical study of interfacial structure of Co/Cu and Co/Pd multilayers. J. Phys. Condens. Matter 11, 9601 (1999).
Shiiki, K., Sakaguchi, N. & Kaiju, H. Effect of unoxidized residual Al at the boundary of Co/Al-oxide/Co junction on TMR estimated by LMTO band calculation. Thin Solid Films 505, 64 (2006).
Burton, J. D., Jaswal, S. S. & Tsymbal, E. Y. Atomic and electronic structure of the CoFeB/MgO interface from first principles. Appl. Phys. Lett. 89, 142507 (2006).
Zhang, S., Levy, P. M., Marley, A. C. & Parkin, S. S. P. Quenching of magnetoresistance by hot electrons in magnetic tunnel junctions. Phys. Rev. Lett. 79, 3744 (1997).
Yuasa, S., Fukushima, A., Kubota, H., Suzuki, Y. & Ando, K. Giant tunneling magnetoresistance up to 410% at room temperature in fully epitaxial Co∕MgO∕Co magnetic tunnel junctions with bcc Co(001) electrodes. Appl. Phys. Lett. 89, 042505 (2006).
Sheng, P. Fluctuation-induced tunneling conduction in disordered materials. Phys. Rev. B 21, 2180 (1980).
Cao, Y., Kobayashi, N., Ohnuma, S. & Masumoto, H. Composition-graded multilayer nanogranular films enabling broadband tunneling magneto-dielectric effect: Role of the granular distribution. Appl. Phys. Lett. 118, 032901 (2021).
Acknowledgements
This research was supported by the Grant-in-Aid for Scientific Research (B) (under Grant No. 21H01397) and Challenging Exploratory Research Program (No. 19K22093) funded by the Japan Society for the Promotion of Science (JSPS), the Dynamic Alliance for Open Innovation Bridging Human, Environment and Materials and the Cooperative Research Program of “Network Joint Research Center for Materials and Devices” funded by the Ministry of Education, Culture, Sports, Science, and Technology (MEXT), Research Project funded by the Center for Spintronics Research Network (CSRN) at Keio and Tohoku University. The work at Brown was supported by the U.S. National Science Foundation (NSF) under Grant No. OMA-1936221.
Author information
Authors and Affiliations
Contributions
H.K., H.S. and G.X. conceived and designed the experiments using the help of other authors. H.S. performed the sample preparation and structural analysis. K.S. and H.K. performed ac impedance measurements. K.S., K.O. and H.K. performed the theoretical analysis and calculation. All the authors contributed to analysing and interpreting the data, and to writing the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Sato, K., Sukegawa, H., Ogata, K. et al. Large magnetocapacitance beyond 420% in epitaxial magnetic tunnel junctions with an MgAl2O4 barrier. Sci Rep 12, 7190 (2022). https://doi.org/10.1038/s41598-022-11545-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-022-11545-6
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.