Abstract
In this paper, the composition, structure, morphology and kinetics of evolution during isothermal oxidation of Fe48Cr15Mo14Y2C15B6 metallic glass powder in the supercooled region are investigated by an integrated ex-situ and in-situ characterization and modelling approach. Raman and X-ray diffraction spectra established that oxidation yielded a hierarchical structure across decreasing length scales. At larger scale, Fe2O3 grows as a uniform shell over the powder core. This shell, at smaller scale, consists of multiple grains. Ultra-small angle X-ray scattering intensity acquired during isothermal oxidation of the powder over a wide Q-range delineated direct quantification of oxidation behavior. The hierarchical structure was employed to construct a scattering model that was fitted to the measured intensity distributions to estimate the thickness of the oxide shell. The relative gain in mass during oxidation, computed theoretically from this model, relatively underestimated that measured in practice by a thermogravimetric analyzer due to the distribution in sizes of the particles. Overall, this paper presents the first direct quantification of oxidation in metallic glass powder by ultra-small angle X-ray scattering. It establishes novel experimental environments that can potentially unfold new paradigms of research into a wide spectrum of interfacial reactions in powder materials at elevated temperatures.
Similar content being viewed by others
Introduction
Progress of human civilization has been inextricably associated with the discovery of novel materials that exhibit exceptional properties. One of the recent examples of such a class of materials is metallic glasses1,2,3. These are solid metallic alloys that exhibit an atomic structure that is fundamentally different from polycrystalline materials4,5. Metallic glasses possess a homogeneous disordered atomic structure that is devoid of conventional crystalline defects such as dislocations and grain boundaries6,7. As a result of this defect-free, disordered atomic structure, metallic glasses manifest mechanical8,9, tribological10,11 and magnetic properties12,13 that are superior to those of their polycrystalline counterparts. Among them, iron-based metallic glasses are particularly attractive14,15, being comparatively inexpensive in materials costs as compared to palladium and zirconium-based ones. For example, Fe48Cr15Mo14Y2C15B6 metallic glass exhibits exceptionally high elastic modulus of 200 GPa and compressive fracture strength of 3200 MPa. The hardness of this metallic glass is also high (13 GPa)16,17,18,19. Metallic glasses in the Fe-Si-B alloy system also possess excellent soft magnetic properties such as high permeability and low core loss. The saturation induction and maximum dc permeability of MetglasR 2605SA1 are 1.56T and 600 kNA−2 respectively20,21,22. These outstanding properties of metallic glasses harbor the potential to be utilized in a wide spectrum of applications spanning hard dies and tools, wear resistant cutting materials and transformer cores thereby ushering rapid technological and industrial advancement.
In order that an extensive commercial utilization of metallic glasses be viable, it is critical to evaluate these materials for their environmental stability at elevated temperatures23. It is imperative that metallic glasses exhibit adequate resistance against detrimental oxygen environments to be able to execute satisfactory performance24. For example, it is necessary to anneal metallic glass ribbons under a magnetic field to reduce stress and attain the requisite domain structure25. In most industrial manufacturing processes an ideal vacuum annealing environment is seldom achievable26. The result is an occurrence of oxidation on the surface of metallic glasses that introduces magnetic anisotropy and pinning centers that severely deteriorates soft magnetic properties26. This phenomenon of oxidation in metallic glasses is fundamentally different than that in polycrystalline materials and is expected to be more uniform due to the absence of grain boundaries23. Additionally, it has been observed that the composition of oxide films naturally formed in air on metallic glasses exerts strong influence on their passivity and corrosion behavior27,28. From a different perspective, thermally induced oxidation is a major chemical approach to synthesize oxide thin films for applications such as sensors, catalysts, insulators and bioimplants29. Oxidation of metallic glasses have also been reported to yield a ten times improvement in the wear resistance of these materials30,31,32. This could be utilized by metallic glass alloys and coatings fabricated by a number of processing techniques such as laser cladding and spark plasma sintering33,34,35. Thus, the successful manufacturing and applications of metallic glasses mandates a fundamental understanding of their behavior in oxygen-containing atmospheres during thermally activated processes.
The utilization of metallic glass alloy systems during manufacturing as well as applications is most extensive in the temperature regime of the supercooled liquid region (SLR) or, in other words, between the glass transition temperature Tg and the onset crystallization temperature Tx36. This temperature regime enables harnessing the drastic decrease in viscosity of metallic glasses37. Indeed these materials have been observed to exhibit viscosities varying from 1 × 1012 Pas at Tg to 1 × 105 Pas at Tx38. Superplastic forming of metallic glasses can thus be achieved to fabricate complex near net components39. Additionally, this temperature regime, which is an evidence of the remarkable stability of the metallic glass against crystallization, restricts devitrification and permits preservation of the amorphous structure of the material and hence its superior properties discussed earlier40. Thus investigation of the response of metallic glasses to oxidation in the supercooled liquid region without devitrification of its structure is of paramount importance.
An accurate investigation of the oxidation behavior of metallic glasses in the supercooled liquid region warrants the selection of materials and employment of characterization techniques that enable precise and reliable identification of chemistry and quantification of the volume of oxide species evolved. It is established that oxidation is a slow, diffusion based phenomenon that occurs on the surface of materials. Reported examinations of oxidation are mostly limited to bulk and ribbon forms of metallic glasses41,42,43. The relatively lower specific surface area of these materials result in the evolution of a minute volumes of oxides44. Consequently, reliable quantification of oxidation is significantly impeded. It is thus commonplace to observe that such quantification is generally performed by indirect means such as estimation of weight45. This impediment is especially severe during the initial stages of oxidation, which, in fact, provide deeper insight into the reaction and hence arouses further intrigue. Conventional characterization techniques too induce drawbacks in analyzing the oxidation behavior of these materials. Scanning electron microscopy (SEM), for example, can resolve the morphology of films evolved only over a prolonged duration of oxidation44. Laboratory scale desktop X-ray diffraction (XRD) instruments while capable of determining the structure of oxides, the intensity of scattering is not representative of the minute volume of oxides formed23.
Circumvention of these problems validates both the utilization of metallic glass in powder form that exhibits higher specific surface area as well as characterization techniques that can directly enumerate the evolution of oxides, particularly at the initial stages. In this regard, synchrotron-based in-situ X-ray scattering techniques are particularly attractive46,47. For example, ultra-small angle X-ray scattering (USAXS) is a powerful technique that enables the acquisition of a high intensity of scattering48,49 even from a minute volume of structural features in metallic glasses50. Recent development of experimental environments have equipped the scientific community to acquire USAXS intensities in-situ during thermally-activated phenomena51. The USAXS intensity, I(Q) can be acquired over a broad range of the scattering vector, Q52. The dimensions of the scattering features are directly correlated to the scattering vector as 2π/Q53. Thus the distribution of USAXS intensity, I(Q) over the scattering vector, Q enables analysis of hierarchical structural features across a wide span of length scales from hundreds of micrometres to a few nanometres. The nature of the USAXS intensity distribution as a function of the scattering vector is also characteristic of the morphology of the scattering features due to the unique form factor each generates. For example, each of spheres, disks and cylinders of the same material will generate characteristic form factors and hence intensity distributions that can be utilized to distinguish between features of different morphologies54. The measured intensity distributions can be further fitted by small angle scattering analysis software tools based upon physical models that replicate the evolution of reactions55,56. This in turn can be utilized to yield quantitative information on the evolution of the scattering features. In summary, while ex-situ characterization techniques are suitable for the identification of chemistry and structure of oxides, in-situ techniques can enable quantification of time dependent evolution. These strongly complement each other and, utilized in conjunction, provide an excellent procedure of accurately establishing the oxidation behavior of metallic glass powder throughout the initial stages towards conclusion.
The present paper aims to establish a fundamental understanding of the oxidation behavior of metallic glass powder by investigating the composition, structure, morphology and isothermal evolution by an integrated approach employing complementary ex-situ and in-situ characterization techniques. The chemistry of the oxide species and their morphology are presented followed by an analysis of their microstructure. These are employed to construct a physical model to interpret the distribution in intensity of ultra-small angle X-rays scattered in-situ during isothermal evolution. The theoretical computation from this distribution is compared with thermogravimetric measurement to establish the isothermal oxidation behavior of the metallic glass powder. This paper, to the best of the authors’ knowledge, presents the first report of oxidation kinetics of metallic glass powder by ultra-small angle X-rays scattering, complemented by Raman spectroscopy and X-ray diffraction techniques. En route, novel experimental environments and analytical methods are established. In principle, these harbor the potential to be utilized for investigating the mechanism and kinetics of a wide spectrum of slow, surface controlled reactions beyond oxidation, in powder materials not limited to metallic glasses. Indeed, the presented framework manifests the prospect to unfold new paradigms of surface research on heterogeneous catalysis, adsorption, adhesion and so forth at ambient and elevated temperatures based upon combined ex-situ and in-operando characterization capabilities.
Results and Discussion
Powder morphology and structure
The morphology of the pristine Fe48Cr15Mo14Y2C15B6 metallic glass powder consists of particles of various shapes with the majority of them being spherical. The sizes of the particles measured from several SEM micrographs (see Supplementary Fig. S1) showed that more than 90% of the particles exhibit a diameter ranging from 20 μm to 60 μm with the mean diameter, D being 40 μm57.
This paper is aimed at investigating the oxidation behavior of this metallic glass powder within the supercooled liquid region of the material, without the occurrence of crystallization. Thus, in order to determine the temperatures of isothermal time dependent oxidation experiments, the thermal behavior of the material was examined first. The isochronal DSC trace of the metallic glass powder, measured at a heating rate of 50 °C min−1 (see Supplementary Fig. S2a) exhibited a glass transition temperature Tg of about 570 °C and a crystallization onset temperature Tx of about 660 °C. Based on this thermogram, the temperatures of isothermal oxidation were determined to be 580 °C and 650 °C, completely within the glass transition and onset crystallization temperatures. Two more isochronal annealing experiments were conducted at the same heating rate, with the powder being heated up to 580 °C and 650 °C. The XRD spectra acquired from the powder in both pristine and annealed conditions (see Supplementary Fig. S2b) exhibited absence of crystallization as confirmed by the diffused peak in each spectra, characteristic of fully amorphous materials.
Oxide chemistry
The iron-rich section of the iron-oxygen phase diagram58 (see Supplementary Fig. S3) shows that at the temperatures of isothermal oxidation experiments employed in this investigation, 580 °C and 650 °C, the oxides that are thermodynamically stable are FeO, Fe2O3 and Fe3O4. It is thus expected that the oxidation of this metallic glass powder would yield oxides among the aforementioned ones. The surface of the pristine and oxidized metallic glass powder particles was examined by Raman spectroscopy. Spectra were acquired from multiple spots on individual particles among which, one, representative of the entire powder, is presented for each sample in Fig. 1. No Raman features are observed in the spectrum acquired from the pristine powder. This confirms that the surface of the pristine metallic glass powder is clean, devoid of any detectable oxides or other compounds on the metal surface. The spectra acquired from the surface of the powder oxidized at 580 °C and 650 °C for 120 min, each exhibit peaks that have been identified by their frequencies. The peaks at 226, 241, 295, 409, 501, 613 and 1317 cm−1 all correspond to Fe2O3 oxide59,60. Only the peak at 663 cm−1 is assigned to Fe3O4 oxide61. A low intensity peak at 804 cm−1 is observed only for the sample oxidized at 650 °C for 120 min which is attributed to the formation of B2O3. This observation agrees with the literature that boron is oxidized at a temperature higher than 600 °C62. B2O3 has also been observed upon oxidation of Fe-based metallic glasses containing boron43,44,63,64. Thus it can be concluded that the oxide phases grow as a shell over the entire surface of the metallic glass powder particles. This is reasonable as the powder possesses a homogeneous amorphous structure and all sites on the surface are equally preferred for the growth of oxides. Additionally, according to the Raman spectra (Fig. 1), the major constituent of the oxide shell is Fe2O3.
Raman spectra acquired from the surface of the metallic glass powder isothermally oxidized for systematically increasing duration of time at 580 °C for 120; 240; 360; 480; 600 and 720 min and at 650 °C for 60; 120; 180; 240 and 300 min are presented in Fig. 2. The oxides are consistently observed to grow during the entire duration of isothermal oxidation at both temperatures. No noticeable peak shift is detected which suggests the uniformity of oxide growth with time, over the entire surface of the metallic glass powder particles.
With increasing time of isothermal oxidation, the volume of oxide shell growing on the surface of the powder is expected to increase, thereby resulting in an increase in intensity of the characteristic peaks in the Raman spectra. However, as presented in Fig. 2, the trend in intensity of the peaks are observed to be irregular at both temperatures. This irregularity in intensity of the peaks can possibly be an outcome of optical interference caused by multiple reflections of the incident laser in the oxide shell. The constructive or destructive interference, based on the thickness of the oxide shell regulates the intensity of the Raman-scattered radiation emitted to the far field. Indeed, oscillation of the intensities of the peaks in the Raman spectrum with thickness of oxide has been reported previously65,66. Variation in the particle color was also observed, that is suggestive of the same.
Heating of sample due to interaction with laser is frequently encountered in Raman spectroscopy67. It may result in artifacts, such as oxidation of sample and temperature-induced peak shifts. In the present investigation, the absence of Raman peaks in the spectrum acquired from the surface of the pristine metallic glass powder particles suggests that no oxides are formed during excitation where the laser power is optimized to 3 mW for highest signal counts without artifacts. On the other hand, oxidation of the powder was clearly observed when the laser power was increased to 4 mW (not shown here). Hence the presence of laser heating during the acquisition of Raman spectra was anticipated, although it was not high enough to drive oxidation. To this end, the laser-induced rise in temperature of the sample was estimated from the anti-Stokes-to-Stokes intensity ratio, IaS/IS, which is approximately the Boltzmann factor68,69. Figure 3 presents the Raman spectrum acquired from the surface of the powder oxidized at 580 °C for 720 min with an incident laser power of 3 mW. The most intense anti-Stokes peak, being at −409 cm−1, was used for calculation of temperature. IaS/IS is found to be 0.342 after background subtraction (inset, Fig. 3). Hence, the temperature is estimated to be 278 °C, which is too low to induce oxidation. Similarly, the temperature is estimated to be 152 °C for an incident laser power of 1 mW where the corresponding Raman mode was observed at 410.5 cm−1. Accordingly, by linear extrapolation, the peak is estimated to be at 412 cm−1 at room temperature. Therefore, the acquisitions of Raman spectra in this investigation were not subject to significant spectral shifts due to laser heating and the assignments of the peaks are thus accurate.
Oxide structure
In order to further analyze the oxidation behavior of the metallic glass powder particles, the structure of the oxides was investigated by X-ray diffraction. The XRD spectra acquired from the metallic glass powder isothermally oxidized at 580 °C for 720 min and at 650 °C for 300 min are presented in Fig. 4. In addition to the diffused peak as in the pristine powder, these spectra exhibit sharper peaks, superimposed on the amorphous background. These peaks are identified to be Fe2O3 and Fe3O4 oxides. No peaks corresponding to B2O3 were observed in the XRD spectra owing to the minor amount formed as exhibited by the Raman spectra. The XRD spectra thus confirm the results obtained from Raman spectroscopy. During isothermal oxidation at the lower temperature of 580 °C for shorter duration of time up to 240 min the volume of the oxide shell is possibly too low to be detectable in the XRD spectra. This is also observed during isothermal oxidation at 650 °C for the shortest duration of time of 60 min. With an increase in duration of time of isothermal oxidation at both temperatures, the intensity of the characteristic peaks gradually increase, that suggests an increase in the volume of the oxide shell growing on the surface of the powder.
Hence from the Raman and XRD spectra it can be concluded that the growth of oxides on the surface of the metallic glass powder has a hierarchical structure. First, the growth occurs as a shell over the entire surface of the powder. Second, this oxide shell is polycrystalline, or in other words, constitutes of multiple oxide grains. However, both Raman and XRD spectra are incapable of providing quantitative information on the trend in volume of oxides formed as a function of time during isothermal oxidation.
USAXS interpretation of hierarchical oxide structure
In order to enumerate the isothermal evolution of oxide in this metallic glass powder, in-situ ultra-small angle X-ray scattering (USAXS) was employed. The number of particles subjected to exposure in the beam is of the order of thousand and hence is representative of the entire sample of powder. This powder consists of non-interacting, mostly spherical particles with an average diameter, D of about 40 μm which yields D−1 of 0.0000025 Å−1. The USAXS intensity, I(Q) acquired from this pristine metallic glass powder at ambient temperature over a scattering vector, Q-range of 0.0005 Å−1 to 0.2 Å−1 (see Supplementary Fig. S4), in accord with the expected Q-dependence for a dilute solution of identical uniform spheres at Q ≫ D−1, can be observed to decay following a power-law as Q−4 70. This confirms that the powder consists of particles with a smooth surface devoid of any structural features as shown by the Raman and XRD spectra. Over the Q-range above 0.1 Å−1, a constant, low-intensity background arising from the detector and environment is observed, which is independent of Q and not related to the morphology and structure of the powder particles and the oxides formed on their surface.
The evolution of oxides during in-situ isothermal time dependent experiments is manifested by the USAXS intensity distributions acquired at 580 °C for 720 min and 650 °C for 300 min as presented in Fig. 5. These intensities are calibrated on relative scale as the motivation of the present investigation is to enumerate the average volume of oxide shell formed on the particles71. Based on the intensity, I(Q) measured as a function of the scattering vector, Q, the characteristics of scattering, corresponding interpretation as representative of the hierarchical structure of the oxide over decreasing length scales and their evolution with increase in time during isothermal oxidation are discussed across four discrete Q-ranges as follows.
First, over the Q-range from 0.0005 Å−1 to 0.002 Å−1, scattering results from the oxidized particles. The average diameter of the particles, 40 μm is at a length scale larger than that resolved in the present USAXS measurements. It is clearly observed that with increase in time of in-situ isothermal experiments, the size of the particles themselves do not change appreciably, as evidenced by the intensity distributions at both temperatures. As a result, I(Q) continues to decay following the power-law as Q−4, identical to that presented for the particles at room temperature (see Supplementary Fig. S4).
Second, over the Q-range from 0.002 Å−1 to 0.02 Å−1, scattering results from the Fe2O3 oxide that grows as a uniform shell over the entire surface of the metallic glass powder particles. The length scale of the oxide shell can be estimated from this Q-range to be approximately between few tens to few hundreds of nanometres. As a result, the oxidized metallic glass powder exhibits a core-shell structure with the powder particle behaving as the core and the oxide behaving as the shell. A form factor is produced due to the difference in X-ray scattering contrasts of the core and the shell. In such a form factor the characteristic Fourier-Bessel oscillations72, as observed in the intensity distributions, convey quantitative information on the thickness of the oxide shell. During in-situ isothermal oxidation at both temperatures, with increase in time these oscillations shift towards lower Q, suggesting a corresponding increase in thickness of the oxide shell.
Third, over the Q-range from 0.02 Å−1 to 0.1 Å−1, scattering occurs due to the multiple grains in the polycrystalline oxide shell. The length scale of the oxide grains can be computed from this Q-range to be approximately between few to few tens of nanometres. The intensity distributions in this Q-range exhibit the well-recognized Guinier ‘knee’ that is characteristic of the radius of gyration of the grains73 followed by the Porod power-law slope. With increase in time during isothermal oxidation, small nuclei of oxides are formed while pre-existing grains grow into larger ones. Thus the evolution of sizes of the grains has an irregular trend and consequently the variation in intensity distribution is less conspicuous.
Finally, over the Q-range from 0.1 Å−1 to 0.2 Å−1, a constant background scattering is manifested. This originates from the instrument and environment, without any dependence on Q. This is confirmed by the fact that the measured intensities are significantly lower at this Q-range and does not evolve with time of isothermal oxidation at both temperatures.
In summary, the evolution of the hierarchical structure of the metallic glass powder with time during isothermal oxidation at both 580 °C and 650 °C across decreasing length scales is based on a powder core over which an oxide grows as a uniform shell which further consists of multiple grains. This hierarchical structure is utilized to construct a physical model under the aegis of which the fitting of parameters enables the quantitative analysis of oxidation in this material as described in the following section.
USAXS quantitative modelling
The physical model representing the hierarchical structure is depicted by a schematic in Fig. 6. At large length scale (small Q), scattering is representative of the ensemble of a large number of non-interacting oxidized particles (Fig. 6a). With further decrease in length scale (medium Q) individual oxidized particles with distinct powder core and oxide shell can be distinguished (Fig. 6b). A section is made to clarify the internal structure. At small length scale (large Q), the scatterers are the multiple grains in the oxide shell (Fig. 6c).
In order to achieve consistency with the physical characteristics three components are utilized to construct the scattering model. In the first component, the mean diameter was fixed at 40 μm. The standard deviation was obtained from fitting the scattering intensity acquired from the pristine powder at room temperature. This was kept constant thereafter. The X-ray scattering length densities of the Fe48Cr15Mo14Y2C15B6 core and Fe2O3 shell were computed to be 60.24 × 1010 cm−2 and 42.32 × 1010 cm−2 respectively while that of air as solvent was kept zero. It is to be noted here that while the major constituent of the oxide shell is Fe2O3, both Raman and XRD spectra detected the presence of Fe3O4 as well. However, the X-ray scattering length density of Fe3O4, 41.68 × 1010 cm−2, is almost equal to that of Fe2O3. Hence, in relevance to USAXS, these oxides are similar and thus the thickness estimated from the intensity distributions are also accurate. In the second component, the Porod power-law slope was fixed at −4 and the radius of gyration was fitted. The third component accounted for the background which was set to a constant value at the beginning of the fitting routine. Figure 7 presents the result of a representative fitting routine performed on the USAXS intensity acquired from the metallic glass powder oxidized at 650 °C for 300 min. The model can be observed to be in good agreement with the measured USAXS intensity. The small misfit results from the fact that the present model is utilized to estimate a single value of the thickness of the oxide shell growing over all the particles. In practice, however, in a distribution of diameters of the powder cores with a mean and standard deviation, the thickness of the oxide shell is not constant and is dependent on the diameter of the individual particles. Thus, although the model underestimates the thickness of the oxide shell and hence the USAXS intensity near the Q-range of the misfit, the overall concurrence yields a good estimate of the oxide shell thickness. This fitting routine is employed to all the USAXS intensity distributions measured during isothermal oxidation at 580 °C for 720 min and 650 °C for 300 min to estimate the evolution of thickness of oxide shell (see Supplementary Fig. S5) and validate the mass gain by thermogravimetric analysis as described in the following section.
Quantitative validation of oxide evolution
In order to examine the accuracy of the quantitative analysis by USAXS, the gain in mass of the powder due to isothermal oxidation, per unit mass of powder was theoretically estimated. Three assumptions were made for this theoretical computation. First, all the particles of this metallic glass powder can be represented by solid spheres of identical diameter equal to 40 μm. Second, oxidation of the particles result in the formation of only one oxide, Fe2O3. Third, the thickness of oxide formed on each particle is equal. Based on these assumptions, the initial mass of a single powder particle was calculated from its diameter and density (7500 kg m−3)17. The mass of oxide was calculated from its thickness and density (5240 kg m−3). The percentage gain in mass was estimated by dividing the mass of oxide formed on a single particle by the mass of that particle. The results from this theoretical estimation was compared with the gain in mass measured in-situ during isothermal oxidation by a thermogravimetric analyzer. This is presented in Fig. 8 for the temperatures 580 °C and 650 °C. It is observed that the theoretically estimated gain in mass continuously underestimates that actually measured in practice. This can be explained on the basis of the assumptions and the mechanism of oxidation. The isothermal oxidation investigated here is controlled by diffusion at the surface with the rate being dependent on the surface area of the powder particles. For a given volume, the surface area is least for a sphere. This theoretical calculation performed assuming all particles hence estimates a lower gain in mass. In practice, non-spherical particles oxidize to yield a higher gain in mass that is measured by the thermogravimetric analyzer as observed in Fig. 8.
Conclusions
Oxidation of Fe48Cr15Mo14Y2C15B6 metallic glass powder at 580 °C upto 720 min and 650 °C upto 300 min results primarily in the formation of polycrystalline Fe2O3. This oxide grows over the entire surface of the powder particles as a uniform shell which further constitutes of multiple grains. The ultra-small angle X-ray scattering intensity acquired in-situ during isothermal oxidation and modelled based on this hierarchical structure of the oxide, enumerated the increase in thickness of the oxide with time, rapid initially which gradually decreased. The relative gain in mass due to oxidation computed theoretically from this model, relatively underestimates that measured in practice owing to the distribution in size of the pristine particles. Overall, the results presented here establish the chemical identification, structural analysis and quantitative computation of isothermal oxidation in metallic glass powder. In the broad perspective, this manifests the potential to unfold new paradigms of research on interfacial reactions in powder materials at elevated temperatures and develop predictive analytical capabilities built on complementary ex-situ and in-operando scattering techniques.
Methods
Metallic glass powder
The composition of the atomized metallic glass powder used in this investigation was Fe48Cr15Mo14Y2C15B6 (at.%). The morphology of the pristine powder particles was observed in a scanning electron microscope (FEI, Quanta 600). Size of individual particles was measured from the secondary electron micrographs using a public domain image processing software, ImageJ (available from the National Institute of Health, USA).
Differential scanning calorimetry
Thermal behavior of the pristine metallic glass powder was evaluated using a simultaneous thermal analyzer (TA Instruments, SDT Q600) under dry high purity argon gas atmosphere at a flow rate of 50 ml min−1. About 100 mg of the powder was heated in an alumina crucible, continuously from ambient temperature to 900 °C, at a constant heating rate of 50 °C min−1.
Isothermal oxidation
Ex-situ isothermal oxidation of the metallic glass powder was carried out in a muffle furnace (Thermo Fisher Scientific, FB1315M) in freely flowing dry air at atmospheric pressure at 580 °C and 650 °C. For each experiment, the furnace was first preheated to the desired temperature. After the temperature stabilized, about 3 g of the powder was placed in an alumina crucible and introduced inside the furnace. Isothermal time dependent experiments were conducted at the lower temperature, 580 °C for 120; 240; 360; 480; 600 and 720 min and at the higher temperature, 650 °C for 60; 120; 180; 240 and 300 min respectively. Temperature was controlled within ±0.3 °C during all the experiments.
Single-particle Raman spectroscopy
Chemical identification of the oxides was conducted by Raman spectroscopy. Spectra were acquired by a micro-Raman spectrometer (WITec, alpha300 R) equipped with a grating of 600 lines mm−1. A laser wavelength of 532 nm was utilized to excite the spectra with an incident laser power of 3 mW. The laser spot size on the samples was 10 μm in diameter. The signal was accumulated for 200 s by employing a 20X objective lens.
X-ray diffraction
Structural analysis of the pristine and oxidized metallic glass powder was performed using an X-ray diffractometer (PANalytical, PW 1830) operated with Cu-Kα radiation (λ = 1.5418 Å). At least three measurements were performed for each sample of oxidized powder to ensure reliability of the results and a representative spectra was plotted.
In-situ ultra-small angle X-ray scattering
In-situ ultra-small angle X-ray scattering experiments were performed during isothermal oxidation of the metallic glass powder. For each experiment, a sample ‘sandwich’ was prepared using mica sheets and the metallic glass powder as described here. First, a circular sheet of mica with thickness 25 μm and diameter 6 mm was laid out horizontally. Another annular sheet of mica of the same thickness with external diameter of 6 mm and internal aperture of 3 mm was placed on top of and concentric to the first sheet. A thin layer of the metallic glass powder was spread uniformly within the internal aperture of the annular mica sheet. Thus, the annular sheet behaved as a ‘washer’, thereby securing the powder sample in place. A third sheet of mica, identical to the first one, was placed on top, covering the powder and the annular sheet. A thin sample with the metallic glass powder sandwiched between mica sheets was thus assembled. In this configuration air flowed freely at atmospheric pressure. This assembly was introduced within the sample cell of a temperature controlled stage (Linkam Scientific, TS1500) with a temperature stability of 1 °C. The temperature of the sample cell in the stage was increased from ambient to the desired values of 580 °C and 650 °C at a heating rate of 50 °C min−1. Isothermal time dependent experiments were conducted at the lower temperature, 580 °C for 720 min and at the higher temperature, 650 °C for 300 min.
X-ray scattering intensities were measured as a function of the scattering vector in the range of 0.0005 to 0.2 Å−1, in-situ during isothermal oxidation, by the Ultra-Small Angle X-ray Scattering instrument at beamline 9-ID of the Advanced Photon Source, Argonne National Laboratory48,49,74. The instrument was operated with an X-ray wavelength of 0.59 Å that corresponds to an X-ray energy of 21 keV, beam size of 0.8 × 0.8 mm and X-ray photon flux of approximately 1013 mm−2 s−1. The exposure time for each measurement was 1 min and the duration between two consecutive measurements was approximately 3 min. Background scattering from the environment, instrument and temperature controlled stage was subtracted from the measured intensities by the USAXS data reduction package, INDRA. The small angle scattering data analysis tool suite IRENA was utilized for modeling the reduced scattering intensities. X-ray scattering length densities and the corresponding X-ray scattering contrasts of the materials were calculated based on their compositions by the scattering contrast calculator support tool, also available in IRENA56.
Thermogravimetric analysis
The gain in mass was measured in-situ during isothermal oxidation of the metallic glass powder at 580 °C and 650 °C by a simultaneous thermal analyzer (TA Instruments, SDT Q600). About 100 mg of the powder was placed in an alumina crucible and the temperature of the sample was increased from ambient to the desired values of 580 °C and 650 °C at a heating rate of 50 °C min−1. The gain in mass was measured continuously during isothermal time dependent experiments at the lower temperature, 580 °C for 720 min and at the higher temperature, 650 °C for 300 min.
Data Availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
References
Telford, M. The case for bulk metallic glass. Mater. Today 7, 36–43 (2004).
Greer, A. L. Metallic glasses… on the threshold. Mater. Today 12, 14–22 (2009).
Axinte, E. Metallic glasses from “alchemy” to pure science: Present and future of design, processing and applications of glassy metals. Mater. & Des. 35, 518–556 (2012).
Gleiter, H. Our thoughts are ours, their ends none of our own: are there ways to synthesize materials beyond the limitations of today? Acta Materialia 56, 5875–5893 (2008).
Paul, T., Loganathan, A., Agarwal, A. & Harimkar, S. P. Kinetics of isochronal crystallization in a fe-based amorphous alloy. J. Alloy. Compd. 753, 679–687 (2018).
Cheng, Y. & Ma, E. Atomic-level structure and structure–property relationship in metallic glasses. Prog. Mater. Sci. 56, 379–473 (2011).
Sun, B. & Wang, W. The fracture of bulk metallic glasses. Prog. Mater. Sci. 74, 211–307 (2015).
Yavari, A. R., Lewandowski, J. & Eckert, J. Mechanical properties of bulk metallic glasses. MRS Bull. 32, 635–638 (2007).
Trexler, M. M. & Thadhani, N. N. Mechanical properties of bulk metallic glasses. Prog. Mater. Sci. 55, 759–839 (2010).
Gloriant, T. Microhardness and abrasive wear resistance of metallic glasses and nanostructured composite materials. J. Non-crystalline Solids 316, 96–103 (2003).
Ji, X., Wang, H., Bao, Y. & Zheng, D. Wear resistance of cuzr-based amorphous-forming alloys against bearing steel in 3.5% nacl solution. Philos. Mag. 97, 3042–3054 (2017).
Hausleitner, C. & Turek, I. Structural, electronic, and magnetic properties of metallic glasses. J. Non-crystalline solids 156, 210–218 (1993).
Herzer, G. Modern soft magnets: Amorphous and nanocrystalline materials. Acta Materialia 61, 718–734 (2013).
Suryanarayana, C. & Inoue, A. Iron-based bulk metallic glasses. Int. Mater. Rev. 58, 131–166 (2013).
Sarac, B. et al. Origin of large plasticity and multiscale effects in iron-based metallic glasses. Nat. Commun. 9, 1333 (2018).
Lavorato, G., Fiore, G., Castellero, A., Baricco, M. & Moya, J. Preparation and characterization of fe-based bulk metallic glasses in plate form. Phys. B: Condens. Matter 407, 3192–3195 (2012).
Singh, A., Paul, T., Katakam, S., Dahotre, N. B. & Harimkar, S. P. In situ nanocrystallization-induced hardening of amorphous alloy matrix composites consolidated by spark plasma sintering. JOM 68, 1932–1937 (2016).
Shen, J., Chen, Q., Sun, J., Fan, H. & Wang, G. Exceptionally high glass-forming ability of an fecocrmocby alloy. Appl. Phys. Lett. 86, 151907 (2005).
Greer, A., Rutherford, K. & Hutchings, I. Wear resistance of amorphous alloys and related materials. Int. Mater. Rev. 47, 87–112 (2002).
Katakam, S. & Dahotre, N. Laser patterning of fe–si–b amorphous ribbons in magnetic field. Appl. Phys. A 117, 1241–1247 (2014).
Lin, C. Y., Tien, H. Y. & Chin, T. S. Soft magnetic ternary iron-boron-based bulk metallic glasses. Appl. Phys. Lett. 86, 162501 (2005).
Gupta, A. Nanocrystalline soft-magnetic alloys produced by controlled crystallization of amorphous alloys. Proceedings-Indian Natl. Sci. Acad. Part A 67, 31–46 (2001).
Nie, X. et al. The effect of oxidation on the corrosion resistance and mechanical properties of a zr-based metallic glass. Corros. Sci. 53, 3557–3565 (2011).
Noh, T.-H. & Jang, W.-H. Effects of surface oxidation on magnetic properties of amorphous alloy for choke core use. IEEE Transactions on Magn. 35, 3388–3390 (1999).
Zhang, S.-l, Liu, H.-p & Fu, X.-t Oxidation behavior of fe-based amorphous ribbons. J. Iron Steel Res. Int. 23, 1219–1225 (2016).
Pang, J. et al. Oxidation and refreshing behaviors of p-containing fe-based amorphous ribbons. J. Non-Crystalline Solids 471, 137–141 (2017).
Kai, W. et al. Oxidation behavior of cuzr-based glassy alloys at 400 c to 500 c in dry air. Metall. Mater. Transactions A 39, 1838–1846 (2008).
Kai, W. et al. Air-oxidation of a zr50cu43al7 bulk metallic glass at 400–500 c. Corros. Sci. 64, 98–104 (2012).
Yamashita, H., Yoshikawa, M., Funabiki, T. & Yoshida, S. Catalysis by amorphous metal alloys. part 6.-factors controlling the activity of skeletal nickel catalysts prepared from amorphous and crystalline ni–zr powder alloys. J. Chem. Soc. Faraday Transactions 1: Phys. Chem. Condens. Phases 83, 2883–2893 (1987).
Kang, S. et al. Importance of surface oxide for the tribology of a zr-based metallic glass. Frict. 5, 115–122 (2017).
Zhou, K. et al. Enhanced wear resistance of zr-based bulk metallic glass by thermal oxidation treatment. Mater. Transactions 58, 520–523 (2017).
Louzguine-Luzgin, D. et al. Exceptionally high nanoscale wear resistance of a cu47zr45al8 metallic glass with native and artificially grown oxide. Intermet. 93, 312–317 (2018).
Paul, T., Alavi, S. H., Biswas, S. & Harimkar, S. P. Microstructure and wear behavior of laser clad multi-layered fe-based amorphous coatings on steel substrates. Lasers Manuf. Mater. Process. 2, 231–241 (2015).
Kasturi, H., Paul, T., Biswas, S., Alavi, S. H. & Harimkar, S. P. Sliding wear behavior of spark-plasma-sintered fe-based amorphous alloy coatings on cu-ni alloy. J. Mater. Eng. Perform. 27, 3629–3635 (2018).
Paul, T. & Harimkar, S. P. Initial stage densification during spark plasma sintering of fe-based amorphous alloy powder: Analysis of viscous flow. J. Appl. Phys. 120, 134901 (2016).
Paul, T., Chawake, N., Kottada, R. S. & Harimkar, S. P. Pressure controlled micro-viscous deformation assisted spark plasma sintering of fe-based bulk amorphous alloy. J. Alloy. Compd. 738, 10–15 (2018).
Schroers, J. The superplastic forming of bulk metallic glasses. JOM 57, 35–39 (2005).
Paul, T. & Harimkar, S. P. Viscous flow activation energy adaptation by isochronal spark plasma sintering. Scripta Materialia 126, 37–40 (2017).
Li, N., Chen, W. & Liu, L. Thermoplastic micro-forming of bulk metallic glasses: a review. JOM 68, 1246–1261 (2016).
Wang, W.-H., Dong, C. & Shek, C. Bulk metallic glasses. Mater. Sci. Eng. R: Reports 44, 45–89 (2004).
Mondal, K., Chatterjee, U. & Murty, B. Oxidation behavior of multicomponent zr-based amorphous alloys. J. Alloy. Compd. 433, 162–170 (2007).
Wang, H.-S. et al. The oxidation behavior of a novel ni-free zr–cu-based bulk metallic glass composite in the supercooled liquid and crystallization states. Intermet. 53, 34–39 (2014).
Kai, W., Ren, I., Wang, R., Kao, P. & Liu, C. The oxidation behavior of an fe61b15zr8mo7co5y2cr2 bulk metallic glass at 650 c in various oxygen-containing environments. Intermet. 17, 165–168 (2009).
Hennayaka, H., Lee, H. S. & Yi, S. Surface oxidation of the fe based amorphous ribbon annealed at temperatures below the glass transition temperature. J. Alloy. Compd. 618, 269–279 (2015).
Hu, Y., Cao, W. & Shek, C. The corrosion and oxidation behavior of zr-based metallic glasses. J. Mater. Res. 29, 1248–1255 (2014).
Li, J. et al. Application of the small-angle x-ray scattering technique for structural analysis studies: A review. J. Mol. Struct. 1165, 391–400 (2018).
Fratzl, P. Small-angle scattering in materials science-a short review of applications in alloys, ceramics and composite materials. J. Appl. Crystallogr. 36, 397–404 (2003).
Ilavsky, J. et al. Development of combined microstructure and structure characterization facility for in situ and operando studies at the advanced photon source. J. Appl. Crystallogr. 51, 867–882 (2018).
Ilavsky, J. et al. Ultra-small-angle x-ray scattering instrument at the advanced photon source: History, recent development, and current status. Metall. Mater. Transactions A 44, 68–76 (2013).
Chirikov, N. & Skakov, Y. Analysis of concentration inhomogeneities of amorphous metal-alloys with the aid of small-angle scattering of x-rays and neutrons. Ind. Lab. 54, 633–640 (1988).
Zhang, F. et al. Effect of heat treatment on the microstructural evolution of a nickel-based superalloy additive-manufactured by laser powder bed fusion. Acta Materialia 152, 200–214 (2018).
Deschamps, A. & De Geuser, F. Quantitative characterization of precipitate microstructures in metallic alloys using small-angle scattering. Metall. Mater. Transactions A 44, 77–86 (2013).
Zhang, F. et al. In situ structural characterization of ageing kinetics in aluminum alloy 2024 across angstrom-to-micrometer length scales. Acta Materialia 111, 385–398 (2016).
Glatter, V. O. & Kratky, O. Small angle x-ray scattering. (London: Academic Press Inc. Ltd., 1982).
Tjioe, E. & Heller, W. T. Ornl_sas: software for calculation of small-angle scattering intensities of proteins and protein complexes. J. Appl. Crystallogr. 40, 782–785 (2007).
Ilavsky, J. & Jemian, P. R. Irena: tool suite for modeling and analysis of small-angle scattering. J. Appl. Crystallogr. 42, 347–353 (2009).
Paul, T., Singh, A. & Harimkar, S. P. Densification and crystallization in fe–based bulk amorphous alloy spark plasma sintered in the supercooled liquid region. Adv. Eng. Mater. 19 (2017).
Wriedt, H. The fe-o (iron-oxygen) system. J. Phase Equilibria 12, 170–200 (1991).
Ahmmad, B. et al. Green synthesis of mesoporous hematite (a-fe2o3) nanoparticles and their photocatalytic activity. Adv. Powder Technol. 24, 160–167 (2013).
Chen, L. et al. Continuous shape-and spectroscopy-tuning of hematite nanocrystals. Inorg. Chem. 49, 8411–8420 (2010).
Lu, J.-F. & Tsai, C.-J. Hydrothermal phase transformation of hematite to magnetite. Nanoscale Res. Lett. 9, 230 (2014).
Rizzo, H. F. Oxidation of boron at temperatures between 400 and 1300 c in air. In Boron Synthesis, Structure, and Properties, 175–189 (Springer, 1960).
Kai, W., Ren, I., Kao, P., Huang, R. & Liu, C. The oxidation behavior of an fe61b15zr8mo7co5y2cr2 bulk metallic glass at 550–700 c. Intermet. 17, 205–210 (2009).
Kai, W. et al. Air-oxidation behavior of a [(fe50co50) 75b20si5] 96nb4 bulk metallic glass at 500–650 c. Corros. Sci. 66, 26–32 (2013).
Wang, Y., Ni, Z., Shen, Z., Wang, H. & Wu, Y. Interference enhancement of raman signal of graphene. Appl. Phys. Lett. 92, 043121 (2008).
Li, S.-L. et al. Quantitative raman spectrum and reliable thickness identification for atomic layers on insulating substrates. ACS Nano 6, 7381–7388 (2012).
Pope, S. J. & West, Y. D. Comparison of the ft raman spectra of inorganic tetrahedral ions over the temperature range 77 to 473 k. Spectrochimica Acta Part A: Mol. Biomol. Spectrosc. 51, 2027–2037 (1995).
LaPlant, F., Laurence, G. & Ben-Amotz, D. Theoretical and experimental uncertainty in temperature measurement of materials by raman spectroscopy. Appl. Spectrosc. 50, 1034–1038 (1996).
Topal, C. O., Tan, S., Lu, H., Leventis, N. & Kalkan, A. K. Resonant two-photon oxidation in vanadium oxyhydrate nanowires above a threshold laser intensity. The J. Phys. Chem. C 116, 10186–10192 (2012).
Sivia, D. S. Elementary Scattering Theory: For X-ray and Neutron Users. (Oxford University Press, 2011).
Imhoff, S. et al. Kinetic transition in the growth of al nanocrystals in al-sm alloys. J. Appl. Phys. 111, 063525 (2012).
Schnablegger, H. & Singh, Y. The SAXS guide: getting acquainted with the principles. (Austria: Anton Paar GmbH, 2011).
Andrews, R. N., Serio, J., Muralidharan, G. & Ilavsky, J. An in situ usaxs–saxs–waxs study of precipitate size distribution evolution in a model ni-based alloy. J. Appl. Crystallogr. 50, 734–740 (2017).
Ilavsky, J. et al. Ultra-small-angle x-ray scattering at the advanced photon source. J. Appl. Crystallogr. 42, 469–479 (2009).
Acknowledgements
This material is based upon work supported by the National Science Foundation under Grant No. CMMI-1462602. This research used resources of the Advanced Photon Source, a U.S. Department of Energy (DOE) Office of Science User Facility operated for the DOE Office of Science by Argonne National Laboratory under Contract No. DE-AC02-06CH11357. Ultra-small angle X-rays scattering data was collected at the 9-ID beamline, X-ray Science Division at the Advanced Photon Source, Argonne National Laboratory. T.P. acknowledges the Oklahoma State University Graduate College Robberson Summer Dissertation Fellowships and Research and Creative Activities Grants.
Author information
Authors and Affiliations
Contributions
T.P. and S.P.H. conceived the project. T.P., L.Z., S.B., A.L., M.G.F., J.I. and I.K. conducted the experiments. T.P., L.Z., S.B. and A.L. analyzed the data. All authors discussed the results, wrote and reviewed the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Paul, T., Zhang, L., Biswas, S. et al. Quantification of Thermal Oxidation in Metallic Glass Powder using Ultra-small Angle X-ray Scattering. Sci Rep 9, 6836 (2019). https://doi.org/10.1038/s41598-019-43317-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-43317-0