## Abstract

The origin of the ferromagnetism in metal-free graphitic materials has been a decade-old puzzle. The possibility of long-range magnetic order in graphene has been recently questioned by the experimental findings that point defects in graphene, such as fluorine adatoms and vacancies, lead to defect-induced paramagnetism but no magnetic ordering down to 2 K. It remains controversial whether collective magnetic order in graphene can emerge from point defects at finite temperatures. This work provides a new framework for understanding the ferromagnetism in hydrogenated graphene, highlighting the key contribution of the spin-polarized pseudospin as a “mediator” of long-range magnetic interactions in graphene. Using first-principles calculations of hydrogenated graphene, we found that the unique ‘zero-energy’ position of H-induced quasilocalized states enables notable spin polarization of the graphene’s sublattice pseudospin. The pseudospin-mediated magnetic interactions between the H-induced magnetic moments stabilize the two-dimensional ferromagnetic ordering with Curie temperatures of T_{c} = n_{H} × 34,000 K for the atom percentage n_{H} of H adatoms. These findings show that atomic-scale control of hydrogen adsorption on graphene can give rise to a robust magnetic order.

## Introduction

The two-dimensional (2D) magnetism in graphene has attracted considerable attention because of its exceptional promise in graphene-based spintronics^{1,2,3,4,5,6,7,8,9,10,11,12}. Several experiments showed that the ferromagnetic order in graphitic materials originates from the carbon *π*-electron systems rather than from magnetic impurities^{13,14,15}. Further studies have shown that point defects in graphitic materials contribute to carbon-based ferromagnetism^{16,17,18,19,20,21}. Recently, proximity-induced ferromagnetism^{22,23,24,25} was also demonstrated for a single-layer graphene placed on an insulating magnetic substrate. Despite decades of research on carbon-based magnetism, it remains unclear under what conditions long-range magnetic order can emerge from point defects in graphitic materials. Contrary to the previous notion that graphene ferromagnetism arises from defect-induced magnetic moments^{16,17,18,19,20,21}, Nair *et al*.^{5} recently demonstrated that point defects in graphene, such as fluorine adatoms and vacancies, lead to notable paramagnetism but no magnetic ordering down to liquid helium temperatures. The maximum response of the induced paramagnetism was limited to one moment per approximately 1,000 carbon atoms. The lack of collective magnetic order in graphene was attributed to the absence of long-range magnetic interactions between the well-separated magnetic moments^{5}, with the implication that previously reported room-temperature ferromagnetism in graphitic materials^{3,13,14,15,26,27} might originate from undetected magnetic impurities or particles.

Recent scanning tunneling microscope experiments^{11} have provided direct evidence that individual hydrogen atoms adsorbed on graphene induce magnetic moments, creating opportunities for atomic-scale control of graphene ferromagnetism^{11,12}. As in the graphene systems with fluorine adatoms or carbon vacancies^{5}, however, the magnetic response in hydrogenated graphene is limited because the phase separation into pure graphene and fully hydrogenated graphene (called graphane) parts is thermodynamically more stable^{28}. The ferromagnetism at reasonably high temperatures in such a magnetically dilute system thus requires long-range magnetic interactions between the H-induced magnetic moments, as well as controlled hydrogenation of graphene under non-equilibrium conditions.

Using spin-polarized density functional theory (DFT) calculations, we show that hydrogenated graphene not only hosts H-induced localized spins but also responds to them by forming spin-polarized pseudospin as a “mediator” of long-range magnetic interactions in graphene. In hydrogenated graphene, it is well-known that the C–H *σ*-bond formation effectively induces a “vacancy” in the *π*-electron system^{2,29,30,31}, creating a quasilocalized state occupied by an electron^{11,32,33} and an associated magnetic moment (Fig. 1a). The H-induced ‘vacancy’ state lies almost at the Dirac-point energy^{11,30,31}, unlike the cases of fluorine adatoms and carbon vacancies with the corresponding defect state at lower energy^{2,30}. The unique energy position of the H-induced ‘vacancy’ state in the half-filled *π*-electron system enables strong pseudospin-mediated magnetic interactions. Hereafter, we refer to the H-induced “vacancy” state as an “A-vacancy” or “B-vacancy”, depending on which sublattice of the graphene contains the adsorption site.

## Results and Discussion

### Direct versus “mediated” magnetic interactions in hydrogenated graphene

Figure 1b depicts two different types of magnetic interaction in hydrogenated graphene: (i) The direct (DR) exchange interaction J_{DR}, which arises from the overlap between the wavefunctions of “vacancies”, leads to ferromagnetic (FM) interaction between “vacancies” in the same sublattices^{11,18}. Because of the slow decay of the wavefunctions, the interaction range is relatively large (Fig. 2a). For two nearby “vacancies” in opposing sublattices (not shown in Fig. 1b), the electronic coupling between the “vacancy” states leads to short-range antiferromagnetic (AFM) interaction or even quenching of the defect-induced magnetic moments if the distance is too small^{11,18,34}. (ii) In addition to the “conventional” magnetic interactions based on the wavefunction overlap, we show that “unconventional” long-range interactions exist that involve a delocalized “mediator” between the localized spins (zoomed-in view in Fig. 1b). The “mediator” (its physical nature will be discussed later) interacts with individual localized spins in a mean-field sense. The “mediated” magnetic interaction can be interpreted as a long-range pairwise interaction, whose strength is inversely proportional to the number of sites |*Λ*| in the graphene. The long-range (LR) interaction is FM for a pair of “vacancies” in the same sublattice \((\frac{{J}_{LR}^{FM}}{|{\rm{\Lambda }}|})\), while it is AFM for a pair in opposing sublattices \((\frac{{J}_{LR}^{AFM}}{|{\rm{\Lambda }}|})\).

To distinguish the long-range “mediated” magnetic interaction from the direct exchange interaction, we performed DFT calculations of hydrogenated graphene using judiciously chosen H-adatom positions (see Methods and Supplementary Table S1). The H adatoms in a graphene supercell exist either as an isolated H or as an H pair of a single type, which was chosen among the three types of pairs denoted by pair 1, 2, and 3 in the inset of Fig. 2a. The direct exchange interaction beyond 20 Å was neglected. First, we consider only the “A-vacancies”. The magnetic interaction energy is then given by

where the symbol (*i*, *j*) in the first term denotes the H pairs of a given type, and \({J}_{DR}^{{\rm{pair}}}\) is the corresponding direct exchange interaction. A local magnetic moment \({m}_{i}^{A}\) at site *i* on the A sublattice can take either 1 (spin up) or –1 (down). The spin-polarized DFT calculations were performed in the S_{z} = S subspace; thus, \(S=\frac{1}{2}| \sum _{i}{m}_{i}^{A}| \). We considered two different spin configurations, {*m*^{(1)}} and {*m*^{(2)}}, for which some of the FM-coupled (*i*, *j*) pairs in {*m*^{(1)}} were changed to the AFM-coupled (*i*, *j*) pairs in {*m*^{(2)}} (Supplementary Table S1). From the number of FM-to-AFM spin flips (*N*_{flip}), the energy difference is given by \({E}^{(1)}-{E}^{(2)}=-\,2{N}_{{\rm{f}}{\rm{l}}{\rm{i}}{\rm{p}}}\,\,{J}_{DR}^{{\rm{p}}{\rm{a}}{\rm{i}}{\rm{r}}}-{J}_{LR}^{FM}\frac{{({\sum }_{i}{m}_{i}^{A(1)})}^{2}-{({\sum }_{i}{m}_{i}^{A(2)})}^{2}}{2|{\rm{\Lambda }}|}\). By defining \({\rm{\Delta }}{E}^{\ast }=\frac{{E}^{(1)}-{E}^{(2)}}{2{N}_{{\rm{flip}}}}\) and \({\rm{\Delta }}{M}^{\ast }=\frac{{({\sum }_{i}{m}_{i}^{A(1)})}^{2}-{({\sum }_{i}{m}_{i}^{A(2)})}^{2}}{4{N}_{{\rm{flip}}}|{\rm{\Lambda }}|}\), we obtain a simple linear relation between them:

Indeed, the DFT data in Fig. 2b lie almost on straight lines with \({J}_{LR}^{FM}\) = 2.2 eV, which indicates that in addition to the direct exchange interaction (first term in Eq. 1), a long-range “mediated” interaction exists that is scaled with \(\frac{1}{|{\rm{\Lambda }}|}\) (second term in Eq. 1).

### Long-range magnetic interactions mediated by spin-polarized pseudospin

We next turn to the question of what mediates the long-range magnetic interaction in graphene. We temporarily ignore the spin degree of freedom and focus on the low-energy graphene states in the presence of a finite density of “A-vacancies”. Each “A-vacancy” induces a ‘zero-energy’ quasilocalized state, whose charge density is distributed only on the B sublattice sites^{32}. The electron hopping between sites on the opposing sublattices of graphene then makes the “A-vacancy” state selectively hybridized with the \(| {\rm{A}}\rangle \) sublattice state (Supplementary Fig. S1). As a result, the low-energy graphene state near the Fermi energy becomes “polarized” to the remaining \(| {\rm{B}}\rangle \) pseudospin. We now consider the real spin polarization. Because their constituent orbitals are on the same sublattice, the direct exchange interaction between the spin-up “A-vacancy” state and the \(| {\rm{B}}\rangle \) pseudospin induces parallel magnetization on the \(| {\rm{B}}\rangle \) pseudospin. To demonstrate this effect, we considered two H_{A} impurities in a graphene supercell (Fig. 3a–c). For the FM state in Fig. 3a, the spin-up polarized \(| {\rm{B}}\rangle \) (yellow) is induced as the spin-polarized pseudospin (SPPS), which fills the graphene (see Fig. 3c and legend for more details). The spin polarization of \(| {\rm{B}}\rangle \) does not violate Lieb’s theorem^{35} because the local magnetic moments of the “A-vacancies” are reduced by the hybridization with \(| {\rm{A}}\rangle \). We note that as a secondary effect, the spin-up \(| {\rm{B}}\rangle \) induces the antiparallel magnetization (blue) on the opposite sublattice in Fig. 3a due to exchange polarization^{18}. For the AFM state in Fig. 3b, however, the \(| {\rm{B}}\rangle \) pseudospin is non-spin-polarized due to the spin up-down symmetry of the two “A-vacancies”, which results in spin polarization only around the impurities.

Figure 3d illustrates the mechanism of the SPPS-mediated FM interaction between the “vacancies” in the same sublattices. Here, we assume many “A-vacancies”, although only two of them are shown in the schematic. For the local magnetic moments \(\{{m}_{i}^{A}\}\), \(\sum _{i}{m}_{i}^{A} > 0\) was assumed; thus, the \(| {\rm{B}}\rangle \) pseudospin is spin-up polarized. Regarding individual localized spins, each spin *m*^{A} interacts with the spin-up \(| {\rm{B}}\rangle \) through the direct exchange interaction, which lowers the system’s energy when *m*^{A} takes the same spin direction as that of the SPPS (i.e., *m*^{A} = 1), with an energy gain proportional to \({J}_{LR}^{FM}\frac{{\sum }_{i}{m}_{i}^{A}}{|{\rm{\Lambda }}|}\). Therefore, the SPPS effectively mediates the pairwise FM interaction with the coupling strength of \(\frac{{J}_{LR}^{FM}}{|{\rm{\Lambda }}|}\).

We now consider the mixture of H_{A} and H_{B} in graphene. The spin ground state has \(\sum _{i}{m}_{i}^{A}=| {H}_{A}| \) and \(\sum _{i}{m}_{i}^{B}=-\,| {H}_{B}| \) at zero temperature^{18}, where |H_{A}| and |H_{B}| are the number of H adatoms at the graphene’s A and B sublattices. Assuming an antiparallel net magnetization on opposite sublattices at finite temperatures, the low-energy graphene state for the occupied electrons is characterized by the spin-up \(| {\rm{B}}\rangle \) and spin-down \(| {\rm{A}}\rangle \) (Supplementary Fig. S2). The spin-flipped counterparts constitute the unoccupied pseudospin state above the Fermi energy (Fig. 3e). In addition to the FM interaction between a pair of “vacancies” in the same sublattices, a superexchange interaction exists between the occupied (or unoccupied) “vacancy” state and the unoccupied (or occupied) SPPS of the same spin. The electron hopping between opposite sublattices results in the sublattice-dependent hybridization between the localized spins and the SPPS with the effective coupling \(\alpha =\frac{{t}^{\ast }}{\sqrt{|{\rm{\Lambda }}|}}\), where *t*^{*} = 3.3 eV in the DFT calculations (Supplementary Fig. S1). The superexchange interaction is a second-order interaction proportional to 𝛼^{2} and thus scales with \(\frac{1}{|{\rm{\Lambda }}|}\). For \(\sum _{i}{m}_{i}^{A} > 0\) and \(\sum _{i}{m}_{i}^{B} < 0\), the SPPS-mediated interaction energetically favors *m*^{B} = −1 and *m*^{A} = 1, hence effectively leading to the AFM interaction of \(\frac{{J}_{LR}^{AFM}}{|{\rm{\Lambda }}|}\) for a pair of “vacancies” in opposing sublattices.

### Mean-field ferromagnetism in graphene

By combining the two types of SPPS-mediated interactions, we obtain the interaction energy for a given spin state \(\{{m}_{i}^{A},\,{m}_{j}^{B}\}\),

Our DFT calculations show that the AFM interaction is stronger than the FM interaction, with a ratio of \(\frac{{J}_{LR}^{AFM}}{{J}_{LR}^{FM}}\) = 4.3 (see Methods for details). The long-range nature of the SPPS-mediated interactions allows us to use a mean-field approximation with \({E}_{LR}^{MFA}\) = \(-(\tfrac{{J}_{LR}^{FM}|{H}_{A}|}{2|{\rm{\Lambda }}|}\langle {m}^{A}\rangle -\tfrac{{J}_{LR}^{AFM}|{H}_{B}|}{2|{\rm{\Lambda }}|}\langle {m}^{B}\rangle )\sum _{i}{m}_{i}^{A}\) − \((\tfrac{{J}_{LR}^{FM}|{H}_{B}|}{2|{\rm{\Lambda }}|}\langle {m}^{B}\rangle -\tfrac{{J}_{LR}^{AFM}|{H}_{A}|}{2|{\rm{\Lambda }}|}\langle {m}^{A}\rangle )\sum _{i}{m}_{i}^{B}\), in which the ensemble-averaged spins, 〈*m*^{A}(T)〉 and 〈*m*^{B}(T)〉, at temperature T are calculated self-consistently (Methods). We define two characteristic temperatures, \({T}_{F}=\frac{{n}_{H}{J}_{LR}^{FM}}{4{k}_{B}}\) and \({T}_{AF}=\frac{{n}_{H}{J}_{LR}^{AFM}}{4{k}_{B}}\), where k_{B} is the Boltzmann constant, and n_{H} is the atom percentage of H adatoms. Figure 4a shows the magnetization as a function of the reduced temperature T/T_{F} for the different probabilities, P_{A} and P_{B}, of having H_{A} and H_{B} on the graphene layer. The magnetization per H adatom is \(m=\frac{|{H}_{A}|-|{H}_{B}|}{|{H}_{A}|+|{H}_{B}|}={P}_{A}-{P}_{B}\) at T = 0, which is consistent with Lieb’s theorem^{35}. A slight imbalance with P_{A} = 0.51 and P_{B} = 0.49, for example, induces *m* = 0.02 μ_{B}/atom, which corresponds to the magnetization per weight of 0.1 Am^{2}/kg at n_{H} = 1 at. % (Supplementary Fig. S3). The preferential H adsorption for one sublattice might be possible using a suitable substrate for graphene such as hexagonal boron nitride^{36} or exploiting the effect of the stacking order of multilayer graphene^{18}. Near the Curie temperature T_{c}, the magnetization M ~ (T_{c} – T)^{β} has the critical exponent β = 0.5, regardless of P_{A} and P_{B} (Fig. 4b), as expected from mean-field theory^{37}.

Unlike the magnetization in Fig. 4a, the Curie temperature weakly depends on P_{A} and P_{B}, which enables the enhanced magnetization while maintaining the high T_{c}. The T_{c} is \({T}_{c}={T}_{F}+\sqrt{{({P}_{A}-{P}_{B})}^{2}{T}_{F}^{2}+4{P}_{A}{P}_{B}{T}_{AF}^{2}}\) and has a maximum at P_{A} = P_{B} with \({{T}_{c}}^{max}={T}_{F}+{T}_{AF}\) = n_{H} × 34,000 K (Fig. 4c). To achieve room-temperature ferromagnetism (Supplementary Fig. S3), it is necessary to introduce a relatively high concentration (~1 at. %) of H adatoms, which are magnetically active and not quenched by forming H-adatom “dimers”^{11,18,34}. Partial hydrogenation of graphene with high n_{H} is challenging because of the phase separation of hydrogenated graphene^{28}. Therefore, controlled hydrogenation under non-equilibrium conditions is required to realize room-temperature FM graphene.

We note that the AFM interaction contributes to \({{T}_{c}}^{max}={T}_{F}+{T}_{AF}\) as much as the FM interaction. This may appear to contradict the notion that the AFM interaction typically reduces the T_{c}; for carrier-mediated FM semiconductors (e.g., Mn-doped GaAs), the T_{c} is determined by competition between the FM and AFM interactions^{38}, i.e., \({T}_{c}={T}_{F}-{T}_{AF}\). For hydrogenated graphene, however, the SPPS-mediated FM and AFM interactions do not compete (Eq. 3); the spin-up \(| {\rm{B}}\rangle \) pseudospin in Fig. 3e, for example, stabilizes the spin-up polarized H_{A} through the direct exchange interaction, and the same SPPS simultaneously stabilizes the spin-down H_{B} through the superexchange interaction. The FM and AFM interactions thus “cooperate”, rather than compete, in hydrogenated graphene.

## Summary and Conclusions

In summary, we have shown that the SPPS-mediated, long-range magnetic interactions give rise to a robust magnetic order in hydrogenated graphene, which can be stable even at room temperature for the H concentration of n_{H} ~ 1 at. %. The “cooperativeness” of the FM and AFM interactions contributes to the high T_{c}. The realization of the robust 2D ferromagnetism in such a magnetically and electrically dilute system is unusual; the 2D magnetism in hydrogenated graphene is described by mean-field theory owing to the intrinsic long-range nature of the SPPS-mediated interactions. Our new finding of the mechanism underlying graphene ferromagnetism should have enormous implications for understanding and atomic-scale control of graphene-based magnetism, which is an important step toward bringing the vision described in “*Painting magnetism on a canvas of graphene* (ref.^{12})” closer to reality.

## Methods

### Spin-polarized density-functional theory (DFT) calculations

We calculated total energies and spin densities of partially hydrogenated graphene using the generalized gradient approximation (GGA-PBE^{39}) to DFT, as implemented in the Vienna ab-initio Simulation Package^{40}. The DFT calculations employed the projector augmented wave method^{41,42} with an energy cutoff of 500 eV for the plane-wave part of the wave function. For the Brillouin zone integration, we used a *Γ*-centred grid containing enough *k* points, as dense as the 60 × 60 grid for the two-atom unitcell of graphene.

### Calculations of the SPPS-mediated magnetic interactions

We first performed spin-polarized DFT calculations for H adatoms on the same sublattice of graphene to distinguish the long-range “mediated” FM interactions from the direct exchange interactions. To this end, the H positions in a graphene supercell were chosen so that only the direct pair interactions for the H pairs of a single type are involved in Eq. 1. The H pairs were selected among the three types of pairs denoted by pair 1, 2, and 3 in Fig. 2a. Different H concentrations were considered by changing either the number of H adatoms on a graphene supercell (*N*_{H} = 2, 3 or 4) or the number of the C atoms in a supercell with |*Λ*| = 96, 150, 216, 300, 384, 432, and 864 (see Supplementary Table S1 and legend for more details). Each data point in Fig. 2b was obtained from the energy difference for two different spin configurations that are listed in Supplementary Table S1. For the cases of *N*_{flip} = 0, we arbitrarily selected the “*N*_{flip} values” in \({\rm{\Delta }}{E}^{\ast }=\frac{{E}^{(1)}-{E}^{(2)}}{2{N}_{{\rm{flip}}}}\) and \({\rm{\Delta }}{M}^{\ast }=\frac{{({\sum }_{i}{m}_{i}^{A(1)})}^{2}-{({\sum }_{i}{m}_{i}^{A(2)})}^{2}}{4{N}_{{\rm{flip}}}|{\rm{\Lambda }}|}\) to plot the data in the same figure; note that these data also lie on a line with the y-intercept of zero as expected.

To extract the interaction strength of the long-range AFM interaction \({J}_{LR}^{{\rm{AFM}}}\), we considered two H adatoms on the opposing sublattices of the 864-atom graphene supercell. The two H adatoms in the supercell are well separated to ensure that the direct exchange interaction is negligible. Two spin configurations, {*m*^{(1)}} = (up, down) and {*m*^{(2)}} = (up, up), were considered. Then, from Eq. 3, the energy difference is \({E}_{LR}^{(1)}-{E}_{LR}^{(2)}=-\,\frac{2{J}_{LR}^{AFM}}{|{\rm{\Lambda }}|}\), which was calculated from the spin-polarized DFT calculations to determine \({J}_{LR}^{{\rm{AFM}}}\).

### Finite-temperature magnetism of hydrogenated grapheme

We used a mean-field approximation with \({E}_{LR}^{MFA}\) = \(-(\tfrac{{J}_{LR}^{FM}|{H}_{A}|}{2|{\rm{\Lambda }}|}\langle {m}^{A}\rangle -\tfrac{{J}_{LR}^{AFM}|{H}_{B}|}{2|{\rm{\Lambda }}|}\langle {m}^{B}\rangle )\sum _{i}{m}_{i}^{A}\) − \((\tfrac{{J}_{LR}^{FM}|{H}_{B}|}{2|{\rm{\Lambda }}|}\langle {m}^{B}\rangle -\tfrac{{J}_{LR}^{AFM}|{H}_{A}|}{2|{\rm{\Lambda }}|}\langle {m}^{A}\rangle )\sum _{i}{m}_{i}^{B}\) to obtain the ensemble averaged spins at temperature T. We introduced two characteristic temperatures, \({T}_{F}=\frac{{n}_{H}{J}_{LR}^{FM}}{4{k}_{B}}\) and \({T}_{AF}=\frac{{n}_{H}{J}_{LR}^{AFM}}{4{k}_{B}}\), where k_{B} is the Boltzmann constant, and n_{H} is the H concentration, \({n}_{H}=\frac{|{H}_{A}|+|{H}_{B}|}{|\Lambda |}\). For \({P}_{A}=\frac{|{H}_{A}|}{|{H}_{A}|+|{H}_{B}|}\) and \({P}_{B}=\frac{|{H}_{B}|}{|{H}_{A}|+|{H}_{B}|}\), the coupled equations for \(\langle {m}^{{\rm{A}}}\rangle \) and \(\langle {m}^{{\rm{B}}}\rangle \) are given by \(\langle {m}^{A}\rangle =\,\tanh [\frac{2}{T}({T}_{F}{P}_{A}-{T}_{AF}{P}_{B}\eta (T)){\langle m\rangle }^{A}]\) and \(\langle {m}^{B}\rangle =\,\tanh [\frac{2}{T}({T}_{F}{P}_{B}-{T}_{AF}{P}_{A}\frac{1}{\eta (T)})\langle {m}^{B}\rangle ]\), where \(\eta (T)\) is the ratio of the magnetization on the opposing sublattices. \(\eta (T)\) was determined numerically as a function of temperatures. We found that \(\eta \) is always negative; for P_{A} = P_{B}, \(\eta \) is constant with \(\eta =-\,1\), while for the case of P_{A} ≠ P_{B}, it gradually increases in magnitude with increasing T. From the condition of no net magnetization on each sublattice at T_{c}, we obtained \(\eta ({T}_{c})=-\frac{1}{2}\frac{{T}_{F}}{{T}_{AF}}(1-\frac{{P}_{A}}{{P}_{B}})-\) \(\sqrt{\frac{{P}_{A}}{{P}_{B}}+\frac{1}{4}{(\frac{{T}_{F}}{{T}_{AF}})}^{2}{(1-\frac{{P}_{A}}{{P}_{B}})}^{2}}\) and \({T}_{c}={T}_{F}+\sqrt{{({P}_{A}-{P}_{B})}^{2}{T}_{F}^{2}+4{P}_{A}{P}_{B}{T}_{AF}^{2}}\).

## References

- 1.
Makarova, T. & Palacio, F.

*Carbon Based Magnetism: An Overview of the Magnetism of Metal Free Carbon-based Compounds and Materials*. (Elsevier, Amsterdam, 2006). - 2.
Yazyev, O. V. Emergence of magnetism in graphene materials and nanostructures.

*Rep. Prog. Phys.***73**, 056501 (2010). - 3.
Wang, Y.

*et al*. Room-temperature ferromagnetism of graphene.*Nano Lett.***9**, 220–224 (2009). - 4.
Sepioni, M.

*et al*. Limits on intrinsic magnetism in graphene.*Phys. Rev. Lett.***105**, 207205 (2010). - 5.
Nair, R. R.

*et al*. Spin-half paramagnetism in graphene induced by point defects.*Nat. Phys.***8**, 199–202 (2012). - 6.
Lee, A. T., Kang, J., Wei, S.-H., Chang, K. J. & Kim, Y.-H. Carrier-mediated long-range ferromagnetism in electron-doped Fe-C

_{4}and Fe-N_{4}incorporated graphene.*Phys. Rev. B.***86**, 165403 (2012). - 7.
Giesbers, A. J. M.

*et al*. Interface-induced room-temperature ferromagnetism in hydrogenated epitaxial graphene.*Phys. Rev. Lett.***111**, 166101 (2013). - 8.
Zhang, Y.

*et al*. Scanning tunneling microscopy of the*π*magnetism of a single carbon vacancy in graphene.*Phys. Rev. Lett.***117**, 166801 (2016). - 9.
Son, Y.-W., Cohen, M. L. & Louie, S. G. Half-metallic graphene nanoribbons.

*Nature***444**, 347 (2006). - 10.
Magda, G. Z.

*et al*. Room-temperature magnetic order on zigzag edges of narrow graphene nanoribbons.*Nature.***514**, 608–611 (2014). - 11.
González-Herrero, H.

*et al*. Atomic-scale control of graphene magnetism by using hydrogen atoms.*Science.***352**, 437–441 (2016). - 12.
Hollen, S. M. & Gupta, J. A. Painting magnetism on a canvas of graphene.

*Science***352**, 415 (2016). - 13.
Ohldag, H.

*et al*.*π*-electron ferromagnetism in metal-free carbon probed by soft x-ray dichroism.*Phys. Rev. Lett.***98**, 187204 (2007). - 14.
Barzola-Quiquia, J.

*et al*. Experimental evidence for two-dimensional magnetic order in proton bombarded graphite.*Phys. Rev. B.***76**, 161403 (2007). - 15.
Ohldag, H.

*et al*. The role of hydrogen in room-temperature ferromagnetism at graphite surfaces.*New J. Phys.***12**, 123012 (2010). - 16.
Červenka, J., Katsnelson, M. I. & Flipse, C. F. J. Room-temperature ferromagnetism in graphite driven by two-dimensional networks of point defects.

*Nat. Phys.***5**, 840–844 (2009). - 17.
Yazyev, O. V. & Helm, L. Defect-induced magnetism in graphene.

*Phys. Rev. B***75**, 125408 (2007). - 18.
Yazyev, O. V. Magnetism in disordered graphene and irradiated graphite.

*Phys. Rev. Lett.***101**, 037203 (2008). - 19.
Kumazaki, H. & Hirashima, D. S. Nonmagnetic-defect-induced magnetism in graphene.

*J. Phys. Soc. Jpn.***76**, 064713 (2007). - 20.
Palacios, J. J., Fernández-Rossier, J. & Brey, L. Vacancy-induced magnetism in graphene and graphene ribbons.

*Phys. Rev. B.***77**, 195428 (2008). - 21.
Ugeda, M. M., Brihuega, I., Guinea, F. & Gómez-Rodríguez, J. M. Missing atom as a source of carbon magnetism.

*Phys. Rev. Lett.***104**, 096804 (2010). - 22.
Wang, Z., Tang, C., Sachs, R., Barlas, Y. & Shi, J. Proximity-induced ferromagnetism in graphene revealed by the anomalous Hall effect.

*Phys. Rev. Lett.***114**, 016603 (2015). - 23.
Wei, P.

*et al*. Strong interfacial exchange field in the graphene/EuS heterostructure.*Nat. Mater.***15**, 711–716 (2016). - 24.
Leutenantsmeyer, J. C., Kaverzin, A. A., Wojtaszek, M. & van Wees, B. J. Proximity induced room temperature ferromagnetism in graphene probed with spin currents.

*2D Mater.***4**, 014001 (2017). - 25.
Song, Y. Electric-field-induced extremely large change in resistance in graphene ferromagnets.

*J. Phys. D: Appl. Phys.***51**, 025002 (2018). - 26.
Esquinazi, P.

*et al*. Induced magnetic ordering by proton irradiation in graphite.*Phys. Rev. Lett.***91**, 227201 (2003). - 27.
Xia, H.

*et al*. Tunable magnetism in carbon-ion-implanted highly oriented pyrolytic graphite.*Adv. Mater.***20**, 4679–4683 (2008). - 28.
Xiang, H., Kang, E., Wei, S.-H., Whangbo, M.-H. & Yang, J. “Narrow” graphene nanoribbons made easier by partial hydrogenation.

*Nano Lett.***9**, 4025–4030 (2009). - 29.
Kang, J. & Wei, S.-H. Tunable Anderson localization in hydrogenated graphene based on the electric field effect.

*Phys. Rev. Lett.***111**, 216801 (2013). - 30.
Wehling, T. O., Katsnelson, M. I. & Lichtenstein, A. I. Impurities on graphene: Midgap states and migration barriers.

*Phys. Rev. B***80**, 085428 (2009). - 31.
Halbertal, D.

*et al*. Imaging resonant dissipation from individual atomic defects in graphene.*Science***358**, 1303–1306 (2017). - 32.
Pereira, V. M. & Guinea, F. Lopes dos Santos, J. M. B., Peres, N. M. R. & Castro Neto, A. H. Disorder induced localized states in graphene.

*Phys. Rev. Lett.***96**, 036801 (2006). - 33.
Castro, E. V., López-Sancho, M. P. & Vozmediano, M. A. H. New type of vacancy-induced localized states in multilayer graphene.

*Phys. Rev. Lett.***104**, 036802 (2010). - 34.
Boukhvalov, D. W., Katsnelson, M. I. & Lichtenstein, A. I. Hydrogen on graphene: Electronic structure, total energy, structural distortions and magnetism from first-principles calculations.

*Phys. Rev. B***77**, 035427 (2008). - 35.
Lieb, E. H. Two theorems on the Hubbard model.

*Phys. Rev. Lett.***62**, 1201–1204 (1989). - 36.
Hemmatiyan, S., Polini, M., Abanov, A., MacDonald, A. H. & Sinova, J. Stable path to ferromagnetic hydrogenated graphene growth.

*Phys. Rev. B***90**, 035433 (2014). - 37.
Sethna, J. P. Statistical Mechanics: Entropy, Order Parameters, and Complexity (Oxford, 2006).

- 38.
Dietl, T., Ohno, H., Matsukura, F., Cibert, J. & Ferrand, D. Zener model description of ferromagnetism in zinc-blende magnetic semiconductors.

*Science***287**, 1019–1022 (2000). - 39.
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple.

*Phys. Rev. Lett.***77**, 3865–3868 (1996). - 40.
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set.

*Phys. Rev. B***54**, 11169–11186 (1996). - 41.
Blöchl, P. E. Projector augmented-wave method.

*Phys. Rev. B***50**, 17953–17979 (1994). - 42.
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method.

*Phys. Rev. B***59**, 1758–1775 (1999).

## Acknowledgements

This work was supported by the DGIST R&D Program of the Ministry of Science and ICT of Korea (Grant No. 18-BT-02).

## Author information

### Affiliations

### Contributions

J.K. conceived the project, H.K. did the calculations, all authors analyzed the data and wrote the manuscript.

### Corresponding author

## Ethics declarations

### Competing Interests

The authors declare no competing interests.

## Additional information

**Publisher's note:** Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## Electronic supplementary material

## Rights and permissions

**Open Access** This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

## About this article

### Cite this article

Kim, H., Bang, J. & Kang, J. Robust ferromagnetism in hydrogenated graphene mediated by spin-polarized pseudospin.
*Sci Rep* **8, **13940 (2018). https://doi.org/10.1038/s41598-018-31934-0

Received:

Accepted:

Published:

### Keywords

- Pseudospin
- Long-range Magnetic Interactions
- Collective Magnetic Order
- Atomic-scale Control
- Adatoms

## Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.