Abstract
Plastic deformation and fracture of materials is accompanied by generation of elastic wave transients known as acoustic emissions (AE). A novel complex methodology combining the statistical analysis of distributions of time intervals between the successive AE events, and the unsupervised cluster analysis of the time series is proposed to test for possible correlations between emitting sources and to highlight their intrinsic dynamics. Aiming at revealing the essential temporal features of the twinning and dislocation dynamics, the proposed methodology was applied to the AE signals produced during plastic deformation in a magnesium alloy where both primary deformation modes - dislocation slip and twinning - operate concurrently. It has been undoubtedly demonstrated that the mechanical twinning belongs to a class of non-Poisson processes having a memory of the past in the millisecond range. As opposes to the correlated behaviour of twins, it was shown that the dislocation slip falls into the category of Poisson processes caused by independent sources.
Similar content being viewed by others
Introduction
Motivation and Methodology
Plastic deformation in many metals and alloys with the hexagonal close-packed (HCP) lattice is mediated by a combination of dislocation slip and mechanical twinning - two primary mechanisms of plastic flow at low homologous temperatures. Local stress fields associated with twinning are pivotal in the deformation behaviour and fracture but are extremely difficult to characterize experimentally1, particularly in dynamics whereby the twins interact with each other and/or with dislocations. Their mutual activity and interactions control the work hardening behaviour of magnesium-based alloys. Both these mechanisms generate elastic waves commonly referred to as acoustic emissions (AE)2 reflecting the specific dynamics of the sources and allowing for unique access to real-time information on underlying deformation processes. Bearing a strong similarity to seismology3,4,5, the AE technique, combined with multi-parametric descriptive statistical analysis and pattern recognition methods6, provides a powerful means of correlating the activity of elementary deformation processes - slip and twinning with the strain hardening behaviour7. The influence of various metallurgical factors (texture, grain size, and solute content) on AE and underlying twinning and dislocation slip behaviour under different loading modes (tension or compression) has been investigated in significant detail8,9,10,11,12. Similarly to pure FCC and BCC metals under uniaxial tensile loading, the AE activity in HCP Mg and its alloys commences at the very beginning of loading, peaks shortly after yielding and decays gradually with strain13,14). Due to its inherent sensitivity to dynamic processes only, the AE technique is an ideal tool for probing intermittency of the plastic flow, which is spatially heterogeneous and temporally fluctuating in nature due to a discrete character of dislocations and their avalanches15,16. AE stemming from dislocation mechanisms such as breaking away from unevenly distributed pinning points, motion between randomly spaced obstacles, escaping to a free surface at random locations along the gauge length, etc. involves a relatively large number of cooperatively moving dislocation segments and appears as an autoregressive stochastic process represented by a train of low-amplitude transients17,18. The question remains if the same applies to mechanical twins arising as a result of the strongly correlated motion of twinning dislocations, and generating powerful AE bursts with the amplitude proportional to the length and velocity of the nucleating twin19,20. The random AE time series can be fully characterised statistically in the multivariate space of features the shortest list of which includes the amplitude of transients and their inter-arrival times. In this way, the AE time series can be regarded as a point process. In fact, point processes can represent a wide variety of behaviours. The two most distinct types of underlying dynamics comprise a history-independent behaviour of autonomous and uncorrelated sources, and a history-dependent dynamics of interconnected, statistically correlated events. Thus, the temporal complexity of the collective dynamics of defects in solids during plastic flow is reflected in AE and can be made explicit through an adequate data analysis. While the statistical properties and the non-linear dynamics of dislocation avalanches arising during both smooth and jerky plastic flow have been intensively studied using the AE amplitude distributions16,21,22,23,24, the statistical behaviour of mechanical twins has not been explored to that extent25.
The Poisson random process model is the first choice to assess the dynamics of the emitting sources and possible correlations between them. It has indisputably set the basis for modelling efforts in many fields. It has become a widespread tool in materials science and geoscience, aiming at characterising strongly localised deformation and fracture evolving on different scales in time and in different patterns ranging from the nanometre-wide shear band in metallic glasses26,27 to rock mechanics4,28,29 and mega-earthquakes30,31. The Poisson distribution dominates the stochastic modelling philosophy whenever the sources are considered independent and it constitutes the grounds for a family of derivative renewal models accounting for deviations from the ideal Poissonian distribution due to the memory of the past and the correlation between the sources32,33,34 or due to inhomogeneity of the time-dependent intensity λ which itself might be a stochastic process (c.f. Cox or Pólya processes and their generalisations)35,36.
For the assessment of possible correlations in the behaviour of emitting defects, the AE time series is characterised by a single parameter – a set of arrival times of events \(\{{t}_{0},{t}_{1}\,\mathrm{...}\,{t}_{i}\,\mathrm{...}\,{t}_{N}\}\) as is commonly adopted for point processes. In practice, it is more convenient to investigate the distribution of time intervals between successive events \({\rm{\Delta }}{t}_{i}={t}_{i+1}-{t}_{i}\), Fig. 1. Assuming that the sources of local stress relaxation resulting in the AE events are independent, one should observe a Poisson time series defined as a train of Dirac’s δ-impulses \(\delta (t-{t}_{k})\) with amplitudes Uk
and the inter-arrival time intervals Δti obeying an exponential distribution with the probability density function
where \(\overline{{\rm{\Delta }}t}\) is the average (over the time interval T) time interval between the pulses in a time-series (or its chosen fragment) and \(\lambda =1/\overline{{\rm{\Delta }}t}\) is the average intensity (count rate or activity) of the pulse flow on the chosen time interval T.
Using the proposed robust statistical approach based on a blend of independent statistical procedures applied to the AE time series recorded during twinning-mediated plastic deformation of the magnesium alloy ZK60, we endeavour to reveal (and make explicit) correlations in the collective dynamics of mechanical twins, and to demonstrate that twinning is a history-dependent stochastic process.
Results and Data Analysis
Twin nucleation in HCP crystals occurs primarily from grain boundaries1,37 by simultaneous glide of multiple twinning dislocations38. This cooperative dislocation motion produces strong AE transients rising to peak values within few microseconds since the twins nucleate very fast, at a sizable fraction of the velocity of sound39, due to the fact that the stress required for twin propagation is lower than that for twin nucleation. Therefore, once nucleated, the twin propagates through the grain in both longitudinal and lateral directions until another twin variant, the opposite grain boundary or immobile dislocations impede twin movement. It has been well understood that AE results from rapid twin nucleation while the slow lateral twin growth (thickening) does not produce any measurable AE20,40,41,42. The mutual interactions between twins can, therefore, be elucidated by the use of statistical analysis of transients in AE time series.
Raw data representing the typical AE time series recorded in the course of tensile testing of the Mg-alloy ZK60 are shown in Fig. 1 at different scales revealing the discrete nature of AE signals mixed with continuous background noise. Similarly to most structural metals (c.f. Fig. 2 for well-annealed α-Fe), AE exhibits a broad peak after yielding, Fig. 1a, which then reduces as strain hardening proceeds. Figure 1b and c show that the AE stream in Mg alloy consists of a large number of randomly appearing well-separated transient signals with broadly varying amplitudes. The AE arrival times \(\{{t}_{0},{t}_{1},\,\mathrm{...},\,{t}_{N}\}\) obtained from the continuously recorded AE signal constitute the point process as illustrated schematically in Fig. 1c,d. Since the properties of any random process are fully determined by a probability density function (PDF) of a descriptive random variable, the PDF \(\rho ({\rm{\Delta }}t)\) is obtained for each j-th realisation, and the statistical goodness-of-fit χ2 test is applied to probe the agreement between the inter-arrival times Δt and the Poisson distribution (2) with the count rate \({\lambda }_{j}={N}_{j}/T\) for each realisation \(j\in [1,K]\). Main findings of the statistical analysis are shown in Figs 2 and 3 for pure α-Fe and ZK60 alloy, respectively (for comparison, α-Fe is taken here as a representative of a class of materials deforming solely by intermittent dislocation slip mechanisms while the Mg-based alloy demonstrates profuse twinning). In these figures, the AE intensity \(\lambda \) is superimposed with the loading diagram and the original raw AE stream shown on a background.
It is instructive to notice that two generic types of AE behaviour – Poisson and non-Poisson, arise depending on the underlying deformation mechanism as highlighted in these figures. The individual slip lines, such as those reflecting the dislocation-mediated AE response in pure well annealed Fe with mean grain size of 150 μm, Fig. 2, emerge on a free surface as a result of the collective dislocation behaviour which can be resolved by the modern AE technique revealing separated transients masked in the continuous noise-like signal17. Even though every elementary slip event involves the correlated motion of a large number of atoms on a microscale, during strain hardening, numerous slip lines appear sporadically and independently in different grains of polycrystalline aggregates18. The Poisson type AE is therefore reasonably expected unless the collective effects in dislocation ensembles come into force in the form of coarse slip bands or plastic instabilities43,44. This can be nicely seen in Fig. 2, where the Poisson type AE is confirmed over the entire uniform hardening range in excellent agreement with the assumption made in18, while the non-Poisson (correlated) behaviour is seen during the Lüders band propagation stage where the correlated dislocation behaviour is naturally anticipated. The collective dynamics of twins is notably different. Typical randomly chosen experimental distributions of inter-arrival times observed on different stages of deformation of the alloy ZK60 are shown in Fig. 4 where the expected ideal theoretical Poisson distributions with the count rate λ (same as that observed experimentally for a given sample) according to Eq. (1) are also displayed by solid lines. The χ2 test shows that at the very beginning of deformation, AE commences as the Poisson process, i.e. good agreement exists between the observed and expected exponential distributions of waiting times. The same can be said with high confidence for the mature stage of deformation (ca.12–20 s) before necking and fracture sets in. Similarly to Fig. 2, this is illustrated schematically in Fig. 3 by green squares. As opposes to this, the χ2 Pearson’s p-value being much less than the 0.05 significance level suggests that we cannot accept the null hypothesis and that there is a significant difference between the observed and the expected Poisson distribution from approximately 5 to 12 s of the deformation process. This is highlighted by red on the intensity curve in Fig. 3. We should notice that this time interval corresponds to the appearance of the broad peak of AE intensity which is most commonly associated with the dominance of twinning in plastic deformation of Mg and its alloys41,45,46.
To confirm the results of the \({\chi }^{2}\) hypothesis testing and to get a deeper insight into the nature of the event–event correlations, the independent Bi-test47 was used. Originally proposed in astrophysics as a method for probing local correlations in time series, this test has been successfully used to characterise the statistics of the local fracture events during compression of shale rocks48. As opposes to the Pearson’s the \({\chi }^{2}\) test, it is valid also for strongly non-stationary processes. The application of the Bi-test with a floating window has fully confirmed the results of the \({\chi }^{2}\) test. In particular, in the realisations where the hypothesis of the exponential distribution of time intervals is rejected, the Bi-test also suggests the presence of local correlations (the hypothesis of uniformity of B is rejected). Therefore, the consistency of the results of both independent tests can only lead one to conclude undeniably that there are local correlations in the studied stream of AE events.
As a matter of fact, two remarkably different statistics characterise AE data on different loading stages, and this has to be rationalised on the basis of operating deformation mechanisms. The observed significant deviation in the distribution of AE emitting sources from the Poisson-like behaviour is a prominent result since it expressly provides the evidence for the existence of a sort of statistical correlation between the defects underlying plastic flow in Mg and its alloys. To draw any conclusions on the nature of this correlation, one has (i) to identify the deformation mechanisms responsible for the observed correlations (e.g. dislocation slip, twinning, the interplay between these two, etc.), and (ii) to clarify its character by specifying an appropriate model of the non-Poisson process describing experimental data. To address the first problem, we employ the signal categorisation technique capable of distinguishing between different AE sources (see Methods for details).
Since the plastic strain associated with a single mechanical twin shooting through the grain is small49, a part of plastic strain has to be accommodated by dislocation slip, and both mechanisms co-exist in the course of plastic deformation. This implies that virtually any realisation of the AE random process contains contributions from both mechanisms and it is important to distinguish the respective contributions. This has been accomplished with aid from a quantitative statistical cluster analysis of AE time series in Mg and its alloys7,19,50,51. This analysis is based on the premise that dislocation slip and twinning are significantly different in their dynamics and therefore they generate AE with different waveforms. Specifically, continuous low-amplitude waveforms produced by dislocation slip can be compared to high amplitude transients for twinning7,40. Using the adaptive sequential k-means (ASK) AE signal clusterisation algorithm6 (see also7,50,52,53 for details), the realisations of 4k samples with similar Fourier power spectral density (PSD) were grouped in the same category, while the realisations with statistically different PSDs were disjoined. This non-supervised procedure reveals that the AE signals fall naturally into two primary categories with statistically different shapes of power spectra, as demonstrated in Fig. 5, representing the cluster centroids (mean PSD) for each AE source. Evidently, both clusters differ in the relative fraction of low and high-frequency components in their PSD. The noise-like Cluster 1 is characterised by the prevailing lower frequency content and low amplitude AE, which is typically associated with the dominance of dislocation slip in materials. Cluster 2 is composed of high-frequency transient signals with high peak amplitudes assuming from the preponderance of mechanical twinning. Thus, following the similar reasoning provided in7,50,53, Cluster 1 was associated with dislocation slip while Cluster 2 was attributed to twinning which appeared to be predominant from 5 to 12 s of deformation, Fig. 3. One should bear in mind that, in fact, as deformation proceeds, both deformation mechanisms - dislocation slip and twinning - co-exist contributing to the resultant AE throughout the entire loading process. The ASK algorithm makes it possible to identify the predominant mechanisms underlying the particular stages of strain hardening, and the contributions of each mechanism to the released AE energy have been found to be different depending on the strain, c.f. also7,50.
The remarkable result is that both independent data processing methods (the analysis of the distributions of waiting times between transients and the cluster analysis) show a strikingly good agreement on the time domains where the AE time series has distinct statistical features, Fig. 3: the non-AE Poisson behaviour is observed when the twinning appears as a dominant deformation mode, whereas when dislocation slip prevails as the predominant mechanism of plastic deformation (after of 12 s deformation), the AE obeys the Poisson statistics. In other words, while the dislocation motion during uniform plastic flow can be regarded as a random process of independent, uncorrelated sources, the mechanical twinning is a stochastic process with intrinsic correlations or some memory of the past.
The most intriguing finding of the present work is the deviation of the experimental AE time-series generated by mechanical twinning from the ideal Poisson process. The observed memory of the past can be short or long resulting in a conceptually different understanding of the background process. The short memory processes are grouped around a Poissonian background process with possible foreground dependants triggered by Poisson-distributed precursors while emphasising the long memory in the temporal and spatial evolution leads to self-organised criticality, power-law behaviour and long tail distributions. In order to get a deeper insight into the nature of this phenomenon, one has to identify a model of the point process which adequately describes experimental data.
A broad variety of candidates belonging to different classes of stochastic processes can be considered as potentially appropriate for characterising the observed correlations. Generally speaking, a temporal point process is specified through its conditional intensity function \({\lambda }^{\ast }{(t)}_{{H}_{t}}\) defined as35,54,55;
where the subscript Ht denotes symbolically the history of the process to time t, containing the list of arrival times (i.e. \({\lambda }^{\ast }\) at the moment generally depends on all ti < t), \({f}^{\ast }(t)\) is the conditional probability density function and \({F}^{\ast }(t)\) is the cumulative distribution function (CDF). Here the term “conditional” indicates that the process depends on the past and evolves. Hence, the conditional intensity function appears as a convenient means characterising how the present depends on the past in an evolutionary point process. For the Poisson process, the conditional intensity function is equal to the history-independent intensity \(\lambda (t)\) entering Eq. (2), i.e. \({\lambda }^{\ast }{(t)}_{{H}_{t}}=\lambda (t)\).
Let us recall that a class of point processes, which are referred to as renewal processes, is defined via independent identically distributed intervals. The Poisson processes (both homogeneous with \(\lambda (t)=const\) and heterogeneous with \(\lambda (t)\ne const\)) belong to this class. Considering its alternative with the short memory of the past, the so-called Hawkes process introduced in 197134,56 is admittedly one of the best-known candidates. In this process, the parent events follow a Poisson process, and multiple generations of descendants are triggered, relative to their parent. In this sense, the Hawkes process can be regarded as the “autoregressive” point process35. Modifications of this model have become the predominant models for earthquake aftershocks (ETAS) as well as for many other applications. Unlike Markovian processes disregarding the history of the process, the idea of the Hawkes process is centred on the premise that the memory of the past is an important intrinsic property of the generating process. Thus, the Hawkes process is the simplest extension of the Poisson point process, in which past events influence future events in such a way that the occurrence of any event increased the probability of further events occurring. It is therefore defined as a point process whose conditional intensity is a function of the past data \({H}_{t}\)34,56:
where \(\mu \in (0,\infty )\) is the positively defined deterministic count rate providing a Poisson base level for the process, and \(\varphi (t-{t}_{i})=a{e}^{-C(t-{t}_{i})}\) is the triggering/self-excitation kernel, which regulates the intensity at time t that is made by an event that occurs in the past at a previous time \({t}_{i}\) (both a and C are the positive constants)57. According to Eq. (4), each time a new event arrives, the conditional intensity increases sharply by a factor of a and then decreases exponentially back towards the μ value of the background Poisson process. Here a determines the magnitude of growth while С controls the rate of decay. One can notice that the conditional intensity (4) at the time moment t depends, indeed, on the whole time history ti < t, and the set of model parameters includes μ, a, and C: \({\rm{\Theta }}=\{\mu ,a,C\}\).
The Hawkes model was tested for consistency with experimental AE data using the statistical procedure described in Methods section. The dataset shown in Fig. 1 was taken as a typical example for illustration. Assuming the Hawkes model, the optimal parameters determined by the Nelder-Mead solver are given as \({{\rm{\Theta }}}_{opt}=\{\mu ,\,a,\,C\}=\{170,\,14.04,\,9.86\}\). The further detailed statistical analysis performed according to the scheme outlined above confirms that the Hawkes model provides an adequate first-order fit to the investigated time series:
-
(i)
the cumulative distribution function, Fig. 6a, of the doubly transformed AE point process is linear for its U values;
-
(ii)
the Q-Q plot, Fig. 6b, showing the quantile of the distribution of \({\tau }^{\ast }\) in the rescaled AE time series against the quantile of the \(\exp (\,-\,{\tau }^{\ast })\) distribution strongly suggests that both distributions are essentially the same;
-
(iii)
the points on the correlation plot \({U}_{i}-{U}_{i-1}\), Fig. 6c, are almost evenly distributed;
-
(iv)
the results of testing the null hypothesis that the distribution of inter-arrival times of the transformed process corresponds to the exponential distribution \(\exp (\,-\,{\tau }^{\ast })\) with the p-value greater than the criterial 0.05 while the initial distribution of inter-arrival times, Fig. 6d, cannot be considered Poissonian according to the same testing procedure.
In conclusion, the behaviour of AE produced primarily by mechanical twinning exhibits a short time correlation, and this memory of the past can be adequately described by the Hawkes type self-excited point process.
Discussion
Virtually any modelling, including the probabilistic ones, inevitably exaggerates some aspects of the phenomenon of interest while disregarding others. An adequate model is supposed to highlight the essential aspects and shadow the less important details. In this sense, the Hawkes point process model of the observed AE behaviour is the first order approximation that adequately captures the most salient feature of mechanical twinning evolution in Mg and its alloys – it is a correlated process having the memory of the past not only at the initiation phase generating the AE pulse, but also during collective dynamics of twin ensembles generating pulse trains. It also suggests that this memory is caused by the influence of twinning events on the immediately following events on the sub-millisecond time scale. Figure 4(c–e) illustrate clearly that the largest deviation of the inter-arrival times from the exponential Poisson distribution is seen in the short time domain below 1 ms.
There is abundant literature regarding dislocation-twin and twin-twin interactions58,59,60,61, which helps to shed light on the observed temporal correlation between the twinning-induced events in AE time series. The possible reasons for that include (a) the twin-dislocation interaction revealing itself, for example, as the activation of dislocation slip ahead of the propagating twin58,62 to relieve the stresses that exist at the tip of the twin terminating within the crystal63,64 (Fig. 7a), (b) the relay-like “twin induced nucleation mechanism” (Fig. 7b) whereby the lenticular twin shoots through the grain, terminates at the grain boundary and promotes initiation of a new adjoined twin in the neighbouring grain due to the stress concentration at its tip65,66,67,68,69,70, (c) lengthwise propagation of twin bundles (Fig. 7c) whereby several closely spaced parallel twin variants extend nearly concurrently in the same parent grain40 (see also71 for the evidence of twin clustering) and (d) auto-correlated jerky motion of the twin front (Fig. 7d) controlled by the intermittent flow of twinning dislocations72,73. All of these scenarios are illustrated in Fig. 7 showing the consecutive snap-shots of the specimen surface obtained by in situ high-speed video recording of deformation processes in Mg (the experimental setup has been described in74). Although none of these three scenarios can be completely disregarded, the first three cannot be considered as leading contributors to the existing temporal correlations since their time scales do not match the relatively short characteristic times where the deviation of the observed process from the ideal Poisson distribution is observed in the AE signal. On the other hand, Fig. 7d illustrates that the thin twin lamella can advance rapidly in the longitudinal direction in the jerky “stop-and-go” manner with short waiting times between jumps. It has been demonstrated experimentally and argued theoretically20 that even a micrometre scale advance of the twin with the velocity being of the order of the speed of sound, or a sizable fraction of it, induces measurable transient AE signals.
As a matter of caution, one should bear in mind that all the above considerations regarding the random data analysis have been originally developed for stationary (homogeneous) processes. One could reasonably suspect that the observed deviations of inter-arrival times from the Poisson distribution may not necessarily be caused by the longer memory of the past but might occur as a result of non-stationarity of the process at different points. Strictly speaking, the AE time series presented in Fig. 1, as well as other similar data we have obtained so far on Mg alloys, cannot be regarded as a “perfectly” stationary stochastic process, i.e. as a process whose unconditional joint probability distribution does not change in time. However, it can be considered as a weakly or “quasi-stationary” process on the time scale of individual realisations used for the analysis. Nevertheless, to make sure that the non-stationarity associated with varying AE activity cannot be the reason for the observed features, the same algorithm of signal detection and processing was applied to the synthetic time series simulating the strongly inhomogeneous Poisson process with the intensity \(\lambda (t)\) changing from 0 to 600 s−1 within 20 s according to the sine function. In all cases tested, the proposed algorithm correctly identifies the process as the non-stationary Poisson one even though the variation in λ was much stronger than that measured experimentally in our tests. Thus, the observed AE behaviour cannot be attributed to the non-stationarity of the slowly evolving time-series.
Summary and Conclusions
The results of the present work provide new insights into the physics of the twinning generation process and the temporal evolution of plasticity in twinning-prone materials through the proposed quantitative statistical analysis of the AE time series. The most intriguing result is that unlike dislocation slip, the mechanical twinning falls into a class of non-Poisson processes, i.e. it manifests itself as a process with a memory of the past. The AE time series were analysed statistically with independent methods from different angles, aiming at revealing fine features in the temporal dynamics of the underlying processes. The innovative threshold-less detection method was applied to determine the arrival times of events constituting the AE point process. The temporal event flow structure was described by the distribution of time intervals between successive events. Combining this analysis with the advanced adaptive sequential k-means signal categorisation technique, the predominant contributions of both dislocation slip and twinning were separated in the AE signal. The dislocation slip appeared as the random Poisson process with the exponential distribution of waiting times between the points. As opposes to this, it was undoubtedly demonstrated that the mechanical twinning in Mg alloys did not belong to the same class. Rather it can be approximated by the Hawkes self-excited process with the short memory of the past being of the order of 1 ms or less, and corresponding to the auto-correlated lengthwise propagation of the twin front.
As the additional outcome of this work, it can be concluded that the AE, when powered by modern signal detection, characterization and classification techniques, opens up a way to characterize the intimate details of the evolution of the dislocation and twin sub-systems quantitatively. While each of the two proposed analytical methods - statistical analysis of the inter-arrival times and adaptive categorization of spectral density functions - taken in isolation offers access to the dynamics of the AE sources on different scales, employing them together yields a much more conclusive picture.
As a final note, we should notice that the observed non-Poisson type behaviour of the twinning–related AE sources during tensile deformation of the coarse grain alloy ZK60 is not specific to the alloy, its grain structure or the deformation mode. Although in the present work the conclusions were supported by the results obtained in monotonic tension of the specific alloy, essentially the same AE behaviour was ubiquitously observed whenever the twinning was a dominant deformation mode in pure Mg, Ti, Zn or in their alloys with different grain sizes subjected to either tensile, compressive of cyclic deformation.
Materials and Methods
Materials and testing
Commercial magnesium alloy ZK60 (Mg-5.8Zn-0.44Zr, in wt.%) with the average grain size of 70 ± 13 μm after hot pressing was used as a representative of materials prone to twinning. Further details of its microstructural characteristics can be found in7,75. For the sake of comparison between the materials exhibiting twining and materials with dislocation-mediated plasticity, a plate of high purity 99.99% α-Iron produced by Nilaco Corporation (Japan) was two-step annealed at 1250 °C and 900 °C for 1 h per step in vacuum to obtain a uniform microstructure with random texture and grain size of 100 ± 30 μm. Mechanical tests were conducted on flat dog-bone shaped specimens having the gauge dimensions of 10 × 4 × 3 mm3. The specimens from both metals were shaped by an electric wire cutter and mechanically polished to a mirror-like finish. They were tensile tested to failure with a nominal strain rate of 5 × 10−3 s−1. A miniature broadband AE sensor PICO was mounted securely on an unstrained shoulder part in close proximity to the gauge part of the specimen. Vacuum oil was used as a coupling medium to ensure efficient transfer of elastic waves from the surface to the transducer. The signal was amplified by 60 dB in the frequency band from 50 to 1200 kHz and transferred to the AE data acquisition system based on a 16 bits PCI-2 (Physical Acoustics Corp., USA) board. AE recording was performed continuously in a threshold-less mode at a sampling rate of 2 MHz.
Data processing
Data processing includes the following steps:
-
(i)
signal detection and arrival time picking;
-
(ii)
analysis of the arrival time statistics by calculating the probability density function and performing its Chi-square goodness-of-fit test for the Poisson distribution;
-
(iii)
independent Bi-test for the same purpose;
-
(iv)
non-supervised signal classification by the Adaptive Sequential K-means (ASK) clustering algorithm aiming at the discrimination between the signals mediated by dislocation slip and twinning;
-
(v)
modelling the non-Poissonian time-series by a Hawkes type self-exciting process and its statistical verification vis à vis experimental data, using the random time change theorem.
Signal detection
To convert the continuously recorded AE data, Fig. 1a, into a sequence of arrival times, the signal detecting algorithm proposed in76 (see also77 for details) was used. The sliding-window technique employed a time window of 4096 samples moving by 4 samples through the whole raw dataset. For each signal fragment, a Fourier power spectral density (PSD) function \(G(f)\) was calculated using a periodogram technique. The signal detector ϕ is constructed as:
with \({\rm{\Delta }}f={f}_{{\rm{\max }}}-{f}_{{\rm{\min }}}\) - the frequency band. As long as the process is stationary, e.g., when no AE appears, and the recorded signal is due to noise, its spectral density does not change, \(G(f,t)=const\) and \(\phi (t)=0\). However, as soon as the burst AE signal arises and \(G(f,t)\) changes correspondingly, \(\phi (t)\ne 0\) and the signal is detected, Fig. 1c (inset). Due to the derivative nature of \(\phi (t)\), it is extremely sensitive even to the very subtle transient signals buried into the stationary background noise. To implement this algorithm, the raw streaming data were divided into K successive realisations of duration T, Fig. 1d, which is chosen to be long enough to ensure a sufficiently large number of events detected. For each j-th realisation, the ϕ-transform detects \({N}_{j}\) readings of arrival times \({t}_{j}\). Finally, a complete set of arrival times \(\{{t}_{0},{t}_{1}\,\mathrm{...}{t}_{i}\,\mathrm{...}\,{t}_{N}\}\) was obtained for the whole dataset.
Analysis of arrival times statistics
Since the properties of any random process are fully determined by the probability density function (PDF) of a descriptive random variable, the PDF \(\rho ({\rm{\Delta }}t)\) is obtained for each j-th realisation, and the statistical goodness-of-fit χ2 (Chi-square) test is applied to probe the agreement between the inter-arrival times Δt and the Poisson distribution according to Eq. (2). Note that for a Chi-square goodness of fit test, the null hypothesis states that the data are consistent with a specified distribution (Poisson distribution of inter-arrival times in our case). The alternative hypothesis is that the data are not consistent with the Poisson distribution. The null hypothesis is rejected if the computed Chi-square value is greater than the table critical value at a given level of significance. The process intensity (count rate) entering Eq. (1) is computed as \({\lambda }_{j}={N}_{j}/T\) for each realisation \(j\in [1,K]\).
Bi-test
The advantage of this test is that it is applicable to strongly non-stationary processes. For each tk event, a value \({B}_{k}=\frac{{{\rm{\Delta }}}_{k}}{{{\rm{\Delta }}}_{k}+{\delta }_{k}/2}\) is calculated47,48, where \({{\rm{\Delta }}}_{k}=\,{\rm{\min }}\,[{t}_{k}-{t}_{k-1};{t}_{k+1}-{t}_{k}]\) is the time distance to the nearest event, and \({\delta }_{k}=\{\begin{array}{c}{t}_{k-1}-{t}_{k-2}\,if{{\rm{\Delta }}}_{k}={t}_{k}-{t}_{k-1}\\ {t}_{k+2}-{t}_{k+1}\,if\,{{\rm{\Delta }}}_{k}={t}_{k+1}-{t}_{k}\end{array}\) is the time distance to the second successive event. If the AE process obeys a local Poissonian behaviour, the variable B should be evenly distributed between 0 and 1 with the mean \(\langle B\rangle =1/2\). The deviation of the experimental cumulative distribution function F(Bk) from the theoretical uniform distribution according to the Kolmogorov-Smirnov test with the 95% confidence interval indicates the event-event correlations.
Cluster Analysis
Mathematical details of this procedure are discussed in6 along with the benefits of this algorithm. The two most important features should be emphasised: (a) the number of clusters to be derived from a dataset is not specified a priori but is ‘data-driven’, and (b) the process is non-iterative, i.e. the AE signals are associated with a certain cluster sequentially as they arrive one after another. The procedure starts with an evaluation of the power spectrum of a background noise, which serves as a first reference point for comparison and the first cluster creation6. The symmetrised Kullback-Leibler divergence \({d}_{KL}\) was chosen as a measure of pair-wise similarity/dissimilarity between normalised discrete PSDs \({G^{\prime} }_{i}(f)\,\) and \({G^{\prime} }_{j}(f)\,\)6:
Each signal is either assigned to the nearest cluster or is used as a seed of a new cluster. The algorithm tends to minimise intra-cluster distances and maximise inter-cluster distances.
Model verification (the goodness of the model fit testing)
When a candidate model for the process studied is considered (e.g. Pólya, Hawkes, Cox, or, etc.), it is necessary to check it against experimental data to verify how good it is. In statistics, the random time change theorem78 is often used for this purpose. This theorem is an important result of martingale-based point process theory demonstrating a fundamental possibility to transform a wide class of point processes into a homogeneous Poisson process. It states that if t1, t2, … tn (\({t}_{i}\in [0,T],\forall i\)) is a realisation from a point process with the positive conditional intensity function \({\lambda }^{\ast }{(t)}_{{H}_{t}}\) and if the function
is strictly ascending and \({\rm{\Lambda }}(t) < \infty \), then the transformed time-series \(\{{t}_{1}^{\ast },{t}_{2}^{\ast }\,\mathrm{...},{t}_{n}^{\ast }\}=\{{\rm{\Lambda }}({t}_{1}),{\rm{\Lambda }}({t}_{2})\,\mathrm{...},{\rm{\Lambda }}({t}_{n})\}\) called a residual (or rescaled residual) process form the Poisson process with unit rate55,79. In other words, the distribution of rescaled time-intervals \(\{{\tau }_{1}^{\ast },{\tau }_{2}^{\ast },{\tau }_{3}^{\ast }\}=\{{t}_{1}^{\ast },{t}_{2}^{\ast }-{t}_{1}^{\ast },{t}_{3}^{\ast }-{t}_{2}^{\ast }\mathrm{..}\}\) should obey the exponential distribution with unit mean intensity \(\lambda =1\) and probability density \(f({\tau }^{\ast })=\exp (\,-\,{\tau }^{\ast })\). This theorem yields a powerful means for both the diagnostics for point process models and/or simulation of various point processes. Since the point process is defined by the conditional intensity function:
which is a function of time t and the set of parameters Θ specific for a given model, c.f. Eq. (4) for the Hawkes model, it is plausible to start from the numerical computation of model parameters Θopt approximating the experimental count rate \(\lambda (t)\) using the Nelder-Mead simplex optimization method80. Optimal parameters Θopt are then used to compute the expected model intensity function \({\lambda }^{\ast }{(t)}_{{H}_{t}}\). Finally, the goodness of the model fit is verified on the basis of the random time change theorem with an aid from the following four independent statistical procedures which are commonly used to test the suitability of the candidate model.
-
(i)
The quantile of the \({\tau }^{\ast }\) distribution is plotted against the quantile of the \(\exp (-{\tau }^{\ast })\) distribution for visual evaluation whether the two data sets come from populations with a common distribution.
-
(ii)
Transforming the intervals \({\tau }_{i}^{\ast }\) once again by applying the following transform
$${U}_{i}=1-\,\exp (-{\tau }_{i}^{\ast }),$$(9)one should obtain a set of uniformly distributed variables \(U\in [0,1]\). The mutual independence of variables U can be visually judged from the Ui vs Ui−1 scatter plot. If the intervals \({\tau }_{i}^{\ast }\) are independent over the whole definition range, the uniform distribution of points is supposed to be seen. The irregular patterns such as dense clusters of points would assume a memory of the past or some sort of correlation between the events in the initial process.
-
(iii)
The CDF for the uniformly distributed variables Ui should be a straight line.
-
(iv)
The \({\chi }^{2}\) Pearson’s criterion can be used for quantitative comparison of the goodness of agreement between experimental inter-arrival times \({\tau }_{i}^{\ast }\) and the theoretical distribution \(\exp (\,-\,{\tau }^{\ast })\).
References
Arul Kumar, M. et al. Deformation twinning and grain partitioning in a hexagonal close-packed magnesium alloy. Nature Communications 9, 4761 (2018).
Heiple, C. R. & Carpenter, S. H. Acoustic Emission Produced by Deformation of Metals and Alloys - A review: Part I and II. J. Acoustic Emission. 6, 177–237 (1987).
Aki, K. & Richards, P. G. Quantitative Seismology Theory and Methods. (W.H. Freeman and Company 1980).
Manthei, G. & Eisenblätter, J. In Acoustic Emission Testing: Basics for Research-Applications in Civil Engineering 239-310 (Springer Berlin Heidelberg 2008).
Weiss, M. & Louchet, F. Seismology of plastic deformation. Scripta Materialia 54, 747–751 (2006).
Pomponi, E. & Vinogradov, A. A real-time approach to acoustic emission clustering. Mech. Syst. Signal Proc. 40, 791–804 (2013).
Vinogradov, A., Orlov, D., Danyuk, A. & Estrin, Y. Effect of grain size on the mechanisms of plastic deformation in wrought Mg–Zn–Zr alloy revealed by acoustic emission measurements. Acta Materialia 61, 2044–2056 (2013).
Lamark, T. T., Chmelik, F., Estrin, Y. & Lukac, P. Cyclic deformation of a magnesium alloy investigated by the acoustic emission technique. Journal of Alloys and Compounds 378, 202–206 (2004).
Dobron, P. et al. Acoustic emission study of the mechanical anisotropy of the extruded AZ31 alloy. International Journal of Materials Research 100, 888–891 (2009).
Dobron, P., Chmelik, F., Bohlen, J., Letzig, D. & Kainer, K. U. Acoustic emission analysis of extruded AZ31 with varying grain size. Kovove Materialy-Metallic Materials 43, 193–201 (2005).
Bohlen, J. et al. Orientation effects on acoustic emission during tensile deformation of hot rolled magnesium alloy AZ31. Journal of Alloys and Compounds 378, 207–213 (2004).
Bohlen, J. et al. The effect of grain size on the deformation behaviour of magnesium alloys investigated by the acoustic emission technique. Advanced Engineering Materials 8, 422–427 (2006).
Lu, Y., Gharghouri, M. & Taheri, F. Effect of texture on acoustic emission produced by slip and twinning in AZ31B magnesium alloy - part II: clustering and neural network analysis. Nondestructive Testing and Evaluation 23, 211–228 (2008).
Li, Y. & Enoki, M. Twinning behavior of pure magnesium quantitatively investigated by acoustic emission. Materials Science and Engineering: A 536, 8–13 (2012).
Zaiser, M. & Seeger, A. In Dislocations in Solids Vol. Volume 11 Dislocations in Solids (eds Nabarro, F. R. N. & Duesbery, M. S.) Ch. 56, 1–100 (Elsevier 2002).
Miguel, M. C., Vespignani, A., Zapperi, S., Weiss, J. & Grasso, J. R. Intermittent dislocation flow in viscoplastic deformation. Nature 410, 667–671 (2001).
Vinogradov, A., Danyuk, A. V., Merson, D. L. & Yasnikov, I. S. Probing elementary dislocation mechanisms of local plastic deformation by the advanced acoustic emission technique. Scripta Materialia 151, 53–56 (2018).
Vinogradov, A., Yasnikov, I. S. & Estrin, Y. Stochastic dislocation kinetics and fractal structures in deforming metals probed by acoustic emission and surface topography measurements. Journal of Applied Physics 115, 233506 (2014).
Vinogradov, A., Vasilev, E., Merson, D. & Estrin, Y. A Phenomenological Model of Twinning Kinetics. Advanced Engineering Materials 19, 1600092 (2017).
Vinogradov, A. et al. On the limits of acoustic emission detectability for twinning. Materials Letters 183, 417–419 (2016).
Richeton, T., Weiss, J. & Louchet, F. Breakdown of avalanche critical behaviour in polycrystalline plasticity. Nature Materials 4, 465–469 (2005).
Richeton, T., Weiss, J. & Louchet, F. Dislocation avalanches: Role of temperature, grain size and strain hardening. ACTA MATERIALIA 53, 4463–4471 (2005).
Lebyodkin, M. A. et al. Role of superposition of dislocation avalanches in the statistics of acoustic emission during plastic deformation. Physical Review E 88, 042402 (2013).
Lebyodkin, M. A. et al. On the similarity of plastic flow processes during smooth and jerky flow: Statistical analysis. Acta Materialia 60, 3729–3740 (2012).
Shashkov, I. V. et al. Acoustic-emission study of intermittency of plastic flow during twinning and dislocation glide. Acta Phys Pol A 122, 430–434 (2012).
Vinogradov, A. & Leksovskii, A. Acoustic Emission in Amorphous Metals. Mater. Sci. Forum 210–213, 549–556 (1996).
Kovács, Z. et al. Statistical analysis of acoustic emission events in torsional deformation of a Vitreloy bulk metallic glass. Acta Materialia 70, 113–122 (2014).
Manthei, G. Application of the cluster analysis and time statistic of acoustic emission events from tensile test of a cylindrical rock salt specimen. Engineering Fracture Mechanics (2018).
Scholz, C. H. M. Microfractures, aftershocks, and seismicity. Bull. Seismol. Soc. Am. 58, 1117–1130 (1968).
Surkov, V. V. & Hayakawa, M. ULF geomagnetic perturbations due to seismic noise produced by rock fracture and crack formation treated as a stochastic process. Physics and Chemistry of the Earth 31, 273–280 (2006).
Parsons, T. & Geist, E. L. Were Global M ≥ 8.3 Earthquake Time Intervals Random between 1900 and 2011? Bulletin of the Seismological Society of America 102, 1583–1592 (2012).
Sornette, D. & Utkin, S. Limits of declustering methods for disentangling exogenous from endogenous events in time series with foreshocks, main shocks, and aftershocks. Physical Review E 79, 061110 (2009).
Barani, S. et al. Long-range dependence in earthquake-moment release and implications for earthquake occurrence probability. Scientific Reports 8, 5326 (2018).
Hawkes, A. G. Spectra of some self-exciting and mutually exciting point processes. Biometrika 58, 83–90 (1971).
Cox, D. R. & Isham, V. Point processes. (Chapman and Hall, 1980).
Minkova, L. D. I-Pólya Process and Applications. Communications in Statistics - Theory and Methods 40, 2847–2855 (2011).
Capolungo, L., Marshall, P. E., McCabe, R. J., Beyerlein, I. J. & Tomé, C. N. Nucleation and growth of twins in Zr: A statistical study. Acta Materialia 57, 6047–6056 (2009).
Wang, J., Hirth, J. P. & Tomé, C. N. Twinning nucleation mechanisms in hexagonal-close-packed crystals. Acta Materialia 57, 5521–5530 (2009).
Bowden, F. P. & Cooper, R. E. Velocity of Twin Propagation in Crystals. Nature 195, 1091–1092 (1962).
Máthis, K. et al. Effect of the loading mode on the evolution of the deformation mechanisms in randomly textured magnesium polycrystals – Comparison of experimental and modeling results. International Journal of Plasticity 72, 127–150 (2015).
Drozdenko, D. et al. Investigating a twinning–detwinning process in wrought Mg alloys by the acoustic emission technique. Acta Materialia 110, 103–113 (2016).
Drozdenko, D., Čapek, J., Clausen, B., Vinogradov, A. & Máthis, K. Influence of the solute concentration on the anelasticity in Mg-Al alloys: A multiple-approach study. Journal of Alloys and Compounds 786, 779–790 (2019).
Neuhäuser, H. Collective micro shear processes and plastic instabilities in crystalline and amorphous structures. International Journal of Plasticity 9, 421–435 (1993).
Shashkov, I. V., Lebyodkin, M. A. & Lebedkina, T. A. Multiscale study of acoustic emission during smooth and jerky flow in an AlMg alloy. Acta Materialia 60, 6842–6850 (2012).
Bohlen, J. et al. On the influence of the grain size and solute content on the AE response of magnesium alloys tested in tension and compression. Materials Science and Engineering: A 462, 302–306 (2007).
Čapek, J. et al. Study of the loading mode dependence of the twinning in random textured cast magnesium by acoustic emission and neutron diffraction methods. Materials Science and Engineering: A 602, 25–32 (2014).
Newman, R. C., Shahrabi, T. & Sieradzki, K. Film-induced cleavage of alpha-brass. Scripta Metallurgica 23, 71–74 (1989).
Baró, J., Planes, A., Salje, E. K. H. & Vives, E. Fracking and labquakes. Philosophical Magazine 96, 3686–3696 (2016).
Kocks, U. F. & Westlake, D. G. Importance of twinning for ductility of hcp polycrystals. Transactions of the Metallurgical Society of Aime 239, 1107–& (1967).
Vinogradov, A., Orlov, D., Danyuk, A. & Estrin, Y. Deformation mechanisms underlying tension–compression asymmetry in magnesium alloy ZK60 revealed by acoustic emission monitoring. Materials Science and Engineering: A 621, 243–251 (2015).
Vinogradov, A., Vasilev, E., Linderov, M. & Merson, D. In situ observations of the kinetics of twinning–detwinning and dislocation slip in magnesium. Materials Science and Engineering: A 676, 351–360 (2016).
Takeda, R., Kaneko, Y., Merson, D. L. & Vinogradov, A. Cluster analysis of acoustic emissions measured during deformation of duplex stainless steels. Materials Transactions 54, 532–539 (2013).
Vinogradov, A., Lazarev, A., Linderov, M., Weidner, A. & Biermann, H. Kinetics of deformation processes in high-alloyed cast transformation-induced plasticity/twinning-induced plasticity steels determined by acoustic emission and scanning electron microscopy: Influence of austenite stability on deformation mechanisms. Acta Materialia 61, 2434–2449 (2013).
Rasmussen, J. G. Temporal point processes: the conditional intensity function, http://people.math.aau.dk/~jgr/teaching/punktproc11/tpp.pdf (2009).
Daley, D. J. & Vere-Jones, D. Introduction to the theory of point processes. (Springer, 2008).
Hawkes, A. G. & Oakes, D. A Cluster Process Representation of a Self-Exciting Process. Journal of Applied Probability 11, 493–503 (1974).
Hawkes, A. G. Hawkes processes and their applications to finance: a review. Quantitative Finance 18, 193–198 (2018).
Zhang, J., Xi, G., Wan, X. & Fang, C. The dislocation-twin interaction and evolution of twin boundary in AZ31 Mg alloy. Acta Materialia 133, 208–216 (2017).
Christian, J. W. & Mahajan, S. Deformation twinning. Progress in Materials Science 39, 1–157 (1995).
Yu, Q. et al. Twin-twin interactions in magnesium. Acta Materialia 77, 28–42 (2014).
Capolungo, L., Beyerlein, I. J., Kaschner, G. C. & Tomé, C. N. On the interaction between slip dislocations and twins in HCP Zr. Materials Science and Engineering: A 513–514, 42–51 (2009).
Roberts, E. & Partridge, P. G. The accommodation around {1012} 〈1011〉 twins in magnesium. Acta Metallurgica 14, 513–527 (1966).
Mahajan, S. & Chin, G. Y. The interaction of twins with existing substructure and twins in cobalt-iron alloys. Acta Metallurgica 22, 1113–1119 (1974).
Arul Kumar, M., Kanjarla, A. K., Niezgoda, S. R., Lebensohn, R. A. & Tomé, C. N. Numerical study of the stress state of a deformation twin in magnesium. Acta Materialia 84, 349–358 (2015).
Beyerlein, I. J., McCabe, R. J. & Tomé, C. N. Effect of microstructure on the nucleation of deformation twins in polycrystalline high-purity magnesium: A multi-scale modeling study. Journal of the Mechanics and Physics of Solids 59, 988–1003 (2011).
Cheng, J., Shen, J., Mishra, R. K. & Ghosh, S. Discrete twin evolution in Mg alloys using a novel crystal plasticity finite element model. Acta Materialia 149, 142–153 (2018).
Guo, Y., Abdolvand, H., Britton, T. B. & Wilkinson, A. J. Growth of {112−2} twins in titanium: A combined experimental and modelling investigation of the local state of deformation. Acta Materialia 126, 221–235 (2017).
Basu, I., Fidder, H., Ocelík, V. & De Hosson, J. T. M. Local stress states and microstructural damage response associated with deformation twins in hexagonal close packed metals. Crystals 8, 1–15 (2018).
Culbertson, D., Yu, Q. & Jiang, Y. In situ observation of cross-grain twin pair formation in pure magnesium. Philosophical Magazine Letters, 1–8 (2018).
Kumar, M. A., Beyerlein, I. J., Lebensohn, R. A. & Tomé, C. N. Modeling the effect of neighboring grains on twin growth in HCP polycrystals. Modelling and Simulation in Materials Science and Engineering 25, 064007 (2017).
Nervo, L., King, A., Fitzner, A., Ludwig, W. & Preuss, M. A study of deformation twinning in a titanium alloy by X-ray diffraction contrast tomography. Acta Materialia 105, 417–428 (2016).
Yoo, M. H. & Lee, J. K. Deformation twinning in h.c.p. metals and alloys. Philosophical Magazine A 63, 987–1000 (1991).
Messerschmidt, U. Dislocation dynamics during plastic deformation. (Springer, 2010).
Seleznev, M. & Vinogradov, A. Note: High-speed optical imaging powered by acoustic emission triggering. Rev Sci. Instruments 85, 076103 (2014).
Orlov, D., Raab, G., Lamark, T. T., Popov, M. & Estrin, Y. Improvement of mechanical properties of magnesium alloy ZK60 by integrated extrusion and equal channel angular pressing. Acta Materialia 59, 375–385 (2011).
Vinogradov, A. & Ueno, H. Method of signal detection, patent of Japan JP4754651, B (2009).
Agletdinov, E., Pomponi, E., Merson, D. & Vinogradov, A. A novel Bayesian approach to acoustic emission data analysis. Ultrasonics 72, 89–94 (2016).
Brown, T. C. & Nair, M. G. A simple proof of the multivariate random time change theorem for point processes. Journal of Applied Probability 25, 210-214 (2016988).
Brockwell, P. J. & Davis, R. A. Introduction to time series and forecasting (Springer Texts in Statistics). (Springer-Verlag New York, 2002).
Nelder, J. A. & Mead, R. A Simplex Method for Function Minimization. The Computer Journal 7, 308–313 (1965).
Acknowledgements
The support from the Ministry of Education and Science of RF through the State Assignment according to the contract No. 11.5281.2017/8.9 is gratefully appreciated.
Author information
Authors and Affiliations
Contributions
A.V. devised the concept of this study and wrote the paper, E.A. developed signal processing algorithms, performed data analysis and prepared the figures, D.M. carried out experiments and discussed the results. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Vinogradov, A., Agletdinov, E. & Merson, D. Mechanical Twinning is a Correlated Dynamic Process. Sci Rep 9, 5748 (2019). https://doi.org/10.1038/s41598-019-42317-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-42317-4
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.