Sediment phosphorus (P) removal is crucial for the control of eutrophication, and the in-situ adsorption is an essential technique. In this study, modified maifanite (MMF) prepared by acidification, alkalization, salinization, calcination and combined modifications, respectively, were first applied to treat sediment P. The morphology and microstructure of MMF samples were characterized by X-ray fluorescence (XRF), Fourier transform infrared (FTIR), X-ray diffraction (XRD), scanning electron microscope (SEM) and Brunauer-Emmett-Teller (BET). Various adsorption parameters were tested, such as dosage of maifanite, time, operation pH and temperature. The adsorption mechanisms were also investigated and discussed. Results showed that CMMF-H2.5-400 (2.5 mol/L H2SO4 and calcined at 400 °C) exhibited the highest P adsorption capacity. Thus, it was selected as the in-situ adsorbent material to control the internal P loading. Under the optimal conditions of dynamic experiments, the adsorption rates of TP, IP, OP, Fe/Al-P and Ca-P by CMMF-H2.5-400 were 37.22%, 44.41%, 25.54%, 26.09% and 60.34%, respectively. The adsorption mechanisms analysis revealed that the adsorption of P onto CMMF-H2.5-400 mainly by ligand exchange. Results of this work indicated that the modification treatment could improve the adsorption capacity of maifanite, and CMMF-H2.5-400 could be further applied to eutrophication treatment.
Eutrophication has become a worldwide water quality issue1,2. Phosphorus (P) is an essential element that can trigger severe eutrophication3,4. Many recent reports have shown that both nitrogen (N) and P, which are the key limiting nutrients in eutrophication play a dominant role in aquatic ecosystem5,6. Accordingly, P limitation occurs in spring, while N becomes the limiting factor in summer and fall7. The change in the dual limitation paradigm is because the P concentration in water bodies can be sustained by the release of P from sediments, whereas loss of N through denitrification often occur in warm season8. The release of sediment P, also known as internal P loading, has been recognized that the supply of sediment P to the growth of algae has two phases, which is dominated by the cycling of Iron (Fe)-bound P (Fe-P) and algal degradation. The internal loading of P from sediments plays a primary role in seasonal N limitation for harmful algal bloom (HAB), which in turn can drive the release of sediment P9. Fe is a redox-sensitive element and its redox cycle play a vital role in controlling the P mobility in sediments10. Some recent studies revealed that the formation of anoxic condition at the sediment-water interface during HAB events (HABs), causes the reductive dissolution of Fe (III) oxyhydroxides and the release of Fe-P11,12. Furthermore, the algal degradation appears during HABs, resulting in the release of P from the degraded algal cells13. In addition, previous studies found that the distribution of soluble reactive P (SRP) and labile P stratified into two layers, called static layer and active layer. In static layer, the concentration of soluble reactive phosphate and labile P remained at a low level, which is the key to sustain the immobilization effectiveness14. The active layer not only retains P liberated from the underlying old sediment, but also draws P out of the overlying fresh sediment, thus reducing P release from the sediment15,16. More recently, the use of high-resolution dialysis (HR-Peeper) and diffusive gradient in thin films (DGT) techniques for investigating the P mobilization processes in sediments had achieved great progress9,14,17,18.
The sediment plays a great role in the overall P dynamics of water bodies-it may either act as a sink to adsorb P or an internal source to release P on the base of concentration gradients19. Reducing internal P loading in sediments has been proposed as an essential technique for eutrophication control20,21.
The techniques for reducing the release of sediment P are either ex-situ or in-situ techniques. Sediment dredging, which could reduce P from sediment permanently, has been widely applied to control sediment P in lakes22,23. Nevertheless, dredging may destroy the lake ecosystems and enhance the risk in contaminants resuspension, nor are they cost-effective. Therefore, in-situ techniques for reducing the sediment internal P loading have received increasing attention in recent years.
Many in-situ techniques have been applied to reduce internal P loading in sediment, including in-situ capping24,25, hypolimnetic aeration26,27, phytoremediation28,29, and in-situ physicochemical adsorption30,31, etc. Among these, in-situ physicochemical adsorption turns out to be an efficient technique for controlling eutrophication in lakes. The selection of an effective in-situ adsorbent materials, which should be environmentally friendly, geographically available, and economically feasible, is critical for the in-situ physicochemical adsorption technology. Some natural or modified clay minerals selected as P adsorbent materials have been applied to reduce the sediment internal P loading.
Maifanite is a kind of natural clay minerals with an eco-friendly characteristic, which is abundant in China32,33. Maifanite has great surface area and strong adsorption capacity due to the vesicular pores and sponge shaped morphological structure34,35. It could adsorb P via chemisorption due to the aluminum (Al) and iron (Fe), etc. in the maifanite36. The market price of raw maifanite (RMF) is about 300–400 yuan (¥)/t. Due to its low cost and high capability, maifanite has been applied to soil improvement35, which contains amino acid and some trace elements, and could be further combined with ecological remediation. The adsorption capacity of RMF material is usually limited, attributed to the presence of impurity and the permanent negative charges due to isomorphous substitution effect37. Thus, there is a need to modify RMF to enhance its confined capacity of adsorption.
Here, RMF granules were modified by acidification, alkalization, salinization, calcination and combined modifications, respectively. Modified maifanite (MMF) granules were prepared and tested as promising in-situ physicochemical adsorbent materials to adsorb sediment P in all fractions. This study investigated the adsorptive effects of sediment P in all fractions with MMF for the first time. The specific objectives of the study were to explore the optimal modification methods of maifanite applied as adsorbent material and investigate the adsorption effects and mechanisms of MMF on sediment P in West Lake, Hangzhou, China.
Results and discussion
Analysis of sediment characteristics
The quantities of TP, IP, OP, Fe/Al-P and Ca-P in sediment from West Lake were 1652.31 mg·kg−1, 1022.29 mg·kg−1, 630.02 mg·kg−1, 494.45 mg·kg−1 and 499.79 mg·kg−1, respectively. This illustrated the internal P loading, which was mainly due to the quantities of Fe/Al-P and Ca-P, in West lake was volatile and at the risk of P release. Additionally, the values of CEC and pH of lake sediments were 52.4 meq/100 g and 7.39, respectively.
Adsorption capacities of various MMF samples
Compared with the RMF, MMF samples exhibited higher adsorption capacities (Fig. 1). The modification could improve the adsorption capacity of RMF. MMF-H2.5, MMF-OH3.0, MMF-La5.0 and CMMF-400 were the optimal MMF samples among all acidification, alkalization, salinization and calcination MMF samples, respectively. The adsorption quantities of sediment TP by RMF, MMF-H2.5, MMF-OH3.0, MMF-La5.0 and CMMF-400 were 284.84 mg·kg−1, 318.35 mg·kg−1, 308.29 mg·kg−1, 311.644 mg·kg−1 and 304.94 mg·kg−1, respectively. The corresponding adsorption rates were 17.24%, 19.27%, 18.66%, 18.86%, and 18.46%, respectively. Based on these results, MMF-H2.5, MMF-OH3.0 and MMF-La5.0 samples were further calcined at 400 °C to obtain the combined MMF samples, named as CMMF-H2.5-400, CMMF-OH3.0–400 and CMMF-La5.0–400, respectively. The adsorption quantities of sediment TP by CMMF-H2.5-400, CMMF-OH3.0–400 and CMMF-La5.0–400 were 331.75 mg·kg−1, 314.99 mg·kg−1, and 321.7 mg·kg−1, respectively. The corresponding adsorption rates were 20.08%, 19.06% and 19.45, respectively. CMMF-H2.5-400 exhibited the highest adsorption capacity. Thus, CMMF-H2.5-400 was selected as the optimal adsorption material in the following experiments.
Characterization of RMF and MMF
The XRF results (Table 1) showed that there were significant differences in the chemical compositions of RMF and various MMF samples, which were mainly composed of SiO2, Al2O3, Na2O, CaO and Fe2O3. The modification treatment resulted in an obvious increase in the content of SiO2 and a significant decrease in MgO and P2O5 of MMF samples. Typically, SiO2 and Al2O3 were the major compositions of these maifanite samples. Compared to the RMF, the content of Na2O in MMF-OH3.0 was increased. It indicated Na ion from 3.0 mol/L NaOH was intercalated in the layers of the RMF after the NaOH modification. This was also confirmed by XRD analyses.
FTIR is a supporting tool to distinguish characteristic functional groups38,39. In the spectrum of RMF and MMF samples (Fig. 2), a broad intense peak near 3430 cm−1 was due to the stretching vibrations of O-H and N-H groups39. The broad peak at 3430 cm−1 in RMF was shifted to 3423 cm−1, 3435 cm−1, 3413 cm−1, 3435 cm−1 and 3432 cm−1 in MMF-H2.5, MMF-OH3.0, MMF-La5.0, MMF-400, and CMMF-H2.5-400, respectively, suggesting that interfacial interaction between chemical reagent of the modification treatments and maifanite surface, and this was consistent with XRD results (Fig. 3). In the FTIR spectrum of the various maifanite samples, a prominent band at 1035 cm−1 could be assigned to a fundamental frequency of the PO43− stretching40. The peak at 777 cm−1 was assigned to Mg-Fe-OH41, and it remained unchanged after the modification treatments. The peak at 589 cm−1, probably assigned to the Fe-O bands42, was obviously unchanged, although with a low intensity, in the MMF samples.
XRD analyses of various maifanite samples were carried out to discuss the crystal structure and identity. XRD patterns (Fig. 3) revealed that the RMF and various MMF samples mainly contained Quartz (SiO2) and Margarite (CaAl2(Si2Al2)O10(OH)2). Additionally, it is obvious that the d001 value increased after the modification treatment (Table 2), and this result was agreement with the previous results43. Comparing the intensity of obvious diffraction peaks of RMF with MMF samples, there was no significant change. No obvious peaks of metal oxide were observed in the maifanite diffractograms, which indicated that the maifanite structures remained intact after the modification treatment and the metal oxide was well dispersed on the surface of maifanite44. XRD patterns (Fig. 3(a,e,f)) of maifanite before and after calcining at 400 °C indicated that their main mineral diffraction peak position remained unchanged. It indicated that 400 °C was the appropriate temperature on calcination. The result was in accordance with that of Yang et al. (2011), who reported that the main mineral diffraction peak position of maifanite did not change after calcining at 500 °C45. On the other hand, some peaks were disappeared and weakened a little after the modification treatment, which might be caused by the decrease of impurity after the modification treatment. This was consistent with BET and FTIR results.
To compare the morphology of RMF with MMF samples, the SEM analysis were performed. It was seen that the morphology of MMF samples changed obviously due to the modification treatment (Fig. 4). The surface of the RMF was smooth, and few pores were observed. Comparing with the RMF, the surface of the MMF samples was rougher and more pores were obtained, which indicated that a porous structure with irregularly defined channel was formed. Additionally, there were more flakes appeared in MMF samples. The SEM micrographs of MMF-H2.5 (Fig. 4b), MMF-OH3.0 (Fig. 4c), MMF-La5.0 (Fig. 4d) and CMMF-H2.5-400 (Fig. 4f) showed that the activation of MMF samples resulted in smaller grain sizes caused by the dispersive effect of H+, Na+, La3+, respectively, on the MMF-H2.5, MMF-OH3.0, MMF-La5.0, and CMMF-H2.5-400 structures46,47,48. Calcination led to microporous, followed by the removal of surface water, bound water and water of hydration of CMMF-400 (Fig. 4e) and CMMF-H2.5-400 (Fig. 4f)49,50. These changes could improve the reactivity of maifanite and impart a higher capacity of adsorption.
Generally, the BET equation has been applied to measure and compare the specific surface areas of a variety of porous materials51. The BET surface area was regarded as an important factor in determining the pore properties of the adsorbent materials42. The pHPZC, CEC, the maifanite basal plane diffractions d001, the specific surface (SBET), the total pore volume (Vt), the volume of micropores (Vmikro), the external surface (Sexternal) and the average pore size (Dp) before and after the modification were given in Table 2. The results suggested that the modification caused the disintegration of maifanite structural. Based on these, it led to a significant increase in the SBET and an obvious decrease in the Dp. It could provide more active sites for the adsorption reaction, and made the surface more available for the sediment P. These findings supported the SEM results. The pHPZC of sorbents depended on various factors, including crystallinity nature, Si/Al ration, operation temperature and sorption capacity of the electrolytes, contents of impurity and degree of H+ and OH− ions adsorption, etc. Thus, it might vary from adsorbent to adsorbent. Chutia et al.52 revealed that pHPZC had a significant impact in As(V) adsorption by natural zeolites. That’s because the adsorption of multivalent cation occurred effectively at a pH below pHPZC. Compared to the RMF, the pHPZC values of MMF-H2.5, MMF-OH3.0, MMF-La5.0, CMMF-400 and CMMF-H2.5-400 were increased in different degrees, respectively. On the other hand, The CEC of MMF samples was found to be higher than RMF, and the CEC of CMMF-H2.5-400 was the maximum. The above information revealed that modification treatments could improve the sediment P adsorption capacity of maifanite.
P adsorption on maifanite by dynamic experiments
Effect of maifanite dosage
The amount of the sorbent dosage plays a vital role in sediment P adsorption. Experiments were carried out with various dosages of RMF and CMMF-H2.5-400, respectively at 20 ± 2 °C, pH 7.0 ± 0.2 and shaken at 200 rpm for 12 h to investigate the effects of maifanite dosage. Figure 5a,b indicated that the adsorption effects on sediment P by CMMF-H2.5-400 were better than RMF, with the tendency of increased at first then decreased and stabilized with an increase of dosage (Fig. 5b). Compared to the RMF, CMMF-H2.5-400 showed more considerable micropore adsorption and higher ion exchange capacity due to the more microporous microstructure and superior charge number31. Figure 5a indicated that the adsorption quantity of P from the sediment increased with an increase of RMF dosages. The quantity of adsorption sites becomes more availability with an increase of sorbent dosage53,54. From Fig. 5b, the adsorption quantity of P first increased and then decreased with the increasing of CMMF-H2.5-400 dosages. Typically, the adsorption of P didn’t have an immense change when CMMF-H2.5-400 was more than 4 g. This might be due to saturation between CMMF-H2.5-400 and P 55. The highest adsorption quantities for RMF and CMMF-H2.5-400 were found at 12 g and 2 g, respectively. The adsorption amounts of TP, IP, OP, Fe/Al-P and Ca-P by CMMF-H2.5-400 (2 g dosage) were 444.01 mg·kg−1, 343.44 mg·kg−1, 100.56 mg·kg−1, 195.87 mg·kg−1 and 131.53 mg·kg−1, respectively. The corresponding adsorption rates were 26.87%, 33.60%, 15.96%, 39.61% and 26.32%, respectively. The adsorption amounts of TP, IP, OP, Fe/Al-P and Ca-P by RMF (12 g dosage) were 360.23 mg·kg−1, 289.83 mg·kg−1, 70.41 mg·kg−1, 185.31 mg·kg−1 and 100.53 mg·kg−1, respectively. The corresponding adsorption rates were 21.80%, 28.35%, 11.18%, 37.48% and 20.12%, respectively. Based on the above results, optimal dosages were fixed as 2 g and 12 g, respectively for CMMF-H2.5-400 and RMF and pursued in further investigations.
Effect of stirring time
To investigate the effects of stirring time on P adsorption by maifanite, the experiments were carried out with 2 g CMMF-H2.5-400 or 12 g RMF at 20 ± 2 °C, pH 7.0 ± 0.2 and shaken at 200 rpm. Figure 5c,d presented the results. After the initial rapid reaction, the adsorption quantities of sediment P by CMMF-H2.5-400 or RMF decreased gradually. The P adsorption amounts by CMMF-H2.5-400 and RMF respectively increased from 2 h to 4 h and then decreased after 4 h. The adsorption amount of P from sediment reached the maximum at 4 h by CMMF-H2.5-400 and RMF, respectively. Thus, 4 h was chosen as the optimal stirring time to investigate the effects of pH and operation temperature on the P adsorption by CMMF-H2.5-400 and RMF, respectively. Especially, the adsorption quantities of IP and Fe/Al-P by CMMF-H2.5-400 and RMF increased markedly (P < 0.05), respectively.
Influence of pH
The operation pH is a key factor that controls the P adsorption from sediments56. To investigate the influence of extremely high or low pH value on adsorption of sediment P, the experiments were carried out at different pH conditions ranged from 2.0 to 12.0. Figure 5e,f confirmed that the operation pH influenced the adsorption capacity: the adsorption of TP by CMMF-H2.5-400 reached the maximum at the optimal pH (pHopt) 2.0 and decreased with the increasing pH value. The adsorption of TP by RMF increased with the increasing pH (2.0–6.0), then decreased when pH exceeded 6.0 (P < 0.05). The adsorption amounts of TP, IP, OP, Fe/Al-P and Ca-P by CMMF-H2.5-400 at pHopt 2.0 were 604.86 mg·kg−1, 440.62 mg·kg−1, 164.23 mg·kg−1, 126.67 mg·kg−1 and 290.70 mg·kg−1, respectively. The corresponding adsorption rates were 36.61%, 43.10%, 26.07%, 25.62% and 58.16%, respectively. The adsorption amounts of TP, IP, OP, Fe/Al-P and Ca-P by RMF at pHopt 6.0 were 514.38 mg·kg−1, 373.60 mg·kg−1, 140.78 mg·kg−1, 188.83 mg·kg−1 and 161.69 mg·kg−1, respectively. The corresponding adsorption rates were 31.13%, 36.55%, 22.35%, 38.19% and 32.35%, respectively. When the pH value increased from 2.0 to 12.0, the adsorption quantity of Ca-P by CMMF-H2.5-400 and RMF, respectively, decreased immensely (P < 0.05) while the adsorption amount of Fe/Al-P was the highest in alkaline conditions (P < 0.05). These results were agreement with the previous reports31,57. The effects of P adsorption in various pH were due to a series of mechanisms, including chemical interaction, ligand exchange, electrostatic attraction/repulsion and coagulation/precipitation58.
Effect of temperature
Operation temperature is a significant factor influencing the P adsorption in sediment, which could remarkably improve p release59,60. Shallow lakes are usually isothermal, and the sediment is susceptible to temperature variations61. Thus, the temperature may have a larger influence on adsorption P in sediment from shallow lakes. The results were depicted in Fig. 5g,h. As temperatures increased from 5 °C to 20 °C, the P adsorption efficiencies of CMMF-H2.5-400 and RMF, respectively, increased remarkably (P < 0.05). High temperatures facilitated the P adsorption confirming that the sediment P adsorption on the maifanite samples was an endothermic reaction. This result was agreement with the previous reports61,62. The adsorption amounts of TP, IP, OP, Fe/Al-P and Ca-P by CMMF-H2.5-400 at 20 °C were 614.91 mg·kg−1, 454.03 mg·kg−1, 160.88 mg·kg−1, 129.01 mg·kg−1 and 301.59 mg·kg−1, respectively. The corresponding adsorption rates were 37.22%, 44.41%, 25.54%, 26.09% and 60.34%, respectively. On the other hand, the adsorption amounts of TP, IP, OP, Fe/Al-P and Ca-P by RMF at 20 °C were 521.08 mg·kg−1, 390.36 mg·kg−1, 130.72 mg·kg−1, 194.69 mg·kg−1 and 175.93 mg·kg−1, respectively. The corresponding adsorption rates were 31.54%, 38.18%, 20.75%, 39.38% and 35.20%, respectively. Additionally, the adsorption quantities of P in all fractions decreased in various degrees above 20 °C. The results could be explained that the process of desorption as well as the Brownian movement were enhanced due to the high temperature59,60.
Static adsorption experiments
To simulate the P adsorption under in-situ treatment, static experiments were carried out with time from 0 d to 30 d. Figure 6 depicted the adsorption of sediment P by RMF and CMMF-H2.5-400, respectively, under static conditions. The P adsorption on CMMF-H2.5-400 included quick, slow and dynamic balance adsorption steps (P < 0.05). Firstly, the quick adsorption step mainly occurred from 0 d to 10 d, and then followed by a slower second step (10 d–18 d). Furthermore, there was no obvious difference in adsorption quantities of P in all fractions from the sediment after 18 d (Fig. 6b). The adsorption quantity of sediment P by CMMF-H2.5-400 reached the peak value at 18 d. On the other side, the amounts of P adsorption on RMF increased rapidly within 20 d and then decreased slowly. Finally, the adsorption amounts of P barely achieved to a real equilibrium within the selected time (P < 0.05). The adsorption quantities of sediment P by RMF reached the maximum at 20 d (Fig. 6a). The adsorption amounts of TP, IP, OP, Fe/Al-P and Ca-P by CMMF-H2.5-400 at 18 d were 568 mg·kg−1, 433.92 mg·kg−1, 134.07 mg·kg−1, 341.30 mg·kg−1 and 85.45 mg·kg−1, respectively. The corresponding adsorption rates were 34.38%, 42.45%, 21.28%, 69.03% and 17.10%, respectively. On the other hand, the adsorption quantities of TP, IP, OP, Fe/Al-P and Ca-P by RMF at 20 d were 457.41 mg·kg−1, 296.53 mg·kg−1, 147.48 mg·kg−1, 224.01 mg·kg−1 and 68.70 mg·kg−1, respectively. The corresponding adsorption rates were 27.68%, 29.01%, 23.41%, 45.31% and 13.75%, respectively. Figure 6 also showed that the P adsorption capacity of CMMF-H2.5-400 was higher than RMF. Furthermore, it indicated that the modification treatment could improve the P adsorption capacity of maifanite, and this result was in agreement with our previous study, which reported that the P adsorption capacity of modified bentonite granules (MBGs) was higher than raw bentonite granules (RBGs)31.
Characterization of maifanite after adsorption
Ion-exchange occurred and altered the elements content of CMMF-H2.5-400 and RMF, respectively, during the adsorption process (Table 3). The contents of SiO2, Fe2O3, MgO, K2O, TiO2 and P2O5 were increased respectively. However, the contents of Al2O3, CaO, Na2O and P2O5 were decreased respectively. Figure 7(A) depicted the FTIR spectra of CMMF-H2.5-400 and RMF after adsorption. Comparing the spectrum of CMMF-H2.5-400 after adsorption with that of CMMF-H2.5-400 before adsorption (Fig. 2b), a new adsorption peak emerged at 1393 cm−1, which referred to the O-H bending vibration with Fe (III), Al (III) species present on the surface of CMMF-H2.5-400 after adsorption51. It indicated that Fe (III), Al (III) species were intercalated into interlayers of CMMF-H2.5-400 by adsorption process. Additionally, the peaks of CMMF-H2.5-400 at 3432 cm−1, 1634 cm−1 and 1093 cm−1 were shifted to 3413 cm−1, 1627 cm−1 and 1085 cm−1, respectively. For the RMF, a new adsorption peak emerged at 3568 cm−1, which were attributed to broad OH-stretching in RMF after adsorption. On the other hand, the peaks of RMF at 3430 cm−1 and 776 cm−1 were shifted to 3420 cm−1 and 778 cm−1, respectively. Comparing the Fig. 7(A) with Fig. 2, it could be seen that the peaks observed on the maifanite samples were obviously unchanged after adsorption. XRD patterns of RMF and CMMF-H2.5-400 after adsorption were shown in Fig. 7(B). Comparing the intensity of obvious diffraction peaks of maifanite before and after adsorption, a reasonable shifting of peaks was observed from 20 to 70° 2 theta indicating that the adsorption of sediment P on maifanite granules changed the peaks of chemical composition intensities on the maifanite granules. According to the XRD spectra, it was thought that there was a ligand exchange between sediment P in all fractions and maifanite granules. The results of XRD in Figs 3 and 7(B) clearly reveal the presence of phosphate salts on the structure of adsorbent material after the adsorption process63. The d001 values of CMMF-H2.5-400 and RMF were 3.73 nm and 3.07 nm, respectively, before adsorption (Table 2), and then increased to 3.91 nm and 3.13 nm after adsorption, respectively (Table 4). SEM images were used to examine the surface morphology of RMF and CMMF-H2.5-400 before and after sediment P adsorption, respectively. Figure 7(C) exhibited the SEM images of RMF and CMMF-H2.5-400 after adsorption. Comparing the SEM images of maifanite samples before and after adsorption, some rough exterior and fresh cavities emerged after adsorption. The micrograph obtained after adsorption indicated that the flakes of the phosphate were observed on the adsorbent surface (Fig. 7(C))64,65. Furthermore, the pores of the particles of the adsorbent have been covered with adsorbate63. After the adsorption process, the SEM micrographs of CMMF-H2.5-400 and RMF revealed the formation of metal-hydroxyl-phosphate ligand (Yang et al., 2009). Table 4 confirmed that adsorption caused the disintegration of maifanite structural and led to a significant increase in the SBET. These findings supported the SEM results.
Phosphate is adsorbed onto clay minerals via electrostatic, ligand exchange, and Lewis acid-base interaction66,67,68. Surface hydroxyl groups are protonated in the ligand exchange process at low pH. That’s because, compared to the hydroxyl groups, -OH2+ is easier to displace from the metal binding sites43. Therefore, it was likely that the adsorption of phosphate onto CMMF-H2.5-400 mainly using ligand exchange. This result was in agreement with our previous study, which reported that MBG adsorbed phosphorus mainly by anionic coordination exchange adsorption31. On the CMMF-H2.5-400 samples, phosphate replaced the hydroxyl groups, which were then released into the solution. The adsorption of phosphate could be speculated to take place as follows: the phosphate in the sediment was first transferred to the sites on the adsorbent; then, chemical complexation/ion exchange occurred at the active sites69,70.
Comparing the SEM images of the CMMF-H2.5-400 before and after adsorption process, we observed an aggregated morphology and some large flakes in CMMF-H2.5-400 samples after adsorption process. Additionally, the size of the intra-particle voids was decreased due to a stacking structure formed by some thin lamellas (Table 4). These results revealed that phosphate did adsorb onto the CMMF-H2.5-400 surface and it could be combined in the form of oxygen bridge43,63. Meanwhile, the hydroxyl and hydration base could be swop out31.
In this study, MMF samples were prepared by various modification methods and applied to adsorb sediment P in all fractions for the first time. The results revealed that the modification treatment could improve the adsorption capacity of maifanite and CMMF-H2.5-400 was selected as the optimal in-suit adsorption material. The results of adsorption experiments showed that the dosage of maifanite, adsorption time, operation pH and operation temperature were the main factors influencing the adsorption performance on sediment P of CMMF-H2.5-400. Under the optimal conditions of dynamic experiments, the adsorption rates of TP, IP, OP, Fe/Al-P and Ca-P by CMMF-H2.5-400 were 37.22%, 44.41%, 25.54%, 26.09% and 60.34%, respectively. The adsorption mechanisms analyses revealed that the adsorption of phosphate onto CMMF-H2.5-400 mainly by ligand exchange. The above information indicated that CMMF-H2.5-400 exhibited a promising adsorption capacity on sediment P and could be further applied to reduce internal P loading in the eutrophic lakes. Furthermore, a combined technology of MMF and other ecological methods would be a significative orientation to treat sediment P.
Study site and sampling
West Lake (30°14′45′′N, 120°08′30′′E) is located on the western side of Hangzhou City, China. West Lake, which has been listed in the World Heritage Site in 2011, is a typical eutrophic lake with an area of 6.5 km2 and a mean depth of 2.27 m30. The sediment in West Lake is unstable, at the risk of releasing P to West lake71. Currently, developing and applying an effective in-situ technology for sediment P control was urgent.
The sampling site is located in a severe eutrophic region (30°23′16′′N, 120°13′18′′E) in Xiaonan Lake, one sub lake of West Lake. The surface lake sediments, at a depth of 0–10 cm, were collected by a Peterson grab sampler (model HNM1-2) on May 14th, 2017. The sediment samples were then stored in plastic bags. After transportation to the laboratory, the sediment samples were air-dried. The content of TP, TN, NH4+-N and NO2-N of overlying water above sediments in the lake was 0.06 ± 0.01 mg/L, 3.57 ± 0.03 mg/L, 0.15 ± 0.02 mg/L and 0.12 ± 0.01 mg/L, respectively. The pH values of the interstitial water and overlying water were 8.07 and 7.9, respectively.
Preparation of MMF
RMF (3–5 mm in diameter, gray-white colour) granules were purchased from Kangyuan maifanite factory in mengyin country, Shandong Province, China. Firstly, the RMF granules were soaked in deionized water for 10 h and then washed with deionized water until the pH value reached 7.0. After that, the samples were dried at 105 °C for 24 h. Finally, the samples were cooled to room temperature for further studies, which were used as RMF. To improve the sediment P adsorption capacity of RMF, acidification, alkalization, salinization, calcination and combined modifications were used to modify the RMF granules, respectively. The preparation of various MMF samples was listed in Table 5.
To explore the optimal modification method of RMF, 5 g sediment samples and 8 g various MMF samples were added to Erlenmeyer flasks, containing 250 mL 0.02 mol/L KCl solution with pH 7.0 ± 0.2, then shaken at 200 rpm for 12 h in a thermostatic shaker (Shanghai Boxun Medical Equipment Plant, China) at 20 ± 2 °C. After the adsorption process, the mixture was filtered through a steel screen (60 mesh) to remove maifanite granules. The sediment was then dried in an oven at 55 °C for 24 h. Each treatment consisted of three replicates.
Dynamic adsorption experiments
Dynamic adsorption experiments were carried out in thermostatic bottle shakers. Typically, 250 mL KCl solution (0.02 mol/L) was poured into Erlenmeyer flasks, and then 5 g sediment samples and different dosages (1 g, 2 g, 4 g, 6 g, 8 g, 10 g and 12 g) of maifanite samples (RMF and MMF, respectively) were added into the Erlenmeyer flasks. After that, they were shaken at 200 rpm for certain hours (2 h, 4 h, 6 h, 8 h, 10 h, 12 h and 15 h) at different pH (2.0–12.0). The dynamic adsorption experiments were carried out at temperatures of 5 °C, 10 °C, 20 °C, 30 °C, 40 °C, 50 °C, and 60 °C. Two drops of 0.1% chloroform were added in each Erlenmeyer flask to inhibit bacterial activity.
Static adsorption experiments
Static adsorption experiments were carried out in Erlenmeyer flasks with pH 7.0 ± 0.2 in the dark condition for 0–30 d at 20 ± 2 °C. A certain quantity of maifanite (12 g RMF and 2 g CMMF-H2.5-400, respectively) and 5 g sediment samples were added to Erlenmeyer flasks. Two drops of 0.1% chloroform were added in each Erlenmeyer flask to inhibit bacterial activity.
The Standards and Measurements and Testing (SMT) protocol72 were used for determining P fractions. The P fractions can be characterized as TP (total P), IP (inorganic P), OP (organic P), Fe/Al-P (P bound to Al, Fe, and manganese (Mn) oxides extracted by NaOH) and Ca-P (P bound to calcium (Ca) extracted by HCl). The presence of metals in sediment can mediate the transport of P. Each P fraction concentration was measured directly using the ammonium molybdate spectrophotometric method with an UV-visible spectrophotometer at 700 nm (DR4000/U, HACH company, USA). The cation exchange capacity (CEC) of the sediment samples was analyzed using NH4Cl-NH4OAc method. Sediment pH was measured in 1:10 (w/v) solid/water suspensions by a PHS-3C digital pH meter (Shanghai LeiCi instrument plant, China).
The chemical compositions of RMF and MMF samples were determined by X-ray fluorescence (XRF, RU-200B/D/MAX-RB RU-200B, China). Fourier transform infrared (FTIR) spectra of the RMF and MMF samples were measured by a FTIR spectrometer (Nicolet6700, USA) in the wavenumber range of 400–4000 cm−1. The mineralogical and chemical compositions of the lake RMF and MMF samples were determined by X-ray diffractometer (XRD, RU-200B/D/MAX-RB RU-200B, Japan) operating with CuKα radiation (30 kV, 15 mA) over the range (2 Theta) of 5–70°. The microstructure of RMF and MMF samples was characterized by scanning electron microscope (SEM, JSM-5610LV, Japan). The CEC of maifanite samples, which was defined by the ability of maifanite granules to adsorb the cations, was analyzed using the ammonium acetate method. The specific surface areas were calculated by nitrogen adsorption using the Brunauer-Emmett-Teller (BET) equation on an analyzer (ASAP 2020 M, America). The t-plot method was applied to gain the volume of micropores and the surface of mesopores together with the external surface. The total pore volume was derived from the nitrogen volume adsorbed at the relative pressure p/p0 → 1 73. The batch equilibrium techniques were applied to estimate the points of zero charge (pHpzc) of maifanite samples52.
All the chemicals and reagents used were analytical grade. All glassware and sample bottles were presoaked before use in diluted HCl solution for at least 12 h followed by washing with deionized water and drying in oven. Deionized water was used for preparing solutions.
The amount of P adsorbed on the maifanite granules and the adsorbed efficiency (A) were calculated using the following equations:
where q is the adsorption quantity of P per unit weight of maifanite samples (mg·kg−1), and q0 and qe (mg·kg−1) are the initial and final P quantity, respectively.
All treatments were conducted in triplicate. OriginPro 8.0 (OriginLab Corporation, Northampton, MA, USA) was used to plot various figures. All statistical analyses were estimated using SPSS 18.0 (SPSS software, IBM, USA). Analyses of the variance (ANOVA, one factor) were applied to test the significant differences between the dependent variables (the adsorption quantity of P) and independent variables (the corresponding adsorption parameter). The difference was considered statistically significant when the significance level was smaller than 0.05.
Li, H., Song, C. L., Cao, X. Y. & Zhou, Y. Y. The phosphorus release pathways and their mechanisms driven by organic carbon and nitrogen in sediments of eutrophic shallow lakes. Sci. Total Environ. 572, 280–288 (2016).
Feng, W. et al. Forms and Lability of Phosphorus in Algae and Aquatic Macrophytes Characterized by Solution 31 P NMR Coupled with Enzymatic Hydrolysis. Sci. Rep. 6, 37164 (2016).
Schindler, D. W. et al. Eutrophication of lakes cannot be controlled by reducing nitrogen input: Results of a 37-year whole-ecosystem experiment. Proc. Natl. Acad. Sci. 105, 11254–11258 (2008).
Jia, B. et al. Impact of Fish Farming on Phosphorus in Reservoir Sediments. Sci. Rep. 5, 16617 (2015).
Conley, D. J. et al. Controlling Eutrophication: Nitrogen and Phosphorus. Science 323, 1014–1015 (2009).
Ding, S. et al. Internal phosphorus loading from sediments causes seasonal nitrogen limitation for harmful algal blooms. Sci. Total Environ. 625, 872–884 (2018).
Abell, J. M., Özkundakci, D. & Hamilton, D. P. Nitrogen and Phosphorus Limitation of Phytoplankton Growth in New Zealand Lakes: Implications for EutrophicationControl. Ecosystems 13, 966–977 (2010).
Lewis, W. M., Wurtsbaugh, W. A. & Paerl, H. W. Rationale for control of anthropogenic nitrogen and phosphorus to reduce eutrophication of inland waters. Environ. Sci. Technol. 45, 10300–10305 (2011).
Ding, S. et al. Synergistic adsorption of phosphorus by iron in lanthanum modified bentonite (Phoslock®): New insight into sediment phosphorus immobilization. Water Res. 134, 32–43 (2018).
Ding, S. et al. In situ, high-resolution evidence for iron-coupled mobilization of phosphorus in sediments. Sci. Rep. 6, 1–11 (2016).
Smolders, E. et al. Internal Loading and Redox Cycling of Sediment Iron Explain Reactive Phosphorus Concentrations in Lowland Rivers. Environ. Sci. Technol. 51, 2584–2592 (2017).
Wang, P. et al. Impact of macrozoobenthic bioturbation and wind fluctuation interactions on net methylmercury in freshwater lakes. Water Res. 124, 320–330 (2017).
Pearce, A. R., Rizzo, D. M., Watzin, M. C. & Druschel, G. K. Unraveling associations between cyanobacteria blooms and in-lake environmental conditions in Missisquoi Bay, Lake Champlain, USA, using a modified self-organizing map. Environ. Sci. Technol. 47, 14267–14274 (2013).
Wang, Y. et al. Static layer: A key to immobilization of phosphorus in sediments amended with lanthanum modified bentonite (Phoslock®). Chem. Eng. J. 325, 49–58 (2017).
Lewandowski, J., Schauser, I. & Hupfer, M. Long term effects of phosphorus precipitations with alum in hypereutrophic Lake Süsser See (Germany). Water Res. 37, 3194–3204 (2003).
Yin, H., Du, Y., Kong, M. & Liu, C. Interactions of riverine suspended particulate matter with phosphorus inactivation agents across sediment-water interface and the implications for eutrophic lake restoration. Chem. Eng. J. 327, 150–161 (2017).
Ding, S. et al. Reactivation of phosphorus in sediments after calcium-rich mineral capping: Implication for revising the laboratory testing scheme for immobilization efficiency. Chem. Eng. J. 331, 720–728 (2018).
Ding, S., Xu, D., Sun, Q., Yin, H. & Zhang, C. Measurement of dissolved reactive phosphorus using the diffusive gradients in thin films technique with a high-capacity binding phase. Environ. Sci. Technol. 44, 8169–8174 (2010).
Yuan, S. et al. Spatial variability of phosphorus adsorption in surface sediment at channel confluences: Field and laboratory experimental evidence. J. Hydro-Environment Res. 18, 25–36 (2018).
Dithmer, L. et al. Responses in sediment phosphorus and lanthanum concentrations and composition across 10 lakes following applications of lanthanum modified bentonite. Water Res. 97, 101–110 (2016).
Zhu, Y. et al. Characterization of organic phosphorus in lake sediments by sequential fractionation and enzymatic hydrolysis. Environ. Sci. Technol. 47, 7679–7687 (2013).
Choi, Y. et al. Secondary environmental impacts of remedial alternatives for sediment contaminated with hydrophobic organic contaminants. J. Hazard. Mater. 304, 352–359 (2016).
Yu, J. et al. Evaluation of in situ simulated dredging to reduce internal nitrogen flux across the sediment-water interface in Lake Taihu, China. Environ. Pollut. 214, 866–877 (2016).
Yin, H. & Kong, M. Reduction of sediment internal P-loading from eutrophic lakes using thermally modified calcium-rich attapulgite-based thin-layer cap. J. Environ. Manage. 151, 178–185 (2015).
Douglas, G. B., Lurling, M. & Spears, B. M. Assessment of changes in potential nutrient limitation in an impounded river after application of lanthanum-modified bentonite. Water Res. 97, 47–54 (2015).
Gerling, A. B. et al. First report of the successful operation of a side stream supersaturation hypolimnetic oxygenation system in a eutrophic, shallow reservoir. Water Res. 67, 129–143 (2014).
Pourabadehei, M. & Mulligan, C. N. Resuspension of sediment, a new approach for remediation of contaminated sediment. Environ. Pollut. 213, 63–75 (2016).
Perelo, L. W. Review: In situ and bioremediation of organic pollutants in aquatic sediments. J. Hazard. Mater. 177, 81–89 (2010).
Wang, C. et al. Synergistic removal effect of P in sediment of all fractions by combining the modified bentonite granules and submerged macrophyte. Sci. Total Environ. 626, 458–467 (2018).
Zhang, Y., He, F., Xia, S., Zhou, Q. & Wu, Z. Studies on the treatment efficiency of sediment phosphorus with a combined technology of PCFM and submerged macrophytes. Environ. Pollut. 206, 705–711 (2015).
Liu, Z. et al. Adsorption performance of modified bentonite granular (MBG) on sediment phosphorus in all fractions in the West Lake, Hangzhou, China. Ecol. Eng. 106, 124–131 (2017).
Chen, C. et al. Evaluation of an up-flow anaerobic sludge bed (UASB) reactor containing diatomite and maifanite for the improved treatment of petroleum wastewater. Bioresour. Technol. 243, 620–627 (2017).
Li, H. et al. Simultaneous determination of ultratrace lead and cadmium by square wave stripping voltammetry with in situ depositing bismuth at Nafion-medical stone doped disposable electrode. J. Hazard. Mater. 191, 26–31 (2011).
Huang, H., He, L., Lei, Z. & Zhang, Z. Contribution of precipitates formed in fermentation liquor to the enhanced biogasification of ammonia-rich swine manure by wheat-rice-stone addition. Bioresour. Technol. 175, 486–493 (2015).
Zhao, H. et al. In situ anchor of magnetic Fe3O4nanoparticles onto natural maifanite as efficient heterogeneous Fenton-like catalyst. Front. Mater. Sci. 10, 300–309 (2016).
Pan, G. et al. In-lake algal bloom removal and submerged vegetation restoration using modified local soils. Ecol. Eng. 37, 302–308 (2011).
Tsai, W. T., Hsien, K. J. & Lai, C. W. Chemical activation of spent diatomaceous earth by alkaline etching in the preparation of mesoporous adsorbents. Ind. Eng. Chem. Res. 43, 7513–7520 (2004).
Mandal, A., Biswas, B., Sarkar, B., Patra, A. K. & Naidu, R. Surface tailored organobentonite enhances bacterial proliferation and phenanthrene biodegradation under cadmium co-contamination. Sci. Total Environ. 550, 611–618 (2016).
Hu, P., Wang, J. & Huang, R. International Journal of Biological Macromolecules Simultaneous removal of Cr (VI) and Amido black 10B (AB10B) from aqueous solutions using quaternized chitosan coated bentonite. Int. J. Biol. Macromol. 92, 694–701 (2016).
Gogoi, S., Nath, S. K., Bordoloi, S. & Dutta, R. K. Fluoride removal from groundwater by limestone treatment in presence of phosphoric acid. J. Environ. Manage. 152, 132–139 (2015).
Chinoune, K., Bentaleb, K., Bouberka, Z., Nadim, A. & Maschke, U. Applied Clay Science Adsorption of reactive dyes from aqueous solution by dirty bentonite. Appl. Clay Sci. 123, 64–75 (2016).
Tsai, W. T. et al. Preparation of mesoporous solids by acid treatment of a porphyritic andesite (wheat-rice-stone). Microporous Mesoporous Mater. 102, 196–203 (2007).
Yan, L. G. et al. Adsorption of phosphate from aqueous solution by hydroxy-aluminum, hydroxy-iron and hydroxy-iron-aluminum pillared bentonites. J. Hazard. Mater. 179, 244–250 (2010).
Ni, Y. et al. Aromatization of methanol over La/Zn/HZSM-5 catalysts. Chinese J. Chem. Eng. 19, 439–445 (2011).
Yang, Z. Z., Wei, J. Y., Liu, H. T., Zhao, W. X. & Zhang, Y. Preparation and Antibacterial Ability of Silver-Loaded Maifanite. Adv. Mater. Res. 197–198, 947–952 (2011).
Schütz, T., Dolinská, S., Hudec, P., Mockovčiaková, A. & Znamenáčková, I. Cadmium adsorption on manganese modified bentonite and bentonite–quartz sand blend. Int. J. Miner. Process. 150, 32–38 (2016).
Yang, Z. et al. Comparison of effect of La-modification on the thermostabilities of alumina and alumina-supported Pd catalysts prepared from different alumina sources. Appl. Catal. B Environ. 29, 185–194 (2001).
Huang, W. et al. Phosphate removal from wastewater using red mud. J. Hazard. Mater. 158, 35–42 (2008).
Liu, Y., Lin, C. & Wu, Y. Characterization of red mud derived from a combined Bayer Process and bauxite calcination method. J. Hazard. Mater. 146, 255–261 (2007).
Yin, H., Han, M. & Tang, W. Phosphorus sorption and supply from eutrophic lake sediment amended with thermally-treated calcium-rich attapulgite and a safety evaluation. Chem. Eng. J. 285, 671–678 (2016).
Gao, Y., Guo, Y. & Zhang, H. Iron modified bentonite: Enhanced adsorption performance for organic pollutant and its regeneration by heterogeneous visible light photo-Fenton process at circumneutral pH. J. Hazard. Mater. 302, 105–113 (2016).
Chutia, P., Kato, S., Kojima, T. & Satokawa, S. Adsorption of As(V) on surfactant-modified natural zeolites. J. Hazard. Mater. 162, 204–211 (2009).
Hasmath Farzana, M. & Meenakshi, S. Photocatalytic aptitude of titanium dioxide impregnated chitosan beads for the reduction of Cr(VI). Int. J. Biol. Macromol. 72, 1265–1271 (2015).
El-korashy, S. A., Elwakeel, K. Z. & El-hafeiz, A. A. Fabrication of bentonite/thiourea-formaldehyde composite material for Pb (II), Mn (VII) and Cr (VI) sorption: A combined basic study and industrial application. J. Clean. Prod. 137, 40–50 (2016).
Gopalakannan, V., Periyasamy, S. & Viswanathan, N. Synthesis of assorted metal ions anchored alginate bentonite biocomposites for Cr (VI) sorption. Carbohydr. Polym. 151, 1100–1109 (2016).
Zhang, Y. et al. In-situ Adsorption-Biological Combined Technology Treating Sediment Phosphorus in all Fractions. Sci. Rep. 6, 29725 (2016).
Li, Y. et al. Phosphate removal from aqueous solutions using raw and activated red mud and fly ash. J. Hazard. Mater. 137, 374–383 (2006).
Wang, D., Chen, N., Yu, Y., Hu, W. & Feng, C. Investigation on the adsorption of phosphorus by Fe-loaded ceramic adsorbent. J. Colloid Interface Sci. 464, 277–284 (2016).
Huang, L. et al. Effect of temperature on phosphorus sorption to sediments from shallow eutrophic lakes. Ecol. Eng. 37, 1515–1522 (2011).
Sugiyama, S. & Hama, T. Effects of water temperature on phosphate adsorption onto sediments in an agricultural drainage canal in a paddy-field district. Ecol. Eng. 61, 94–99 (2013).
Jin, X., Wang, S., Pang, Y., Zhao, H. & Zhou, X. The adsorption of phosphate on different trophic lake sediments. Colloids Surfaces A Physicochem. Eng. Asp. 254, 241–248 (2005).
Mezenner, N. Y. & Bensmaili, A. Kinetics and thermodynamic study of phosphate adsorption on iron hydroxide-eggshell waste. Chem. Eng. J. 147, 87–96 (2009).
Oguz, E. Removal of phosphate from aqueous solution with blast furnace slag. J. Hazard. Mater. 114, 131–137 (2004).
Rahni, S. Y., Mirghaffari, N., Rezaei, B. & Ghaziaskar, H. S. Removal of phosphate from aqueous solutions using a new modified bentonite-derived hydrogel. Water. Air. Soil Pollut. 225 (2014).
Yang, Q., Zhang, J., Zhu, K. & Zhang, H. Influence of oxytetracycline on the structure and activity of microbial community in wheat rhizosphere soil. J. Environ. Sci. 21, 954–959 (2009).
Ho, Y. S. Review of second-order models for adsorption systems. J. Hazard. Mater. 136, 681–689 (2006).
Liu, J., Wan, L., Zhang, L. & Zhou, Q. Effect of pH, ionic strength, and temperature on the phosphate adsorption onto lanthanum-doped activated carbon fiber. J. Colloid Interface Sci. 364, 490–496 (2011).
Xue, Y., Hou, H. & Zhu, S. Characteristics and mechanisms of phosphate adsorption onto basic oxygen furnace slag. J. Hazard. Mater. 162, 973–980 (2009).
Arai, Y. & Sparks, D. L. ATR-FTIR spectroscopic investigation on phosphate adsorption mechanisms at the ferrihydrite-water interface. J. Colloid Interface Sci. 241, 317–326 (2001).
Ma, J. & Zhu, L. Simultaneous sorption of phosphate and phenanthrene to inorgano-organo-bentonite from water. J. Hazard. Mater. 136, 982–988 (2006).
Zhang, Y. et al. Release characteristics of sediment phosphorus in all fractions of West Lake, Hang Zhou, China. Ecol. Eng. 95, 645–651 (2016).
Ruban, V. et al. Harmonized protocol and certified reference material for the determination of extractable contents of phosphorus in freshwater sediments–a synthesis of recent works. Fresenius. J. Anal. Chem. 370, 224–228 (2001).
Sing, K. The use of nitrogen adsorption for the characterisation of porous materials. Colloids Surfaces A Physicochem. Eng. Asp. 187–188, 3–9 (2001).
This research was supported by National Natural Science Foundation of China (No. 51709254), and the Knowledge Innovation Program of the Chinese Academy of Sciences. We thank Drs Dong Xu, Enrong Xiao and Junmei Wu for the experimental help. Thanks are also due to Ms Liping Zhang for her valuable comments on this paper. The authors thank Yunyun Zou from shiyanjia lab for support of FTIR analysis (www.Shiyanjia.com).
The authors declare no competing interests.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Liu, Z., Zhang, Y., Han, F. et al. Investigation on the adsorption of phosphorus in all fractions from sediment by modified maifanite. Sci Rep 8, 15619 (2018). https://doi.org/10.1038/s41598-018-34144-w
- Adsorption Rate
- Fourier Transform Infrared (FTIR)
- Adsorption Capacity
- Modification Treatment
- Combined Modifications
Implications of phosphorus partitioning at the suspended particle-water interface for lake eutrophication in China’s largest freshwater lake, Poyang Lake
Effects of maifanite on growth, physiological and phytochemical process of submerged macrophytes Vallisneria spiralis
Ecotoxicology and Environmental Safety (2020)
Influence of fermentation on antioxidant and hypolipidemic properties of maifanite mineral water-cultured common buckwheat sprouts
Food Chemistry (2020)
The effect of silicate mineral maifanite on the growth of submerged macrophytes <i>Vallisneria spiralis</i>
Journal of Lake Sciences (2020)