Abstract
Metamaterials have recently established a new paradigm for enhanced light absorption in state-of-the-art photodetectors. Here, we demonstrate broadband, highly efficient, polarization-insensitive, and gate-tunable photodetection at room temperature in a novel metadevice based on gold/graphene Sierpinski carpet plasmonic fractals. We observed an unprecedented internal quantum efficiency up to 100% from the near-infrared to the visible range with an upper bound of optical detectivity of 1011 Jones and a gain up to 106, which is a fingerprint of multiple hot carriers photogenerated in graphene. Also, we show a 100-fold enhanced photodetection due to highly focused (up to a record factor of |E/E0| ≈ 20 for graphene) electromagnetic fields induced by electrically tunable multimodal plasmons, spatially localized in self-similar fashion on the metasurface. Our findings give direct insight into the physical processes governing graphene plasmonic fractal metamaterials. The proposed structure represents a promising route for the realization of a broadband, compact, and active platform for future optoelectronic devices including multiband bio/chemical and light sensors.
Similar content being viewed by others
Introduction
Nowadays, the conversion of light into electrical signals is at the heart of several technologies. Notwithstanding the high level of maturity, the large scale, and diversity of application areas, the need for a compact photodetection platform with higher performance in terms of speed, efficiency, spectral range, as well as flexibility, semitransparency, and compatibility with complementary metal-oxide-semiconductor (CMOS), is becoming more eminent1.
Such features can be greatly fulfilled by combining functional systems with metamaterials2 (i.e. structured materials on the subwavelength scale with engineered electromagnetic properties). This leads to the concept of metadevices2, a logical extension of the metamaterial paradigm, where interactions are nonlinear and the response is dynamic, using systems with spatially variable elements. Generally, such metadevices can operate at low voltages, which is a competitive advantage over conventional technology exploiting bulk and expensive electro-optical crystals, often non-integrated in silicon photonics. However, the bandwidth of such metamaterials is generally narrow due to their resonant nature and most of them are working in the infrared band. Mastering control in the optical regime is technologically a more challenging task, due to the expensive and demanding fabrication of nanostructures, resulting from the need of high-resolution electron- or ion-beam techniques. Also, devices working in a wide spectral range are important for multiband photodetection3, on-chip sensing of multiple analytes4, as well as multiplexed fluorescence and Raman detection5. Hybridization of low-dimensional carbon allotropes with plasmonic metamaterials6,7,8,9,10,11,12,13,14,15,16 is known to provide broadband and strong light-matter interactions, improvement of the nonlinear response due to the electromagnetic field enhancement given by the metamaterial, and compatibility with well-established silicon photonic and CMOS technologies17,18, therefore realizing a platform for high-speed19 light modulation and detection on the same chip.
In this regard, graphene — a two-dimensional system composed of carbon atoms arranged in a hexagonal lattice — has rapidly established itself as intriguing building block for optoelectronic applications20, with a strong focus on various photodetection frameworks1. The versatility of this exceptional material enables its application in a number of areas including ultrafast and electrically tunable detection of light over a wide spectral range from ultraviolet to THz3,9,10,13,14,17,18,19,21,22,23,24,25,26,27,28,29,30. However, single-layer graphene absorbs 2.3% of the incident light in a large spectral range31, which is remarkably high for an atomically thin material, but it leads to a low photocarrier absorption efficiency that constitute a limiting factor for highly sensitive state-of-the-art photodetectors. By coupling plasmonic metamaterials with graphene, localized surface plasmons32 (LSP) — collective charge oscillations at the interface between a subwavelength metal object and a dielectric — can be excited in photodetectors to improve graphene absorption by the resulting field enhancement, therefore increasing the device responsivity. However, plasmonic structures with periodic geometries can be used only for filtering light polarization and selective absorption at designed frequencies3,9,10,14,33, restricting their application field. Recently, the first graphene plasmonic fractals6,7 have been realized, reporting a polarization-insensitive, gate-tunable, and enhanced photodetection. So far, such metamaterials are still narrow-band and have low photodetection efficiency with poor electrical modulation.
Here, we show that plasmonic fractal metamaterials can be designed to significantly improve broadband and polarization-independent light absorption in graphene photodetectors, thus enabling multiband photodetection. A novel graphene-based electrically active metadevice for efficient control and detection of radiation in the visible (VIS)–mid-infrared (MIR) range was realized. The metamaterial consists of an Au Sierpinski carpet (SC) fractal34 fabricated on a graphene/SiO2/Si substrate. The gold/graphene (Au/G) fractal absorbs light 25 times stronger than an Au SC. As a result of the strong electromagnetic field enhancement (up to |E/E0| ≈ 20) within the interstructure gaps, the graphene-light interaction is greatly enhanced (up to an unprecedented factor of |E/E0|4 ≈ 105) at designed frequencies. This provides a multimodal plasmonic response that covers a broad range of the electromagnetic spectrum (VIS–MIR). Owing to the continuous nature of the Au/G fractal metamaterial, both its absorption intensity and bandwidth can be controlled electrically by varying the charge carrier concentration in graphene, through a gate voltage. This approach allows modulation of the device optical reflectance up to 23% in intensity and 60% in photon energy, much higher than that reported by Aygar et al.6. We observed in the optical range up to 100% internal quantum efficiency, remarkably higher than that reported by Fang et al.7, with a gain up to 106 and an upper bound of optical detectivity of 2 × 1011 cm Hz1/2W−1. Moreover, we present up to 100-fold enhancement of the responsivity, with respect to an unpatterned graphene photodetector.
Results and Discussion
Deterministic fractals35 are self-similar objects generated by geometrical rules, having a non-integer (Hausdorff-Besicovitch) dimension. Sierpinski carpets can be generated by a recursive geometrical algorithm employing a Lindenmayer system implementation34. We designed Au/G SCs starting from a graphene unit cell of side L0 = 10 μm that is divided into a 3 × 3 array of sub-cells of lateral size L1 = L03−1, with an Au square placed in the central sub-cell. By iteratively applying the same rule to the generated sub-cells of size \({L}_{t}={L}_{0}{3}^{-t}={L}_{0}{ {\mathcal L} }_{t}\), it is possible to obtain fractals for higher orders t of complexity34. In this way, we indirectly patterned graphene, thereby realizing an Au/G fractal metamaterial that can be thought as a discrete Au SC and a complementary continuous graphene SC. At each iteration the side of the sub-cells is reduced by a factor \( {\mathcal L} ={3}^{-1}\). Since the number of graphene sub-cells in the SC increases by a factor \({\mathscr{N}}=8\) at each iteration, the fractal dimension is \({d}_{H}={\rm{l}}{\rm{o}}{\rm{g}}{\mathscr{N}}/{\rm{l}}{\rm{o}}{\rm{g}}{ {\mathcal L} }^{-1}\approx 1.89\)34.
By employing electron-beam lithography, reactive-ion etching, metal evaporation, and lift-off techniques (see Methods), we fabricated the first five orders of an Au/G SC on a Si/SiO2 substrate (see Supplementary Information 1). The nominal thickness of the Au squares is 35 ± 3 nm, while their lateral sizes are L1 = 3.33 ± 0.05 μm, L2 = 1.11 ± 0.01 μm, L3 = 370 ± 17 nm, L4 = 123 ± 7 nm, and L5 = 41 ± 3 nm. A representative optical micrograph of the sample for t = 5 order is shown in Fig. 1a along with a scanning electron microscopy (SEM) micrograph in Fig. 1b, which illustrates the excellent homogeneity and uniformity of the fractal structure. In Fig. 1c, a scheme of an Au/G fractal photodetector is depicted. In order to understand the physics governing the metadevice, before presenting the device characterization we discuss the optical properties of the Au/G fractal metamaterial in the following.
As we have previously reported in ref. 34, the Au SC can be regarded as a metallo-dielectric photonic quasi-crystal. In Fig. 1d the singular-continuous36 reciprocal lattice of the SC for t = 5 order is shown, by computing the fast Fourier transform of its SEM micrograph. Such a reciprocal lattice is self-similar as its direct counterpart34. It follows that the diffraction patterns and the related optical spectra of such fractals are themselves self-similar34,36. Also, the SC has a larger number of points in the reciprocal space than a periodic array, since its fractal reciprocal lattice is a superposition of five periodic lattices with different constants at = 3Lt, under the periodic approximation34,36,37.
In Fig. 2a, a comparison between the reflectance r of an Au and Au/G SC divided by the reflectance rsub of the SiO2/Si substrate is shown. The reflectance of the substrate is dominated by a minimum around 0.7 eV due to thin-film interference effects between SiO2 and Si. The spectra of Au and Au/G SCs exhibit multiple features in the VIS–MIR range, which for the Au SC appear as maxima \({\omega }_{n}^{{\prime} }\) due to the radiative scattering in air, while for the Au/G SC result in shifted minima ωn owing to the thin-film interference effects between Au and graphene. In ref. 34, we have reported that the optical spectrum of an Au SC at a given fractal order t mainly manifests t diffraction-mediated LSP resonances \({\omega }_{n}\approx 2\pi c/3{L}_{0}{ {\mathcal L} }_{n}\), where n = 1,2,…t, for small LSP wavevectors kp. For large kp, \({\omega }_{n}\equiv {\omega }_{sp}/\sqrt{3}\mathrm{=2.40}\) eV with ωsp = 4.17 eV the Au surface plasmon32 (see Supplementary Information 2). These LSP resonances are self-similar as their photon energy has the same scale-invariance law \(({ {\mathcal L} }_{t}{=8}^{-t/{d}_{H}})\) as the SC lattice constant at, depending on the fractal dimension dH (see Supplementary Information 2). On the other hand, graphene surface plasmons polaritons are expected at lower photon energy38. Furthermore, the relative reflectance change (RAu − RAu/G)/RAu between the two samples is up to 25% at ω3, which means a remarkable relative absorption variation (RAu/G − RAu)/(1 − RAu) of 2500%. Therefore, graphene can be exploited as an ultrathin, broadband, anti-reflective coating. From the comparison with the reflectance spectra of Au/G periodic arrays in Fig. 2b, it is possible to observe that the energy of the Au/G SC resonances scales with the periodicity at of the Au structures. Also, the SC resonances in Fig. 2a are blue-shifted with respect to those of the periodic arrays in Fig. 2b, due to a far-field hybridization of LSPs belonging to the different fractal orders34. In particular, the ω3 mode overlaps with the SiO2 minimum. From data in Fig. 2b, we can draw the dispersion relation of the hybrid Au/G LSP modes in Fig. 2c. From the electromagnetic calculations (see Supplementary Information 3), kp = 2π/Lt = 6π/at is the self-similar LSP wavevector of the Au SC. From the plot we observe that the out-of-plane coupling between the Au SC LSP modes and graphene is two times stronger than the in-plane coupling between the LSP modes of the Au SC squares (see Supplementary Information 2).
Moreover, the Au SC interaction with graphene allows to tune the Au/G LSP modes by applying a gate voltage to the device. The intensity of the relative reflectance to the charge neutrality point (CNP), (R − RCNP)/RCNP, for the five LSPs can be enhanced up to 23% (2d). Also, we noticed that only the position in energy \(\hslash {\omega }_{F}\) 2EF of the graphene interband threshold (Fig. 2d inset) can be modulated up to 60%, following the law \(\hslash {\omega }_{F}=2\hslash {v}_{F}\sqrt{\pi n}\), being \(n\approx C({V}_{G}-{V}_{CNP})\) the charge carrier density, \(C={\varepsilon }_{Si{O}_{2}}{\varepsilon }_{0}/e{t}_{ox}\mathrm{=7.2}\times {10}^{10}\) V−1 cm−2 the SiO2 gate capacitance per area, VG the gate voltage, VCNP = 30 V the voltage at the charge neutrality point, and vF = 108 cm/s the graphene Fermi velocity. We did not observe any shift in energy for the the other LSP modes for such values of applied gate voltage. The dispersion of ω3 is shown in Fig. 2d, for instance.
Additionally, in ref. 34 we demonstrated that having a centrosymmetric geometry, plasmonic SCs are insensitive to the linear polarization of the incident light (i.e., the SC response does not change if light polarization is parallel to the edge of the SC or to its diagonal). This is an important feature in order to realize polarization-independent devices7, since other aperiodic metamaterial6,12,15,16 and periodic metamaterials3,9,10,14 usually depend strongly on light polarization.
Plasmonic fractals provide a hierarchical spatial distribution of near-field electromagnetic enhancement, due to LSP modes supported on the surface of the self-similar resonators forming the whole structure34,36. When a mode of the Au fractal is excited, a considerable field enhancement not only near the squares but also across the graphene layer is observed. In fact, graphene represents a unique model system where nonlinear applications, such as surface enhanced Raman spectroscopy (SERS), can be studied in detail39,40,41,42,43. In Fig. 3a, average Raman spectra for the t = 5 order of the Au/G SC and for an unpatterned graphene sample (t = 0) are plotted. A SERS enhancement factor on the Au/G SC can be evaluated in Fig. 3b as a function of the SC lattice constant at for the graphene G and 2D phonon bands. As for Au SCs, the SERS enhancement factor follows a power law34, but for Au/G SCs is 10-fold higher for the smallest feature, achieving a value of 105. Additionally, as shown in Fig. 3a, depositing metal structures on graphene represents an elegant way to pattern it without directly etching it, thus without altering the graphene crystalline structure (see Supplementary Information 4). Furthermore, by depositing on the t = 5 order Au/G SC a thin layer of Brilliant Cresyl Blue (BCB) dye as a probe (see Supplementary Information 5), it is possible to map the SERS enhancement all over the fractal surface (Fig. 3c). The contour plot presents a maximum of contrast among the squares with size L4 and L5 in excellent agreement with the electromagnetic simulation illustrated in Fig. 3d (see Supplementary Information 3). At the probed excitation wavelength the dye is not resonant34, therefore the observed signal is entirely related to a surface-enhanced electromagnetic effect.
Recently, the quantum properties of electrons in fractals have been investigated both theoretically44 and experimentally45, however their classical electronic behavior has not been experimentally reported so far. As shown in Fig. 1a,c, the phototransistor channel in the photodetector devices consists of a 40 × 40 μm CVD-grown, single-crystal single-layer graphene flake sensitized with an Au SC fractal (see Methods). Graphene is the active material of the device and the Au fractal acts as a plasmonic sensitizer to improve the overall light sensing. In the inset of Fig. 4a, a scheme of the electronic band profile of the Au/G photodetector device is depicted. Upon contact, graphene forms an ohmic junction with the Au electrodes (Fig. 4a). Therefore, an electrostatic contact potential ΔΦ = 0.3 eV is built, due to the difference between the graphene and Au work functions ΦG = 4.5 eV20 and ΦAu = 4.8 eV46, respectively. For the same reason, the Au fractal also provides an hole charge-transfer to graphene (Fig. 4b), resulting in a p-type doping. As illustrated in the inset of Fig. 4b, such a doping is linear with the Au/G fill factor, i.e. the area fraction of graphene uncovered by Au (see Supplementary Information 1). This effect leads to an increase of the hole carrier density n in graphene, therefore to a decrease of the carrier mobility μe = σ/ne, as a function of the fractal order or fill factor (Fig. 4c,d).
Since all the leads are made of the same material, a symmetric potential that traps the photogenerated electrons occurs in the device (Fig. 4a, inset). By applying a bias voltage VSD, the photogenerated holes can be extracted, provided that the graphene Fermi level EF compensates the trapping potential by applying for instance a gate voltage VG (see Supplementary Information 6).
In Fig. 5a, it is possible to observe that for a t = 5 order device, the photocurrent divided by the illuminated active area J = Iph/(4L0)2 exhibits a nonlinear dependence on the incident power of light P, due to electrostatic and thermal effects, trapping, and recombination occurring at high values of power7,47. The photocurrent response results linear up to 6 mW/cm2 for VG = −50 V at a photon energy of 1.94 eV. Furthermore, by photogating effect, the device produces a DC photovoltage that is dependent on the incident photon energy and power (see Supplementary Information 6). Moreover, the Au/G SC can linearly detect light down to 2 nA for VG = −50 V at 1.94 eV (Fig. 5b).
In Fig. 6a,b, the broadband and electrically tunable responsivity \( {\mathcal R} =J/P\) of a t = 5 order Au/G SC 3 × 3 array can be observed as a function of the applied gate voltage. An enhancement factor \({ {\mathcal R} }_{Au/G}/{ {\mathcal R} }_{G}\) up to 100-fold of the Au/G SC device over an unpatterned graphene device (see Supplementary Information 6) is presented in the inset of Fig. 6a. The array was introduced in order to increase the photocurrent signal-to-noise ratio. In addition, the device total absorption A = 1–r, and the external \(EQE= {\mathcal R} \hslash \omega /e\) and internal IQE = EQE/A quantum efficiencies are evaluated in Fig. 6c. It is worth noting that in the spectral range investigated, the Au/G SC photodetector IQE is up to 100% in correspondence of the ω5 LSP resonance.
From the application perspective, the relevant figure of merit to characterize a photodetector is the optical noise-equivalent-power \(NEP={\sum }_{i}{N}_{i}/ {\mathcal R} \), which corresponds to the lowest detectable power in 1 Hz output bandwidth47. Usually, the noise level of photodetectors in current-operating mode is due to the shot noise47 \({N}_{1}=\sqrt{2e{I}_{SD}}\) and to the thermal Johnson-Nyquist contribution47 \({N}_{2}=\sqrt{4{k}_{B}T\sigma }\), which ultimately limits the NEP. In Fig. 6d NEP is shown as a function of the incident photon energy for VG = −50 V. At room temperature, we observed a minimum NEP of 2 × 10−14 W Hz−1/2 for a 2.38 eV photon energy, while D* ≡ L/NEP = 2 × 1011 cm Hz1/2W−1 or Jones represents the device maximum specific detectivity at the same photon energy. Such a high value of detectivity is compatible with state-of-the-art two-dimensional photodetectors1,48.
Generally, five main phenomena compete in the operation of a graphene-based photodetector: the photovoltaic, the bolometric, the photothermoelectric, the photogating, and the plasma-wave-assisted effect1. In our case of study, we can reasonably exclude the latter mechanism, as it is likely to occur for THz radiation28 (ωτ = 1, with τ ≈ 0.1 ps the graphene carrier scattering time in our samples). In a metal-graphene-metal configuration, in which graphene is contacted with metal electrodes as source and drain, a p-n junction occurs close to the contacts because of the difference in the work functions between the metal and graphene49. Consequently, a charge transfer with a shift of the graphene Fermi level in the region below the metal pads occurs. The junction results in an internal electric field able to separate the light-induced electron-hole pairs (photovoltaic effect). Unless the contacts are made of different materials, the photocurrent produced at both the contacts will be of opposite polarity for symmetry reasons, resulting in zero net current at small gate voltages close to the CNP19. Usually, in such devices a light-induced photogating and photothermoelectric effect are also present at gate voltages close to the CNP, while at larger gate voltages the bolometric effect is typically dominant1,26,49. We observed the photovoltaic and photogating effects in the unpatterned graphene photodetectors (see Supplementary Information 6). In the Au/G SC devices, at gate voltages close to the CNP and for a symmetrical electronic band profile, the photovoltaic and bolometric effects are expected to play a minor role in comparison to the photothermoelectric and photogating effects26, due to the plasmonic Au SC sensitizer (see Supplementary Information 6). On the other hand, at sufficiently larger gate voltages (VG < −40 V), where the photothermoelectric and photogating effects become smaller, the bolometric effect should be dominant. Therefore, we propose the following explanation for the photogeneration mechanism in Au/G SC photodetectors. When light is shone on the metadevice, it is absorbed by Au fractal LSPs generating electron-hole pairs in the sensitizer (gating layer), which are transferred to graphene (channel layer). This results in a photocurrent and a photovoltage due to the change in electronic temperature between the Au SC and graphene regions, thus a variation of the carrier density Δn = CΔVG (see Supplementary Information 6). Since the device electronic bands are symmetric, the photogenerated electrons are trapped in graphene for \({\tau }_{trap}\equiv \Delta n\hslash \omega /IQEP\approx 27\) ms (see Supplementary Information 6). Therefore, only holes at relatively high gate voltages contribute to the photocurrent. For the t = 5 order Au/G SC array at VG = −50 V the hole carrier transit time is \({\tau }_{trans}\equiv {L}^{2}/{\mu }_{e}{V}_{SD}\approx 20\) ns, with FET channel length L = 40 μm and carrier mobility μe ≈ 8 × 103 cm2V−1s−1. Therefore, the lower bound (i.e. by neglecting the circuit RC constant) of the device bandwidth is \(\Delta {f}_{-3dB}\approx \mathrm{3.5/2}\pi {\tau }_{trans}\mathrm{=30}\) MHz, while the photoconductive gain is up to \(G\equiv {\tau }_{trap}/{\tau }_{trans}{\mathrm{=}10}^{6}\), providing evidence of a multiple carrier generation29,50 in graphene (see Supplementary Information 6). Evidently, such a high gain, produced by prolonged carrier lifetime due to trapping, limits the photodetector response speed and bandwidth.
In summary, we presented a novel graphene-based, plasmonic metamaterial having a multiresonant optical response hierarchically distributed on the fractal structure, which can be employed to realize a highly sensitive and polarization-independent, broadband photodetector. The metadevice is compact and can operate at room temperature under small voltages, with low power consumption. The detectivity could be further improved by depositing the Au fractal on high-mobility graphene-based van der Waals heterostructures, such as G/hBN51. Moreover, the deterministic chemical vapor deposition (CVD) growth of large area graphene52 would grant integration over wafer scale at a low cost of graphene-based photodetectors. Finally, the wide-range and high-gain spectral response of the Au/G fractal and its ability to hierarchically localize strong electromagnetic fields on a sub-wavelength scale could pave the way to a new generation of materials for integrated optics and optoelectronics, such as multiband photosensor pixel arrays for imaging cameras and optical communication devices.
Methods
Device fabrication
Single-layer, single-crystal graphene was grown on copper foil by CVD using an Aixtron BM cold-wall reactor at a temperature of 1060 °C and a pressure of 25 mbar. A semi-dry transfer approach was used to transfer the graphene from Cu to the target substrate52. The foil was spin-coated by a PMMA membrane and the graphene was electrochemically delaminated from the growth substrate in 1 M NaOH solution. Using a frame, the graphene/PMMA membrane was removed from the electrolyte, rinsed in deionized water and dried in ambient conditions. The membrane was deposited on the target Si/SiO2 substrates at 120 °C and the PMMA carrier polymer was removed in acetone. Graphene and Au SCs were patterned by EBL (Raith 150-Two) on Si wafers (1–5 mΩ cm) with a tox = 285 nm tick layer of thermal oxide. A layer of approximately 160 nm of 950 K poly-methyl-methacrylate (PMMA A2 1:1, 1% in anisole) was deposited by spincoating on the substrates, which were then post-baked for 7 min on a hot plate at 180 °C. The electron beam was operated at 20 kV with a current of 35 pA. After exposure, graphene was etched by O2 (5 sccm) reactive ion etching (Sentech instruments ICP-RIE 500) for 30 s at a RF power of 35 W and temperature of 15 °C in an Ar inert atmosphere (80 sccm). The SC patterns were exposed with a varying dose inversely proportional to the size of the squares of the fractal. Contacts pads and probes were exposed for the electrical measurements. The resist was developed for 30 s in a cold (8 °C) 1:3 mixture of MIBK:IPA. A 35/5 nm thick Au/Ti film was deposited on the substrates at a rate of 0.2 Å/s by electron-beam evaporation (Kenosistec) at an operating pressure of 10−6 mbar. Lift-off was then performed by hot (80 °C) acetone. A wire bonder (F&S Bontec Series 56) was used to wire the contact pads to an external circuit board. For SERS measurements, SCs were dip-coated for 1 h in 1 mM BCB [(C17H20ClN3O)2ZnCl2] aqueous solution, then rinsed in deionized water to wash the excess molecules in order to form a thin layer 12 ± 2 nm thick, and finally dried in nitrogen flow.
Sample characterization
Samples were characterized as in ref. 34. Scanning electron microscopy micrographs of Au/G SC samples deposited on Si/SiO2 were acquired by FEI Helios NanoLab DualBeam 650. Atomic force microscopy height profiles of the samples deposited on Si/SiO2 were measured in tapping mode by Bruker Innova in combination with v-type cantilever and SiN tips. Optical spectroscopy in reflection mode was performed with unpolarized light on SCs deposited on CaF2 substrates, by Thermo Fisher FTIR spectrometer and Thermo Fisher Nicolet Continu μm microscope equipped with NO2-cooled MCT and Si detectors, KBr and quartz beamsplitters, and a 15× (0.58 N.A.) Cassegrain objective. Surface enhanced Raman spectroscopy was carried out by Renishaw inVia micro-Raman microscope equipped with a 100× (0.85 N.A.) and 150× (0.95 N.A.) objectives, and 514 nm and 532 nm lasers at power 1.2 W/cm2 and 0.1 W/cm2 respectively, and integration time 1 s. All spectra were calibrated with respect to the first-order silicon LO phonon peak at 520 cm−1 and recorded in backscattering geometry at room temperature. Raman measurements were performed on Au/G SCs and as a reference on bare graphene deposited on the same Si/SiO2 substrate. Raman maps of graphene G and 2D, and BCB ω* = 1655 cm−1 vibrational bands were scanned at 0.3 μm steps in both the directions in the plane of the sample. Renishaw WiRE 3.0 software was used to analyze the collected spectra, whose baseline was corrected to the third-order polynomial. Two- and four-probe electrical measurements in van der Pauw configuration were performed in vacuum (10−6 mbar) by Keithley 2612 A digital source-measure unit and Agilent 34410 A digital voltmeter. In order to estimate the value of the residual carrier density n0 ≈ 1011 cm−2, two-probe resistance curves were fitted by the formula Rtot = 2Rc + Rsh, with \({R}_{sh}=L/We{\mu }_{e}{({n}^{2}+{n}_{0}^{2})}^{\mathrm{1/2}}\) the sheet resistance and L, W the FET channel length and width, respectively. For four-probe resistance curves Rc = 0 and Rsh = 4.53Rtot, due to the van der Pauw geometrical correction. Carrier mobility was then evaluated by μe = σ/ne. Photocurrent was measured using 0.80 eV, 1.46 eV, 1.94 eV, and 2.38 eV laser sources at different powers. The output power density was calibrated by a power meter. Responsivity was measured by using the following custom optical setup. An ASB-XE-175 source emitted panchromatic light passing through a SP CM110 monochromator controlled by PC. Emerging monochromatic light was coupled to an optical fiber, modulated at 173 Hz by a mechanical chopper, and focused by a lens first on the samples, then on Si and Ge photodiodes. The AC current from the sample was measured through a current pre-amplifier (DL 1211) with a amplification factor C = 10−6 A/V, whose output was read by a Signal Recovery 7265 lock-in amplifier. The photocurrent was given by the relation \(J=2\pi \sqrt{2}{V}_{lock-in}\ast C\mathrm{/4}\), where the factor 2 is due to the peak-to-peak magnitude, the factor \(\sqrt{2}\) originates from the lock-in amplifier rms amplitude, π/4 is the fundamental sine wave Fourier component of the square wave produced by the chopper, and Vlock-in the amplitude of the signal read by the lock-in.
Change history
16 July 2020
An amendment to this paper has been published and can be accessed via a link at the top of the paper.
References
Koppens, F. H. L. et al. Photodetectors based on graphene, other two-dimensional materials and hybrid systems. Nat. Nanotechnol. 9, 780–793 (2014).
Zheludev, N. I. & Kivshar, Y. S. From metamaterials to metadevices. Nat. Nanotechnol. 11, 917–924 (2012).
Liu, Y. et al. Plasmon resonance enhanced multicolour photodetection by graphene. Nat. Commun. 2, 1–7 (2011).
Aslan, E. et al. Multispectral Cesaro-type fractal plasmonic nanoantennas. ACS Photonics 3, 2102–2111 (2016).
Aouani, H. et al. Plasmonic nanoantennas for multispectral surface-enhanced spectroscopies. J. Phys. Chem. C 117, 18620–18626 (2013).
Aygar, A. M. et al. Comparison of back and top gating schemes with tunable graphene fractal metasurfaces. ACS Photonics 3, 2303–2307 (2016).
Fang, J. et al. Enhanced graphene photodetector with fractal metasurface. Nano Lett. 17, 57–62 (2017).
Nikolaenko, A. E. et al. Carbon nanotubes in a photonic metamaterial. Phys. Rev. Lett. 104, 1539021–1539024 (2010).
Yao, Y. et al. Wide wavelength tuning of optical antennas on graphene with nanosecond response time. Nano Lett. 14, 214–219 (2014).
Yao, Y. et al. High-responsivity mid-infrared graphene detectors with antenna-enhanced photocarrier generation and collection. Nano Lett. 14, 3749–3754 (2014).
Zhu, X. et al. Enhanced light-matter interactions in graphene-covered gold nanovoid arrays. Nano Lett. 13, 4690–4696 (2013).
Lee, S. H. et al. Switching terahertz waves with gate-controlled active graphene metamaterials. Nat. Mater. 11, 936–941 (2012).
Fang, Z. et al. Plasmon-induced doping of graphene. ACS Nano 11, 10222–10228 (2012).
Echtermeyer, T. J. et al. Strong plasmonic enhancement of photovoltage in graphene. Nat. Commun. 2, 1–5 (2011).
Papasimakis, N. et al. Graphene in a photonic metamaterial. Optics Express 18, 8353–8359 (2010).
Emani, N. K. et al. Electrical modulation of Fano resonance in plasmonic nanostructures using graphene. Nano Lett. 14, 78–82 (2014).
Gan, X. et al. Chip-integrated ultrafast graphene photodetector with high responsivity. Nat. Photon. 7, 883–887 (2013).
Liu, M. et al. A graphene-based broadband optical modulator. Nature 474, 64–67 (2011).
Mueller, T., Xia, F. & Avouris, P. Graphene photodetectors for high-speed optical communications. Nat. Photon. 4, 297–301 (2010).
Bonaccorso, F., Sun, Z., Hasan, T. & Ferrari, A. C. Graphene photonics and optoelectronics. Nat. Photonics 4, 611–622 (2010).
Massicotte, M. et al. Picosecond photoresponse in van der Waals heterostructures. Nat. Nanotechnol. 11, 42–47 (2016).
Ding, Y. et al. Ultra-compact integrated graphene plasmonic photodetector with bandwidth above 110 GHz. Nanophotonics 9, 317–325 (2020).
Tielrooij, K. J. et al. Generation of photovoltage in graphene on a femtosecond timescale through efficient carrier heating. Nat. Nanotechnol. 10, 437–443 (2015).
Liu, C.-H., Chang, Y.-C., Norris, T. B. & Zhong, Z. Graphene photodetectors with ultra-broadband and high responsivity at room temperature. Nat. Nanotechnol. 9, 273–278 (2014).
Freitag, M. et al. Photocurrent in graphene harnessed by tunable intrinsic plasmons. Nat. Commun. 4, 1–8 (2013).
Freitag, M., Low, T., Xia, F. & Avouris, P. Photoconductivity of biased graphene. Nat. Photon. 7, 53–59 (2013).
Konstantatos, G. et al. Hybrid graphene-quantum dot phototransistors with ultrahigh gain. Nat. Nanotechnol. 7, 363–368 (2012).
Vicarelli, L. et al. Graphene field-effect transistors as room-temperature terahertz detectors. Nat. Nanotechnol. 11, 865–871 (2012).
Gabor, N. M. et al. Hot carrier-assisted intrinsic photoresponse in graphene. Science 334, 648–652 (2011).
Xia, F., Mueller, T., Ming Lin, Y., Valdes-Garcia, A. & Avouris, P. Ultrafast graphene photodetector. Nat. Nanotechnol. 4, 839–843 (2009).
Li, Z. Q. et al. Dirac charge dynamics in graphene by infrared spectroscopy. Nat. Physics 4, 532–535 (2008).
Maier, S. A. Plasmonics: Fundamentals and Applications (Springer, New York, 2007).
Gilbertson, A. M. et al. Plasmon-induced optical anisotropy in hybrid graphene-metal nanoparticle systems. Nano Lett. 15, 3458–3464 (2015).
De Nicola, F. et al. Multiband plasmonic Sierpinski carpet fractal antennas. ACS Photonics 5, 2418–2425 (2018).
Mandelbrot, B. The Fractal Geometry of Nature (W. H. Freeman and Co., New York, 1982).
Dal Negro, L. & Boriskina, S. V. Deterministic aperiodic nanostructures for photonics and plasmonics applications. Laser Photonics Rev. 6, 178–218 (2012).
Gambaudo, J.-M. & Vignolo, P. Brillouin zone labelling for quasicrystals. New Journal of Physics 16, 1–11 (2014).
Tantiwanichapan, K. et al. Graphene terahertz plasmons: A combined transmission spectroscopy and Raman microscopy study. ACS Photonics 4, 2011–2017 (2017).
Schedin, F. et al. Surface-enhanced Raman spectroscopy of graphene. ACS Nano 4, 5617–5626 (2010).
Heeg, S. et al. Polarized plasmonic enhancement by au nanostructures probed through raman scattering of suspended graphene. Nano Lett. 13, 301–308 (2013).
Zhang, S. G. et al. Raman peak enhancement and shift of few-layer graphene induced by plasmonic coupling with silver nanoparticles. Appl. Phys. Lett. 104, 1211091–1211095 (2014).
Zhao, Y. et al. Strong light matter interactions in sub-nanometer gaps defined by monolayer graphene: toward highly sensitive SERS substrates. Nanoscale 6, 11112–11120 (2014).
Iyer, G. R. S. et al. Large-area, freestanding, single-layer graphene-gold: A hybrid plasmonic nanostructure. ACS Nano 8, 6353–6362 (2014).
van Veen, E., Yuan, S., Katsnelson, M. I., Polini, M. & Tomadin, A. Quantum transport in Sierpinski carpets. Phys. Rev. B 93, 1154281–1–115428–5 (2016).
Kempkes, S. N. et al. Design and characterization of electrons in a fractal geometry. Nat. Physics (2018).
Kittel, C. Introduction to Solid State Physics (John Wiley & Sons, New York, 2005).
Sze, S. M. Physics of Semiconductor devices (John Wiley & Sons, New York, 1969).
Xie, C., Mak, C., Tao, X. & Yan, F. Photodetectors based on two-dimensional layered materials beyond graphene. Adv. Funct. Mater. 27, 1603886–1603927 (2017).
Echtermeyer, T. J. et al. Photothermoelectric and photoelectric contributions to light detection in metal-graphene-metal photodetectors. Nano Lett. 14, 3733–3742 (2014).
Tielrooij, K. J. et al. Photoexcitation cascade and multiple hot-carrier generation in graphene. Nat. Physics 9, 248–252 (2013).
Banszerus, L. et al. Ultrahigh-mobility graphene devices from chemical vapor deposition on reusable copper. Sci. Adv. 1, 1–6 (2015).
Miseikis, V. et al. Deterministic patterned growth of high-mobility large-crystal graphene: a path towards wafer scale integration. 2D Materials 4, 021004 (2017).
Acknowledgements
The authors acknowledge that this work has received funding from the European Union’s Horizon 2020 research and innovation programme under grant agreement No. 696656 - GrapheneCore1.
Author information
Authors and Affiliations
Contributions
F.D.N., A.T., M.P., R.K. and V.P. conceived the experiments. V.M. and C.C. grew and transferred the graphene. N.P.P. fabricated the devices. F.D.N. performed the sample optical characterization, Raman spectroscopy, simulations, and data analysis. F.D.N., D.S. and N.P.P. carried out the electrical measurements. All the authors discussed the experimental implementation, the results, and contributed in writing the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
De Nicola, F., Puthiya Purayil, N.S., Miŝeikis, V. et al. Graphene Plasmonic Fractal Metamaterials for Broadband Photodetectors. Sci Rep 10, 6882 (2020). https://doi.org/10.1038/s41598-020-63099-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-63099-0
This article is cited by
-
Optimal design of graphene-based plasmonic enhanced photodetector using PSO
Scientific Reports (2024)
-
Enhanced Photoelectric Responsivity of Graphene/GaAs Photodetector Using Surface Plasmon Resonance Based on Ellipse Wall Grating-Nanowire Structure
Plasmonics (2024)
-
Plasmonic sensors based on graphene and graphene hybrid materials
Nano Convergence (2022)
-
A tunable multi-band absorber based on graphene metasurface in terahertz band
Optical and Quantum Electronics (2022)
-
Disordered photonics behavior from terahertz to ultraviolet of a three-dimensional graphene network
NPG Asia Materials (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.