Abstract
Several metal nanoparticle based catalysts have been synthesized for catalyzing the hydrogen production process by hydrolysis of methylamine-borane (MeAB). However, there was only one study that catalyzes the producing of hydrogenvia the methanolysis of MeAB, and it was carried out by our research group. For this reason, in this work, a new catalyst system entitled by single-walled carbon nanotube (SWCNT) supported bimetallic platinum-ruthenium nanoparticles were developed and called as PtRu@SWCNT. These NPs were characterized by several techniques (XRD, XPS, Raman, and TEM), and they were performed for the methanolysis of MeAB with high catalytic activity. The prepared PtRu@SWCNT NPs were also tested in the methanolysis of MeAB at different parameters including different temperatures, catalyst and substrate concentrations, and reusability performance. Experimental results revealed that the new PtRu@SWCNT NPs had excellent catalytic activity and reusability for removing of hydrogen from the methanolysis of MeAB at ambient conditions. According to the obtained data, the turnover frequency is 136.25 mole H2/mole PtRu × min, and the activation energy (Ea) is 17.29 kJ/mole. More than 99% of conversion was observed at room temperature.
Similar content being viewed by others
Introduction
As a renewable energy source, hydrogen promises to be a carrier of energy for the future1,2. However, since hydrogen is light and has a secure storage problem, there are some disadvantages in the application phase3,4,5. For this reason, intensive studies are being carried out for suitable chemicals with high gravimetric hydrogen density for portable and stationary applications6. Recently, many chemical hybrid solid hydrogen storage substances such as ammonia-borane (AB), dimethylamine borane (DMAB), methylamine-borane (MeAB) with B-N additives were investigated the situated application7,8,9,10,11. The reason for the investigation of these structures is due to the high hydrogen content of the protic N-H, hybrid B-H structures in multiple structures12,13,14,15,16,17,18,19,20,21,22,23,24. The simplest B-N compound is AB, which has a hydrogen mass of 19.6% and low molecular weight (30.9 g/Mol)25,26. They have a stable structure under ambient conditions with metal amido-borane, MeAB, and dimethylamine-borane. MeAB (CH3NH2-BH3) is an AB derivative having 11.1% hydrogen mass and stable to operating conditions27,28. Solvent (methanolysis and hydrolysis) and solid phase thermolysis reactions were applied from MeAB in the hydrogen production29,30. In the presence of the suitable catalyst, the hydrogen release in the solvolysis of MeAB yields 3 moles of hydrogen for 1 mole of MeAB according to following Eqs (1) and (2).
In the literature, there are several metal nanoparticles based catalysts for catalyzing the hydrogen production process by hydrolysis of MeAB. However, until the present study, there was only one study that catalyzes the producing of hydrogen via the methanolysis of MeAB, and it was carried out by our research group1.
In this study, Pt-Ru alloy nanoparticle decorated on SWCNT was synthesized and characterized by several techniques. The prepared new PtRu@SWCNT NPs nanocatalyst was tested effectively to complete dehydrogenation of MeAB by the methanolysis reaction. The methanolysis reaction with the use of the PtRu@SWCNT NPs began without any observing induction time at room conditions. The detailed kinetic study of synthesized nanoparticles for the methanolysis reaction of MeAB catalyzed by PtRu@SWCNT NPs were performed with the help of Arrhenius and Eyring equations.
Results and Discussion
The chemical and morphological structure of PtRu@SWCNT NPs
In order to reveal the chemical and morphological structure of PtRu@SWCNT NPs, various advanced analytical analysis techniques were conducted, and the details of characterization studies were given in supporting information. Figure 1 shows TEM analysis for PtRu@SWCNT NPs to reveal the mean particle size and distribution of PtRu alloy nanometals on SWCNT. As seen in Fig. 1, the mean particle size of PtRu@SWCNT NPs were found to be 3.62 ± 0.5 nm and this figure also show monodisperse and homogeneous distribution of the Pt and Ru metals on the supporting material. There was no agglomeration of PtRu nanoparticles on SWCNT.
XRD analysis was used to determine the crystalline structure of the monodisperse PtRu@SWCNT NPs nanocatalyst (containing 3.34 ± 0.02 wt % PtRu as founded using ICP-OES). Figure 2 shows XRD patterns of Pt@SWCNT NPs and PtRu@SWCNT NPs. As seen in Fig. 2, the similar XRD patterns were determined for Pt@SWCNT NPs and PtRu@SWCNT NPs, however, there was a small shift to the higher 2θ values which shows the alloy formation of PtRu@SWCNT compared to the Pt@SWCNT after 2nd metal addition. Both of Pt@SWCNT and PtRu@SWCNT have showed face centered cubic (fcc) structure and the XRD analysis also revealed the crystalline structures of PtRu@SWCNT NPs after the stabilization of metal ions to metallic forms31.
The Raman spectroscopy was shown in Fig. 3. The peaks observed at 1349 and 1589 cm−1, correspond to the D and G bands of carbon based materials, respectively. The intensity of graphite and the degree of graphitization of the carbonaceous materials represent the density ratio of the D-G band (ID/IG). After the functionalization of SWCNT with PtRu nanoparticles, ID/IG value increased from 1.31 to 1.42. The change in this ratio means the increase in deficiency of SWCNT which supports their functionalization with nanoparticles32.
For further investigations about the oxidation state of metals in PtRu@SWCNT NPs nanocatalyst, X-ray photoelectron spectroscopy (XPS) analyses were conducted. The electronic features of Pt and Ru, and their synergistic effect with SWCNT support material were investigated using XPS analysis. Figure 4 shows the XPS spectrum of PtRu@SWCNT NPs nanocatalyst. The oxidation state analysis of Pt and Ru in the PtRu@SWCNT NPs superb nanocatalyst was analyzed with Pt 4 f and Ru 3p regions in the spectrum. Pt 4 f and Ru 3p regions at XPS spectrum of the PtRu@SWCNT NPs give three doublets at 71.0 (metallic), 72.4 (Pt2+) and 73.9 eV (Pt4+) and two doublets at about 464.4 (metallic) − 467.5 eV (Ru4+), respectively31,32.
The methanolysis of MeAB catalyzed by PtRu@SWCNT NPs nanocatalyst
For the catalytic performance experiments, PtRu@SWCNT NPs nanocatalyst (0.96 mM) was added to a vacuum Schlenk tube. 4 mL of pre-dried methanol added to Schlenk tube and closed with the septum. 50 mM MeAB (0.25 mmol, 11.25 mg) was dissolved in 1 mL of dry methanol. In the presence of dissolved MeAB and N2 gas, it is placed in a jacketed Schlenk. Then the timer is started at t = 0. The released hydrogen gas amount was recorded using a cylinder burette. The experimental results obtained from different PtRu@SWCNT NPs nanocatalyst concentrations (0.48–1.20 mM) in the methanolysis of MeAB at mild conditions were given in Fig. 5. The hydrogen evolves began no observing any induction time as seen in Fig. 5(a). The complete hydrogen releasing from MeAB catalyzed by PtRu@SWCNT NPs nanocatalyst occurred in a very little time like 3.5 min at mild conditions. The plot obtained from the experiments carried out at different PtRu@SWCNT NPs nanocatalyst concentrations is given in Fig. 5(b) (lnkobs versus to ln[PtRu]) and the obtained plot is linear. The slope of the plot was found to be 0.92. According to experimental results, the rate of MeAB methanolysis, in the presence of PtRu@SWCNT NPs nanocatalyst was determined as 0.92nd depending on the concentration of PtRu@SWCNT NPs superb nanocatalyst.
Figure 6(a) indicates the volume of generated hydrogen versus time for the methanolysis of MeAB catalyzed by PtRu@SWCNT NPs nanocatalyst, started with different MeAB concentrations (25.0, 37.5, 50.0 and 62.5 mM) in dry methanol at ambient conditions. A linear graph of lnkobs versus ln [MeAB] plot was acquired from the Fig. 6(b), and a 0.70 of slope was obtained from Fig. 6. The results demonstrated that the rate of methanolysis of MeAB catalyzed by PtRu@SWCNT NPs nanocatalyst was suitable to the 0.70th order equation, depending on the concentration of MeAB. Based on the results mentioned above, catalytic rate law for hydrolysis of MeAB with PtRu@SWCNT NPs nanocatalyst was obtained as follows:
To set the optimal temperature for the methanolysis of MeAB catalyzed with PtRu@SWCNT NPs various experiments were carried out containing 50 mM MeAB and 0.96 mM PtRu@SWCNT NPs nanocatalyst at different temperatures (25–55 °C). The results obtained from the experiment conducted at different temperatures and Arrhenius – Eyring equations were used to calculate activation (activation energy (Ea) enthalpy (ΔH#) and entropy (ΔS≠)) and the kinetic parameters of MeAB catalyzed with PtRu@SWCNT NPs nanocatalyst. The results of the experiments conducted at different temperatures are given in Fig. 7(a). As seen in this figure, when increased temperatures, the catalytic activity of PtRu@SWCNT NPs nanocatalyst were increased. The activation energy (Ea) for the methanolysis of MeAB catalyzed with PtRu@SWCNT NPs nanocatalyst was calculated to be 17.29 kJ/mole using Arrhenius plot (given in Fig. 7(b)). Additionally, the observed reaction constant given in Fig. 7(c) was used to calculate enthalpy and entropy values for the methanolysis of MeAB catalyzed with PtRu@SWCNT NPs nanocatalyst, and these values were found to be ΔH# = 15.46 kJ/mole and ΔS# = −171.68 J/(mole × K), respectively. To test the stability and recyclability of PtRu@SWCNT NPs nanocatalyst in the methanolysis of MeAB at room temperatures, the same concentration of MeAB was subsequently added the completed experiment reaction after the previous run. Finally, the recyclability performance of PtRu@SWCNT NPs nanocatalyst has been shown to maintain its initial activity (87%) and provides high conversion (>99%) at the end of the 5th catalytic cycle (Fig. 8).
The initial turn-over frequency (TOFinitial) for PtRu@SWCNT NPs was found to be 8175 h−1 (136.25 min−1) at room temperatures and the calculated this TOF value were compared the TOF values present in literature as seen in Table 1. This TOF value is higher than the other study used for the methanolysis of MeAB at room conditions. As a result, the synthesized PtRu@SWCNT NPs nanocatalyst exhibited a superior catalytic activity compared the previous catalyst used for the methanolysis of MeAB. This unique catalytic activity can be ascribed to the large surface area of the catalysts, the synergic effects of alloy metals (Pt-Ru) with SWCNT and ultrafine structure.
Conclusions
In summary, even though several metal nanoparticles based catalysts have been synthesized for catalyzing the hydrogen production process by hydrolysis of MeAB, there was only one study related to the methanolysis of MeAB. For above reason, the superb PtRu@SWCNT NPs nanocatalyst was synthesized and tested as an effective catalyst in the methanolysis of MeAB with an easy and facile technique at mild conditions. With this report, a new and effective PtRu@SWCNT NPs nanocatalyst was developed for the methanolysis reaction of MeAB with complete hydrogen evolve at mild conditions. PtRu@SWCNT NPs superb nanocatalyst showed very high catalytic activity in the dehydrogenation of MeAB in dry methanol environment. The rate law of catalytic methanolysis of MeAB including PtRu@SWCNT NPs superb nanocatalyst was obtained as -d[CH3NH2BH3]/dt = +d[H2]/3dt = kobs [PtRu@SWCNT NPs]0.92 [MeAB]0.70. The activation energy, enthalpy, and entropy of the methanolysis of MeAB were found to be 17.29 kJ/mole, 15.46 kJ/mole, and −171.68 J/(mole × K), respectively. The initial TOF value of superb PtRu@SWCNT NPs nanocatalyst was found to be 8175 h−1 (136.25 min−1) as a record catalytic activity for methanolysis of MeAB, at 298 K in literature as shown in Table 1. This unique catalytic activity can be ascribed to the large surface area of the catalysts, the synergic effects of alloy metals (PtRu) with SWCNT and ultrafine structure. This new, effective and superb PtRu@SWCNT NPs nanocatalyst can be used for evolving hydrogen from MeAB as a solid hydrogen source in fuel cell applications at mild conditions. The catalysts exhibiting high catalytic activity have significant importance in the hydrogen technologies.
Experimental
Preparation of methylamine-borane (MeAB, CH3NH2-BH3)
Yang et al. reported a method for the synthesis of MeAB33. For this aim, 0.1 mole (3.88 g) of NaBH4 was weighed into a 250 mL two-necked flask, and 200 mL of anhydrous tetrahydrofurane (THF) was added. After stirring for 30 minutes at 25 °C, 0.1 mol (6.752 g) of methylamine hydrochloride was added through 24 hours at 25 °C under N2 atmosphere. The mixture was filtered, and the liquid phase was evaporated, allowing the THF to leave the medium. THF was entirely removed from the medium, and 100 mL of dry ether was added. The mixture was stirred for 2 hours in a cryostat system at a temperature of 0 °C. At the end of this period, the solid phase was re-filtered. The supernatant was left at room temperature for complete removal of water. When the supernatant was evaporated entirely, the white solids were formed as shown in following scheme (3).
Preparation of single-walled carbon nanotube supported platinum-ruthenium nanoparticles (PtRu@SWCNT NPs)
In the preparation of the new PtRu@SWCNT NPs nanocatalyst, an easy and facile one-step reduction technique was used at room conditions. Briefly, a solution containing 30 mg K2PtCl4, 30 mg RuCl3∙xH2O, and 60 mg SWCNT were mixed in 20 mL of water. After that, a solution containing NaBH4 was added to the mixture and waited until the bubble formation was finished. After that, black colored PtRu@SWCNT NPs superb nanocatalyst was obtained. The resulting mixture was filtered, and the obtained solid residue was washed with plenty of deionized water (3 × 10 mL), dried at inert medium at 80 °C.
Change history
05 August 2020
Editor’s Note: Readers are alerted that the reliability of data presented in this manuscript is currently in question. Further editorial action may be taken as appropriate once the investigation into the concerns is complete and all parties have been given an opportunity to respond in full.
References
Kanat, M. et al. Preparation and detailed characterization of zirconia nanopowder supported rhodium (0) nanoparticles for hydrogen production from the methanolysis of methylamine-borane in room conditions. Int. J. Hydrogen Energy43, 22548–22556 (2018).
Niemann, M. U. et al. Nanomaterials for Hydrogen Storage Applications: A Review. J. Nanomater.2008, 1–9 (2008).
Eberle, U., Felderhoff, M. & Schüth, F. Chemical and Physical Solutions for Hydrogen Storage. Angew. Chemie Int. Ed.48, 6608–6630 (2009).
Sakintuna, B., Lamari-Darkrim, F. & Hirscher, M. Metal hydride materials for solid hydrogen storage: A review. Int. J. Hydrogen Energy32, 1121–1140 (2007).
Russell H. & Jones, G. J. T. Materials for the Hydrogen Economy. 22 December 2007 91, (2007).
Targets for Onboard Hydrogen Storage Systems for Light-Duty Vehicles (2009).
Jaska, C. A. & Manners, I. Heterogeneous or homogeneous catalysis? Mechanistic studies of the rhodium-catalyzed dehydrocoupling of amine-borane and phosphine-borane adducts. J. Am. Chem. Soc. https://doi.org/10.1021/ja0478431 (2004).
Clark, T. J., Russell, C. A. & Manners, I. Homogeneous, titanocene-catalyzed dehydrocoupling of amine-borane adducts. J. Am. Chem. Soc. https://doi.org/10.1021/ja062217k (2006).
Zahmakıran, M. et al. Aminopropyltriethoxysilane stabilized ruthenium(0) nanoclusters as an isolable and reusable heterogeneous catalyst for the dehydrogenation of dimethylamine–borane. Chem. Commun.46, 2938 (2010).
Sen, B., Kuzu, S., Demir, E., Akocak, S. & Sen, F. Polymer-graphene hybride decorated Pt nanoparticles as highly efficient and reusable catalyst for the dehydrogenation of dimethylamine–borane at room temperature. Int. J. Hydrogen Energy42, 23284–23291 (2017).
Sen, B., Şavk, A. & Sen, F. Highly efficient monodisperse Pt nanoparticles confined in the carbon black hybrid material for hydrogen liberation. J. Colloid Interface Sci.520, 112–118 (2018).
Ogden, J. M. Developing an infrastructure for hydrogen vehicles: a Southern California case study. Int. J. Hydrogen Energy24, 709–730 (1999).
Schlapbach, L. & Züttel, A. Hydrogen-storage materials for mobile applications. Nature414, 353–358 (2001).
Feng, W. et al. In situ facile synthesis of bimetallic CoNi catalyst supported on graphene for hydrolytic dehydrogenation of amine borane.Int. J. Hydrogen Energy. https://doi.org/10.1016/j.ijhydene.2013.12.113 (2014).
Hamilton, C. W., Baker, R. T., Staubitz, A. & Manners, I. B–N compounds for chemical hydrogenstorage. Chem. Soc. Rev.38, 279–293 (2009).
Gulcan, M. & Karataş, Y. Synthesized polyvidone-stabilized Rh(0) nanoparticles catalyzed the hydrolytic dehydrogenation of methylamine-borane in ambient conditions. New J. Chem. https://doi.org/10.1039/c7nj02481a (2017).
Bacsa, R., Laurent, C., Morishima, R., Suzuki, H. & Le Lay, M. Hydrogen Storage in High Surface Area Carbon Nanotubes Produced by Catalytic Chemical Vapor Deposition. J. Phys. Chem. B108, 12718–12723 (2004).
Chandra, M. & Xu, Q. A high-performance hydrogen generation system: Transition metal-catalyzed dissociation and hydrolysis of ammonia–borane. J. Power Sources156, 190–194 (2006).
Chandra, M. & Xu, Q. Room temperature hydrogen generation from aqueous ammonia-borane using noble metal nano-clusters as highly active catalysts. J. Power Sources168, 135–142 (2007).
Durap, F., Zahmakiran, M. & Özkar, S. Water soluble laurate-stabilized rhodium(0) nanoclusters catalyst with unprecedented catalytic lifetime in the hydrolytic dehydrogenation of ammonia-borane. Appl. Catal. A Gen. https://doi.org/10.1016/j.apcata.2009.08.031 (2009).
Sanyal, U., Demirci, U. B., Jagirdar, B. R. & Miele, P. Hydrolysis of Ammonia Borane as a Hydrogen Source: Fundamental Issues and Potential Solutions Towards Implementation. ChemSusChem4, 1731–1739 (2011).
Yan, J.-M., Zhang, X.-B., Akita, T., Haruta, M. & Xu, Q. One-Step Seeding Growth of Magnetically Recyclable Au@Co Core−Shell Nanoparticles: Highly Efficient Catalyst for Hydrolytic Dehydrogenation of Ammonia Borane. J. Am. Chem. Soc.132, 5326–5327 (2010).
Baguc, I. B. et al. Nanocrystalline metal organic framework (MIL-101) stabilized copper Nanoparticles: Highly efficient nanocatalyst for the hydrolytic dehydrogenation of methylamine borane. Inorganica Chim. Acta483, 431–439 (2018).
Shen, J., Yang, L., Hu, K., Luo, W. & Cheng, G. Rh nanoparticles supported on graphene as efficient catalyst for hydrolytic dehydrogenation of amine boranes for chemical hydrogen storage. Int. J. Hydrogen Energy40, 1062–1070 (2015).
Yao, Q., Lu, Z.-H., Zhang, Z., Chen, X. & Lan, Y. One-pot synthesis of core-shell Cu@SiO2 nanospheres and their catalysis for hydrolytic dehydrogenation of ammonia borane and hydrazine borane. Sci. Rep.4, 7597 (2015).
Karatas, Y. et al. Palladium(0) nanoparticles supported on hydroxyapatite nanospheres: Active, long-lived, and reusable nanocatalyst for hydrogen generation from the dehydrogenation of aqueous ammonia-borane solution. J. Nanoparticle Res. https://doi.org/10.1007/s11051-014-2547-3 (2014).
Lee, S. M., Kang, X. D., Wang, P., Cheng, H. M. & Lee, Y. H. A comparative study of the structural, electronic, and vibrational properties of NH3BH3 and LiNH2BH3: Theory and experiment. ChemPhysChem. https://doi.org/10.1002/cphc.200900283 (2009).
Chen, Y., Fulton, J. L., Linehan, J. C. & Autrey, T. In Situ XAFS and NMR Study of Rhodium-Catalyzed Dehydrogenation of Dimethylamine Borane, https://doi.org/10.1021/JA0437050 (2005).
Yamamoto, Y. et al. Synthesis of B-trisubstituted borazines via the rhodium-catalyzed hydroboration of alkenes with N,N′,N″-trimethyl or N,N′,N″-triethylborazine. J. Organomet. Chem. https://doi.org/10.1016/j.jorganchem.2006.08.024 (2006).
Yang, L., Luo, W. & Cheng, G. Graphene-supported Ag-based core-shell nanoparticles for hydrogen generation in hydrolysis of ammonia borane and methylamine borane. ACS Appl. Mater. Interfaces. https://doi.org/10.1021/am402373p (2013).
Çelik, B. et al. Monodisperse Pt(0)/DPA@GO nanoparticles as highly active catalysts for alcohol oxidation and dehydrogenation of DMAB. Int. J. Hydrogen Energy41, 5661–5669 (2016).
Yıldız, Y. et al. Monodisperse Pt Nanoparticles Assembled on Reduced Graphene Oxide: Highly Efficient and Reusable Catalyst for Methanol Oxidation and Dehydrocoupling of Dimethylamine-Borane (DMAB). J. Nanosci. Nanotechnol.16, 5951–5958 (2016).
Yang, Z., Cheng, F., Tao, Z., Liang, J. & Chen, J. Decreasing the thermal dehydrogenation temperature of methylamine borane (MeAB) by mixing with poly(methyl acrylate) (PMA). Int. J. Hydrogen Energy. https://doi.org/10.1016/j.ijhydene.2012.01.134 (2012).
Wen, L., Zheng, Z., Luo, W., Cai, P. & Cheng, G. Z. Ruthenium deposited on MCM-41 as efficient catalyst for hydrolytic dehydrogenation of ammonia borane and methylamine borane. Chinese Chem. Lett. https://doi.org/10.1016/j.cclet.2015.06.019 (2015).
Shen, J. et al. Hydrolytic dehydrogenation of amine-boranes catalyzed by graphene supported rhodium-nickel nanoparticles. Catal. Commun. https://doi.org/10.1016/j.catcom.2014.09.042 (2015).
Meng, X. et al. Graphene-supported trimetallic core-shell Cu@CoNi nanoparticles for catalytic hydrolysis of amine borane. Chempluschem. https://doi.org/10.1002/cplu.201300336 (2014).
Du, Y., Cao, N., Yang, L., Luo, W. & Cheng, G. One-step synthesis of magnetically recyclable rGO supported Cu@Co core-shell nanoparticles: Highly efficient catalysts for hydrolytic dehydrogenation of ammonia borane and methylamine borane. New J. Chem. https://doi.org/10.1039/c3nj00552f (2013).
Yang, L., Su, J., Luo, W. & Cheng, G. Size-controlled synthesis of tetrametallic Ag@CoNiFe core-shell nanoparticles supported on graphene: A highly efficient catalyst for the hydrolytic dehydrogenation of amine boranes.ChemCatChem. https://doi.org/10.1002/cctc.201400042 (2014).
Meng, X. et al. Decoration of graphene with tetrametallic Cu@FeCoNi core-shell nanoparticles for catalytic hydrolysis of amine boranes. RSC Adv. https://doi.org/10.1039/c4ra04894f (2014).
Acknowledgements
The authors would like to thank Van Yuzuncu Yil (FAP-2018-7373) and Dumlupinar University for funding.
Author information
Authors and Affiliations
Contributions
M.G. and F.S. organized all experiments and wrote the manuscript. E.G.S., H.A., E.K. and Y.K. performed all experiments and characterizations. They have also drawn the figures.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
41598_2019_52182_MOESM1_ESM.docx
Single-walled carbon nanotube supported Pt-Ru bimetallic superb nanocatalyst for the hydrogen generation from the methanolysis of methylamine-borane at mild conditions
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Sogut, E.G., Acidereli, H., Kuyuldar, E. et al. Single-walled carbon nanotube supported Pt-Ru bimetallic superb nanocatalyst for the hydrogen generation from the methanolysis of methylamine-borane at mild conditions. Sci Rep 9, 15724 (2019). https://doi.org/10.1038/s41598-019-52182-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-52182-w
This article is cited by
-
Architecture engineering of nanostructured catalyst via layer-by-layer adornment of multiple nanocatalysts on silica nanorod arrays for hydrogenation of nitroarenes
Scientific Reports (2022)
-
Electro-catalytic amplified sensor for determination of N-acetylcysteine in the presence of theophylline confirmed by experimental coupled theoretical investigation
Scientific Reports (2021)
-
Monodisperse palladium–cobalt alloy nanocatalyst supported on activated carbon (AC) as highly effective catalyst for the DMAB dehydrocoupling
Scientific Reports (2020)
-
A novel highly active and reusable carbon based platinum-ruthenium nanocatalyst for dimethylamine-borane dehydrogenation in water at room conditions
Scientific Reports (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.