Abstract
This paper discusses the use of nanomaterials for the improved performance of time-of-flight particle detectors based on secondary electron emission (SEE). The purpose of the research presented in this paper is to find a nanomaterial that has a higher SEE than gold. In this article, we present a measurement of the SEE properties from 1D (one-dimensional) nanostructures of ZnO and ZnO/GaN (ZnO with GaN coating) composed of a mostly regular pattern of nanotubes grown on a thin Si3N4 substrate. The study was performed with 4.77 meV/u Au beam. We observed an average increase of 2.5 in the SEE properties from the 1D ZnO nanotubes compared to gold.
Similar content being viewed by others
Introduction
Stimulated electrons in the interaction of charged particles and radiation with matter which escape the material surface are called secondary electrons1. This secondary electron emission (SEE) is utilized in particle and radiation detectors2,3. The secondary electrons stimulated near the material surface have a better chance to escape the material, therefore nanomaterials may improve the SEE yield through the manipulation of material geometry. Further modification of the surface coating can be used to decrease the energy necessary for the electrons to leave the materials surface, further enhancing the SEE yield.
Significant work has been performed on the enhancement of SEE properties under different conditions for various applications, centered towards applications in flat screens4, the detection of electrons, and X-rays3. The 1D nanotubes were investigated by Cholewa et al.5. These results motivated the present study, wherein using nanomaterials in thin SEE detector for heavy ions was investigated. A typical detector of this type will utilize thin gold or carbon foil(s). The ions of interest will pass through the foil inducing SEE. The electrons will be collected with electrical fields and subsequently detected. An example of such a detector can be found in5.
In this work, we present the data from ZnO nanotubes and GaN coated ZnO nanotubes. ZnO nanotubes with a diameter of 1 µm and a length of 5 µm were employed for this research and the GaN was covered with 10 nm on the ZnO nanotubes6. Additionally, a 20 nm Au deposited on thin (1 µm) silicon nitride (Si3N4) substrate sample was used as a reference/normalization.
We also used thin (1 µm) Si3N4 foils as a substrate for ZnO nanotube growth.
Methods
All samples were prepared on a 1 µm thick Si3N4 windows from SILSON Ltd in the UK. To enhance the electric conductivity, for a more homogeneous electric field of the applied bias voltage, and for growing the nanostructures, chemical vapor deposited (CVD) graphene films were transferred on a Si3N4 substrate. Subsequently, position-controlled ZnO structures were grown via Metal Organic Vapor Phase Epitaxy (MOVPE), as described by Park et al.6. Following this, the GaN was coated on the ZnO nanotube arrays.
Sample preparation
Preparation of the substrate for the selective growth of ZnO nanotubes consisted of the deposition of a 50 nm of SiO2 growth mask on the CVD graphene films using the PECVD (Plasma-Enhanced Chemical Vapor Deposition) system. The oxide layer was annealed at 600° C in an oxygen rich condition to reduce the oxygen defect in the deposited SiO2 growth mask, which could lead to undesirable growth. The next step was to determine the pattern of the sample traces using electron beam lithography. The patterned SiO2 film was then dry etched with CF4 plasma, and the remains of the oxide layer on graphene films after the dry etching process was removed with buffered oxide etchant (BOE). Before any growth, samples were cleaned with acetone, isopropyl alcohol and nitric acid.
After the the ZnO nanotube growth (Fig. 1), they were coated with a GaN about 10 nm thick using low-pressure metal–organic phase epitaxy (MOVPE) using trimethyl-Ga (TMGa) as a precursor7. The GaN layer was deposited at both ends of ZnO nanotubes, and evenly coated along the side wall6,8.
The nanotube arrays were examined by scanning electron microscopy (SEM) and transmission electron microscopy (TEM) after production. And they presented uniform morphologies and high structural quality over a large area and could be prepared on a broad variety of substrates, including amorphous, metallic, flexible substrates and thin Si3N4 commercial films6.
Bottom-up growth of one-dimensional (1D) semiconductor nanostructures has been extensively studied for fabricating different nanodevices including sensors, light-emitting diodes, transistors, and photovoltaic cells9,10,11.
The proposed coating is based on the wide bandgap (Eg = 3.4 eV) semiconductor gallium nitride (GaN). The electrical conductivity of GaN can be controlled over a wide range through modifications to the film composition or structure. GaN is also refractory and chemically stable. Such material had been studied before8 with carbon ions and we observed higher SEE properties when compared with uncoated ZnO nanomaterial.
Experiment
All measurements were performed at GSI Helmholtzzentrum für Schwerionenforschung GmbH, Germany. A 4.77 meV/u gold beam was delivered by the UNILAC5,12,13 accelerator to the microbeam experiment setup. Details of the system forming a heavy ion microbeam in GSI is described by Fischer et al.5. The Au beam was focused to a ca. 0.1 mm beam spot. The heavy ions had sufficient energy, effectively penetrating the samples. The ions were stopped in a silicon surface barrier detector. A BURLE Electro-Optics channeltron Model 4028 was position 5 mm upstream from the target and a 180 V potential difference was applied between the sample surface and the channeltron, guiding the SEE electrons to the detector. Schematics of this experiment setup are shown in Fig. 1.
In order to assess the efficiency of the system, and to confirm there were no unknown sources of electrons, data was taken with the acquisition system triggering on the silicon detector, and then the trigger was changed to the channeltron signal. The shaped signal from the channeltron and the silicon detector were simultaneously recorded. The average beam intensity was less than 50 particle/s, leading to no acquisition dead-time.
When triggering the Si detector, the number of events where the Si detector had a valid signal, above noise, was equal to within 0.02% to the number of events from the channeltron. Therefore, all Au ions which passed the targets created secondary electrons, part of which were detected by the channeltron.
The Au ions pass through the investigated sample and halt in a Silicon detector. The channeltron registers secondary electrons collected from the surface of the target. The secondary electrons are schematically depicted with red and green arrows. The green arrows symbolize δ-electrons, which can create further secondary electrons if they encounter the sample surface In the inset, SEM pictures of the investigated nanostructures, to the left ZnO covered with GaN, and ZnO without coating to the right. The nanotubes, with spacing and diameters, are: 1.57 µm and 0.6–0.7 µm for the sample shown to the left; and 1.57 µm and 1–1.3 µm for the sample shown to the right. The approximate nanorod length is 5 µm, which is perpendicular to the surface.
In the data presented below, a gate requiring signal above noise for both silicon and channeltron detectors, was applied. Thus, selecting events where the gold ions pass through the sample, created secondary electrons and interact with the active volume of the Si detector. In order to provide an absolute comparison of the measured secondary electron yield (SEY) to other experiments, we measured the SEY from the gold sample. The SEY spectrum obtained from the Au sample is shown at the inset of Fig. 2. The mean value of the distribution is proportional to the average number of secondary electrons created by a single gold ion passing through the sample. The area under the peak is equal to the number of ions which passed through the sample, while the distribution width is determined by the statistical processes involved in the creation of the SEY and their detection. Therefore, the two parameters of interest are the mean and width of the measured distribution. The data for the sample discussed below are normalized to 10,000 Au ions detected by the Si detector, whilst coinciding with secondary electrons.
The experiment utilizes the difference in energy loss of the Au beam ions when passing through a nanotube or a lull between the tubes. Due to the two distinct energy losses, one can expect two peaks in the Si detector amplitude spectra, a low energy peak corresponding to the ions which lose more energy when they pass through the nanorods and a higher energy peak, corresponding to the ions which pass in the space between the nanorods. Figure 2 shows the spectrum registered by the Si detector for an Au sample and a ZnO/GaN sample. The gold sample is homogeneous, yet there are two peaks in the measured spectra. This is related to a damage of the surface barrier detector. The detector is mechanically moved during data collection. This movement is introduced in order to minimize the risk of damaging a particular area of the detector. If the response of the detector is different along its surface, we might observe a structure in the measured beam energy, which is the case in Fig. 2. In a latter study, we compare the response of the detector in question, and a brand new detector. The double hump/peak was not present in the spectrum measured with the new detector.
Results
When comparing the shape of the two spectra shown in Fig. 2, one can see that the continuous black spectra for the ZnO sample is shifted to the left relative to the spectrum from the Au sample. This is due to the higher energy loss in the ZnO sample. Furthermore, there is a tail to the left corresponding to lower energies. These events should correspond to the Au ions which pass through the ZnO nanotubes, and thus lose more energy.
The inset of Fig. 3 show the spectra observed from the Si detector for the ZnO/GaN, and the corresponding SEY spectra observed in the channeltron. There are two dominant peaks in the secondary electron spectra. If we gate on the higher peak in the SEY spectra, the blue dashed area, we select the events shown with the same pattern in the Si spectra. Gating on the lower SEY peak, shown in solid red, selects events which have a higher energy, as indicated in the corresponding Si spectra. Therefore, based on the above results and contentions, it can be concluded that the measured higher electron yield is related to Au ions, which have lower energy after the ZnO samples, while the lower SEY peak occurs due to the lulls between the nanotubes, giving higher signal in the Si detector. For a comparison of the SEY spectrum from the Au sample, shown in the inset of Fig. 2, shows one peak, as expected, from a homogeneous material (Fig. 4).
Discussion
The measured SEY spectra can be fitted with a sum of 3 normal distributions. In Fig. 3 the fit for the corresponding spectra obtained from ZnO/GaN and the ZnO (without GaN coating) are shown. The same samples are shown in the inset of Fig. 1. The higher SEY peak can be well described by a normal distribution. While for the low SEY yield, the peak is not well described around the peak maxima. Hence, there is a single source with higher secondary yield related to the nanotubes. There are at least 3 sources of lower secondary electron yield—two of these are represented by the two Gaussian distributions used in the fit. The presence of a third source is indicated by the poor fit for the low SEY peak.
The area under the SEY peaks should be related to the area presented to the beam from the different sources. The counts under the higher SEY peak to the total number of counts in the SEY spectra, is expected to be equal to (the area of the nanotube exposed to the beam)/(arc of the valleys) = π (nanotube radius)2/(distance between the nanotubes)2. The measured and calculated rations are 0.3 and 0.3–0.5 for ZnO/GaN and 0.1 and 0.11–0.16 for ZnO, respectively. This supports the interpretation that the higher SEY peak is related to Au ions interacting with the ZnO nanotubes.
The calculated energy loss of Au ions in the sample, further confirms the above analysis. There is an uncertainty in the ZnO average density that should be used in the calculation, we assumed 5.5 g/cm3. A calculation with ATIMA14 yield:
E(after passing through a nanotube)/E(after passing through a lull) = (3.5 meV/u) / (4.6 meV/u) . Assuming 10% error in the energy loss calculation a ratio of 0.76(11) is obtained. Hence, a peak in the Si spectra in channel 2.1 k, due to an ion passing through a lull, should have a corresponding peak in channel 1.6(3) k. The second peak, due to the defect Si detector, centered around 1.9 k will have a corresponding peak centered around 1.4(3) k due to ions passing through nanotubes. Considering the uncertainties in the energy calculation this result is consistent with the data shown in the inset of Fig. 3.
The relations between the energy deposited in the Si detector and the SEY discussed above are reflected in the two dimensional histogram shown in Fig. 5. An additional feature is visible around channel 1400 of the SEY. The yield reduces as the deposited energy in the Si detector increases. There is insufficient data to explain this relation. A possible clue is visible in the SEM image shown in Fig. 1, the nanotubes are not perfect cylinders perpendicular to the substrate. The large energy spread measured for ions passing through a nanotubes compere to the one that went through a lull indicates a variation of the amount of ZnO material in the ion path. The SEM image shown in the inset of Fig. 1 shows the irregular structure of the nanotubes. Calculating the energy loss variation due to nanotube length change by 1 µm leads to a shift of order of 100 channels in the energy spectra shown in Fig. 5.
The results of the measurements are summarized in Table 1. An average increase of the SEY from ZnO nanotubes of 2.5 times compared to the gold sample, was observed. The data shows that GaN coating does not lead to a higher SEY yield.
Outlook
What is interesting in the presented data, where we used Au heavy ion beam probe, we did not find any increase in the SEY due to the GaN coating. This is an open question for further investigation.
From this research we have several conclusions: (1) the increase in the SEY from the investigate nanomaterial is of order of 2.5 when compared to Au foil (2) the GaN coating did not lead to measureable increase in the SEY compere to non-coated nanomaterial. This is different from observation in ref.8 which could be attributed to the fact that the carbon ions were used in the past.
From point of view if practical detector applications, the measured increase in SEY yield comes at a price of beam with broader energy spread after detection.
One possible direction in future investigations is: (1) search for coating leading to larger SEY (2) investigating materials with smaller nano-tube diameter and larger density. These investigations may lead to increase of the SEY.
Here we would like to suggest an alternative direction for future material development and experimental investigations where the SEY can be increased by more than an order of magnitude, while the energy broadening will approach the energy straggling introduced by a new µm of homogeneous ZnO layer. This idea is introduced bellow.
When considering thin detectors we suggest the use of a nanomaterial made by growing high aspect ridges on a thin substrate, with ridges regularly spaced and perpendicular to the substrate. If this material is placed at an angle relative to the beam, as illustrated in Fig. 6, the ions will pass through multiple ridges. Utilizing this approach, the SEY is increased due to passing through multiple surfaces. It is worth noting that presenting further surfaces due to the to the higher energy δ-electrons bumped by a neighboring nanostructure, the SEY will be further increased via secondary interactions with the material. These δ-electrons are schematically depicted as green arrows in Fig. 6.
In the sketched example the ion trajectory passes through 8 surfaces, compare to 2 for a flat foil. Hence the SEY yield will increase by more than 8*2.5/2 times compare to foil covered with gold. Here we assume that all secondary electrons can be extracted from the volume between the ridges vial electrical field. The exact gain will be determined from the geometry of the nanoridges, e.g. high, spacing, width and the materials used to build them.
In the above approach, the energy spread is significantly reduced as the variation of the total geometric length of the ion track in the nanomaterial is reduced to (ridge thickness)/cos(angle between the beam and the substrate surface). For example, a ridge structure placed at 45° relative to the beam, with 0.5 µm thick ridges, ridge depth of 2.5 µm placed 0.5 µm apart will introduce energy spread of the beam equivalent to of 0.7 µm of ZnO. Which corresponds to energy broadening of order of 3% for Au ions beam at 4.77 meV/u, while the average ion path through the foil will be 1.75 µm of ZnO + (substrate thickness)/cos 45°.
The above purely geometrical considerations indicate a possibility for a major improvement of TOF detector based on SEE detection.
Conclusions
We have measured the secondary electron yield from 1D ZnO based nanomaterials with 4.77 meV/u gold ions. We used thin samples, utilizing the different energy loss of the probe ions in said samples, in order to separate the SEY from nanorods and the lulls. This approach allows for the differentiation of the SEY yield from nanostructures and other features without specialized accelerator systems delivering micro or nanobeams. This technique can be used to investigate samples with radiation sources, for instance alpha sources, and in bench-top experiments.
There is no narrow peak in the secondary electron yield for the studied structures. This is related to the larger diameter of the ion beam compared to the diameter of a single nanotube. The observed yields from the ZnO nanorods are, on average, 2.5 times higher compared to gold samples.
We propose a concept for a detector based on a tilted thin foil with nanoridges. Combining the observed increase of the SEY from ZnO nanorods with the proposed detector concept would significantly increase the SEY for the transition of ion detectors compared to a detector with a gold foil. The planned solution addresses the problem at hand with an increased energy spread due to the nanostructures.
Data availability
The data that support the findings of this study are mostly available within the paper. Additional data is available upon request from the corresponding author.
References
Zangwill, A. Physics at Surfaces (Cambridge University Press, New York, 1988).
Lorikyan, M. P. & Trofimchuk, N. N. Particle detection by means of controllable secondary electron emission method. NuclInstrum. Methods 140(3), 505–509 (1977).
Cerrito, L. Radiation and Detectors (Springer, Berlin, 2017).
Webster, J. G. The Measurement, Instrumentation, and Sensors: Handbook (CRC Press LLC, Boca Raton, 1999).
Cholewa, M., Fischer, B. E. & Heiß, M. Preparatory experiments for a single ion hit facility at GSI. Nucl. Instrum. Methods Phys. Res. B 210, 296–301 (2003).
Park, J. B. et al. Scalable ZnO nanotube arrays grown on CVD-graphene films. APL Mater. 4, 106104 (2016).
Sake, W., Tian, H., Ren, C., Yu, J. & Sun, M. Electronic and optical properties of heterostructures based on transition metal dichalcogenides and graphene-like zinc oxide. Sci. Rep. https://doi.org/10.1038/s41598-018-30614-3 (2018).
Cholewa, M. et al. Secondary elektron emission properties of III-nitride/ZnO coaxial heterostructures under ion and X-ray bombardment. Nucl. Instrum. Methods B 254, 55–58 (2006).
Wang, X. D., Summers, C. J. & Wang, Z. L. Large-scale hexagonal-patterned growth of aligned ZnOnanorods for nano-optoelectronics and nanosensor arrays. NanoLett. 4, 423. https://doi.org/10.1021/nl035102c (2004).
Lu, W. & Lieber, C. M. Nanoelectronics from the bottom up. Nat. Mater. 6, 841. https://doi.org/10.1038/nmat2028 (2007).
Roddaro, S. et al. InAs nanowire metal-oxide-semiconductor capacitors. Appl. Phys. Lett. 92, 3509. https://doi.org/10.1063/1.2949080 (2008).
Barth, W. et al. Upgrade program of the high current heavy ion UNILAC as an injector for FAIR. Nucl. Instrum. Methods Physics Res. A 577, 211–214 (2007).
Fischer, B. E., Cholewa, M. & Noguchi, H. Some experiences on the way to biological single ion experiments. Nucl. Instrum. Methods B 181, 60–65 (2001).
Acknowledgements
This work was supported by ENSAR2-PASPAG within the European Union's Horizon 2020 research and innovation programme H2020-INFRAIA-2014-2015 Grant Agreement 654002 –ENSAR2-PASPAG. We would like to thank BMBF for financial support.
Author information
Authors and Affiliations
Contributions
K.L., M.S.S. and C.Y. prepared samples. K.O.V. prepared the experiment setup. P.B, M.Ca., K.O.V., W.K., A.L. and M.Ch. performed the experiment. P.B. analyzed the presented data. P.B. and M.Ch. organized financial support and all coordination/collaboration between the authors. All authors commented/collaborated on this manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Boutachkov, P., Voss, K.O., Lee, K. et al. An investigation of secondary electron emission from ZnO based nanomaterials for future applications in radiation detectors. Sci Rep 11, 737 (2021). https://doi.org/10.1038/s41598-020-80788-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-80788-y
This article is cited by
-
In search of nano-materials with enhanced secondary electron emission for radiation detectors
Scientific Reports (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.