Abstract
Temperature-modulated space-charge-limited-current spectroscopy (TMSCLC) is applied to quantitatively evaluate the density of trap states in the band-gap with high energy resolution of semiconducting hybrid lead halide perovskite single crystals. Interestingly multicomponent deep trap states were observed in the pure perovskite crystals, which assumingly caused by the formation of nanodomains due to the presence of the mobile species in the perovskites.
Similar content being viewed by others
Introduction
Organometallic and inorganic halide perovskites are prospective candidates to replace conventional inorganic materials not only in the photovoltaic application1,2,3,4,5,6,7,8 but also, in solid states lasers9, light-emitting diodes10, photodetectors11 and solar fuels production12. Lead halide perovskites possess high-absorption coefficients, long-ranged ambipolar transport13 and low cost and facile deposition techniques such as coating and printing14,15,16. Moreover, it has been reported on facile growth of large monocrystals of lead halide17,18,19 (or even lead free20) perovskites by various techniques. Such single crystals, possessing very low defect density, are good candidates to disclose a variety of interesting and important properties of this group of materials. Perovskite single crystals have shown interesting properties, e.g., perovskite solar cells can harvest below the bandgap21, and perovskite photodetectors possess impressive characteristics for the detection of various wavelengths22. Furthermore, single crystals of lead halide perovskites are high-gain materials for lasing because of their high absorption coefficient, high photoluminescence quantum yield, slow Auger recombination rate, long carrier diffusion length and low defect density23,24.
Alongside with the other interesting properties of the lead halide perovskites, these materials possess two types of conductivity: electronic and ionic one25. Ionic conductivity in lead halide perovskite is the result of cations and/or anions migration across the perovskite under the influence of an electric field. As the result of the ionic diffusion, the open regions or the significant population of vacancies on the appropriate sublattice of perovskite lattice, which allow the ionic movement, appear. Aforesaid vacancy assisted ionic defects act as traps for charge carriers in the perovskite. Therefore the ionic diffusion in lead halide perovskites results in the appearance of lattice defects, which has important implications in terms of long-term stability and performance of perovskite-based devices (i.e. solar cells, LEDs, photodetectors etc.). Moreover polarization of the solar cell electrodes is usually associated with mobile ions and surface carrier recombination, and achievable open-circuit voltage26,27. In this regard, the understanding of the complex charge carrier dynamics induced by the ion migration is highly important. However it has to be noted, that kinetics of the mobile ions in the perovskites is a complex multicomponent phenomenon, which is still poorly understood. The existence of several ionic species, which can be a subject to diffusion, make the experimental evaluation rather obscure. As an example, it has been predicted theoretically and measured experimentally28, that, in fact three types of ionic species can be associated with vacancy-assisted ionic conductivity. The activation energy values to provoke the ionic movement were evaluated as: 0.58, 0.84 and 2.31 eV for I−, MA+ and Pb2+ respectively.
In the present communication the MAPbBr3 perovskite single crystals were studied by temperature-modulated space-charge-limited current (TMSCLC) method29,30,31,32. While regular SCLC technique is based on the measurement of current-voltage characteristic (steady-state regime) or time-of-flight of charge carriers (dynamic regime) to get information concerning the current non-linearity, charge carrier concentration, hole or electron mobility, and charge trapping process in various device architectures and materials, the TMSCLC technique is suggested as a self-consistent spectroscopic method for the determination of both the distribution of localized states (traps) and their energy. The spectroscopic character of the method follows from the simultaneous measurement of space-charge current on both voltage and temperature (energy window associated with the Fermi-Dirac statistics and the shift of the Fermi level).
Results and Discussion
As it can be seen from the experimental current-voltage characteristic (Fig. 1), the current is influenced by the barrier up to 0.3 V, it is ohmic (I~V) in the voltage range (0.3–1.2) V. Then it is a superlinear dependence (I∼Vm) with non-constant exponent m (m increases with voltage). It suggests the presence of charge carrier traps distributed in energy. The current decrease was observed in the voltage range (1.5–1.8) V. For higher voltages the I–V characteristic is typical for the material with Gaussian distribution of traps for charge carriers33,34. The last part of I–V characteristic (voltages higher than about 2 V) can be expressed by Child’s law (trap-free SCLC conduction). Here, for the current density j we can write
where μ is the charge carrier mobility, ε0 is the permittivity of vacuum, εr is the relative permittivity, V is the voltage, and L is the sample thickness. From this equation the trap free charge carrier mobility can be determined for εr = 25.535 as μ = 17.8 cm2V−1s−1.
The open question is the decrease of current in the voltage region (1.5–1.8) V. Here, we assume that the “negative differential resistance” is associated with the crystal polarization. As it was reported previously, lead halide perovskites can exhibit unipolar self-doping properties. Thus, depending on the composition of intrinsic point defects the material can be either n- or p-type36,37. Hence, due to the presence of the mobile ionic species in lead halide perovskites, biasing the sample results in the crystal polarization, which in its turn may be considered as an appearance of the depletion region between highly n-doped or n++ (i.e. MA+ rich or Br− poor) and highly p-doped or p++ polar nanodomains38. The increasing voltage at the “N-shaped” I-V curve is presumably caused by the majority charge carriers tunneling through the depletion region between the MA+ and Br− ion rich states at the bias voltage (1.2–1.8) V for the MAPbBr3. At higher voltage the charge carriers injected across the depletion region can be observed.
It follows from equations below that each point in the SCL current-voltage characteristic comprises the information about the trap density which influences the current value at the given Fermi level EF. The expression for the current density j in the SCLC regime can be written as:
where \(\gamma ={\rm{d}}\,\mathrm{ln}\,V/{\rm{d}}\,\mathrm{ln}\,j\) is the slope of logarithmic dependence of I-V characteristics, and \(\Theta ={n}_{{\rm{f}}}/{n}_{{\rm{t}}}\) is the ratio of the free (nf) and trapped (nt) charge carrier concentration.
The concentration of trapped charge carriers at the Fermi level (EF) is equal
Traps below the Fermi level are usually all occupied and the relation is valid
where E is the trap energy, Nt is the concentration of electronic states, and H(E − EF) is the Heaviside step function. Thus, using the slope of the current-voltage characteristic \(\gamma ={\rm{d}}\,\mathrm{ln}\,V/{\rm{d}}\,\mathrm{ln}\,j\), we can determine the density of the localized electronic states.
Using the equation \(j=\sigma F=e\mu {n}_{{\rm{f}}}(2-\gamma )\,V/L\), where \(\sigma =e\mu {n}_{{\rm{f}}}\) is electric conductivity and \(F=(2-\gamma )\,V/L\) is electric field, it is possible to determine the position of the Fermi level with the relation to the band energy levels (i.e. valence or conduction bands)
where EV is energy of valence band and NV is its states concentration. In ohmic region (γ = 1) is this position proportional to activation energy \({E}_{{\rm{a0}}}={E}_{{\rm{F0}}}-{E}_{{\rm{V}}}\), where EF0 is position of Fermi level in thermodynamic equilibrium.
For this reason the activation energy of the current (conductance) was measured for each applied voltage in range of (0–3) V, with step 28 mV. The temperature was changed (modulated) in the range of (0–40) °C. Figure 2 shows the level of accuracy at the measurement of activation energy according to the relation \(\sigma =(I/V)(L/S)={\sigma }_{0}\exp (-{E}_{{\rm{a}}}/{k}_{{\rm{B}}}T)\) for heating and cooling cycle. Here, L is the distance between the electrodes of the certain area S. The slope of these dependences is directly activation energy.
An approximate relation can be considered: \({E}_{{\rm{a}}}\approx {E}_{{\rm{F}}}-{E}_{{\rm{V}}}\) and \(\Delta {E}_{{\rm{a}}}\approx \Delta {E}_{{\rm{F}}}\). The shift of the Fermi level ΔEF can be determined according to the relation mentioned above. Note, that Fermi level position represents the energy at which the localized state (trap) is filled during the measurement of current-voltage characteristic.
Figure 3 represents the activation energy and Fermi level shift for the dark (A) and illuminated (B) sample (each point in the plot is averaged from 300 experimental values). Note, that for the low voltages (subohmic regime, V < 0.3 V) where the Schottky barrier is predominant, traps also significantly influence the activation energy. Here, the dependence of the Fermi level on the initial voltage value (V0 ≈ 0.03 V)
and the dominant energy determined as the difference between the activation energy and the shift of the Fermi level Ed = Ea − ΔEF32, both in the dark and under the illumination. From the Fig. 3C in which the two dominant energies are plotted together, it can be observed that the dominant energy under illumination being shifted by 0.46 eV to higher values, which indicates that the charge trapping takes place in the same states
From the Fig. 3 follows that three main trap states (Et) influence the electric behavior of the sample under study Et = 0.63 eV, 0.55 eV, and 0.38 eV. The activation energy Ea = 0.80 eV is associated with the thermodynamic equilibrium position of the Fermi level. During the charge injection (the superlinear I–V characteristic), the charge carriers is influenced by traps. The deepest trap Et = 0.63 eV, can be related to the vacancy assisted mobile ionic species (presumably MA+); thus in the range of (1.1–1.4) V of the current-voltage characteristic we observe trap filled limit for p-type charge carriers. At higher voltages the interchange of dominant charge carriers is observed, which is represented by the significant perturbations in activation energy. In this region a negative differential current is observed. The interchange between the dominant charge carriers (MA+ vs. Br−), can be observed as a tunneling through the depletion region between p++ and n++ sites.
Under the illumination, the Fermi level is strongly influenced by the light generated charge carriers (electrons), From the overall thermal conductivity measurement the Drude-like behavior is expected39. The dominant energy is significantly lower (0.17 V); no contact barrier was observed (Fig. 3B). The dominant states close to the valence band (0.09 eV) are taken over by the charge carrier traps above the edge of the valence band (−0.08 eV). As a result (see Fig. 3C), three trap states with the energies Et = 0.17 eV, 0.09 eV, and −0.08 eV are formed under illumination. These are the same relationships as in the dark, but they are related to the other position of the edge of the valence band (shifted by 0.46 eV to lower values).
Under the assumption, that the concentration of states in the valence band of the MAPbBr3 crystal equals to \({N}_{{\rm{V}}}\approx 6\times {10}^{17}{{\rm{cm}}}^{-3}\) and crystal thickness is \(L\approx {10}^{-3}{\rm{m}}\), the mobility for holes was determined in the dark conditions as \({\mu }_{{\rm{p}}}=17.8\) cm2V−1s−1.
Using the expression for trapped charge carriers (equation 3) it is possible to calculate their concentration for various energies and therefore to get energy distribution of traps. For the more representative dependence of the charge carriers on individual traps the charge carrier concentration vs. activation energy \(g(E)\approx {\rm{d}}{n}_{{\rm{tL}}}/{\rm{d}}{E}_{{\rm{F}}}\) (Fig. 4A) can be plotted. The red dashed vertical lines represent individual charge carrier traps as it was estimated from the I-V characteristics. It can be clearly seen how the concentration of the charge carrier increases at each individual trap states, which means charge carriers accumulation at the trap density. For the above-mentioned calculation the relative permittivity of the MAPbBr3 was taken as \({\varepsilon }_{{\rm{r}}}\approx 25.5\)35. Generally, the values for the concentrations and charge carrier mobilities obtained by the TMSCLC method are close to the values reported before40,41,42,43,44. In the Fig. 4B the concentrations were calculated using the equation (2).
Interestingly, the band diagram (see Fig. 4C) shows, that the charge transfer is associated only with holes in the valence band. Trap state Et1 is located above the edge of the valence band, when no light illumination is applied, however, under light illumination it shifts under the edge of the valence band.
The results for all the determined traps are summarized In the Table 1: their position (dominant energy is equal to activation energy when the trap is fulfilled \({E}_{{\rm{d}}}\approx {E}_{{\rm{a}}}\)), the concentration of trap states for this case (\({N}_{{\rm{t}}}\approx {n}_{{\rm{t}}}\)) and drift mobility of the charge carriers in the traps (\({\mu }_{{\rm{d}}}\approx \Theta {\mu }_{{\rm{0}}}\), where μ0 is microscopic mobility), it can be determined from Childs law (when \(\Theta =1\), see Eq. 1), or from Fermi level position in ohmic regime (\({E}_{{\rm{F0}}}\approx {E}_{{\rm{a}}}\), when \({E}_{{\rm{V}}}=0\,{\rm{eV}}\), see Eq. 5)
Comparing current results with previously reported, it has to be emphasized, that the mobility values in lead halide perovskite may vary within the several orders of magnitude43,45, whilst theoretically, mobilities in lead halide perovskite supposed to be comparable with the ones of inorganic semiconductors, e.g. GaAs, as far as it has only slightly lower effective masses for conduction band electrons and valence band holes, however there are some limiting factors for the charge carrier mobilities in perovskites, which are extrinsic and intrinsic effects.
Intrinsic effects cannot be avoided, as far as they are originated result from charge-carrier interactions with the crystal lattice. On the other hand extrinsic effects are the result of material imperfections, such as grain boundaries, energetic disorder, or impurities. In the present case, the growth of the crystals was precisely controlled, thus regular rectangular shaped samples were obtained (see Fig. 5B), Moreover, it is assumed, that the carbon contacts prepared from the non-polar solvent xylene (which is antisolvent for the perovskite46) resulted in contact interface with less defects, in comparison with the samples where thermally evaporated contacts were deposited.
Experimental
As it is shown in Fiugure 6, macroscopic 2–5 mm sized (MAPbBr3) perovskite single crystals were prepared from a solution by an inverse temperature crystallization method without a nucleation35. Lead bromide (PbBr2, 99.999%, Sigma-Aldrich), methylammonium bromide (CH3NH2.HBr, 98%, Sigma-Aldrich) and dimethylformamide (DMF, 99.8%, Sigma-Aldrich), were used as received without further purification. 1 M solution of PbBr2 and CH3NH2.HBr in DMF was added to ultrasonic bath under Ar atmosphere at room temperature for 3 min. The transparent solution was filtered using PVDF filter (pore size 0.45 μm). The resulting filtrate was gradually heated up in the oil bath from the room temperature up to 80 °C for about an hour, and consequently temperature was kept constant to obtain the crystals of the desired size. Then obtained crystals were rinsed in diethylether, dried with argon gun and instantly transferred to the glove box with a nitrogen atmosphere. Contacts were deposited at two opposite facets with a non-polar solvent (hexane) carbon paste, with the subsequent encapsulation with Ossila epoxy resin to avoid any influence of the atmospheric oxygen and moisture, when the electrical measurements outside of the glove box were performed.
XRD spectra (MAPbBr3) showed diffraction angles typical for perovskite. Moreover, in our previous work18 we have measured 2D XRD mapping of the samples prepared by the same method, which proved the single crystal nature of the samples.
Current- or photocurrent-voltage characteristics for TMSCLC method were measured using Keithley 2410 Source Meter in the interval (0–3) V with 0.028 V step. At each step the temperature was changed from 0 to 40 °C, using Lauda ECO Silver RE 415 thermostat and measured with thermocouple of type K by Agilent 34420 A, Digit NanoVolt/MicroOhm Meter. The current-voltage response was measured for 3 minutes at each point, in this regards the measurements are considered as steady-state.
For photoconductivity measurements the sample was irradiated by the white LED lamp with the intensity of 34 W/m2.
Conclusion
To sum up, in the present paper the implementation of the temperature-modulated space-charge-limited-current spectroscopy is applied to the single crystal methylammonium lead bromide perovskites. As a result, charge carrier mobilities (holes in the valence band) were calculated as 1.6, 9.1 and 17.8 cm2V−1s−1. Furthermore, with no illumination applied the activation energy Ea = 0.80 eV is associated with the thermodynamic equilibrium position of the Fermi level, additionally three individual trap states were found with the activation energies 0.63, 0.55 and 0.38 eV and concentrations of 2.4 × 109, 4.5 × 109, 6.2 × 1010, cm−3 respectively, notably under the light illumination Et = 0.38 shifts under the edge of the valence band resulting in Drude-like model.
References
Docampo, P., Ball, J. M., Darwich, M., Eperon, G. E. & Snaith, H. J. Efficient organometal trihalide perovskite planar-heterojunction solar cells on flexible polymer substrates. Nat. Commun. 4, 2761 (2013).
Kim, H.-S. et al. Mechanism of carrier accumulation in perovskite thin-absorber solar cells. Nat. Commun. 4, 2242 (2013).
Stranks, S. D. et al. Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 342, 341–344 (2013).
Mei, A. et al. A hole-conductor-free, fully printable mesoscopic perovskite solar cell with high stability. Science 345, 295–298 (2014).
Christians, J. A., Fung, R. C. M. & Kamat, P. V. An inorganic hole conductor for organo-lead halide perovskite solar cells. Improved hole conductivity with copper iodide. J. Am. Chem. Soc. 136, 758–764 (2014).
Liu, D., Yang, J. & Kelly, T. L. Compact layer free perovskite solar cells with 13.5% efficiency. J. Am. Chem. Soc. 136, 17116–17122 (2014).
Nie, W. et al. High-efficiency solution-processed perovskite solar cells with millimeter-scale grains. Science 347, 522–525 (2015).
Choi, J. J., Yang, X., Norman, Z. M., Billinge, S. J. L. & Owen, J. S. Structure of methylammonium lead iodide within mesoporous titanium dioxide: active material in high-performance perovskite solar cells. Nano Lett. 14, 127–133 (2014).
Xing, G. et al. Low-temperature solution-processed wavelength-tunable perovskites for lasing. Nat. Mater. 13, 476–480 (2014).
Tan, Z. K. et al. Bright light-emitting diodes based on organometal halide perovskite. Nat. Nano 9, 687–692 (2014).
Dou, L. et al. Solution-processed hybrid perovskite photodetectors with high detectivity. Nat. Commun. 5, 5404 (2014).
Chen, Y.-S., Manser, J. S. & Kamat, P. V. All solution-processed lead halide perovskite-BiVO4 tandem assembly for photolytic solar fuels production. J. Am. Chem. Soc. 137, 974–981 (2015).
Xing, G. et al. Long-range balanced electron- and hole-transport lengths in organic-inorganic CH3NH3PbI3. Science 342, 344–347 (2013).
Noh, J. H., Im, S. H., Heo, J. H., Mandal, T. N. & Seok, S. I. Chemical management for colorful, efficient, and stable inorganic–organic hybrid nanostructured solar cells. Nano Lett. 13, 1764–1769 (2013).
Filip, M. R., Eperon, G. E., Snaith, H. J. & Giustino, F. Steric engineering of metal-halide perovskites with tunable optical band gaps. Nat. Commun. 5, 5757 (2014).
D’Innocenzo, V., Kandada, A. R. S., De Bastiani, M., Gandini, M. & Petrozza, A. Tuning the light emission properties by band gap engineering in hybrid lead halide perovskite. J. Am. Chem. Soc. 136, 17730–17733 (2014).
Dang, Y., Ju, D., Wang, L. & Tao, X. Recent progress in the synthesis of hybrid halide perovskite single crystals. CrystEngComm 18, 4476–4484 (2016).
Kovalenko, A. et al. Interface inductive currents and carrier injection in hybrid perovskite single crystals. Appl. Phys. Lett. 111, 163504 (2017).
Kovalenko, A., Pospisil, J., Zmeskal, O., Krajcovic, J. & Weiter, M. Ionic origin of a negative capacitance in lead halide perovskites. Phys. Status Solidi RRL 11, 1600418 (2017).
Ji, C. et al. Inch‐Size Single Crystal of a Lead‐Free Organic–Inorganic Hybrid Perovskite for High‐Performance Photodetector. Adv. Funct. Mater. 28, 1705467 (2018).
Chen, Z. et al. Thin single crystal perovskite solar cells to harvest below-bandgap light absorption. Nat. Comm. 8, 1890 (2017).
Wang, L. et al. Tunable bandgap in hybrid perovskite CH3NH3Pb(Br3−yXy) single crystals and photodetector applications. AIP Advances 6, 045115 (2016).
Nguyen, V.-C., Katsuki, H., Sasaki, H. & Yanagi, H. Optically pumped lasing in single crystals of organometal halide perovskites prepared by cast-capping method. Appl. Phys. Lett. 108, 261105 (2016).
Harwell, J. R., Whitworth, G. L., Turnbull, G. A. & Samuel, I. D. W. Green Perovskite Distributed Feedback Lasers. Scientific Reports 7, 11727 (2017).
Zhao, Y.-C. et al. Quantification of light-enhanced ionic transport in lead iodide perovskite thin films and its solar cell applications. Light: Science & Applications 6, 16243 (2017).
Almora, O., Guerrero, A. & Garcia-Belmonte, G. Ionic charging by local imbalance at interfaces in hybrid lead halide perovskites. Appl. Phys. Lett. 108, 043903 (2016).
Zarazua, I., Bisquert, J. & Garcia-Belmonte, G. Light-Induced Space-Charge Accumulation Zone as Photovoltaic Mechanism in Perovskite Solar Cells. J. Phys. Chem. Lett. 7, 525–528 (2016).
Eames, C. et al. Ionic transport in hybrid lead iodide perovskite solar cells. Nat. Commun. 6, 7497 (2015).
Zmeskal, O., Nespurek, S. & Weiter, M. Space-charge-limited currents: An E-infinity Cantorian approach. Chaos, Solitons & Fractals 34(2), 143–158 (2007).
Nespurek, S., Zmeskal, O. & Sworakowski, J. Space-charge-limited currents in organic films: Some open problems. Thin Solid Films 516(24), 8949–8962 (2008).
Krellner, C. et al. Density of bulk trap states in organic semiconductor crystals: Discrete levels induced by oxygen in rubrene. Phys. Rev. B 75, 245115 (2007).
Zmeskal, O., Schauer, F. & Nespurek, S. The bulk trap spectroscopy of solids by temperature modulated space-charge-limited currents (TMSCLC) in the steady state. J. Phys. C: Solid State Phys. 18, 1873–1884 (1985).
Nespurek, S. & Smejtek, P. Space-charge-limited currents in insulators with the Gaussian distribution of traps. Czech. J. Phys. B22, 160–175 (1972).
Nespurek, S. & Silinsh, E. A. Space-charge-limited current theory for molecular crystals with Gaussian distribution of local trapping states. Phys. stat. sol (a) 34, 747–759 (1976).
Saidaminov, M. I. et al. High-quality bulk hybrid perovskite single crystals within minutes by inverse temperature crystallization. Nat. Commun. 6, 7586 (2015).
Shi, T., Yin, W. J., Hong, F., Zhu, K. & Yan, Y. Unipolar self-doping behavior in perovskite CH3NH3PbBr3. Appl. Phys. Lett. 106, 103902 (2015).
Wang, Q. et al. Qualifying composition dependent p and n self-doping in CH3NH3PbI3. Appl. Phys. Lett. 105, 163508 (2014).
Frost, J. M. & Walsh, A. What Is Moving in Hybrid Halide Perovskite Solar Cells? Acc. Chem. Res. 49, 528–535 (2016).
Tritt, T. M. Thermal Conductivity: Theory, Properties, and Applications, Physics of Solids and Liquids, Springer Science & Business Media, ISBN 038726017X (2006)
Shi, D. et al. Low trap-state density and long carrier diffusion in organolead trihalide perovskite single crystals. Science 347(6221), 519–522 (2015).
Saidaminov, M. I. et al. Planar-integrated single-crystalline perovskite photodetectors. Nat. Commun. 6, 8724 (2015).
Peng, J., Chen, Y., Zheng, K., Pulleritsb, T. & Liang, Z. Insights into charge carrier dynamics in organo-metal halide perovskites: from neat films to solar cells. Chem. Soc. Rev. 46, 5714 (2017).
Herz, L. M. Charge-Carrier Mobilities in Metal Halide Perovskites: Fundamental Mechanisms and Limits. ACS Energy Lett. 2, 1539–1548 (2017).
Wang, Y., Zhang, Y., Zhang, P. & Zhang, W. High intrinsic carrier mobility and photon absorption in the perovskite CH3NH3PbI3. Phys. Chem. Chem. Phys. 17, 11516–11520 (2015).
Adinolfi, V. et al. The In-Gap Electronic State Spectrum of Methylammonium Lead Iodide Single-Crystal Perovskites. Adv. Mater. 28, 3406–3410 (2016).
Konstantakou, M., Perganti, D., Falaras, P. & Stergiopoulos, T. Anti-Solvent Crystallization Strategies for Highly Efficient Perovskite Solar Cells. Crystals 7, 291 (2017).
Acknowledgements
The work was supported by the Czech Science Foundation grant No. 17-21105S. Research infrastructure was supported by project no. REG LO1211 from the National Programme for Sustainability I (MEYS CR).
Author information
Authors and Affiliations
Contributions
J.P. – conducted the experiments. S.N. and O.Z. – contributed with the theoretical part of the manuscript and calculations. J.K. – provided the synthesis of single crystals. M.W., as a head of the lab, provided materials and necessary equipment. A. K. – designed the experiments and wrote the main text of the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Pospisil, J., Zmeskal, O., Nespurek, S. et al. Density of bulk trap states of hybrid lead halide perovskite single crystals: temperature modulated space-charge-limited-currents. Sci Rep 9, 3332 (2019). https://doi.org/10.1038/s41598-019-40139-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-40139-y
This article is cited by
-
Electron-phonon interactions in halide perovskites
NPG Asia Materials (2022)
-
Space-charge-limited electron and hole currents in hybrid organic-inorganic perovskites
Nature Communications (2020)
-
Strain engineering and epitaxial stabilization of halide perovskites
Nature (2020)
-
Extraction technique of trap states based on transient photo-voltage measurement
Scientific Reports (2020)
-
Impact of electron transport layer material on the performance of CH3NH3PbBr3 perovskite-based photodetectors
Journal of Materials Science (2020)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.