Biological Deep Temperature Imaging with Fluorescence Lifetime of Rare-Earth-Doped Ceramics Particles in the Second NIR Biological Window


Contactless thermal imaging generally relies on mid-infrared cameras and fluorescence imaging with temperature-sensitive phosphors. Fluorescent thermometry in the near-infrared (NIR) region is an emerging technique for analysing deep biological tissues but still requires observation depth calibration. We present an NIR fluorescence time-gated imaging (TGI) thermometry technology based on fluorescence lifetime, an intrinsic fluorophore time constant unrelated to observation depth. Fluorophore used is NaYF4 co-doped with Nd3+ and Yb3+ that emits fluorescence at 1000 nm. An agarose gel-based phantom with the fluorophore embedded at a 5-mm depth was covered by sheets of meat to vary the observation depth. The temperature was determined independently from depth by sequences of NIR fluorescence decay images, and the rate of change in the fluorescence lifetime per temperature was almost constant (−0.0092 ~ −0.010 °C−1) at depths ranging from 0 to 1.4 mm of meat, providing non-contact and absolute measurements of temperature in deep biological tissues.


There is considerable interest in the development of temperature measurements for use in biomedicine since conventional contact thermometries, such as thermocouples and thermometers, are unsuitable for remote temperature measurement1. Because temperature is highly important for controlling various biological functions, including growth2, response3, and cell division4, the development of contactless thermometries is important to visualize dynamic thermal changes in vivo and is also necessary for thermal therapies5,6,7.

Recently, fluorescence imaging has been developed for contactless thermometry applications8,9,10,11 since temperature-dependent changes in the fluorescence lifetime of materials such as rare-earth-doped ceramics particles12, carbonous compounds13, and Cr3+-activated compounds14 have been reported. The fluorescence lifetime is calculated from the decay rate and is unperturbed by the absolute intensity. Thus, thermometry based on the change in fluorescence lifetime is free from fluctuations in excitation power or in concentration-dependent output15,16,17. Temperature imaging using lifetime thermometry has been reported previously13,18; however, use of ultraviolet (UV) and visible (VIS) light limits the measurable depth, and thermometers that detect mid-infrared are limited by the optical loss from biological tissues. Only surface temperature can be measured by the current methods.

For temperature imaging, fluorescence in the near-infrared (NIR) biological window is useful due to less absorption and scattering in biological tissues19,20, and small disturbance from autofluorescence21. The NIR biological window is separated into NIR-I (650–950 nm), NIR-II (1000–1350 nm), and NIR-III (1500–1800 nm). The NIR-II window is appropriate for in vivo deep imaging because of its lower absorption and scattering by biological tissues compared to NIR-I or NIR-III. The use of NIR-II expands the light penetration depth to ≈2–3 cm and allowed through-skull fluorescence imaging of the brain of mice22, whereas the penetration depth is limited to <1 mm in the UV and VIS wavelength ranges23. Recent works reported rare-earth-doped NaYF4 ceramics as NIR-II/III ratiometric nanothermometers24 for deep tissues25; however, this technique still required an observation depth-dependent calibration.

Here, we first attempt temperature imaging that is based on NIR-II fluorescence lifetime of rare-earth-doped NaYF4, which depends on the temperature of the surrounding media but not on observation depth. This material shows NIR-II emission with high efficiency26 and a relatively long lifetime27,28. To realize lifetime imaging of the NIR fluorophores, we constructed a time-gated imaging (TGI) system by controlling the delay of the timing between laser excitation and image acquisition29 (Fig. 1). Using an InGaAs camera that is sensitive to NIR-II19, the TGI system captures a pixel-level fluorescence decay curve that is simultaneously converted into fluorescence lifetime. Previous studies suggested that the TGI system also affords clear fluorescence images by minimizing autofluorescence of biological tissues in the NIR28,30,31. In addition, in vivo multiplexed imaging based on the fluorescence intensity and lifetime in NIR is available in the TGI system32. In this work, the capability of NIR-II fluorophore NaYF4 co-doped with Nd3+ and Yb3+ (NaYF4: Nd3+, Yb3+) as the lifetime-based thermometer was investigated. Temperature imaging of NaYF4: Nd3+, Yb3+ was demonstrated in a mimic of deep biological tissues to investigate the depth dependency of our TGI thermometry for NIR-II fluorescence.

Figure 1

Schematic diagram of the experimental setup used for lifetime imaging. The pulsed laser and NIR camera are computer-controlled by a pulse generator to allow a time series of the fluorescence decay images for lifetime imaging. Analysis of the attenuation rate of fluorescence decay images obtained by the system allowed for measurement of the fluorescence lifetime at each pixel.


Fluorescence lifetime imaging of NaYF4: Nd3+, Yb3+ with changing temperature

First, elemental analysis of NaYF4: Nd3+, Yb3+ by energy-dispersive X-ray spectrometer (EDS) under field emission-type scanning electron microscope (FE-SEM) showed the material contained Y3+, Nd3+, and Yb3+ ions at a ratio of 60: 31: 9 (mol %) (Supplementary Fig. 1). The crystal phase of NaYF4: Nd3+, Yb3+ was mixture of α- and β-phases of NaYF4. Its NIR-II fluorescence was measured under excitation at 808 nm. Figure 2a shows the fluorescence spectra generated by the NaYF4: Nd3+, Yb3+ samples at room temperature. The spectrum shows a major emission band at approximately 1000 nm that is attributed to the Yb3+ (2F5/2 → 2F7/2) and a very small emission peak at 1064 nm derived from Nd3+ (Fig. 2b). The emission profile with the presence of the emission band generated by Yb3+ ions is clear evidence of an efficient energy transfer from Nd3+ to Yb3+ as described in detail previously32. The fluorescence lifetime of the sample was 460 μs at 25 °C as calculated from the fluorescence decay curve determined by infrared photomultiplier (Supplementary Fig. 2).

Figure 2

NIR fluorescence of NaYF4: Nd3+, Yb3+ sample under 808-nm laser excitation. (a) Emission spectrum of NIR fluorescence of Yb3+ (4F5/2 → 4F7/2) from NaYF4: Nd3+, Yb3+ at room temperature. (b) Schematic energy level diagram of NaYF4: Nd3+, Yb3+, which was used as the sensitizer excited by 808-nm laser and as the 1000-nm emitter.

Next, the fluorescence lifetime of the NaYF4: Nd3+, Yb3+ was detected on images acquired by the TGI system, where the temperature was controlled using a heater beneath the sample cuvette. According to the fluorescence decay curve of the NaYF4: Nd3+, Yb3+ (ex. 808 nm; em. 1000 nm) detected by NIR camera (Fig. 3a), its fluorescence lifetime was calculated as τ = \(\int {I}_{em}({t}_{{\rm{delay}}}){\rm{d}}t/{I}_{0}\), where Iem(tdelay) is the emission intensity after the delay time (tdelay) with respect to the excitation pulse, and I0 is the emitted intensity at tdelay = 0 s. The relationship between the calculated fluorescence lifetime and the grey values, which are the signal intensity levels at each pixel in greyscale images captured by the NIR camera, at a delay time of 0 ms was investigated on the biplots for each pixel to optimize the range of delay time used for calculation (Supplementary Fig. 3). The accuracy of fluorescence lifetime calculation at low grey values (15–20 at the delay time of 0 ms) was highest when the analysis was made by the data of delay times from 0 ms to 0.4 ms. Essentially, the plot contains two factors for analysis. One is the number of the delay-time points to be used for the analysis. If the points are more, that should give better analysis because of the averaging effects for avoiding the error due to the fractuation of the data. The other factor is the time range of the analysis. If the latter time points are contained, that causes more introduction of the errors due to worse signal-to-noise ratio at late timings. Accordingly, earlier time-range only contains less data to cause error and longer time range contains more noise to do so. Finally, medium range gives the best accuracy of the analysis as shown in the Supplementary Fig. 3b. Even in this case, the standard deviation of the calculated lifetime was over ±3.0% from the average at each temperature for pixels with grey values ≤15 (as an average of ten images for each condition) at the delay time of 0 ms (Supplementary Fig. 4a). These pixels with weak signals were excluded from the region of interest (ROI) of the temperature mapping. In addition, the biplots (Supplementary Fig. 3a) revealed that the lifetime was overestimated at the pixels with high grey values. The fluorescence lifetime of the pixels with grey values > 65 (tdelay = 0 ms) was overestimated (>3.0% over 460 μs, the lifetime determined by an infrared photomultiplier; Supplementary Fig. 4b) due to exceeding the number of photons over the linear dynamic range of the camera. This overestimation was solved by shifting the delay times for lifetime calculation from 0.1−0.5 ms to 0.4−0.8 ms (Supplementary Fig. 5). To obtain accurate data on the pixels with strong fluorescence intensities, the fluorescence lifetime of the pixels with grey values of >65 at tdelay = 0 ms was calculated from the values at tdelay of ≥0.1 ms at the same pixels. If the grey values at tdelay = 0.1 ms was >65, the fluorescence lifetime of the pixels was calculated from the value of longer delay times at the same pixel. Images of the fluorescence lifetime distribution of phosphor were successfully obtained by using the decay of NIR fluorescence at each pixel collected by the TGI system.

Figure 3

Thermal sensitivity of the fluorescence lifetime of NaYF4: Nd3+, Yb3+ detected by NIR camera. (a) Fluorescence decay curves of NaYF4: Nd3+, Yb3+ in optical cuvette at different experimental temperatures. (b) Calibration curve of temperature vs. fluorescence lifetime detected by NIR camera. (c) Examples of fluorescence images of NaYF4: Nd3+, Yb3+ at delay times of 0, 0.4, and 0.8 ms and calculated lifetime collected at each experimental temperature with excitation by 808-nm pulsed laser (5 W/cm2) from the right side.

As shown in Fig. 3c, as the measurement temperature increased, the fluorescence lifetime of phosphor decreased markedly. The average fluorescence lifetime decreased from 470 ± 11 μs (25 °C) to 390 ± 12 μs (45 °C) (Fig. 3b). The calculated thermal coefficient, ατ, which represents the relative thermal sensitivity of the fluorescence lifetime, using the data obtained by the TGI system was 0.0096 °C−1. These results suggest that the use of NaYF4: Nd3+, Yb3+ is beneficial when applied to thermometry because its fluorescence lifetime is highly sensitive to temperature. Furthermore, the NIR camera in the TGI system detected the thermal dependence of the fluorescence lifetime. Thus, the fluorescence lifetime imaging detected by the TGI system in the NIR biological window could function as a thermometer.

Temperature mapping by TGI

Multiplexed NIR imaging was performed with a combination of NaYF4: Nd3+, Yb3+ and the TGI system. NaYF4: Nd3+, Yb3+ was inserted into agarose gel, which was used as a mimic of a biological phantom, on a hotplate to evaluate the temperature-dependent change in the fluorescence lifetime (Fig. 4a). NIR fluorescence images of NaYF4: Nd3+, Yb3+ in the phantom are shown in Fig. 4c. The thermal coefficient (ατ) in this experiment was calculated from the average values of fluorescence lifetime images at the ROI and was approximately 0.0093 °C−1, similar to the cuvette experiment (Supplementary Fig. 6). These results suggest that the fluorescence lifetime images calculated from the decay for each pixel can be converted to thermal images (Fig. 4c) by using the calibration curve between the temperature and fluorescence lifetime obtained by the TGI system (Supplementary Fig. 6). This indicates that the NaYF4: Nd3+, Yb3+ sample can be used as a lifetime-based thermometer in deep biological tissues because the emission of NaYF4: Nd3+, Yb3+ is not disturbed by water overtone absorbance.

Figure 4

Thermal images obtained by calculation from the calibration curves of the thermally sensitive phosphor in Fig. 3. (a) Schematic representation of the biological deep imaging experiment using agarose gel and thin meat sheets. A hot plate was used as a heat source. (b) Thermal sensitivity of NaYF4: Nd3+, Yb3+ at each experimental condition. (c) Thermal images of NaYF4: Nd3+, Yb3+ while heating the biological tissue phantom from 25 °C to 45 °C with and without meat. Integration times: the sample without meat, 30 μs; the sample with one or two sheets of meat, 1000 μs. Laser power: 20 W/cm2.

Subsequently, 0.7-mm-thick sheets of meat were used to vary the depth of the phantom object. In this setting, with increased attenuation of excitation and emission lights, temperature imaging was carried out in a similar manner to the previous experiments by correcting the conversion from the lifetime to temperature based on the data shown in Supplementary Figs 4 and 5. The measured temperatures of the scattered parts and the ROI containing NaYF4: Nd3+, Yb3+ showed almost the same values, suggesting that the expanded area with fluorescence on the meat is caused by the scattering of fluorescence but not by excitation light. In the case of covering the phantom containing the NaYF4: Nd3+, Yb3+ sample with two sheets of meat, the fluorescence intensity decreased by the attenuation of excitation and emission light. However, the temperature-dependent change in the fluorescence lifetime was detected in the same manner as the phantom with no or less meat (Fig. 4b,c). For example, the lifetime 400 μs is converted to 40.6, 38.5, and 38.9 °C while the uncertainty, the estimated minimal resolvable temperature given by the product of 1/ατ, which is attributed to the intrinsic properties of the material, and the δτ/τ, which is the relative uncertainty of the thermometric parameter given by the experimental instrumentation, is 3.11~6.15 °C in the present study. The thermal sensitivities (ατ), which were calculated from the temperature dependence of the fluorescence lifetimes for each condition as shown in Fig. 4b, were 0.0095 °C−1 (without meat), 0.010 °C−1 (with 0.7-mm-thick meat), and 0.0092 °C−1 (1.4-mm-thick meat). The thermal sensitivity of the phosphor used was 0.0096 °C−1 and was almost constant as the observation depth was varied from 0 to 1.4 mm by the sheets of meat. Thus, the results indicated that the temperature can be measured on the images independent of depth by fluorescence lifetime thermometry using an NIR fluorophore and the TGI system. The designed experimental system of biological deep temperature imaging as demonstrated here will open the pathway to in vivo temperature imaging independent of fluorescence intensity and tissue depth.


The lifetime imaging of NIR-II fluorescence is advantageous for temperature imaging of deep regions because of its independence of the observation depth. Our recent work has realized a conventional ratiometric method of temperature imaging for deep biological tissues (≈2-mm depth) using two bands of fluorescence wavelength (1150 and 1550 nm) of NaYF4 co-doped with Yb3+, Ho3+, and Er3+ phosphors25. However, it still required a calibration by the depth due to a slight shift of absorption spectrum of water, which is contained in the tissues, by temperature change. The possible change in the optical loss by biological tissues should be taken care in in vivo deep temperature imaging such as the brain in mice34. In contrast, the lifetime-based method principally normalizes the original data of fluorescence intensity by the simultaneously obtained data with different delay time after cutting off the excitation irradiation. Therefore, this method shown in the present study does not need further calibrations by excitation power density or the observation depth for absolute temperature measurement. The most advantage of using rare-earth-based materials is their long lifetime at several microseconds. The long lifetime of the phosphors makes their lifetime measurable by the TGI system with conventional cameras for NIR-II. Basically, this fluorescence lifetime sensing method is done by the measurement of luminescence lifetimes of the excited energy levels over the temperature range of investigation as previously mentioned12. The fluorescence lifetime of NaYF4: Nd3+, Yb3+ increases if the Nd3+ → Yb3+ energy transfer was enhanced, while it decreases when the Nd3+ ← Yb3+ energy back-transfer process was activated32. The temperature-dependent change in the fluorescence lifetime is possibly due to the dependence of phonon-assisted energy transfers between Nd3+ and Yb3+ (Fig. 2b) on temperature. In fact, the mechanism is known to be a pure and simple one. It is always a mixture of resonant and phonon-assisted energy transfer, multi-phonon relaxation and back transfers. For wider range of temperature for discussing the characteristics of the thermometry, various kinds of analysis will be required. Although the inaccuracy of 3.0% was accepted for the lifetime calculation to make the temperature images in this article, it is improved to less than 1.5% if the pixels with low grey values would be excluded from the ROI (Supplementary Fig. 4a). Previous studies have shown that visible emission by upconversion of rare-earth-based nanoparticles is available for sub-tissue thermal sensing (1-mm depth) by lifetime analysis35. Ratiometric fluorescence thermometry was also reported using NIR emission bands in shorter NIR wavelength (762 and 825 nm) of a material co-doped with Nd3+ and Yb3+ ions36. Our methods that use the lifetime of NIR emission at longer wavelength have an advantage to do thermal sensing for deeper regions at several millimetres depth. Because we used micro-sized particle that has small surface area in the present study, its fluorescence properties including the lifetime were not affected by the environment, such as pH, surrounding the surface of the particle.

Note that a complete linearity between the number of photons and detected grey values is required for determining fluorescence intensity from the decay images. The linearity is possibly distorted by temporal shortage of electrons in the sensor to cause a negative bias. The electrons are concentrated in the negative bias when very strong pulse comes to decrease the output of modulated phenomena. If not suffered by the strong pulse, the camera output is linear for luminescence observation. Only with this great excitation earlier timing signals are suppressed. The lifetime-based temperature imaging is available using the grey value data of appropriate delay times in the linear range for each pixel. The appropriate delay times should be found for each pixel using the biplots to investigate the relationship between detected fluorescence intensities and calculated fluorescence lifetime in the TGI system. The system reported here is potentially able to show the distribution of temperature in objects. The observation depth of our new temperature imaging technique is several millimeters that may not be perfect for the clinical use. However, this new method based on the long fluorescence lifetime of the NIR-II fluorophores is potentially available as a contactless biomedical imaging tool for understanding the mechanisms of temperature distribution changes in animal models. The error of temperature estimation is still large (3~4 °C) for the samples covered by meat. The cause of the large error is not likely to be the power of excitation because the error was not dependent of the thickness, but is possibly the difference in the integration time to collect images of the fluorescence decay, even though the thermal sensitivity of the fluorescence lifetime is independent of meat thicknesses. The thermal sensitivity of our fluorescence probe was calculated as the thermal coefficient at 0.0096 °C−1, which is in a similar range to the previously reported high-sensitive thermometers based on the fluorescence lifetime35,37. The probes with high thermal sensitivity, along with high quantum yield and higher biocompatibility, will realize definitive optical and contactless sensing of the temperature in biological organs and help us to understand the mechanism of biological phenomena controlled by temperature distributions.

Some limitations of our study merit discussion. First, we used micro-sized particle composed of a mixture of α- and β-phase NaYF4. With the method for synthesising the particles, it is very difficult to control the single phase formation. Since the singularity of the phase is not a focus of our study, we gave up this control to seek for. We suppose it does not affect onto the story of this manuscript. Further investigation is required to determine how the temperature-dependent fluorescence decay can be observed on a single phase NaYF4: Nd3+, Yb3+ nanoparticle, which is suitable for biomedical thermometry application, by NIR cameras with the TGI system. Second, we used a long-pass filter with a cut-on wavelength at 980 nm. We chose this filter to cut the photo-excitation pulse as well as possible; however, it also cut a part of Yb3+ emission spectrum. Ideally, if one has a sharper cutting filter with better optical density, that results in more convenient. The effect of the excitation pulse might be enhanced when nanoparticles would be used as a thermometer because of their lower emission quantum yield than micro-sized powders. Further investigation with optimized optical system with more appropriate spectral filters is also needed. Finally, the uncertainty of the estimation of temperature reported here (3.11~6.15 °C) is not good compared to previously reported nanothermometers25,33. Further experiments are currently underway for optimising dopant concentration and core/shell architecture31 to enhance the thermal sensitivity of the NIR fluorescence lifetime and to improve the accuracy of the temperature measurement.


In summary, we successfully visualized temperature changes by using the TGI system for analysing the decay time of NIR-II fluorescence of NaYF4: Nd3+, Yb3+ particles in biological deep tissue under 808-nm laser excitation. The results obtained at different thermometer depths, controlled by covering the agarose gel with sheets of meat, showed that thermometry regardless of depth could be realized. The thermal sensitivity of the phosphor used for the measurement was 0.0096 °C−1, and the sensitivity of its fluorescence lifetime was almost constant (−0.0092 ~ −0.010 °C−1) while estimating the fluorescence decay through varying meat thicknesses from 0 to 1.4 mm. Therefore, a thermal imaging system comprised of a rare-earth-doped fluorophore and the TGI system can image deep tissue temperatures without the issues introduced by tissue in the optical pathway or laser power. Future work will focus on the development of novel NIR-II fluorophores with high quantum yields, high thermal sensitivities, and high biocompatibilities, all of which could lead to further advances towards in vivo optical temperature imaging.



Yttrium(III) nitrate hexahydrate (Y(NO3)3·6H2O) and sodium fluoride (NaF) were purchased from Kanto Chemicals (Tokyo, Japan). Neodymium(III) nitrate hexahydrate (Nd(NO3)3·6H2O) and ytterbium(III) nitrate (Yb(NO3)3·6H2O) were purchased from Sigma-Aldrich (St. Louis, MO, USA). Agarose powder was purchased from Nacalai Tesque Inc. (Kyoto, Japan). All the reagents were used without further purification.

Synthesis and optical characterization of rare-earth-doped NaYF4

NaYF4: Nd3+, Yb3+ was synthesized by a standard co-precipitation method38. Y(NO)3·6H2O (6.0 mmol), Nd(NO)3·6H2O (3.0 mmol), and Yb(NO)3·6H2O (1.0 mmol) were dissolved in 10 mL of distilled water. The mixture solution was dropped into 40 mL of an aqueous solution of NaF (60 mmol) and stirred for 1 h at 75 °C. After stirring, the precipitate was collected by centrifugation (20,000 g, 10 min, ×3). The sample was then dried at 80 °C for 24 h. Subsequently, the samples were treated with NH4F (800 mg) for 1 h at 550 °C to yield NaYF4 co-doped with 30 mol% Nd3+ and 10 mol% Yb3+. The crystalline phase of synthesized NaYF4: Nd3+, Yb3+ was analysed by using RINT-TTR III (Rigaku, Japan). Elemental component of the NaYF4: Nd3+, Yb3+ was analysed by FE-SEM/EDS (S-4200; Hitachi High-Technologies Co., Tokyo, Japan). Fluorescence spectra of the NaYF4: Nd3+, Yb3+ under 808-nm excitation were detected with a spectrometer (NIRQuest; Ocean Optics Inc., Dunedin, FL, USA). Fluorescence lifetime of the sample at room temperature (25 °C) was investigated by using an optical parametric oscillator (Surelite II-10; Continuum Inc., San Jose, CA, USA) pumped by a frequency tripled Nd-doped yttrium aluminum garnet laser operating at 355 nm. The optical parametric oscillator provides 5 ns pulses at 808 nm wavelength with an average energy of 9.5 mJ and a repetition rate of 10 Hz. Time evolution was detected by an infrared photomultiplier (H10330C; Hamamatsu Photonics Co. Ltd., Shizuoka, Japan) connected to a digital oscilloscope (TDS2024C; Tektronix Inc., Beaverton, OR, USA) with a 980-nm long-pass filter (#86–248; Edmund Optics Inc., Barrington, NJ, USA) to detect only fluorescence.

Time-gated imaging of rare-earth-doped ceramics nanoparticle

The TGI system, composed of a pulsed laser, an NIR camera, and a pulse generator, was used to acquire fluorescence decay and lifetime images, as schematically shown in Fig. 1. A custom-built pulsed laser diode (wavelength: 808 nm; power: 4 W) was used to generate 10 ms pulses at a repetition rate of 20 Hz. The pulse-to-pulse separation was set to 40 ms, during which the fluorescence of the phosphors disappears completely. A time series of fluorescence decay images was obtained with an NIR camera (ARTCAM-0016TNIR; Artlay Co. Ltd., Tokyo, Japan). A 980-nm long-pass filter was placed in front of the NIR camera. A digital delay/pulse generator (DG535; SRS Inc., Sunnyvale, CA, USA) connected the laser and the camera to trigger them at a delayed time (tdelay). To obtain the fluorescence decay curves, a series of fluorescence images (8-bit) was acquired, where tdelay ranged from 0 to 1.0 ms in increments of 0.1 ms. For lifetime measurements, NaYF4: Nd3+, Yb3+ (30 v/v% in water) in an optical glass cuvette (PSK-10; Sansyo Co. Ltd., Tokyo, Japan) was placed in a temperature-controlled cuvette holder (qpod-2e, Ocean Optics Inc., Dunedin, FL, USA) and imaged in the TGI system, and the temperature was varied from 25 °C to 45 °C. For temperature imaging, a phantom consisting of NaYF4: Nd3+, Yb3+-embedded agarose gel (3%) was placed on a hot plate (CH-180; As One Co. Ltd., Osaka, Japan). A thermocouple (DS-2000-0121; As One Co. Ltd., Tokyo, Japan) was inserted into the phantom to measure the temperature at the position of the embedded fluorophores. Note that the vertical position of the thermocouple and the fluorophores was the same. After heating the phantom with the hot plate to 45 °C, the fluorescence decay of the phosphors was recorded using the TGI system during the thermal relaxation. To study the influence of observation depth in biological tissues, one or two sheets of commercial raw pork meat (0.7 mm thick each) were placed over the phantom, and the temperature imaging was performed through the sheets. The influence of depth on temperature distribution measurements was evaluated by calculating the normalized lifetime thermal coefficient, which was defined as \({\alpha }_{\tau }=|d{\tau }^{{\rm{nor}}}{(T)}_{\tau }/dT|\), where \({\tau }_{f}^{nor}(T)\) is the fluorescence decay time at temperature T normalized to the room temperature value (i.e. \({\tau }_{f}^{{\rm{nor}}}(T)={\tau }_{f}(T)/{\tau }_{f}({\rm{25}}\,^\circ {\rm{C}})\))37.

Data Availability

The data required to reproduce these findings are available to download from


  1. 1.

    Kolesnikov, I. E. et al. Y2O3: Nd3+ nanocrystals as ratiometric luminescence thermal sensors operating in the optical windows of biological tissues. J. Luminescence 204, 506–512 (2018).

    ADS  CAS  Article  Google Scholar 

  2. 2.

    Forrest, W. W. & Walker, D. J. Thermodynamics of biological growth. Nature 196, 990–991 (1962).

    ADS  CAS  Article  Google Scholar 

  3. 3.

    Lindquist, S. The heat-shock response. Ann. Rev. Biochem. 55, 1151–1191 (1986).

    CAS  Article  Google Scholar 

  4. 4.

    Begasse, M. L., Leaver, M., Vazquez, F., Gril, S. W. & Hyman, A. A. Temperature dependence of cell division timing accounts for a shift in the thermal limits of C. elegans and C. briggsae. Cell Rep. 10, 647–653 (2015).

    CAS  Article  Google Scholar 

  5. 5.

    Lal, S., Clare, S. E. & Halas, N. J. Nanoshell-enabled photothermal therapy: Impending clinical impact. Acc. Chem. Res. 41, 1842–1851 (2008).

    CAS  Article  Google Scholar 

  6. 6.

    Jaque, D. et al. Nanoparticles for photothermal therapies. Nanoscale 6, 9494–9530 (2014).

    ADS  CAS  Article  Google Scholar 

  7. 7.

    Ai, X., Mu, J. & Xing, B. Recent advances of light-mediated theranostics. Theranostics 6, 2439–2457 (2016).

    CAS  Article  Google Scholar 

  8. 8.

    Hemmer, E., Acosta-Mora, P., Méndez-Ramos, J. & Fischer, S. Optical nanoprobes for biomedical applications: shining a light on upconverting and near-infrared emitting nanoparticles for imaging, thermal sensing, and photodynamic therapy. J. Mater. Chem. B 5, 4365–4392 (2017).

    CAS  Article  Google Scholar 

  9. 9.

    del Rosal, B., Ximendes, E., Rocha, U. & Jaque, D. In vivo luminescence nanothermometry: from materials to applications. Adv. Opt. Mater. 5, 1600508 (2017).

    Article  Google Scholar 

  10. 10.

    Brites, C. D., Balabhadra, S. & Carlos, L. D. Lanthanide-based thermometers: At the cutting-edge of luminescence thermometry. Adv. Opt. Mater. 2018, 1801239 (2018).

    Google Scholar 

  11. 11.

    Okabe, K., Sakaguchi, R., Shi, B. & Kiyonaka, S. Intracellular thermometry with fluorescent sensors for thermal biology. Eur. J. Physiol. 470, 717–731 (2018).

    CAS  Article  Google Scholar 

  12. 12.

    Gharouel, S., Labrador-Páez, L., Haro-González, P., Horchani-Naifer, K. & Férid, M. Fluorescence intensity ratio and lifetime thermometry of praseodymium phosphates for temperature sensing. J. Luminescence 201, 372–382 (2018).

    ADS  CAS  Article  Google Scholar 

  13. 13.

    Li, H. et al. Multifunctional carbon dot for lifetime thermal sensing, nucleolus imaging and antialgal activity. J. Mater. Chem. B 6, 5078–5717 (2018).

    Google Scholar 

  14. 14.

    Back, M. et al. Revisiting Cr3+-Doped Bi2Ga4O9 spectroscopy: Crystal field effect and optical thermometric behavior of near-infrared-emitting singly-activated phosphors. ACS Appl Mater Interfaces 10, 41512–41524 (2018).

    CAS  Article  Google Scholar 

  15. 15.

    Lippitsch, M. E., Pasterhofer, J., Leiner, M. J. P. & Wolfbeis, O. S. Fibre-optic oxygen sensor with the fluorescence decay time as the information carrier. Anal. Chim. Acta 205, 1–6 (1988).

    CAS  Article  Google Scholar 

  16. 16.

    Lakowicz, J. R., Szmacinski, H., Nowaczyk, K., Berndt, K. W. & Johnson, M. Fluorescence lifetime imaging. Anal. Bio. Chem. 202, 316–330 (1992).

    CAS  Google Scholar 

  17. 17.

    Szmacinski, H. & Lakowicz, J. R. Fluorescence lifetime-based sensing and imaging. Sens. Actuators B Chem. 29, 16–24 (1995).

    CAS  Article  Google Scholar 

  18. 18.

    Okabe, K. et al. Intracellular temperature mapping with a fluorescent polymeric thermometer and fluorescence lifetime imaging microscopy. Nat. Commun. 3, 705 (2012).

    ADS  Article  Google Scholar 

  19. 19.

    Smith, A. M., Mancini, M. C. & Nie, S. Bioimaging: second window for in vivo imaging. Nat. Nanotechnol. 4, 710–711 (2010).

    ADS  Article  Google Scholar 

  20. 20.

    Anderson, R. R. & Parrish, J. A. The optics of human skin. J. Invest. Dermatol. 77, 13–19 (1981).

    CAS  Article  Google Scholar 

  21. 21.

    del Rosal, B., Villa, I., Jaque, D. & Sanz-Rodríguez, F. In vivo autofluorescence in the biological windows: the role of pigmentation. J. Biophotonics 9, 1059–1067 (2016).

    Article  Google Scholar 

  22. 22.

    Hong, G. et al. Through-skull fluorescence imaging of the brain in a new near-infrared window. Nat. Photonics 8, 723–730 (2014).

    ADS  CAS  Article  Google Scholar 

  23. 23.

    Hemmer, E. et al. Upconverting and NIR-emitting rare earth based nanostructures for NIR-bioimaging. Nanoscale 5, 11339–11361 (2013).

    ADS  CAS  Article  Google Scholar 

  24. 24.

    Kamimura, M., Matsumoto, T., Suyari, S., Umezawa, M. & Soga, K. Ratiometric near-infrared fluorescence nanothermometry in the OTN-NIR (NIR II/III) biological window based on rare-earth doped β-NaYF4 nanoparticles. J. Mater. Chem. B 5, 1917–1925 (2017).

    CAS  Article  Google Scholar 

  25. 25.

    Sekiyama, S. et al. Temperature sensing of deep abdominal region in mice by using over-1000 nm near-infrared luminescence of rare-earth-doped NaYF4 nanothermometer. Sci. Rep. 8, 16979 (2018).

    ADS  Article  Google Scholar 

  26. 26.

    Naczynski, D. J. et al. Rare-earth-doped biological composites as in vivo shortwave infrared reporters. Nat. Commun. 4, 2199 (2013).

    ADS  CAS  Article  Google Scholar 

  27. 27.

    Sun, T., Zhang, Z. Y., Grattan, K. T. V. & Palmer, A. W. Ytterbium-based fluorescence decay time fiber optic temperature sensor systems. Rev. Sci. Instruments 69, 4179–4185 (1998).

    ADS  CAS  Article  Google Scholar 

  28. 28.

    del Rosal, B. et al. Overcoming autofluorescence: long-lifetime infrared nanoparticles for time-gated in vivo imaging. Adv. Mater. 28, 10188–10193 (2016).

    Article  Google Scholar 

  29. 29.

    Gu, L. et al. In vivo time-gated fluorescence imaging with biodegradable luminescent porous silicon nanoparticles. Nat. Commun. 4, 2326 (2013).

    ADS  Article  Google Scholar 

  30. 30.

    Joo, J. et al. Gated luminescence imaging of silicon nanoparticles. ACS Nano 9, 6233–6241 (2015).

    CAS  Article  Google Scholar 

  31. 31.

    Tan, M. et al. Rare-earth-doped fluoride nanoparticles with engineered long luminescence lifetime for time-gated in vivo optical imaging in the second biological window. Nanoscale 10, 17771–17780 (2018).

    CAS  Article  Google Scholar 

  32. 32.

    Ortgies, D. H. et al. Lifetime-encoded infrared-emitting nanoparticles for in vivo multiplexed imaging. ACS Nano 12, 4362–4368 (2018).

    CAS  Article  Google Scholar 

  33. 33.

    Wang, Z. et al. Lanthanide-organic framework nanothermometers prepared by Spray-Drying. Adv. Funct. Mater. 25, 2824–2830 (2015).

    CAS  Article  Google Scholar 

  34. 34.

    del Rosal, B. et al. In vivo contactless brain nanothermometry. Adv. Funct. Mater. 2018, 1806088 (2018).

    Article  Google Scholar 

  35. 35.

    Savchuk, O. A. et al. Er: Yb: NaY2F5O up-converting nanoparticles for sub-tissue fluorescence lifetime thermal sensing. Nanoscale 6, 9727–9733 (2014).

    ADS  CAS  Article  Google Scholar 

  36. 36.

    Gao, G. et al. Wide-range non-contact fluorescence intensity ratio thermometer based on Yb3+/Nd3+ co-doped La2O3 microcrystals operating from 290 to 1230 K. J Mater Chem C 6, 4163–4170 (2018).

    CAS  Article  Google Scholar 

  37. 37.

    He, F. et al. Influence of surfactants on the morphology, upconversion emission, and magnetic properties of β-NaGdF4: Yb3+, Ln3+ (Ln = Er, Tm, Ho). Dalton Trans. 42, 10019–10028 (2013).

    CAS  Article  Google Scholar 

  38. 38.

    Haro-González, P., Martínez-Maestro, L., Martín, I. R., García-Solé, J. & Jaque, D. High-sensitivity fluorescence lifetime thermal sensing based on CdTe quantum dots. Small 8, 2652–2658 (2012).

    Article  Google Scholar 

Download references


This work was partially supported by the MEXT Grant-in-Aid for Scientific Research on Innovative Areas (Resonance Bio), No. 15H05950, the MEXT Grant-in-Aid for Scientific Research (B), No. 16H04499, the MEXT-Supported Program for the Strategic Research Foundation at Private Universities, no. S1511012, and the Center of Innovation Program “COINS” from Japan Science and Technology Agency, JST.

Author information




K.S. is the main project leader and conceived the overall research idea. T.C. and M.U. mainly designed and performed all experiment procedures and the acquisition, analysis, and interpretation of data, and drafted the manuscript. K.M. and N.H. contributed to the development of the method to handle the large amount of data obtained. S.S. was substantially involved in designing the work with changing the temperature of objects. M.K. contributed to the conception of the work. K.O. was substantially involved in the interpretation of data and drafting the manuscript. All authors have given approval to the final version of the manuscript, and have agreed both to be personally accountable for the author’s own contributions and to ensure that questions related to the accuracy or integrity of any part of the work, even ones in which the author was not personally involved, are appropriately investigated, resolved, and the resolution documented in the literature.

Corresponding authors

Correspondence to Masakazu Umezawa or Kohei Soga.

Ethics declarations

Competing Interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Chihara, T., Umezawa, M., Miyata, K. et al. Biological Deep Temperature Imaging with Fluorescence Lifetime of Rare-Earth-Doped Ceramics Particles in the Second NIR Biological Window. Sci Rep 9, 12806 (2019).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing