Facile and Sustainable Synthesis of Erythritol bis(carbonate), a Valuable Monomer for Non-Isocyanate Polyurethanes (NIPUs)


Recently, R. Mülhaupt et al. introduced the first high yielding synthesis of erythritol bis(carbonate) from erythritol with diphenyl carbonate (DPC) as reagent. They utilized it as monomer for the synthesis of non-isocyanate polyurethanes (NIPUs). Here, we present a significantly more sustainable procedure for the carbonate formation regarding solvent, carbonyl source, reaction temperature, reaction time, reduced pressure during the reaction, simplicity of the workup as well as recycling of reagents. Catalysed by triazabicyclodecene (TBD), dimethyl carbonate as solvent as well as reagent leads to selective product formation and facile product separation by filtration. After addition of new starting materials, the mixture of catalyst and DMC was reused up to 8 times without loss of catalytic activity.


Polyurethanes are among the most widely used polymers in industry – in particular for specialty applications in furniture, construction, electronics, automotive and packaging. Typically, polyurethanes are obtained by polymerization of polyols with diisocyanates as co-monomer. However, the use of isocyanates is not considered sustainable1. Several methods are available for the synthesis of non-isocyanate polyurethanes (NIPU)2,3. A first step towards more sustainable polyurethanes was the synthesis of isocyanates using the Curtius rearrangement to avoid the use of phosgene, even though it has to be viewed critically, as it proceeds via toxic acyl azides4. Sustainable polyurethanes with backbones similar to the petroleum-based ones can be produced by transurethanization of carbamates5,6,7. Moreover, a sustainable synthesis of bio-based carbamates was performed by Lossen rearrangement of hydroxamic acids, which are activated in situ by dialkyl carbonates in the presence of catalytic amounts of tertiary amine bases (0.1–0.4 eq.)8. Still, NIPU synthesis from bis-cyclic carbonates (bCC) and diamines is arguably the most promising approach9, as the obtained molecular weights are typically higher than with the other approaches. The first route for the synthesis of five-membered carbonates is on the example of ethylene carbonate and involves phosgenation of ethylene glycol by phosgene or triphosgene, which is due to obvious reasons not suitable for a sustainable synthesis, as the original purpose of NIPUs is to avoid phosgene10. More sustainable approaches are typically based on the insertion of CO2 into epoxides, which are synthesized from renewable resources containing double bonds or from 1,2-diols.

For some carbonates, such as e.g. glycerol carbonate, the direct synthesis from the 1,2-diol and supercritical CO2 (SCCO2) has been established11, although the reaction is currently still not feasible on an industrial scale due to low conversions (32%)2. Another method utilizing supercritical CO2 was reported by M. Aresta et al. first obtaining the ketal of cyclohexanone and 1,2-ethanediol followed by transition-metal complex catalyzed carbonate formation in SCCO2 or with CO2 in organic solvents12. Other methods involving pressurized CO2 and 1,2-diols are performed in acetonitrile at 170 °C and catalyzed by metallic acetates13, by electrosynthesis14, or with diazabicycloundecen in dibromomethane15. The carbonate interchange reaction between 1,2-diols and ethylene carbonate or linear carbonates (dimethyl carbonate, diethyl carbonate or diphenyl carbonate)16,17,18 is more common and also used for the herein reported approach. A different type of transesterification can be achieved with urea and ZnO or various other solid catalysts releasing ammonia in the process19. Very interesting is the oxidative carbonylation with carbon monoxide using, for instance, palladium-based catalysts20,21, which is also the established synthesis of most linear carbonates. Alternatively to a two-step procedure (first synthesizing the epoxide and insertion of CO2 afterwards), olefins can be directly converted by oxidative carboxylation with a catalytic system of MoO2(acac)2, a quaternary ammonium salt and tert-butyl hydroperoxide as an oxidant in an one-pot multistep process22. Other methods available for this oxidative carboxylation were reviewed in 2011 by J. Sun and coworkers23. Methods involving other starting materials are of minor importance, e.g. from halohydrins23, substituted propargyl alcohols24,25, halogenated carbonates26, or linear oligo-carbonates27,28,29. Six- or seven- membered cyclic carbonates can be obtained from 1,3-diols or 1,4 diols by similar means as five-membered cyclic carbonates. While they provide a better reactivity due to a lower thermodynamic stability (six-membered cyclic carbonates react up to 60 times faster, seven-membered cyclic carbonates react up to 2,400 times faster)9, the synthesis of six- or seven- membered carbonates is significantly more difficult for exactly the same reason30. Still, K. Tomishige et al. reported a particularly efficient catalyst (CeO2) with high yields for six- membered carbonates (62–99%) from CO2 and diols in 201431. However, a high excess (10 times) of 2-cyanopyridine was needed to remove water from the reaction mixture and obtain a high selectivity.

Erythritol bis(carbonate) (EBC) was already synthesized in 1960 from butadiene and patented by Union Carbide Whelan for polyurethane synthesis32, however it can also be synthesized in a more sustainable fashion by transesterification from the renewable sugar substitute erythritol. Erythritol is a narurally occuring sugar alcohol, which is present in many fruits and vegetables and used as a bulk sweetener. It is industrially produced by a fermentation process with the naturally occurring yeast Moniliella pollinis from aqueous solutions of glucose or sucrose33. Starting from erythritol, several routes to EBC are known. T. Griesser et al. achieved high yields up to 88%, however the phosgene based 1,1′-carbonyldiimidazole was used as carbonyl source34. Until now, the carboxylation of erythritol with dimethyl carbonate was claimed to be unfeasible due to low yields35, since in 2012 G. Rokicki et al. reported it as side reaction of an intramolecular etherification with only 10% yield36. They utilized an excess of dimethyl carbonate (DMC) at 70 °C and 226 mbar with K2CO3 as catalyst, only obtaining the desired EBC in 5% yield. In 2017, based on these results, R. Mülhaupt et al. used diphenyl carbonate (DPC) instead of DMC at 120 °C and 30 mbar in DMSO with Zn(OAc)2 as catalyst, thus avoiding the intramolecular etherification and obtaining EBC in 80–90% yield35. Additionally, the same method was later applied to sorbitol in order to obtain sorbitol tricarbonate37. Even though the yield is good, the synthesis lacks in sustainability regarding several aspects. DPC is far less sustainable than DMC. Aside from the classic unsustainable phosgenation of alcohols, both can be produced by oxidative carbonylation from the respective alcohol and carbon monoxide38. However, while phenol is typically produced in the cumene process from fossil benzene and propene39, methanol can be obtained via various different routes from renewables (e.g. from bio-derived synthesis gas or methane)40. Moreover, the process of the oxidative carbonylation of methanol is more efficient and involves cheaper catalysts (copper instead of palladium) and auxiliaries than the one of phenol. Industrially, the oxidative carbonylation of phenol is barely realized, while for methanol this route is established38. Here, we report on an efficient and sustainable synthesis of EBC based on DMC (Fig. 1).

Figure 1

General reaction scheme of the reaction of erythritol to erythritol bis(carbonate). The pure product can be separated by filtration and the reaction mixture reused for another reaction cycle.


To avoid the intramolecular ether formation described in literature36, a selective transesterification catalyst with high activity even at low temperatures was needed. TBD is known for such properties41 and was utilized in a moderate amount of 5 mol%. Erythritol was barely soluble in DMC, however at 60 °C, a small amount was soluble and thus successfully transesterified without observing any side reactions via GC-MS. By removing the methanol under reduced pressure, EBC precipitated from the reaction mixture and the overall equilibrium was shifted giving 90% yield after 40 minutes. After completion and cooling the mixture to room temperature, the product was simply filtered off and the mother liquor, which still contained DMC, the catalyst and dissolved trace amounts of product, could be reused in another reaction (compare Fig. 1). The recovery of the reaction mixture was performed eight times in triplicate with the same amount of reactant and solvent (i.e. adding fresh DMC and erythritol each time).

After the first run, the reaction time was shortened from 40 minutes to 25 minutes, which can be explained by product residue in the mixture promoting the crystallization. A similar decrease in reaction time could be obtained by adding 3.5 mol% product from the beginning, confirming that already present product promotes crystallization. After eight runs, an average yield of 90 ± 1% was observed, which fits to the initial 90%, indicating that the catalyst retained its activity. Even after storage of the reaction mixture overnight, the catalyst was still active and showed no signs of degradation. In contrast, evaporation of the mixture to dryness led to change in color to dark red after heating for additional 30 minutes, indicating the decomposition of the catalyst. Typically, after simple filtration and washing with DMC, the product was already highly pure, however, in case of remaining reactant or catalyst, the impurities might simply be removed by washing the product with water. In the 1H-NMR spectrum (see Fig. 2), three distinct peaks can be observed as the methylene group of signal b undergoes diastereotopic signal splitting due to hindered rotation, which can be confirmed by HSQC as signals b1 and b2 both couple with the same carbon at 64.7 ppm. The data of the 1H-NMR and 13C-NMR spectrum were in accordance with the literature36.

Figure 2

1H-NMR, HSQC and COSY of erythritol bis(carbonate). Chemical shifts of the 1H-NMR are depicted in green, correlated shifts of the 13C-NMR in black.

The simplicity of the synthesis and workup coupled with its sustainability clearly highlight the advantages compared to the literature procedure (see Table 1 and Scheme 1).

Table 1 Comparison of literature procedure and new procedure for the synthesis of erythritol bis(carbonate).

DMSO, the solvent for the literature procedure, achieves a total rating of “some issues” in GSK’s solvent sustainability guide, while DMC is among the few solvents with “few issues42”. DPC is, as mentioned above, a less sustainable carbonyl source compared to DMC due to its production but also because of the bad atom economy of the reaction itself (see Fig. 3). By using DMC, the atom economy could be improved from 31.6 to 57.7% compared to literature. The reaction temperature for the new procedure is far lower (60 °C compared to 120 °C) minimizing energy use. A shorter reaction time (2 h instead of 19 h) brings obvious advantages as well as a moderately (314 mbar) instead of a highly (30 mbar) reduced pressure. In fact, the reaction worked just as selective without any reduced pressure, however the product did not precipitate if a considerable amount of methanol formed during the reaction was present. The catalyst TBD is more expensive than Zn(OAc)2*2H2O (0.16 € g−1, product number 383058-500G compared to 6.80 € g−1, product number 345571-5G; Sigma Aldrich; checked 06.05.2018), but as it can be recovered and reused, the overall price might not be much higher. The workup consisted of a simple filtration compared to a recrystallization, which requires additional solvent and thus results in additional waste, as it cannot be reused or recycled. When testing the developed reactions conditions with sorbitol, another important renewable alditol that could yield a useful tricarbonate for NIPU synthesis, unfortunately, significantly lower conversion as well as selectivity was observed. Thus, the development of specific conditions for each alditol seems necessary. For instance, L. Avérous et al. reported a yield of up to 50% of (1R,4S,5R,6R)-6-(1,3-dioxolan-2-one-4-yl)-2,4,7trioxa-3-oxy-bicyclo[3.3.0]octane, a bCC from D-sorbitol obtained after intramolecular etherification, using 5 mol% TBD in DMC at 75 °C and a reaction time of 16 hours43.

Figure 3

Schematic comparison of literature procedure and new procedure for the synthesis of erythritol bis(carbonate).

In conclusion, erythritol bis(carbonate) – a valuable monomer for NIPU synthesis – was obtained from erythritol featuring mild reaction conditions and a facile workup in 90% yield. The reusability of catalyst and reaction mixture was demonstrated up to 8 times, while the catalyst showed no sign of decrease in activity. In principle, the developed procedure might enable a one-pot polymerization by directly adding the diamine to the reaction mixture due to its high selectivity as well as the presence of a TBD as a suitable catalyst, but keeping the catalyst in the monomer synthesis cycle even longer seems more practical and more sustainable.

Materials and Methods


GC-MS (electron impact, EI) measurements were performed on the following system: a Varian 431 GC instrument with a capillary column FactorFour VF-5 ms (30 m × 0.25 mm × 0.25 mm) and a Varian 210 ion trap mass detector. Scans were performed from 40 to 650 m/z at rate of 1.0 scans s−1. The oven temperature program was: initial temperature 95 °C, hold for 1 min, ramp at 15 °C min−1 to 220 °C, hold for 4 min, ramp at 15 °C min−1 to 300 °C, hold for 2 min. The injector transfer line temperature was set to 250 °C. Measurements were performed in the split – split mode (split ratio 50:1) using helium as carrier gas (flow rate 1.0 mL min−1).

NMR spectra (300 MHz for 1H- and at 75 MHz for 13C-measurements) were recorded on a Bruker AVANCE DPX spectrometer operating at 300 K. For all NMR-spectra the residual non-deuterated solvent (1H NMR) or CDCl3 (13C NMR) signal was used as internal standard. Infrared spectra (IR) were recorded on a Bruker Alpha-p instrument in a frequency range from 3998 to 374 cm−1 applying ATR technology.

ESI-MS spectra were recorded on a Q Exactive (Orbitrap) mass spectrometer (Thermo Fisher Scientific, San Jose, CA, USA) equipped with a HESI II probe to record high resolution electrospray ionization – MS (ESI-MS). Calibration was carried out in the m/z range of 74–1.822 using premixed calibration solutions (Thermo Fisher Scientific). A constant spray voltage of 4.7 kV and a dimensionless sheath gas of 5 were employed. The S-lens RF level was set to 62.0, while the capillary temperature was set to 250 °C.

Synthesis of erythritol bis(carbonate)

In a 100 mL flask, erythritol (2.00 g, 16.4 mmol, 1.00 eq) and TBD (114 mg, 0.820 mmol, 0.05 eq.) were dispersed in 41 mL DMC and heated to 60 °C for 40 min at the rotary evaporator at 314 mbar. The crystalline erythritol dissolved completely after 30 min and after 35 min, a white precipitate was formed. The product was filtered off after the mixture was cooled down to room temperature and washed with dimethyl carbonate yielding a white powder (2.53 g, 90%).

1H-NMR (DMSO-d6, 300 MHz): δ (ppm) = 5.25–5.07 (m, 2 H, CH), 4.69–4.52 (m, 2H, CH2(a), diastereotopic signals), 4.47–4.31 (m, 2H, CH2, diastereotopic signals); 13C-NMR (DMSO-d6, 75 MHz): δ (ppm) = 158.2 (CO), 74.9 (CH), 64.7 (–CH2-); HRMS (ESI) of C6H6O6 [M + H]+ m/z calc. 175.0237, found 175.0234; IR (ATR): ν = 1803.7, 1779.0, 1545.5, 1476.1, 1381.2, 1299.6, 1206.5, 1144.6, 1067.0, 1030.9, 978.1, 896.2, 771.8, 739.1, 719.1, 532.1, 384.9 cm−1.

Recovery experiments

In a 100 mL flask, erythritol (2.00 g, 16.4 mmol, 1.00 eq) and TBD (114 mg, 0.820 mmol, 0.05 eq.) were dispersed in 41 mL DMC and heated to 60 °C for 40 min at the rotary evaporator at 314 mbar. The crystalline erythritol dissolved completely after 30 min and after 35 min, a white precipitate was formed. The product was filtered off after the mixture was cooled down to room temperature and washed with 15 mL dimethyl carbonate, which was combined with the mother liquor, to obtain the product (2.53 g, 90%) and again 41 mL volume of a mixture containing the catalyst and non-precipitated product. Another batch of erythritol (2.00 g, 16.4 mmol, 1.00 eq) was dispersed in the mother liquor and the procedure was repeated for 7 additional times yielding on average 90 ± 1% (procedure carried out in triplicate) of the product.


  1. 1.

    Llevot, A. & Meier, M. Perspective: green polyurethane synthesis for coating applications. Polym. Int. 59, 257 (2018).

    Google Scholar 

  2. 2.

    Maisonneuve, L., Lamarzelle, O., Rix, E., Grau, E. & Cramail, H. Isocyanate-Free Routes to Polyurethanes and Poly(hydroxy Urethane)s. Chem. Rev. 115, 12407–12439 (2015).

    CAS  Article  Google Scholar 

  3. 3.

    Kreye, O., Mutlu, H. & Meier, M. A. R. Sustainable routes to polyurethane precursors. Green Chem. 15, 1431–1455 (2013).

    CAS  Article  Google Scholar 

  4. 4.

    More, A. S. et al. Novel fatty acid based di-isocyanates towards the synthesis of thermoplastic polyurethanes. Eur. Polym. J. 49, 823–833 (2013).

    CAS  Article  Google Scholar 

  5. 5.

    Deepa, P. & Jayakannan, M. Solvent-free and nonisocyanate melt transurethane reaction for aliphatic polyurethanes and mechanistic aspects. J. Polym. Sci. A 46, 2445–2458 (2008).

    CAS  Article  Google Scholar 

  6. 6.

    Deepa, P. & Jayakannan, M. Solvent-induced self-organization approach for polymeric architectures of micropores, hexagons and spheres based on polyurethanes prepared via novel melt transurethane methodology. J. Polym. Sci. A 45, 2351–2366 (2007).

    CAS  Article  Google Scholar 

  7. 7.

    Deepa, P. & Jayakannan, M. Polyurethane-oligo(phenylenevinylene) random copolymers: π-Conjugated pores, vesicles, and nanospheres via solvent-induced self-organization. J. Polym. Sci. A 46, 5897–5915 (2008).

    CAS  Article  Google Scholar 

  8. 8.

    Unverferth, M., Kreye, O., Prohammer, A. & Meier, M. A. R. Renewable Non-Isocyanate Based Thermoplastic Polyurethanes via Polycondensation of Dimethyl Carbamate Monomers with Diols. Macromol. Rapid Commun. 34, 1569–1574 (2013).

    CAS  Article  Google Scholar 

  9. 9.

    Datta, J. & Włoch, M. Progress in non-isocyanate polyurethanes synthesized from cyclic carbonate intermediates and di- or polyamines in the context of structure–properties relationship and from an environmental point of view. Polym. Bull. 73, 1459–1496 (2016).

    CAS  Article  Google Scholar 

  10. 10.

    Nemirowsky, J. Ueber die Einwirkung von Chlorkohlenoxyd auf Aethylenglycol; vorläufige Mittheilung. J. Prakt. Chem. 28, 439–440 (1883).

    Article  Google Scholar 

  11. 11.

    Vieville, C., Yoo, J. W., Pelet, S. & Mouloungui, Z. Synthesis of glycerol carbonate by direct carbonatation of glycerol in supercritical CO2 in the presence of zeolites and ion exchange resins. Catal. Lett. 56, 245–247 (1998).

    CAS  Article  Google Scholar 

  12. 12.

    Aresta, M., Dibenedetto, A., Dileo, C., Tommasi, I. & Amodio, E. The first synthesis of a cyclic carbonate from a ketal in SC-CO2. J. Supercrit. Fluids 25, 177–182 (2003).

    CAS  Article  Google Scholar 

  13. 13.

    Huang, S.-y. et al. Synthesis of cyclic carbonate from carbon dioxide and diols over metal acetates. Journal of Fuel Chemistry and Technology 35, 701–705 (2007).

    CAS  Article  Google Scholar 

  14. 14.

    Wang, H. et al. Synthesis of cyclic carbonates from CO2 and diols via electrogenerated cyanomethyl anion. Greenhouse Gas Sci Technol 2, 59–65 (2012).

    ADS  CAS  Article  Google Scholar 

  15. 15.

    Lim, Y. N., Lee, C. & Jang, H.-Y. Metal-Free Synthesis of Cyclic and Acyclic Carbonates from CO2 and Alcohols. Eur. J. Org. Chem. 2014, 1823–1826 (2014).

    CAS  Article  Google Scholar 

  16. 16.

    Pyo, S.-H. et al. Cyclic carbonates as monomers for phosgene- and isocyanate-free polyurethanes and polycarbonates. Pure Appl. Chem. 84, 637–661 (2011).

    MathSciNet  Article  Google Scholar 

  17. 17.

    Shaikh, A.-A. G. & Sivaram, S. Organic Carbonates. Chem. Rev. 96, 951–976 (1996).

    CAS  Article  Google Scholar 

  18. 18.

    Takagaki, A., Iwatani, K., Nishimura, S. & Ebitani, K. Synthesis of glycerol carbonate from glycerol and dialkyl carbonates using hydrotalcite as a reusable heterogeneous base catalyst. Green Chem. 12, 578–581 (2010).

    CAS  Article  Google Scholar 

  19. 19.

    Bhanage, B. M., Fujita, S.-i., Ikushima, Y. & Arai, M. Transesterification of urea and ethylene glycol to ethylene carbonate as an important step for urea based dimethyl carbonate synthesis. Green Chem. 5, 429–432 (2003).

    CAS  Article  Google Scholar 

  20. 20.

    Gabriele, B. et al. A novel and efficient method for the catalytic direct oxidative carbonylation of 1,2- and 1,3-diols to 5-membered and 6-membered cyclic carbonates. Tetrahedron Lett. 50, 7330–7332 (2009).

    CAS  Article  Google Scholar 

  21. 21.

    Pearson, D. M., Conley, N. R. & Waymouth, R. M. Palladium-Catalyzed Carbonylation of Diols to Cyclic Carbonates. Adv. Synth. Catal. 353, 3007–3013 (2011).

    CAS  Article  Google Scholar 

  22. 22.

    Chen, F., Dong, T., Xu, T., Li, X. & Hu, C. Direct synthesis of cyclic carbonates from olefins and CO2 catalyzed by a MoO2(acac)2-quaternary ammonium salt system. Green Chem. 13, 2518–2524 (2011).

    CAS  Article  Google Scholar 

  23. 23.

    Sun, J. et al. Direct Synthetic Processes for Cyclic Carbonates from Olefins and CO2. Catal Surv Asia 15, 49–54 (2011).

    CAS  Article  Google Scholar 

  24. 24.

    Della Ca’, N. et al. Effective Guanidine-Catalyzed Synthesis of Carbonate and Carbamate Derivatives from Propargyl Alcohols in Supercritical Carbon Dioxide. Adv. Synth. Catal. 353, 133–146 (2011).

    Article  Google Scholar 

  25. 25.

    Bruneau, C. & Dixneuf, P. H. Catalytic incorporation of CO2 into organic substrates: Synthesis of unsaturated carbamates, carbonates and ureas. J Mol Catal 74, 97–107 (1992).

    CAS  Article  Google Scholar 

  26. 26.

    Pews, R. G. Synthesis of cyclic carbonates by a novel carbonate rearrangement. J. Chem. Soc., Chem. Commun. 0, 119a (1974).

    Article  Google Scholar 

  27. 27.

    Carothers, W. H. & van Natta, F. J. Studies on polymerization and ring formation. Iii. Glycol esters of carbonic acid. J. Am. Chem. Soc. 52, 314–326 (1930).

    CAS  Article  Google Scholar 

  28. 28.

    Hill, J. W. & Carothers, W. H. Studies of Polymerization and Ring Formation. XX. Many-Membered Cyclic Esters. J. Am. Chem. Soc. 55, 5031–5039 (1933).

    CAS  Article  Google Scholar 

  29. 29.

    Spanagel, E. W. & Carothers, W. H. Macrocyclic Esters 1. J. Am. Chem. Soc. 57, 929–934 (1935).

    CAS  Article  Google Scholar 

  30. 30.

    Kathalewar, M. S., Joshi, P. B., Sabnis, A. S. & Malshe, V. C. Non-isocyanate polyurethanes: from chemistry to applications. RSC Adv. 3, 4110–4129 (2013).

    CAS  Article  Google Scholar 

  31. 31.

    Honda, M. et al. Direct Cyclic Carbonate Synthesis from CO2 and Diol over Carboxylation/Hydration Cascade Catalyst of CeO2 with 2-Cyanopyridine. ACS Catal. 4, 1893–1896 (2014).

    CAS  Article  Google Scholar 

  32. 32.

    Whelan, J. Union Carbide Corporation. US2935494 (A) (1960).

  33. 33.

    Schiweck, H. et al. Sugar Alcohols. In Ullmann’s Encyclopedia of Industrial Chemistry (Wiley-VCH), p. 163 (2000).

  34. 34.

    Roth, M. et al. Highly Water-Soluble Alpha-Hydroxyalkylphenone Based Photoinitiator for Low-Migration Applications. Macromol. Chem. Phys. 218, 1700022 (2017).

    Article  Google Scholar 

  35. 35.

    Schmidt, S. et al. Erythritol Dicarbonate as Intermediate for Solvent- and Isocyanate-Free Tailoring of Bio-Based Polyhydroxyurethane Thermoplastics and Thermoplastic Elastomers. Macromolecules 50, 2296–2303 (2017).

    ADS  CAS  Article  Google Scholar 

  36. 36.

    Tomczyk, M., Guńka, K. A., Parzuchowski, P. G., Janusz Zachara, P. & Rokicki, G. Intramolecular etherification of five-membered cyclic carbonates bearing hydroxyalkyl groups. Green Chem. 14, 1749–1758 (2012).

    CAS  Article  Google Scholar 

  37. 37.

    Schmidt, S., Göppert, N. E., Bruchmann, B. & Mülhaupt, R. Liquid sorbitol ether carbonate as intermediate for rigid and segmented non-isocyanate polyhydroxyurethane thermosets. Eur. Polym. J. 94, 136–142 (2017).

    CAS  Article  Google Scholar 

  38. 38.

    Buysch, H.-J. Carbonic Esters. In Ullmann’s Encyclopedia of Industrial Chemistry (Wiley-VCH), p. 111 (2000).

  39. 39.

    Weber, M., Weber, M. & Kleine‐Boymann, M. Phenol. In Ullmann’s Encyclopedia of Industrial Chemistry (Wiley-VCH), p. 505 (2000).

  40. 40.

    Ott, J. et al. Methanol. In Ullmann’s Encyclopedia of Industrial Chemistry (Wiley-VCH), p. 197 (2000).

  41. 41.

    Pratt, R. C., Lohmeijer, B. G. G., Long, D. A., Waymouth, R. M. & Hedrick, J. L. Triazabicyclodecene: a simple bifunctional organocatalyst for acyl transfer and ring-opening polymerization of cyclic esters. J. Am. Chem. Soc. 128, 4556–4557 (2006).

    CAS  Article  Google Scholar 

  42. 42.

    Alder, C. M. et al. Updating and further expanding GSK’s solvent sustainability guide. Green Chem. 18, 3879–3890 (2016).

    CAS  Article  Google Scholar 

  43. 43.

    Furtwengler, P. & Avérous, L. From D-sorbitol to five-membered bis(cyclo-carbonate) as a platform molecule for the synthesis of different original biobased chemicals and polymers. Scientific Reports 8, 9134 (2018).

Download references


The authors would like to thank Rieke Schulte and Rebecca Seim for skillful technical assistance.

Author information




M.M. designed the project and reviewed the manuscript. P.D. performed the synthetic and analytical work and wrote the manuscript.

Corresponding author

Correspondence to Michael A. R. Meier.

Ethics declarations

Competing Interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Dannecker, PK., Meier, M.A.R. Facile and Sustainable Synthesis of Erythritol bis(carbonate), a Valuable Monomer for Non-Isocyanate Polyurethanes (NIPUs). Sci Rep 9, 9858 (2019). https://doi.org/10.1038/s41598-019-46314-5

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing